MX2017000189A - Metodo para producir una hoja de acero de alta resistencia y hoja obtenida por dicho metodo. - Google Patents

Metodo para producir una hoja de acero de alta resistencia y hoja obtenida por dicho metodo.

Info

Publication number
MX2017000189A
MX2017000189A MX2017000189A MX2017000189A MX2017000189A MX 2017000189 A MX2017000189 A MX 2017000189A MX 2017000189 A MX2017000189 A MX 2017000189A MX 2017000189 A MX2017000189 A MX 2017000189A MX 2017000189 A MX2017000189 A MX 2017000189A
Authority
MX
Mexico
Prior art keywords
steel
sheet
cooling
temperature
mpa
Prior art date
Application number
MX2017000189A
Other languages
English (en)
Inventor
Arlazarov Artem
Xu Wei
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=52000883&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=MX2017000189(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2017000189A publication Critical patent/MX2017000189A/es

Abstract

Un método para fabricar una hoja de acero de alta resistencia que tiene una resistencia a la tracción superior a 1,100 MPa y una resistencia a elasticidad superior a 700 MPa, un alargamiento uniforme UE de al menos 8.0% y un alargamiento total de al menos 10%, hecha de un acero que contiene en porcentaje en peso: 0.1% = C = 0,25%, 4,5% = Mn = 10%, 1% = Si = 3%, 0.03% = Al = 2.5%, siendo el resto Fe e impurezas resultantes de la fundición, siendo la composición tal que el Índice CMn = Cx(1 + Mn/3.5)=0.6, el método comprende las etapas de recocer una hoja laminada realizada de dicho acero embebiéndola a una temperatura de recocido TA mayor al punto de transformación Ac1 del acero pero inferior a 1,000°C, enfriando la hoja recocida a una temperatura de templado QT entre 190°C y 80°C a una velocidad de enfriamiento suficiente para obtener una estructura justo después del enfriamiento que contiene martensita y austenita retenida, manteniendo la hoja de acero a una temperatura de sobre-envejecimiento PT entre 350°C y 500°C durante un tiempo de sobre-envejecimiento Pt superior a 5 seg enfriando la hoja hasta la temperatura ambiente. Asimismo se describe la oja obtenida por dicho método.
MX2017000189A 2014-07-03 2015-07-03 Metodo para producir una hoja de acero de alta resistencia y hoja obtenida por dicho metodo. MX2017000189A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2014/002285 WO2016001703A1 (en) 2014-07-03 2014-07-03 Method for manufacturing a high strength steel sheet and sheet obtained by the method
PCT/IB2015/055033 WO2016001889A2 (en) 2014-07-03 2015-07-03 Method for manufacturing a high-strength steel sheet and sheet obtained by the method

Publications (1)

Publication Number Publication Date
MX2017000189A true MX2017000189A (es) 2017-05-01

Family

ID=52000883

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2017000189A MX2017000189A (es) 2014-07-03 2015-07-03 Metodo para producir una hoja de acero de alta resistencia y hoja obtenida por dicho metodo.

Country Status (16)

Country Link
US (2) US10844455B2 (es)
EP (2) EP3656879B1 (es)
JP (2) JP6636962B2 (es)
KR (2) KR102432167B1 (es)
CN (1) CN106661654B (es)
BR (1) BR112017000027B1 (es)
CA (1) CA2954135C (es)
ES (2) ES2999365T3 (es)
FI (1) FI3656879T3 (es)
HU (2) HUE069028T2 (es)
MA (2) MA49660B1 (es)
MX (1) MX2017000189A (es)
PL (1) PL3164513T3 (es)
RU (1) RU2683785C2 (es)
UA (1) UA118793C2 (es)
WO (2) WO2016001703A1 (es)

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102016104800A1 (de) * 2016-03-15 2017-09-21 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung eines warmumgeformten Stahlbauteils und ein warmumgeformtes Stahlbauteil
KR101798771B1 (ko) 2016-06-21 2017-11-17 주식회사 포스코 항복강도가 우수한 초고강도 고연성 강판 및 그 제조방법
WO2018055425A1 (en) * 2016-09-22 2018-03-29 Arcelormittal High strength and high formability steel sheet and manufacturing method
KR101839235B1 (ko) * 2016-10-24 2018-03-16 주식회사 포스코 구멍확장성 및 항복비가 우수한 초고강도 강판 및 그 제조방법
CN108929992B (zh) * 2017-05-26 2020-08-25 宝山钢铁股份有限公司 一种热浸镀中锰钢及其制造方法
WO2019122964A1 (en) * 2017-12-19 2019-06-27 Arcelormittal Steel sheet having excellent toughness, ductility and strength, and manufacturing method thereof
CN121161156A (zh) * 2018-03-30 2025-12-19 Ak钢铁产权公司 低合金第三代先进高强度钢和制造方法
JP6690793B1 (ja) * 2018-06-29 2020-04-28 日本製鉄株式会社 高強度鋼板およびその製造方法
WO2021123888A1 (en) 2019-12-19 2021-06-24 Arcelormittal Cold rolled and heat-treated steel sheet and method of manufacturing the same
WO2021123887A1 (en) 2019-12-19 2021-06-24 Arcelormittal High toughness hot rolled steel sheet and method of manufacturing the same
WO2021123889A1 (en) * 2019-12-19 2021-06-24 Arcelormittal Hot rolled and heat-treated steel sheet and method of manufacturing the same
WO2021123886A1 (en) 2019-12-19 2021-06-24 Arcelormittal High toughness hot rolled and annealed steel sheet and method of manufacturing the same
WO2022018500A1 (en) 2020-07-24 2022-01-27 Arcelormittal Cold rolled and double annealed steel sheet
WO2022242859A1 (en) 2021-05-20 2022-11-24 Nlmk Clabecq Method for manufacturing a high strength steel plate and high strength steel plate
CN113943896B (zh) * 2021-10-18 2022-10-18 宁波祥路中天新材料科技股份有限公司 一种抗拉强度≥1200MPa级的异型材用钢及生产方法
CN114178783A (zh) * 2021-11-11 2022-03-15 常熟晶晟汽车零部件有限公司 一种高压油泵的冷镦工艺方法
CN117144244A (zh) * 2023-08-25 2023-12-01 首钢集团有限公司 一种环境友好型农机用钢及其制备方法

Family Cites Families (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6217125A (ja) * 1985-07-15 1987-01-26 Nippon Steel Corp 高強度高延性鋼材の製造方法
JP2588421B2 (ja) 1988-04-11 1997-03-05 日新製鋼株式会社 延性に優れた超高強度鋼材の製造方法
JPH06128631A (ja) 1992-10-20 1994-05-10 Nippon Steel Corp 低温靱性の優れた高マンガン超高張力鋼の製造方法
JP3857939B2 (ja) 2001-08-20 2006-12-13 株式会社神戸製鋼所 局部延性に優れた高強度高延性鋼および鋼板並びにその鋼板の製造方法
AU2003270334A1 (en) * 2002-09-04 2004-03-29 Colorado School Of Mines Method for producing steel with retained austenite
AR042494A1 (es) 2002-12-20 2005-06-22 Sumitomo Chemical Co Acero inoxidable martensitico de alta resistencia con excelentes propiedades de resistencia a la corrosion por dioxido de carbono y resistencia a la corrosion por fisuras por tensiones de sulfuro
CN101376945B (zh) 2007-08-28 2011-06-15 宝山钢铁股份有限公司 2000MPa级超高强度高韧性钢板及其制造方法
JP5365216B2 (ja) 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
EP2123787A1 (fr) 2008-05-06 2009-11-25 Industeel Creusot Acier à hautes caractéristiques pour pièces massives
KR101027250B1 (ko) 2008-05-20 2011-04-06 주식회사 포스코 고연성 및 내지연파괴 특성이 우수한 고강도 냉연강판,용융아연 도금강판 및 그 제조방법
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5365112B2 (ja) 2008-09-10 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
CN101638749B (zh) 2009-08-12 2011-01-26 钢铁研究总院 一种低成本高强塑积汽车用钢及其制备方法
JP5883211B2 (ja) 2010-01-29 2016-03-09 株式会社神戸製鋼所 加工性に優れた高強度冷延鋼板およびその製造方法
JP5287770B2 (ja) 2010-03-09 2013-09-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5327106B2 (ja) 2010-03-09 2013-10-30 Ｊｆｅスチール株式会社 プレス部材およびその製造方法
JP5333298B2 (ja) * 2010-03-09 2013-11-06 Ｊｆｅスチール株式会社 高強度鋼板の製造方法
KR101243002B1 (ko) * 2010-12-22 2013-03-12 주식회사 포스코 연신율이 우수한 고강도 강판 및 그 제조방법
KR20120071583A (ko) 2010-12-23 2012-07-03 주식회사 포스코 저온인성이 우수한 고강도 고망간강
KR101253885B1 (ko) 2010-12-27 2013-04-16 주식회사 포스코 연성이 우수한 성형 부재용 강판, 성형 부재 및 그 제조방법
JP5440672B2 (ja) 2011-09-16 2014-03-12 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板およびその製造方法
CN103890202B (zh) 2011-10-24 2015-09-30 杰富意钢铁株式会社 加工性优良的高强度钢板的制造方法
RU2474623C1 (ru) 2011-10-31 2013-02-10 Валентин Николаевич Никитин Способ производства высокопрочной листовой стали мартенситного класса и деформационно-термический комплекс для его осуществления
KR101382981B1 (ko) * 2011-11-07 2014-04-09 주식회사 포스코 온간프레스 성형용 강판, 온간프레스 성형 부재 및 이들의 제조방법
JP2013237923A (ja) * 2012-04-20 2013-11-28 Jfe Steel Corp 高強度鋼板およびその製造方法
RU2491357C1 (ru) 2012-05-10 2013-08-27 Федеральное государственное автономное образовательное учреждение высшего профессионального образования "Национальный исследовательский технологический университет "МИСиС" Способ производства листовой стали
JP2014019928A (ja) 2012-07-20 2014-02-03 Jfe Steel Corp 高強度冷延鋼板および高強度冷延鋼板の製造方法
JP5585623B2 (ja) 2012-07-23 2014-09-10 新日鐵住金株式会社 熱間成形鋼板部材およびその製造方法
JP5857905B2 (ja) 2012-07-25 2016-02-10 新日鐵住金株式会社 鋼材およびその製造方法
WO2014020640A1 (ja) 2012-07-31 2014-02-06 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
CN102912219A (zh) * 2012-10-23 2013-02-06 鞍钢股份有限公司 一种高强塑积trip钢板及其制备方法

Also Published As

Publication number Publication date
BR112017000027A2 (pt) 2017-10-31
WO2016001703A1 (en) 2016-01-07
CA2954135A1 (en) 2016-01-07
FI3656879T3 (fi) 2024-11-04
HUE050194T2 (hu) 2020-11-30
JP2019214792A (ja) 2019-12-19
ES2811838T3 (es) 2021-03-15
EP3164513A2 (en) 2017-05-10
EP3656879A3 (en) 2020-07-22
CA2954135C (en) 2023-09-12
MA49660A (fr) 2020-05-27
RU2683785C2 (ru) 2019-04-02
WO2016001889A2 (en) 2016-01-07
UA118793C2 (uk) 2019-03-11
ES2999365T3 (en) 2025-02-25
KR20220097546A (ko) 2022-07-07
MA49660B1 (fr) 2024-11-29
KR102432167B1 (ko) 2022-08-11
WO2016001889A3 (en) 2016-03-17
EP3656879A2 (en) 2020-05-27
JP6894476B2 (ja) 2021-06-30
BR112017000027B1 (pt) 2021-05-11
CN106661654A (zh) 2017-05-10
JP6636962B2 (ja) 2020-01-29
JP2017524824A (ja) 2017-08-31
US10844455B2 (en) 2020-11-24
MA40191B1 (fr) 2020-08-31
US11692235B2 (en) 2023-07-04
EP3164513B1 (en) 2020-05-13
HUE069028T2 (hu) 2025-02-28
KR102464730B1 (ko) 2022-11-07
EP3656879B1 (en) 2024-09-18
PL3164513T3 (pl) 2020-11-02
CN106661654B (zh) 2018-12-25
US20200399733A1 (en) 2020-12-24
RU2016151791A (ru) 2018-06-27
RU2016151791A3 (es) 2018-12-10
US20170137909A1 (en) 2017-05-18
KR20170026440A (ko) 2017-03-08

Similar Documents

Publication Publication Date Title
MX2017000189A (es) Metodo para producir una hoja de acero de alta resistencia y hoja obtenida por dicho metodo.
MX2016017400A (es) Metodo para fabricar una hoja de acero de alta resistencia y hoja obtenida.
MX2016011987A (es) Metodo para producir un producto de acero plano laminado en frio con alto limite elastico y producto de acero plano laminado en frio.
MX2017000177A (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia, ductilidad y capacidad de formacion mejoradas.
MX2017000201A (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia y capacidad de formacion mejoradas y hoja obtenida.
MX375455B (es) Metodo para producir una hoja de acero revestida o no revestida de resistencia ultra alta y hoja obtenida por dicho metodo.
MX2016012491A (es) Metodo para producir un producto plano de acero altamente resistente.
MX371103B (es) Metodo para producir material de acero de alta resistencia, excelente en resistencia a agrietamiento por tension de sulfuro.
UA122878C2 (uk) Спосіб виробництва високоміцної листової сталі, яка характеризується покращеними пластичністю і штампованістю, і одержана листова сталь
MX2018007641A (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
UA114044C2 (xx) Сталевий лист з високими механічними властивостями, як-то механічна міцність і пластичність, спосіб виготовлення такого листа та його застосування
MX394289B (es) Lámina de acero laminada en frío de alta resistencia y método para fabricar la misma.
MX2016014990A (es) Hoja de acero doblemente recocida que tiene resistencia mecanica alta y caracteristicas de ductilidad, metodo de fabricacion y uso de tales hojas.
MX2016017398A (es) Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida.
MX2016017399A (es) Metodo para producir una hoja de acero recubierta de alta resistencia con una resistencia, ductilidad y capacidad de formacion mejoradas.
MX380199B (es) Método para producir una hoja de acero de alta resistencia que tiene capacidad de formación mejorada y hoja obtenida por dicho método.
MX2016013771A (es) Metodo para la produccion de lamina de acero galvanizada de alta resistencia y lamina de acero galvano-recocida de alta resistencia.
MX2018004385A (es) Acero, producto creado a partir de tal acero, y metodo de fabricacion del mismo.
MX2021006508A (es) Lamina de acero recocida y laminada en frio, metodo de produccion de la misma y uso de tal acero para producir piezas de vehiculos.
CO2017009718A2 (es) Hoja de acero para una lata y método para fabricarla
WO2016001892A3 (en) Method for manufacturing a high strength steel sheet having improved formability and ductility and sheet obtained
MX2017008027A (es) Hoja de acero martensitico de calibre liviano laminada en caliente y metodo para fabricarla.
RU2016129453A (ru) Горячепрессованное стальное листовое изделие, способ его изготовления и стальной лист для горячего прессования
MX2018007648A (es) Metodo para producir una hoja de acero que tiene resistencia, ductilidad y formabilidad mejoradas.
MX2021015145A (es) Metodo de produccion de lamina de acero revestida de alta resistencia con resistencia y conformabilidad mejoradas.