MX2016016129A - Hoja de acero galvanizada multifasica de alta resistencia, metodo de produccion y uso. - Google Patents

Hoja de acero galvanizada multifasica de alta resistencia, metodo de produccion y uso.

Info

Publication number
MX2016016129A
MX2016016129A MX2016016129A MX2016016129A MX2016016129A MX 2016016129 A MX2016016129 A MX 2016016129A MX 2016016129 A MX2016016129 A MX 2016016129A MX 2016016129 A MX2016016129 A MX 2016016129A MX 2016016129 A MX2016016129 A MX 2016016129A
Authority
MX
Mexico
Prior art keywords
steel sheet
production method
high strength
galvanized steel
strength multiphase
Prior art date
Application number
MX2016016129A
Other languages
English (en)
Other versions
MX380760B (es
Inventor
Dongwei Fan
Jun Hyun Jo
A Rotole John
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2016016129A publication Critical patent/MX2016016129A/es
Publication of MX380760B publication Critical patent/MX380760B/es

Abstract

La invención se refiere a una hoja de acero que comprende, en porcentaje en peso: 0.05 = C = 0.15%, 2 = Mn = 3%, Al = 0.1%, 0.3 = Si = 1.5%, 0.01% = Nb = 0.05%, N = 0.02%, 0.1 = Cr + Mo = 1%, 0.0001 = B < 0.0025%, Ti = 0.5%, V<0.01%, S = 0.01%, P = 0.05%, el restante de la composición siendo hierro e impurezas inevitables que resultan de la fundición y la microestructura consiste de, en fracción de superficie: entre 50 y 95% de martensita y entre 5 y 50% de la suma de ferrita y bainita, en donde el tamaño de grano de ferrita está por debajo de 10 pm. El acero de acuerdo con la invención se oxida y posteriormente se reduce durante las etapas de calentamiento, inmersión y enfriamiento del recocido.
MX2016016129A 2014-06-06 2014-06-06 Hoja de acero galvanizada multifásica de alta resistencia, método de producción y uso. MX380760B (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IB2014/000991 WO2015185956A1 (en) 2014-06-06 2014-06-06 High strength multiphase galvanized steel sheet, production method and use

Publications (2)

Publication Number Publication Date
MX2016016129A true MX2016016129A (es) 2017-03-28
MX380760B MX380760B (es) 2025-03-04

Family

ID=51212883

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2016016129A MX380760B (es) 2014-06-06 2014-06-06 Hoja de acero galvanizada multifásica de alta resistencia, método de producción y uso.

Country Status (16)

Country Link
US (2) US10612107B2 (es)
EP (1) EP3152336B1 (es)
JP (1) JP6599902B2 (es)
KR (1) KR102389648B1 (es)
CN (1) CN106471147B (es)
BR (1) BR112016027681B1 (es)
CA (1) CA2951215C (es)
ES (1) ES2729870T3 (es)
HU (1) HUE044866T2 (es)
MA (1) MA39954B1 (es)
MX (1) MX380760B (es)
PL (1) PL3152336T3 (es)
RU (1) RU2675025C2 (es)
TR (1) TR201907448T4 (es)
UA (1) UA117865C2 (es)
WO (2) WO2015185956A1 (es)

Families Citing this family (50)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6131919B2 (ja) * 2014-07-07 2017-05-24 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法
ES2674133T3 (es) * 2014-12-01 2018-06-27 Voestalpine Stahl Gmbh Procedimiento para el tratamiento térmico de un producto de manganeso-acero
JP6020605B2 (ja) * 2015-01-08 2016-11-02 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法
WO2016198906A1 (fr) 2015-06-10 2016-12-15 Arcelormittal Acier a haute résistance et procédé de fabrication
EP3415653B1 (en) * 2016-02-10 2020-03-04 JFE Steel Corporation High-strength galvanized steel sheet and method for producing same
EP3421633B1 (en) * 2016-03-31 2020-05-13 JFE Steel Corporation Thin steel sheet, plated steel sheet, method for producing hot-rolled steel sheet, method for producing cold-rolled full-hard steel sheet, method for producing thin steel sheet, and method for producing plated steel sheet
WO2017168961A1 (ja) * 2016-03-31 2017-10-05 Ｊｆｅスチール株式会社 薄鋼板およびめっき鋼板、並びに、熱延鋼板の製造方法、冷延フルハード鋼板の製造方法、薄鋼板の製造方法およびめっき鋼板の製造方法
CN105908089B (zh) * 2016-06-28 2019-11-22 宝山钢铁股份有限公司 一种热浸镀低密度钢及其制造方法
MX2019001147A (es) * 2016-08-10 2019-06-10 Jfe Steel Corp Lamina de acerro de alta resistencia y metodo para producir la misma.
US11091817B2 (en) 2016-08-30 2021-08-17 Jfe Steel Corporation High-strength steel sheet and method for manufacturing the same
JP6432705B2 (ja) * 2016-09-30 2018-12-05 Ｊｆｅスチール株式会社 高強度めっき鋼板及びその製造方法
KR101889181B1 (ko) 2016-12-19 2018-08-16 주식회사 포스코 굽힘성 및 신장플랜지성이 우수한 고장력강 및 이의 제조방법
CN107164624B (zh) * 2017-04-10 2020-02-21 首钢集团有限公司 一种控制含磷冷轧高强钢表面麻点缺陷的方法
CN107254572B (zh) * 2017-06-01 2019-07-02 首钢集团有限公司 一种冷轧硅锰双相钢表面麻点缺陷的控制方法
CN109207841B (zh) 2017-06-30 2021-06-15 宝山钢铁股份有限公司 一种低成本高成型性1180MPa级冷轧退火双相钢板及其制造方法
BR112019026926A2 (pt) * 2017-08-09 2020-07-07 Nippon Steel Corporation chapa de aço laminada a quente e método para produção da mesma
DE102017123236A1 (de) * 2017-10-06 2019-04-11 Salzgitter Flachstahl Gmbh Höchstfester Mehrphasenstahl und Verfahren zur Herstellung eines Stahlbandes aus diesem Mehrphasenstahl
EP3653745A4 (en) * 2017-10-20 2020-07-15 JFE Steel Corporation HIGH-STRENGTH STEEL SHEET AND MANUFACTURING METHOD THEREOF
KR102398709B1 (ko) * 2017-10-20 2022-05-16 제이에프이 스틸 가부시키가이샤 고강도 강판 및 그 제조 방법
CN107761007A (zh) * 2017-10-23 2018-03-06 攀钢集团攀枝花钢铁研究院有限公司 低碳冷轧超高强双相钢及其制备方法
JP6607339B1 (ja) 2017-12-22 2019-11-20 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板の製造方法及び連続溶融亜鉛めっき装置
JP7137492B2 (ja) * 2018-03-28 2022-09-14 株式会社神戸製鋼所 合金化溶融亜鉛めっき鋼板、及び合金化溶融亜鉛めっき鋼板の製造方法
WO2020049344A1 (en) * 2018-09-07 2020-03-12 Arcelormittal Method for improving the formability of steel blanks
MX2021007713A (es) 2018-12-26 2021-08-05 Jfe Steel Corp Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para producir la misma.
BE1026986B1 (fr) * 2019-01-23 2020-08-25 Drever Int S A Procédé et four pour le traitement thermique d’une bande d’acier de haute résistance comprenant une chambre d’homogénéisation en température
WO2020158228A1 (ja) * 2019-01-29 2020-08-06 Ｊｆｅスチール株式会社 高強度鋼板及びその製造方法
WO2021123887A1 (en) * 2019-12-19 2021-06-24 Arcelormittal High toughness hot rolled steel sheet and method of manufacturing the same
WO2021176249A1 (en) * 2020-03-02 2021-09-10 Arcelormittal High strength cold rolled and galvannealed steel sheet and manufacturing process thereof
CN111411295B (zh) * 2020-03-24 2021-06-15 首钢集团有限公司 一种多相钢构件及其制备方法、应用
CN113737108A (zh) * 2020-05-27 2021-12-03 宝山钢铁股份有限公司 一种耐延迟开裂的电镀锌超强双相钢及其制造方法
EP3925771A1 (en) * 2020-06-16 2021-12-22 SSAB Technology AB High strength steel product and method of manufacturing the same
KR102457019B1 (ko) * 2020-06-17 2022-10-21 주식회사 포스코 성형성이 우수한 고강도 강판 및 이의 제조방법
CN114107789B (zh) * 2020-08-31 2023-05-09 宝山钢铁股份有限公司 一种780MPa级高表面高性能稳定性超高扩孔钢及其制造方法
WO2022042730A1 (zh) * 2020-08-31 2022-03-03 宝山钢铁股份有限公司 一种高强度低碳马氏体高扩孔钢及其制造方法
WO2022191008A1 (ja) * 2021-03-08 2022-09-15 株式会社神戸製鋼所 溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法
JP2022136976A (ja) * 2021-03-08 2022-09-21 株式会社神戸製鋼所 溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法
CN117098867B (zh) * 2021-03-31 2025-10-24 日本制铁株式会社 钢板及钢板的制造方法
CN115181891B (zh) * 2021-04-02 2023-07-11 宝山钢铁股份有限公司 980MPa级别低碳低合金热镀锌双相钢及快速热处理热镀锌制造方法
CN113930599B (zh) * 2021-09-24 2023-06-13 首钢集团有限公司 一种改善镀锌hsla组织均匀性的制造方法
CN114231838A (zh) * 2021-11-17 2022-03-25 邯郸钢铁集团有限责任公司 低残余应力冷成型高强钢s700mc及其生产方法
CN114480986B (zh) * 2022-01-28 2023-03-24 本钢板材股份有限公司 一种热镀锌双相钢带钢及其生产工艺
CN114807755B (zh) * 2022-04-15 2024-03-26 马鞍山钢铁股份有限公司 一种具有良好涂层质量的高强韧性预涂覆钢板及其制备方法以及钢构件及其应用
EP4303516A1 (en) 2022-07-05 2024-01-10 John Cockerill S.A. Device for improving preoxidation in an annealing furnace
CN115584440A (zh) * 2022-10-19 2023-01-10 攀钢集团攀枝花钢铁研究院有限公司 一种具有不同屈强比的1180MPa级连退双相钢及其制备方法
EP4636110A1 (en) * 2022-12-15 2025-10-22 Nippon Steel Corporation Steel sheet and manufacturing method for steel sheet
CN116732428A (zh) * 2023-02-24 2023-09-12 首钢集团有限公司 一种1180MPa级别热镀锌复相钢及其制备方法
WO2024192218A1 (en) 2023-03-14 2024-09-19 Cleveland-Cliffs Steel Properties Inc. High strength galvanized and galvannealed steel sheets and manufacturing method
CN116727440B (zh) * 2023-05-22 2026-01-09 鞍钢股份有限公司 一种提高屈服强度315MPa级钢板轧制节奏的方法
WO2025056941A1 (en) * 2023-09-12 2025-03-20 Arcelormittal A cold rolled martensitic steel and a method of martensitic steel thereof
CN118471357B (zh) * 2024-05-17 2025-02-18 深圳问鼎生态环境有限公司 一种铁系高级氧化过程模拟方法及系统

Family Cites Families (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3646538B2 (ja) * 1998-10-02 2005-05-11 Ｊｆｅスチール株式会社 加工性に優れた溶融亜鉛めっき高張力鋼板の製造方法
JP3882679B2 (ja) * 2002-05-23 2007-02-21 Ｊｆｅスチール株式会社 めっき外観の良好な深絞り性に優れた複合組織型高張力溶融亜鉛めっき冷延鋼板の製造方法
US6811624B2 (en) 2002-11-26 2004-11-02 United States Steel Corporation Method for production of dual phase sheet steel
US20070006948A1 (en) * 2003-05-27 2007-01-11 Toshiki Nonaka High strength thin steel sheet excellent in resistance to delayed fracture after forming and method for preparation thereof , and automobile parts requiring strength manufactured from high strength thin steel sheet
US7883769B2 (en) 2003-06-18 2011-02-08 3M Innovative Properties Company Integrally foamed microstructured article
JP4486336B2 (ja) * 2003-09-30 2010-06-23 新日本製鐵株式会社 溶接性と延性に優れた高降伏比高強度冷延鋼板および高降伏比高強度溶融亜鉛めっき鋼板、並びに、高降伏比高強度合金化溶融亜鉛めっき鋼板とその製造方法
CA2540762C (en) 2003-09-30 2012-09-18 Nippon Steel Corporation High yield ratio and high-strength thin steel sheet superior in weldability and ductility, high-yield ratio high-strength hot-dip galvanized thin steel sheet, high-yield ratio high-strength hot-dip galvannealed thin steel sheet, and methods of production of same
JP5162836B2 (ja) * 2006-03-01 2013-03-13 新日鐵住金株式会社 溶接部の耐水素脆性に優れる高強度冷延鋼板及びその製造方法
US9067260B2 (en) 2006-09-06 2015-06-30 Arcelormittal France Steel plate for producing light structures and method for producing said plate
EP1897963A1 (fr) 2006-09-06 2008-03-12 ARCELOR France Tole d'acier pour la fabrication de structures allegées et procédé de fabrication de cette tole
JP5194878B2 (ja) * 2007-04-13 2013-05-08 Ｊｆｅスチール株式会社 加工性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
EP2009127A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvanized or a galvannealed steel sheet by DFF regulation
PL2028282T3 (pl) * 2007-08-15 2012-11-30 Thyssenkrupp Steel Europe Ag Stal dwufazowa, płaski wyrób wytworzony ze stali dwufazowej i sposób wytwarzania płaskiego wyrobu
ES2578952T3 (es) * 2008-03-27 2016-08-03 Nippon Steel & Sumitomo Metal Corporation Chapa de acero laminada en frío, chapa de acero galvanizado de alta resistencia y chapa de acero galvanizado por inmersión en caliente aleada de alta resistencia que tiene excelente conformabilidad y soldabilidad, y métodos para fabricar las mismas
JP5251208B2 (ja) 2008-03-28 2013-07-31 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
JP5504643B2 (ja) * 2008-08-19 2014-05-28 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP2010126757A (ja) * 2008-11-27 2010-06-10 Jfe Steel Corp 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5394709B2 (ja) * 2008-11-28 2014-01-22 株式会社神戸製鋼所 耐水素脆化特性および加工性に優れた超高強度鋼板
JP5564784B2 (ja) * 2008-12-05 2014-08-06 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板の製造方法
MX2011010247A (es) * 2009-03-31 2011-10-11 Jfe Steel Corp Plancha de acero galvanizado por inmersion en caliente de alta resistencia y metodo para producir la misma.
JP4924730B2 (ja) * 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
ES2613410T3 (es) * 2009-05-27 2017-05-24 Nippon Steel & Sumitomo Metal Corporation Lámina de acero de alta resistencia, lámina de acero bañado en caliente, y lámina de acero bañado en caliente de aleación que tienen excelentes características de fatiga, alargamiento y colisión, y método de fabricación para dichas láminas de acero
ES2384135T3 (es) 2009-08-25 2012-06-29 Thyssenkrupp Steel Europe Ag Procedimiento para fabricar un componente de acero provisto de un recubrimiento metálico de protección contra la corrosión y componente de acero
GB2493302A (en) * 2010-03-29 2013-01-30 Kobe Steel Ltd Ultra high strength steel plate having excellent workability, and protection method for same
JP5771034B2 (ja) 2010-03-29 2015-08-26 株式会社神戸製鋼所 加工性に優れた超高強度鋼板、およびその製造方法
JP5434960B2 (ja) * 2010-05-31 2014-03-05 Ｊｆｅスチール株式会社 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
KR20120075260A (ko) * 2010-12-28 2012-07-06 주식회사 포스코 도금밀착성이 우수한 용융도금강판 및 그 제조방법
UA112771C2 (uk) 2011-05-10 2016-10-25 Арселормітталь Інвестігасьон І Десароло Сл Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
DE102011051731B4 (de) 2011-07-11 2013-01-24 Thyssenkrupp Steel Europe Ag Verfahren zur Herstellung eines durch Schmelztauchbeschichten mit einer metallischen Schutzschicht versehenen Stahlflachprodukts
CN103827335B (zh) * 2011-09-30 2015-10-21 新日铁住金株式会社 镀锌钢板及其制造方法
BR112014007500A2 (pt) * 2011-09-30 2017-04-04 Nippon Steel & Sumitomo Metal Corp folha de aço galvanizada por imersão a quente e método de fabricação da mesma
ES2614465T3 (es) * 2012-07-10 2017-05-31 Thyssenkrupp Steel Europe Ag Producto plano de acero laminado en frío y procedimiento para su fabricación

Also Published As

Publication number Publication date
ES2729870T3 (es) 2019-11-06
US10612107B2 (en) 2020-04-07
CA2951215A1 (en) 2015-12-10
CN106471147B (zh) 2018-07-10
MA39954A (fr) 2017-04-12
BR112016027681B1 (pt) 2021-04-27
TR201907448T4 (tr) 2019-06-21
CA2951215C (en) 2023-08-01
US11047020B2 (en) 2021-06-29
US20190256942A1 (en) 2019-08-22
MA39954B1 (fr) 2019-05-31
CN106471147A (zh) 2017-03-01
WO2015185956A1 (en) 2015-12-10
PL3152336T3 (pl) 2019-08-30
WO2015185975A1 (en) 2015-12-10
US20170137906A1 (en) 2017-05-18
MX380760B (es) 2025-03-04
JP6599902B2 (ja) 2019-10-30
KR20170015303A (ko) 2017-02-08
UA117865C2 (uk) 2018-10-10
RU2016147787A3 (es) 2018-10-26
EP3152336A1 (en) 2017-04-12
KR102389648B1 (ko) 2022-04-21
RU2675025C2 (ru) 2018-12-14
RU2016147787A (ru) 2018-06-06
HUE044866T2 (hu) 2019-11-28
EP3152336B1 (en) 2019-02-20
JP2017520681A (ja) 2017-07-27

Similar Documents

Publication Publication Date Title
MX2016016129A (es) Hoja de acero galvanizada multifasica de alta resistencia, metodo de produccion y uso.
UA118036C2 (uk) Високоміцна сталь та спосіб виготовлення
MX2017015841A (es) Acero de alta resistencia y metodo de fabricacion.
UA117134C2 (uk) Холоднокатаний сталевий лист, спосіб його виробництва і автотранспортний засіб
MX2019006862A (es) Producto de acero plano laminado en caliente y metodo para la produccion del mismo.
UA114877C2 (uk) Двічі відпалений сталевий лист з високою механічною міцністю і пластичністю, спосіб виготовлення і використання такого листа
MX359361B (es) Acero de baja densidad laminado en caliente o frio, metodo de implementacion y su uso.
MX375453B (es) Metodo para fabricar una hoja de acero de alta resistencia y hoja obtenida.
MX2017006303A (es) Metodo para fabricar un producto de acero de alta resistencia y un producto de acero obtenido por el mismo.
UA115745C2 (uk) Спосіб виготовлення високоміцного сталевого листа з покриттям або без покриття і одержаний лист
UA122807C2 (uk) Спосіб виробництва високоміцної листової сталі, яка характеризується покращеними тягучістю і формованістю, та отримана листова сталь
AR100959A1 (es) Acero inoxidable martensítico - ferrítico, producto manufacturado, proceso para la producción de piezas o barras forjadas o laminadas de acero inoxidable martensítico - ferrítico y proceso para la producción de tubo sin costura de acero inoxidable martensítico - ferrítico
MX2016014963A (es) Tira de acero que tiene alta resistencia y alta plasticidad, la tira de acero tiene un recubrimiento a base de zinc en caliente.
RU2015136606A (ru) Высокопрочная стальная полоса с низким отношением предела текучести к пределу прочности и способ ее производства
MX2017009200A (es) Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
JP2016509130A5 (es)
MX2015011027A (es) Hoja de acero laminada en caliente y metodo para fabricar la misma.
MX2016015400A (es) Material de acero tratado con calor y metodo para producir el mismo.
UA116699C2 (uk) Лист з мартенситної сталі і спосіб його отримання, а також деталь і конструктивний елемент транспортного засобу, виконані з вказаного листа, і сам транспортний засіб
UA118793C2 (uk) Спосіб виготовлення високоміцного сталевого листа і одержаний лист
MX2016002824A (es) Metodo de fabricacion de una tuberia de acero inoxidable de alta resistencia y una tuberia de acero inoxidable de alta resistencia.
MX386195B (es) Lámina de acero laminada en caliente de alto contenido en carbono y método para la producción de la misma.
GB2548049A (en) Hot rolled light-gauge martensitic steel sheet and method for making the same
MX2016014667A (es) Acero inoxidable ferritico.
EA201270785A1 (ru) Низколегированная сталь с повышенным пределом текучести и высокой устойчивостью к образованию трещин под действием нагрузки, вызываемой сульфидами