WO2026008399A1 - Procédé de fabrication d'un (oxy)hydroxyde ou d'un oxyde particulaire, (oxy)hydroxyde particulaire et utilisation associée - Google Patents

Procédé de fabrication d'un (oxy)hydroxyde ou d'un oxyde particulaire, (oxy)hydroxyde particulaire et utilisation associée

Info

Publication number
WO2026008399A1
WO2026008399A1 PCT/EP2025/067803 EP2025067803W WO2026008399A1 WO 2026008399 A1 WO2026008399 A1 WO 2026008399A1 EP 2025067803 W EP2025067803 W EP 2025067803W WO 2026008399 A1 WO2026008399 A1 WO 2026008399A1
Authority
WO
WIPO (PCT)
Prior art keywords
range
hydroxide
solution
zero
oxy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/EP2025/067803
Other languages
English (en)
Inventor
Joop Enno FRERICHS
Maike WIRTZ
Balazs Barnabas BERKES
Kathrin Michel
Rafael Benjamin BERK
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF SE filed Critical BASF SE
Publication of WO2026008399A1 publication Critical patent/WO2026008399A1/fr
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

L'invention concerne un procédé de fabrication d'un (oxy)hydroxyde ou d'un oxyde particulaire de TM, TM représentant des métaux, ledit procédé étant mis en œuvre dans une cascade de deux réacteurs à cuve agitée.
PCT/EP2025/067803 2024-07-01 2025-06-24 Procédé de fabrication d'un (oxy)hydroxyde ou d'un oxyde particulaire, (oxy)hydroxyde particulaire et utilisation associée Pending WO2026008399A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP24185796 2024-07-01
EP24185796.0 2024-07-01

Publications (1)

Publication Number Publication Date
WO2026008399A1 true WO2026008399A1 (fr) 2026-01-08

Family

ID=91759399

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2025/067803 Pending WO2026008399A1 (fr) 2024-07-01 2025-06-24 Procédé de fabrication d'un (oxy)hydroxyde ou d'un oxyde particulaire, (oxy)hydroxyde particulaire et utilisation associée

Country Status (1)

Country Link
WO (1) WO2026008399A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2720305A1 (fr) 2011-06-07 2014-04-16 Sumitomo Metal Mining Co., Ltd. Hydroxyde composite contenant du nickel et procédé de fabrication dudit hydroxyde, matériau actif positif pour batterie secondaire à électrolyte non aqueux et procédé de fabrication dudit matériau actif, et batterie secondaire à électrolyte non aqueux
CN112591807A (zh) 2020-12-23 2021-04-02 华友新能源科技（衢州）有限公司 一种高致密度镍钴锰氢氧化物的制备方法
WO2022207383A1 (fr) * 2021-03-31 2022-10-06 Basf Se Procédé de fabrication d'oxyhydroxyde ou d'oxydes de particules
WO2023135055A1 (fr) * 2022-01-17 2023-07-20 Basf Se Procédé de fabrication d'(oxy) hydroxydes particulaires et d'(oxy) hydroxydes particulaires (oxy)
EP4149890B1 (fr) * 2020-05-12 2024-02-14 Basf Se Matériaux actifs d'électrode et leur procédé de fabrication
EP4149889B1 (fr) * 2020-05-15 2024-05-22 Basf Se Procédé de fabrication d'un (oxy)hydroxyde particulaire et matériau actif d'électrode fabriqué à partir de celui-ci

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2720305A1 (fr) 2011-06-07 2014-04-16 Sumitomo Metal Mining Co., Ltd. Hydroxyde composite contenant du nickel et procédé de fabrication dudit hydroxyde, matériau actif positif pour batterie secondaire à électrolyte non aqueux et procédé de fabrication dudit matériau actif, et batterie secondaire à électrolyte non aqueux
EP4149890B1 (fr) * 2020-05-12 2024-02-14 Basf Se Matériaux actifs d'électrode et leur procédé de fabrication
EP4149889B1 (fr) * 2020-05-15 2024-05-22 Basf Se Procédé de fabrication d'un (oxy)hydroxyde particulaire et matériau actif d'électrode fabriqué à partir de celui-ci
CN112591807A (zh) 2020-12-23 2021-04-02 华友新能源科技（衢州）有限公司 一种高致密度镍钴锰氢氧化物的制备方法
WO2022207383A1 (fr) * 2021-03-31 2022-10-06 Basf Se Procédé de fabrication d'oxyhydroxyde ou d'oxydes de particules
WO2023135055A1 (fr) * 2022-01-17 2023-07-20 Basf Se Procédé de fabrication d'(oxy) hydroxydes particulaires et d'(oxy) hydroxydes particulaires (oxy)

Similar Documents

Publication Publication Date Title
JP7638966B2 (ja) 粒子状物質、その製造方法及び使用方法
EP4149889B1 (fr) Procédé de fabrication d'un (oxy)hydroxyde particulaire et matériau actif d'électrode fabriqué à partir de celui-ci
KR20230085913A (ko) 미립자 (옥시)수산화물의 제조 방법, 및 미립자 (옥시)수산화물 및 그 용도
WO2024033132A1 (fr) Procédé de fabrication d'un (oxy)hydroxyde et (oxy)hydroxydes
EP4263435B1 (fr) Procédé de fabrication d'un matériau actif d'électrode et matériau actif d'électrode
EP4499575A1 (fr) Procédé de fabrication d'un matériau actif de cathode dopé
WO2026008399A1 (fr) Procédé de fabrication d'un (oxy)hydroxyde ou d'un oxyde particulaire, (oxy)hydroxyde particulaire et utilisation associée
WO2026008425A1 (fr) Procédé de fabrication d'un (oxy)hydroxyde ou d'un oxyde particulaire, (oxy)hydroxyde ou oxyde particulaire et utilisation associée
EP4649057A1 (fr) Procédé de fabrication d'un (oxy)hydroxyde ou oxyde particulaire, (oxy)hydroxyde ou oxyde particulaire et utilisation
JP2023547996A (ja) ドープされたカソード活物質の製造方法
US20260028242A1 (en) Process for making an (oxy)hydroxide, and (oxy)hydroxide
WO2025078192A1 (fr) Procédé de fabrication d'un précurseur pour un matériau actif de cathode
WO2025011920A1 (fr) Procédé de fabrication d'un matériau actif de cathode et de ses précurseurs
JP2025527533A (ja) （オキシ）水酸化物の製造方法、及び（オキシ）水酸化物
CN121443558A (zh) 用于制造阴极活性材料及其前体的方法
EP4494195A1 (fr) Procédé de fabrication de matériau actif d?électrode revêtue
WO2025061478A1 (fr) Procédé de fabrication de matériau actif de cathode, et matériau actif de cathode
WO2023057280A1 (fr) Procédé de fabrication d'un matériau actif de cathode revêtue, et matériau actif de cathode revêtue
JP2023516112A (ja) カソード活物質、及びこのようなカソード活物質の製造方法