WO2024162189A1 - 化合物、硬化性樹脂組成物およびその硬化物 - Google Patents

化合物、硬化性樹脂組成物およびその硬化物 Download PDF

Info

Publication number
WO2024162189A1
WO2024162189A1 PCT/JP2024/002335 JP2024002335W WO2024162189A1 WO 2024162189 A1 WO2024162189 A1 WO 2024162189A1 JP 2024002335 W JP2024002335 W JP 2024002335W WO 2024162189 A1 WO2024162189 A1 WO 2024162189A1
Authority
WO
WIPO (PCT)
Prior art keywords
compound
acid
resin composition
represent
bis
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2024/002335
Other languages
English (en)
French (fr)
Inventor
隆行 遠島
昌典 橋本
政隆 中西
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Kayaku Co Ltd
Original Assignee
Nippon Kayaku Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Kayaku Co Ltd filed Critical Nippon Kayaku Co Ltd
Priority to JP2024519128A priority Critical patent/JP7561302B1/ja
Publication of WO2024162189A1 publication Critical patent/WO2024162189A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本発明は、優れた低誘電特性を有する化合物、硬化性樹脂組成物及びその硬化物を提供する。　スチレン系単量体からなる重合体のブロック単位（Ａ）と共役ジエン化合物からなる重合体のブロック単位（Ｂ）とからなるブロック共重合体の水素添加物（Ｈ－ＡＢ）の酸変性物である酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）とアリルアミンまたはアリルアミン塩酸塩とを反応して得られる化合物。

Description

化合物、硬化性樹脂組成物およびその硬化物
　本発明は、特定構造を有する化合物、硬化性樹脂組成物およびその硬化物に関するものであり、半導体封止材、プリント配線基板、ビルドアップ積層板などの電気・電子部品、炭素繊維強化プラスチック、ガラス繊維強化プラスチックなどの軽量高強度材料、３Ｄプリンティング用途に好適に使用される。
　近年、電気・電子部品を搭載する積層板はその利用分野の拡大により、要求特性が広範かつ高度化している。従来の半導体チップは金属製のリードフレームに搭載することが主流であったが、中央処理装置（以下、ＣＰＵと表す。）などの処理能力の高い半導体チップは高分子材料で作られる積層板に搭載されることが多くなってきている。
　現在開発が加速している第５世代通信システム「５Ｇ」では、さらなる大容量化と高速通信が進むことが予想されている。５Ｇでは使用する周波数の高周波化が進むことになるが、高周波を利用した高速通信の実現には伝送損失の低減が重要であり、基板材料の更なる低誘電特性（低誘電率および低誘電正接）が求められることとなる。プリント基板上で発生する伝送損失は導体損失と誘電損失に由来する。非特許文献１で述べられている通り、誘電損失αＤは誘電体の比誘電率εγの平方根および誘電正接ｔａｎδに比例するため、誘電損失の低減には比誘電率以上に寄与度の高い誘電正接を低減することが効果的であると言える。低誘電材料としてはＰＴＦＥ（ポリテトラフルオロエチレン）やＬＣＰ（液晶ポリマー）に代表される熱可塑性材料が挙げられるが、熱硬化性樹脂と比較し成形性に乏しい。これを踏まえ、低誘電特性に優れた熱硬化性樹脂の開発が望まれている。
　このような背景を受けて、低誘電特性に優れる熱硬化性樹脂が検討されている。例えば、特許文献１ではマレイミド基を有するイミド化合物と脂肪族不飽和結合を有するフェノールアラルキル樹脂を含む熱硬化性樹脂組成物が提案されている。しかしながら、一方で硬化反応時に反応に関与しないフェノール性水酸基が残存するため、電気特性が十分とは言えない。また特許文献２ではフェノール性水酸基にアリル基を付加したアリルエーテル変性ビフェニルアラルキルノボラック樹脂が開示されている。しかしながら、アリルエーテル変性ビフェニルノボラック樹脂は１９０℃においてクライゼン転位が起こることが示されており、一般的な基板の成型温度である２００℃においては、硬化反応に寄与しないフェノール性水酸基が生成することから電気特性を満足できるものではない。
「プリント基板上高速信号伝送における信号損失要因」、第２９回エレクトロニクス実装学会春季講演大会、セッションＩＤ：１６Ｐ１－１７、２０１５年
日本国特開平０４－３５９９１１号公報 国際公開２０１６／００２７０４号
　本発明は、このような状況を鑑みてなされたものであり、優れた低誘電特性を有する化合物、硬化性樹脂組成物及びその硬化物を提供することを目的とする。
　すなわち本発明は、下記［１］～［１１］に関する。なお、本願において「（数値１）～（数値２）」は上下限値を含むことを示す。
［１］
　スチレン系単量体からなる重合体のブロック単位（Ａ）と共役ジエン化合物からなる重合体のブロック単位（Ｂ）とからなるブロック共重合体の水素添加物（Ｈ－ＡＢ）の酸変性物である酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）とアリルアミンまたはアリルアミン塩酸塩とを反応して得られる化合物。
［２］
　前記スチレン系単量体からなる重合体のブロック単位（Ａ）は下記式（ａ）で表される構造である、前項［１］に記載の化合物。
Figure JPOXMLDOC01-appb-C000005
 　式（１）中、Ｒ１およびＲ２はそれぞれ水素原子または炭素数１～５のアルキル基であり、ｐは１～５であり、ｑは繰り返し数の平均値であり、１～１００００の実数を表す。
［３］
　前記共役ジエン化合物からなる重合体のブロック単位（Ｂ）は１，３－ブタジエン、イソプレン、ファルネセン、２，３－ジメチル－１，３－ブタジエン、１，３－ペンタジエンより選ばれる少なくとも１種以上のジエン化合物を重合させることによって得られる、前項［１］に記載の化合物。
［４］
　前記ブロック共重合体の水素添加物（Ｈ－ＡＢ）が下記式（１）で表される化合物である、前項［１］に記載の化合物。
Figure JPOXMLDOC01-appb-C000006
　式（１）中、Ｒ１およびＲ２はそれぞれ水素原子または炭素数１～５のアルキル基であり、ｐは１～５であり、ｊ，ｋ，ｌ，ｍ，ｎは繰り返し数の平均値であり、１～１００００の実数を表す。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
［５］
　前記酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）が下記式（２）で表される化合物である、前項［１］に記載の化合物。
Figure JPOXMLDOC01-appb-C000007
 
式（２）中、Ｒ１およびＲ２はそれぞれ水素原子または炭素数１～５のアルキル基であり、ｐは１～５であり、ｊ，ｋ，ｌ，ｍ，ｎは繰り返し数の平均値であり、１～１００００の実数を表す。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
［６］
　下記式（３）で表される化合物。
Figure JPOXMLDOC01-appb-C000008
（式（３）中、ｊ，ｋ，ｌ，ｍ，ｎは繰り返し数の平均値であり、１～１００００の実数を表す。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。）
［７］
　前項［１］から［６］のいずれか一項に記載の化合物を含有する硬化性樹脂組成物。
［８］
　さらに、重合開始剤を含有する前項［７］に記載の硬化性樹脂組成物。
［９］
　さらに、マレイミド化合物、ポリフェニレンエーテル化合物、エチレン性不飽和結合を有する化合物、シアネートエステル樹脂、ポリブタジエンおよびこの変性物、ポリスチレンおよびこの変性物、ポリエチレンおよびこの変性物、のうちから選ばれる少なくとも１種以上を含有する前項［７］または［８］に記載の硬化性樹脂組成物。
［１０］
　前項［１］から［６］のいずれか一項に記載の化合物の硬化物。
［１１］
　前項［７］から［９］のいずれか一項に記載の硬化性樹脂組成物の硬化物。
　本発明によれば、低誘電特性に優れる化合物、硬化性樹脂組成物、及びこれらの硬化物を提供することが可能である。
合成例１のＧＰＣチャートを示す。
　本発明の化合物は、スチレン系単量体からなる重合体のブロック単位（Ａ）と共役ジエン化合物からなる重合体のブロック単位（Ｂ）とからなるブロック共重合体の水素添加物（Ｈ－ＡＢ）の酸変性物である酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）とアリルアミンまたはアリルアミン塩酸塩とを反応させることにより得られる。
　スチレン系単量体からなる重合体のブロック単位（Ａ）は下記式（ａ）で表される構造が好ましい。
Figure JPOXMLDOC01-appb-C000009
　Ｒ１およびＲ２はそれぞれ水素原子または炭素数１～５のアルキル基であることが好ましく、水素原子または炭素数１～３のアルキル基であることがさらに好ましく、水素原子またはメチル基であることが特に好ましく、水素原子であることが最も好ましい。炭素数が５より大きい場合、分子振動により誘電正接が悪化するおそれがあるとともに、耐熱性が低下する恐れがある。ｐは１～５であることが好ましく、１～３であることがさらに好ましく、１であることが特に好ましい。ｑは繰り返し数の平均値であり、１～１００００の実数を表し、ｑは１～７５００であることが好ましく、１～５０００であることがより好ましく、１～３０００であることがさらに好ましい。
　共役ジエン化合物からなる重合体のブロック単位（Ｂ）は１，３－ブタジエン、イソプレン、ファルネセン、２，３－ジメチル－１，３－ブタジエン、１，３－ペンタジエン等の鎖状共役ジエンより選ばれる少なくとも１種以上のジエン化合物を重合させることによって得られる。原料の入手しやすさの観点から、鎖状共役ジエンの中でも、１，３－ブタジエン、イソプレン、ファルネセンが好ましく、１，３－ブタジエン、イソプレンがより好ましく、１，３－ブタジエンが最も好ましい。
　ブロック共重合体の水素添加物（Ｈ－ＡＢ）としては公知のいかなる材料を用いても良いが、下記式（１）で表される化合物であることが好ましい。
Figure JPOXMLDOC01-appb-C000010
 
　式（１）中、Ｒ１，Ｒ２，ｐの値および好ましい範囲は前記式（ａ）と同じである。ｊ，ｋ，ｌ，ｍ，ｎは繰り返し数の平均値であり、１～１００００の実数を表し、１～９０００であることが好ましく、１～８０００であることがさらに好ましい。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
　特に、下記式（１－１）で表される化合物であることが好ましい。
Figure JPOXMLDOC01-appb-C000011
　式（１－１）中、ｊ，ｋ，ｌ，ｍ，ｎの値及び好ましい範囲は前記式（１）と同じである。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
　ブロック共重合体の水素添加物（Ｈ－ＡＢ）として最も好ましい実施形態としては水添スチレン－ブタジエン－スチレンブロック共重合体（ＳＥＢＳ）を用いる場合である。
　前記式（１）で表される化合物は極性基を有さず、脂肪族炭化水素に由来する不飽和結合も有さないため、半導体動作保証温度である１２５℃以上に長期間晒されても酸化されにくく、極性基に含まれる酸素が骨格に取り込まれにくい。それ故に高温放置試験後の誘電特性悪化が低減でき、低吸水特性にも優れる。
　酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）としては公知のいかなる材料を用いても良いが、下記式（２）で表される化合物であることが好ましい。
Figure JPOXMLDOC01-appb-C000012
 
　式（２）中のＲ１，Ｒ２，ｐ，ｊ，ｋ，ｌ，ｍ，ｎの値及び好ましい範囲は前記式（１）と同じである。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
　特に、下記式（２－１）で表される化合物であることが好ましい。
Figure JPOXMLDOC01-appb-C000013
　式（２－１）中のｊ，ｋ，ｌ，ｍ，ｎの値及び好ましい範囲は前記式（１）と同じである。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
　酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）として最も好ましい実施形態としては酸変性水添スチレン－ブタジエン－スチレンブロック共重合体（ＳＥＢＳ）を用いる場合である。
　前記式（２）で表される化合物は前記式（１）で表される化合物をラジカル重合開始剤存在下で無水マレイン酸と反応させる、もしくは、前記式（１）で表される化合物をラジカル重合開始剤存在下でマレイン酸と反応させた後、脱水することにより得られる。
　前記式（２－１）で表される化合物は前記式（１－１）で表される化合物をラジカル重合開始剤存在下で無水マレイン酸と反応させる、もしくは、前記式（１－１）で表される化合物をラジカル重合開始剤存在下でマレイン酸と反応させた後、脱水することにより得られる。
　酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）中の、スチレン由来の構造単位の含有率（以下、スチレン含有率と略称することがある。）は、高周波特性（低誘電率、低誘電正接）、導体との接着性、耐熱性、ガラス転移温度及び熱膨張係数の観点から、５～８０質量％であってもよく、５～７０質量％であってもよく、１０～７０質量％であってもよく、１０～５０質量％であってもよい。酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）のメルトフローレート（ＭＦＲ）は、特に制限はないが、２３０℃、荷重２．１６ｋｇｆ（２１．２Ｎ）の測定条件では、０．１～２０ｇ／１０ｍｉｎであってもよく、０．５～１５ｇ／１０ｍｉｎであってもよい。
　酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）の市販品としては、例えば、旭化成株式会社製のタフテック（登録商標）Ｍシリーズ等が挙げられる。
　酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）とアリルアミンまたはアリルアミン塩酸塩とを反応させて得られる本発明の化合物として好ましい構造としては下記式（３）で表される。
Figure JPOXMLDOC01-appb-C000014
 
　式（３）中のＲ１，Ｒ２，ｐ，ｊ，ｋ，ｌ，ｍ，ｎの値及び好ましい範囲は前記式（１）と同じである。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
　特に、下記式（３－１）で表される化合物であることが好ましい。
Figure JPOXMLDOC01-appb-C000015
　式（３－１）中のｊ，ｋ，ｌ，ｍ，ｎの値及び好ましい範囲は前記式（１）と同じである。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
　本発明の化合物として最も好ましい実施形態としては酸変性水添スチレン－ブタジエン－スチレンブロック共重合体（ＳＥＢＳ）に由来する構造を有する化合物を用いる場合である。
　酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）とアリルアミンまたはアリルアミン塩酸塩との反応は、公知のいかなるイミド化反応法を用いても良いが、例えば、トルエン、キシレン、メシチレン等の非水溶性芳香族炭化水素系溶媒中、共沸により生成水を系内から除きながら、酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）に対し、アリルアミンまたはアリルアミン塩酸塩を反応させることによって行われる。イミド化触媒としてはトリエチルアミン等の塩基触媒または、活性白土、パラトルエンスルホン酸、メタンスルホン酸、塩酸等の酸触媒を用いても良い。アミック酸を溶解させ、イミド化行程を促進する目的でＮ－メチル－２－ピロリドンやＮ，Ｎ－ジメチルホルムアミドのような非プロトン性極性溶剤を併用しても良い。アリルアミンまたはアリルアミン塩酸塩は酸無水物構造１ｍоｌに対し０．５～１．５ｍоｌ用いることが好ましく、０．８～１．２ｍоｌ用いることがさらに好ましく、０．９～１．１ｍоｌ用いることが最も好ましい。上記範囲を外れた場合、残存する原料の極性基に由来し誘電特性が悪化するおそれがある。上記反応は８０～２００℃、好ましくは１００～１８０℃で０．５～２０時間反応を行う。
　本発明の化合物のゲルパーミエーションクロマトグラフィー（ＧＰＣ）の測定により求められる数平均分子量は、１０，０００以上１，０００，０００未満であることが好ましく、２０，０００以上、５００，０００未満であることがより好ましく、３０，０００以上２５０，０００未満であることがさらに好ましい。１０，０００未満の場合、はんだリフロー工程における耐熱性が損なわれるおそれがある。１，０００，０００以上の場合、溶剤溶解性が損なわれたり、他の熱硬化性樹脂成分と十分相溶しないおそれがある。
　本発明の硬化性樹脂組成物は、本発明の化合物の他に、以下に示す各種材料と混合して用いることができる。
［重合開始剤］
　本発明の硬化性樹脂組成物は、重合開始剤を添加することにより硬化性を向上させることもできる。重合開始剤とは、エチレン性不飽和結合等のオレフィン官能基を重合させることが可能な化合物であり、オレフィンメタセシス重合開始剤、アニオン重合開始剤、カチオン重合開始剤、ラジカル重合開始剤等が挙げられる。このなかでも硬化性および適度な安定性を有するラジカル重合開始剤を使用することが好ましい。ラジカル重合開始剤とは紫外線や可視光の照射または加熱によりラジカルを生じ、連鎖重合反応を開始させる化合物をいう。用い得るラジカル重合開始剤としては、有機過酸化物、アゾ系化合物、ベンゾピナコール類等が挙げられ、硬化温度制御やアウトガス抑制、分解物の電気特性への影響が少ないことから有機過酸化物を使用することが好ましい。
　上記有機過酸化物としては、例えば、メチルエチルケトンパーオキサイド、アセチルアセトンパーオキサイド等のケトンパーオキサイド類、過酸化ベンゾイル等のジアシルパーオキサイド類、ジクミルパーオキサイド、１，３－ビス－（ｔ－ブチルパーオキシイソプロピル）－ベンゼン等のジアルキルパーオキサイド類、ｔ－ブチルパーオキシベンゾエート、１，１－ジ－ｔ－ブチルパーオキシシクロヘキサン等のパーオキシケタール類、α－クミルパーオキシネオデカノエート、ｔ－ブチルパーオキシネオデカノエート、ｔ－ブチルペルオキシピバレート、１，１，３，３－テトラメチルブチルパーオキシ－２－エチルヘキサノエート、ｔ－アミルパーオキシ－２－エチルヘキサノエート、ｔ－ブチルパーオキシ－２－エチルヘキサノエート、ｔ－アミルパーオキシ－３，５，５－トリメチルヘキサノエート、ｔ－ブチルパーオキシ－３，５，５－トリメチルヘキサノエート、ｔ－アミルパーオキシベンゾエート等のアルキルパーエステル類、ジ－２－エチルヘキシルパーオキシジカーボネート、ビス（４－ｔ－ブチルシクロヘキシル）パーオキシジカーボネート、ｔ－ブチルパーオキシイソプロピルカーボネート、１，６－ビス（ｔ－ブチルパーオキシカルボニルオキシ）ヘキサン等のパーオキシカーボネート類、ｔ－ブチルハイドロパーオキサイド、クメンハイドロパーオキサイド、ｔ－ブチルパーオキシオクトエート、ラウロイルパーオキサイド等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。上記有機過酸化物の中でも、ケトンパーオキサイド類、ジアシルパーオキサイド類、ハイドロパーオキサイド類、ジアルキルパーオキサイド類、パーオキシケタール類、アルキルパーエステル類、パーカーボネート類等が好ましく、ジアルキルパーオキサイド類がより好ましい。
　上記アゾ系化合物としては、例えば、アゾビスイソブチロニトリル、４，４’－アゾビス（４－シアノ吉草酸）、２，２’－アゾビス（２，４－ジメチルバレロニトリル）、等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
　重合開始剤の添加量としては、硬化性樹脂組成物１００質量部中、０．０１～５質量部が好ましく、０．０１～３質量部が特に好ましい。用いる重合開始剤の量が０．０１質量部未満であると重合反応時に分子量が十分に伸長しない恐れがあり、５質量部より多いと誘電率、誘電正接等の誘電特性を損なう恐れがある。
［硬化促進剤］
　本発明の硬化性樹脂組成物は、硬化促進剤を添加することにより硬化性を向上させることもできる。硬化促進剤としては、紫外線や可視光の照射または加熱によりアニオンを発生することで硬化反応を促すアニオン系硬化促進剤、もしくは紫外線や可視光の照射または加熱によりカチオンを発生することで硬化反応を促すカチオン系硬化促進剤が好ましい。
　アニオン系硬化促進剤としては、例えば、２－メチルイミダゾール、２－エチルイミダゾール、２－エチル－４－メチルイミダゾール等のイミダゾール類、トリエチルアミン、トリブチルアミン等のトリアルキルアミン、４－ジメチルアミノピリジン、ベンジルジメチルアミン、２，４，６，－トリス（ジメチルアミノメチル）フェノール、１，８－ジアザビシクロ（５，４，０）－ウンデセン等が挙げられ、４－ジメチルアミノピリジン、１，８－ジアザビシクロ（５，４，０）－ウンデセンが好ましい。その他、トリフェニルホスフィン等のホスフィン類、テトラブチルアンモニウム塩、トリイソプロピルメチルアンモニウム塩、トリメチルデカニルアンモニウム塩、セチルトリメチルアンモニウム塩、ヘキサデシルトリメチルアンモニウムヒドロキシドなどの４級アンモニウム塩等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
　カチオン系硬化促進剤としては例えば、トリフェニルベンジルフォスフォニウム塩、トリフェニルエチルフォスフォニウム塩、テトラブチルフォスフォニウム塩などの４級フォスフォニウム塩（４級塩のカウンターイオンはハロゲン、有機酸イオン、水酸化物イオンなど、特に指定は無いが、特に有機酸イオン、水酸化物イオンが好ましい。）、オクチル酸スズ、カルボン酸亜鉛（２－エチルヘキサン酸亜鉛、ステアリン酸亜鉛、ベヘン酸亜鉛、ミリスチン酸亜鉛）、リン酸エステル亜鉛（オクチルリン酸亜鉛、ステアリルリン酸亜鉛）等の遷移金属化合物（遷移金属塩）等を挙げることができるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
　硬化促進剤の配合量は、硬化性樹脂組成物１００質量部中、０．０１～５．０質量部が必要に応じて用いられる。
［無機充填剤］
　本発明の硬化性樹脂組成物は、無機充填剤を含有しても良い。無機充填剤としては、例えば、溶融シリカ、結晶シリカ、多孔質シリカ、アルミナ、ジルコン、珪酸カルシウム、炭酸カルシウム、石英粉、炭化珪素、窒化珪素、窒化ホウ素、ジルコニア、窒化アルミニウム、グラファイト、フォルステライト、ステアタイト、スピネル、ムライト、チタニア、タルク、クレー、酸化鉄アスベスト、ガラス粉末等の粉体、またはこれらを球形状あるいは破砕状にした無機充填材等を挙げることができるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
　無機充填材を半導体封止用の硬化性樹脂組成物を得る場合の使用量は硬化性樹脂組成物１００質量部中、好ましくは８０～９２質量部であり、さらに好ましくは８３～９０質量部である。また、層間絶縁層形成材料、銅張積層板やプリプレグ、ＲＣＣ等の基板材料用の硬化性樹脂組成物を得る場合、上記の無機充填材の使用量は硬化性樹脂組成物１００質量部中、好ましくは５～８０質量部、さらに好ましくは１０～６０質量部である。
［重合禁止剤］
　本発明の硬化性樹脂組成物は、重合禁止剤を含有しても良い。重合禁止剤を含有することで保管安定性が向上するとともに、反応開始温度を制御することができる。反応開始温度を制御することで、流動性の確保が容易となり、ガラスクロスなどへの含浸性が損なわれない上に、プリプレグ化などＢステージ化が容易となる。プリプレグ化時に重合反応が進行しすぎると積層工程で積層が困難となるなどの不具合が発生しやすい。
　重合禁止剤は、本発明の化合物を合成するときに添加しても、合成後に添加してもよい。重合禁止剤の使用量は、本発明の化合物１００質量部中、０．００８～１重量部、好ましくは０．０１～０．５重量部である。
　重合禁止剤としては、例えば、フェノール系、イオウ系、リン系、ヒンダートアミン系、ニトロソ系、ニトロキシルラジカル系等が挙げられる。また、重合禁止剤は１種類で用いても、複数併用してもよい。これらのうち本発明では、フェノール系、ヒンダートアミン系、ニトロソ系、ニトロキシルラジカル系が好ましい。
　上記フェノール系重合禁止剤としては、例えば、２，６－ジ－ｔ－ブチル－ｐ－クレゾール、ブチル化ヒドロキシアニソール、２，６－ジ－ｔ－ブチル－ｐ－エチルフェノール、ステアリル－β－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート、イソオクチル－３－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート、２，４－ビス－（ｎ－オクチルチオ）－６－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルアニリノ）－１，３，５－トリアジン、２，４－ビス［（オクチルチオ）メチル］－ｏ－クレゾール等のモノフェノール類、２，２’－メチレンビス（４－メチル－６－ｔ－ブチルフェノール）、２，２’－メチレンビス（４－エチル－６－ｔ－ブチルフェノール）、４，４’－チオビス（３－メチル－６－ｔ－ブチルフェノール）、４，４’－ブチリデンビス（３－メチル－６－ｔ－ブチルフェノール）、トリエチレングリコール－ビス［３－（３－ｔ－ブチル－５－メチル－４－ヒドロキシフェニル）プロピオネート］、１，６－ヘキサンジオール－ビス［３－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、Ｎ，Ｎ’－ヘキサメチレンビス（３，５－ジ－ｔ－ブチル－４－ヒドロキシ－ヒドロシンナマミド）、２，２－チオ－ジエチレンビス［３－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジルフォスフォネート－ジエチルエステル、３，９－ビス［１，１－ジメチル－２－｛β－（３－ｔ－ブチル－４－ヒドロキシ－５－メチルフェニル）プロピオニルオキシ｝エチル］２，４，８，１０－テトラオキサスピロ［５，５］ウンデカン、ビス（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジルスルホン酸エチル）カルシウム等のビスフェノール類、１，１，３－トリス（２－メチル－４－ヒドロキシ－５－ｔ－ブチルフェニル）ブタン、１，３，５－トリメチル－２，４，６－トリス（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）ベンゼン、テトラキス－［メチレン－３－（３’，５’－ジ－ｔ－ブチル－４’－ヒドロキシフェニル）プロピオネート］メタン、ビス［３，３’－ビス－（４’－ヒドロキシ－３’－ｔ－ブチルフェニル）ブチリックアシッド］グリコールエステル、トリス－（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）－イソシアヌレイト、１，３，５－トリス（３’，５’－ジ－ｔ－ブチル－４’－ヒドロキシベンジル）－Ｓ－トリアジン－２，４，６－（１Ｈ，３Ｈ，５Ｈ）トリオン、トコフェノール等の高分子型フェノール類等が挙げられるが、これらに限定されるものではない。
　上記イオウ系重合禁止剤としては、例えば、ジラウリル－３，３’－チオジプロピオネート、ジミリスチル－３，３’－チオジプロピオネート、ジステアリル－３，３’－チオジプロピオネート等が挙げられるが、これらに限定されるものではない。
　上記リン系重合禁止剤としては、例えば、トリフェニルホスファイト、ジフェニルイソデシルホスファイト、フェニルジイソデシルホスファイト、トリス（ノニルフェニル）ホスファイト、ジイソデシルペンタエリスリトールホスファイト、トリス（２，４－ジ－ｔ－ブチルフェニル）ホスファイト、サイクリックネオペンタンテトライルビス（オクタデシル）ホスファイト、サイクリックネオペンタンテトライルビス（２，４－ジ－ｔ－ブチルフェニル）ホスファイト、サイクリックネオペンタンテトライルビス（２，４－ジ－ｔ－ブチル－４－メチルフェニル）ホスファイト、ビス［２－ｔ－ブチル－６－メチル－４－｛２－（オクタデシルオキシカルボニル）エチル｝フェニル］ヒドロゲンホスファイト等のホスファイト類、９，１０－ジヒドロ－９－オキサ－１０－ホスファフェナントレン－１０－オキサイド、１０－（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）－９，１０－ジヒドロ－９－オキサ－１０－ホスファフェナントレン－１０－オキサイド、１０－デシロキシ－９，１０－ジヒドロ－９－オキサ－１０－ホスファフェナントレン－１０－オキサイド等のオキサホスファフェナントレンオキサイド類等が挙げられるが、これらに限定されるものではない。
　上記ヒンダートアミン系重合禁止剤としては、例えば、アデカスタブＬＡ－４０ＭＰ、アデカスタブＬＡ－４０Ｓｉ、アデカスタブＬＡ－４０２ＡＦ、アデカスタブＬＡ－８７、アデカスタブＬＡ－８２、アデカスタブＬＡ－８１、アデカスタブＬＡ－７７Ｙ、アデカスタブＬＡ－７７Ｇ、アデカスタブＬＡ－７２、アデカスタブＬＡ－６８、アデカスタブＬＡ－６３Ｐ、アデカスタブＬＡ－５７、アデカスタブＬＡ－５２、Ｃｈｉｍａｓｓｏｒｂ２０２０ＦＤＬ、Ｃｈｉｍａｓｓｏｒｂ９４４ＦＤＬ、Ｃｈｉｍａｓｓｏｒｂ９４４ＬＤ、Ｔｉｎｕｖｉｎ６２２ＳＦ、ＴｉｎｕｖｉｎＰＡ１４４、Ｔｉｎｕｖｉｎ７６５、Ｔｉｎｕｖｉｎ７７０ＤＦ、ＴｉｎｕｖｉｎＸＴ５５ＦＢ、Ｔｉｎｕｖｉｎ１１１ＦＤＬ、Ｔｉｎｕｖｉｎ７８３ＦＤＬ、Ｔｉｎｕｖｉｎ７９１ＦＢ等が挙げられるが、これらに限定されるものではない。
　上記ニトロソ系重合禁止剤としては、例えば、ｐ－ニトロソフェノール、Ｎ－ニトロソジフェニルアミン、Ｎ－ニトロソフェニルヒドロキシアミンのアンモニウム塩（クペロン）等が挙げられるが、これらに限定されるものではない。これらのうち、好ましくは、Ｎ－ニトロソフェニルヒドロキシアミンのアンモニウム塩（クペロン）である。
　上記ニトロキシルラジカル系重合禁止剤としては、例えば、ジ－ｔｅｒｔ－ブチルニトロキサイド、２，２，６，６－テトラメチルピペリジン－１－オキシル、４－ヒドロキシ－２，２，６，６－テトラメチルピペリジン－１－オキシル、４－オキソ－２，２，６，６－テトラメチルピペリジン－１－オキシル、４－アミノ－２，２，６，６－テトラメチルピペリジン－１－オキシル、４－メトキシ－２，２，６，６－テトラメチルピペリジン－１－オキシル、４－アセトキシ－２，２，６，６－テトラメチルピペリジン－１－オキシル、４－ベンゾイルオキシ－２，２，６，６－テトラメチルピペリジン－１－オキシル等が挙げられるが、これらに限定されるものではない。
［難燃剤］
　本発明の硬化性樹脂組成物は、難燃剤を用いてもよい。難燃剤としては、例えば、ハロゲン系難燃剤、無機系難燃剤（アンチモン化合物、金属水酸化物、窒素化合物、ホウ素化合物等）、リン系難燃剤等が挙げられるが、ハロゲンフリー難燃性を達成する観点からリン系難燃剤が好ましい。
　上記リン系難燃剤としては反応型のものでも添加型のものでもよい。具体例としては、トリメチルホスフェート、トリエチルホスフェート、トリクレジルホスフェート、トリキシリレニルホスフェート、クレジルジフェニルホスフェート、クレジル－２，６－ジキシリレニルホスフェート、１，３－フェニレンビス（ジキシリレニルホスフェート）、１，４－フェニレンビス（ジキシリレニルホスフェート）、４，４’－ビフェニル（ジキシリレニルホスフェート）等のリン酸エステル類、９，１０－ジヒドロ－９－オキサ－１０－ホスファフェナントレン－１０－オキサイド、１０（２，５－ジヒドロキシフェニル）－１０Ｈ－９－オキサ－１０－ホスファフェナントレン－１０－オキサイド等のホスファン類のほか、エポキシ樹脂と前記ホスファン類の活性水素とを反応させて得られるリン含有エポキシ化合物、赤リン等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。上記例示物質のうち、リン酸エステル類、ホスファン類またはリン含有エポキシ化合物が好ましく、１，３－フェニレンビス（ジキシリレニルホスフェート）、１，４－フェニレンビス（ジキシリレニルホスフェート）、４，４’－ビフェニル（ジキシリレニルホスフェート）またはリン含有エポキシ化合物が特に好ましい。
　難燃剤の含有量は硬化性樹脂組成物１００質量部中、０．１～０．６質量部の範囲であることが好ましい。０．１質量部未満では難燃性が不十分となる恐れがあり、０．６質量部より多いと硬化物の吸湿性、誘電特性に悪影響を及ぼす恐れがある。
［光安定剤］
　本発明の硬化性樹脂組成物は、光安定剤を用いてもよい。光安定剤としては、ヒンダートアミン系の光安定剤、特にＨＡＬＳ等が好適である。ＨＡＬＳとしては、例えば、ジブチルアミン・１，３，５－トリアジン・Ｎ，Ｎ’－ビス（２，２，６，６－テトラメチル－４－ピペリジル－１，６－ヘキサメチレンジアミンとＮ－（２，２，６，６－テトラメチル－４－ピペリジル）ブチルアミンの反応物、コハク酸ジメチル－１－（２－ヒドロキシエチル）－４－ヒドロキシ－２，２，６，６－テトラメチルピペリジン反応物、ポリ〔｛６－（１，１，３，３－テトラメチルブチル）アミノ－１，３，５－トリアジン－２，４－ジイル｝｛（２，２，６，６－テトラメチル－４－ピペリジル）イミノ｝ヘキサメチレン｛（２，２，６，６－テトラメチル－４－ピペリジル）イミノ｝〕、ビス（１，２，２，６，６－ペンタメチル－４－ピペリジル）〔〔３，５－ビス（１，１－ジメチルエチル）－４－ヒドロキシフェニル〕メチル〕ブチルマロネート、ビス（２，２，６，６－テトラメチル－４－ピペリジル）セバケート、ビス（１，２，２，６，６－ペンタメチル－４－ピペリジル）セバケート、ビス（１－オクチロキシ－２，２，６，６－テトラメチル－４－ピペリジル）セバケート、２－（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）－２－ｎ－ブチルマロン酸ビス（１，２，２，６，６－ペンタメチル－４－ピペリジル）等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
　光安定剤の含有量は硬化性樹脂組成物１００質量部中、０．００１～０．１質量部の範囲であることが好ましい。０．００１質量部未満では光安定効果を発現するのに不十分となる恐れがあり、０．１質量部より多いと硬化物の吸湿性、誘電特性に悪影響を及ぼす恐れがある。
［バインダー樹脂］
　本発明の硬化性樹脂組成物は、バインダー樹脂を用いてもよい。バインダー樹脂としては、例えば、ブチラール系樹脂、アセタール系樹脂、アクリル系樹脂、エポキシ－ナイロン系樹脂、ＮＢＲ－フェノール系樹脂、エポキシ－ＮＢＲ系樹脂、シリコーン系樹脂等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
　バインダー樹脂の配合量は、硬化物の難燃性、耐熱性を損なわない範囲であることが好ましく、硬化性樹脂組成物１００質量部中、０．０５～５０質量部であることが好ましく、さらに好ましくは０．０５～２０質量部が必要に応じて用いられる。
［添加剤］
　本発明の硬化性樹脂組成物は、添加剤を用いてもよい。添加剤としては、例えば、アクリロニトリル共重合体の変性物、ポリエチレン、フッ素樹脂、シリコーンゲル、シリコーンオイル、シランカップリング剤のような充填材の表面処理剤、離型剤、カーボンブラック、フタロシアニンブルー、フタロシアニングリーン等の着色剤が挙げられる。
　添加剤の配合量は、硬化性樹脂組成物１００質量部に対して好ましくは１質量部以下、より好ましくは０．７質量部以下の範囲である。
　本発明の硬化性樹脂組成物は、さらに、エポキシ樹脂、活性エステル化合物、フェノール樹脂、ポリフェニレンエーテル化合物、アミン樹脂、エチレン性不飽和結合を有する化合物、イソシアネート樹脂、ポリアミド樹脂、マレイミド化合物、シアネートエステル樹脂、ポリイミド樹脂、ポリブタジエンおよびこの変性物、ポリスチレンおよびこの変性物、ポリエチレンおよびこの変性物等を用いてもよく、これらは１種類で用いても、複数併用してもよい。これらの化合物のうち、耐熱性、密着性、誘電特性のバランスから、マレイミド化合物、ポリフェニレンエーテル化合物、エチレン性不飽和結合を有する化合物、シアネートエステル樹脂、ポリブタジエンおよびこの変性物、ポリスチレンおよびこの変性物、ポリエチレンおよびこの変性物を含有することが好ましい。これらの化合物を含有することによって、硬化物の脆さの改善および金属への密着性を向上でき、はんだリフロー時や冷熱サイクルなどの信頼性試験におけるパッケージのクラックを抑制できる。上記化合物の総使用量は、特に断りがない場合、本発明の化合物に対して、好ましくは１０質量倍以下、さらに好ましくは５質量倍以下、特に好ましくは３質量倍以下の質量範囲である。また、好ましい下限値は０．１質量倍以上、より好ましくは０．２５質量倍以上、更に好ましくは０．５質量倍以上である。上記範囲内であることにより、本発明の化合物の低誘電特性の効果を活かしつつ、添加する各化合物の効果を付加することができる。これらの成分については、以下に例示するものを使用することができる。
［エポキシ樹脂］
　エポキシ樹脂として好ましいものを以下に例示するがこれらに限定されるものではない。なお、エポキシ樹脂の性状は液状であっても固形であってもよく、１種類で用いても、複数併用してもよい。
　液状エポキシ樹脂としては、例えば、ビスフェノールＡ型エポキシ樹脂、ビスフェノールＦ型エポキシ樹脂、ビスフェノールＡＦ型エポキシ樹脂、ナフタレン型エポキシ樹脂、グリシジルエステル型エポキシ樹脂、グリシジルアミン型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、エステル骨格を有する脂環式エポキシ樹脂、シクロヘキサン型エポキシ樹脂、シクロヘキサンジメタノール型エポキシ樹脂、グリシジルアミン型エポキシ樹脂、及びブタジエン構造を有するエポキシ樹脂等を挙げることができる。具体例としては、「ＲＥ３１０Ｓ」、「ＲＥ４１０Ｓ」（以上、日本化薬社製、ビスフェノールＡ型エポキシ樹脂）、「ＲＥ３０３Ｓ」、「ＲＥ３０４Ｓ」、「ＲＥ４０３Ｓ」、「ＲＥ４０４Ｓ」（以上、日本化薬社製、ビスフェノールＦ型エポキシ樹脂）、「ＨＰ４０３２」、「ＨＰ４０３２Ｄ」、「ＨＰ４０３２ＳＳ」（以上、ＤＩＣ社製、ナフタレン型エポキシ樹脂）、「８２８ＵＳ」、「ｊＥＲ８２８ＥＬ」、「８２５」、「８２８ＥＬ」（以上、三菱ケミカル社製、ビスフェノールＡ型エポキシ樹脂）、「ｊＥ８０７」、「１７５０」（以上、三菱ケミカル社製、ビスフェノールＦ型エポキシ樹脂）、「ｊＥＲ１５２」（三菱ケミカル社製、フェノールノボラック型エポキシ樹脂）、「６３０」、「６３０ＬＳＤ」（以上、三菱ケミカル社製、グリシジルアミン型エポキシ樹脂）、「ＺＸ１０５９」（新日鉄住金化学社製、ビスフェノールＡ型エポキシ樹脂とビスフェノールＦ型エポキシ樹脂の混合品）、「ＥＸ－７２１」（ナガセケムテックス社製、グリシジルエステル型エポキシ樹脂）、「セロキサイド２０２１Ｐ」（ダイセル社製、エステル骨格を有する脂環式エポキシ樹脂）、「ＰＢ－３６００」（ダイセル社製、ブタジエン構造を有するエポキシ樹脂）、「ＺＸ１６５８」、「ＺＸ１６５８ＧＳ」（以上、新日鉄住金化学社製、液状１，４－グリシジルシクロヘキサン型エポキシ樹脂）等が挙げられる。これらは１種単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　固形エポキシ樹脂としては、例えば、ビキシレノール型エポキシ樹脂、ナフタレン型エポキシ樹脂、ナフタレン型４官能エポキシ樹脂、クレゾールノボラック型エポキシ樹脂、ジシクロペンタジエン型エポキシ樹脂、トリスフェノール型エポキシ樹脂、ナフトール型エポキシ樹脂、ビフェニル型エポキシ樹脂、ナフチレンエーテル型エポキシ樹脂、アントラセン型エポキシ樹脂、ビスフェノールＡ型エポキシ樹脂、ビスフェノールＡＦ型エポキシ樹脂、テトラフェニルエタン型エポキシ樹脂が好ましく、ナフトール型エポキシ樹脂、ビスフェノールＡＦ型エポキシ樹脂、ナフタレン型エポキシ樹脂、及びビフェニル型エポキシ樹脂を挙げることができる。具体例としては、「ＨＰ４０３２Ｈ」（ＤＩＣ社製、ナフタレン型エポキシ樹脂）、「ＨＰ－４７００」、「ＨＰ－４７１０」（以上、ＤＩＣ社製、ナフタレン型４官能エポキシ樹脂）、「Ｎ－６９０」（ＤＩＣ社製、クレゾールノボラック型エポキシ樹脂）、「Ｎ－６９５」（ＤＩＣ社製、クレゾールノボラック型エポキシ樹脂）、「ＨＰ－７２００」（ＤＩＣ社製、ジシクロペンタジエン型エポキシ樹脂）、「ＨＰ－７２００」、「ＨＰ－７２００ＨＨ」、「ＨＰ－７２００Ｈ」（以上、ＤＩＣ社製、ジシクロペンタジエン型エポキシ樹脂）、「ＥＸＡ－７３１１」、「ＥＸＡ－７３１１－Ｇ３」、「ＥＸＡ－７３１１－Ｇ４」、「ＥＸＡ－７３１１－Ｇ４Ｓ」、「ＨＰ－６０００」（以上、ＤＩＣ社製、ナフチレンエーテル型エポキシ樹脂）、「ＥＰＰＮ－５０２Ｈ」（日本化薬社製、トリスフェノール型エポキシ樹脂）、「ＮＣ－７０００Ｌ」、「ＮＣ－７３００」（以上、日本化薬社製、ナフトール－クレゾールノボラック型エポキシ樹脂）、「ＮＣ－３０００Ｈ」、「ＮＣ－３０００」、「ＮＣ－３０００Ｌ」、「ＮＣ－３１００」（以上、日本化薬社製、ビフェニルアラルキル型エポキシ樹脂）、「ＸＤ－１０００－２Ｌ」、「ＸＤ－１０００－Ｌ」、「ＸＤ－１０００－Ｈ」、「ＸＤ－１０００－Ｈ」（以上、日本化薬社製、ジシクロペンタジエン型エポキシ樹脂）、「ＥＳＮ４７５Ｖ」（新日鉄住金化学社製、ナフトール型エポキシ樹脂）、「ＥＳＮ４８５」（新日鉄住金化学社製、ナフトールノボラック型エポキシ樹脂）、「ＹＸ－４０００Ｈ」、「ＹＸ－４０００」、「ＹＬ６１２１」（以上、三菱ケミカル社製、ビフェニル型エポキシ樹脂）、「ＹＸ－４０００ＨＫ」（三菱ケミカル社製、ビキシレノール型エポキシ樹脂）、「ＹＸ－８８００」（三菱ケミカル社製、アントラセン型エポキシ樹脂）、「ＰＧ－１００」、「ＣＧ－５００」（大阪ガスケミカル社製、フルオレン系エポキシ樹脂）、「ＹＬ－７７６０」（三菱ケミカル社製、ビスフェノールＡＦ型エポキシ樹脂）、「ＹＬ－７８００」（三菱ケミカル社製、フルオレン型エポキシ樹脂）「ｊＥＲ１０１０」（三菱ケミカル社製、固体状ビスフェノールＡ型エポキシ樹脂）、「ｊＥＲ１０３１Ｓ」（三菱ケミカル社製、テトラフェニルエタン型エポキシ樹脂）等が挙げられる。これらは１種単独で用いてもよく、２種以上を組み合わせて用いてもよい。
［活性エステル化合物］
　活性エステル化合物とは、構造体中にエステル結合を少なくとも１つ含み、かつ、エステル結合の両側に脂肪族鎖、脂肪族環又は芳香族環が結合している化合物をいう。活性エステル化合物としては、例えば、フェノールエステル類、チオフェノールエステル類、Ｎ－ヒドロキシアミンエステル類、複素環ヒドロキシ化合物のエステル類等の反応活性の高いエステル基を１分子中に２個以上有する化合物を挙げることができ、カルボン酸化合物、酸塩化物、またはチオカルボン酸化合物の少なくともいずれかの化合物と、ヒドロキシ化合物またはチオール化合物の少なくともいずれかの化合物との縮合反応によって得られる。特に、耐熱性向上の観点から、カルボン酸化合物または酸塩化物とヒドロキシ化合物から得られるときが好ましく、ヒドロキシ化合物としてはフェノール化合物またはナフトール化合物が好ましい。活性エステル化合物は１種単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　上記カルボン酸化合物としては、例えば、安息香酸、酢酸、コハク酸、マレイン酸、イタコン酸、フタル酸、イソフタル酸、テレフタル酸、ピロメリット酸等が挙げられる。
　上記酸塩化物としては、例えば、アセチルクロリド、アクリル酸クロリド、メタクリル酸クロリド、マロニルクロリド、こはく酸ジクロリド、ジグリコリルクロリド、グルタル酸ジクロリド、スベリン酸ジクロリド、セバシン酸ジクロリド、アジピン酸ジクロリド、ドデカンジオイルジクロリド、アゼラオイルクロリド、２，５－フランジカルボニルジクロリド、フタロイルクロリド、イソフタロイルクロリド、テレフタロイルクロリド、トリメシン酸クロリド、ビス（４－クロロカルボニルフェニル）エーテル、４，４’－ジフェニルジカルボニルクロリド、４，４’－アゾジベンゾイルジクロリド等が挙げられる。
　上記フェノール化合物及び上記ナフトール化合物としては、例えば、ハイドロキノン、レゾルシン、ビスフェノールＡ、ビスフェノールＦ、ビスフェノールＳ、フェノールフタリン、メチル化ビスフェノールＡ、メチル化ビスフェノールＦ、メチル化ビスフェノールＳ、フェノール、ｏ－クレゾール、ｍ－クレゾール、ｐ－クレゾール、カテコール、α－ナフトール、β－ナフトール、１，５－ジヒドロキシナフタレン、１，６－ジヒドロキシナフタレン、２，６－ジヒドロキシナフタレン、ジヒドロキシベンゾフェノン、トリヒドロキシベンゾフェノン、テトラヒドロキシベンゾフェノン、フロログルシン、ベンゼントリオール、ジシクロペンタジエン型ジフェノール化合物、フェノールノボラック、後述するフェノール樹脂等が挙げられる。ここで、「ジシクロペンタジエン型ジフェノール化合物」とは、ジシクロペンタジエン１分子にフェノール２分子が縮合して得られるジフェノール化合物をいう。
　活性エステル化合物の好ましい具体例としては、ジシクロペンタジエン型ジフェノール構造を含む活性エステル化合物、ナフタレン構造を含む活性エステル化合物、フェノールノボラックのアセチル化物を含む活性エステル化合物、フェノールノボラックのベンゾイル化物を含む活性エステル化合物、国際公開第２０２０／０９５８２９号実施例２に記載の化合物、国際公開第２０２０／０５９６２５号にて開示されている化合物等が挙げられる。中でも、ナフタレン構造を含む活性エステル化合物、ジシクロペンタジエン型ジフェノール構造を含む活性エステル化合物がより好ましい。ジシクロペンタジエン型ジフェノール構造とは、フェニレン－ジシクロペンチレン－フェニレンからなる２価の構造単位を表す。
　活性エステル化合物の市販品としては、例えば、ジシクロペンタジエン型ジフェノール構造を含む活性エステル化合物として、「ＥＸＢ９４５１」、「ＥＸＢ９４６０」、「ＥＸＢ９４６０Ｓ」、「ＨＰＣ－８０００－６５Ｔ」、「ＨＰＣ－８０００Ｈ－６５ＴＭ」、「ＥＸＢ－８０００Ｌ－６５ＴＭ」、「ＥＸＢ－８１５０－６５Ｔ」（ＤＩＣ社製）、ナフタレン構造を含む活性エステル化合物として「ＥＸＢ９４１６－７０ＢＫ」（ＤＩＣ社製）、フェノールノボラックのアセチル化物を含む活性エステル化合物として「ＤＣ８０８」（三菱化学社製）、フェノールノボラックのベンゾイル化物を含む活性エステル化合物として「ＹＬＨ１０２６」、「ＹＬＨ１０３０」、「ＹＬＨ１０４８」（三菱化学社製）、フェノールノボラックのアセチル化物である活性エステル系硬化剤として「ＤＣ８０８」（三菱化学社製）、リン原子含有活性エステル系硬化剤としてＤＩＣ社製の「ＥＸＢ－９０５０Ｌ－６２Ｍ」等が挙げられる。
　活性エステル化合物およびエポキシ樹脂の配合比に関しては、活性エステル当量（α）とエポキシ当量（β）の比率（α／β）が０．５～１．５であることが好ましく、より好ましくは０．８～１．２、さらに好ましくは、０．９０～１．１０である。上記範囲を外れる場合、過剰となったエポキシ基もしくは活性エステル基が系中に残存するおそれがあり、高温放置試験（１５０℃、１０００時間など）や高温高湿条件下（温度：８５℃、湿度：８５％など）での長期信頼性試験等で特性が悪化するおそれがある。
［フェノール樹脂］
　フェノール樹脂とは、分子内に２つ以上フェノール性水酸基を有する化合物である。フェノール樹脂としては、例えば、フェノール類とアルデヒド類との反応物、フェノール類とジエン化合物との反応物、フェノール類とケトン類との反応物、フェノール類と置換ビフェニル類との反応物、フェノール類と置換フェニル類との反応物、ビスフェノール類とアルデヒド類との反応物等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
　上記各原料の具体例を以下に例示するが、これらに限定されるものではない。
＜フェノール類＞
　フェノール、アルキル置換フェノール、芳香族置換フェノール、ハイドロキノン、レゾルシン、ナフトール、アルキル置換ナフトール、ジヒドロキシベンゼン、アルキル置換ジヒドロキシベンゼン、ジヒドロキシナフタレン等。
＜アルデヒド類＞
　ホルムアルデヒド、アセトアルデヒド、アルキルアルデヒド、ベンズアルデヒド、アルキル置換ベンズアルデヒド、ヒドロキシベンズアルデヒド、ナフトアルデヒド、グルタルアルデヒド、フタルアルデヒド、クロトンアルデヒド、シンナムアルデヒド、フルフラール等。
＜ジエン化合物＞
　ジシクロペンタジエン、テルペン類、ビニルシクロヘキセン、ノルボルナジエン、ビニルノルボルネン、テトラヒドロインデン、ジビニルベンゼン、ジビニルビフェニル、ジイソプロペニルビフェニル、ブタジエン、イソプレン等。
＜ケトン類＞
　アセトン、メチルエチルケトン、メチルイソブチルケトン、アセトフェノン、ベンゾフェノン、フルオレノン等。
＜置換ビフェニル類＞
　４，４’－ビス（クロロメチル）－１，１’－ビフェニル、４，４’－ビス（メトキシメチル）－１，１’－ビフェニル、４，４’－ビス（ヒドロキシメチル）－１，１’－ビフェニル等。
＜置換フェニル類＞
　１，４－ビス（クロロメチル）ベンゼン、１，４－ビス（メトキシメチル）ベンゼン、１，４－ビス（ヒドロキシメチル）ベンゼン等。
［ポリフェニレンエーテル化合物］
　ポリフェニレンエーテル化合物としては、耐熱性と電気特性の観点から、エチレン性不飽和結合を有するポリフェニレンエーテル化合物であることが好ましく、アクリル基、メタクリル基、又はスチレン構造を有するポリフェニレンエーテル化合物であることがさらに好ましい。市販品としては、ＳＡ－９０００（ＳＡＢＩＣ社製、メタクリル基を有するポリフェニレンエーテル化合物）やＯＰＥ－２Ｓｔ　１２００（三菱瓦斯化学社製、スチレン構造を有するポリフェニレンエーテル化合物）などが挙げられる。
　ポリフェニレンエーテル化合物の数平均分子量（Ｍｎ）は、５００～５０００であることが好ましく、２０００～５０００であることがより好ましく、２０００～４０００であることがより好ましい。分子量が５００未満であると、硬化物の耐熱性としては充分なものが得られない傾向がある。また、分子量が５０００より大きいと、溶融粘度が高くなり、充分な流動性が得られないため、成形不良となりやすくなる傾向がある。また、反応性も低下して、硬化反応に長い時間を要し、硬化系に取り込まれずに未反応のものが増加して、硬化物のガラス転移温度が低下し、硬化物の耐熱性が低下する傾向がある。
　ポリフェニレンエーテル化合物の数平均分子量が５００～５０００であれば、優れた誘電特性を維持したまま、優れた耐熱性及び成形性等を発現させることができる。なお、ここでの数平均分子量は、具体的には、ゲルパーミエーションクロマトグラフィー等を用いて測定することができる。
　ポリフェニレンエーテル化合物は、重合反応により得られたものであっても、数平均分子量１００００～３００００程度の高分子量のポリフェニレンエーテル化合物を再分配反応させて得られたものであってもよい。また、これらを原料として、メタクリルクロリド、アクリルクロリド、クロロメチルスチレン等、エチレン性不飽和結合を有する化合物と反応させることでラジカル重合性を付与してもよい。再分配反応によって得られたポリフェニレンエーテル化合物は、例えば、高分子量のポリフェニレンエーテル化合物をトルエン等の溶媒中で、フェノール化合物とラジカル開始剤との存在下で加熱し再分配反応させて得られる。このように再分配反応により得られるポリフェニレンエーテル化合物は、分子鎖の両末端に硬化に寄与するフェノール系化合物に由来する水酸基を有するために、さらに高い耐熱性を維持することができることに加え、エチレン性不飽和結合を有する化合物で変性した後も分子鎖の両末端に官能基を導入できる点から好ましい。また、重合反応により得られたポリフェニレンエーテル化合物は、優れた流動性を示す点から好ましい。
　ポリフェニレンエーテル化合物の分子量の調整は、重合反応により得られたポリフェニレンエーテル化合物の場合、重合条件等を調整することにより行うことができる。また、再分配反応によって得られたポリフェニレンエーテル化合物の場合は、再分配反応の条件等を調整することにより、得られるポリフェニレンエーテル化合物の分子量を調整することができる。より具体的には、再分配反応において用いるフェノール系化合物の配合量を調整すること等が考えられる。すなわち、フェノール系化合物の配合量が多いほど、得られるポリフェニレンエーテル化合物の分子量が低くなる。この際、再分配反応を受ける高分子量のポリフェニレンエーテル化合物としては、ポリ（２，６－ジメチル－１，４－フェニレンエーテル）等を用いることができる。また、前記再分配反応に用いられるフェノール系化合物としては、特に限定されないが、例えば、ビスフェノールＡ、フェノールノボラック、クレゾールノボラック等のように、フェノール性水酸基を分子中に２個以上有する多官能のフェノール系化合物が好ましく用いられる。これらは、単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
［アミン樹脂］
　アミン樹脂とは、分子内に２つ以上アミノ基を有する化合物である。アミン樹脂としては、例えば、ジアミノジフェニルメタン、ジアミノジフェニルスルホン、イソホロンジアミン、ナフタレンジアミン、アニリンノボラック（アニリンとホルマリンの反応物）、Ｎ－メチルアニリンノボラック（Ｎ－メチルアニリンとホルマリンの反応物）、オルソエチルアニリンノボラック（オルソエチルアニリンとホルマリンの反応物）、２－メチルアニリンとホルマリンの反応物、２，６－ジイソプロピルアニリンとホルマリンの反応物、２，６－ジエチルアニリンとホルマリンの反応物、２－エチル－６－エチルアニリンとホルマリンの反応物、２，６－ジメチルアニリンとホルマリンの反応物、アニリンとキシリレンクロライドとの反応により得られるアニリン樹脂、日本国特許第６４２９８６２号公報に記載のアニリンと置換ビフェニル類（４，４’－ビス（クロロメチル）－１，１’－ビフェニル及び４，４’－ビス（メトキシメチル）－１，１’－ビフェニル等）の反応物、アニリンと置換フェニル類（１，４－ビス（クロロメチル）ベンゼン、１，４－ビス（メトキシメチル）ベンゼン及び１，４－ビス（ヒドロキシメチル）ベンゼン等）の反応物、４，４’－（１，３－フェニレンジイソプロピリデン）ビスアニリン、４，４’－（１，４－フェニレンジイソプロピリデン）ビスアニリン、アニリンとジイソプロペニルベンゼンの反応物、ダイマージアミン等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
［エチレン性不飽和結合を含有する化合物］
　エチレン性不飽和結合を含有する化合物とは、重合開始剤の使用・不使用を問わず、熱もしくは光により重合可能なエチレン性不飽和結合を分子内に１つ以上有する化合物である。
　エチレン性不飽和結合を含有する化合物としては、例えば、前記のフェノール樹脂とエチレン性不飽和結合含有のハロゲン系化合物（クロロメチルスチレン、アリルクロライド、メタリルクロライド、アクリル酸クロリド、メタクリル酸クロリド等）の反応物、エチレン性不飽和結合含有フェノール類（２－アリルフェノール、２－プロペニルフェノール、４－アリルフェノール、４－プロペニルフェノール、オイゲノール、イソオイゲノール等）とハロゲン系化合物（１，４－ビス（クロロメチル）ベンゼン、４，４’－ビス（クロロメチル）ビフェニル、４，４’－ジフルオロベンゾフェノン、４，４’－ジクロロベンゾフェノン、４，４’－ジブロモベンゾフェノン、塩化シアヌル等）の反応物、エポキシ樹脂若しくはアルコール類と（メタ）アクリル酸類（アクリル酸、メタクリル酸等）の反応物及びこれらの酸変性化物等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
［イソシアネート樹脂］
　イソシアネート樹脂とは、分子内に２つ以上イソシアネート基を有する化合物である。イソシアネート樹脂としては、例えば、ｐ－フェニレンジイソシアネート、ｍ－フェニレンジイソシアネート、ｐ－キシレンジイソシアネート、ｍ－キシレンジイソシアネート、２，４－トリレンジイソシアネート、２，６－トリレンジイソシアネート、４，４’－ジフェニルメタンジイソシアネート、ナフタレンジイソシアネート等の芳香族ジイソシアネート類、イソホロンジイソシアネート、ヘキサメチレンジイソシアネート、４，４’－ジシクロヘキシルメタンジイソシアネート、水添キシレンジイソシアネート、ノルボルネンジイソシアネート、リジンジイソシアネート等の脂肪族又は脂環構造のジイソシアネート類、イソシアネートモノマーの一種類以上のビュレット体、又は上記ジイソシアネート化合物を３量化したイソシアネート体等のポリイソシアネート、上記イソシアネート化合物とポリオール化合物とのウレタン化反応によって得られるポリイソシアネート等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
［ポリアミド樹脂］
　ポリアミド樹脂としては、例えば、ジアミン、ジイソシアネート、オキサゾリンのいずれか１種以上とジカルボン酸の反応物、ジアミンと酸塩化物の反応物、ラクタム化合物の開環重合物が挙げられる。また、これらは１種類で用いても、複数併用してもよい。
　上記各原料の具体例を以下に例示するが、これらに限定されるものではない。
＜ジアミン＞
　エチレンジアミン、トリメチレンジアミン、テトラメチレンジアミン、ペンタメチレンジアミン、ヘキサメチレンジアミン、ヘプタメチレンジアミン、オクタメチレンジアミン、ノナメチレンジアミン、デカンジアミン、ウンデカンジアミン、ドデカンジアミン、トリデカンジアミン、テトラデカンジアミン、ペンタデカンジアミン、ヘキサデカンジアミン、ヘプタデカンジアミン、オクタデカンジアミン、ノナデカンジアミン、エイコサンジアミン、２－メチル－１，５－ジアミノペンタン、２－メチル－１，８－ジアミノオクタン、ダイマージアミン、シクロヘキサンジアミン、ビス－（４－アミノシクロヘキシル）メタン、ビス（３－メチル－４－アミノシクロヘキシル）メタン、キシリレンジアミン、ノルボルナンジアミン、イソホロンジアミン、ビスアミノメチルトリシクロデカン、フェニレンジアミン、ジエチルトルエンジアミン、ナフタレンジアミン、ジアミノジフェニルメタン、ビス（４－アミノ－３，５－ジメチルフェニル）メタンビス（４－アミノ－３，５－ジエチルフェニル）メタン、４，４'－メチレンビス－о－トルイジン、４，４'－メチレンビス－о－エチルアニリン、４，４'－メチレンビス－２－エチル－６－メチルアニリン、４，４'－メチレンビス－２，６－ジイソプロピルアニリン、４，４－エチレンジアニリン、ジアミノジフェニルスルホン、ジアミノジフェニルエーテル、１，３－ビス（３－アミノフェノキシ）ベンゼン、１，３－ビス（４－アミノフェノキシ）ベンゼン、４，４－ビス（４－アミノフェノキシ）ビフェニル、２，２－ビス［４－（４－アミノフェノキシ）フェニル］プロパン、ビス［４－（４－アミノフェノキシ）フェニル］スルホン、２，２－ビス（３－アミノ－４－ヒドロキシフェニル）プロパン、２，２－ビス（４－アミノフェニル）ヘキサフルオロプロパン、４，４'－（１，３－フェニレンジイソプロピリデン）ビスアニリン、４，４'－（１，４－フェニレンジイソプロピリデン）ビスアニリン、９，９－ビス（４－アミノフェニル）フルオレン、２，７－ジアミノフルオレン、アミノベンジルアミン、ジアミノベンゾフェノン等。
＜ジイソシアネート＞
　ベンゼンジイソシアネート、トルエンジイソシアネート、１，３－ビス（イソシアナトメチル）ベンゼン、１，３－ビス（イソシアナトメチル）シクロヘキサン、ビス（４－イソシアナトフェニル）メタン、イソホロンジイソシアネート、１，３－ビス（２－イソシアナト－２－プロピル）ベンゼン、２，２－ビス（４－イソシアナトフェニル）ヘキサフルオロプロパン、ジシクロヘキシルメタン－４，４'－ジイソシアナート等。
＜ジカルボン酸＞
　シュウ酸、マロン酸、スクシン酸、グルタル酸、アジピン酸、スベリン酸、アゼライン酸、セバシン酸、ウンデカン二酸、ドデカン二酸、テレフタル酸、イソフタル酸、５－ヒドロキシイソフタル酸、２－クロロテレフタル酸、２－メチルテレフタル酸、５－メチルイソフタル酸、５－ナトリウムスルホイソフタル酸、ヘキサヒドロテレフタル酸、ヘキサヒドロイソフタル酸、シクロヘキサンジカルボン酸、ビフェニルジカルボン酸、ナフタレンジカルボン酸、ベンゾフェノンジカルボン酸、フランジカルボン酸、４，４'－ジカルボキシジフェニルエーテル、４，４'－ジカルボキシジフェニルスルフィド等。
＜酸塩化物＞
　アセチルクロリド、アクリル酸クロリド、メタクリル酸クロリド、マロニルクロリド、こはく酸ジクロリド、ジグリコリルクロリド、グルタル酸ジクロリド、スベリン酸ジクロリド、セバシン酸ジクロリド、アジピン酸ジクロリド、ドデカンジオイルジクロリド、アゼラオイルクロリド、２，５－フランジカルボニルジクロリド、フタロイルクロリド、イソフタロイルクロリド、テレフタロイルクロリド、トリメシン酸クロリド、ビス（４－クロロカルボニルフェニル）エーテル、４，４’－ジフェニルジカルボニルクロリド、４，４’－アゾジベンゾイルジクロリド等。
＜ラクタム＞
　ε－カプロラクタム、ω－ウンデカンラクタム、ω－ラウロラクタム等。
［ポリイミド樹脂］
　ポリイミド樹脂としては、例えば、前記ジアミンと以下に例示するテトラカルボン酸二無水物の反応物が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
＜テトラカルボン酸二無水物＞
　４，４’－（ヘキサフルオロイソプロピリデン）ジフタル酸無水物、５－（２，５－ジオキソテトラヒドロ－３－フラニル）－３－メチル－シクロヘキセン－１，２ジカルボン酸無水物、ピロメリット酸二無水物、１，２，３，４－ベンゼンテトラカルボン酸二無水物、３，３’，４，４’－ベンゾフェノンテトラカルボン酸二無水物、２，２’，３，３’－ベンゾフェノンテトラカルボン酸二無水物、３，３’，４，４’－ビフェニルテトラカルボン酸二無水物、３，３’，４，４’－ジフェニルスルホンテトラカルボン酸二無水物、２，２’，３，３’－ビフェニルテトラカルボン酸二無水物、メチレン－４，４’－ジフタル酸二無水物、１，１－エチリデン－４，４’－ジフタル酸二無水物、２，２’－プロピリデン－４，４’－ジフタル酸二無水物、１，２－エチレン－４，４’－ジフタル酸二無水物、１，３－トリメチレン－４，４’－ジフタル酸二無水物、１，４－テトラメチレン－４，４’－ジフタル酸二無水物、１，５－ペンタメチレン－４，４’－ジフタル酸二無水物、４，４’－オキシジフタル酸二無水物、チオ－４，４’－ジフタル酸二無水物、スルホニル－４，４’－ジフタル酸二無水物、１，３－ビス（３，４－ジカルボキシフェニル）ベンゼン二無水物、１，３－ビス（３，４－ジカルボキシフェノキシ）ベンゼン二無水物、１，４－ビス（３，４－ジカルボキシフェノキシ）ベンゼン二無水物、１，３－ビス［２－（３，４－ジカルボキシフェニル）－２－プロピル］ベンゼン二無水物、１，４－ビス［２－（３，４－ジカルボキシフェニル）－２－プロピル］ベンゼン二無水物、ビス［３－（３，４－ジカルボキシフェノキシ）フェニル］メタン二無水物、ビス［４－（３，４－ジカルボキシフェノキシ）フェニル］メタン二無水物、２，２－ビス［３－（３，４－ジカルボキシフェノキシ）フェニル］プロパン二無水物、２，２－ビス［４－（３，４－ジカルボキシフェノキシ）フェニル］プロパン二無水物、ビス（３，４－ジカルボキシフェノキシ）ジメチルシラン二無水物、１，３－ビス（３，４－ジカルボキシフェニル）－１，１，３，３－テトラメチルジシロキサン二無水物、２，３，６，７－ナフタレンテトラカルボン酸二無水物、１，４，５，８－ナフタレンテトラカルボン酸二無水物、１，２，５，６－ナフタレンテトラカルボン酸二無水物、３，４，９，１０－ペリレンテトラカルボン酸二無水物、２，３，６，７－アントラセンテトラカルボン酸二無水物、１，２，７，８－フェナントレンテトラカルボン酸二無水物、エチレンテトラカルボン酸二無水物、１，２，３，４－ブタンテトラカルボン酸二無水物、１，２，３，４－シクロブタンテトラカルボン酸二無水物、シクロペンタンテトラカルボン酸二無水物、シクロヘキサン－１，２，３，４－テトラカルボン酸二無水物、シクロヘキサン－１，２，４，５－テトラカルボン酸二無水物、３，３’，４，４’－ビシクロヘキシルテトラカルボン酸二無水物、カルボニル－４，４’－ビス（シクロヘキサン－１，２－ジカルボン酸）二無水物、メチレン－４，４’－ビス（シクロヘキサン－１，２－ジカルボン酸）二無水物、１，２－エチレン－４，４’－ビス（シクロヘキサン－１，２－ジカルボン酸）二無水物、１，１－エチリデン－４，４’－ビス（シクロヘキサン－１，２－ジカルボン酸）二無水物、２，２－プロピリデン－４，４’－ビス（シクロヘキサン－１，２－ジカルボン酸）二無水物、オキシ－４，４’－ビス（シクロヘキサン－１，２－ジカルボン酸）二無水物、チオ－４，４’－ビス（シクロヘキサン－１，２－ジカルボン酸）二無水物、スルホニル－４，４’－ビス（シクロヘキサン－１，２－ジカルボン酸）二無水物、ビシクロ［２，２，２］オクト－７－エン－２，３，５，６－テトラカルボン酸二無水物、ｒｅｌ－［１Ｓ，５Ｒ，６Ｒ］－３－オキサビシクロ［３，２，１］オクタン－２，４－ジオン－６－スピロ－３’－（テトラヒドロフラン－２’，５’－ジオン）、４－（２，５－ジオキソテトラヒドロフラン－３－イル）－１，２，３，４－テトラヒドロナフタレン－１，２－ジカルボン酸無水物、エチレングリコール－ビス－（３，４－ジカルボン酸無水物フェニル）エーテル、４，４’－ビフェニルビス（トリメリット酸モノエステル酸無水物）、９，９’－ビス（３，４－ジカルボキシフェニル）フルオレン二無水物等。
［マレイミド化合物］
　本発明の硬化性樹脂組成物は、マレイミド化合物を含有しても良い。マレイミド化合物とは分子内に１つ以上マレイミド基を有する化合物である。マレイミド化合物としては、例えば、４，４’－ジフェニルメタンビスマレイミド、ポリフェニルメタンマレイミド、ｍ－フェニレンビスマレイミド、２，２’－ビス〔４－（４－マレイミドフェノキシ）フェニル〕プロパン、３，３’－ジメチル－５，５’－ジエチル－４，４’－ジフェニルメタンビスマレイミド、４－メチル－１，３－フェニレンビスマレイミド、４，４’－ジフェニルエーテルビスマレイミド、４，４’－ジフェニルスルフォンビスマレイミド、１，３－ビス（３－マレイミドフェノキシ）ベンゼン、１，３－ビス（４－マレイミドフェノキシ）ベンゼン）、ザイロック型マレイミド化合物（アニリックス　マレイミド、三井化学ファイン社製）、ビフェニルアラルキル型マレイミド化合物（日本国特開２００９－００１７８３号公報の実施例４に記載のマレイミド化合物（Ｍ２）を含む樹脂溶液を減圧下溶剤留去することにより固形化したもの）、ビスアミノクミルベンゼン型マレイミド（国際公開第２０２０／０５４６０１号記載のマレイミド化合物）、特許６６２９６９２号または国際公開第２０２０／２１７６７９号記載のインダン構造を有するマレイミド化合物、ＭＡＴＥＲＩＡＬ　ＳＴＡＧＥ　Ｖоｌ．１８，Ｎо．１２　２０１９　『～続・エポキシ樹脂ＣＡＳ番号物語～硬化剤ＣＡＳ番号備忘録　第３１回　ビスマレイミド（１）』やＭＡＴＥＲＩＡＬ　ＳＴＡＧＥ　Ｖоｌ．１９，Ｎо．２　２０１９　『～続・エポキシ樹脂ＣＡＳ番号物語～硬化剤ＣＡＳ番号備忘録　第３２回　ビスマレイミド（２）』に記載されているマレイミド化合物等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
［シアネートエステル樹脂］
　シアネートエステル樹脂は、フェノール樹脂をハロゲン化シアンと反応させることにより得られるシアネートエステル化合物であり、具体例としては、ジシアナートベンゼン、トリシアナートベンゼン、ジシアナートナフタレン、ジシアナートビフェニル、２、２’－ビス（４－シアナートフェニル）プロパン、ビス（４－シアナートフェニル）メタン、ビス（３，５－ジメチル－４－シアナートフェニル）メタン、２，２’－ビス（３，５－ジメチル－４－シアナートフェニル）プロパン、２，２’－ビス（４－シアナートフェニル）エタン、２，２’－ビス（４－シアナートフェニル）ヘキサフロロプロパン、ビス（４－シアナートフェニル）スルホン、ビス（４－シアナートフェニル）チオエーテル、フェノールノボラックシアナート、フェノール・ジシクロペンタジエン共縮合物の水酸基をシアネート基に変換したもの等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。
　また、日本国特開２００５－２６４１５４号公報に合成方法が記載されているシアネートエステル化合物は、低吸湿性、難燃性、誘電特性に優れているためシアネートエステル化合物として特に好ましい。
　シアネートエステル樹脂は、必要に応じてシアネート基を三量化させてｓｙｍ－トリアジン環を形成するために、ナフテン酸亜鉛、ナフテン酸コバルト、ナフテン酸銅、ナフテン酸鉛、オクチル酸亜鉛、オクチル酸錫、鉛アセチルアセトナート、ジブチル錫マレエート等の触媒を含有させることもできる。
　触媒は、シアネートエステル樹脂および硬化性樹脂組成物１００質量部中、０．０００１～０．１０質量部、好ましくは０．０００１５～０．００１５質量部使用することが好ましい。
［ポリブタジエンおよびこの変性物］
　ポリブタジエンおよびこの変性物とは、ポリブタジエン、もしくはポリブタジエンに由来する構造を分子内に有する化合物である。ポリブタジエンに由来する構造は水素添加により、不飽和結合を一部、もしくは全て単結合に変換されていても良い。
　ポリブタジエンおよびこの変性物としては、例えば、ポリブタジエン、水酸基末端ポリブタジエン、末端（メタ）アクリレート化ポリブタジエン、カルボン酸末端ポリブタジエン、アミン末端ポリブタジエン、スチレンブタジエンゴム等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。これらのうち、誘電特性の観点からポリブタジエンもしくはスチレンブタジエンゴムが好ましい。スチレンブタジエンゴム（ＳＢＲ）としては例えば、ＲＩＣＯＮ－１００、ＲＩＣＯＮ－１８１、ＲＩＣＯＮ－１８４（いずれもクレイバレー社製）、１，２－ＳＢＳ（日本曹達社製）などが挙げられ、ポリブタジエンとしては、Ｂ－１０００、Ｂ－２０００、Ｂ－３０００（いずれも日本曹達社製）等が挙げられる。ポリブタジエンおよびスチレンブタジエンゴムの分子量としては重量平均分子量５００～１００００が好ましく、より好ましくは７５０～７５００、さらに好ましくは１０００～５０００である。上記範囲の下限以下では揮発量が多く、プリプレグ作成時の固形分調整が困難となり、上記範囲の上限以上では、他の硬化性樹脂との相溶性が悪化する。一般に、ビスマレイミドやポリマレイミドのような酸素や窒素などのヘテロ原子を含む化合物の場合、その極性に起因し、主に炭化水素から構成される化合物もしくは炭化水素のみからなる化合物のような低極性化合物との相溶性の担保が困難である。一方、本発明の化合物は、それ自体が酸素や窒素などのヘテロ原子を積極的に導入した骨格設計ではないことに起因し、低極性かつ低誘電特性を有する材料や、炭化水素のみで構成される化合物との相溶性にも優れる。
［ポリスチレンおよびこの変性物］
　ポリスチレンおよびこの変性物とは、ポリスチレン、もしくはポリスチレンに由来する構造を分子内に有する化合物である。
　ポリスチレンおよびこの変性物としては、例えば、ポリスチレン、スチレン・２－イソプロペニル－２－オキサゾリン共重合体（エポクロス　ＲＰＳ－１００５、ＲＰ－６１　いずれも日本触媒社製）、ＳＥＰ（スチレン－エチレン・プロピレン共重合体：セプトン１０２０　クラレ社製）、ＳＥＰＳ（スチレン－エチレン・プロピレン－スチレン共重合体：セプトン２００２、セプトン２００４Ｆ、セプトン２００５、セプトン２００６、セプトン２０６３、セプトン２１０４　いずれもクラレ社製）、ＳＥＥＰＳ（スチレン－エチレン／エチレン・プロピレン－スチレンブロック共重合体：セプトン４００３、セプトン４０４４、セプトン４０５５、セプトン４０７７、セプトン４０９９　いずれもクラレ社製）、ＳＥＢＳ（スチレン－エチレン・ブチレン－スチレン　ブロック共重合体：セプトン８００４、セプトン８００６、セプトン８００７Ｌ　いずれもクラレ社製）、ＳＥＥＰＳ－ОＨ（スチレン－エチレン／エチレン・プロピレン－スチレンブロック共重合体の末端に水酸基を有する化合物：セプトンＨＧ２５２　クラレ社製）、ＳＩＳ（スチレン－イソプレン－スチレン　ブロック共重合体：セプトン５１２５、セプトン５１２７　いずれもクラレ社製）、水添ＳＩＳ（水添スチレン－イソプレン－スチレン　ブロック共重合体：ハイブラー７１２５Ｆ、ハイブラー７３１１Ｆ　いずれもクラレ社製）、ＳＩＢＳ（スチレン－イソブチレン－スチレンブロック共重合体：ＳＩＢＳＴＡＲ０７３Ｔ、ＳＩＢＳＴＡＲ１０２Ｔ、ＳＩＢＳＴＡＲ１０３Ｔ（いずれもカネカ社製）、セプトンＶ９８２７（クラレ社製））等が挙げられるが、これらに限定されるものではない。また、これらは１種類で用いても、複数併用してもよい。ポリスチレンおよびこの変性物は、より高い耐熱性を有し、かつ酸化劣化しにくいため、不飽和結合を有さないものが好ましい。また、ポリスチレンおよびこの変性物の重量平均分子量は１００００以上であれば特に制限はないが、大きすぎるとポリフェニレンエーテル化合物のほか、重量平均分子量５０～１０００程度の低分子量成分および、重量平均分子量１０００～５０００程度のオリゴマー成分との相溶性が悪化し、混合および溶剤安定性の担保が困難になることから、１００００～３０００００程度であることが好ましい。
［ポリエチレンおよびこの変性物］
　ポリエチレンおよびこの変性物とは、ポリエチレン、もしくはポリエチレンに由来する構造を分子内に有する化合物である。ポリエチレンおよびこの変性物としては、例えば、エチレン－プロピレン共重合体、エチレン－スチレン共重合体、エチレン－プロピレン－エチリデンノルボルネン共重合体（三井化学社製ＥＢＴ：Ｋ－８３７０ＥＭ、Ｋ－９３３０Ｍ等）、エチレン－プロピレン－ビニルノルボルネン共重合体（三井化学社製ＶＮＢ－ＥＰＴ：ＰＸ－００６Ｍ、ＰＸ－００８Ｍ、ＰＸ－００９Ｍ等）、エチレン－ビニルアルコール共重合体、エチレン－酢酸ビニル共重合体等が挙げられるが、これらに限定されるものではない。耐熱性向上の観点から、架橋可能な構造を含有するエチレン－プロピレン－エチリデンノルボルネン共重合体、エチレン－プロピレン－ビニルノルボルネン共重合体を用いることが好ましい。また、これらは１種類で用いても、複数併用してもよい。ポリエチレンおよびこの変性物の重量平均分子量は１００００以上であれば特に制限はないが、大きすぎるとポリフェニレンエーテル化合物のほか、重量平均分子量５０～１０００程度の低分子量成分および、重量平均分子量１０００～５０００程度のオリゴマー成分との相溶性が悪化し、混合および溶剤安定性の担保が困難になることから、１００００～３０００００程度であることが好ましい。
　本発明の硬化性樹脂組成物は、上記各成分を所定の割合で調製することにより得られ、１３０～１８０℃で３０～５００秒の範囲で予備硬化し、更に、１５０～２００℃で２～１５時間、後硬化することにより充分な硬化反応が進行し、本発明の硬化物が得られる。また、硬化性樹脂組成物の成分を溶剤等に均一に分散または溶解させ、溶媒を除去した後硬化させることもできる。
　本発明の硬化性樹脂組成物の調製方法は特に限定されないが、各成分を均一に混合するだけでも、あるいはプレポリマー化してもよい。例えば本発明の化合物を配合した混合物に対し硬化促進剤や重合開始剤の存在下または非存在下、溶剤の存在下または非存在下において加熱することによりプレポリマー化する。同様に、アミン化合物、エチレン性不飽和結合を有する化合物、マレイミド化合物、シアネートエステル化合物、ポリブタジエンおよびこの変性物、ポリスチレンおよびこの変性物などの化合物、無機充填剤、及びその他添加剤を追加してプレポリマー化してもよい。各成分の混合またはプレポリマー化は溶剤の非存在下では例えば押出機、ニーダ、ロールなどを用い、溶剤の存在下では攪拌装置つきの反応釜などを使用する。
　均一に混合する手法としては５０～１００℃の範囲内の温度でニーダ、ロール、プラネタリーミキサー等の装置を用いて練りこむように混合し、均一な樹脂組成物とする。得られた樹脂組成物は粉砕後、タブレットマシーン等の成型機で円柱のタブレット状に成型、もしくは顆粒状の粉体、もしくは粉状の成型体とする、もしくはこれら組成物を表面支持体の上で溶融し０．０５ｍｍ～１０ｍｍの厚みのシート状に成型し、硬化性樹脂組成物成型体とすることもできる。得られた成型体は０～２０℃でべたつきのない成型体となり、－２５～０℃で１週間以上保管しても流動性、硬化性をほとんど低下させない。
　得られた成型体についてトランスファー成型機、コンプレッション成型機にて硬化物に成型することができる。
　本発明の硬化性樹脂組成物は、有機溶剤を添加してワニス状の組成物（以下、単にワニスという。）とすることもできる。本発明の硬化性樹脂組成物を必要に応じてトルエン、キシレン、アセトン、メチルエチルケトン、メチルイソブチルケトン、ジメチルホルムアミド、ジメチルアセトアミド、Ｎ－メチルピロリドン等の溶剤に溶解させてワニスとし、ガラス繊維、カーボン繊維、ポリエステル繊維、ポリアミド繊維、アルミナ繊維、紙などの基材に含浸させて加熱乾燥して得たプリプレグを熱プレス成形することにより、本発明の硬化性樹脂組成物の硬化物とすることができる。この際の溶剤は、本発明の硬化性樹脂組成物と該溶剤の混合物中で１０～７０重量％、好ましくは１５～７０重量％を占める量を用いる。また液状組成物であれば、そのまま例えば、ＲＴＭ方式でカーボン繊維を含有する硬化性樹脂硬化物を得ることもできる。
　また、本発明の硬化性樹脂組成物をフィルム型組成物の改質剤としても使用できる。具体的にはＢ－ステージにおける柔軟性等を向上させる場合に用いることができる。このようなフィルム型の樹脂組成物は、本発明の硬化性樹脂組成物をワニスとして剥離フィルム上に塗布し、加熱下で溶剤を除去した後、Ｂステージ化を行うことによりシート状の接着剤として得られる。このシート状接着剤は多層基板などにおける層間絶縁層として使用することができる。
　本発明の硬化性樹脂組成物は、加熱溶融し、低粘度化してガラス繊維、カーボン繊維、ポリエステル繊維、ポリアミド繊維、アルミナ繊維などの強化繊維に含浸させることによりプリプレグを得ることもできる。その具体例としては、例えば、Ｅガラスクロス、Ｄガラスクロス、Ｓガラスクロス、Ｑガラスクロス、球状ガラスクロス、ＮＥガラスクロス、及びＴガラスクロス等のガラス繊維、更にガラス以外の無機物の繊維やポリパラフェニレンテレフタラミド（ケブラー（登録商標）、デュポン社製）、全芳香族ポリアミド、ポリエステル、ポリパラフェニレンベンズオキサゾール、ポリイミド及び炭素繊維などの有機繊維が挙げられるが、これらに特に限定されない。基材の形状としては、特に限定されないが、例えば、織布、不織布、ロービング、チョップドストランドマットなどが挙げられる。また、織布の織り方としては、平織り、ななこ織り、綾織り等が知られており、これら公知のものから目的とする用途や性能により適宜選択して使用することができる。また、織布を開繊処理したものやシランカップリング剤などで表面処理したガラス織布が好適に使用される。基材の厚さは、特に限定されないが、好ましくは０．０１～０．４ｍｍ程度である。また、前記ワニスを、強化繊維に含浸させて加熱乾燥させることによりプリプレグを得ることもできる。
　また、上記プリプレグを用いて積層板を製造することもできる。積層板はプリプレグを１枚以上備えるものであれば特に限定されず、他のいかなる層を有していてもよい。積層板の製造方法としては、一般に公知の方法を適宜適用でき、特に限定されない。例えば、金属箔張積層板の成形時には多段プレス機、多段真空プレス機、連続成形機、オートクレーブ成形機などを用いることができ、上記プリプレグ同士を積層し、加熱加圧成形することで積層板を得ることができる。このとき、加熱する温度は、特に限定されないが、６５～３００℃が好ましく、１２０～２７０℃がより好ましい。また、加圧する圧力は、特に限定されないが、加圧が大きすぎると積層板の樹脂の固形分調整が難しく品質が安定せず、また、圧力が小さすぎると、気泡や積層間の密着性が悪くなってしまうため２．０～５．０ＭＰａが好ましく、２．５～４．０ＭＰａがより好ましい。本実施形態の積層板は、金属箔からなる層を備えることにより、後述する金属箔張積層板として好適に用いることができる。
　上記プリプレグを所望の形に裁断、必要により銅箔などと積層後、積層物にプレス成形法やオートクレーブ成形法、シートワインディング成形法などで圧力をかけながら硬化性樹脂組成物を加熱硬化させることにより電気電子用積層板（プリント配線板）や、炭素繊維強化材を得ることができる。
　本発明の硬化性樹脂組成物は、樹脂シートにすることもできる。本発明の硬化性樹脂組成物から樹脂シートを得る方法としては、例えば、支持フィルム（支持体）上に硬化性樹脂組成物を塗布したのち、乾燥させて、支持フィルムの上に樹脂組成物層を形成する方法が挙げられる。本発明の硬化性樹脂組成物を樹脂シートに用いる場合、該フィルムは、真空ラミネート法におけるラミネートの温度条件（７０℃～１４０℃）で軟化し、回路基板のラミネートと同時に、回路基板に存在するビアホール或いはスルーホール内の樹脂充填が可能な流動性（樹脂流れ）を示すことが肝要であり、このような特性を発現するよう前記各成分を配合することが好ましい。なお、得られる樹脂シートや回路基板(銅張積層板等)においては、相分離などに起因する、局所的に異なる特性値を示すといった現象を生じさせず、任意の部位において、一定の性能を発現させるため、外観均一性が要求される。
　ここで、回路基板のスルーホールの直径は０．１～０．５ｍｍ、深さは０．１～１．２ｍｍであり、この範囲で樹脂充填を可能とするのが好ましい。なお回路基板の両面をラミネートする場合はスルーホールの１／２程度充填されることが望ましい。
　前記樹脂シートを製造する具体的な方法としては、有機溶剤を配合してワニス化した樹脂組成物を調製した後、支持フィルム（Ｙ）の表面に、前記ワニス化した樹脂組成物を塗布し、更に加熱、あるいは熱風吹きつけ等により有機溶剤を乾燥して、樹脂組成物層（Ｘ）を形成する方法が挙げられる。
　ここで用いる有機溶剤としては、例えば、アセトン、メチルエチルケトン、シクロヘキサノン等のケトン類、酢酸エチル、酢酸ブチル、セロソルブアセテート、プロピレングリコールモノメチルエーテルアセテート、カルビトールアセテート等の酢酸エステル類、セロソルブ、ブチルカルビトール等のカルビトール類、トルエン、キシレン等の芳香族炭化水素類、ジメチルホルムアミド、ジメチルアセトアミド、Ｎ－メチルピロリドン等を用いることが好ましい。また、不揮発分が全体の３０～６０質量％となる割合で有機溶剤を使用することが好ましい。
　なお、形成される前記樹脂組成物層（Ｘ）の厚さは、前記樹脂組成物層（Ｘ）をラミネートする回路基板が有する導体層の厚さ以上とする必要がある。回路基板が有する導体層の厚さは５～７０μｍの範囲であるので、前記樹脂組成物層（Ｘ）の厚さは１０～１００μｍの厚みを有するのが好ましい。なお、本発明における前記樹脂組成物層（Ｘ）は、後述する保護フィルムで保護されていてもよい。保護フィルムで保護することにより、樹脂組成物層（Ｘ）の表面へのゴミ等の付着やキズを防止することができる。
　前記支持フィルム及び保護フィルムは、ポリエチレン、ポリプロピレン、ポリ塩化ビニル等のポリオレフィン、ポリエチレンテレフタレート（ＰＥＴ）、ポリエチレンナフタレート等のポリエステル、ポリカーボネート、ポリイミド、更には離型紙や銅箔、アルミニウム箔等の金属箔などを挙げることができる。なお、支持フィルム及び保護フィルムはマッド処理、コロナ処理の他、離型処理を施してあってもよい。支持フィルムの厚さは特に限定されないが、１０～１５０μｍであり、好ましくは２５～５０μｍの範囲で用いられる。また保護フィルムの厚さは１～４０μｍとするのが好ましい。
　前記支持フィルム（Ｙ）は、回路基板に前記樹脂組成物層（Ｘ）をラミネートした後に、あるいは、前記樹脂組成物層（Ｘ）を加熱硬化することにより絶縁層を形成した後に、剥離される。樹脂シートを構成する樹脂組成物層（Ｘ）が加熱硬化した後に支持フィルム（Ｙ）を剥離すれば、硬化工程でのゴミ等の付着を防ぐことができる。前記樹脂組成物層（Ｘ）が加熱硬化した後に支持フィルム（Ｙ）を剥離する場合、支持フィルム（Ｙ）には予め離型処理が施される。
　なお、前記のようにして得られた樹脂シートから多層プリント回路基板を製造することができる。例えば、前記樹脂組成物層（Ｘ）が保護フィルムで保護されている場合は、保護フィルムを樹脂組成物層（Ｘ）から剥離した後、前記樹脂組成物層（Ｘ）を回路基板に直接接するように回路基板の片面又は両面に、例えば真空ラミネート法によりラミネートする。ラミネートの方法はバッチ式であってもロールでの連続式であってもよい。また必要により、ラミネートを行う前に樹脂シート及び回路基板を必要により加熱（プレヒート）しておいてもよい。ラミネートの条件は、圧着温度（ラミネート温度）を７０～１４０℃とすることが好ましく、圧着圧力を１～１１ｋｇｆ／ｃｍ２（９．８×１０４～１０７．９×１０４Ｎ／ｍ２）とすることが好ましく、空気圧を２０ｍｍＨｇ（２６．７ｈＰａ）以下の減圧下でラミネートすることが好ましい。
　また、本発明の硬化性樹脂組成物を用いて半導体装置を製造することができる。半導体装置としては、例えばＤＩＰ（デュアルインラインパッケージ）、ＱＦＰ（クワッドフラットパッケージ）、ＢＧＡ（ボールグリッドアレイ）、ＣＳＰ（チップサイズパッケージ）、ＳＯＰ（スモールアウトラインパッケージ）、ＴＳＯＰ（シンスモールアウトラインパッケージ）、ＴＱＦＰ（シンクワッドフラットパッケージ）等が挙げられる。
　本発明の硬化性樹脂組成物およびその硬化物は、広範な分野で用いることができる。具体的には、成型材料、接着剤、複合材料、塗料など各種用途に使用できる。本発明記載の硬化性樹脂組成物の硬化物は優れた耐熱性と誘電特性を示すため、半導体素子用封止材、液晶表示素子用封止材、有機ＥＬ素子用封止材、積層板（プリント配線板、ＢＧＡ用基板、ビルドアップ基板など）等の電気・電子部品や炭素繊維強化プラスチック、ガラス繊維強化プラスチック等の軽量高強度構造材用複合材料、３Ｄプリンティング等に好適に使用される。
　次に本発明を実施例により更に具体的に説明する。以下、特に断わりのない限り、部は質量部である。尚、本発明はこれら実施例に限定されるものではない。
　以下に実施例で用いた各種分析方法について記載する。
・ＧＰＣ（ゲルパーミエーションクロマトグラフィー）分析
装置：オンライン脱気ユニット（ＤＧＵ－２０Ａ）、送液ユニット（ＬＣ－２０ＡＤ）、オートサンプラ（ＳＩＬ－２０Ａ）、フォトダイオードアレイ検出器（ＳＰＤ－Ｍ４０）、カラムオーブン（ＣＴО－２０Ａ）、システムコントローラ（ＣＢＭ－２０Ａ）、いずれも株式会社島津製作所製
カラム：ＳＨＯＤＥＸ　ＧＰＣ　ＫＦ－６０１（２本）、ＫＦ－６０２、ＫＦ－６０２．５、ＫＦ－６０３
流速：１．５ｍｌ／ｍｉｎ．
カラム温度：４０℃
使用溶剤：ＴＨＦ（テトラヒドロフラン）
検出器：示差屈折検出器（ＲＩＤ－２０Ａ）、株式会社島津製作所製
［実施例１］
　温度計、冷却管、撹拌機を取り付けたフラスコに、アスピレータおよび塩基トラップを設置した。このフラスコに、酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）としてタフテックＭ１９１３（旭化成株式会社製）２０部、トルエン１８０部、アリルアミン塩酸塩（東京化成社製）０．３４部を加え、発生する塩化水素を塩基トラップで捕集しながら１１０℃で１２時間反応させた。放冷後、得られた反応溶液を１Ｌのアセトンに滴下することで再沈殿を行った。室温で１２時間乾燥させ、目的の化合物（ＡＡ）を１８．２ｇ（薄黄色固体）として得た。（Ｍｎ：６９４６２、Ｍｗ：９５６２３）。得られた化合物のＧＰＣチャートを図１に示す。
［実施例２、３、比較例１、２］
　実施例１で得られた化合物（ＡＡ）、ポリフェニレンエーテル化合物：ＳＡ－９０００（ＳＡＢＩＣ社製）、スチレンブタジエンゴム：Ｒｉｃｏｎ－１００（クレイバレー社製）、重合開始剤：ジクミルパーオキサイド（ＤＣＰ）を表１に示す量用いて、実施例２、３では固形分３０重量％のトルエン溶液、比較例１、２では固形分７０重量％のトルエン溶液を調製し、塗工厚み２００μｍのアプリケータを用いて鏡面銅箔（Ｔ４Ｘ：福田金属銅箔社製）にトルエン溶液を塗布した後、イナートオーブン中で２２０℃で２時間硬化させることで硬化物を得た。評価にあたっては、必要に応じてレーザーカッターを用いて所望のサイズに試験片を切り出して実施した。
＜誘電正接試験＞
　（株）ＡＥＴ社製の１０ＧＨｚ空洞共振器を用いて、２５℃において空洞共振器摂動法にてテストを行った。サンプルサイズは幅１．７ｍｍ×長さ１００ｍｍとし、厚さは０．３ｍｍで試験を行った。評価結果は表１に示す。
Figure JPOXMLDOC01-appb-T000016
・ＳＡ－９０００：末端メタクリル化ポリフェニレンエーテル（ＳＡＢＩＣ社製）
・Ｒｉｃｏｎ－１００：スチレンブタジエンゴム（クレイバレー社製）
・ＤＣＰ：ジクミルパーオキサイド
　表１の結果より、実施例１で得られた化合物（ＡＡ）は、比較例１および２よりも誘電正接が小さく、低誘電特性に優れることが確認された。
　本願は、２０２３年２月３日付で出願された日本国特許出願第２０２３－１５０８８号に基づく優先権を主張する。
　本発明の化合物は、半導体封止材、プリント配線基板、ビルドアップ積層板などの電気・電子部品に好適に使用される。

Claims (11)

  1. 　スチレン系単量体からなる重合体のブロック単位（Ａ）と共役ジエン化合物からなる重合体のブロック単位（Ｂ）とからなるブロック共重合体の水素添加物（Ｈ－ＡＢ）の酸変性物である酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）とアリルアミンまたはアリルアミン塩酸塩とを反応して得られる化合物。
  2. 　前記スチレン系単量体からなる重合体のブロック単位（Ａ）は下記式（ａ）で表される構造である、請求項１に記載の化合物。
    Figure JPOXMLDOC01-appb-C000001
    　式（１）中、Ｒ１およびＲ２はそれぞれ水素原子または炭素数１～５のアルキル基であり、ｐは１～５であり、ｑは繰り返し数の平均値であり、１～１００００の実数を表す。
  3. 　前記共役ジエン化合物からなる重合体のブロック単位（Ｂ）は１，３－ブタジエン、イソプレン、ファルネセン、２，３－ジメチル－１，３－ブタジエン、１，３－ペンタジエンより選ばれる少なくとも１種以上のジエン化合物を重合させることによって得られる、請求項１に記載の化合物。
  4. 　前記ブロック共重合体の水素添加物（Ｈ－ＡＢ）が下記式（１）で表される化合物である、請求項１に記載の化合物。
    Figure JPOXMLDOC01-appb-C000002
      
    式（１）中、Ｒ１およびＲ２はそれぞれ水素原子または炭素数１～５のアルキル基であり、ｐは１～５であり、ｊ，ｋ，ｌ，ｍ，ｎは繰り返し数の平均値であり、１～１００００の実数を表す。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
  5. 　前記酸変性水添熱可塑性スチレン系エラストマー（ＡＨ－ＡＢ）が下記式（２）で表される化合物である、請求項１に記載の化合物。
    Figure JPOXMLDOC01-appb-C000003
     
    式（２）中、Ｒ１およびＲ２はそれぞれ水素原子または炭素数１～５のアルキル基であり、ｐは１～５であり、ｊ，ｋ，ｌ，ｍ，ｎは繰り返し数の平均値であり、１～１００００の実数を表す。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
  6. 　下記式（３）で表される化合物。
    Figure JPOXMLDOC01-appb-C000004
     
    式（３）中、Ｒ１およびＲ２はそれぞれ水素原子または炭素数１～５のアルキル基であり、ｐは１～５であり、ｊ，ｋ，ｌ，ｍ，ｎは繰り返し数の平均値であり、１～１００００の実数を表す。ｋとｌ、またはｊとｍとｎで括られた各繰り返し単位の順序は限定されず、結合様式は、交互、ブロック、ランダムのいずれであってもよい。
  7. 　請求項１から６のいずれか一項に記載の化合物を含有する硬化性樹脂組成物。
  8. 　さらに、重合開始剤を含有する請求項７に記載の硬化性樹脂組成物。
  9. 　さらに、マレイミド化合物、ポリフェニレンエーテル化合物、エチレン性不飽和結合を有する化合物、シアネートエステル樹脂、ポリブタジエンおよびこの変性物、ポリスチレンおよびこの変性物、ポリエチレンおよびこの変性物、のうちから選ばれる少なくとも１種以上を含有する請求項７または８に記載の硬化性樹脂組成物。
  10. 　請求項１から６のいずれか一項に記載の化合物の硬化物。
  11. 　請求項７から９のいずれか一項に記載の硬化性樹脂組成物の硬化物。
PCT/JP2024/002335 2023-02-03 2024-01-26 化合物、硬化性樹脂組成物およびその硬化物 Ceased WO2024162189A1 (ja)