WO2024063158A1 - 電解質組成物、電解質、及び電池 - Google Patents

電解質組成物、電解質、及び電池 Download PDF

Info

Publication number
WO2024063158A1
WO2024063158A1 PCT/JP2023/034482 JP2023034482W WO2024063158A1 WO 2024063158 A1 WO2024063158 A1 WO 2024063158A1 JP 2023034482 W JP2023034482 W JP 2023034482W WO 2024063158 A1 WO2024063158 A1 WO 2024063158A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
hydrocarbon group
electrolyte composition
electrolyte
carbon atoms
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2023/034482
Other languages
English (en)
French (fr)
Inventor
康貴 諏訪
秀人 中島
誠 大内
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Chemical Co Ltd
Kyoto University NUC
Original Assignee
Sumitomo Chemical Co Ltd
Kyoto University NUC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Chemical Co Ltd, Kyoto University NUC filed Critical Sumitomo Chemical Co Ltd
Priority to EP23868279.3A priority Critical patent/EP4576301A1/en
Priority to KR1020257008474A priority patent/KR20250060882A/ko
Priority to CN202380066522.9A priority patent/CN119895612A/zh
Publication of WO2024063158A1 publication Critical patent/WO2024063158A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

イオン伝導性無機固体電解質と、金属イオンを優先的に伝導する能力を有するポリマーと、イオン液体と、を含む、電解質組成物。

Description

電解質組成物、電解質、及び電池
　本開示は、電解質組成物、電解質、及び電池に関する。
　リチウムイオン電池等の正極及び負極間の金属イオンの移動に伴い充放電を行う電池は、高容量であることから盛んに研究が進められている。リチウムイオン電池等の電解質としては、有機溶媒又はイオン液体を含むリチウム塩の溶液などが知られているが、安全性とプロセス性の観点から固体電解質の研究が進められている（特許文献１及び２、並びに非特許文献１）。固体電解質としては、酸化物系固体電解質、硫化物系固体電解質等、様々な種類の化合物が知られている。
中国特許出願明細書第１１２４４８１００号 中国特許出願明細書第１１０２４７１１１号 韓国公開特許第２０１８－００５１０７９号
Journal of The Electrochemical Society, 2020, 167, 070559.
　ここで、固体電解質は、イオン伝導度、安全性に優れる一方、その剛直性から加工性に難があり、界面抵抗も高いという課題がある。そこで、例えば、特許文献１及び２、並びに非特許文献１に記載されるように、柔軟な高分子材料と複合化することにより、固体電解質に柔軟性を付与する検討が行われている。しかしながら、本発明者らが鋭意検討したところ、既存の高分子材料との複合化では、複合体のイオン伝導度が十分な水準に達しないという課題があることが判明した。
　本開示は、上述の課題に鑑みなされたものであって、イオン伝導度に優れる電解質組成物、及び電解質、並びにそれを備える電池を提供することを目的とする。
　本開示は、以下の例示的実施形態［１］～［１０］を含む。
［１］イオン伝導性無機固体電解質と、金属イオンを優先的に伝導する能力を有するポリマーと、イオン液体と、を含む、電解質組成物。
［２］前記イオン伝導性無機固体電解質はアルカリ金属元素及びアルカリ土類金属の少なくとも一方を含む、酸化物、硫化物、水素化物、又はハロゲン化物である、［１］の電解質組成物。
［３］前記イオン伝導性無機固体電解質が、ペロブスカイト型酸化物、ＮＡＳＩＣＯＮ型酸化物、ＬＩＳＩＣＯＮ型酸化物、又はガーネット型酸化物である、［２］の電解質組成物。
［４］前記ポリマーが、アルカリ金属イオンを対カチオンとするアニオン性官能基、及びアニオン捕捉能を有する官能基の少なくとも一方を有する、［１］～［３］のいずれか一つの電解質組成物。
［５］２５℃におけるイオン伝導度が１０－４Ｓ／ｃｍ以上である、［１］～［４］のいずれか一つの電解質組成物。
［６］活性化エネルギーが３０ｋＪ／ｍｏｌ以下である、［１］～［５］のいずれか一つの電解質組成物。
［７］２５℃におけるナノインデンターによる試験結果を用いて下記式から算出したダイナミック硬さＤＨが、１０３Ｎ／ｍｍ２以下である、電解質組成物。
ＤＨ＝α×Ｆ／ｈ２×１０３
α＝３．８５８４
Ｆ：試験力
ｈ：押し込み深さ
［８］２５℃におけるナノインデンターによる試験結果を用いて下記式から算出したダイナミック硬さＤＨが、１０３Ｎ／ｍｍ２以下である、［１］～［６］のいずれか一つの電解質組成物。
ＤＨ＝α×Ｆ／ｈ２×１０３
α＝３．８５８４
Ｆ：試験力
ｈ：押し込み深さ
［９］［１］～［８］のいずれか一つの電解質組成物を含む、電解質。
［１０］［１］～［８］のいずれか一つの電解質組成物を含む、電池。
　本開示によれば、イオン伝導度に優れる電解質組成物、及び電解質、並びにそれを備える電池を提供することができる。
　本実施形態の電解質組成物はイオン伝導性無機固体電解質と、金属イオンを優先的に伝導する能力を有するポリマーと、イオン液体と、を含む。
［イオン伝導性無機固体電解質］
　イオン伝導性無機固体電解質としては、特に制限されず、酸化物（酸化物系固体電解質）、硫化物（硫化物系固体電解質）、水素化物（水素化物系固体電解質）又はハロゲン化物（ハロゲン化物系固体電解質）等であってよい。イオン伝導性無機固体電解質は、アルカリ金属元素及びアルカリ土類金属元素の少なくとも一方を含んでいてよく、アルカリ金属元素を含んでいてよい。
（酸化物系固体電解質）
　酸化物系固体電解質としては、例えば、ペロブスカイト型酸化物、ＮＡＳＩＣＯＮ型酸化物、ＬＩＳＩＣＯＮ型酸化物、ガーネット型酸化物等の酸化物、及び当該酸化物に他のカチオン又はアニオンをドープしたものなどが挙げられる。
　ペロブスカイト型酸化物としては、ＬｉａＬａ１－ａＴｉＯ３（０＜ａ＜１）などのＬｉ－Ｌａ－Ｔｉ系酸化物、ＬｉｂＬａ１－ｂＴａＯ３（０＜ｂ＜１）などのＬｉ－Ｌａ－Ｔａ系酸化物、ＬｉｃＬａ１－ｃＮｂＯ３（０＜ｃ＜１）などのＬｉ－Ｌａ－Ｎｂ系酸化物などが挙げられる。
　ＮＡＳＩＣＯＮ型酸化物としては、Ｌｉ１＋ｄＡｌｄＴｉ２－ｄ（ＰＯ４）３（０≦ｄ≦１）などが挙げられる。ＮＡＳＩＣＯＮ型酸化物は、ＬｉｍＭ１ ｎＭ２ ｏＰｐＯｑ（式中、Ｍ１は、Ｂ、Ａｌ、Ｇａ、Ｉｎ、Ｃ、Ｓｉ、Ｇｅ、Ｓｎ、Ｓｂ及びＳｅからなる群から選ばれる１種以上の元素。Ｍ２は、Ｔｉ、Ｚｒ、Ｇｅ、Ｉｎ、Ｇａ、Ｓｎ及びＡｌからなる群から選ばれる１種以上の元素。ｍ、ｎ、ｏ、ｐ及びｑは、任意の正数。）で表される酸化物であり、Ｌｉ１＋ｘ＋ｙＡｌｘ（Ｔｉ，Ｇｅ）２－ｘＳｉｙＰ３－ｙＯ１２（０＜ｘ＜２、０＜ｙ＜３）（ＬＡＴＰ）などが挙げられる。
　ＬＩＳＩＣＯＮ型酸化物としては、Ｌｉ４Ｍ３Ｏ４－Ｌｉ３Ｍ４Ｏ４（Ｍ３は、Ｓｉ、Ｇｅ、及びＴｉからなる群から選ばれる１種以上の元素。Ｍ４は、Ｐ、Ａｓ及びＶからなる群から選ばれる１種以上の元素。）で表される酸化物などが挙げられる。
　ガーネット型酸化物としては、Ｌｉ７Ｌａ３Ｚｒ２Ｏ１２（ＬＬＺ）、Ｌｉ７－ａ２Ｌａ３Ｚｒ２－ａ２Ｔａａ２Ｏ１２（ＬＬＺＴ、０＜ａ２＜１であってよく、０．１＜ａ２＜０．８であってよく、０．２＜ａ２＜０．６）等のＬｉ－Ｌａ－Ｚｒ系酸化物などが挙げられる。
　酸化物系固体電解質は、結晶性材料であってもよく、非晶質材料であってもよい。
　酸化物系固体電解質としては、Ｌｉ６．６Ｌａ３Ｚｒ１．６Ｔａ０．４Ｏ１２、Ｌｉ０．３３Ｌａ０．５５ＴｉＯ３等が挙げられる。
（硫化物系固体電解質）
　硫化物系固体電解質としては、Ｌｉ２Ｓ－Ｐ２Ｓ５系化合物、Ｌｉ２Ｓ－ＳｉＳ２系化合物、Ｌｉ２Ｓ－ＧｅＳ２系化合物、Ｌｉ２Ｓ－Ｂ２Ｓ３系化合物、Ｌｉ２Ｓ－Ｐ２Ｓ３系化合物、ＬｉＩ－Ｓｉ２Ｓ－Ｐ２Ｓ５、ＬｉＩ－Ｌｉ２Ｓ－Ｐ２Ｏ５、ＬｉＩ－Ｌｉ３ＰＯ４－Ｐ２Ｓ５、Ｌｉ１０ＧｅＰ２Ｓ１２などを挙げることができる。
　なお、本明細書において、硫化物系固体電解質を指す「系化合物」という表現は、「系化合物」の前に記載した「Ｌｉ２Ｓ」「Ｐ２Ｓ５」などの原料を主として含む固体電解質の総称として用いる。例えば、Ｌｉ２Ｓ－Ｐ２Ｓ５系化合物には、Ｌｉ２ＳとＰ２Ｓ５とを含み、さらに他の原料を含む固体電解質が含まれる。また、Ｌｉ２Ｓ－Ｐ２Ｓ５系化合物には、Ｌｉ２ＳとＰ２Ｓ５との混合比を異ならせた固体電解質も含まれる。
　Ｌｉ２Ｓ－Ｐ２Ｓ５系化合物としては、Ｌｉ２Ｓ－Ｐ２Ｓ５、Ｌｉ２Ｓ－Ｐ２Ｓ５－ＬｉＩ、Ｌｉ２Ｓ－Ｐ２Ｓ５－ＬｉＣｌ、Ｌｉ２Ｓ－Ｐ２Ｓ５－ＬｉＢｒ、Ｌｉ２Ｓ－Ｐ２Ｓ５－Ｌｉ２Ｏ、Ｌｉ２Ｓ－Ｐ２Ｓ５－Ｌｉ２Ｏ－ＬｉＩ、Ｌｉ２Ｓ－Ｐ２Ｓ５－ＺｍＳｎ（ｍ、ｎは正の数。Ｚは、Ｇｅ、ＺｎまたはＧａ）などを挙げることができる。
　Ｌｉ２Ｓ－ＳｉＳ２系化合物としては、Ｌｉ２Ｓ－ＳｉＳ２、Ｌｉ２Ｓ－ＳｉＳ２－ＬｉＩ、Ｌｉ２Ｓ－ＳｉＳ２－ＬｉＢｒ、Ｌｉ２Ｓ－ＳｉＳ２－ＬｉＣｌ、Ｌｉ２Ｓ－ＳｉＳ２－Ｂ２Ｓ３－ＬｉＩ、Ｌｉ２Ｓ－ＳｉＳ２－Ｐ２Ｓ５－ＬｉＩ、Ｌｉ２Ｓ－ＳｉＳ２－Ｌｉ３ＰＯ４、Ｌｉ２Ｓ－ＳｉＳ２－Ｌｉ２ＳＯ４、Ｌｉ２Ｓ－ＳｉＳ２－ＬｉｘＭＯｙ（ｘ、ｙは正の数。Ｍは、Ｐ、Ｓｉ、Ｇｅ、Ｂ、Ａｌ、Ｇａ又はＩｎ）などを挙げることができる。
　Ｌｉ２Ｓ－ＧｅＳ２系化合物としては、Ｌｉ２Ｓ－ＧｅＳ２、Ｌｉ２Ｓ－ＧｅＳ２－Ｐ２Ｓ５などを挙げることができる。
　硫化物系固体電解質は、結晶性材料であってもよく、非晶質材料であってもよい。
（水素化物系固体電解質）
　水素化物系固体電解質材料としては、ＬｉＢＨ４、ＬｉＢＨ４－３ＫＩ、ＬｉＢＨ４－ＰＩ２、ＬｉＢＨ４－Ｐ２Ｓ５、ＬｉＢＨ４－ＬｉＮＨ２、３ＬｉＢＨ４－ＬｉＩ、ＬｉＮＨ２、Ｌｉ２ＡｌＨ６、Ｌｉ（ＮＨ２）２Ｉ、Ｌｉ２ＮＨ、ＬｉＧｄ（ＢＨ４）３Ｃｌ、Ｌｉ２（ＢＨ４）（ＮＨ２）、Ｌｉ３（ＮＨ２）Ｉ、Ｌｉ４（ＢＨ４）（ＮＨ２）３などを挙げることができる。
（ハロゲン化物系固体電解質）
　ハロゲン化物固体電解質としては、Ｌｉと金属元素とハロゲン元素を含む化合物などを挙げることができる。
　ハロゲン化物固体電解質は、結晶性材料であってもよく、非晶質材料であってもよい。
　イオン伝導性無機固体電解質としては、酸化物系固体電解質、硫化物系固体電解質、水素化物系固体電解質又はハロゲン化物系固体電解質の具体例として挙げた化合物のＬｉの一部又は全部をＮａ、Ｋ、Ｒｂ又はＣｓで置き換えた化合物も挙げられる。
　イオン伝導性無機固体電解質の含有量は、電解質組成物の総量に対して、５０質量％以上であってよく、５５質量％以上であってよく、６０質量％以上であってよく、６５質量％以上であってよく、７０質量％以上であってよい。また、イオン伝導性無機固体電解質の含有量は、電解質組成物の総量に対して、９５質量％以下であってよく、９０質量％以下であってよい。また、イオン伝導性無機固体電解質の含有量は、電解質組成物の総量に対して、５０～９９質量％であってよく、５５～９５質量％であってよく、６５～９０質量％であってよい。
　イオン伝導性無機固体電解質の含有量は、電解質組成物の総量に対して、１５体積％以上であってよく、２５体積％以上であってよく、３５体積％以上であってよく、４０体積％以上であってよく、４５体積％以上であってよい。また、イオン伝導性無機固体電解質の含有量は、電解質組成物の総量に対して、９０体積％以下であってよく、８０体積％以下であってよく、７０体積％以下であってよく、６０体積％以下であってよい。また、イオン伝導性無機固体電解質の含有量は、電解質組成物の総量に対して、１５～９０体積％であってよく、２０～８０体積％であってよく、３０～７０体積％であってよい。なお、本明細書では、特に断らない限り、体積％は、電解質組成物に含まれる各成分の混合前の体積に基づいて計算され、電解質組成物に含まれる各成分の質量割合が分かっている場合は、各成分の質量割合を密度で除した値であってよい。
　イオン伝導性無機固体電解質は、粒子表面に処理を施したものであってよい。具体的には、酸により表面不導体層を除く処理や、原子と共有結合を形成する処理などが挙げられる。酸としては特に限定されるものではないが、塩酸、硝酸、リン酸などが挙げられる。
［金属イオンを優先的に伝導する能力を有するポリマー］
　金属イオンを優先的に伝導する能力を有するポリマー（以下、単にポリマーとも呼ぶ。）としては、例えば、室温（２５℃）において、以下の（Ａ）及び（Ｂ）の少なくとも一方の組成物について金属イオンの輸率を測定した場合に、金属イオンの輸率が０．４以上、０．５以上、０．６以上、又は０．７以上となるものであってよい。
（Ａ）当該ポリマーを３３質量％と、非イオン性の可塑剤６７質量％を含む組成物
（Ｂ）当該ポリマーを３１．９質量％と、金属塩と、非イオン性の可塑剤を残りの全量含み、金属イオン濃度が０．３ｍｏｌ/Ｌである組成物
　組成物に含まれる金属イオンは、ポリマーがアニオン性官能基を有する場合、当該アニオン性官能基の対カチオンであってよく、金属塩として添加したものであってもよい。金属イオンを優先的に伝導する能力を有するポリマーは、アルカリ金属イオンを優先的に伝導する能力を有するポリマーであってよい。非イオン性の可塑剤としては、有機溶媒及びフッ素系樹脂等のその他の樹脂の少なくとも一方が挙げられる。有機溶媒は、非プロトン性溶媒であってよい。非プロトン性溶媒は、カーボネート系溶媒、フッ素系溶媒、及びエーテル系溶媒からなる群から選択される少なくとも一種であってよい。カーボネート系溶媒としては、ジメチルカーボネート、ジエチルカーボネート、エチルメチルカーボネート等の鎖状カーボネート；エチレンカーボネート、プロピレンカーボネート、ブチレンカーボネート、ビニレンカーボネート等の環状カーボネートなどが挙げられる。フッ素系溶媒としては、パーフルオロオクタン等のハイドロフルオロカーボン類；メチルノナフルオロブチルエーテル、エチルノナフルオロブチルエーテル等のハイドロフルオロエーテル類、１，３，３，３－テトラフルオロプロペン等のハイドロフルオロオレフィン類などが挙げられる。エーテル系溶媒としては、テトラヒドロフラン、２－メチルテトラヒドロフラン、テトラヒドロピラン、１，３－ジオキソラン等の環状エーテル；１，２－ジエトキシエタン、及びエトキシメトキシエタン等の鎖状エーテルなどが挙げられる。有機溶媒は、エチレンカーボネート及びプロピレンカーボネートを１：１の体積比で含む混合溶媒であってよい。
　フッ素系樹脂としては、炭素鎖を主鎖として有する樹脂であってよい。炭素鎖はエチレン性不飽和基のラジカル重合により形成されたものであってよい。フッ素系樹脂は、ポリ（フッ化ビニリデン－ｃｏ－ヘキサフルオロプロピレン）（ＰＶＤＦ－ＨＦＰ）であってよい。
　金属イオンの濃度は金属塩を添加することにより調整してよい。例えば、金属塩がアルカリ金属塩である場合、アルカリ金属塩としては特に限定されないが、アルカリ金属をＭとして、ＭＦ、ＭＣｌ、ＭＢｒ、ＭＩ、ＭＣｌＯ４、ＭＰＦ６、ＭＢＦ４、Ｍ２ＳＯ４、Ｍ［（ＣｈＦ２ｈ＋１）ＳＯ３］（ｈは、０～３）、Ｍ［（ＣｈＦ２ｈ＋１）ＳＯ２］２Ｎ（ｈは、０～３）等が挙げられる。Ｍはポリマーが構造単位（Ａ）を有する場合、構造単位（Ａ）が有するアルカリ金属元素と同じアルカリ金属元素であってよい。
　金属イオンを優先的に伝導する能力を有するポリマーは、金属イオンを対カチオンとして有するアニオン性官能基（官能基（Ａ）とも呼ぶ。）、及びアニオン捕捉能を有する官能基（官能基（Ｂ）とも呼ぶ。）の少なくとも一方を含むものが挙げられる。ポリマーの構造としては、特に制限はないが、主鎖として炭素鎖を有するものが挙げられ、当該炭素鎖はエチレン性不飽和基を有する単量体のラジカル付加重合により形成されたものであってよい。
　官能基（Ａ）の対カチオンである金属イオンは、アルカリ金属イオン及びアルカリ土類金属イオンの少なくとも一方であってよく、アルカリ金属イオンであってよい。アルカリ金属イオンとしては、リチウムイオン、ナトリウムイオン、カリウムイオン、ルビジウムイオン、セシウムイオン等が挙げられ、リチウムイオン、ナトリウムイオン、又はカリウムイオンであってよく、リチウムイオン、又はナトリウムイオンであってよく、リチウムイオンであってよい。以下、官能基（Ａ）と、官能基（Ａ）の対カチオンである金属イオンを含む構造単位を構造単位（Ａ）とも呼ぶ。構造単位（Ａ）はエチレン性不飽和基を有するモノマーをラジカル付加重合することによって得られる構造を有していてよい。官能基（Ａ）の対カチオンである金属イオンは、イオン伝導性無機固体電解質に含まれるアルカリ金属イオンと同じアルカリ金属イオンであってよい。
　構造単位（Ａ）は、官能基（Ａ）として、スルホニルイミド基の共役アニオン、スルホン酸基の共役アニオン、及びフェノール性水酸基の共役アニオンからなる群から選択される少なくとも一つを有していてよい。スルホニルイミド基の共役アニオン、スルホン酸基の共役アニオン、及びフェノール性水酸基の共役アニオンは、例えば、以下で説明するスルホニルイミド基の共役アニオンを有する基、スルホン酸基の共役アニオン（スルホネート基）を有する基、及びフェノール性水酸基の共役アニオンを有する基に含まれていてよい。
　スルホニルイミド基を有する基は、以下の式（Ａ１）で表される構造単位に含まれていてよい。
Figure JPOXMLDOC01-appb-C000001
 （式（Ａ１）において、Ｘは、１～２０個の炭素原子を有する２価の有機基であり、Ｙは、ハロゲン原子、又は１～２０個の炭素原子を有する１価の有機基であり、Ｍ＋は、アルカリ金属イオンであり、＊は、構造単位（Ａ１）が他の構造単位と結合する位置を表す。）
　Ｘとしては、特に制限はなく、炭化水素基であってもヘテロ原子を有する基であってもよく、複素環を有していてもよい。Ｘとして、より具体的には、炭化水素基、炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換された化学構造を有する基等の２価の基が挙げられる。なお、連結基が複数ある場合、当該連結基は互いに隣り合わない。また、上記２価の基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基としては、１価の置換基であってよく、例えば、ハロゲン原子等が挙げられる。上記炭化水素基としては特に限定されず、脂肪族炭化水素基であってもよく、芳香族炭化水素基であってもよい。脂肪族炭化水素基としては、直鎖状炭化水素基、分岐鎖状炭化水素基、及び環式炭化水素基のいずれであってもよい。また、炭化水素基は、飽和炭化水素基及び不飽和炭化水素基のいずれであってもよい。Ｘは、Ｘが有する炭素原子により、マレイミド基の窒素原子及びスルホニル基の硫黄原子の一方又は両方と結合していてよい。
　Ｘが有する炭素原子の個数は１～１５個であってよく、２～１０個であってよく、３～８個であってよい。Ｘは芳香環を有する基であってよく、ベンゼン環等の芳香族の炭素環を有する基であってよい。当該炭素環の環員である炭素原子にはアルキル基、ハロゲン原子等の電子求引基などの置換基が結合していてもよい。Ｘとしての炭化水素基は、フェニレン基、１～８個の炭素原子を有するアルキレン基、ポリオキシアルキレン基、又はこれらが有する炭素原子に結合する水素原子の一部又は全部がフッ素原子等のハロゲン原子に置換された基であると好ましく、フェニレン基又はアルキル基、ハロゲン原子、電子求引基等に置換された置換フェニレン基であるとより好ましい。電子求引基としては、ハロゲン原子、スルホン酸基又はその塩、スルホン酸エステル、ニトロ基、ニトリル基などが挙げられる。
　式（Ａ１）において、Ｙが１価の有機基である場合、当該有機基としては、特に制限はなく、炭化水素基であってもヘテロ原子を有する基であってもよく、複素環を有していてもよい。Ｙとして、より具体的には、炭化水素基、炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換された化学構造を有する基等の１価の基が挙げられる。なお、連結基が複数ある場合、連結基は互いに隣り合わない。また、上記１価の基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基としては、１価の置換基であってよく、例えば、ハロゲン原子等が挙げられる。上記炭化水素基としては特に限定されず、脂肪族炭化水素基であってもよく、芳香族炭化水素基であってもよい。脂肪族炭化水素基としては、直鎖状炭化水素基、分岐鎖状炭化水素基、及び環式炭化水素基のいずれであってもよい。また、炭化水素基は、飽和炭化水素基及び不飽和炭化水素基のいずれであってもよい。
　Ｙが有する炭素原子の個数は１～１５個であってよく、１～１０個であってよく、１～８個であってよく、１～５個であってよく、１～３個であってよい。Ｙとしての炭化水素基は、フェニル基、１～５個の炭素原子を有するアルキル基、又はこれらの基が有する炭素原子に結合する水素原子の一部又は全部がフッ素原子等のハロゲン原子に置換されたものが好ましく、１～５個の炭素原子を有するフッ素化アルキル基がより好ましく、トリフルオロメチル基等の１～３個の炭素原子を有するフッ素化アルキル基が更に好ましい。フッ素化アルキル基は全フッ素化アルキル基であってよい。Ｙがハロゲン原子である場合、ハロゲン原子としては、フッ素原子又は塩素原子が好ましく、フッ素原子がより好ましい。
　式（Ａ１）中、Ｍ＋は、アルカリ金属イオンであり、リチウムイオン（Ｌｉ＋）、ナトリウムイオン（Ｎａ＋）、又はカリウムイオン（Ｋ＋）であると好ましく、リチウムイオンであることがより好ましい。Ｍ＋は、Ｌｉ＋、Ｎａ＋、及びＫ＋のうち２種又は３種のイオンを含んでいてもよいが、実質的に単一のイオンのみを含むことが好ましい。
　フェノール性水酸基の共役アニオンを有する基は、芳香環に直接結合した水酸基（すなわち、フェノール性水酸基（－ＯＨ））がアルカリ金属化した基（つまり、Ｍをアルカリ金属として－ＯＭ基）を有する基である。
　構造単位（Ａ）は、以下の式（Ａ２）で表される基であってよい。
Figure JPOXMLDOC01-appb-C000002
 （式（Ａ２）中、Ｙ２は、アルカリ金属化されたフェノール性水酸基を有する基、又はスルホン酸の共役アニオンを有する基であり、＊は、構造単位（Ａ２）の他の構造単位との結合位置を表す。Ｒ１５～Ｒ１７は、それぞれ独立に水素原子若しくは１価の置換基である、又はＲ１６は水素原子若しくは１価の置換基であり、Ｒ１５及びＲ１７は一緒になって２価の置換基を形成している。）
　Ｒ１５～Ｒ１７は１つ以上が水素原子であってもよく、すべて水素原子であってもよい。
　Ｒ１５～Ｒ１７が１価の置換基である場合、当該１価の置換基は１価の有機基であってもよい。当該有機基が有する炭素原子の個数は、１～２０個であってよく、１～１５個であってよく、１～１０個であってよく、１～５個であってよく、１～３個であってよい。有機基としては、炭化水素基、当該炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換されて形成された化学構造を有する基等、複素環を有する基等の１価の置換基が挙げられる。また、上記１価の置換基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基としては、例えば、ハロゲン原子等が挙げられる。上記炭化水素基としては特に限定されず、脂肪族炭化水素基であってもよく、芳香族炭化水素基であってもよい。脂肪族炭化水素基としては、直鎖状炭化水素基、分岐鎖状炭化水素基、及び環式炭化水素基のいずれであってもよい。また、炭化水素基は、飽和炭化水素基及び不飽和炭化水素基のいずれであってもよい。炭化水素基としては、メチル基、エチル基、プロピル基、フェニル基等が挙げられる。
　Ｒ１５～Ｒ１７について、１価の置換基は電子求引基を有していてよく、電子求引基自体であってもよい。電子求引基は上記１価の有機基に結合していてもよく、上記１価の有機基が電子求引基であってもよい。電子求引基としては、ハロゲン原子、スルホン酸基又はその塩、スルホン酸エステル、ニトロ基、ニトリル基などが挙げられる。ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子のいずれであってもよい。
　Ｒ１５及びＲ１７が一緒になって２価の有機基を形成している場合、２価の有機基が有する炭素原子の個数は、１～２０個であってよく、１～１５個であってよく、１～１０個であってよく、１～５個であってよく、１～３個であってよい。有機基としては、炭化水素基、当該炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換されて形成された化学構造を有する基等、複素環を有する基等の２価の置換基が挙げられる。また、上記２価の有機基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基としては、例えば、ハロゲン原子等が挙げられる。上記炭化水素基としては特に限定されず、脂肪族炭化水素基であってもよく、芳香族炭化水素基であってもよい。脂肪族炭化水素基としては、直鎖状炭化水素基、分岐鎖状炭化水素基、及び環式炭化水素基のいずれであってもよい。また、炭化水素基は、飽和炭化水素基及び不飽和炭化水素基のいずれであってもよい。炭化水素基としては、プロピレン基、ブチレン基等が挙げられる。
　Ｙ２がフェノール性水酸基を有する基である場合、Ｙ２は、以下の式（Ａ２１）～（Ａ２６）のいずれかの式で表される基であってよい。
Figure JPOXMLDOC01-appb-C000003
 （式（Ａ２１）中、ＲＡ基のうち少なくとも一つが－ＯＭ基であり、残りは、水素原子又は１価の置換基であり、Ｍは、アルカリ金属元素であり、Ｌｉ、Ｎａ又はＫであってよい。式（Ａ２２）中、ＲＢ基のうち少なくとも一つが－ＯＭ基であり、残りは、水素原子又は１価の置換基であり、Ｍは、アルカリ金属元素であり、Ｌｉ、Ｎａ又はＫであってよい。式（Ａ２３）中、ＲＣ基のうち少なくとも一つが－ＯＭ基であり、残りは、水素原子又は１価の置換基であり、Ｍは、アルカリ金属元素であり、Ｌｉ、Ｎａ又はＫであってよい。式（Ａ２４）中、ＲＤ基のうち少なくとも一つが－ＯＭ基であり、残りは、水素原子又は１価の置換基であり、Ｍは、アルカリ金属元素であり、Ｌｉ、Ｎａ又はＫであってよい。式（Ａ２５）中、ＲＥ基のうち少なくとも一つが－ＯＭ基であり、残りは、水素原子又は１価の置換基であり、Ｍは、アルカリ金属元素であり、Ｌｉ、Ｎａ又はＫであってよい。式（Ａ２６）中、ＲＦ基のうち少なくとも一つが－ＯＭ基であり、残りは、水素原子又は１価の置換基であり、Ｍは、アルカリ金属元素であり、Ｌｉ、Ｎａ又はＫであってよい。）
　ポリマーが式（Ａ２１）の官能基を有する場合、式（Ａ２１）のベンゼン環において、式（Ａ２１）の官能基とポリマーとの結合部位から見て、パラ位に－ＯＭ基が結合していてよい。また、ＲＡ３基が－ＯＡ基であってもよい。上記結合部位から見てメタ位又はオルト位及びメタ位には、それぞれ独立に水素原子、－ＯＡ基、メチル基、エチル基、１～２０個の炭素原子を有する１価の有機基（ただし、当該１価の有機基が飽和炭化水素基である場合、メチル基、エチル基又は６～２０個若しくは６～１５個の炭素原子を有する基であり、１価の有機基がアルコキシ基である場合、４～２０個若しくは４～１５個の炭素原子を有する基である。）が結合していてよい。
　式（Ａ２１）～（Ａ２６）で表される基は、１～３個の－ＯＭ基を有していてよく、１又は２個の－ＯＭ基を有していてよく、１個の－ＯＭ基を有していてよい。
　式（Ａ２１）～（Ａ２６）において、１価の置換基は、電子求引基であると好ましい。電子求引基としては、ハロゲン原子、スルホン酸基又はその塩、スルホン酸エステル、ニトロ基、ニトリル基などが挙げられる。ハロゲン原子としては、Ｆ、Ｃｌ、Ｂｒ及びＩのいずれであってもよい。
　また、式（Ａ２１）～（Ａ２６）において、１価の置換基は、１～２０個の炭素原子を有する有機基であってよい。当該有機基が有する炭素原子の個数は、１～１５個であってよく、１～１０個であってよく、１～５個であってよく、１～３個であってよい。有機基としては、炭化水素基、当該炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換されて形成された化学構造を有する基等、複素環を有する基等の１価の基が挙げられる。また、上記１価の基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基としては、例えば、ハロゲン原子等が挙げられる。上記炭化水素基としては特に限定されず、脂肪族炭化水素基であってもよく、芳香族炭化水素基であってもよい。脂肪族炭化水素基としては、直鎖状炭化水素基、分岐鎖状炭化水素基、及び環式炭化水素基のいずれであってもよい。また、炭化水素基は、飽和炭化水素基及び不飽和炭化水素基のいずれであってもよい。炭化水素基としては、メチル基、エチル基、プロピル基、フェニル基等が挙げられる。なお、１価の有機基は、それ自体が電子求引基であってもよい。
　Ｙ２がスルホン酸の共役アニオンを有する基である場合、Ｙ２としては、下記式（Ａ３）で表される基が挙げられる。
Figure JPOXMLDOC01-appb-C000004
 （式（Ａ３）において、Ｒ１９は、共有結合又は２価の有機基である。Ｍは、アルカリ金属元素であり、Ｌｉ、Ｎａ又はＫであってよい。）
　式（Ａ３）において、２価の有機基が有する炭素原子の個数は、１～２０個であってよく、１～１５個であってよく、１～１０個であってよく、１～５個であってよく、１～３個であってよい。有機基としては、炭化水素基、当該炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換されて形成された化学構造を有する基等、複素環を有する基等の２価の置換基が挙げられる。また、上記２価の有機基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基としては、例えば、ハロゲン原子等が挙げられる。上記炭化水素基としては特に限定されず、脂肪族炭化水素基であってもよく、芳香族炭化水素基であってもよい。脂肪族炭化水素基としては、直鎖状炭化水素基、分岐鎖状炭化水素基、及び環式炭化水素基のいずれであってもよい。また、炭化水素基は、飽和炭化水素基及び不飽和炭化水素基のいずれであってもよい。炭化水素基としては、メチレン基、フェニレン基等が挙げられる。
　スルホン酸の共役アニオンを有する基としては、－ＳＯ３Ｍ、－ＣＨ２－ＳＯ３Ｍ、－Ｃ６Ｈ４－ＳＯ３Ｍ等が挙げられる。
　官能基（Ｂ）は、アニオンレセプターとしての機能を有する官能基である。アニオンレセプターは、アニオンと静電相互作用、水素結合、酸塩基錯体等を形成することによりアニオンを捕捉する化学種を言う。官能基（Ｂ）は、金属塩における金属イオンの対アニオンを捕捉し、当該対アニオンと金属イオンとの解離を促す。これにより、金属イオンの移動度が増す。また、対アニオンは、構造単位（Ｂ）を介してポリマーに捕捉されるため、対アニオンの移動度は低下する。結果として金属イオンの輸率が向上すると考えられる。また、金属イオンの移動度が増すため、金属イオンの伝導性も向上する傾向にある。
　アニオンレセプターとして機能する低分子の化学種（化合物等）は知られており、そのようなものとしては、例えば、米国特許６０２２６４３号明細書、米国特許５７０５６８９号明細書、米国特許６１２０９４１号明細書等に記載の化合物が挙げられる。官能基（Ｂ）は、アニオンレセプターとして機能する化学種に対応する構造を有する。当該官能基は、ポリマーに固定されているため、従来の低分子のアニオンレセプターとは異なり、捕捉したアニオンをポリマーの構造上に固定できる。そのため、当該アニオンが移動することによる電流への関与をより有効に抑制することができると考えられる。
　なお、アルカリ金属塩の対アニオンは、上記官能基に捕捉される際に完全に電離した遊離のアニオンである必要はなく、金属イオンとイオン結合又はイオン対を形成した状態で上記官能基と相互作用することにより捕捉されてよい。
　アニオンレセプターとしての機能を有する官能基は、ルイス酸性を有するものであってよい。この場合、上記官能基は、アニオンの非共有電子対を受容し、酸塩基錯体を形成することによりアニオンを捕捉することができる。このような官能基としては、電子不足の原子を有する官能基が挙げられる。なお、電子不足の原子とは、他の原子と共有結合しているものの、当該原子の最外殻の電子がオクテットを形成していないものを言う。電子不足の原子としては、周期表第１３族に属する原子が挙げられ、より具体的には、アルミニウム及びホウ素の少なくとも一方であってよく、ホウ素であってよい。
　また、アニオンレセプターとしての機能を有する官能基としては、アザエーテル部分を有する基であってもよい。アザエーテル部分を有する基は、アザエーテル化合物を置換基として有する基であり、アザエーテル化合物は、エーテル化合物の－Ｏ－を－ＮＲＥ－（ここで、ＲＥは水素原子又は有機基である）で置き換えた化合物である。アザエーテル部分は鎖状アザエーテル部分及び環状アザエーテル部分のいずれであってもよく、鎖状アザエーテル部分及び環状アザエーテル部分の両方を有していてよい。アザエーテル部分を有する基は、例えば炭化水素部分等に、電子求引基を有していてもよい。
　官能基（Ｂ）は、例えば、下記式（Ｂ）で表される構造単位（Ｂ）に含まれていてもよい。
Figure JPOXMLDOC01-appb-C000005
 （式（Ｂ）中、Ｗは、アニオンレセプターとしての機能を有する官能基であり、Ｒ１～Ｒ３は、それぞれ独立に水素原子若しくは１価の置換基である、又はＲ３は水素原子若しくは１価の置換基であり、Ｒ１及びＲ２は一緒になって２価の有機基を形成している。＊は、構造単位（Ｂ）が他の構造単位と結合する位置を表す。）
　金属イオンを優先的に伝導する能力を有するポリマーは、１種又は２種以上の式（Ｂ）で表される構造単位を含んでいてよい。
　Ｒ１～Ｒ３は１つ以上が水素原子であってもよく、すべて水素原子であってもよい。Ｗは後述の式（Ｂ１）で表される基であってよい。
　Ｒ１～Ｒ３が１価の置換基である場合、当該１価の置換基は１価の有機基であってもよい。当該有機基が有する炭素原子の個数は、１～２０個であってよく、１～１５個であってよく、１～１０個であってよく、１～５個であってよく、１～３個であってよい。有機基としては、炭化水素基、当該炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換されて形成された化学構造を有する基等、複素環を有する基等の１価の置換基が挙げられる。また、上記１価の置換基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基としては、例えば、ハロゲン原子等が挙げられる。上記炭化水素基としては特に限定されず、脂肪族炭化水素基であってもよく、芳香族炭化水素基であってもよい。脂肪族炭化水素基としては、直鎖状炭化水素基、分岐鎖状炭化水素基、及び環式炭化水素基のいずれであってもよい。また、炭化水素基は、飽和炭化水素基及び不飽和炭化水素基のいずれであってもよい。炭化水素基としては、メチル基、エチル基、プロピル基、フェニル基等が挙げられる。
　なお、本明細書において、芳香族炭化水素基は、芳香族部分を含む基であり、脂肪族部分を有していてもよい。また、本明細書において環式炭化水素基は、環式の炭化水素部分を含む基であり、直鎖又は分岐鎖の炭化水素部分を含んでいてもよい。
　１価の置換基は電子求引基を有していてよく、電子求引基自体であってもよい。電子求引基は上記１価の有機基に結合していてもよく、上記１価の有機基が電子求引基であってもよい。電子求引基としては、ハロゲン原子、スルホン酸基又はその塩、スルホン酸エステル、ニトロ基、ニトリル基などが挙げられる。ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子のいずれであってもよい。
　Ｒ１及びＲ２は一緒になって２価の有機基を形成している場合、２価の有機基が有する炭素原子の個数は、１～２０個であってよく、１～１５個であってよく、１～１０個であってよく、１～５個であってよく、１～３個であってよい。有機基としては、炭化水素基、当該炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換されて形成された化学構造を有する基等、複素環を有する基等の２価の置換基が挙げられる。また、上記２価の有機基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基としては、例えば、ハロゲン原子等が挙げられる。上記炭化水素基としては特に限定されず、脂肪族炭化水素基であってもよく、芳香族炭化水素基であってもよい。脂肪族炭化水素基としては、直鎖状炭化水素基、分岐鎖状炭化水素基、及び環式炭化水素基のいずれであってもよい。また、炭化水素基は、飽和炭化水素基及び不飽和炭化水素基のいずれであってもよい。炭化水素基としては、プロピレン基、ブチレン基等が挙げられる。
　Ｗは下記式（Ｂ１）で表される基を有すると好ましい。
Figure JPOXMLDOC01-appb-C000006
 （式（Ｂ１）中、ＷＢは周期表第１３族に属する原子であり、Ｒ５は共有結合又は２価の有機基であり、Ｒ６及びＲ７は水素原子、－ＯＨ基、ハロゲン原子若しくは１価の有機基である、又は一緒になって２価の有機基を形成している。Ｒ６及びＲ７は同じ基であっても異なる基であってもよい。）
　ＷＢは、アルミニウム及びホウ素の少なくとも一方であってよく、ホウ素であってよい。
　Ｒ５が２価の有機基である場合、２価の有機基が有する炭素原子の個数は、１～２０個であってよく、１～１５個であってよく、１～１０個であってよく、１～５個であってよく、１～３個であってよい。有機基としては、炭化水素基、当該炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換されて形成された化学構造を有する基等、複素環を有する基等の１価の置換基が挙げられる。また、上記２価の有機基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基は、電子求引基であってよい。電子求引基としては、ハロゲン原子、スルホン酸基又はその塩、スルホン酸エステル、ニトロ基、ニトリル基などが挙げられる。ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子のいずれであってもよい。Ｒ５は、炭化水素基、ハロゲン置換炭化水素基、又は炭化水素基若しくはハロゲン置換炭化水素基がエーテル結合を介してＷＢに結合する基であってよい。ハロゲン置換炭化水素基は、炭化水素基が有する水素原子の一部又は全部をハロゲン原子で置換したものであってよく、部分フッ素置換炭化水素基又は全フッ素置換炭化水素基であってよい。Ｒ５は共有結合であってもよい。
　Ｒ６又はＲ７がハロゲン原子である場合、フッ素原子、塩素原子、臭素原子及びヨウ素原子のいずれであってもよく、フッ素原子が好ましい。
　Ｒ６又はＲ７が１価の有機基である場合、１価の有機基が有する炭素原子の個数は、１～２０個であってよく、１～１５個であってよく、１～１０個であってよく、１～５個であってよく、１～３個であってよい。有機基としては、炭化水素基、当該炭化水素基における一つ以上の炭素原子（メチレン基）が－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－又は－Ｃ（＝Ｏ）Ｏ－の連結基により置換されて形成された化学構造を有する基等、複素環を有する基等の１価の置換基が挙げられる。また、上記１価の有機基は、炭素原子に結合する水素原子を置換する置換基を有していてもよい。置換基は、電子求引基であってよい。電子求引基は、としては、ハロゲン原子、スルホン酸基又はその塩、スルホン酸エステル、ニトロ基、ニトリル基などが挙げられる。ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子のいずれであってもよい。Ｒ６又はＲ７は、炭化水素基、ハロゲン置換炭化水素基、又は炭化水素基若しくはハロゲン置換炭化水素基がエーテル結合を介してＷＢに結合する基であってよい。ハロゲン置換炭化水素基は、炭化水素基が有する水素原子の一部又は全部をハロゲン原子で置換したものであってよく、部分フッ素置換炭化水素基又は全フッ素置換炭化水素基であってよい。
　Ｗは下記式（Ｂ１ａ）で表される基、又は下記式（Ｂ１ｂ）で表される基であってよい。
Figure JPOXMLDOC01-appb-C000007
 （式（Ｂ１ａ）中、Ｘ１及びＸ２はそれぞれ酸素原子（エーテル結合）又は共有結合であり、Ｒ１１及びＲ１２は、それぞれハロゲン原子、１価の炭化水素基、水素原子、又は１価のハロゲン置換炭化水素基であり、ハロゲン原子（Ｘが酸素原子の場合を除く）、１価の炭化水素基、又は１価のハロゲン置換炭化水素基であってよく、Ｒ１１及びＲ１２の少なくとも一方が１価の炭化水素基、又は１価のハロゲン置換炭化水素基であってよい。Ｒ１１及びＲ１２は同じ基であってよく、異なる基であってもよい。）
Figure JPOXMLDOC01-appb-C000008
 （式（Ｂ１ｂ）中、Ｘ３及びＸ４はそれぞれ酸素原子（エーテル結合）又は共有結合であり、Ｒ１３は、２価の炭化水素基、又は２価のハロゲン置換炭化水素基である。）
　式（Ｂ１ａ）において、Ｒ１１がハロゲン原子である場合、Ｘ１は共有結合であってよく、Ｒ１２がハロゲン原子である場合、Ｘ２は共有結合であってよい。Ｒ１１もしくはＲ１２が１価の炭化水素基、又は１価のハロゲン置換炭化水素基である場合、１価の炭化水素基、又は１価のハロゲン置換炭化水素基が有する炭素原子の個数は、１～２０個であってよく、１～１５個であってよく、１～１０個であってよく、１～５個であってよく、１～３個であってよい。ハロゲン置換炭化水素基は、炭化水素基が有する水素原子の一部又は全部をハロゲン原子で置換したものであってよく、部分フッ素置換炭化水素基又は全フッ素置換炭化水素基であってよい。
　Ｒ１１及びＲ１２は、それぞれ独立に－Ｆ、－ＣＨ３、－Ｃ２Ｈ５、－Ｃ３Ｈ７、－Ｃ６Ｈ５（フェニル基）、－Ｃ６ＨｎＦ５－ｎ（ｎは０～４の整数であり、０～３の整数であってよい。）、－ＣＦ３、－ＣＨ２ＣＦ３、－ＣＨ２ＣＦ３ＣＦ７、－ＣＨ（ＣＦ３）２、－Ｃ（ＣＦ３）２－Ｃ６Ｈ５、－Ｃ（ＣＦ３）３、－Ｃ６Ｈｎ（ＣＦ３）５－ｎ（ｎは０～４の整数であり、１又は２であってよい。）
　式（Ｂ１ｂ）において、２価の炭化水素基、又は２価のハロゲン置換炭化水素基が有する炭素原子の個数は、１～２０個であってよく、１～１５個であってよく、２～１０個であってよく、３～８個であってよい。ハロゲン置換炭化水素基は、炭化水素基が有する水素原子の一部又は全部をハロゲン原子で置換したものであってよく、部分フッ素置換炭化水素基又は全フッ素置換炭化水素基であってよい。
　Ｒ１３は、－Ｃ２Ｈ４－、－Ｃ３Ｈ６－、－Ｃ４Ｈ８－、－Ｃ５Ｈ１０－、－Ｃ６Ｈ１２－、－Ｃ７Ｈ１４－、－Ｃ８Ｈ１６－、－Ｃ９Ｈ１８－、－Ｃ１０Ｈ２０－等、これらの水素原子を部分的に又は全部フッ素に置換したものなどが挙げられる。より具体的には、－Ｃ（ＣＨ３）２－Ｃ（ＣＨ３）２－が好ましい。
　ポリマーに含まれる全構造単位に対する構造単位（Ｂ）のモル比ｍは、０．２～０．８であってよく、０．２５～０．７５であってよく、０．３～０．７であってよく、０．３５～０．６５であってよく、０．４～０．６であってよい。
　ポリマーに含まれる全構造単位に対する構造単位（Ａ）のモル比ｎは、０．２５～０．７５であってよく、０．３～０．７であってよく、０．３５～０．６５であってよく、０．４～０．６であってよい。
　ｍ及びｎの合計は、１以下であれば問題ないが、０．９５以下であってもよい。また、ｍ及びｎの合計は、０．５以上であってよく、０．６以上であってよく、０．７以上であってよく、０．８以上であってよく、０．９以上であってよく、０．９５以上であってよい。
　ポリマーの総質量に対する構造単位（Ａ）の含有量は、５～９０質量％であってよく、２０～８０質量％であってよく、４０～７５質量％であってよく、５５～７０質量％であってよい。
　ポリマーの総質量に対する構造単位（Ｂ）の含有量は、１０～９５質量％であってよく、１５～９５質量％であってよく、２０～９５質量％であってよく、２０～８０質量％であってよく、２５～６０質量％であってよく、３０～４５質量％であってよい。
　構造単位（Ａ）と構造単位（Ｂ）との含有量の合計は、ポリマーの総質量に対して５０質量％以上であってよく、７０質量％以上であってよく、９０質量％以上であってよく、９５質量％以上であってよい。
　ポリマーは、構造単位（Ａ）及び構造単位（Ｂ）のいずれとも異なる構造単位である構造単位（Ｃ）を含んでいてよい。構造単位（Ｃ）としては、以下の構造単位（Ｃ１）で表される構造単位、構造単位（Ｃ２）で表される構造単位等が挙げられる。
Figure JPOXMLDOC01-appb-C000009
 （式（Ｃ１）において、Ｒ２１～Ｒ２４は、それぞれ独立に水素原子、ハロゲン原子、１～２０個の炭素原子を有する１価の有機基である。＊は、構造単位（Ｃ１）が他の構造単位と結合する位置を表す。）
Figure JPOXMLDOC01-appb-C000010
 （式（Ｃ２）中、Ｒ２５は、１～２０個の炭素原子を有する２価の有機基であり、Ｒ２６及びＲ２７は、それぞれ、水素原子、ハロゲン原子、又は１～２０個の炭素原子を有する１価の有機基である。Ｒ２５は、式（Ｃ２）のエチレン単位とイミド基を有する環（コハク酸イミド環又はそのＮ－誘導体）、又は酸無水物基を有する環（コハク酸無水物環）を構成していてよい。）
　Ｒ２１～Ｒ２４の一つ又は２つ以上は１価の有機基であってよい。当該１価の有機基は－Ｚ１－Ｒ２９で表される基であってよい。Ｒ２１～Ｒ２４のそれぞれが有する炭素原子の個数は、１～４０個であってよく、１～２０個であってよく、２～１５個であってよく、４～１３個であってよい。ここで、Ｚ１は、２価の連結基であり、例えば、共有結合、－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－、－Ｃ（＝Ｏ）Ｏ－、－ＯＣ（＝Ｏ）－、－Ｃ（＝Ｏ）ＮＲ３８－又は－ＮＲ３９Ｃ（＝Ｏ）－で表される基であってよい。Ｚ１が共有結合、－Ｏ－、－Ｓ－、－Ｃ（＝Ｏ）－、－Ｃ（＝Ｏ）Ｏ－又は－ＯＣ（＝Ｏ）－である場合、Ｒ２９は水素原子又は１価の有機基である。Ｚが－Ｃ（＝Ｏ）ＮＲ３８－である場合、Ｒ２９、Ｒ３８はそれぞれ水素原子若しくは１価の有機基である、又はＲ２９は、Ｒ３８と一緒になって環を形成している。－ＮＲ３９Ｃ（＝Ｏ）－である場合、Ｒ２９、及びＲ３９はそれぞれ独立に水素原子若しくは１価の有機基である、又はＲ２９は、Ｒ３９と一緒になって環を形成している。Ｒ２９、Ｒ３８及びＲ３９としての１価の有機基は１～２０個、又は１～１０個の有機基を有していてよい。Ｒ３８が１価の有機基である場合、１～２０個の炭素原子を有する１価の炭化水素基であってよい。Ｚ１が共有結合又は－Ｃ（＝Ｏ）Ｏ－である場合、Ｒ２９は水素原子又は１～２０個の炭素原子を有する１価の炭化水素基であってよい。Ｚ１が共有結合であり且つＲ２９が炭化水素基である場合、当該炭化水素基は脂肪族炭化水素基であってよい。また、Ｒ２９は、炭化水素基以外の１価の有機基又は環構造を有する炭化水素基であってよい。Ｚ１が－Ｏ－である場合、ＷをアルキルエーテルとしてＷ－Ｈで表される基以外の１価の有機基であってよい。Ｒ２６～Ｒ２８が１価の有機基である場合、１価の有機基としては、Ｒ２５の例として挙げたものと同じものが挙げられる。
　また、構造単位（Ｃ）には、構造単位（Ａ）の前駆体である構造単位（構造単位（Ａｐ）とも呼ぶ。）が含まれていてもよい。このような構造単位としては、構造単位（Ａ）の前駆体である構造単位（例えば、後述の単量体（Ａ２’）に由来する構造単位）のうち、構造単位（Ａ）に変換できなかった未反応の構造単位及び中間的な構造単位が挙げられ、例えば、構造単位（Ａ）の共役酸である基（つまり、構造単位（Ａ）の対カチオンであるアルカリ金属イオンをＨ＋に置き換えたもの）、及び構造単位（Ａ）の対カチオンをアルカリ金属イオン以外のカチオンに置き換えた基などが挙げられる。構造単位（Ａｐ）に含まれる対カチオンとしては、ＮＨ４ ＋、有機アンモニウムカチオン、アルカリ土類金属イオン等の金属イオンなどが挙げられる。ポリマーは、構造単位（Ａ）と構造単位（Ａｐ）との合計量に対して構造単位（Ａ）を８５モル％以上、９０モル％以上、又は９５モル％以上含んでいてもよい。
　ポリマーは、ブタジエン、イソプレン等の複数のエチレン性不飽和基を有する炭化水素化合物に由来する構造単位を含んでいてもよい。
　ポリマーは、架橋剤に由来する構造単位を有していてもよい。架橋剤としては、ヘキサンジオールジアクリレート、ペンタエリスリトールテトラアクリレート、ジビニルベンゼン、トリエチレングリコールジビニルエーテル等の分子内に複数のエチレン性不飽和基を有する化合物が挙げられる。
　ポリマーの数平均分子量（Ｍｎ）は、５０００～２０００００であってよく、８０００～１２００００であってよく、１００００～１０００００であってよい。ポリマーの重量平均分子量（Ｍｗ）は、５０００～３０００００であってよく、１００００～２５００００であってよく、２００００～１０００００であってよい。ポリマーの分子量分布（Ｍｗ／Ｍｎ）は、１．０～３．５であってよく、１．３～２．７であってよい。ポリマーの数平均分子量及び重量平均分子量は、例えば、ゲルパーミエイションクロマトグラフィーにより測定することができる。
　電解質組成物におけるポリマーの含有量は、０．５～４０質量％であってよく、１～３０質量％であってよく、２～２０質量％であってよい。　電解質組成物におけるポリマーの含有量は、１～５０体積％であってよく、３～４０体積％であってよく、７～３５体積％であってよい。
　ポリマーの製造方法としては、特に限定されないが、例えば、アルカリ金属イオン化されたアニオン性官能基を有する単量体又は当該アニオン性官能基の前駆体を有する単量体（以下、単量体（Ａ'）と呼ぶ。）、及びアニオンレセプターとしての機能を有する官能基を有する単量体（Ｂ’）の少なくとも一方を含む単量体（単量体混合物）を重合させる方法が挙げられる。単量体は更に単量体（Ａ’）及び単量体（Ｂ’）と異なる単量体（Ｃ’）を含んでいてよい。
　単量体（Ａ'）及び単量体（Ｂ’）は、エチレン性不飽和基を有していてよい。この場合、ラジカル付加重合により単量体（Ａ'）及び単量体（Ｂ’）を重合することができる。この場合、単量体は、開始剤の存在下で重合することができる。つまり、重合反応は、単量体と開始剤とを含む重合性組成物において行われてよい。
　単量体（Ａ'）は、ポリマーにおいて構造単位（Ａ）を誘導する単量体である。単量体（Ａ’）としては、以下の式（Ａ１’）で表される単量体（Ａ１’）、式（Ａ２’）で表される単量体（Ａ２’）等を挙げることができる。
Figure JPOXMLDOC01-appb-C000011
 （式（Ａ１’）のＸ、Ｙ及びＭ＋は式（Ａ１）と同じ意味である。）
Figure JPOXMLDOC01-appb-C000012
 （式（Ａ２’）において、Ｒ１５～Ｒ１７は、式（Ａ２）のＲ１５～Ｒ１７と同じ意味であり、Ｙ２’は、式（Ａ２）におけるＹ２が有する－ＯＭ基に対応するフェノール性水酸基を誘導することができる基、又はＹ２が有する－ＳＯ３Ｍ基に対応するスルホン酸基を誘導することができる基を有する基である。）
　Ｙ２’は、Ｙ２と同じ基であってもよいが、Ｙ２の前駆体である基であってよい。すなわち、Ｙ２’は、得ようとするＹ２が有する－ＯＭ基又は－ＳＯ３Ｍ基と同じ位置に－ＯＭ基又は－ＳＯ３Ｍ基に変換可能な基を有する基である。
　Ｙ２が有する－ＯＭ基に対応するフェノール性水酸基を誘導することができる基としては、例えば、加水分解性基が挙げられ、当該加水分解性基を加水分解することによりＹ２が有する－ＯＭ基に対応する位置にフェノール性水酸基を導入することができる。加水分解性基としては、例えば、アルコキシド基、又は－ＯＳｉ（Ｒｋ）３基（Ｒｋは、炭化水素基等の１価の有機基）が挙げられる。フェノール性水酸基は、例えば、ＭＯＨ、Ｍ２ＣＯ３、ＭＨＣＯ３等のアルカリ金属の塩基性塩と反応させることにより－ＯＭ基に変換できる。
　同様に、Ｙ２が有する－ＳＯ３Ｍ基に対応するスルホン酸基を誘導することができる基としては、例えば、スルホン酸エステル基、－ＳＯ２Ｃｌ基等のスルホン酸基（－ＳＯ３Ｈ）を誘導できる基が挙げられる。スルホン酸基は、例えば、ＭＯＨ、Ｍ２ＣＯ３、ＭＨＣＯ３、ハロゲン化アルカリ金属等のアルカリ金属の塩と反応させることにより－ＯＭ基に変換できる。また、－ＳＯ２Ｃｌ基については、ＭＯＨと反応して－ＳＯ３Ｍ基に変換させることもできる。過剰量のＭＯＨを用いる場合、ほとんどの－ＳＯ２Ｃｌ基を－ＳＯ３Ｍ基に変換させることもできる。かかる反応では、－ＳＯ２Ｃｌ基の一部が－ＳＯ３Ｈ基となる場合もあるが、－ＳＯ３Ｈ基については、別途Ｍを含む塩基と反応させて－ＳＯ３Ｍ基としてもよい。また、Ｙ２’は、Ｙ２と同じアニオン部分を有し、アルカリ金属イオン以外のカチオンと塩を形成している基であってもよい。この場合、得られたポリマーにカチオン交換反応を行うことによって、構造単位（Ａ２）を誘導することができる。Ｙ２’の反応率（Ｙ２’の総量のうちＹ２に変換されたものの割合）は、８５モル％以上、９０モル％以上、又は９５モル％以上であってよい。
　単量体（Ｂ'）は、ポリマーにおいて構造単位（Ｂ）を誘導する単量体である。単量体（Ｂ’）としては、以下の式（Ｂ’）で表される単量体（Ｂ’）を挙げることができる。
Figure JPOXMLDOC01-appb-C000013
 （式中、Ｒ１～Ｒ３及びＷは、式（Ｂ）におけるＲ１～Ｒ３及びＷと同じ意味である。）
　ラジカル重合開始剤は熱開始剤及び光開始剤のいずれであってもよい。たとえば、熱開始剤としては、２，２－アゾビス（イソブチロニトリル）（ＡＩＢＮ）；２，２－アゾビス（２－メチルブチロニトリル）（ＡＭＢＮ）、２，２－アゾビス（２，４－ジメチルバレロニトリル）（ＡＤＶＮ）、１，１－アゾビス（１－シクロヘキサンカルボニトリル）（ＡＣＨＮ、Ｖ－４０）、ジメチル－２，２－アゾビスイソブチレート（ＭＡＩＢ）等のアゾ系開始剤；ジベンゾイルパーオキシド、ジ－８，５，５－トリメチルヘキサノイルパーオキシド、ジラウロイルパーオキシド、ジデカノイルパーオキシド、ジ（２，４－ジクロロベンゾイル）パーオキシド等の有機過酸化物などが挙げられる。光開始剤としては、オキシム系化合物、メタロセン系化合物、アシルホスフィン系化合物、アミノアセトフェノン化合物などが挙げられる。開始剤は、１種又は２種以上を使用してよい。
［イオン液体］
　イオン液体としては特に限定されず、例えば、電池等の用途に使用できるものであってよい。具体的には、イミダゾリウム塩、ピロリジニウム塩、ピペリジニウム塩、ピリジニウム塩、第４級アンモニウム塩、第４級ホスホニウム塩等が挙げられる。イオン液体が有するアニオンとしては特に制限はなく、例えば、Ｃｌ－、Ｂｒ－、Ｉ－、ＣｌＯ４ －、ＰＦ６ －、ＢＦ４ －、ＣＦ３ＳＯ３ －、（ＦＳＯ２）２Ｎ－、（ＣＦ３ＳＯ２）２Ｎ－、（ＣｒＦ２ｒ＋１ＳＯ２）２Ｎ－（ｒは２以上の整数）、ＨＳＯ３ －等が挙げられ、電気化学的な安定性の観点からはＰＦ６ －、ＢＦ４ －、ＣＦ３ＳＯ３ －、（ＦＳＯ２）２Ｎ－、（ＣＦ３ＳＯ２）２Ｎ－又は（ＣｍＦ２ｍ＋１ＳＯ２）２Ｎ－が好ましく、（ＣＦ３ＳＯ２）２Ｎ－がより好ましい。イオン液体は、２５℃で液体であってよい。
　ピロリジニウム塩が有するピロリジニウムカチオンとしては、例えば以下のものが挙げられる。
Figure JPOXMLDOC01-appb-C000014
 　式中、Ｒ４１及びＲ４２は、それぞれ独立に１価の有機基であり、当該有機基は１～１５個の炭素原子を有すると好ましい。１価の有機基としては、ブチル基等の１～１５個の炭素原子を有するアルキル基、又は式：－Ａ１－Ｏ－（Ａ２－Ｏ）ｋ－Ａ３により表される基（Ａ１は１又は２個の炭素原子を有するアルキレン基であり、Ａ２は２又は３個の炭素原子を有するアルキレン基であり、Ａ３は、１～３個の炭素原子を有するアルキル基であり、ｋは０～３である。）である。
　式：－Ａ１－Ｏ－（Ａ２－Ｏ）ｋ－Ａ３により表される基としては、１～１０個の炭素原子を有する基であると好ましく、－ＣＨ３ＯＣＨ２ＣＨ２ＯＣＨ３基又は－ＣＨ２ＣＨ２－Ｏ－ＣＨ３がより好ましい。Ｒ４１は、１～３個の炭素原子を有するアルキル基であり、メチル基であってよい。Ｒ４１及びＲ４２は同じであっても異なっていてもよい。なお、ピロリジン環を構成する炭素原子に結合している水素は置換基により置換されていてもよい。
　ピペリジニウム塩が有するピペリジニウムカチオンとしては、例えば以下のものが挙げられる。
Figure JPOXMLDOC01-appb-C000015
 　式中、Ｒ４３及びＲ４４は、それぞれ独立に１価の有機基であり、当該有機基は１～１５個の炭素原子を有すると好ましい。１価の有機基としては、１～１５個の炭素原子を有するアルキル基又は式：－Ａ１－Ｏ－（Ａ２－Ｏ）ｋ－Ａ３により表される基（Ａ１は１又は２個の炭素原子を有するアルキレン基であり、Ａ２は２又は３個の炭素原子を有するアルキレン基であり、Ａ３は、１～３個の炭素原子を有するアルキル基であり、ｋは０～３である。）である。
　Ｒ４４のアルキル基は、ブチル基等の２～６個の炭素原子を有するアルキル基であるとより好ましい。式：－Ａ１－Ｏ－（Ａ２－Ｏ）ｋ－Ａ３により表される基としては、１～１０個の炭素原子を有する基であると好ましく、－ＣＨ３ＯＣＨ２ＣＨ２ＯＣＨ３基又は－ＣＨ２ＣＨ２－Ｏ－ＣＨ３がより好ましい。Ｒ４３は、１～３個の炭素原子を有するアルキル基であり、メチル基であってよい。Ｒ４３及びＲ４４は同じであっても異なっていてもよい。なお、ピペリジン環を構成する炭素原子に結合している水素は置換基により置換されていてもよい。
　イミダゾリウム塩が有するイミダゾリウムカチオンとしては、例えば以下のものが挙げられる。
Figure JPOXMLDOC01-appb-C000016
 　式中、Ｒ４６及びＲ４７は、それぞれ独立に１価の有機基であり、当該有機基は１～１５個の炭素原子を有すると好ましい。１価の有機基としては、１～１５個の炭素原子を有するアルキル基又は式：－Ａ１－Ｏ－（Ａ２－Ｏ）ｋ－Ａ３により表される基（Ａ１は１又は２個の炭素原子を有するアルキレン基であり、Ａ２は２又は３個の炭素原子を有するアルキレン基であり、Ａ３は、１～３個の炭素原子を有するアルキル基であり、ｋは０～３である。）である。
　Ｒ４７のアルキル基としては、ブチル基等の２～６個の炭素原子を有するアルキル基であると好ましい。式：－Ａ１－Ｏ－（Ａ２－Ｏ）ｋ－Ａ３により表される基としては、１～１０個の炭素原子を有する基であると好ましく、－ＣＨ３ＯＣＨ２ＣＨ２ＯＣＨ３基又は－ＣＨ２ＣＨ２－Ｏ－ＣＨ３がより好ましい。Ｒ４６は、１～３個の炭素原子を有するアルキル基であり、メチル基であってよい。Ｒ４６及びＲ４７は同じであっても異なっていてもよい。なお、イミダゾール環を構成する炭素原子に結合している水素は置換基により置換されていてもよい。
　第４級アンモニウム塩が有するアンモニウムカチオンとしては、例えば以下のものが挙げられる。
Figure JPOXMLDOC01-appb-C000017
 　式中、Ｒ５１～Ｒ５４はそれぞれ独立に１価の有機基であり、当該有機基は１～１５個の炭素原子を有すると好ましい。１価の有機基としては、１～１５個の炭素原子を有するアルキル基又は式：－Ａ１－Ｏ－（Ａ２－Ｏ）ｋ－Ａ３により表される基（Ａ１は１又は２個の炭素原子を有するアルキレン基であり、Ａ２は２又は３個の炭素原子を有するアルキレン基であり、Ａ３は、１～３個の炭素原子を有するアルキル基であり、ｋは０～３である。）であると好ましい。Ｒ５１～Ｒ５４はすべて同じであってよいが、２つ以上の異なる基であってもよい。例えば、Ｒ５１が１～１０個の炭素原子を有するアルキル基であり、Ｒ５２～Ｒ５４が１～３個の炭素原子を有するアルキル基であると好ましく、Ｒ５１がブチル基等の３～８個の炭素原子を有するアルキル基であり、Ｒ５２～Ｒ５４がメチル基又はエチル基であるとより好ましい。式：－Ａ１－Ｏ－（Ａ２－Ｏ）ｋ－Ａ３により表される基としては、１～１０個の炭素原子を有する基であると好ましく、－ＣＨ３ＯＣＨ２ＣＨ２ＯＣＨ３基又は－ＣＨ２ＣＨ２－Ｏ－ＣＨ３がより好ましい。
　第４級ホスホニウム塩が有するホスホニウムカチオンとしては、例えば以下のものが挙げられる。
Figure JPOXMLDOC01-appb-C000018
 　式中、Ｒ５６～Ｒ５９はそれぞれ独立に１価の有機基であり、当該有機基は１～１５個の炭素原子を有すると好ましい。１価の有機基としては、１～１５個の炭素原子を有するアルキル基又は式：－Ａ１－Ｏ－（Ａ２－Ｏ）ｋ－Ａ３により表される基（Ａ１は１又は２個の炭素原子を有するアルキレン基であり、Ａ２は２又は３個の炭素原子を有するアルキレン基であり、Ａ３は、１～３個の炭素原子を有するアルキル基であり、ｋは０～３である。）であると好ましい。Ｒ５６～Ｒ５９はすべて同じであってよいが、２つ以上の異なる基であってもよい。例えば、Ｒ５６が１～１０個の炭素原子を有するアルキル基であり、Ｒ５７～Ｒ５９が１～３個の炭素原子を有するアルキル基であると好ましく、Ｒ５６がペンチル基等の３～８個の炭素原子を有するアルキル基であり、Ｒ５７～Ｒ５９がメチル基又はエチル基であるとより好ましい。）
　イオン液体としては、具体的には、１－（２－メトキシエトキシメチル）－１－メチルピロリジニウムビス（トリフルオロメチルスルホニル）イミド、１－エチル－３－メチルイミダゾリウムビス（トリフルオロメチルスルホニル）イミド、１－エチル－３－メチルイミダゾリウムテトラフルオロボレート、１－ｎ－ブチル－１－メチルピロリジニウムビス（フルオロスルホニル）イミド、１－ｎ－ブチル－１－メチルピロリジニウムトリフルオロメタンスルホン酸、１－ｎ－ブチル－１－メチルピロリジニウムビス（トリフルオロメチルスルホニル）イミド、トリエチル－ｎ－ペンチルホスホニウムビス（トリフルオロメチルスルホニル）イミド、ｎ－ブチルトリメチルアンモニウムビス（トリフルオロメチルスルホニル）イミド等が挙げられる。
　イオン液体の含有量は、電解質組成物の総量に対して１～５０質量％であってよく、３～４０質量％であってよく、５～３０質量％であってよい。
　イオン液体の含有量は、電解質組成物の総量に対して１～７０体積％であってよく、５～６０体積％であってよく、１５～５５体積％であってよい。電解質組成物において、上記ポリマーはイオン液体を含む溶媒により膨潤されていてよい。
　電解質組成物は、上記ポリマー以外に金属塩を含んでいてもよい。金属塩は、アルカリ金属塩及びアルカリ土類金属塩の少なくとも一方であってよく、アルカリ金属塩であってよい。アルカリ金属塩としては、特に限定されないが、アルカリ金属をＭとして、ＭＦ、ＭＣｌ、ＭＢｒ、ＭＩ、ＭＣｌＯ４、ＭＰＦ６、ＭＢＦ４、Ｍ２ＳＯ４、Ｍ［（ＣｈＦ２ｈ＋１）ＳＯ３］（ｈは、０～３）、Ｍ［（ＣｈＦ２ｈ＋１）ＳＯ２］２Ｎ（ｈは、０～３）等が挙げられる。Ｍはポリマーが構造単位（Ａ）を有する場合、構造単位（Ａ）が有するアルカリ金属元素と同じアルカリ金属元素であってよい。Ｍは、リチウム、ナトリウム又はカリウムであってよく、リチウムであってよい。また、ポリマーが官能基（Ｂ）を有する場合、電解質組成物は、アルカリ金属塩を含んでいてもよい。
　電解質組成物は、更にフッ素系樹脂等のその他の樹脂、不織布等の布帛、多孔質材料、粘度調整材等を含む複合体としてもよい。他の樹脂としては、フッ素系樹脂が挙げられる。フッ素系樹脂としては、炭素鎖を主鎖として有する樹脂が好ましい。炭素鎖はエチレン性不飽和基のラジカル重合により形成されたものであってよい。フッ素樹脂としては、ポリ（フッ化ビニリデン－ｃｏ－ヘキサフルオロプロピレン）（ＰＶＤＦ－ＨＦＰ）、ポリフッ化ビニリデン（ＰＶＤＦ）等が挙げられる。
　電解質組成物におけるイオン伝導性無機固体電解質と、金属イオンを優先的に伝導する能力を有するポリマーと、イオン液体との合計量は、電解質組成物の総量に対して、７０質量％以上であってよく、８０質量％以上であってよく、９０質量％以上であってよく、９５質量％以上であってよく、９７質量％以上であってよく、９９．９質量％以下であってよく、９９質量％以下であってよい。また、電解質組成物におけるイオン伝導性無機固体電解質と、金属イオンを優先的に伝導する能力を有するポリマーと、イオン液体との合計量は、電解質組成物の総量に対して、７０～９９．９質量％であってよく、８０～９９質量％であってもよい。
　電解質組成物におけるイオン伝導性無機固体電解質と、金属イオンを優先的に伝導する能力を有するポリマーと、イオン液体との合計量は、電解質組成物の総量に対して、７０体積％以上であってよく、８０体積％以上であってよく、９０体積％以上であってよく、９５体積％以上であってよく、９７体積％以上であってよく、９９．９体積％以下であってよく、９９体積％以下であってよい。また、電解質組成物におけるイオン伝導性無機固体電解質と、金属イオンを優先的に伝導する能力を有するポリマーと、イオン液体との合計量は、電解質組成物の総量に対して、７０～９９．９体積％であってよく、８０～９９体積％であってもよい。
　本実施形態の電解質組成物の２５℃におけるイオン伝導度は、１０－４Ｓ／ｃｍ以上であってよく、２．０×１０－４Ｓ／ｃｍ以上であってよく、３．０×１０－４Ｓ／ｃｍ以上であってよく、５．０×１０－４Ｓ／ｃｍ以上であってよい。
　本実施形態の電解質組成物の活性化エネルギーは、３０ｋＪ／ｍｏｌ以下であってよく、２８ｋＪ／ｍｏｌ以下であってよく、２６ｋＪ／ｍｏｌ以下であってよい。
　本実施形態の電解質組成物は、柔軟性が高い傾向にある。例えば、本実施形態の電解質組成物の２５℃においてナノインデンターによる試験結果を用いて下記式から算出したダイナミック硬さＤＨは、１０３Ｎ／ｍｍ２以下であってよく、８．０×１０２Ｎ／ｍｍ２以下であってよく、６．０×１０２Ｎ／ｍｍ２以下であってよく、５．０×１０２Ｎ／ｍｍ２以下であってよい。ナノインデンターによる測定では、予め設定した押し込み深さｈに達する試験力を測定してもよいし、予め設定した試験力による押し込み深さを測定してもよい。ナノインデンターの測定サンプルとしては、例えば、１５０ｍｇの電解質組成物を２００ＭＰａの圧力でプレス成型することにより得られた直径１．５ｃｍのシート状のサンプルであってよい。なお、ダイナミック硬さＤＨの値は互いに重なり合わないよう測定された数点（例えば５点）の試験結果の平均値から求められてもよい。
ＤＨ＝α×Ｆ／ｈ２×１０３
α＝３．８５８４：圧子形状による定数
Ｆ：試験力
ｈ：押し込み深さ
　本実施形態の電解質組成物は、２５℃におけるナノインデンターによる試験結果を用いて下記式から算出したダイナミック硬さＤＨは、１０３Ｎ／ｍｍ２以下のものであり、金属イオンを優先的に伝導する能力を有するポリマーと、イオン液体と、を含んでいてよく、更にイオン伝導性無機固体電解質を含んでいてよい。
　本実施形態の電解質組成物は、キャパシタ、電池等の電気化学デバイスの構成材料として使用することができ、例えば、電池の電解質の材料として使用することができる。電解質は、電解質組成物を加圧成形することにより形成されたものであってよい。電池としては、リチウムイオン電池、ナトリウムイオン電池等のアルカリ金属イオンの移動により充放電を行う電池が挙げられる。電池は一次電池であっても二次電池であってもよく、全固体電池であってもよい。本実施形態の電解質組成物は、固体電解質組成物等の非液状の電解質組成物であってよい。
　本実施形態の電池は、正極、負極、及び正極と負極との間に配置された電解質を含む。当該電解質は、本実施形態の電解質組成物を含んでいてもよい。例えば、リチウムイオン電池の場合、正極としては特に限定されず、正極活物質を含み、且つ必要に応じて導電助剤、結合剤等を含むものであってよい。
　正極は、これらの材料を含む層が集電体上に形成されたものであってよい。正極活物質としては、例えば、リチウム（Ｌｉ）と、Ｖ、Ｃｒ、Ｍｎ、Ｆｅ、Ｃｏ、Ｎｉ、Ｃｕ、Ａｌからなる群から選択される少なくとも１種の遷移金属とを含むリチウム含有複合金属酸化物が挙げられる。このようなリチウム複合金属酸化物としては、例えば、ＬｉＣｏＯ２、ＬｉＮｉＯ２、ＬｉＭｎ２Ｏ４、Ｌｉ２ＭｎＯ３、ＬｉＮｉｘＭｎｙＣｏ１－ｘ－ｙＯ２［０＜ｘ＋ｙ＜１］）、ＬｉＮｉｘＣｏｙＡｌ１－ｘ－ｙＯ２［０＜ｘ＋ｙ＜１］）、ＬｉＣｒ０．５Ｍｎ０．５Ｏ２、ＬｉＦｅＰＯ４、Ｌｉ２ＦｅＰ２Ｏ７、ＬｉＭｎＰＯ４、ＬｉＦｅＢＯ３、Ｌｉ３Ｖ２（ＰＯ４）３、Ｌｉ２ＣｕＯ２、Ｌｉ２ＦｅＳｉＯ４、Ｌｉ２ＭｎＳｉＯ４などが挙げられる。
　リチウムイオン電池の負極としては特に限定されず、負極活物質を含み、且つ必要に応じて導電助剤、結合剤等を含むものであってよい。例えば、Ｌｉ、Ｓｉ、Ｐ、Ｓｎ、Ｓｉ－Ｍｎ、Ｓｉ－Ｃｏ、Ｓｉ－Ｎｉ、Ｉｎ、Ａｕなどの元素の単体及びこれらの元素を含む合金又は複合体、グラファイト等の炭素材料、当該炭素材料の層間にリチウムイオンが挿入された物質などを挙げることができる。
　リチウムイオン電池はセパレータを有していてもよい。セパレータとしては、多孔質材料であってよく、樹脂製の多孔質材料であってよい。具体的には多孔質ポリオレフィン膜、多孔セラミック膜などが挙げられる。
　電解質組成物の製造方法としては、電解質組成物の各成分を混合できる方法であれば特に限定されないが、電解質組成物の各成分を乳鉢等で混合する方法（固相法）と、電解質組成物の各成分を有機溶媒に溶解及び分散させて前駆体組成物を製造し、当該前駆体組成物から有機溶媒を乾燥等により除去する方法（液相法）が挙げられる。液相法で使用する有機溶媒としては、非プロトン性溶媒であってよく、Ｎ－メチル－２－ピロリドン等が挙げられる。有機溶媒の使用量は、製造される電解質組成物１００質量部に対して２００～２０００質量部であってよく、５００～１５００質量部であってよい。イオン伝導性無機固体電解質には、他成分との混合前に酸処理を行ってもよい。
　本実施形態の電池の製造方法としては、例えば、電解質組成物（電池用コーティング剤）を調製する工程と、電解質組成物を加圧して電解質を製造する工程を備えていてもよい。製造された電解質は正極及び負極の間に配置される。加圧は、電解質組成物を負極若しくは正極上、又は正極及び負極の間に配置して行ってもよい。加圧は、電解質組成物を負極及び正極の間に配置して行ってもよい。加圧の際の圧力は、例えば、１０～３００ＭＰａであってよく、１００～２５０ＭＰａであってよい。加圧は１０℃～６０℃、２０℃～５０℃で行われてよい。
［金属イオンを優先的に伝導する能力を有するポリマーの製造］
　まず、単量体Ａ１を以下のとおり、製造した。
Figure JPOXMLDOC01-appb-C000019
（単量体Ａ１の合成）
　窒素雰囲気下、トリフルオロメタンスルホンアミド（５２．５ｍｍｏｌ、７．８３ｇ、東京化成工業株式会社製）を脱水アセトニトリル（１５０ｍＬ、関東化学株式会社製）に溶解させた。この溶液に水酸化リチウム（１０５ｍｍｏｌ、２．５１ｇ、東京化成工業株式会社製）及び４－アセトアミドベンゼンスルホニルクロリド（５０ｍｍｏｌ、１１．６８ｇ、東京化成工業株式会社製）を順に加えて５時間加熱還流した。室温への冷却後、過剰量のアセトニトリル（７００ｍＬ）を加えて固体を析出させ、ろ過で分離したのちジクロロメタン（関東化学株式会社製）で洗浄し、中間体１を得た。収率は、９７．１％であった。
・中間体１の構造式：
Figure JPOXMLDOC01-appb-C000020
　窒素雰囲気下、中間体１（１５ｍｍｏｌ、５．２８ｇ）に５％塩酸（２２．５ｍＬ）を加え、９０℃で２時間撹拌した。室温への冷却後、ｐＨ試験紙などでの確認のもと、ｐＨが７以上になるまで水酸化リチウム水溶液を加えたのち、減圧乾燥により固体を得た。得られた固体をアセトニトリル溶液にて抽出、減圧乾燥により中間体２を得た。収率は、上記中間体１の原料に基づいて９２．６％であった。
・中間体２の構造式：
Figure JPOXMLDOC01-appb-C000021
　窒素雰囲気下、無水マレイン酸（１３．３ｍｍｏｌ、１．３０ｇ、東京化成工業株式会社製）を脱水１，４－ジオキサン（関東化学株式会社製）に溶解した。この溶液に窒素雰囲気下で調整した中間体２（１３．２ｍｍｏｌ、４．０９ｇ）の脱水テトラヒドロフラン（２６．４ｍＬ、関東化学株式会社製）溶液を全量滴下し、室温で１２時間撹拌した。反応後、析出物をろ過、６０℃で４時間真空乾燥することで中間体３を含む固体を得た。
・中間体３の構造式：
Figure JPOXMLDOC01-appb-C000022
　窒素雰囲気下、中間体３を含む固体（１４．０ｍｍｏｌ、５．７０ｇ）と酢酸ナトリウム水溶液（１３．３ｍｍｏｌ、１．０９ｇ、東京化成工業株式会社製）を無水酢酸（１２．３ｍＬ、東京化成工業株式会社製）に加え、７０℃で３時間撹拌した。反応後の溶液を０℃の過剰量のジエチルエーテル（関東化学株式会社製）に全量滴下し、析出物をろ過にて回収した。不活性雰囲気下にて、析出物を脱水アセトニトリル（関東化学株式会社製）で抽出し、減圧乾燥することで単量体Ａ１を得た。全工程を通した収率は７２．８％であった。
（ポリマー１）
　単量体Ａ１：０．９３６ｇ、ｎ－ドデシルビニルエーテル：１．５３ｇ、ＡＩＢＮ：１６．４ｍｇを脱水アセトニトリル２０ｍＬに溶解させ、内部標準物質としてテトラリンを加えてモノマー消費率を確認しながら、窒素雰囲気下６０℃で２４時間反応させた。重合溶液をアセトニトリル中で透析し、１２０℃で真空乾燥することで、０．６３７ｇ（収率４４％）のポリマー１を得た。モノマー導入比はＡ１：ｎ－ドデシルビニルエーテル＝５５：４５であった。モノマー導入比は共重合体の１Ｈ－ＮＭＲより算出した。なお、ｎ－ドデシルビニルエーテルとしては、アルドリッチ社製の純度＞９８％の市販試薬をＣａＣｌ２と密封して１晩乾燥、ＣａＨ２を加えて減圧蒸留することで純度を向上させ使用した。
　ポリマー１では、数平均分子量Ｍｎ＝４．９×１０４、重量平均分子量Ｍｗ＝７．９×１０４、分子量分布Ｍｗ／Ｍｎ＝１．６３であった。
（ポリマー２）
　単量体Ａ１：１．１７ｇ、テトラエチレングリコールメチルビニルエーテル：２．２５ｇ、ＡＩＢＮ：２４．６ｍｇを脱水アセトニトリル３０ｍＬに溶解させ、内部標準物質としてテトラリンを加えてモノマー消費率を確認しながら、窒素雰囲気下６０℃で２４時間反応させた。重合溶液をアセトニトリル中で透析し、１２０℃で真空乾燥することで、１．４９ｇ（収率７９％）のポリマー２を得た。モノマー導入比はＡ１：テトラエチレングリコールメチルビニルエーテル＝４１：５９であった。モノマー導入比は共重合体の１Ｈ－ＮＭＲより算出した。なお、テトラエチレングリコールメチルビニルエーテルとしては、アルドリッチ社製の純度＞９８％の市販試薬をそのまま使用した。
　ポリマー２では、数平均分子量Ｍｎ＝１．４×１０４、重量平均分子量Ｍｗ＝２．７×１０４、分子量分布Ｍｗ／Ｍｎ＝１．８５であった。
（ポリマー３）
　単量体Ａ１：３．１２１ｇ、スチレン：０．８３３ｇ、ＡＩＢＮ：５７．５ｍｇを脱水アセトニトリル７０ｍＬに溶解させ、内部標準物質としてテトラリンを加えてモノマー消費率を確認しながら、窒素雰囲気下６０℃で２４時間反応させた。重合溶液をアセトニトリル中で透析し、１２０℃で真空乾燥することで、３．５０ｇ（収率８９％）のポリマー３を得た。モノマー導入比はＡ１：スチレン＝５４：４６であった。モノマー導入比は共重合体の１Ｈ－ＮＭＲより算出した。なお、スチレンとしては、アルドリッチ社製の純度＞９８％の市販試薬をＣａＣｌ２と密封して１晩乾燥、ＣａＨ２を加えて減圧蒸留することで純度を向上させ使用した。
　合成されたポリマー３では数平均分子量Ｍｎ＝９．３×１０４、重量平均分子量Ｍｗ＝３．０×１０５、分子量分布Ｍｗ／Ｍｎ＝３．１９であった。
［イオン伝導性無機固体電解質］
　イオン伝導性無機固体電解質としてＬＬＺＴ粉末：株式会社豊島製作所製、Ｌｉ６．６Ｌａ３Ｚｒ１．６Ｔａ０．４Ｏ１２を使用した。
（実施例１）
　６質量部のポリマー１と、１３質量部のエチルメチルイミダゾリウムビスフルオロスルホニルイミド（ＥＭＩＦＳＩ）とを混合し、ゲル状のポリマー組成物を製造した。次いで、８１質量部のＬＬＺＴ粉末と１９質量部のゲル状のポリマー組成物とを、室温（２５℃）、３００ｒｐｍの条件で４時間ボールミルを行うことにより混合物を得た。上記混合物１５０ｍｇを２００ＭＰａの圧力でプレス成型することにより直径１．５ｃｍの電解質組成物を得た（固相法）。
（実施例２）
　ポリマー１をポリマー２に変更したこと以外は実施例１と同様に電解質組成物を製造した。
（実施例３）
　６質量部のポリマー１と、１３質量部のエチルメチルイミダゾリウムビスフルオロスルホニルイミド（ＥＭＩＦＳＩ）と、８１質量部のＬＬＺＴ粉末とを１０００質量部のＮ－メチル－２－ピロリドン中で混合し、乾燥することにより溶媒を除去して混合物を得た。上記混合物１５０ｍｇを２００ＭＰａの圧力でプレス成型することにより直径１．５ｃｍの電解質組成物を得た（液相法）。
（比較例１）
　電解質組成物として１５０ｍｇのＬＬＺＴ粉末を２００ＭＰａの圧力でプレス成型して得た直径１．５ｃｍのペレットを使用した。
（比較例２）
ＬＬＺＴ焼結体：株式会社豊島製作所製、Ｌｉ６．６Ｌａ３Ｚｒ１．６Ｔａ０．４Ｏ１２３Ｎ　Φ１０×０．５ｍｍｔをそのまま使用した。
（比較例３）
　ポリマー１に代えてＡｌｄｒｉｃｈ社製のポリエチレンオキサイド（Ｐｏｌｙ（ｅｔｈｙｌｅｎｅ　ｏｘｉｄｅ）　ａｖｅｒａｇｅ　Ｍｖ　６００，０００，　ｐｏｗｄｅｒ）とリチウムビスフルオロスルホニルイミド（ＬｉＦＳＩ）との混合物（ｍｏｌ比でＯ原子：Ｌｉ原子＝２０：１）を６質量部使用したこと以外は実施例１と同様に電解質組成物を製造した。
＜イオン伝導度の測定＞
　グローブボックス内、乾燥アルゴン雰囲気下にて、コイン型電池ＣＲ２０３２の評価セルを組み立てた。具体的には、評価セル内に以下の順に各層を積層して試験用積層体を作製した。
（ステンレス板／電解質組成物／ステンレス板）
　インピーダンス測定装置を用いて、２５℃、周波数範囲０．１Ｈｚ～１ＭＨｚ、印加電圧１０ｍＶ（ｖｓ．開回路電圧）の条件で測定する。イオン伝導度σは次の式で算出できる。
σ（Ｓ・ｃｍ－１）＝ｔ（ｃｍ）／（Ｒ（Ω）×Ａ（ｃｍ２））
　式中、Ｒは、インピーダンスの値を表す。Ａは、サンプルの面積を表す。ｔは、サンプルの厚さを表す。結果を表１に示す。
＜活性化エネルギーの測定＞
　上記評価セルを用いたイオン伝導度測定を３０、４０、５０、６０、及び７０℃の条件においても実施し、温度に対するイオン伝導度の変化を測定した。イオン伝導度の常用対数値と温度の逆数のグラフの傾きからアレニウスの式（ｌｏｇｋ＝ｌｏｇＡ－Ｅａ／ＲＴ、ｋ：反応速度定数、Ａ：頻度因子、Ｅａ：活性化エネルギー、Ｒ：気体定数、Ｔ：絶対温度）により活性化エネルギーを算出した。結果を表１に示す。
Figure JPOXMLDOC01-appb-T000023
（実施例４及び５）
　表２に記載されるとおり各成分の配合量（重量比）を変更したこと以外は、実施例３と同様に電解質組成物を製造し、２５℃でのイオン伝導度を測定した。
＜ダイナミック硬さの測定＞
　株式会社島津製作所製のナノインデンター　ＤＵＨ－２１１を用いて電解質組成物の機械特性を測定した。ダイナミック硬さは、押し込み深さｈを３μｍとしたときの試験力Ｆの値から以下のように算出された。同様の測定を１サンプルあたり非連続な５点で実施し、平均値を算出した。結果を表２に示す。なお、試験は２５℃において行った。
ダイナミック硬さＤＨ　（Ｎ／ｍｍ２）
ＤＨ＝α×Ｆ／ｈ２×１０３
α＝３．８５８４：圧子形状による定数
Ｆ：試験力　（ｍＮ）
ｈ：押し込み深さ　（μｍ）
Figure JPOXMLDOC01-appb-T000024

Claims (9)

  1. 　イオン伝導性無機固体電解質と、
    　金属イオンを優先的に伝導する能力を有するポリマーと、
    　イオン液体と、を含む、電解質組成物。
  2. 　前記イオン伝導性無機固体電解質はアルカリ金属元素及びアルカリ土類金属の少なくとも一方を含む、酸化物、硫化物、水素化物又はハロゲン化物である、請求項１に記載の電解質組成物。
  3. 　前記イオン伝導性無機固体電解質が、ペロブスカイト型酸化物、ＮＡＳＩＣＯＮ型酸化物、ＬＩＳＩＣＯＮ型酸化物、又はガーネット型酸化物である、請求項２に記載の電解質組成物。
  4. 　前記ポリマーが、アルカリ金属イオンを対カチオンとするアニオン性官能基、及びアニオン捕捉能を有する官能基の少なくとも一方を有する、請求項１又は２に記載の電解質組成物。
  5. 　２５℃におけるイオン伝導度が１０－４Ｓ／ｃｍ以上である、請求項１又は２に記載の電解質組成物。
  6. 　活性化エネルギーが３０ｋＪ／ｍｏｌ以下である、請求項１又は２に記載の電解質組成物。
  7. 　２５℃におけるナノインデンターによる試験結果を用いて下記式から算出したダイナミック硬さＤＨが、１０３Ｎ／ｍｍ２以下である、電解質組成物。
    ＤＨ＝α×Ｆ／ｈ２×１０３
    α＝３．８５８４
    Ｆ：試験力
    ｈ：押し込み深さ
  8. 　請求項１又は２に記載の電解質組成物を含む、電解質。
  9. 　請求項１又は２に記載の電解質組成物を含む、電池。
     
     
PCT/JP2023/034482 2022-09-22 2023-09-22 電解質組成物、電解質、及び電池 Ceased WO2024063158A1 (ja)