WO2023031645A1 - Tôle d'acier laminée à chaud et son procédé de fabrication - Google Patents

Tôle d'acier laminée à chaud et son procédé de fabrication Download PDF

Info

Publication number
WO2023031645A1
WO2023031645A1 PCT/IB2021/057943 IB2021057943W WO2023031645A1 WO 2023031645 A1 WO2023031645 A1 WO 2023031645A1 IB 2021057943 W IB2021057943 W IB 2021057943W WO 2023031645 A1 WO2023031645 A1 WO 2023031645A1
Authority
WO
WIPO (PCT)
Prior art keywords
hot rolled
steel sheet
rolled steel
steel
present
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2021/057943
Other languages
English (en)
Inventor
Dorien DE KNIJF
Tom Waterschoot
Ulrike Lorenz
Lode Duprez
Lieven Bracke
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ArcelorMittal SA
Original Assignee
ArcelorMittal SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to PCT/IB2021/057943 priority Critical patent/WO2023031645A1/fr
Priority to KR1020247009913A priority patent/KR20240056534A/ko
Priority to CN202180101858.5A priority patent/CN117940598A/zh
Priority to JP2024513404A priority patent/JP2024530989A/ja
Priority to EP21773661.0A priority patent/EP4396389A1/fr
Priority to MX2024002449A priority patent/MX2024002449A/es
Application filed by ArcelorMittal SA filed Critical ArcelorMittal SA
Priority to US18/686,951 priority patent/US20240425956A1/en
Priority to CA3229159A priority patent/CA3229159A1/fr
Publication of WO2023031645A1 publication Critical patent/WO2023031645A1/fr
Priority to ZA2024/01170A priority patent/ZA202401170B/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne une tôle d'acier laminée à chaud ayant une composition comprenant des éléments suivants : 0,02 % ≤ carbone ≤ 0,2 %, 3 % ≤ manganèse ≤ 9 %, 0,2 % ≤ silicium ≤ 1,2 %, 0,9 % ≤ aluminium ≤ 2,5 %, 0 % ≤ phosphore ≤ 0,03 %, 0 % ≤ soufre ≤ 0,03 %, 0 % ≤ azote ≤ 0,025 %, 0 % ≤ molybdène ≤ 0,6 %, 0 % ≤ titane ≤ 0,1 %, 0,0001 % ≤ bore ≤ 0,01 %, 0 % ≤ chrome ≤ 0,5 %, 0 % ≤ niobium ≤ 0,1 %, 0 % ≤ vanadium ≤ 0,2 %, 0 % ≤ nickel ≤ 1 %, 0 % ≤ cuivre ≤ 1 %, 0 % ≤ calcium ≤ 0,005 %, 0 % ≤ magnésium ≤ 0,0010 %, la composition restante étant composée de fer et d'impuretés inévitables dues au traitement, la microstructure de ladite tôle d'acier comprenant, en fraction surfacique, au moins 60 % de martensite tempérée, de 15 % à 40 % d'austénite résiduelle, de 0 % à 10 % de ferrite polygonale, de 0 % à 5 % de bainite, de 0 à 15 % de martensite fraîche et de 0 % à 5 % de carbures de niobium, titane, vanadium ou fer.
PCT/IB2021/057943 2021-08-31 2021-08-31 Tôle d'acier laminée à chaud et son procédé de fabrication Ceased WO2023031645A1 (fr)

Priority Applications (9)

Application Number Priority Date Filing Date Title
KR1020247009913A KR20240056534A (ko) 2021-08-31 2021-08-31 열간 압연 강판 및 그 제조 방법
CN202180101858.5A CN117940598A (zh) 2021-08-31 2021-08-31 热轧钢板及其制造方法
JP2024513404A JP2024530989A (ja) 2021-08-31 2021-08-31 熱間圧延鋼板及びその製造方法
EP21773661.0A EP4396389A1 (fr) 2021-08-31 2021-08-31 Tôle d'acier laminée à chaud et son procédé de fabrication
MX2024002449A MX2024002449A (es) 2021-08-31 2021-08-31 Hoja de acero laminada en caliente y metodo de fabricacion de la misma.
PCT/IB2021/057943 WO2023031645A1 (fr) 2021-08-31 2021-08-31 Tôle d'acier laminée à chaud et son procédé de fabrication
US18/686,951 US20240425956A1 (en) 2021-08-31 2021-08-31 Hot rolled and steel sheet and a method of manufacturing thereof
CA3229159A CA3229159A1 (fr) 2021-08-31 2021-08-31 Tole d'acier laminee a chaud et son procede de fabrication
ZA2024/01170A ZA202401170B (en) 2021-08-31 2024-02-06 Hot rolled and steel sheet and a method of manufacturing thereof

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IB2021/057943 WO2023031645A1 (fr) 2021-08-31 2021-08-31 Tôle d'acier laminée à chaud et son procédé de fabrication

Publications (1)

Publication Number Publication Date
WO2023031645A1 true WO2023031645A1 (fr) 2023-03-09

Family

ID=77864616

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2021/057943 Ceased WO2023031645A1 (fr) 2021-08-31 2021-08-31 Tôle d'acier laminée à chaud et son procédé de fabrication

Country Status (9)

Country Link
US (1) US20240425956A1 (fr)
EP (1) EP4396389A1 (fr)
JP (1) JP2024530989A (fr)
KR (1) KR20240056534A (fr)
CN (1) CN117940598A (fr)
CA (1) CA3229159A1 (fr)
MX (1) MX2024002449A (fr)
WO (1) WO2023031645A1 (fr)
ZA (1) ZA202401170B (fr)

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110083774A1 (en) * 2008-05-20 2011-04-14 Posco High Strength Steel Sheet and Hot Dip Galvanized Steel Sheet Having High Ductility and Excellent Delayed Fracture Resistance and Method for Manufacturing the Same
EP2392681A1 (fr) 2009-01-30 2011-12-07 JFE Steel Corporation Tôle forte d'acier laminée à chaud à résistance élevée à la traction présentant une excellente résistance de hic et son procédé de fabrication
EP2971211A1 (fr) 2013-03-15 2016-01-20 ExxonMobil Research and Engineering Company Acier résistant à l'usure perfectionné et ses procédés de fabrication
JP2016194158A (ja) * 2015-04-01 2016-11-17 新日鐵住金株式会社 熱延鋼板及びその製造方法
WO2017208762A1 (fr) * 2016-05-30 2017-12-07 株式会社神戸製鋼所 Tôle d'acier à haute résistance et son procédé de production
CN108950150A (zh) * 2018-08-31 2018-12-07 东北大学 基于完全奥氏体化的超高强度冷轧中锰q&p钢热处理工艺
US20190093191A1 (en) * 2015-10-19 2019-03-28 Jfe Steel Corporation Hot pressed member and method of manufacturing same
WO2019218135A1 (fr) * 2018-05-14 2019-11-21 东北大学 Acier à ultra haute résistance ayant une limite d'élasticité de 1 000 mpa et un faible rapport de limite d'élasticité/résistance à la traction, et son procédé de préparation
US20210115528A1 (en) * 2016-09-22 2021-04-22 Arcelormittal High strength and high formability steel sheet and manufacturing method
WO2021123877A1 (fr) * 2019-12-17 2021-06-24 Arcelormittal Tôle d'acier laminée à chaud et son procédé de fabrication

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH073328A (ja) * 1993-06-18 1995-01-06 Sumitomo Metal Ind Ltd 加工性に優れた高強度熱延鋼板の製造方法
US5470529A (en) * 1994-03-08 1995-11-28 Sumitomo Metal Industries, Ltd. High tensile strength steel sheet having improved formability
JP4062616B2 (ja) * 2002-08-12 2008-03-19 株式会社神戸製鋼所 伸びフランジ性に優れた高強度鋼板
JP5761080B2 (ja) * 2012-03-01 2015-08-12 新日鐵住金株式会社 伸びと穴拡げ性と疲労特性に優れた高強度熱延鋼板及びその製造方法
JP6597374B2 (ja) * 2016-02-18 2019-10-30 日本製鉄株式会社 高強度鋼板
JP6696209B2 (ja) * 2016-02-18 2020-05-20 日本製鉄株式会社 高強度鋼板の製造方法
CN108425070B (zh) * 2018-05-22 2021-01-15 首钢集团有限公司 一种1000MPa级抗冲击波钢板及其制造方法

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110083774A1 (en) * 2008-05-20 2011-04-14 Posco High Strength Steel Sheet and Hot Dip Galvanized Steel Sheet Having High Ductility and Excellent Delayed Fracture Resistance and Method for Manufacturing the Same
EP2392681A1 (fr) 2009-01-30 2011-12-07 JFE Steel Corporation Tôle forte d'acier laminée à chaud à résistance élevée à la traction présentant une excellente résistance de hic et son procédé de fabrication
EP2971211A1 (fr) 2013-03-15 2016-01-20 ExxonMobil Research and Engineering Company Acier résistant à l'usure perfectionné et ses procédés de fabrication
JP2016194158A (ja) * 2015-04-01 2016-11-17 新日鐵住金株式会社 熱延鋼板及びその製造方法
US20190093191A1 (en) * 2015-10-19 2019-03-28 Jfe Steel Corporation Hot pressed member and method of manufacturing same
WO2017208762A1 (fr) * 2016-05-30 2017-12-07 株式会社神戸製鋼所 Tôle d'acier à haute résistance et son procédé de production
US20210115528A1 (en) * 2016-09-22 2021-04-22 Arcelormittal High strength and high formability steel sheet and manufacturing method
WO2019218135A1 (fr) * 2018-05-14 2019-11-21 东北大学 Acier à ultra haute résistance ayant une limite d'élasticité de 1 000 mpa et un faible rapport de limite d'élasticité/résistance à la traction, et son procédé de préparation
CN108950150A (zh) * 2018-08-31 2018-12-07 东北大学 基于完全奥氏体化的超高强度冷轧中锰q&p钢热处理工艺
WO2021123877A1 (fr) * 2019-12-17 2021-06-24 Arcelormittal Tôle d'acier laminée à chaud et son procédé de fabrication

Also Published As

Publication number Publication date
US20240425956A1 (en) 2024-12-26
EP4396389A1 (fr) 2024-07-10
MX2024002449A (es) 2024-03-08
JP2024530989A (ja) 2024-08-27
CA3229159A1 (fr) 2023-03-09
ZA202401170B (en) 2025-02-26
CN117940598A (zh) 2024-04-26
KR20240056534A (ko) 2024-04-30

Similar Documents

Publication Publication Date Title
US20220213573A1 (en) A cold rolled martensitic steel and a method of martensitic steel thereof
WO2014132968A1 (fr) TÔLE D'ACIER LAMINÉE À CHAUD À HAUTE RÉSISTANCE, DOTÉE D'UNE RÉSISTANCE À LA TRACTION MAXIMALE DE 980 MPa OU SUPÉRIEURE ET PRÉSENTANT D'EXCELLENTES TREMPABILITÉ PAR CUISSON ET TÉNACITÉ À BASSES TEMPÉRATURES
WO2020250098A1 (fr) Acier martensitique laminé à froid et procédé d'acier martensitique s'y rapportant
US12509740B2 (en) Hot rolled and steel sheet and a method of manufacturing thereof
JP2023182698A (ja) 熱間圧延鋼及びその製造方法
EP4569150A1 (fr) Acier martensitique laminé à froid et son procédé de production
WO2023031647A1 (fr) Tôle d'acier laminée à chaud et son procédé de fabrication
RU2842345C2 (ru) Горячекатаный стальной лист и способ его изготовления
WO2023031645A1 (fr) Tôle d'acier laminée à chaud et son procédé de fabrication
WO2024013542A1 (fr) Acier laminé à chaud et son procédé de fabrication
WO2025056941A1 (fr) Acier martensitique laminé à froid et procédé d'acier martensitique s'y rapportant
WO2025248287A1 (fr) Tôle d'acier laminée à chaud et son procédé de fabrication
JP2000239783A (ja) 加工性と疲労特性に優れた高強度鋼板
KR20240090672A (ko) 냉연 열처리 강판 및 그 제조 방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21773661

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 202417008964

Country of ref document: IN

WWE Wipo information: entry into national phase

Ref document number: 3229159

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 2401001165

Country of ref document: TH

WWE Wipo information: entry into national phase

Ref document number: 18686951

Country of ref document: US

Ref document number: 202180101858.5

Country of ref document: CN

WWE Wipo information: entry into national phase

Ref document number: 140250140003008329

Country of ref document: IR

Ref document number: 2024513404

Country of ref document: JP

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112024003384

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 20247009913

Country of ref document: KR

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2024108237

Country of ref document: RU

WWE Wipo information: entry into national phase

Ref document number: 2021773661

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2021773661

Country of ref document: EP

Effective date: 20240402

ENP Entry into the national phase

Ref document number: 112024003384

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20240221

WWG Wipo information: grant in national office

Ref document number: 2024108237

Country of ref document: RU