WO2022249762A1 - 固体電解質材料およびそれを用いた電池 - Google Patents

固体電解質材料およびそれを用いた電池 Download PDF

Info

Publication number
WO2022249762A1
WO2022249762A1 PCT/JP2022/016863 JP2022016863W WO2022249762A1 WO 2022249762 A1 WO2022249762 A1 WO 2022249762A1 JP 2022016863 W JP2022016863 W JP 2022016863W WO 2022249762 A1 WO2022249762 A1 WO 2022249762A1
Authority
WO
WIPO (PCT)
Prior art keywords
solid electrolyte
electrolyte material
negative electrode
battery
positive electrode
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/016863
Other languages
English (en)
French (fr)
Inventor
恒星 大浦
智康 横山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Panasonic Intellectual Property Management Co Ltd
Original Assignee
Panasonic Intellectual Property Management Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Panasonic Intellectual Property Management Co Ltd filed Critical Panasonic Intellectual Property Management Co Ltd
Priority to JP2023523335A priority Critical patent/JPWO2022249762A1/ja
Priority to CN202280034724.0A priority patent/CN117413323A/zh
Publication of WO2022249762A1 publication Critical patent/WO2022249762A1/ja
Priority to US18/503,460 priority patent/US20240079645A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本開示の固体電解質材料は、Ｌｉ、Ｍ、Ｉ、およびＸを含む。Ｍは、Ａｌ、Ｇａ、およびＩｎからなる群より選択される少なくとも１種の元素である。Ｘは、Ｆ、Ｏ、およびＳからなる群より選択される少なくとも１種の元素である。本開示の電池１０００は、正極２０１、負極２０３、および正極２０１および負極２０３の間に設けられている電解質層２０２を備える。正極２０１、負極２０３、および電解質層２０２からなる群より選択される少なくとも１つは、本開示の固体電解質材料を含有する。

Description

固体電解質材料およびそれを用いた電池
　本開示は、固体電解質材料およびそれを用いた電池に関する。
　特許文献１は、非水電解液または高分子電解質に含まれるリチウム塩として、Ｌｉ3ＡｌＦ6を開示している。
　非特許文献１および非特許文献２は、固体電解質の原料として、Ｌｉ3ＡｌＦ6を開示している。
特開昭６３－２３９７８１号公報
ECS Electrochemistry Letters, 1 (6) A87-A89 (2012) ACS Appl. Energy Mater., 2, 7196-7203 (2019)
　本開示の目的は、ヨウ素を含む新規な固体電解質材料を提供することにある。
　本開示の固体電解質材料は、Ｌｉ、Ｍ、Ｉ、およびＸを含み、Ｍは、Ａｌ、Ｇａ、およびＩｎからなる群より選択される少なくとも１種の元素であり、Ｘは、Ｆ、Ｏ、およびＳからなる群より選択される少なくとも１種の元素である。
　本開示によれば、ヨウ素を含む新規な固体電解質材料を提供できる。
図１は、第２実施形態による電池１０００の断面図である。 図２は、固体電解質材料のイオン伝導度を評価するために用いられる加圧成形ダイス３００の模式図である。 図３は、実施例１による固体電解質材料のインピーダンス測定により得られたＣｏｌｅ－Ｃｏｌｅプロットを示すグラフである。 図４は、実施例１による電池の初期放電特性を示すグラフである。
　以下、本開示の実施形態が、図面を参照しながら説明される。
　（第１実施形態）
　第１実施形態による固体電解質材料は、Ｌｉ、Ｍ、Ｉ、およびＸを含む。Ｍは、Ａｌ、Ｇａ、およびＩｎからなる群より選択される少なくとも１種の元素である。Ｘは、Ｆ、Ｏ、およびＳからなる群より選択される少なくとも１種の元素である。
　固体電解質材料は、リチウムイオン伝導度の向上に適した固体電解質材料である。第１実施形態による固体電解質材料は、例えば、高いリチウムイオン伝導度を有する。このため、固体電解質材料は、充放電特性に優れた電池を得るために用いられ得る。当該電池の例は、全固体二次電池である。
　ここで、高いリチウムイオン伝導度の一例は、例えば、室温近傍において２．８×１０-5Ｓ／ｃｍ以上である。室温は、例えば、２５℃である。固体電解質材料は、例えば、２．８×１０-5Ｓ／ｃｍ以上のイオン伝導度を有することができる。
　固体電解質材料は、不可避的に混入される元素を含有していてもよい。当該元素の例は、水素、窒素、または酸素である。このような元素は、固体電解質材料の原料粉、または、固体電解質材料を製造あるいは保管するための雰囲気中に存在し得る。固体電解質材料に不可避に混入される元素は、例えば、１モル％以下である。
　固体電解質材料のイオン伝導度を高めるために、固体電解質材料は、実質的に、Ｌｉ、Ｍ、Ｉ、およびＸからなっていてもよい。ここで、「固体電解質材料が、実質的に、Ｌｉ、Ｍ、Ｉ、およびＸからなる」とは、固体電解質材料を構成する全元素の物質量の合計に対する、Ｌｉ、Ｍ、Ｉ、およびＸの物質量の合計のモル比（すなわち、モル分率）が、９０％以上であることを意味する。一例として、当該モル比は、９５％以上であってもよい。
　固体電解質材料のイオン伝導度を高めるために、固体電解質材料は、Ｌｉ、Ｍ、Ｉ、およびＸのみからなっていてもよい。
　固体電解質材料は、以下の組成式（１）により表される材料であってもよい。
　　Ｌｉ1-aＭaＩ(1-b)(1+2a)Ｘb(1+2a)/c　・・・（１）
　ここで、０＜ａ＜１、および０＜ｂ＜１、が充足される。ｃは、Ｘの価数の絶対値を表す。組成式（１）により表される固体電解質材料は、イオン伝導度の向上に適している。
　固体電解質材料のイオン伝導度を高めるために、Ｍは、Ａｌを含んでいてもよい。Ｍは、Ａｌであってもよい。
　固体電解質材料のイオン伝導度を高めるために、Ｘは、Ｆを含んでいてもよい。Ｘは、Ｆであってもよい。
　固体電解質材料のイオン伝導度を高めるために、組成式（１）において、０．３５≦ａ≦０．５、が充足されてもよい。組成式（１）において、０．３５≦ａ≦０．４、が充足されてもよい。
　ａの値の上限値および下限値は、０．３５、０．４、０．４８、および０．５の数値から選ばれる任意の組み合わせによって規定されうる。
　固体電解質材料のイオン伝導度を高めるために、組成式（１）においては、０．０５≦ｂ≦０．６７、が充足されてもよい。組成式（１）においては、０．１５≦ｂ≦０．５、が充足されてもよく、０．１８≦ｂ≦０．５、が充足されてもよい。
　ｂの値の上限値および下限値は、０．０５、０．１、０．１５、０．１８、０．２、０．３３、０．５、および０．６７の数値から選ばれる任意の組み合わせによって規定されうる。
　固体電解質材料は、結晶質であってもよく、あるいは非晶質であってもよい。ここで、結晶質とは、Ｘ線回折パターンにおいてピークが存在することをいう。非晶質とは、Ｘ線回折パターンにおいてブロードなピーク（すなわち、ハロー）が存在することをいう。非晶質と結晶質とが混在している場合には、Ｘ線回折パターンにおいてピークとハローが存在する。
　固体電解質材料の形状は、限定されない。当該形状の例は、針状、球状、または楕円球状である。固体電解質材料は、粒子であってもよい。固体電解質材料は、ペレットまたは板の形状を有していてもよい。
　固体電解質材料の形状が粒子状（例えば、球状）である場合、固体電解質材料は、０．１μｍ以上かつ１００μｍ以下のメジアン径を有していてもよいし、０．５μｍ以上かつ１０μｍ以下のメジアン径を有していてもよい。これにより、固体電解質材料および他の材料が良好に分散し得る。粒子のメジアン径とは、体積基準の粒度分布における累積堆積が５０％に等しい場合の粒径（ｄ５０）を意味する。体積基準の粒度分布は、例えば、レーザー回折式測定装置または画像解析装置により測定される。
　＜固体電解質材料の製造方法＞
　固体電解質材料は、例えば、下記の方法により、製造される。
　目的とする組成を有するように、例えば、ヨウ化物とフッ化物の原料粉が混合される。
　一例として、目的とされる組成がＬｉ0.5Ａｌ0.5Ｉ1.8Ｆ0.2である場合、ＬｉＩ原料粉、ＡｌＩ3原料粉、およびＡｌＦ3原料粉（すなわち、ヨウ化物とフッ化物の原料粉）が、概ねＬｉＩ：ＡｌＩ3：ＡｌＦ3＝１：０．８７：０．１３のモル比で混合される。合成プロセスにおいて生じ得る組成変化を相殺するように、あらかじめ調整されたモル比で原料粉が混合されてもよい。
　ＬｉＩを増やすと、組成式（１）におけるａの値が小さくなる。ＡｌＦ3を増やすと、ｂの値が大きくなる。
　原料として、Ｌｉ金属、Ａｌ金属、Ｉ2、およびＬｉＦ3が用いられてもよい。
　原料粉の混合物を、遊星型ボールミルのような混合装置内でメカノケミカル的に互いに反応させ、反応物を得る。すなわち、メカノケミカルミリングの方法を用いて、原料粉を互いに反応させる。反応物は、真空中または不活性雰囲気中で焼成されてもよい。あるいは、原料粉の混合物を真空中または不活性雰囲気中で焼成し、反応物を得てもよい。不活性雰囲気としては、ヘリウム雰囲気、アルゴン雰囲気、窒素雰囲気などが挙げられる。
　これらの方法により、固体電解質材料が得られる。
　（第２実施形態）
　以下、第２実施形態が説明される。第１実施形態において説明された事項は、適宜、省略され得る。
　第２実施形態による電池は、正極、電解質層、および負極を備える。電解質層は、正極および負極の間に配置されている。正極、電解質層、および負極からなる群より選択される少なくとも１つは、第１実施形態による固体電解質材料を含有する。
　第２実施形態による電池は、第１実施形態による固体電解質材料を含有するため、優れた充放電特性を有する。
　図１は、第２実施形態による電池１０００の断面図である。
　電池１０００は、正極２０１、電解質層２０２、および負極２０３を備える。電解質層２０２は、正極２０１および負極２０３の間に設けられている。
　正極２０１は、正極活物質２０４および固体電解質１００を含有する。
　負極２０３は、負極活物質２０５および固体電解質１００を含有する。
　固体電解質１００は、第１実施形態による固体電解質材料を含む粒子である。固体電解質１００は、第１実施形態による固体電解質材料を主たる成分として含む粒子であってもよい。第１実施形態による固体電解質材料を主たる成分として含む粒子とは、モル比で最も多く含まれる成分が第１実施形態による固体電解質材料である粒子を意味する。固体電解質１００は、第１実施形態による固体電解質材料からなる粒子であってもよい。
　正極２０１は、リチウムイオンのような金属イオンを吸蔵および放出可能な材料を含有する。当該材料は、例えば、正極活物質２０４である。
　正極活物質２０４の例は、リチウム含有遷移金属酸化物、遷移金属フッ化物、ポリアニオン材料、フッ素化ポリアニオン材料、遷移金属硫化物、遷移金属オキシフッ化物、遷移金属オキシ硫化物、または遷移金属オキシ窒化物である。リチウム含有遷移金属酸化物の例は、Ｌｉ（Ｎｉ，Ｃｏ，Ｍｎ）Ｏ2、Ｌｉ（Ｎｉ，Ｃｏ，Ａｌ）Ｏ2、またはＬｉＣｏＯ2である。
　本開示において、「（Ａ，Ｂ，Ｃ）」は、「Ａ、Ｂ、およびＣからなる群より選択される少なくとも１つ」を意味する。
　正極活物質２０４の形状は、特定の形状に限定されない。正極活物質２０４は、粒子であってもよい。正極活物質２０４は、０．１μｍ以上かつ１００μｍ以下のメジアン径を有していてもよい。正極活物質２０４が０．１μｍ以上のメジアン径を有する場合、正極２０１において、正極活物質２０４および固体電解質１００が、良好に分散し得る。これにより、電池１０００の充放電特性が向上する。正極活物質２０４が１００μｍ以下のメジアン径を有する場合、正極活物質２０４内のリチウム拡散速度が向上する。これにより、電池１０００が高出力で動作し得る。
　正極活物質２０４は、固体電解質１００よりも大きいメジアン径を有していてもよい。これにより、正極２０１において、正極活物質２０４および固体電解質１００が良好に分散し得る。
　電池１０００のエネルギー密度および出力を高めるために、正極２０１において、正極活物質２０４の体積および固体電解質１００の体積の合計に対する正極活物質２０４の体積の比は、０．３０以上かつ０．９５以下であってもよい。
　電池１０００のエネルギー密度および出力を高めるために、正極２０１は、１０μｍ以上かつ５００μｍ以下の厚みを有していてもよい。
　電解質層２０２は、電解質材料を含有する。当該電解質材料は、例えば、固体電解質材料である。電解質層２０２は、固体電解質層であってもよい。電解質層２０２は、第１実施形態による固体電解質材料を含有してもよい。
　電解質層２０２は、第１実施形態による固体電解質材料を５０質量％以上含んでいてもよい。電解質層２０２は、第１実施形態による固体電解質材料を７０質量％以上含んでいてもよい。電解質層２０２は、第１実施形態による固体電解質材料を９０質量％以上含んでいてもよい。電解質層２０２は、第１実施形態による固体電解質材料のみからなっていてもよい。
　以下、第１実施形態による固体電解質材料は、第１固体電解質材料という。第１固体電解質材料とは異なる固体電解質材料は、第２固体電解質材料という。
　電解質層２０２は、第１固体電解質材料だけでなく、第２固体電解質材料を含有していてもよい。電解質層２０２において、第１固体電解質材料および第２固体電解質材料は、均一に分散していてもよい。第１固体電解質材料からなる層および第２固体電解質材料からなる層が、電池１０００の積層方向に沿って積層されていてもよい。
　電解質層２０２は、第２固体電解質材料のみからなっていてもよい。
　電解質層２０２は、１μｍ以上かつ１０００μｍ以下の厚みを有していてもよい。電解質層２０２が１μｍ以上の厚みを有する場合、正極２０１および負極２０３が短絡しにくくなる。電解質層２０２が１０００μｍ以下の厚みを有する場合、電池１０００が高出力で動作し得る。
　負極２０３は、リチウムイオンのような金属イオンを吸蔵および放出可能な材料を含有する。当該材料は、例えば、負極活物質２０５である。
　負極活物質２０５の例は、金属材料、炭素材料、酸化物、窒化物、錫化合物、または珪素化合物である。金属材料は、単体の金属であってもよく、あるいは合金であってもよい。金属材料の例は、リチウム金属またはリチウム合金である。炭素材料の例は、天然黒鉛、コークス、黒鉛化途上炭素、炭素繊維、球状炭素、人造黒鉛、または非晶質炭素である。容量密度の観点から、負極活物質の好適な例は、珪素（すなわち、Ｓｉ）、錫（すなわち、Ｓｎ）、珪素化合物、または錫化合物である。
　負極活物質２０５の形状は、特定の形状に限定されない。負極活物質２０５は、粒子であってもよい。負極活物質２０５は、０．１μｍ以上かつ１００μｍ以下のメジアン径を有していてもよい。負極活物質２０５が０．１μｍ以上のメジアン径を有する場合、負極２０３において、負極活物質２０５および固体電解質１００が良好に分散し得る。これにより、電池１０００の充放電特性が向上する。負極活物質２０５が１００μｍ以下のメジアン径を有する場合、負極活物質２０５内のリチウム拡散速度が向上する。これにより、電池１０００が高出力で動作し得る。
　負極活物質２０５は、固体電解質１００よりも大きいメジアン径を有していてもよい。これにより、負極２０３において、負極活物質２０５および固体電解質１００が、良好に分散し得る。
　電池１０００のエネルギー密度および出力を高めるために、負極２０３において、負極活物質２０５の体積および固体電解質１００の体積の合計に対する負極活物質２０５の体積の比は、０．３０以上かつ０．９５以下であってもよい。
　電池１０００のエネルギー密度および出力を高めるために、負極２０３は、１０μｍ以上５００μｍ以下の厚みを有していてもよい。
　正極２０１、電解質層２０２、および負極２０３からなる群より選択される少なくとも１つは、イオン伝導性、化学的安定性、および電気化学的安定性を高める目的で、第２固体電解質材料を含有していてもよい。
　第２固体電解質材料は、ハロゲン化物固体電解質であってもよい。
　ハロゲン化物固体電解質の例は、Ｌｉ2ＭｇＸ’4、Ｌｉ2ＦｅＸ’4、ＬｉＡｌＸ’4、Ｌｉ（Ｇａ，Ｉｎ）Ｘ’4、またはＬｉ3（Ａｌ，Ｇａ，Ｉｎ）Ｘ’6である。ここで、Ｘ’は、Ｆ、Ｃｌ、Ｂｒ、およびＩからなる群より選択される少なくとも１つである。
　ハロゲン化物固体電解質の他の例は、ＬｉpＭｅqＹrＺ6により表される化合物である。ここで、ｐ＋ｍ’ｑ＋３ｒ＝６、およびｒ＞０が充足される。Ｍｅは、ＬｉおよびＹ以外の金属元素と半金属元素とからなる群より選択される少なくとも１つの元素である。Ｚは、Ｆ、Ｃｌ、Ｂｒ、およびＩからなる群より選択される少なくとも１つである。ｍ’の値は、Ｍｅの価数を表す。「半金属元素」は、Ｂ、Ｓｉ、Ｇｅ、Ａｓ、Ｓｂ、およびＴｅである。「金属元素」は、周期表の第１族から第１２族中に含まれる全ての元素（ただし、水素を除く）、および周期表の第１３族から第１６族に含まれる全ての元素（ただし、Ｂ、Ｓｉ、Ｇｅ、Ａｓ、Ｓｂ、Ｔｅ、Ｃ、Ｎ、Ｐ、Ｏ、Ｓ、およびＳｅを除く）である。ハロゲン化物固体電解質のイオン伝導度を高める観点から、Ｍｅは、Ｍｇ、Ｃａ、Ｓｒ、Ｂａ、Ｚｎ、Ｓｃ、Ａｌ、Ｇａ、Ｂｉ、Ｚｒ、Ｈｆ、Ｔｉ、Ｓｎ、Ｔａ、およびＮｂからなる群より選択される少なくとも１つであってもよい。
　第２固体電解質材料は、硫化物固体電解質であってもよい。
　硫化物固体電解質の例は、Ｌｉ2Ｓ－Ｐ2Ｓ5、Ｌｉ2Ｓ－ＳｉＳ2、Ｌｉ2Ｓ－Ｂ2Ｓ3、Ｌｉ2Ｓ－ＧｅＳ2、Ｌｉ3.25Ｇｅ0.25Ｐ0.75Ｓ4、またはＬｉ10ＧｅＰ2Ｓ12である。
　第２固体電解質材料は、酸化物固体電解質であってもよい。
　第２固体電解質材料は、酸化物固体電解質であってもよい。
　酸化物固体電解質の例は、
　（ｉ）ＬｉＴｉ2（ＰＯ4）3またはその元素置換体のようなＮＡＳＩＣＯＮ型固体電解質、（ｉｉ）（ＬａＬｉ）ＴｉＯ3のようなペロブスカイト型固体電解質、（ｉｉｉ）Ｌｉ14ＺｎＧｅ4Ｏ16、Ｌｉ4ＳｉＯ4、ＬｉＧｅＯ4またはその元素置換体のようなＬＩＳＩＣＯＮ型固体電解質、（ｉｖ）Ｌｉ7Ｌａ3Ｚｒ2Ｏ12またはその元素置換体のようなガーネット型固体電解質、または（ｖ）Ｌｉ3ＰＯ4またはそのＮ置換体、である。
　第２固体電解質材料は、有機ポリマー固体電解質であってもよい。
　有機ポリマー固体電解質の例は、高分子化合物およびリチウム塩の化合物である。高分子化合物はエチレンオキシド構造を有していてもよい。エチレンオキシド構造を有する高分子化合物は、リチウム塩を多く含有できるため、イオン伝導度をより高めることができる。
　リチウム塩の例は、ＬｉＰＦ6、ＬｉＢＦ4、ＬｉＳｂＦ6、ＬｉＡｓＦ6、ＬｉＳＯ3ＣＦ3、ＬｉＮ（ＳＯ2ＣＦ3）2、ＬｉＮ（ＳＯ2Ｃ2Ｆ5）2、ＬｉＮ（ＳＯ2ＣＦ3）（ＳＯ2Ｃ4Ｆ9）、またはＬｉＣ（ＳＯ2ＣＦ3）3である。これらから選択される１種のリチウム塩が、単独で使用されてもよい。あるいは、これらから選択される２種以上のリチウム塩の混合物が使用されてもよい。
　正極２０１、電解質層２０２、および負極２０３からなる群より選択される少なくとも１つは、リチウムイオンの授受を容易にし、電池の出力特性を向上する目的で、非水電解質液、ゲル電解質、またはイオン液体を含有していてもよい。
　非水電解液は、非水溶媒および当該非水溶媒に溶けたリチウム塩を含む。
　非水溶媒の例は、環状炭酸エステル溶媒、鎖状炭酸エステル溶媒、環状エーテル溶媒、鎖状エーテル溶媒、環状エステル溶媒、鎖状エステル溶媒、またはフッ素溶媒である。環状炭酸エステル溶媒の例は、エチレンカーボネート、プロピレンカーボネート、またはブチレンカーボネートである。鎖状炭酸エステル溶媒の例は、ジメチルカーボネート、エチルメチルカーボネート、またはジエチルカーボネートである。環状エーテル溶媒の例は、テトラヒドロフラン、１，４－ジオキサン、または１，３－ジオキソランである。鎖状エーテル溶媒の例は、１，２－ジメトキシエタンまたは１，２－ジエトキシエタンである。環状エステル溶媒の例は、γ－ブチロラクトンである。鎖状エステル溶媒の例は、酢酸メチルである。フッ素溶媒の例は、フルオロエチレンカーボネート、フルオロプロピオン酸メチル、フルオロベンゼン、フルオロエチルメチルカーボネート、またはフルオロジメチレンカーボネートである。これらから選択される１種の非水溶媒が、単独で使用されてもよい。あるいは、これらから選択される２種以上の非水溶媒の混合物が使用されてもよい。
　リチウム塩の例は、ＬｉＰＦ6、ＬｉＢＦ4、ＬｉＳｂＦ6、ＬｉＡｓＦ6、ＬｉＳＯ3ＣＦ3、ＬｉＮ（ＳＯ2ＣＦ3）2、ＬｉＮ（ＳＯ2Ｃ2Ｆ5）2、ＬｉＮ（ＳＯ2ＣＦ3）（ＳＯ2Ｃ4Ｆ9）、またはＬｉＣ（ＳＯ2ＣＦ3）3である。これらから選択される１種のリチウム塩が、単独で使用されてもよい。あるいは、これらから選択される２種以上のリチウム塩の混合物が使用されてもよい。リチウム塩の濃度は、例えば、０．５ｍｏｌ／リットル以上２ｍｏｌ／リットル以下である。
　ゲル電解質として、非水電解液を含浸させたポリマー材料が使用され得る。ポリマー材料の例は、ポリエチレンオキシド、ポリアクリルニトリル、ポリフッ化ビニリデン、ポリメチルメタクリレート、またはエチレンオキシド結合を有するポリマーである。
　イオン液体に含まれるカチオンの例は、（ｉ）テトラアルキルアンモニウムまたはテトラアルキルホスホニウムのような脂肪族鎖状４級塩類、（ｉｉ）ピロリジニウム類、モルホリニウム類、イミダゾリニウム類、テトラヒドロピリミジニウム類、ピペラジニウム類、またはピペリジニウム類のような脂肪族環状アンモニウム、または（ｉｉｉ）ピリジニウム類またはイミダゾリウム類のような含窒ヘテロ環芳香族カチオン、である。
　イオン液体に含まれるアニオンの例は、ＰＦ6 -、ＢＦ4 -、ＳｂＦ6 -、ＡｓＦ6 -、ＳＯ3ＣＦ3 -、Ｎ（ＳＯ2ＣＦ3）2 -、Ｎ（ＳＯ2Ｃ2Ｆ5）2 -、Ｎ（ＳＯ2ＣＦ3）（ＳＯ2Ｃ4Ｆ9）-、またはＣ（ＳＯ2ＣＦ3）3 -である。
　イオン液体はリチウム塩を含有してもよい。
　正極２０１、電解質層２０２、および負極２０３からなる群より選択される少なくとも１つは、粒子同士の密着性を向上する目的で、結着剤を含有していてもよい。
　結着剤の例は、ポリフッ化ビニリデン、ポリテトラフルオロエチレン、ポリエチレン、ポリプロピレン、アラミド樹脂、ポリアミド、ポリイミド、ポリアミドイミド、ポリアクリルニトリル、ポリアクリル酸、ポリアクリル酸メチルエステル、ポリアクリル酸エチルエステル、ポリアクリル酸ヘキシルエステル、ポリメタクリル酸、ポリメタクリル酸メチルエステル、ポリメタクリル酸エチルエステル、ポリメタクリル酸ヘキシルエステル、ポリ酢酸ビニル、ポリビニルピロリドン、ポリエーテル、ポリエーテルサルフォン、ヘキサフルオロポリプロピレン、スチレンブタジエンゴム、またはカルボキシメチルセルロースである。共重合体もまた、結着剤として使用され得る。このような結着剤の例は、テトラフルオロエチレン、ヘキサフルオロエチレン、ヘキサフルオロプロピレン、パーフルオロアルキルビニルエーテル、フッ化ビニリデン、クロロトリフルオロエチレン、エチレン、プロピレン、ペンタフルオロプロピレン、フルオロメチルビニルエーテル、アクリル酸、およびヘキサジエンからなる群より選択される２種以上の材料の共重合体である。上記の材料から選択される２種以上の混合物が、結着剤として使用されてもよい。
　正極２０１および負極２０３から選択される少なくとも１つは、電子伝導性を高める目的で、導電助剤を含有していてもよい。
　導電助剤の例は、（ｉ）天然黒鉛または人造黒鉛のようなグラファイト類、（ｉｉ）アセチレンブラックまたはケッチェンブラックのようなカーボンブラック類、（ｉｉｉ）炭素繊維または金属繊維のような導電性繊維類、（ｉｖ）フッ化カーボン、（ｖ）アルミニウムのような金属粉末類、（ｖｉ）酸化亜鉛またはチタン酸カリウムのような導電性ウィスカー類、（ｖｉｉ）酸化チタンのような導電性金属酸化物、または（ｖｉｉｉ）ポリアニリン、ポリピロール、またはポリチオフェンのような導電性高分子化合物、である。低コスト化のために、上記（ｉ）または（ｉｉ）の導電助剤が使用されてもよい。
　第２実施形態による電池の形状の例は、コイン型、円筒型、角型、シート型、ボタン型、扁平型、または積層型である。
　以下、実施例および比較例を参照しながら、本開示がより詳細に説明される。
　（実施例１）
　（固体電解質材料の作製）
　－６０℃以下の露点を有するアルゴン雰囲気（以下、「乾燥アルゴン雰囲気」という）中で、原料粉としてＬｉＩ、ＡｌＩ3、およびＡｌＦ3が、ＬｉＩ：ＡｌＩ3：ＡｌＦ3＝１：０．８７：０．１３のモル比となるように用意された。これらの原料粉が乳鉢中で粉砕され、混合された。このようにして、混合粉が得られた。混合粉は、遊星型ボールミルを用い、１２時間、５００回転／分（ｒｐｍ）でミリング処理された。このようにして、実施例１による固体電解質材料の粉末が得られた。実施例１による固体電解質材料は、Ｌｉ0.5Ａｌ0.5Ｉ1.8Ｆ0.2により表される組成を有していた。
　実施例１による固体電解質材料の単位重量あたりのＬｉ含有量が、原子吸光分析法により測定された。実施例１による固体電解質材料のＡｌ含有量およびＩ含有量が、高周波誘導結合プラズマ発光分光分析法により測定された。これらの測定結果から得られたＬｉ、Ａｌ、およびＩの含有量をもとに、Ｌｉ：Ａｌ：Ｉのモル比が算出された。その結果、実施例１による固体電解質材料は、原料粉のモル比と同様に、Ｌｉ：Ａｌ：Ｉ＝１：１：３．６のモル比を有していた。
　（イオン伝導度の評価）
　図２は、固体電解質材料のイオン伝導度を評価するために用いられた加圧成形ダイス３００を示す模式図である。
　加圧成形ダイス３００は、パンチ上部３０１、枠型３０２、およびパンチ下部３０３を具備していた。パンチ上部３０１およびパンチ下部３０３は、いずれも、電子伝導性のステンレスから形成されていた。枠型３０２は、絶縁性のポリカーボネートから形成されていた。
　図２に示される加圧成形ダイス３００を用いて、下記の方法により、実施例１による固体電解質材料のイオン伝導度が測定された。
　－３０℃以下の露点を有するドライ雰囲気中で、実施例１による固体電解質材料の粉末（すなわち、図２において固体電解質材料の粉末１０１）が加圧成形ダイス３００の内部に充填された。加圧成形ダイス３００の内部で、実施例１による固体電解質材料の粉末１０１に、パンチ上部３０１およびパンチ下部３０３を用いて、３００ＭＰａの圧力が印加された。
　圧力が印加されたまま、パンチ上部３０１およびパンチ下部３０３が、周波数応答アナライザが搭載されたポテンショスタット（Ｐｒｉｎｃｅｔｏｎ　Ａｐｐｌｉｅｄ　Ｒｅｓｅａｒｃｈ社、ＶｅｒｓａＳＴＡＴ４）に接続された。パンチ上部３０１は、作用極および電位測定用端子に接続された。パンチ下部３０３は、対極および参照極に接続された。固体電解質材料のインピーダンスは、室温において、電気化学インピーダンス測定法により測定された。
　図３は、実施例１による固体電解質材料のインピーダンス測定により得られたＣｏｌｅ－Ｃｏｌｅプロットを示すグラフである。図３において、縦軸はインピーダンスの虚数成分を示し、横軸はインピーダンスの実数成分を示す。
　図３において、複素インピーダンスの位相の絶対値が最も小さい測定点でのインピーダンスの実数値が、固体電解質材料のイオン伝導に対する抵抗値とみなされた。当該実数値については、図３において示される矢印Ｒseを参照せよ。当該抵抗値を用いて、以下の数式（２）に基づいて、イオン伝導度が算出された。
　σ＝（Ｒse×Ｓ／ｔ）-1　・・・（２）
　ここで、σは、イオン伝導度を表す。Ｓは、固体電解質材料のパンチ上部３０１との接触面積を表す。Ｓは、図２において、枠型３０２の中空部の断面積を表す。Ｒseは、インピーダンス測定における固体電解質材料の抵抗値を表す。ｔは、固体電解質材料の厚みを表す。ｔは、図２において、固体電解質材料の粉末１０１から形成される層の厚みを表す。
　２２℃で測定された、実施例１による固体電解質材料のイオン伝導度は、３．２×１０-5Ｓ／ｃｍであった。
　（電池の作製）
　乾燥アルゴン雰囲気中で、実施例１による固体電解質材料、Ｌｉ4Ｔｉ5Ｏ12、およびカーボンファイバー（ＶＧＣＦ）が、６５：３０：５の重量比となるように用意された。これらの材料は、乳鉢中で混合された。このようにして、混合物が得られた。なお、「ＶＧＣＦ」は、昭和電工株式会社の登録商標である。
　９．５ｍｍの内径を有する絶縁性の筒の中で、アルジロダイト型硫化物固体電解質であるＬｉ6ＰＳ5Ｃｌ（８０ｍｇ）、実施例１による固体電解質材料（２０ｍｇ）、上記の混合物（１８ｍｇ）、およびＶＧＣＦ（２ｍｇ）が、この順に積層された。この積層体に７４０ＭＰａの圧力が印加され、固体電解質層および第１電極が形成された。
　次に、固体電解質層に、金属Ｉｎ箔、金属Ｌｉ箔、および金属Ｉｎ箔が、この順に積層された。この積層体に４０ＭＰａの圧力が印加され、第２電極が形成された。
　次に、ステンレス鋼から形成された集電体が第１電極および第２電極に取り付けられ、当該集電体に集電リードが取り付けられた。
　最後に、絶縁性フェルールを用いて、絶縁性の筒の内部が外気雰囲気から遮断され、当該筒の内部が密閉された。このようにして、実施例１による電池が得られた。
　（充放電試験）
　図４は、実施例１による電池の初期放電特性を示すグラフである。図４において、縦軸は電圧を示し、横軸は容量を示す。初期放電特性は、下記の方法により、測定された。
　実施例１による電池は、８５℃の恒温槽に配置された。
　６７μＡ／ｃｍ2の電流密度で、０．６０Ｖの電圧に達するまで、実施例１による電池が充電された。当該電流密度は、０．０５Ｃレートに相当する。
　次いで、６７μＡ／ｃｍ2の電流密度で、１．０５Ｖの電圧に達するまで、実施例１による電池が放電された。
　充放電試験の結果、実施例１による電池は、８７１μＡｈの初期放電容量を有していた。
　（実施例２から９）
　（固体電解質材料の作製）
　実施例２では、原料粉として、ＬｉＩ、ＡｌＩ3、およびＡｌＦ3が、ＬｉＩ：ＡｌＩ3：ＡｌＦ3＝１：０．５６：０．４４のモル比となるように用意された。
　実施例３では、原料粉として、ＬｉＩ、ＡｌＩ3、およびＡｌＦ3が、ＬｉＩ：ＡｌＩ3：ＡｌＦ3＝１：０．３３：０．６７のモル比となるように用意された。
　実施例４では、原料粉として、ＬｉＩ、ＡｌＩ3、およびＡｌＦ3が、ＬｉＩ：ＡｌＩ3：ＡｌＦ3＝１：０．１１：０．８９のモル比となるように用意された。
　実施例５では、原料粉として、ＬｉＩ、Ｌｉ2Ｏ、およびＡｌＩ3が、ＬｉＩ：Ｌｉ2Ｏ：ＡｌＩ3＝０．９：０．１：１のモル比となるように用意された。
　実施例６では、原料粉として、ＬｉＩ、Ｌｉ2Ｏ、およびＡｌＩ3が、ＬｉＩ：Ｌｉ2Ｏ：ＡｌＩ3＝０．５：０．５：１のモル比となるように用意された。
　実施例７では、原料粉として、ＬｉＩ、Ｌｉ2Ｏ、およびＡｌＩ3が、ＬｉＩ：Ｌｉ2Ｏ：ＡｌＩ3＝０．７：０．３：０．７のモル比となるように用意された。
　実施例８では、原料粉として、ＬｉＩ、Ｌｉ2Ｓ、およびＡｌＩ3が、ＬｉＩ：Ｌｉ2Ｓ：ＡｌＩ3＝０．９：０．１：１のモル比となるように用意された。
　実施例９では、原料粉として、ＬｉＩ、Ｌｉ2Ｓ、およびＡｌＩ3が、ＬｉＩ：Ｌｉ2Ｓ：ＡｌＩ3＝０．５：０．５：１のモル比となるように用意された。
　上記の事項以外は、実施例１と同様にして、実施例２から９による固体電解質材料が得られた。
　（イオン伝導度の評価）
　実施例２から９による固体電解質材料のイオン伝導度が、実施例１と同様に測定された。測定結果は、表１に示される。
　（充放電試験）
　実施例２から９による固体電解質材料が用いられ、実施例１と同様にして、実施例２から９による電池が得られた。実施例２から９による電池は、実施例１による電池と同様に、良好に充電および放電された。
　（比較例１から８）
　（固体電解質材料の作製）
　比較例１から８による固体電解質材料として、Ｌｉ3ＡｌＦ6、ＬｉＡｌＩ4、Ｌｉ0.5Ａｌ0.5Ｉ1.8Ｃｌ0.2、Ｌｉ0.5Ａｌ0.5Ｉ1.34Ｃｌ0.66、Ｌｉ0.5Ａｌ0.5ＩＣｌ、Ｌｉ0.5Ａｌ0.5Ｉ1.8Ｂｒ0.2、Ｌｉ0.5Ａｌ0.5Ｉ1.34Ｂｒ0.66、およびＬｉ0.5Ａｌ0.5ＩＢｒが用意された。
　（イオン伝導度の評価）
　比較例１から８による固体電解質材料のイオン伝導度は、実施例１と同様に測定された。測定結果は、表１に示される。
Figure JPOXMLDOC01-appb-T000001
　（考察）
　表１から明らかなように、実施例１から９による固体電解質材料は、室温近傍において、２．８×１０-5Ｓ／ｃｍ以上の高いイオン伝導度を有する。
　ＧａおよびＩｎは、Ａｌと同族元素の関係にある。そのため、ＭがＧａまたはＩｎを含む場合であっても、同様の効果を期待できる。
　固体電解質材料が結晶質である場合、イオン伝導度と固体電解質材料の結晶構造との間には相関があると考えられている。一方、固体電解質材料が非晶質である場合、イオン伝導度と固体電解質材料の配位多面体構造との間には相関があると考えられている。ここで、ＭがＧａまたはＩｎを含む固体電解質材料は、ＭがＡｌを含む固体電解質材料と同様の結晶構造および配位多面体構造を有し得る。そのため、ＭがＧａまたはＩｎを含む場合であっても、イオン伝導度の向上の効果を期待できる。
　全ての実施例１から９による電池は、室温において充電および放電された。
　以上のように、本開示による固体電解質材料は、リチウムイオン伝導度を向上させ得る材料であり、かつ良好に充電および放電可能な電池を提供するために適切である。
　本開示の固体電解質材料は、例えば、全固体リチウムイオン二次電池等の電池において利用される。
１００　固体電解質
１０１　固体電解質材料の粉末
２０１　正極
２０２　電解質層
２０３　負極
２０４　正極活物質
２０５　負極活物質
３００　加圧成形ダイス
３０１　パンチ上部
３０２　枠型
３０３　パンチ下部
１０００　電池

Claims (9)

  1. 　Ｌｉ、Ｍ、Ｉ、およびＸを含み、
    　Ｍは、Ａｌ、Ｇａ、およびＩｎからなる群より選択される少なくとも１種の元素であり、
    　Ｘは、Ｆ、Ｏ、およびＳからなる群より選択される少なくとも１種の元素である、
    固体電解質材料。
  2. 　以下の組成式（１）により表され、
    　　Ｌｉ1-aＭaＩ(1-b)(1+2a)Ｘb(1+2a)/c　・・・（１）
    　ここで、０＜ａ＜１、および０＜ｂ＜１、が充足され、
    　ｃは、Ｘの価数の絶対値を表す、
    請求項１に記載の固体電解質材料。
  3. 　Ｍは、Ａｌを含む、
    請求項２に記載の固体電解質材料。
  4. 　Ｘは、Ｆを含む、
    請求項２または３に記載の固体電解質材料。
  5. 　前記組成式（１）において、０．３５≦ａ≦０．５、が充足される、
    請求項２から４のいずれか一項に記載の固体電解質材料。
  6. 　前記組成式（１）において、０．３５≦ａ≦０．４、が充足される、
    請求項５に記載の固体電解質材料。
  7. 　前記組成式（１）において、０．０５≦ｂ≦０．６７、が充足される、
    請求項２から６のいずれか一項に記載の固体電解質材料。
  8. 　前記組成式（１）において、０．１５≦ｂ≦０．５、が充足される、
    請求項７に記載の固体電解質材料。
  9. 　正極、
    　負極、および
    　前記正極および前記負極の間に配置されている電解質層、
    を備え、
    　前記正極、前記負極、および前記電解質層からなる群より選択される少なくとも１つは、請求項１から８のいずれか一項に記載の固体電解質材料を含有する、
    電池。
PCT/JP2022/016863 2021-05-26 2022-03-31 固体電解質材料およびそれを用いた電池 Ceased WO2022249762A1 (ja)