WO2022118625A1 - 負極及び亜鉛二次電池 - Google Patents

負極及び亜鉛二次電池 Download PDF

Info

Publication number
WO2022118625A1
WO2022118625A1 PCT/JP2021/041469 JP2021041469W WO2022118625A1 WO 2022118625 A1 WO2022118625 A1 WO 2022118625A1 JP 2021041469 W JP2021041469 W JP 2021041469W WO 2022118625 A1 WO2022118625 A1 WO 2022118625A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
ldh
secondary battery
nonionic water
particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2021/041469
Other languages
English (en)
French (fr)
Inventor
央 松林
壮太 清水
英一 平山
紗那 岩井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NGK Insulators Ltd
Original Assignee
NGK Insulators Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NGK Insulators Ltd filed Critical NGK Insulators Ltd
Priority to JP2022566811A priority Critical patent/JP7641990B2/ja
Priority to DE112021004624.1T priority patent/DE112021004624T5/de
Priority to KR1020237012910A priority patent/KR102920436B1/ko
Priority to CN202180069600.1A priority patent/CN116391289A/zh
Publication of WO2022118625A1 publication Critical patent/WO2022118625A1/ja
Priority to US18/194,684 priority patent/US20230261251A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

亜鉛二次電池のサイクル寿命を長くすることを可能とする負極が提供される。この負極は、亜鉛二次電池に用いられるものであって、ＺｎＯ粒子及びＺｎ粒子を含む負極活物質と、ノニオン性吸水ポリマーとを含み、ＺｎＯ粒子の少なくとも一部がノニオン性吸水ポリマーで覆われている。

Description

負極及び亜鉛二次電池
　本発明は、負極及び亜鉛二次電池に関するものである。
　ニッケル亜鉛二次電池、空気亜鉛二次電池等の亜鉛二次電池では、充電時に負極から金属亜鉛がデンドライト状に析出し、不織布等のセパレータの空隙を貫通して正極に到達し、その結果、短絡を引き起こすことが知られている。このような亜鉛デンドライトに起因する短絡は繰り返し充放電寿命の短縮を招く。
　上記問題に対処すべく、水酸化物イオンを選択的に透過させながら、亜鉛デンドライトの貫通を阻止する、層状複水酸化物（ＬＤＨ）セパレータを備えた電池が提案されている。例えば、特許文献１（国際公開第２０１３／１１８５６１号）には、ニッケル亜鉛二次電池においてＬＤＨセパレータを正極及び負極間に設けることが開示されている。また、特許文献２（国際公開第２０１６／０７６０４７号）には、樹脂製外枠に嵌合又は接合されたＬＤＨセパレータを備えたセパレータ構造体が開示されており、ＬＤＨセパレータがガス不透過性及び／又は水不透過性を有する程の高い緻密性を有することが開示されている。また、この文献にはＬＤＨセパレータが多孔質基材と複合化されうることも開示されている。さらに、特許文献３（国際公開第２０１６／０６７８８４号）には多孔質基材の表面にＬＤＨ緻密膜を形成して複合材料を得るための様々な方法が開示されている。この方法は、多孔質基材にＬＤＨの結晶成長の起点を与えうる起点物質を均一に付着させ、原料水溶液中で多孔質基材に水熱処理を施してＬＤＨ緻密膜を多孔質基材の表面に形成させる工程を含むものである。
　ところで、亜鉛二次電池の短寿命化を招く別の要因として、負極活物質である亜鉛の形態変化が挙げられる。すなわち、充放電の繰り返しにより亜鉛が溶解及び析出を繰り返すにつれて、負極が形態変化して、気孔の閉塞による高抵抗化、孤立亜鉛の蓄積による充電活物質の減少等を生じ、その結果、充放電が困難になるとの問題がある。この問題に対処すべく、特許文献４（国際公開第２０２０／０４９９０２号）には、ＺｎＯ粒子と、（ｉ）所定粒径の金属Ｚｎ粒子、（ｉｉ）所定の金属元素及び（ｉｉｉ）ヒドロキシル基を有するバインダー樹脂から選択される少なくとも２つとを組み合わせて負極に用いることが提案されている。この負極によれば、亜鉛二次電池において、充放電の繰り返しに伴う負極の劣化を抑制して耐久性を向上し、それによりサイクル寿命を長くすることができるとされている。
　また、特許文献５（特許第６１９０１０１号公報）には、金属Ｚｎ、ＺｎＯ等の負極活物質と、芳香族基含有ポリマー、エーテル基含有ポリマー、水酸基含有ポリマー等のポリマーと、Ｂ、Ｂａ、Ｂｉ、Ｂｒ、Ｃａ、Ｃｄ、Ｃｅ、Ｃｌ、Ｆ、Ｇａ、Ｈｇ、Ｉｎ、Ｌａ、Ｍｎ等の元素の化合物である導電助剤とを含む、負極合材が開示されており、電極活物質のシェイプチェンジやデンドライトといった電極活物質の形態変化、溶解、腐食や不動態形成を抑制したうえで、高いサイクル特性、レート特性、クーロン効率等の電池性能を発現する蓄電池の形成に適することが記載されている。
国際公開第２０１３／１１８５６１号 国際公開第２０１６／０７６０４７号 国際公開第２０１６／０６７８８４号 国際公開第２０２０／０４９９０２号 特許第６１９０１０１号公報
　しかしながら、既存の亜鉛二次電池の充放電サイクル性能は必ずしも十分なものとはいえず、充放電サイクル性能の更なる改善が求められている。
　本発明者らは、今般、Ｚｎ粒子及びＺｎＯ粒子とともにノニオン性吸水ポリマーを含み、かつ、ＺｎＯ粒子の少なくとも一部がノニオン性吸水ポリマーで覆われた合材を負極に用いることにより、サイクル寿命を長くすることができるとの知見を得た。
　したがって、本発明の目的は、亜鉛二次電池のサイクル寿命を長くすることを可能とする負極を提供することにある。
　本発明の一態様によれば、亜鉛二次電池に用いられる負極であって、
　ＺｎＯ粒子及びＺｎ粒子を含む負極活物質と、
　ノニオン性吸水ポリマーと、
を含み、前記ＺｎＯ粒子の少なくとも一部が前記ノニオン性吸水ポリマーで覆われている、負極が提供される。
　本発明の他の一態様によれば、
　正極と、
　前記負極と、
　前記正極と前記負極とを水酸化物イオン伝導可能に隔離するセパレータと、
　電解液と、
を含む、亜鉛二次電池が提供される。
本発明の負極における、ノニオン性吸水ポリマーで一部が覆われたＺｎＯ粒子の一例を示す模式断面図である。 本発明による負極の充電反応時に起きる現象の推定メカニズムを説明するための概念図であり、充電初期の状態を示す図である。 本発明による負極の充電反応時に起きる現象の推定メカニズムを説明するための概念図であり、図２Ａに続く充電中期の状態を示す図である。 本発明による負極の充電反応時に起きる現象の推定メカニズムを説明するための概念図であり、図２Ｂに続く充電後期の状態を示す図である。 本発明による負極の放電反応時に起きる現象の推定メカニズムを説明するための概念図であり、放電開始時の状態を示す図である。 本発明による負極の放電反応時に起きる現象の推定メカニズムを説明するための概念図であり、図３Ａに続く放電進行時の状態を示す図である。 ノニオン性吸水ポリマー１ｃｍ３当たりの、水の吸液量及びＫＯＨ捕集量と、ＫＯＨ濃度との関係の一例を示すグラフである。 例５における負極の断面をＦＥ－ＳＥＭにより観察した画像である。 図５に示される負極の断面におけるＥＤＸ元素マッピング画像である。 例１（比較）における負極の断面をＦＥ－ＳＥＭにより観察した画像である。 例６における負極の断面をＦＥ－ＳＥＭにより観察した画像である。
　負極
　本発明の負極は亜鉛二次電池に用いられる負極である。この負極は、負極活物質と、ノニオン性吸水ポリマーとを含む。負極活物質は、ＺｎＯ粒子及びＺｎ粒子を含む。図１に本発明の負極におけるＺｎＯ粒子及びノニオン性吸水ポリマーの一態様を示す。図１に示されるように、本発明による負極は、ＺｎＯ粒子１２の少なくとも一部がノニオン性吸水ポリマー１４で覆われている。このようにＺｎ粒子及びＺｎＯ粒子１２とともにノニオン性吸水ポリマー１４を含み、かつ、ＺｎＯ粒子１２の少なくとも一部がノニオン性吸水ポリマー１４で覆われた合材を負極に用いることにより、サイクル寿命を長くすることができる。
　前述のとおり、従来の負極においては、充放電の繰り返しにより亜鉛が溶解及び析出を繰り返すにつれて、負極が形態変化して、気孔の閉塞による高抵抗化、孤立亜鉛の蓄積による充電活物質の減少等を生じ、その結果、充放電が困難になるとの問題がある。かかる問題が、ＺｎＯ粒子の少なくとも一部を覆うようにノニオン性吸水ポリマーを負極に加えることで効果的に抑制又は解決される。そのメカニズムは必ずしも定かではないが、ノニオン性吸水ポリマーの添加によって、充電反応及び放電反応がそれぞれ均一化されることで、亜鉛の偏析ないし蓄積が抑制されることによるものと考えられる。
　すなわち、充電反応時においては、ＺｎＯ＋Ｈ２Ｏ＋２ｅ－→Ｚｎ＋２ＯＨ－に基づき負極での反応が進行する。そして、充電反応の進行に伴って、集電体に近い負極内部のＯＨ－濃度がセパレータに近い負極表面のＯＨ－濃度と比べて高くなる。その結果、負極表面での上記反応が進む一方、負極内部での反応が鈍化することになる。このように、従来の負極では充電反応が不均一となり、これにより亜鉛が偏析するものと考えられる。一方、本発明の負極１０においては、図１に示されるように、ＺｎＯ粒子１２の少なくとも一部がノニオン性吸水ポリマー１４で覆われている。この点、ノニオン性吸水ポリマー１４はイオン透過性を有しないため、ＺｎＯ粒子１２の反応可能部分１２ａがノニオン性吸水ポリマー１４と接していない部分に限定される。このようにＺｎＯ粒子１２の反応可能部分１２ａが限定されることにより、充電反応が均一化するものと考えられる。具体的には、本発明の負極１０における充電反応は以下のように進行するものと推測される。ここで、充電初期、充電中期及び充電後期における負極の反応を図２Ａ～２Ｃにそれぞれ示す。まず、図２Ａに示される充電初期においては、負極１０周辺のＯＨ－濃度が低いため、負極１０の内部（集電体１６に近い部分）及び表面（集電体１６から遠い部分）に関わらず全体的に反応が進む。そして、図２Ｂに示される充電中期においては、前述のとおり集電体１６に近い負極１０内部のＯＨ－濃度が上昇するため、負極１０内部での反応が鈍化し、ＯＨ－濃度が低い負極１０表面での反応が優先的に進む。一方、図２Ｃに示される充電後期においては、ＺｎＯ粒子１２がノニオン性吸水ポリマー１４によって覆われていることで、負極１０表面の反応可能部分が減少する。これにより、再び負極１０内部での反応が進むことになり、充電反応が均一化される。その結果、亜鉛の偏析が抑制されて、サイクル寿命を長くすることができるものと考えられる。
　また、放電反応時においては、Ｚｎ＋２ＯＨ－→ＺｎＯ＋Ｈ２Ｏ＋２ｅ－に基づき負極での反応が進行する。そして、放電反応の進行に伴って、集電体に近い負極内部のＯＨ－濃度がセパレータに近い負極表面と比べて低くなり、負極内部での反応が鈍化する。このため、従来の負極では反応が不均一化し、亜鉛が蓄積するものと考えられる。これに対して、本発明の負極１０においては、ノニオン性吸水ポリマー１４が好都合に水を吸収することで負極１０内部の反応継続に寄与する。ここで、本発明の負極１０における、放電反応の開始時及び進行時におけるノニオン性吸水ポリマー１４の吸液能を示す概念図を図３Ａ及び３Ｂにそれぞれ示す。図３Ａに示されるように、放電反応の開始時においては、電解液１８中のＯＨ－濃度が高いため、負極１０の表面及び内部に関わらず上記放電反応が進行する。そして、放電反応の進行に伴って水が生成されるとともに、電解液１８中のＯＨ－濃度が低下する（すなわちｐＨが低下する）。この点、図３Ｂに示されるように、ｐＨの低下に伴い、ノニオン性吸水ポリマー１４はその吸液能が増加して、負極活物質で生成する水を吸収することで上記放電反応がアシストされる。つまり、水が生成される放電反応に対してノニオン性吸水ポリマー１４が好都合に水を吸収することで、負極１０内部においても放電反応が継続され、放電反応が均一化される。その結果、亜鉛の蓄積が抑制されて、サイクル寿命を長くすることができるものと考えられる。なお、上述した本発明による有利な効果は、ノニオン性吸水ポリマー１４を選択したことによる特有の効果である。事実、イオン性吸収ポリマー（例えばポリアクリル酸やポリアクリル酸カリウム）を添加した場合には上述の効果は得られず、むしろサイクル特性は低下する。
　負極活物質は、Ｚｎ粒子（図示せず）及びＺｎＯ粒子１２を含む。Ｚｎ粒子は、典型的には金属Ｚｎ粒子であるが、Ｚｎ合金やＺｎ化合物の粒子を用いてもよい。金属Ｚｎ粒子は、亜鉛二次電池に一般的に使用される金属Ｚｎ粒子が使用可能であるが、それよりも小さい金属Ｚｎ粒子の使用が電池のサイクル寿命を長くする観点からより好ましい。具体的には、金属Ｚｎ粒子の平均粒径Ｄ５０は、好ましくは５～２００μｍであり、より好ましくは５０～２００μｍであり、さらに好ましくは７０～１６０μｍである。負極１０におけるＺｎ粒子の好ましい含有量は、ＺｎＯ粒子１２の含有量を１００重量部とした場合に、１．０～８７．５重量部であるのが好ましく、より好ましくは３．０～７０．０重量部、さらに好ましくは５．０～５５．０重量部である。金属Ｚｎ粒子にはＩｎ、Ｂｉ等のドーパントがドープされていてもよい。ＺｎＯ粒子１２は亜鉛二次電池に用いられる市販の酸化亜鉛粉末、もしくはそれらを出発原料として用いて固相反応等により粒成長させた酸化亜鉛粉末を用いればよく特に限定されない。ＺｎＯ粒子１２の平均粒径Ｄ５０は、好ましくは０.１～２０μｍであり、より好ましくは０．１～１０μｍ、さらに好ましくは０.１～５μｍである。なお、本明細書において、平均粒径Ｄ５０は、レーザー回折・散乱法によって得られる粒度分布において小粒径側からの積算体積が５０％になる粒径を意味するものとする。
　負極１０は、Ｉｎ及びＢｉから選択される１種以上の金属元素をさらに含むのが好ましい。これらの金属元素は負極１０の自己放電による望ましくない水素ガスの発生を抑制することができる。これらの金属元素は、金属、酸化物、水酸化物、その他の化合物等のいかなる形態で負極１０に含まれてもよいが、酸化物又は水酸化物の形態で含まれるのが好ましく、より好ましくは酸化物粒子の形態で含まれる。上記金属元素の酸化物の例としては、Ｉｎ２Ｏ３、Ｂｉ２Ｏ３等が挙げられる。上記金属元素の水酸化物の例としては、Ｉｎ（ＯＨ）３、Ｂｉ（ＯＨ）３等が挙げられる。いずれにしても、ＺｎＯ粒子１２の含有量を１００重量部とした場合に、Ｉｎの含有量が酸化物換算で０～２重量部であり、かつ、Ｂｉの含有量が酸化物換算で０～６重量部であるのが好ましく、より好ましくはＩｎの含有量が酸化物換算で０～１．５重量部であり、かつ、Ｂｉの含有量が酸化物換算で０～４．５重量部である。Ｉｎ及び／又はＢｉが酸化物又は水酸化物の形態で負極１０に含まれる場合、Ｉｎ及び／又はＢｉの全てが酸化物又は水酸化物の形態である必要は無く、それらの一部が金属又は他の化合物等の他の形態で負極に含まれていてもよい。例えば、上記金属元素が金属Ｚｎ粒子に微量元素としてドープされていてもよい。この場合、金属Ｚｎ粒子中のＩｎ濃度は好ましくは５０～２０００重量ｐｐｍ、より好ましくは２００～１５００重量ｐｐｍ、金属Ｚｎ粒子中のＢｉ濃度は好ましくは５０～２０００重量ｐｐｍ、より好ましくは１００～１３００重量ｐｐｍである。
　ノニオン性吸水ポリマー１４は、市販の任意のノニオン性吸水ポリマーであることができるが、上述したように、ｐＨの変動に応じて吸液性が変化する特性を有するものであるのが好ましい。図４に、そのようなノニオン性吸水ポリマー１ｃｍ３当たりの、水の吸液量及びＫＯＨ捕集量と、ＫＯＨ濃度との関係の一例を示す。図４に示されるように、電解液中のＫＯＨ濃度の変化（すなわちｐＨの変化）により水の吸液量は変化するが、ＫＯＨの捕集量は大きく変化しないものが、ｐＨ変動により水のみを吸収ないし放出できる点で好ましい。特に、ｐＨの上昇に伴い水の吸液量が減少する挙動を示すものが好ましい。そのようなノニオン性吸水ポリマー１４の好ましい例としては、ポリアルキレンオキサイド系吸水性樹脂、ポリビニルアセトアミド系吸水性樹脂、ポリビニルアルコール（ＰＶＡ樹脂）、及びポリビニルブチラール（ＰＶＢ樹脂）が挙げられ、より好ましくはポリアルキレンオキサイド系吸水性樹脂である。ポリアルキレンオキサイド系吸水性樹脂としては市販のものが使用可能である。ノニオン性吸水ポリマー１４には、親水性のエーテル基、水酸基、アミド基、及びアセトアミド基から選択される少なくとも１種が含まれていてもよい。これら官能基の存在により、より電池反応に好ましい吸放水性機能を得ることができる。
　負極１０において、ノニオン性吸水ポリマー１４は、ＺｎＯ粒子１２の少なくとも一部を覆っている。すなわち、ノニオン性吸水ポリマー１４は、図１に示されるようにＺｎＯ粒子１２表面の一部を覆うものであってもよいし、ＺｎＯ粒子１２の表面全体を覆うものであってもよい。また、ノニオン性吸水ポリマー１４は、ＺｎＯ粒子１２のみならず、Ｚｎ粒子の少なくとも一部を覆うものであってもよい。ノニオン性吸水ポリマー１４によるＺｎＯ粒子１２の被覆率は２～９９％であるのが好ましく、より好ましくは４～７５％、さらに好ましくは１６～７５％、特に好ましくは４９～７５％、最も好ましくは５５～６８％である。本発明において、ＺｎＯ粒子１２の被覆率とは、負極１０の断面を画像解析した場合に、ＺｎＯ粒子１２の外周部の長さに占める、ＺｎＯ粒子１２とノニオン性吸水ポリマー１４とが接する部分の長さの割合（％）を意味する。ＺｎＯ粒子１２の被覆率の算出は、後述する実施例の評価２に示される手順に従って好ましく行うことができる。
　ＺｎＯ粒子１２にノニオン性吸水ポリマー１４を被覆させる手法は特に限定されない。例えば、以下に示す（ａ）～（ｄ）のいずれかの方法を用いることにより、ＺｎＯ粒子１２をノニオン性吸水ポリマー１４で好ましく被覆することができる。
（ａ）Ｚｎ粒子、ＺｎＯ粒子１２、ノニオン性吸水ポリマー１４、及びバインダー（例えばポリテトラフルオロエチレン）を含む混合粉末を作製する。この混合粉末を溶媒（例えばプロピレングリコール、イソプロピルアルコール）と共に所定温度（例えばノニオン性吸水ポリマー１４の融点以上の温度）で加熱混練する。
（ｂ）ノニオン性吸水ポリマー１４を所定温度の溶媒に溶解させる。ノニオン性吸水ポリマー１４が溶解した溶媒をＺｎＯ粒子及びＺｎ粒子に添加し、ポットミル等で混合後、乾燥させることによりポリマー被覆粉末とする。その後、得られたポリマー被覆粉末及びバインダー樹脂を溶媒と共に混練する。
（ｃ）Ｚｎ粒子、ＺｎＯ粒子１２、及びバインダー樹脂を含む混合粉末に対して、ノニオン性吸水ポリマー１４を溶媒に溶解させた状態で添加し、その後これらを混練する。
（ｄ）得られた負極１０をノニオン性吸水ポリマー１４の融点以上の温度で密閉加熱する。
　ノニオン性吸水ポリマーの融点は、好ましくは４５℃～３５０℃、より好ましくは４５℃～２００℃、さらに好ましくは５０℃～１００℃である。また、負極１０におけるノニオン性吸水ポリマー１４の含有量は、ＺｎＯ粒子１２の含有量を１００重量部とした場合に、固形分で０．０１～６．０重量部であるのが好ましく、より好ましくは０．０１～５．０重量部、さらに好ましくは０．５～４．５重量部、特に好ましくは１．５～４．５重量部である。
　負極１０は導電助剤をさらに含んでいてもよい。導電助剤の例としては、カーボン、金属粉末（錫、鉛、銅、コバルト等）、及び貴金属ペーストが挙げられる。
　負極１０はバインダー樹脂（図示せず）をさらに含んでいてもよい。負極１０がバインダーを含むことで、負極形状を保持しやすくなる。バインダー樹脂は公知の様々なバインダーが使用可能であるが、好ましい例としては、ポリビニルアルコール（ＰＶＡ）、ポリテトラフルオロエチレン（ＰＴＦＥ）が挙げられる。ＰＶＡ及びＰＴＦＥの両方を組み合わせてバインダーとして用いるのが特に好ましい。
　負極１０はシート状のプレス成形体であるのが好ましい。こうすることで、負極活物質の脱落防止や電極密度の向上を図ることができ、負極１０の形態変化をより効果的に抑制することができる。かかるシート状のプレス成形体の作製は、負極材料にバインダーを加えて混練し、得られた混練物にロールプレス等のプレス成形を施してシート状に成形すればよい。ＺｎＯ粒子１２にノニオン性吸水ポリマー１４を被覆させる好ましい混練方法に関しては上述したとおりである。
　負極１０には集電体１６が設けられるのが好ましい。集電体１６の好ましい例としては、銅パンチングメタルや銅エキスパンドメタルが挙げられる。この場合、例えば、銅パンチングメタルや銅エキスパンドメタル上に、Ｚｎ粒子、ＺｎＯ粒子１２、ノニオン性吸水ポリマー１４、及び所望によりバインダー樹脂（例えばポリテトラフルオロエチレン粒子）を含む混合物を塗布して負極１０／集電体１６からなる負極板を好ましく作製することができる。その際、乾燥後の負極板（すなわち負極１０／集電体１６）にプレス処理を施して、負極活物質の脱落防止や電極密度の向上を図ることも好ましい。あるいは、上述したようなシート状のプレス成形体を銅エキスパンドメタル等の集電体１６に圧着してもよい。
　亜鉛二次電池
　本発明の負極１０は亜鉛二次電池に適用されるのが好ましい。したがって、本発明の好ましい態様によれば、正極（図示せず）と、負極１０と、正極と負極１０とを水酸化物イオン伝導可能に隔離するセパレータと、電解液１８とを含む、亜鉛二次電池が提供される。本発明の亜鉛二次電池は、上述した負極１０を用い、かつ、電解液１８（典型的にはアルカリ金属水酸化物水溶液）を用いた二次電池であれば特に限定されない。したがって、ニッケル亜鉛二次電池、酸化銀亜鉛二次電池、酸化マンガン亜鉛二次電池、亜鉛空気二次電池、その他各種のアルカリ亜鉛二次電池であることができる。例えば、正極が水酸化ニッケル及び／又はオキシ水酸化ニッケルを含み、それにより亜鉛二次電池がニッケル亜鉛二次電池をなすのが好ましい。あるいは、正極が空気極であり、それにより亜鉛二次電池が亜鉛空気二次電池をなしてもよい。
　セパレータは層状複水酸化物（ＬＤＨ）セパレータであるのが好ましい。すなわち、前述したように、ニッケル亜鉛二次電池や空気亜鉛二次電池の分野において、ＬＤＨセパレータが知られており（特許文献１～３を参照）、このＬＤＨセパレータを本発明の亜鉛二次電池にも好ましく使用することができる。ＬＤＨセパレータは、水酸化物イオンを選択的に透過させながら、亜鉛デンドライトの貫通を阻止することができる。本発明の負極の採用による効果と相まって、亜鉛二次電池の耐久性をより一層向上することができる。なお、本明細書において、ＬＤＨセパレータは、層状複水酸化物（ＬＤＨ）及び／又はＬＤＨ様化合物（以下、水酸化物イオン伝導層状化合物と総称する）を含むセパレータであって、専ら水酸化物イオン伝導層状化合物の水酸化物イオン伝導性を利用して水酸化物イオンを選択的に通すものとして定義される。本明細書において「ＬＤＨ様化合物」は、ＬＤＨとは呼べないかもしれないがＬＤＨに類する層状結晶構造の水酸化物及び／又は酸化物であり、ＬＤＨの均等物といえるものである。もっとも、広義の定義として、「ＬＤＨ」はＬＤＨのみならずＬＤＨ様化合物を包含するものとして解釈することも可能である。
　ＬＤＨセパレータは、特許文献１～３に開示されるように多孔質基材と複合化されたものであってもよい。多孔質基材はセラミックス材料、金属材料、及び高分子材料のいずれで構成されてもよいが、高分子材料で構成されるのが特に好ましい。高分子多孔質基材には、１）フレキシブル性を有する（それ故薄くしても割れにくい）、２）気孔率を高くしやすい、３）伝導率を高くしやすい（気孔率を高めながら厚さを薄くできるため）、４）製造及びハンドリングしやすいといった利点がある。特に好ましい高分子材料は、耐熱水性、耐酸性及び耐アルカリ性に優れ、しかも低コストである点から、ポリプロピレン、ポリエチレン等のポリオレフィンであり、最も好ましくはポリプロピレンである。多孔質基材が高分子材料で構成される場合、水酸化物イオン伝導層状化合物が多孔質基材の厚さ方向の全域にわたって組み込まれている（例えば多孔質基材内部の大半又はほぼ全部の孔が水酸化物イオン伝導層状化合物で埋まっている）のが特に好ましい。この場合における高分子多孔質基材の好ましい厚さは、５～２００μｍであり、より好ましくは５～１００μｍ、さらに好ましくは５～３０μｍである。このような高分子多孔質基材として、リチウム電池用セパレータとして市販されているような微多孔膜を好ましく用いることができる。
　電解液１８は、アルカリ金属水酸化物水溶液を含むのが好ましい。アルカリ金属水酸化物の例としては、水酸化カリウム、水酸化ナトリウム、水酸化リチウム、水酸化アンモニウム等が挙げられるが、水酸化カリウムがより好ましい。亜鉛含有材料の自己溶解を抑制するために、電解液中に酸化亜鉛、水酸化亜鉛等を添加してもよい。
　ＬＤＨ様化合物
　本発明の好ましい態様によれば、ＬＤＨセパレータは、ＬＤＨ様化合物を含むものであることができる。ＬＤＨ様化合物の定義は前述したとおりである。好ましいＬＤＨ様化合物は、
（ａ）Ｍｇと、Ｔｉ、Ｙ及びＡｌからなる群から選択される少なくともＴｉを含む１以上の元素とを含む層状結晶構造の水酸化物及び／又は酸化物である、又は
（ｂ）（ｉ）Ｔｉ、Ｙ、及び所望によりＡｌ及び／又はＭｇと、（ｉｉ）Ｉｎ、Ｂｉ、Ｃａ、Ｓｒ及びＢａからなる群から選択される少なくとも１種である添加元素Ｍとを含む、層状結晶構造の水酸化物及び／又は酸化物である、又は
（ｃ）Ｍｇ、Ｔｉ、Ｙ、及び所望によりＡｌ及び／又はＩｎを含む層状結晶構造の水酸化物及び／又は酸化物であり、該（ｃ）において前記ＬＤＨ様化合物がＩｎ（ＯＨ）３との混合物の形態で存在する。
　本発明の好ましい態様（ａ）によれば、ＬＤＨ様化合物は、Ｍｇと、Ｔｉ、Ｙ及びＡｌからなる群から選択される少なくともＴｉを含む１以上の元素とを含む層状結晶構造の水酸化物及び／又は酸化物でありうる。したがって、典型的なＬＤＨ様化合物は、Ｍｇ、Ｔｉ、所望によりＹ及び所望によりＡｌの複合水酸化物及び／又は複合酸化物である。ＬＤＨ様化合物の基本的特性を損なわない程度に上記元素は他の元素又はイオンで置き換えられてもよいが、ＬＤＨ様化合物はＮｉを含まないのが好ましい。例えば、ＬＤＨ様化合物は、Ｚｎ及び／又はＫをさらに含むものであってもよい。こうすることで、ＬＤＨセパレータのイオン伝導率をより一層向上することができる。
　ＬＤＨ様化合物はＸ線回折により同定することができる。具体的には、ＬＤＨセパレータは、その表面に対してＸ線回折を行った場合、典型的には５°≦２θ≦１０°の範囲に、より典型的には７°≦２θ≦１０°の範囲にＬＤＨ様化合物に由来するピークが検出される。前述のとおり、ＬＤＨは積み重なった水酸化物基本層の間に、中間層として交換可能な陰イオン及びＨ２Ｏが存在する交互積層構造を有する物質である。この点、ＬＤＨをＸ線回折法により測定した場合、本来的には２θ＝１１～１２°の位置にＬＤＨの結晶構造に起因したピーク（すなわちＬＤＨの（００３）ピーク）が検出される。これに対して、ＬＤＨ様化合物をＸ線回折法により測定した場合、典型的にはＬＤＨの上記ピーク位置よりも低角側にシフトした上述の範囲でピークが検出される。また、Ｘ線回折におけるＬＤＨ様化合物に由来するピークに対応する２θを用いてＢｒａｇｇの式により、層状結晶構造の層間距離を決定することができる。こうして決定されるＬＤＨ様化合物を構成する層状結晶構造の層間距離は０．８８３～１．８ｎｍであるのが典型的であり、より典型的には０．８８３～１．３ｎｍである。
　上記態様（ａ）によるＬＤＨセパレータは、エネルギー分散型Ｘ線分析（ＥＤＳ）により決定される、ＬＤＨ様化合物におけるＭｇ／（Ｍｇ＋Ｔｉ＋Ｙ＋Ａｌ）の原子比が０．０３～０．２５であるのが好ましく、より好ましくは０．０５～０．２である。また、ＬＤＨ様化合物におけるＴｉ／（Ｍｇ＋Ｔｉ＋Ｙ＋Ａｌ）の原子比は０．４０～０．９７であるのが好ましく、より好ましくは０．４７～０．９４である。さらに、ＬＤＨ様化合物におけるＹ／（Ｍｇ＋Ｔｉ＋Ｙ＋Ａｌ）の原子比は０～０．４５であるのが好ましく、より好ましくは０～０．３７である。そして、ＬＤＨ様化合物におけるＡｌ／（Ｍｇ＋Ｔｉ＋Ｙ＋Ａｌ）の原子比は０～０．０５であるのが好ましく、より好ましくは０～０．０３である。上記範囲内であると、耐アルカリ性により一層優れ、かつ、亜鉛デンドライトに起因する短絡の抑制効果（すなわちデンドライト耐性）をより効果的に実現することができる。ところで、ＬＤＨセパレータに関して従来から知られるＬＤＨは一般式：Ｍ２＋ １－ｘＭ３＋ ｘ（ＯＨ）２Ａｎ－ ｘ／ｎ・ｍＨ２Ｏ（式中、Ｍ２＋は２価の陽イオン、Ｍ３＋は３価の陽イオンであり、Ａｎ－はｎ価の陰イオン、ｎは１以上の整数、ｘは０．１～０．４であり、ｍは０以上である）なる基本組成で表しうる。これに対して、ＬＤＨ様化合物における上記原子比は、ＬＤＨの上記一般式から概して逸脱している。このため、本態様におけるＬＤＨ様化合物は、概して、従来のＬＤＨとは異なる組成比（原子比）を有するといえる。なお、ＥＤＳ分析は、ＥＤＳ分析装置（例えばＸ－ａｃｔ、オックスフォード・インストゥルメンツ社製）を用いて、１）加速電圧２０ｋＶ、倍率５，０００倍で像を取り込み、２）点分析モードで５μｍ程度間隔を空け、３点分析を行い、３）上記１）及び２）をさらに１回繰り返し行い、４）合計６点の平均値を算出することにより行うのが好ましい。
　本発明の別の好ましい態様（ｂ）によれば、ＬＤＨ様化合物は、（ｉ）Ｔｉ、Ｙ、及び所望によりＡｌ及び／又はＭｇと、（ｉｉ）添加元素Ｍとを含む、層状結晶構造の水酸化物及び／又は酸化物でありうる。したがって、典型的なＬＤＨ様化合物は、Ｔｉ、Ｙ、添加元素Ｍ、所望によりＡｌ及び所望によりＭｇの複合水酸化物及び／又は複合酸化物である。添加元素Ｍは、Ｉｎ、Ｂｉ、Ｃａ、Ｓｒ、Ｂａ又はそれらの組合せである。ＬＤＨ様化合物の基本的特性を損なわない程度に上記元素は他の元素又はイオンで置き換えられてもよいが、ＬＤＨ様化合物はＮｉを含まないのが好ましい。
　上記態様（ｂ）によるＬＤＨセパレータは、エネルギー分散型Ｘ線分析（ＥＤＳ）により決定される、ＬＤＨ様化合物におけるＴｉ／（Ｍｇ＋Ａｌ＋Ｔｉ＋Ｙ＋Ｍ）の原子比が０．５０～０．８５であるのが好ましく、より好ましくは０．５６～０．８１である。ＬＤＨ様化合物におけるＹ／（Ｍｇ＋Ａｌ＋Ｔｉ＋Ｙ＋Ｍ）の原子比は０．０３～０．２０であるのが好ましく、より好ましくは０．０７～０．１５である。ＬＤＨ様化合物におけるＭ／（Ｍｇ＋Ａｌ＋Ｔｉ＋Ｙ＋Ｍ）の原子比は０．０３～０．３５であるのが好ましく、より好ましくは０．０３～０．３２である。ＬＤＨ様化合物におけるＭｇ／（Ｍｇ＋Ａｌ＋Ｔｉ＋Ｙ＋Ｍ）の原子比は０～０．１０であるのが好ましく、より好ましくは０～０．０２である。そして、ＬＤＨ様化合物におけるＡｌ／（Ｍｇ＋Ａｌ＋Ｔｉ＋Ｙ＋Ｍ）の原子比は０～０．０５であるのが好ましく、より好ましくは０～０．０４である。上記範囲内であると、耐アルカリ性により一層優れ、かつ、亜鉛デンドライトに起因する短絡の抑制効果（すなわちデンドライト耐性）をより効果的に実現することができる。ところで、ＬＤＨセパレータに関して従来から知られるＬＤＨは一般式：Ｍ２＋ １－ｘＭ３＋ ｘ（ＯＨ）２Ａｎ－ ｘ／ｎ・ｍＨ２Ｏ（式中、Ｍ２＋は２価の陽イオン、Ｍ３＋は３価の陽イオンであり、Ａｎ－はｎ価の陰イオン、ｎは１以上の整数、ｘは０．１～０．４であり、ｍは０以上である）なる基本組成で表しうる。これに対して、ＬＤＨ様化合物における上記原子比は、ＬＤＨの上記一般式から概して逸脱している。このため、本態様におけるＬＤＨ様化合物は、概して、従来のＬＤＨとは異なる組成比（原子比）を有するといえる。なお、ＥＤＳ分析は、ＥＤＳ分析装置（例えばＸ－ａｃｔ、オックスフォード・インストゥルメンツ社製）を用いて、１）加速電圧２０ｋＶ、倍率５，０００倍で像を取り込み、２）点分析モードで５μｍ程度間隔を空け、３点分析を行い、３）上記１）及び２）をさらに１回繰り返し行い、４）合計６点の平均値を算出することにより行うのが好ましい。
　本発明の更に別の好ましい態様（ｃ）によれば、ＬＤＨ様化合物は、Ｍｇ、Ｔｉ、Ｙ、及び所望によりＡｌ及び／又はＩｎを含む層状結晶構造の水酸化物及び／又は酸化物であり、ＬＤＨ様化合物がＩｎ（ＯＨ）３との混合物の形態で存在するものでありうる。この態様のＬＤＨ様化合物は、Ｍｇ、Ｔｉ、Ｙ、及び所望によりＡｌ及び／又はＩｎを含む、層状結晶構造の水酸化物及び／又は酸化物である。したがって、典型的なＬＤＨ様化合物は、Ｍｇ、Ｔｉ、Ｙ、所望によりＡｌ、及び所望によりＩｎの、複合水酸化物及び／又は複合酸化物である。なお、ＬＤＨ様化合物に含まれうるＩｎは、ＬＤＨ様化合物中に意図的に添加されたもののみならず、Ｉｎ（ＯＨ）３の形成等に由来してＬＤＨ様化合物中に不可避的に混入したものであってもよい。ＬＤＨ様化合物の基本的特性を損なわない程度に上記元素は他の元素又はイオンで置き換えられてもよいが、ＬＤＨ様化合物はＮｉを含まないのが好ましい。ところで、ＬＤＨセパレータに関して従来から知られるＬＤＨは一般式：Ｍ２＋ １－ｘＭ３＋ ｘ（ＯＨ）２Ａｎ－ ｘ／ｎ・ｍＨ２Ｏ（式中、Ｍ２＋は２価の陽イオン、Ｍ３＋は３価の陽イオンであり、Ａｎ－はｎ価の陰イオン、ｎは１以上の整数、ｘは０．１～０．４であり、ｍは０以上である）なる基本組成で表しうる。これに対して、ＬＤＨ様化合物における原子比は、ＬＤＨの上記一般式から概して逸脱している。このため、本態様におけるＬＤＨ様化合物は、概して、従来のＬＤＨとは異なる組成比（原子比）を有するといえる。
　上記態様（ｃ）による混合物はＬＤＨ様化合物のみならずＩｎ（ＯＨ）３をも含む（典型的にはＬＤＨ様化合物及びＩｎ（ＯＨ）３で構成される）。Ｉｎ（ＯＨ）３の含有により、ＬＤＨセパレータにおける耐アルカリ性及びデンドライト耐性を効果的に向上することができる。混合物におけるＩｎ（ＯＨ）３の含有割合は、ＬＤＨセパレータの水酸化物イオン伝導性を殆ど損なわずに耐アルカリ性及びデンドライト耐性を向上できる量であるのが好ましく、特に限定されない。Ｉｎ（ＯＨ）３はキューブ状の結晶構造を有するものであってもよく、Ｉｎ（ＯＨ）３の結晶がＬＤＨ様化合物で取り囲まれている構成であってもよい。Ｉｎ（ＯＨ）３はＸ線回折により同定することができる。
　本発明を以下の例によってさらに具体的に説明する。
　例１～１２
（１）正極の用意
　ペースト式水酸化ニッケル正極（容量密度：約７００ｍＡｈ／ｃｍ３）を用意した。
（２）負極の作製
　以下に示される各種原料粉末を用意した。
・ＺｎＯ粉末（正同化学工業株式会社製、ＪＩＳ規格１種グレード、平均粒径Ｄ５０：０．２μｍ）
・金属Ｚｎ粉末（ＤＯＷＡエレクトロニクス株式会社製、Ｂｉ及びＩｎがドープされたもの、Ｂｉ：７０重量ｐｐｍ、Ｉｎ：２００重量ｐｐｍ、平均粒径Ｄ５０：１２０μｍ）
・ノニオン性吸水ポリマー（ポリアルキレンオキサイド系吸水性樹脂、住友精化株式会社製、アクアコーク、グレード：ＴＷＢ－Ｐ、製品形態：粉体、平均粒径Ｄ５０：５０μｍ）
・イオン性吸水ポリマー（ポリアクリル酸、住友精化株式会社社製、ＡＱＵＰＥＣ　ＨＶ）
・イオン性吸水ポリマー（ポリアクリル酸カリウム、シグマアルドリッチ社製、Ｐｏｌｙ　ｐａｒｔｉａｌ　ｐｏｔａｓｓｉｕｍ　ｓａｌｔ）
　ＺｎＯ粉末１００重量部に、金属Ｚｎ粉末５．７重量部、ポリテトラフルオロエチレン（ＰＴＦＥ）１重量部、並びに場合によりノニオン性吸水ポリマー又はイオン性吸水ポリマーを表１及び表２に示される配合割合で添加し、プロピレングリコールと共に加熱混練した。こうすることで、ノニオン性吸水ポリマーないしイオン性吸水ポリマーをプロピレングリコールに溶解させながら混練を行った。得られた混練物をロールプレスで圧延して、負極活物質シートを得た。負極活物質シートを、錫メッキが施された銅エキスパンドメタルに圧着して、負極を得た。
（３）電解液の作製
　４８％水酸化カリウム水溶液（関東化学株式会社製、特級）にイオン交換水を加えてＫＯＨ濃度を５．４ｍｏｌ％に調整した後、酸化亜鉛を０．４２ｍｏｌ／Ｌ加熱攪拌により溶解させて、電解液を得た。
（４）評価セルの作製
　正極と負極の各々を不織布で包むとともに、電流取り出し端子を溶接した。こうして準備された正極及び負極を、ＬＤＨセパレータを介して対向させ、電流取り出し口が設けられたラミネートフィルムに挟んで、ラミネートフィルムの３辺を熱融着した。こうして得られた上部開放されたセル容器に電解液を加え、真空引き等により電解液を十分に正極及び負極に浸透させた。その後、ラミネートフィルムの残りの１辺も熱融着して、簡易密閉セルとした。
（５）評価
　評価１：ノニオン性吸水ポリマーの存在状態
　クロスセクションポリッシャ（ＣＰ）により、例１～８の負極を断面研磨し、エネルギー分散型Ｘ線分析装置（ＥＤＸ）を備えた電界放出型走査電子顕微鏡（ＦＥ－ＳＥＭ、日立ハイテク製、Ｓ－４８００）により３００００倍の倍率で負極断面のＦＥ－ＳＥＭ観察及びＥＤＸ観察を行った。例５で取得したＦＥ－ＳＥＭ画像及びＥＤＸ元素マッピング画像を図５及び６にそれぞれ示す。図６に示されるように、ＥＤＸ元素マッピング画像から、負極にＣ及びＦが存在することが確認された。この点、例１～８の負極は樹脂としてノニオン性吸水ポリマー及びＰＴＦＥを含有するところ、ＰＴＦＥはＦを含むため、Ｃのみが検出された部分がノニオン性吸水ポリマーに由来する部分であると考えられる。その結果、ノニオン性吸水ポリマーがＺｎＯ粒子の少なくとも一部を覆う形で存在していることが確認された。
　評価２：被覆率の算出
　例１～８の負極について、電界放出型走査電子顕微鏡（ＦＥ－ＳＥＭ、日本電子株式会社製、ＪＳＭ－７９００Ｍ）により５００００倍の倍率（視野：２．３μｍ×１．６μｍｍ）で、負極断面観察を行った。例１（比較）及び例６で取得した負極断面のＦＥ－ＳＥＭ画像を図７及び８にそれぞれ示す。取得したＦＥ－ＳＥＭ画像を画像処理ソフト（Ａｄｏｂｅ社製、Ａｄｏｂｅ　Ｉｌｌｕｓｔｒａｔｏｒ）に取り込んだ。次いで、視野内に含まれるＺｎＯ粒子の外周部における、ＺｎＯ粒子とノニオン性吸水ポリマーとが接する部分の長さＬ１と、ＺｎＯ粒子と空隙（すなわちノニオン性吸水ポリマーが存在しない箇所）とが接する部分の長さＬ２とを測長した。そして、下記式：
　［Ｌ１／（Ｌ１＋Ｌ２）］×１００
により、ＺｎＯ粒子の外周部の長さに占める、ＺｎＯ粒子とノニオン性吸水ポリマーとが接する部分の長さの割合（％）を求め、ＺｎＯ粒子の被覆率とした。結果は表１に示されるとおりであった。
　評価３：サイクル特性
　充放電装置（東洋システム株式会社製、ＴＯＳＣＡＴ３１００）を用いて、簡易密閉セルに対し、０．１Ｃ充電及び０．２Ｃ放電で化成を実施した。その後、１Ｃ充放電サイクルを実施した。同一条件で繰り返し充放電サイクルを実施し、試作電池の１サイクル目の放電容量の７０％まで放電容量が低下するまでの充放電回数を記録し、これをサイクル特性を示す指標として採用した。結果は表１に示されるとおりであり、ノニオン性吸水ポリマーが所定量添加された負極について、ＺｎＯ粒子がノニオン性吸水ポリマーで被覆されることによりサイクル特性が改善することが確認された。また、表２に示される結果から、イオン性吸収ポリマーを添加した場合には、むしろサイクル特性は低下することが確認された。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002

Claims (15)

  1. 　亜鉛二次電池に用いられる負極であって、
    　ＺｎＯ粒子及びＺｎ粒子を含む負極活物質と、
    　ノニオン性吸水ポリマーと、
    を含み、前記ＺｎＯ粒子の少なくとも一部が前記ノニオン性吸水ポリマーで覆われている、負極。
  2. 　前記ＺｎＯ粒子の被覆率が２～９９％であり、前記被覆率は、前記負極の断面を画像解析した場合に、前記ＺｎＯ粒子の外周部の長さに占める、前記ＺｎＯ粒子と前記ノニオン性吸水ポリマーとが接する部分の長さの割合である、請求項１に記載の負極。
  3. 　前記ＺｎＯ粒子の被覆率が４～７５％である、請求項１又は２に記載の負極。
  4. 　前記ＺｎＯ粒子の含有量を１００重量部とした場合に、前記ノニオン性吸水ポリマーを固形分で０．０１～６．０重量部含む、請求項１～３のいずれか一項に記載の負極。
  5. 　前記ノニオン性吸水ポリマーが、ポリアルキレンオキサイド系吸水性樹脂、ポリビニルアセトアミド系吸水性樹脂、ポリビニルアルコール（ＰＶＡ樹脂）、及びポリビニルブチラール（ＰＶＢ樹脂）からなる群から選択される少なくとも１種である、請求項１～４のいずれか一項に記載の負極。
  6. 　前記ノニオン性吸水ポリマーが、ポリアルキレンオキサイド系吸水性樹脂である、請求項１～５のいずれか一項に記載の負極。
  7. 　前記ノニオン性吸水ポリマーが、ｐＨの変動に応じて吸液性が変化する特性を有する、請求項１～６のいずれか一項に記載の負極。
  8. 　前記ＺｎＯ粒子の含有量を１００重量部とした場合に、前記Ｚｎ粒子を１．０～８７．５重量部含む、請求項１～７のいずれか一項に記載の負極。
  9. 　Ｉｎ及びＢｉから選択される１種以上の金属元素をさらに含む、請求項１～８のいずれか一項に記載の負極。
  10. 　前記負極がシート状のプレス成形体である、請求項１～９のいずれか一項に記載の負極。
  11. 　正極と、
    　請求項１～１０のいずれか一項に記載の負極と、
    　前記正極と前記負極とを水酸化物イオン伝導可能に隔離するセパレータと、
    　電解液と、
    を含む、亜鉛二次電池。
  12. 　前記セパレータが層状複水酸化物（ＬＤＨ）及び／又はＬＤＨ様化合物を含むＬＤＨセパレータである、請求項１１に記載の亜鉛二次電池。
  13. 　前記ＬＤＨセパレータが多孔質基材と複合化されている、請求項１１又は１２に記載の亜鉛二次電池。
  14. 　前記正極が水酸化ニッケル及び／又はオキシ水酸化ニッケルを含み、それにより前記亜鉛二次電池がニッケル亜鉛二次電池をなす、請求項１１～１３のいずれか一項に記載の亜鉛二次電池。
  15. 　前記正極が空気極であり、それにより前記亜鉛二次電池が亜鉛空気二次電池をなす、請求項１１～１３のいずれか一項に記載の亜鉛二次電池。

     
PCT/JP2021/041469 2020-12-03 2021-11-11 負極及び亜鉛二次電池 Ceased WO2022118625A1 (ja)