WO2019225649A1 - Feuille adhésive - Google Patents

Feuille adhésive Download PDF

Info

Publication number
WO2019225649A1
WO2019225649A1 PCT/JP2019/020280 JP2019020280W WO2019225649A1 WO 2019225649 A1 WO2019225649 A1 WO 2019225649A1 JP 2019020280 W JP2019020280 W JP 2019020280W WO 2019225649 A1 WO2019225649 A1 WO 2019225649A1
Authority
WO
WIPO (PCT)
Prior art keywords
pressure
sensitive adhesive
layer
adhesive sheet
adherend
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2019/020280
Other languages
English (en)
Japanese (ja)
Inventor
陽介 清水
哲士 本田
尚史 小坂
大器 下栗
翔 寳田
理仁 丹羽
量子 浅井
昌之 岡本
祐輔 山本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nitto Denko Corp
Original Assignee
Nitto Denko Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corp filed Critical Nitto Denko Corp
Publication of WO2019225649A1 publication Critical patent/WO2019225649A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne une feuille adhésive ayant une couche d'agent adhésif. La couche d'agent adhésif présente une surface adhésive qui peut adhérer à une partie adhérée. La feuille adhésive présente une partie d'alimentation d'agent accroissant la force de décollement : qui est disposée à un emplacement qui est séparé de la surface adhésive par l'intermédiaire d'une partie de surface sur le côté de surface adhésive ; et qui sert à alimenter un agent d'accroissement de la force de décollement à la partie de surface.
PCT/JP2019/020280 2018-05-24 2019-05-22 Feuille adhésive Ceased WO2019225649A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018-099402 2018-05-24
JP2018099402 2018-05-24

Publications (1)

Publication Number Publication Date
WO2019225649A1 true WO2019225649A1 (fr) 2019-11-28

Family

ID=68617005

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/020280 Ceased WO2019225649A1 (fr) 2018-05-24 2019-05-22 Feuille adhésive

Country Status (2)

Country Link
TW (1) TW202003741A (fr)
WO (1) WO2019225649A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021097075A (ja) * 2019-12-13 2021-06-24 日東電工株式会社 半導体加工用粘着シート
WO2022137924A1 (fr) * 2020-12-25 2022-06-30 日東電工株式会社 Structure, feuille adhésive, ensemble et procédé
WO2022202321A1 (fr) * 2021-03-25 2022-09-29 日東電工株式会社 Feuille de protection de surface
CN115151619A (zh) * 2020-02-28 2022-10-04 日东电工株式会社 粘合片及其使用

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017165966A (ja) * 2015-10-07 2017-09-21 大日本印刷株式会社 接着シートセットおよび物品の製造方法

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017165966A (ja) * 2015-10-07 2017-09-21 大日本印刷株式会社 接着シートセットおよび物品の製造方法

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021097075A (ja) * 2019-12-13 2021-06-24 日東電工株式会社 半導体加工用粘着シート
JP7555186B2 (ja) 2019-12-13 2024-09-24 日東電工株式会社 半導体加工用粘着シート
CN115151619A (zh) * 2020-02-28 2022-10-04 日东电工株式会社 粘合片及其使用
WO2022137924A1 (fr) * 2020-12-25 2022-06-30 日東電工株式会社 Structure, feuille adhésive, ensemble et procédé
WO2022202321A1 (fr) * 2021-03-25 2022-09-29 日東電工株式会社 Feuille de protection de surface

Also Published As

Publication number Publication date
TW202003741A (zh) 2020-01-16

Similar Documents

Publication Publication Date Title
JP6864144B2 (ja) 粘着シートおよび粘着シート剥離方法
JP7558649B2 (ja) 光学用粘着剤組成物およびその利用
JP7638618B2 (ja) 積層体および剥離方法
JP7534074B2 (ja) 粘着シートおよびその利用
JP7441012B2 (ja) 粘着シート
WO2021172342A1 (fr) Feuille adhésive et son utilisation
WO2019225649A1 (fr) Feuille adhésive
WO2020218154A1 (fr) Feuille adhésive sensible à la pression et son utilisation
KR102705586B1 (ko) 점착 시트 박리 방법
WO2019151192A1 (fr) Procédé de décollement de feuille adhésive
WO2022202321A1 (fr) Feuille de protection de surface
WO2022201858A1 (fr) Feuille de protection de surface et procédé de traitement
WO2023145360A1 (fr) Feuille de protection de surface et procédé de traitement
WO2022201857A1 (fr) Feuille de protection de surface et procédé de traitement
WO2020262340A1 (fr) Feuille adhésive et son utilisation

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19807469

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19807469

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP