WO2019123161A1 - Ensemble de fermeture de bouteille comprenant un copolymère de polyéthylène ayant de bonnes propriétés organoleptiques - Google Patents

Ensemble de fermeture de bouteille comprenant un copolymère de polyéthylène ayant de bonnes propriétés organoleptiques Download PDF

Info

Publication number
WO2019123161A1
WO2019123161A1 PCT/IB2018/060070 IB2018060070W WO2019123161A1 WO 2019123161 A1 WO2019123161 A1 WO 2019123161A1 IB 2018060070 W IB2018060070 W IB 2018060070W WO 2019123161 A1 WO2019123161 A1 WO 2019123161A1
Authority
WO
WIPO (PCT)
Prior art keywords
bottle
cap portion
tether
molded
cap
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2018/060070
Other languages
English (en)
Inventor
Xiaochuan Wang
Ian Gibbons
Eric Vignola
Cliff Baar
Amin Mirzadeh
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nova Chemicals International SA
Original Assignee
Nova Chemicals International SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nova Chemicals International SA filed Critical Nova Chemicals International SA
Publication of WO2019123161A1 publication Critical patent/WO2019123161A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne des ensembles de fermeture de bouteille qui sont fabriqués au moins en partie avec un copolymère de polyéthylène présentant de bonnes propriétés organoleptiques. L'ensemble de fermeture de bouteille comprend une partie de bouchon, une partie d'attache allongée et une partie de moyen de retenue. La partie de moyen de retenue met en prise un col de bouteille ou une partie supérieure d'une bouteille. La partie d'attache allongée relie au moins un point de la partie de bouchon à au moins un point de la partie de moyen de retenue afin d'empêcher la perte de la partie de bouchon d'une bouteille.
PCT/IB2018/060070 2017-12-19 2018-12-13 Ensemble de fermeture de bouteille comprenant un copolymère de polyéthylène ayant de bonnes propriétés organoleptiques Ceased WO2019123161A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201762607610P 2017-12-19 2017-12-19
US62/607,610 2017-12-19

Publications (1)

Publication Number Publication Date
WO2019123161A1 true WO2019123161A1 (fr) 2019-06-27

Family

ID=65199439

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2018/060070 Ceased WO2019123161A1 (fr) 2017-12-19 2018-12-13 Ensemble de fermeture de bouteille comprenant un copolymère de polyéthylène ayant de bonnes propriétés organoleptiques

Country Status (4)

Country Link
US (1) US20190185219A1 (fr)
AR (1) AR113657A1 (fr)
CA (1) CA3024454A1 (fr)
WO (1) WO2019123161A1 (fr)

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
USD1013512S1 (en) 2019-10-10 2024-02-06 Merrilee Kick Container
TWI798764B (zh) * 2020-08-03 2023-04-11 美商美力肯及公司 熱塑性聚合物組成物及其成型方法
US20220041339A1 (en) 2020-08-07 2022-02-10 Niagara Bottling, Llc Single anchor closure
DE102021106367B3 (de) * 2021-03-16 2021-12-02 Bericap Holding Gmbh Verschlussvorrichtung
US11975889B2 (en) 2021-09-02 2024-05-07 Merrilee Kick Container apparatus

Citations (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3904062A (en) 1973-07-02 1975-09-09 Somepla Sa Tamper-proof and loss-proof screw-type bottle cap
US4474302A (en) 1983-11-03 1984-10-02 James R. Goldberg Safety champagne cork
US4557393A (en) 1984-04-17 1985-12-10 Continental White Cap, Inc. Snap-on cap with tethering strap
US4564114A (en) 1984-12-21 1986-01-14 James R. Goldberg Molded safety closure device
US4573602A (en) 1984-07-10 1986-03-04 Goldberg James R Molded safety closure device and method for making same
US4583652A (en) 1984-07-10 1986-04-22 Goldberg James R Safety closure device
US4805792A (en) 1984-04-17 1989-02-21 Continental White Cap, Inc. Litterless tamper indicating closure
WO1993003093A1 (fr) 1991-07-18 1993-02-18 Exxon Chemical Patents Inc. Article thermosoude
US5292845A (en) 1992-01-23 1994-03-08 Mitsui Petrochemical Industries, Ltd. Ethylene/alpha-olefin/7-methyl-1,6-octadiene copolymer rubber and composition of the same
US5342868A (en) 1991-12-05 1994-08-30 Asahi Denka Kogyo Kabushiki Kaisha Crystalline synthetic resin composition
US5376439A (en) 1992-09-16 1994-12-27 Exxon Chemical Patents Inc. Soft films having enhanced physical properties
US5725115A (en) 1995-02-21 1998-03-10 Crown Cork Ag Closure cap with tether
US5981636A (en) 1996-12-27 1999-11-09 3M Innovative Properties Company Modifying agents for polyolefins
US6465551B1 (en) 2001-03-24 2002-10-15 Milliken & Company Bicyclo[2.2.1]heptane dicarboxylate salts as polyolefin nucleators
US6599971B2 (en) 2001-03-29 2003-07-29 Milliken & Company Metals salts of hexahydrophthalic acid as nucleating additives for crystalline thermoplastics
US20040016715A1 (en) 2000-11-28 2004-01-29 Miran Strikovic Cap for bottle-like containers
WO2005121239A2 (fr) 2004-05-06 2005-12-22 Dow Global Technologies Inc. Compositions polymeres de moulage
US20080197135A1 (en) 2007-02-20 2008-08-21 Berman Ronald H Beverage spout with safety tether
USD593856S1 (en) 2007-01-30 2009-06-09 Kenneth Kubler Bottle cap retainer
WO2011050042A1 (fr) 2009-10-21 2011-04-28 Milliken & Company Composition à base d'un polymère thermoplastique
US8443994B1 (en) 2009-09-09 2013-05-21 Michael C. Desselle Tethered bottle cap assembly with means to retain a detached cap portion
US8720716B2 (en) 2009-06-25 2014-05-13 Phillip John Campbell Closure with spring loaded tether docking
WO2015042561A1 (fr) 2013-09-23 2015-03-26 Milliken & Company Composition de polymère thermoplastique
WO2015042562A1 (fr) 2013-09-23 2015-03-26 Milliken & Company Composition de polymère thermoplastique
WO2015042563A1 (fr) 2013-09-23 2015-03-26 Milliken & Company Composition de polymère thermoplastique
WO2015061834A1 (fr) 2013-10-31 2015-05-07 Doran Brian Dispositif de bouchon pour contenant
US20150251827A1 (en) * 2014-03-10 2015-09-10 Phillip John Campbell Closure with spring loaded tether docking
US9493283B2 (en) 2013-08-02 2016-11-15 Bradley P. Tuyn Bottle cap attachment mechanism
US20170342176A1 (en) * 2016-05-30 2017-11-30 Nova Chemicals (International) S.A. Closure having excellent organoleptic performance

Patent Citations (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3904062A (en) 1973-07-02 1975-09-09 Somepla Sa Tamper-proof and loss-proof screw-type bottle cap
US4474302A (en) 1983-11-03 1984-10-02 James R. Goldberg Safety champagne cork
US4805792A (en) 1984-04-17 1989-02-21 Continental White Cap, Inc. Litterless tamper indicating closure
US4557393A (en) 1984-04-17 1985-12-10 Continental White Cap, Inc. Snap-on cap with tethering strap
US4573602A (en) 1984-07-10 1986-03-04 Goldberg James R Molded safety closure device and method for making same
US4583652A (en) 1984-07-10 1986-04-22 Goldberg James R Safety closure device
US4564114A (en) 1984-12-21 1986-01-14 James R. Goldberg Molded safety closure device
WO1993003093A1 (fr) 1991-07-18 1993-02-18 Exxon Chemical Patents Inc. Article thermosoude
US5342868A (en) 1991-12-05 1994-08-30 Asahi Denka Kogyo Kabushiki Kaisha Crystalline synthetic resin composition
US5292845A (en) 1992-01-23 1994-03-08 Mitsui Petrochemical Industries, Ltd. Ethylene/alpha-olefin/7-methyl-1,6-octadiene copolymer rubber and composition of the same
US5376439A (en) 1992-09-16 1994-12-27 Exxon Chemical Patents Inc. Soft films having enhanced physical properties
US5725115A (en) 1995-02-21 1998-03-10 Crown Cork Ag Closure cap with tether
US5981636A (en) 1996-12-27 1999-11-09 3M Innovative Properties Company Modifying agents for polyolefins
US20040016715A1 (en) 2000-11-28 2004-01-29 Miran Strikovic Cap for bottle-like containers
US6465551B1 (en) 2001-03-24 2002-10-15 Milliken & Company Bicyclo[2.2.1]heptane dicarboxylate salts as polyolefin nucleators
US6599971B2 (en) 2001-03-29 2003-07-29 Milliken & Company Metals salts of hexahydrophthalic acid as nucleating additives for crystalline thermoplastics
WO2005121239A2 (fr) 2004-05-06 2005-12-22 Dow Global Technologies Inc. Compositions polymeres de moulage
USD593856S1 (en) 2007-01-30 2009-06-09 Kenneth Kubler Bottle cap retainer
US20080197135A1 (en) 2007-02-20 2008-08-21 Berman Ronald H Beverage spout with safety tether
US8720716B2 (en) 2009-06-25 2014-05-13 Phillip John Campbell Closure with spring loaded tether docking
US8443994B1 (en) 2009-09-09 2013-05-21 Michael C. Desselle Tethered bottle cap assembly with means to retain a detached cap portion
WO2011050042A1 (fr) 2009-10-21 2011-04-28 Milliken & Company Composition à base d'un polymère thermoplastique
US9493283B2 (en) 2013-08-02 2016-11-15 Bradley P. Tuyn Bottle cap attachment mechanism
WO2015042561A1 (fr) 2013-09-23 2015-03-26 Milliken & Company Composition de polymère thermoplastique
WO2015042563A1 (fr) 2013-09-23 2015-03-26 Milliken & Company Composition de polymère thermoplastique
WO2015042562A1 (fr) 2013-09-23 2015-03-26 Milliken & Company Composition de polymère thermoplastique
WO2015061834A1 (fr) 2013-10-31 2015-05-07 Doran Brian Dispositif de bouchon pour contenant
US20150251827A1 (en) * 2014-03-10 2015-09-10 Phillip John Campbell Closure with spring loaded tether docking
US9776779B2 (en) 2014-03-10 2017-10-03 Phillip John Campbell Closure with spring loaded tether docking
US20170342176A1 (en) * 2016-05-30 2017-11-30 Nova Chemicals (International) S.A. Closure having excellent organoleptic performance

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
RANDALL, REV. MACROMOL. CHEM. PHYS., vol. C29, no. 2&3, pages 285

Also Published As

Publication number Publication date
US20190185219A1 (en) 2019-06-20
CA3024454A1 (fr) 2019-06-19
AR113657A1 (es) 2020-05-27

Similar Documents

Publication Publication Date Title
KR102731846B1 (ko) 폴리에틸렌 조성물을 포함하는 병 마개 조립체
EP3727784B1 (fr) Ensemble de fermeture de bouteille comprenant une composition d'homopolymère de polyéthylène
US20190185219A1 (en) Bottle closure assembly including a polyethylene copolymer
US20230264872A1 (en) Bottle closure assembly including a polyethylene composition
CA2933778C (fr) Composante a charniere faite de polyethylene unimodal haute densite
US10071895B2 (en) Hot fill process with closures made from high density unimodal polyethylene
WO2017208106A1 (fr) Fermeture dotée d'excellentes performances organoleptiques
US20190185232A1 (en) Bottle closure assembly including a polyethylene composition
BR112020012413B1 (pt) Conjunto de fechamento de garrafas com composição de homopolímero de polietileno

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18839541

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18839541

Country of ref document: EP

Kind code of ref document: A1