WO2019098202A1 - Procédé de production de poudre de résine, poudre de résine et procédé de production de stratifié - Google Patents

Procédé de production de poudre de résine, poudre de résine et procédé de production de stratifié Download PDF

Info

Publication number
WO2019098202A1
WO2019098202A1 PCT/JP2018/042010 JP2018042010W WO2019098202A1 WO 2019098202 A1 WO2019098202 A1 WO 2019098202A1 JP 2018042010 W JP2018042010 W JP 2018042010W WO 2019098202 A1 WO2019098202 A1 WO 2019098202A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin
resin powder
group
powder
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/042010
Other languages
English (en)
Japanese (ja)
Inventor
細田　朋也
達也 寺田
等 諏佐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AGC Inc
Original Assignee
Asahi Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Glass Co Ltd filed Critical Asahi Glass Co Ltd
Priority to CN201880073277.3A priority Critical patent/CN111344335A/zh
Priority to JP2019554234A priority patent/JP7205487B2/ja
Priority to KR1020207003997A priority patent/KR102673931B1/ko
Publication of WO2019098202A1 publication Critical patent/WO2019098202A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne : un procédé de production de poudre de résine avec lequel il est possible de produire efficacement une poudre de résine avec une distribution granulométrique étroite ; une poudre de résine capable de former une couche de résine mince dans laquelle des irrégularités de surface sont supprimées ; et un procédé de production d'un stratifié ayant une couche de résine mince formée à partir de ladite poudre de résine. Ce procédé de production de poudre de résine comprend : la soumission d'un corps de résine de matériau comprenant un fluoropolymère thermofusible ayant un D50 de 10 µm ou plus à une pulvérisation primaire par réalisation d'un traitement de pulvérisation mécanique au moins une fois jusqu'à ce que le D50 soit de 1 à 300 µm ; puis la réalisation d'une pulvérisation secondaire avec un broyeur à jet ; et la réalisation d'une classification si nécessaire, pour obtenir une poudre de résine ayant un D50 de 0,01 à 3 µm. Le D90 de la poudre de résine obtenue est de préférence de 2,5 à 4 µm.
PCT/JP2018/042010 2017-11-16 2018-11-13 Procédé de production de poudre de résine, poudre de résine et procédé de production de stratifié Ceased WO2019098202A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201880073277.3A CN111344335A (zh) 2017-11-16 2018-11-13 树脂粉末的制造方法、树脂粉末和层叠体的制造方法
JP2019554234A JP7205487B2 (ja) 2017-11-16 2018-11-13 樹脂パウダーの製造方法、樹脂パウダーおよび積層体の製造方法
KR1020207003997A KR102673931B1 (ko) 2017-11-16 2018-11-13 수지 파우더의 제조 방법, 수지 파우더 및 적층체의 제조 방법

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017-221274 2017-11-16
JP2017221274 2017-11-16

Publications (1)

Publication Number Publication Date
WO2019098202A1 true WO2019098202A1 (fr) 2019-05-23

Family

ID=66538622

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/042010 Ceased WO2019098202A1 (fr) 2017-11-16 2018-11-13 Procédé de production de poudre de résine, poudre de résine et procédé de production de stratifié

Country Status (5)

Country Link
JP (1) JP7205487B2 (fr)
KR (1) KR102673931B1 (fr)
CN (1) CN111344335A (fr)
TW (1) TWI806923B (fr)
WO (1) WO2019098202A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021059616A (ja) * 2019-10-03 2021-04-15 Ａｇｃ株式会社 非水系分散液及び非水系分散液の製造方法
JPWO2021221038A1 (fr) * 2020-04-30 2021-11-04
WO2021246306A1 (fr) * 2020-06-01 2021-12-09 Ａｇｃ株式会社 Poudre ainsi que procédé de fabrication de celle-ci, et dispersion liquide de poudre
WO2022265033A1 (fr) * 2021-06-18 2022-12-22 Ａｇｃ株式会社 Procédé de fabrication d'un corps viscoélastique et corps viscoélastique
JP2023527829A (ja) * 2020-05-26 2023-06-30 ゼウス カンパニー インコーポレイテッド 熱機械的に分解されたｐｔｆｅからの微粒子

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7727402B2 (ja) * 2021-04-08 2025-08-21 株式会社Ｅｎｅｏｓマテリアル 液晶ポリマー粒子の製造方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006509072A (ja) * 2002-11-22 2006-03-16 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー 直接重合された低分子量の粒状ポリテトラフルオロエチレン
JP2008260864A (ja) * 2007-04-12 2008-10-30 Daikin Ind Ltd 水性分散体の製造方法及び水性分散体
WO2016017801A1 (fr) * 2014-08-01 2016-02-04 旭硝子株式会社 Poudre de résine ainsi que procédé de fabrication de celle-ci, corps composite, corps moulé, procédé de fabrication de corps moulé en céramique, plaque stratifiée métallique, carte de circuit imprimé, et préimprégné
WO2017122743A1 (fr) * 2016-01-14 2017-07-20 旭硝子株式会社 Composition durcissable, produit durci, préimprégné et article moulé avec renfort de fibres
WO2018043683A1 (fr) * 2016-09-01 2018-03-08 旭硝子株式会社 Stratifié métallique et son procédé de fabrication, et procédé de fabrication d'une carte de circuit imprimé

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100972721B1 (ko) * 2007-04-12 2010-07-27 다이킨 고교 가부시키가이샤 수성 분산체의 제조 방법, 수성 분산체, 불소 수지 도료조성물, 및 도장 물품

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006509072A (ja) * 2002-11-22 2006-03-16 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー 直接重合された低分子量の粒状ポリテトラフルオロエチレン
JP2008260864A (ja) * 2007-04-12 2008-10-30 Daikin Ind Ltd 水性分散体の製造方法及び水性分散体
WO2016017801A1 (fr) * 2014-08-01 2016-02-04 旭硝子株式会社 Poudre de résine ainsi que procédé de fabrication de celle-ci, corps composite, corps moulé, procédé de fabrication de corps moulé en céramique, plaque stratifiée métallique, carte de circuit imprimé, et préimprégné
WO2017122743A1 (fr) * 2016-01-14 2017-07-20 旭硝子株式会社 Composition durcissable, produit durci, préimprégné et article moulé avec renfort de fibres
WO2018043683A1 (fr) * 2016-09-01 2018-03-08 旭硝子株式会社 Stratifié métallique et son procédé de fabrication, et procédé de fabrication d'une carte de circuit imprimé

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021059616A (ja) * 2019-10-03 2021-04-15 Ａｇｃ株式会社 非水系分散液及び非水系分散液の製造方法
JP7443715B2 (ja) 2019-10-03 2024-03-06 Ａｇｃ株式会社 非水系分散液及び非水系分散液の製造方法
JPWO2021221038A1 (fr) * 2020-04-30 2021-11-04
JP7740234B2 (ja) 2020-04-30 2025-09-17 Ａｇｃ株式会社 分散液の製造方法、ペーストおよび練粉
JP2023527829A (ja) * 2020-05-26 2023-06-30 ゼウス カンパニー インコーポレイテッド 熱機械的に分解されたｐｔｆｅからの微粒子
JP7673095B2 (ja) 2020-05-26 2025-05-08 ゼウス カンパニー エルエルシー 熱機械的に分解されたｐｔｆｅからの微粒子
WO2021246306A1 (fr) * 2020-06-01 2021-12-09 Ａｇｃ株式会社 Poudre ainsi que procédé de fabrication de celle-ci, et dispersion liquide de poudre
WO2022265033A1 (fr) * 2021-06-18 2022-12-22 Ａｇｃ株式会社 Procédé de fabrication d'un corps viscoélastique et corps viscoélastique

Also Published As

Publication number Publication date
TW201930411A (zh) 2019-08-01
KR102673931B1 (ko) 2024-06-10
JP7205487B2 (ja) 2023-01-17
TWI806923B (zh) 2023-07-01
CN111344335A (zh) 2020-06-26
JPWO2019098202A1 (ja) 2020-12-03
KR20200078471A (ko) 2020-07-01

Similar Documents

Publication Publication Date Title
JP7205487B2 (ja) 樹脂パウダーの製造方法、樹脂パウダーおよび積層体の製造方法
CN109415571B (zh) 含有氟树脂粉末的液态组合物的制造方法
JP6954293B2 (ja) 金属積層板およびその製造方法、ならびにプリント基板の製造方法
US11041053B2 (en) Resin powder, method for its production, composite, molded product, method for producing ceramic molded product, metal laminated plate, printed circuit board and prepreg
JP7115589B2 (ja) 液状組成物、並びに該液状組成物を使用した、フィルムおよび積層体の製造方法
JP7444072B2 (ja) 変性粒子の製造方法、変性粒子、分散液、組成物及び積層体
JP2019104843A (ja) 樹脂組成物、積層体、金属積層板及びプリント配線板
JP2022011017A (ja) パウダー分散液及び積層体の製造方法
JP7740238B2 (ja) パウダーの製造方法、パウダー及びパウダー分散液
JP7511124B2 (ja) 分散液の製造方法および分散液
CN116133853A (zh) 分散液、复合粒子及复合粒子的制造方法
JPWO2020050178A1 (ja) 分散液の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18879804

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019554234

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18879804

Country of ref document: EP

Kind code of ref document: A1