WO2018110017A1 - Produit optique - Google Patents

Produit optique Download PDF

Info

Publication number
WO2018110017A1
WO2018110017A1 PCT/JP2017/033841 JP2017033841W WO2018110017A1 WO 2018110017 A1 WO2018110017 A1 WO 2018110017A1 JP 2017033841 W JP2017033841 W JP 2017033841W WO 2018110017 A1 WO2018110017 A1 WO 2018110017A1
Authority
WO
WIPO (PCT)
Prior art keywords
optical product
layer
refractive index
product according
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2017/033841
Other languages
English (en)
Japanese (ja)
Inventor
松坂慶二
能勢正章
中村勝也
青木洋輔
今関秀和
水町靖
野村康之
濱敬二
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Konica Minolta Inc
Original Assignee
Konica Minolta Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Konica Minolta Inc filed Critical Konica Minolta Inc
Publication of WO2018110017A1 publication Critical patent/WO2018110017A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne également un produit optique qui peut atteindre des caractéristiques spectrales souhaitées tout en présentant un effet catalytique. Ce produit optique a un substrat de verre sur lequel est formé un film multicouche de trois couches ou plus, et en utilisant une combinaison d'au moins une couche à faible indice de réfraction et d'au moins une couche à indice de réfraction élevé, le substrat multicouche peut ajuster les caractéristiques spectrales du produit optique. La couche supérieure la plus éloignée du substrat en verre est une couche à faible indice de réfraction, et une couche à indice de réfraction élevé adjacente à la couche supérieure est une couche fonctionnelle ayant un oxyde métallique ayant une fonction photocatalytique en tant que composant principal, et satisfait les expressions conditionnelles ci-dessous. 60 Nm ≤ TL ≤ 350 nm (1) 220 nm ≤ Tcat ≤ 700 nm (2) ici, TL est l'épaisseur de film de la couche supérieure, et Tcat est l'épaisseur de film de la couche fonctionnelle.
PCT/JP2017/033841 2016-12-14 2017-09-20 Produit optique Ceased WO2018110017A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016-242185 2016-12-14
JP2016242185A JP2020024237A (ja) 2016-12-14 2016-12-14 光学製品

Publications (1)

Publication Number Publication Date
WO2018110017A1 true WO2018110017A1 (fr) 2018-06-21

Family

ID=62558373

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/033841 Ceased WO2018110017A1 (fr) 2016-12-14 2017-09-20 Produit optique

Country Status (2)

Country Link
JP (1) JP2020024237A (fr)
WO (1) WO2018110017A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021199466A1 (fr) * 2020-03-31 2021-10-07 日本電産株式会社 Élément optique
TWI828475B (zh) * 2022-12-14 2024-01-01 富元精密科技股份有限公司 用於阻擋紅外線的抗反射塗層及含有其的顯示裝置

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022145208A1 (fr) * 2020-12-28 2022-07-07 富士フイルム株式会社 Guide de lumière et dispositif d'affichage d'image
CN115373054A (zh) * 2021-05-21 2022-11-22 手持产品公司 为光学部件提供光学涂层的方法、设备和系统
WO2025205639A1 (fr) * 2024-03-28 2025-10-02 ニデック株式会社 Élément optique, unité d'élément translucide, dispositif d'imagerie et procédé de fabrication d'élément optique

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000131513A (ja) * 1998-10-28 2000-05-12 Toyota Motor Corp 表面鏡
JP2000326440A (ja) * 1999-05-19 2000-11-28 Hoya Corp 光触媒機能を有する多層光学薄膜を有する物品及びその製造方法
JP2000329904A (ja) * 1999-05-18 2000-11-30 Hoya Corp 光触媒機能を有する反射防止膜を有する物品及びその製造方法
JP2001152418A (ja) * 1999-11-30 2001-06-05 Sekisui Jushi Co Ltd 防曇性反射鏡及びその製造方法
JP2005003614A (ja) * 2003-06-13 2005-01-06 National Institute Of Advanced Industrial & Technology ヒートミラー及びその性能評価法
JP2006106242A (ja) * 2004-10-04 2006-04-20 Seiko Epson Corp 反射防止膜及びその反射防止膜を有する光学物品
JP2008107425A (ja) * 2006-10-23 2008-05-08 Ichikoh Ind Ltd ミラーおよび光触媒活性を有する親水性複合膜
JP2011039218A (ja) * 2009-08-10 2011-02-24 Seiko Epson Corp 光学物品の製造方法
JP2011242697A (ja) * 2010-05-20 2011-12-01 Tokai Kogaku Kk プラスチック光学製品及び眼鏡プラスチックレンズ
JP2013545145A (ja) * 2010-12-10 2013-12-19 エシロール アテルナジオナール カンパニー ジェネラーレ デ オプティック 紫外領域及び可視領域の両方において低い反射性を持つ反射防止膜を有する光学部品

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000131513A (ja) * 1998-10-28 2000-05-12 Toyota Motor Corp 表面鏡
JP2000329904A (ja) * 1999-05-18 2000-11-30 Hoya Corp 光触媒機能を有する反射防止膜を有する物品及びその製造方法
JP2000326440A (ja) * 1999-05-19 2000-11-28 Hoya Corp 光触媒機能を有する多層光学薄膜を有する物品及びその製造方法
JP2001152418A (ja) * 1999-11-30 2001-06-05 Sekisui Jushi Co Ltd 防曇性反射鏡及びその製造方法
JP2005003614A (ja) * 2003-06-13 2005-01-06 National Institute Of Advanced Industrial & Technology ヒートミラー及びその性能評価法
JP2006106242A (ja) * 2004-10-04 2006-04-20 Seiko Epson Corp 反射防止膜及びその反射防止膜を有する光学物品
JP2008107425A (ja) * 2006-10-23 2008-05-08 Ichikoh Ind Ltd ミラーおよび光触媒活性を有する親水性複合膜
JP2011039218A (ja) * 2009-08-10 2011-02-24 Seiko Epson Corp 光学物品の製造方法
JP2011242697A (ja) * 2010-05-20 2011-12-01 Tokai Kogaku Kk プラスチック光学製品及び眼鏡プラスチックレンズ
JP2013545145A (ja) * 2010-12-10 2013-12-19 エシロール アテルナジオナール カンパニー ジェネラーレ デ オプティック 紫外領域及び可視領域の両方において低い反射性を持つ反射防止膜を有する光学部品

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021199466A1 (fr) * 2020-03-31 2021-10-07 日本電産株式会社 Élément optique
TWI828475B (zh) * 2022-12-14 2024-01-01 富元精密科技股份有限公司 用於阻擋紅外線的抗反射塗層及含有其的顯示裝置

Also Published As

Publication number Publication date
JP2020024237A (ja) 2020-02-13

Similar Documents

Publication Publication Date Title
JP5881096B2 (ja) 反射防止膜及び光学素子
JP6451057B2 (ja) 可視域反射防止近赤外域透過抑制光学製品並びに眼鏡レンズ及び眼鏡
US9069125B2 (en) Optical product and method for manufacturing same
US20190383972A1 (en) Layer system and optical element comprising a layer system
WO2018110017A1 (fr) Produit optique
JP4190773B2 (ja) 反射防止膜と光学レンズ及び光学レンズユニット
WO2012169393A1 (fr) Film antiréfléchissant, système optique, et dispositif optique
JP5976363B2 (ja) 光学部材
JP6622381B2 (ja) 光学膜、光学素子および光学系
WO2018110018A1 (fr) Élément optique
JP4171362B2 (ja) 反射防止膜付き透明基板
JP5292318B2 (ja) 反射防止膜、及びこれを有する光学部材
CN1749782A (zh) 镀膜玻璃镜片
TWI901817B (zh) 光學積層體及物品
JP2000111702A (ja) 反射防止膜
JP2004334012A (ja) 反射防止膜及び光学フィルター
US20130258278A1 (en) Lens comprising a polymeric substrate, a hardening layer and a metallic layer
JP7385894B2 (ja) プラスチック基材ｎｄフィルタ及び眼鏡用プラスチック基材ｎｄフィルタ
JP2002277606A (ja) 反射防止膜及び光学素子
TWI879960B (zh) 近紅外線截止濾波器及攝像裝置
JP7405405B2 (ja) 反射防止膜及びこれを有する光学素子、反射防止膜の製造方法
US20210278577A1 (en) Optical coating for organic surface treatments
JP7468624B2 (ja) 光学部材
JP2016186661A (ja) 光学部材
JP2025113884A (ja) 反射防止膜および光学素子

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17881624

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17881624

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP