WO2018179102A1 - Film de réglage d'indice de réfraction photosensible du type à transfert, procédé de formation de modèle de réglage d'indice de réfraction, film durci et panneau tactile - Google Patents

Film de réglage d'indice de réfraction photosensible du type à transfert, procédé de formation de modèle de réglage d'indice de réfraction, film durci et panneau tactile Download PDF

Info

Publication number
WO2018179102A1
WO2018179102A1 PCT/JP2017/012695 JP2017012695W WO2018179102A1 WO 2018179102 A1 WO2018179102 A1 WO 2018179102A1 JP 2017012695 W JP2017012695 W JP 2017012695W WO 2018179102 A1 WO2018179102 A1 WO 2018179102A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin layer
refractive index
group
meth
type photosensitive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2017/012695
Other languages
English (en)
Japanese (ja)
Inventor
友洋 鮎ヶ瀬
向　郁夫
和仁 渡部
吉田　英樹
渡邊　治
匠 渡邊
征志 南
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Resonac Corp
Original Assignee
Hitachi Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hitachi Chemical Co Ltd filed Critical Hitachi Chemical Co Ltd
Priority to PCT/JP2017/012695 priority Critical patent/WO2018179102A1/fr
Publication of WO2018179102A1 publication Critical patent/WO2018179102A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un film de réglage d'indice de réfraction photosensible de type transfert ayant un film de support, une première couche de résine disposée sur le film de support, et une seconde couche de résine disposée sur la première couche de résine et contenant des particules d'oxyde métallique, la première couche de résine comprenant : un polymère liant, qui contient un groupe ayant une structure ramifiée et/ou une structure alicyclique dans une chaîne latérale, un groupe ayant un groupe acide dans une chaîne latérale, et un groupe ayant un groupe à insaturation éthylénique dans une chaîne latérale ; un composé photopolymérisable ; un initiateur de photopolymérisation ; et un ester de phosphate ayant une liaison éthyléniquement insaturée, et le contenu dans la première couche de résine, de l'ester de phosphate ayant une liaison éthyléniquement insaturée est de 1,5 à 3,0 parties en masse par rapport à 100 parties en masse du total du polymère de liant et du composé photopolymérisable.
PCT/JP2017/012695 2017-03-28 2017-03-28 Film de réglage d'indice de réfraction photosensible du type à transfert, procédé de formation de modèle de réglage d'indice de réfraction, film durci et panneau tactile Ceased WO2018179102A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/JP2017/012695 WO2018179102A1 (fr) 2017-03-28 2017-03-28 Film de réglage d'indice de réfraction photosensible du type à transfert, procédé de formation de modèle de réglage d'indice de réfraction, film durci et panneau tactile

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2017/012695 WO2018179102A1 (fr) 2017-03-28 2017-03-28 Film de réglage d'indice de réfraction photosensible du type à transfert, procédé de formation de modèle de réglage d'indice de réfraction, film durci et panneau tactile

Publications (1)

Publication Number Publication Date
WO2018179102A1 true WO2018179102A1 (fr) 2018-10-04

Family

ID=63674791

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/012695 Ceased WO2018179102A1 (fr) 2017-03-28 2017-03-28 Film de réglage d'indice de réfraction photosensible du type à transfert, procédé de formation de modèle de réglage d'indice de réfraction, film durci et panneau tactile

Country Status (1)

Country Link
WO (1) WO2018179102A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012078528A (ja) * 2010-09-30 2012-04-19 Fujifilm Corp 感光性組成物、感光性樹脂転写フィルム、樹脂パターン及び樹脂パターンの製造方法、並びに液晶表示装置用基板及び液晶表示装置
JP2013200577A (ja) * 2011-12-05 2013-10-03 Hitachi Chemical Co Ltd 樹脂硬化膜パターンの形成方法、感光性樹脂組成物、感光性エレメント、タッチパネルの製造方法及び樹脂硬化膜
JP2014108541A (ja) * 2012-11-30 2014-06-12 Fujifilm Corp 転写フィルムおよび透明積層体、それらの製造方法、静電容量型入力装置ならびに画像表示装置
JP2015121929A (ja) * 2013-12-24 2015-07-02 日立化成株式会社 硬化膜付きタッチパネル用基材の製造方法、それに用いる感光性樹脂組成物、感光性エレメント及びタッチパネル

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012078528A (ja) * 2010-09-30 2012-04-19 Fujifilm Corp 感光性組成物、感光性樹脂転写フィルム、樹脂パターン及び樹脂パターンの製造方法、並びに液晶表示装置用基板及び液晶表示装置
JP2013200577A (ja) * 2011-12-05 2013-10-03 Hitachi Chemical Co Ltd 樹脂硬化膜パターンの形成方法、感光性樹脂組成物、感光性エレメント、タッチパネルの製造方法及び樹脂硬化膜
JP2014108541A (ja) * 2012-11-30 2014-06-12 Fujifilm Corp 転写フィルムおよび透明積層体、それらの製造方法、静電容量型入力装置ならびに画像表示装置
JP2015121929A (ja) * 2013-12-24 2015-07-02 日立化成株式会社 硬化膜付きタッチパネル用基材の製造方法、それに用いる感光性樹脂組成物、感光性エレメント及びタッチパネル

Similar Documents

Publication Publication Date Title
WO2016181422A1 (fr) Film de réglage d'indice de réfraction photosensible du type à transfert, procédé de formation de modèle d'indice de réfraction et composant électronique
WO2016001955A1 (fr) Film de régulation d'indice de réfraction photosensible de type transfert
JP2019175226A (ja) タッチセンサの保護膜形成用感光性フィルム、タッチセンサの保護膜形成用感光性屈折率調整フィルム、タッチセンサの保護膜の形成方法及びタッチパネル
JP2017116774A (ja) 転写形感光性屈折率調整フィルム
JP2017201352A (ja) 転写形感光性屈折率調整フィルム、屈折率調整パターンの形成方法及び電子部品
JP2018165788A (ja) 転写型感光性フィルム、硬化樹脂パターンの形成方法及びタッチパネル
JP2017181541A (ja) 感光性フィルム、感光性屈折率調整フィルム、屈折率調整パターンの形成方法、硬化膜及び電子部品
US20180284920A1 (en) Transfer-type photosensitive film for refractive-index modulation
WO2016132401A1 (fr) Film d'ajustement d'indice de réfraction photosensible du type transfert, procédé de formation d'un motif d'ajustement d'indice de réfraction, et composant électronique
JP2019035801A (ja) 転写型感光性フィルム、硬化膜パターンの形成方法、硬化膜及び電子部品
WO2017175642A1 (fr) Film de modulation d'indice de réfraction photosensible, procédé de formation d'un motif de film durci, film durci et composant électronique
JP6943279B2 (ja) 転写型感光性フィルム、硬化膜パターンの形成方法及びタッチパネル
JP7614139B2 (ja) 転写型感光性フィルム、硬化膜パターンの形成方法、硬化膜及びタッチパネル
WO2018179102A1 (fr) Film de réglage d'indice de réfraction photosensible du type à transfert, procédé de formation de modèle de réglage d'indice de réfraction, film durci et panneau tactile
JP2019215395A (ja) 転写型感光性フィルム、硬化膜パターンの形成方法、積層体及びタッチパネル
WO2019186802A1 (fr) Film de transfert, film durci et procédé de formation associé, et composant électronique
JP2019174604A (ja) 転写フィルム、硬化膜及びその形成方法、並びに、電子部品
WO2019224887A1 (fr) Film photosensible de type transfert, substrat d'électrode avec film durci en résine et panneau tactile
WO2019207648A1 (fr) Composition de résine photosensible, film photosensible de type à transfert, substrat ayant un film durci fixé à celui-ci, et dispositif de détection
JP2019219631A (ja) 転写フィルム、硬化膜及びその形成方法、並びに、電子部品
JP2019152750A (ja) 感光性フィルム、及び、硬化物の製造方法
WO2019207677A1 (fr) Film photosensible et film de réglage d'indice de réfraction photosensible
JP2019207377A (ja) 感光性屈折率調整フィルム
WO2019186781A1 (fr) Film de transfert, film durci et procédé de formation associé, et composant électrique
JP2017111245A (ja) 硬化膜付きタッチパネル用基材の製造方法、硬化膜形成剤、感光性エレメント及びタッチパネル

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17902937

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17902937

Country of ref document: EP