WO2018176300A1 - Nouveau liant prépolymère à base de mdi pour application de liant durcissant à l'humidité - Google Patents

Nouveau liant prépolymère à base de mdi pour application de liant durcissant à l'humidité Download PDF

Info

Publication number
WO2018176300A1
WO2018176300A1 PCT/CN2017/078710 CN2017078710W WO2018176300A1 WO 2018176300 A1 WO2018176300 A1 WO 2018176300A1 CN 2017078710 W CN2017078710 W CN 2017078710W WO 2018176300 A1 WO2018176300 A1 WO 2018176300A1
Authority
WO
WIPO (PCT)
Prior art keywords
mdi
based prepolymer
binder
prepolymer
novel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2017/078710
Other languages
English (en)
Inventor
Jiawen Xiong
Xiangyang Tai
Huan CHEN
Jiang Li
Juelin LIU
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Global Technologies LLC
Original Assignee
Dow Global Technologies LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Global Technologies LLC filed Critical Dow Global Technologies LLC
Priority to PCT/CN2017/078710 priority Critical patent/WO2018176300A1/fr
Priority to PCT/US2018/020357 priority patent/WO2018182912A1/fr
Publication of WO2018176300A1 publication Critical patent/WO2018176300A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un nouveau liant prépolymère à base de MDI qui est un produit de réaction d'un prépolymère MDI, ou un mélange d'un prépolymère MDI et d'un monomère MDI, avec un composé de formule (I) ou de formule (II).
PCT/CN2017/078710 2017-03-30 2017-03-30 Nouveau liant prépolymère à base de mdi pour application de liant durcissant à l'humidité Ceased WO2018176300A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
PCT/CN2017/078710 WO2018176300A1 (fr) 2017-03-30 2017-03-30 Nouveau liant prépolymère à base de mdi pour application de liant durcissant à l'humidité
PCT/US2018/020357 WO2018182912A1 (fr) 2017-03-30 2018-03-01 Nouveau liant prépolymère à base de mdi pour l'application d'un liant durcissant à l'humidité

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CN2017/078710 WO2018176300A1 (fr) 2017-03-30 2017-03-30 Nouveau liant prépolymère à base de mdi pour application de liant durcissant à l'humidité

Publications (1)

Publication Number Publication Date
WO2018176300A1 true WO2018176300A1 (fr) 2018-10-04

Family

ID=61768432

Family Applications (2)

Application Number Title Priority Date Filing Date
PCT/CN2017/078710 Ceased WO2018176300A1 (fr) 2017-03-30 2017-03-30 Nouveau liant prépolymère à base de mdi pour application de liant durcissant à l'humidité
PCT/US2018/020357 Ceased WO2018182912A1 (fr) 2017-03-30 2018-03-01 Nouveau liant prépolymère à base de mdi pour l'application d'un liant durcissant à l'humidité

Family Applications After (1)

Application Number Title Priority Date Filing Date
PCT/US2018/020357 Ceased WO2018182912A1 (fr) 2017-03-30 2018-03-01 Nouveau liant prépolymère à base de mdi pour l'application d'un liant durcissant à l'humidité

Country Status (1)

Country Link
WO (2) WO2018176300A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11618814B2 (en) 2020-12-04 2023-04-04 Covestro Llc Elastomeric compositions containing a solid residue of isocyanate manufacturing

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5319053A (en) * 1993-09-02 1994-06-07 Miles Inc. Liquid diphenylmethane diisocyanate
CN1648147A (zh) * 2004-01-28 2005-08-03 日本聚氨酯工业株式会社 多异氰酸酯组合物及其调制方法和硬质聚氨酯泡沫的制造方法
CN102786905A (zh) * 2011-08-19 2012-11-21 苏州赛伍应用技术有限公司 聚酯粘合剂及使用该聚酯粘合剂的薄膜状层压体
CN102876263A (zh) * 2011-07-12 2013-01-16 综研化学株式会社 压敏粘合剂、压敏粘合片及触摸面板用层叠体
CN104513600A (zh) * 2013-09-30 2015-04-15 青岛兴国涂料有限公司 一种地板用底漆
CN104693398A (zh) * 2013-12-09 2015-06-10 上海闵临机电科技有限公司 一种用于化工工业的新型聚氨基甲酸酯原料

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3876760A (en) * 1969-10-23 1975-04-08 Bristol Myers Co Hair dressing compositions containing a hair substantive quaternary resin
BR8406510A (pt) * 1983-04-07 1985-03-12 Minnesota Mining & Mfg Adesivo e material em folha revestido com adesivo para pele umida
US5545706A (en) * 1995-05-09 1996-08-13 Arco Chemical Technology, L.P. PTMEG polyurethane elastomers employing monofunctional polyethers
JP3484187B2 (ja) * 2001-12-18 2004-01-06 紀和化学工業株式会社 インクジェット記録用インク
JP5470775B2 (ja) * 2008-08-29 2014-04-16 東洋インキＳｃホールディングス株式会社 反応性ホットメルト接着剤およびそれを用いてなる積層体
EP3080185B1 (fr) * 2013-12-09 2025-04-23 DDP Specialty Electronic Materials US, LLC Prépolymères améliorés de polyuréthane présentant peu ou pas de plastifiants et leur utilisation dans des adhésifs pour verre de véhicule

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5319053A (en) * 1993-09-02 1994-06-07 Miles Inc. Liquid diphenylmethane diisocyanate
CN1648147A (zh) * 2004-01-28 2005-08-03 日本聚氨酯工业株式会社 多异氰酸酯组合物及其调制方法和硬质聚氨酯泡沫的制造方法
CN102876263A (zh) * 2011-07-12 2013-01-16 综研化学株式会社 压敏粘合剂、压敏粘合片及触摸面板用层叠体
CN102786905A (zh) * 2011-08-19 2012-11-21 苏州赛伍应用技术有限公司 聚酯粘合剂及使用该聚酯粘合剂的薄膜状层压体
CN104513600A (zh) * 2013-09-30 2015-04-15 青岛兴国涂料有限公司 一种地板用底漆
CN104693398A (zh) * 2013-12-09 2015-06-10 上海闵临机电科技有限公司 一种用于化工工业的新型聚氨基甲酸酯原料

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11618814B2 (en) 2020-12-04 2023-04-04 Covestro Llc Elastomeric compositions containing a solid residue of isocyanate manufacturing

Also Published As

Publication number Publication date
WO2018182912A1 (fr) 2018-10-04

Similar Documents

Publication Publication Date Title
US9856357B2 (en) Polyurethane resin composition and polyurethane composite prepared from the same
JP3707777B2 (ja) ポリエーテルポリウレタン
US7763341B2 (en) Filled polymer composite and synthetic building material compositions
CN106751737B (zh) 热固性聚氨酯复合物
CN110114380B (zh) 双组分聚氨酯粘合剂
US5011902A (en) Co-catalyst system for preparing polyurethane based plywood-patch compositions
JPS62502048A (ja) 裏地布に有効なポリウレタン成形組成物およびポリウレタン裏打布を製造する方法
KR0162486B1 (ko) 폴리프로필렌옥사이드와 유기-실리콘 블록공중합체에 기초한 폴리올 중간체의 블렌드로 만든 폴리우레탄
JPH06504075A (ja) ポリウレタンカーペットの裏打ち処理
RU2013133622A (ru) Реакционноспособная полиуретановая композиция, содержащая устойчивые к истиранию наполнители
KR20100122907A (ko) 무용매 접착제에 유용한 액체 폴리우레탄 예비중합체
JP6845161B2 (ja) 疎水性ポリオール
KR101427122B1 (ko) 수작업 시공용 도공제
CN1221430A (zh) 多异氰酸酯改性异单烯烃－对烷基苯乙烯弹性体组合物
CA2539599A1 (fr) Composition a deux composants servant a produire des enduits gelifies en polyurethanne pour des materiaux composites constitues de resine epoxy et de resine vinylester
JP2004231931A (ja) ポリイソシアネート溶液並びにこれを用いた接着剤および塗料
CN112424250A (zh) 玻璃纤维增强的tpu
CN114729093B (zh) 双组分胶粘剂组合物
Dodge Polyurethanes and polyureas
CN116669961A (zh) 混合跑道制品及其制备方法
EP3189090A1 (fr) Tapis de polyuréthane
WO2018176300A1 (fr) Nouveau liant prépolymère à base de mdi pour application de liant durcissant à l'humidité
US8962771B2 (en) Reactive isocyanate-terminated prepolymers for binder applications
CN113631607B (zh) 聚氨酯及其制造方法
CN114605612A (zh) 一种劳保鞋用双组份反应型聚氨酯树脂及其制备方法和劳保鞋

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17904208

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17904208

Country of ref document: EP

Kind code of ref document: A1