[go: up one dir, main page]

WO2018168845A1 - Feuille composite céramique et condensateur - Google Patents

Feuille composite céramique et condensateur Download PDF

Info

Publication number
WO2018168845A1
WO2018168845A1 PCT/JP2018/009710 JP2018009710W WO2018168845A1 WO 2018168845 A1 WO2018168845 A1 WO 2018168845A1 JP 2018009710 W JP2018009710 W JP 2018009710W WO 2018168845 A1 WO2018168845 A1 WO 2018168845A1
Authority
WO
WIPO (PCT)
Prior art keywords
ceramic composite
dielectric
composite sheet
dielectric layer
metal foil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/009710
Other languages
English (en)
Japanese (ja)
Inventor
将之 萩谷
卓 酒谷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Chemi Con Corp
Original Assignee
Nippon Chemi Con Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Chemi Con Corp filed Critical Nippon Chemi Con Corp
Priority to JP2019506042A priority Critical patent/JP7180048B2/ja
Publication of WO2018168845A1 publication Critical patent/WO2018168845A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne : une feuille composite céramique qui, tout en améliorant la tension de tenue, est apte à empêcher de manière plus fiable le pelage entre des feuilles composites céramiques dans lesquelles une couche diélectrique est stratifiée sur une feuille métallique ; et un condensateur comprenant ladite feuille composite céramique. Une feuille composite céramique (1) est chevauchée afin de constituer un condensateur, et est conçue de manière à avoir une couche diélectrique (3) contenant une résine organique et une poudre céramique diélectrique stratifiée sur une feuille métallique (2), et de manière à avoir une couche électriquement conductrice (4) stratifiée sur la couche diélectrique (3).
PCT/JP2018/009710 2017-03-14 2018-03-13 Feuille composite céramique et condensateur Ceased WO2018168845A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2019506042A JP7180048B2 (ja) 2017-03-14 2018-03-13 セラミック複合体シート及びコンデンサ

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017048301 2017-03-14
JP2017-048301 2017-03-14

Publications (1)

Publication Number Publication Date
WO2018168845A1 true WO2018168845A1 (fr) 2018-09-20

Family

ID=63523165

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/009710 Ceased WO2018168845A1 (fr) 2017-03-14 2018-03-13 Feuille composite céramique et condensateur

Country Status (2)

Country Link
JP (1) JP7180048B2 (fr)
WO (1) WO2018168845A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2023503212A (ja) * 2020-09-21 2023-01-27 ティーディーケイ・エレクトロニクス・アクチェンゲゼルシャフト コンデンサ
JP2023046075A (ja) * 2021-09-22 2023-04-03 京セラ株式会社 フィルムコンデンサ素子の製造方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS49103154A (fr) * 1973-02-05 1974-09-30
JPS5061435A (fr) * 1973-10-02 1975-05-27
JPH0917689A (ja) * 1995-06-28 1997-01-17 Hokuriku Electric Ind Co Ltd 印刷コンデンサとその製造方法
JP2010539285A (ja) * 2007-09-14 2010-12-16 オークミツイ，インク．， 優れたｔｃｃを有するポリマー−セラミック複合材料

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS49103154A (fr) * 1973-02-05 1974-09-30
JPS5061435A (fr) * 1973-10-02 1975-05-27
JPH0917689A (ja) * 1995-06-28 1997-01-17 Hokuriku Electric Ind Co Ltd 印刷コンデンサとその製造方法
JP2010539285A (ja) * 2007-09-14 2010-12-16 オークミツイ，インク．， 優れたｔｃｃを有するポリマー−セラミック複合材料

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2023503212A (ja) * 2020-09-21 2023-01-27 ティーディーケイ・エレクトロニクス・アクチェンゲゼルシャフト コンデンサ
JP7464704B2 (ja) 2020-09-21 2024-04-09 ティーディーケイ・エレクトロニクス・アクチェンゲゼルシャフト コンデンサ
US11996239B2 (en) 2020-09-21 2024-05-28 Tdk Electronics Ag Capacitor
JP2024081735A (ja) * 2020-09-21 2024-06-18 ティーディーケイ・エレクトロニクス・アクチェンゲゼルシャフト コンデンサ
JP7653559B2 (ja) 2020-09-21 2025-03-28 ティーディーケイ・エレクトロニクス・アクチェンゲゼルシャフト コンデンサ
JP2023046075A (ja) * 2021-09-22 2023-04-03 京セラ株式会社 フィルムコンデンサ素子の製造方法

Also Published As

Publication number Publication date
JPWO2018168845A1 (ja) 2020-01-16
JP7180048B2 (ja) 2022-11-30

Similar Documents

Publication Publication Date Title
JP5958977B2 (ja) 積層セラミック電子部品及びその実装基板
JP5863714B2 (ja) 積層セラミックキャパシタ及びその製造方法
KR101477430B1 (ko) 적층 세라믹 전자부품, 그 제조방법 및 적층 세라믹 전자부품의 실장 기판
CN105931839B (zh) 陶瓷电子组件及其制造方法
JP6923118B2 (ja) 積層セラミック電子部品及びその製造方法
US9673383B2 (en) Multilayer ceramic electronic component and method of manufacturing the same
US9466424B2 (en) Paste for external electrode, multilayer ceramic electronic component, and method of manufacturing the same
US9520234B2 (en) Multilayer ceramic capacitor, manufacturing method thereof and board for mounting the same thereon
JP2015115601A (ja) 積層セラミックキャパシタ、その製造方法及び積層セラミックキャパシタの実装基板
JP2012253337A (ja) 積層セラミック電子部品
CN110931254B (zh) 多层陶瓷电容器及制造多层陶瓷电容器的方法
JP2011151353A (ja) 固体電解コンデンサ及びその製造方法
CN110880413A (zh) 多层陶瓷电子组件
CN108364786A (zh) 积层陶瓷电容器及其制造方法
JP2020061537A (ja) 積層セラミック電子部品
US20130258551A1 (en) Conductive paste composition for internal electrode and multilayer ceramic electronic component including the same
KR101018240B1 (ko) 적층 세라믹 캐패시터 및 그 제조방법
US20160020031A1 (en) Composite electronic component and board having the same
JP2019096862A (ja) 積層セラミックキャパシタ及びその製造方法
JP7180048B2 (ja) セラミック複合体シート及びコンデンサ
US10028381B2 (en) Composite electronic component and board having the same
US20160141116A1 (en) Metal powder, electronic component and method of producing the same
JP2013073952A (ja) チップ型電子部品及びチップ型電子部品の実装構造
US11211204B2 (en) Solid electrolytic capacitor and method for manufacturing same
US10347429B2 (en) Capacitor and method for manufacturing the same

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18767274

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019506042

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18767274

Country of ref document: EP

Kind code of ref document: A1