WO2018012864A1 - Feuille de métal monocristallin et procédé de fabrication associé - Google Patents

Feuille de métal monocristallin et procédé de fabrication associé Download PDF

Info

Publication number
WO2018012864A1
WO2018012864A1 PCT/KR2017/007438 KR2017007438W WO2018012864A1 WO 2018012864 A1 WO2018012864 A1 WO 2018012864A1 KR 2017007438 W KR2017007438 W KR 2017007438W WO 2018012864 A1 WO2018012864 A1 WO 2018012864A1
Authority
WO
WIPO (PCT)
Prior art keywords
metal foil
single crystal
polycrystalline
chamber
foil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2017/007438
Other languages
English (en)
Korean (ko)
Inventor
에스. 루오프로드니
진성환
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Institute for Basic Science
UNIST Academy Industry Research Corp
Original Assignee
Institute for Basic Science
UNIST Academy Industry Research Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020170087731A external-priority patent/KR101878465B1/ko
Application filed by Institute for Basic Science, UNIST Academy Industry Research Corp filed Critical Institute for Basic Science
Priority to CN201780043041.0A priority Critical patent/CN109477237B/zh
Priority to CA3029783A priority patent/CA3029783C/fr
Priority to EP17827934.5A priority patent/EP3483309A4/fr
Priority to AU2017297850A priority patent/AU2017297850B2/en
Priority to US16/317,332 priority patent/US11078594B2/en
Publication of WO2018012864A1 publication Critical patent/WO2018012864A1/fr
Anticipated expiration legal-status Critical
Priority to US17/354,104 priority patent/US11879183B2/en
Ceased legal-status Critical Current

Abstract

La présente invention concerne un procédé de fabrication d'une feuille de métal monocristallin comprenant une étape de traitement thermique d'une feuille de métal polycristallin positionnée de manière à être espacée d'une base pour obtenir une feuille de métal monocristallin, et une feuille de métal monocristallin ainsi fabriquée, et permet de fournir une feuille de métal monocristallin ayant une grande surface par traitement thermique de la feuille de métal polycristallin dans des conditions de contrainte minimale appliquée à la feuille de métal polycristallin.
PCT/KR2017/007438 2016-07-12 2017-07-12 Feuille de métal monocristallin et procédé de fabrication associé Ceased WO2018012864A1 (fr)

Priority Applications (6)

Application Number Priority Date Filing Date Title
CN201780043041.0A CN109477237B (zh) 2016-07-12 2017-07-12 单晶金属箔及其制造方法
CA3029783A CA3029783C (fr) 2016-07-12 2017-07-12 Ruban metallique monocristallin et methode de fabrication connexe
EP17827934.5A EP3483309A4 (fr) 2016-07-12 2017-07-12 Feuille de métal monocristallin et procédé de fabrication associé
AU2017297850A AU2017297850B2 (en) 2016-07-12 2017-07-12 Single crystalline metal foil and manufacturing method therefor
US16/317,332 US11078594B2 (en) 2016-07-12 2017-07-12 Single crystalline metal foil and manufacturing method therefor
US17/354,104 US11879183B2 (en) 2016-07-12 2021-06-22 Single crystalline metal foil and manufacturing method therefor

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
KR20160087904 2016-07-12
KR10-2016-0087904 2016-07-12
KR10-2017-0087731 2017-07-11
KR1020170087731A KR101878465B1 (ko) 2016-07-12 2017-07-11 단결정 금속포일, 및 이의 제조방법

Related Child Applications (2)

Application Number Title Priority Date Filing Date
US16/317,332 A-371-Of-International US11078594B2 (en) 2016-07-12 2017-07-12 Single crystalline metal foil and manufacturing method therefor
US17/354,104 Division US11879183B2 (en) 2016-07-12 2021-06-22 Single crystalline metal foil and manufacturing method therefor

Publications (1)

Publication Number Publication Date
WO2018012864A1 true WO2018012864A1 (fr) 2018-01-18

Family

ID=60952656

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2017/007438 Ceased WO2018012864A1 (fr) 2016-07-12 2017-07-12 Feuille de métal monocristallin et procédé de fabrication associé

Country Status (1)

Country Link
WO (1) WO2018012864A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110616454A (zh) * 2019-03-07 2019-12-27 北京大学 一种基于单晶二维材料/单晶铜的垂直异质外延单晶金属薄膜的方法
CN111663175A (zh) * 2019-03-07 2020-09-15 北京大学 一种通过嫁接制备单晶金属的方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10298000A (ja) * 1997-04-28 1998-11-10 Dowa Mining Co Ltd 板状単結晶およびその製造方法
US7922812B2 (en) * 2005-05-12 2011-04-12 Intellectual Ventures Holding 40 Llc Method for growing single crystals of metals
KR20130020351A (ko) 2011-08-19 2013-02-27 한국전기연구원 그래핀 박막의 형성방법 및 그 방법에 의해 제조된 그래핀
KR101428498B1 (ko) * 2010-03-09 2014-08-08 가부시키가이샤 도요다 지도숏키 복합 산화물의 제조 방법, 리튬 이온 2차 전지용 정극 활물질, 리튬 이온 2차 전지 및 차량
KR20140137301A (ko) 2013-05-21 2014-12-02 한양대학교 산학협력단 대면적의 단결정 단일막 그래핀 및 그 제조방법
KR20150141139A (ko) * 2014-06-09 2015-12-17 한양대학교 산학협력단 수소 원자 또는 수소 이온을 함유하는 단결정 금속막 및 그 제조방법

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10298000A (ja) * 1997-04-28 1998-11-10 Dowa Mining Co Ltd 板状単結晶およびその製造方法
US7922812B2 (en) * 2005-05-12 2011-04-12 Intellectual Ventures Holding 40 Llc Method for growing single crystals of metals
KR101428498B1 (ko) * 2010-03-09 2014-08-08 가부시키가이샤 도요다 지도숏키 복합 산화물의 제조 방법, 리튬 이온 2차 전지용 정극 활물질, 리튬 이온 2차 전지 및 차량
KR20130020351A (ko) 2011-08-19 2013-02-27 한국전기연구원 그래핀 박막의 형성방법 및 그 방법에 의해 제조된 그래핀
KR20140137301A (ko) 2013-05-21 2014-12-02 한양대학교 산학협력단 대면적의 단결정 단일막 그래핀 및 그 제조방법
KR20150141139A (ko) * 2014-06-09 2015-12-17 한양대학교 산학협력단 수소 원자 또는 수소 이온을 함유하는 단결정 금속막 및 그 제조방법

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
KUMAR, A. ET AL.: "Rapid - synthesis of few-layer graphene over Cu foil", CARBON, vol. 50, no. 4, 25 November 2011 (2011-11-25), pages 1546 - 1553, XP028440551, DOI: 10.1016/j.carbon.2011.11.033 *
See also references of EP3483309A4

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110616454A (zh) * 2019-03-07 2019-12-27 北京大学 一种基于单晶二维材料/单晶铜的垂直异质外延单晶金属薄膜的方法
CN111663175A (zh) * 2019-03-07 2020-09-15 北京大学 一种通过嫁接制备单晶金属的方法
CN111663175B (zh) * 2019-03-07 2021-03-23 北京大学 一种通过嫁接制备单晶金属的方法

Similar Documents

Publication Publication Date Title
KR101997545B1 (ko) 단결정 금속포일, 및 이의 제조방법
CN108950684B (zh) 一种制备单晶金属箔的方法
WO2010056061A2 (fr) Nanofil de cobalt germanium monocristallin, structure de nanofil de cobalt germanium, et procédé de fabrication afférent
CN103531447B (zh) 一种降低氮化镓纳米线阵列晶体缺陷密度的方法
WO2018012864A1 (fr) Feuille de métal monocristallin et procédé de fabrication associé
WO2019106644A1 (fr) Feuille métallique monocristalline et procédé de fabrication associé
CN112456452A (zh) 一种二硒化锗纳米材料的制备方法
WO2014189271A1 (fr) Graphene en monocouche moncristalline a grande surface et procede de fabrication associe
CN105377753B (zh) 利用覆盖构件制造石墨烯的方法和制造包含该石墨烯的电子元件的方法
WO2010134691A2 (fr) Procédé de fabrication de couche mince à base de silicium polycristallin
CN105523548B (zh) 一种控制石墨烯晶核生长的载具
US20090087567A1 (en) Method of fabricating one-dimensional metallic nanostructure
WO2020130371A1 (fr) Film métallique monocristallin formé par croissance de grain anormale d'un film métallique polycristallin, et son procédé de fabrication
Xiang et al. Catalytic synthesis of single-crystalline gallium nitride nanobelts
CN116200824B (zh) 黑磷薄膜的制备方法
CN1834308A (zh) 一种合成碳化硅纳米棒的方法
WO2009093842A2 (fr) Procédé de fabrication de nanofils monocristallins de bismuth
Zhou et al. Large-scale fabrication and characterization of Cd-doped ZnO nanocantilever arrays
CN100402695C (zh) 物理气相沉积法直接生长成份单一的金属纳米线
Stöger-Pollach et al. Phase transformations of an alumina membrane and its influence on silicon nucleation during the aluminium induced layer exchange
CN118996597B (zh) 一种应变协同制备大尺寸单晶金属箔的方法
WO2025089840A1 (fr) Substrat ayant un film mince monocristallin formé sur celui-ci et structure stratifiée monocristalline le comprenant
WO2013118965A1 (fr) Procédé pour la fabrication de nanofil d'alliage or-argent monocristallin
Ma et al. Rapid preparation of Cu (111) foil with large single-crystal grains through a graphene induction and contactless annealing method
WO2025100802A1 (fr) Substrat ayant une surface supérieure orientée vers (111) un plan cristallin, structure stratifiée de graphène le comprenant, et dispositif électrique le comprenant

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17827934

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 3029783

Country of ref document: CA

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2017297850

Country of ref document: AU

Date of ref document: 20170712

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2017827934

Country of ref document: EP

Effective date: 20190211