WO2018006251A1 - Film à barrière élevée modifié - Google Patents

Film à barrière élevée modifié Download PDF

Info

Publication number
WO2018006251A1
WO2018006251A1 PCT/CN2016/088464 CN2016088464W WO2018006251A1 WO 2018006251 A1 WO2018006251 A1 WO 2018006251A1 CN 2016088464 W CN2016088464 W CN 2016088464W WO 2018006251 A1 WO2018006251 A1 WO 2018006251A1
Authority
WO
WIPO (PCT)
Prior art keywords
content
mxd6
rare earth
nucleating agent
barrier film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2016/088464
Other languages
English (en)
Chinese (zh)
Inventor
杜秀艳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to PCT/CN2016/088464 priority Critical patent/WO2018006251A1/fr
Publication of WO2018006251A1 publication Critical patent/WO2018006251A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un film à barrière élevée modifié, ledit film comprenant une couche superficielle (a), une couche centrale et une couche superficielle (b), et étant caractérisé en ce que : dans la couche superficielle (a), la teneur en MXD6 est de 30 à 40 %, la teneur en PA6 est de 63 à 85 %, la teneur en mélange maître anti-collant est de 2 à 4 %, la teneur en agent de compatibilité est de 3 à 8 % et la teneur en agent de nucléation de terres rares nanométrique est de 5,5 à 8 % ; dans la couche centrale, la teneur en MXD6 est de 95 à 99,9 % et la teneur en agent de nucléation de terres rares nanométrique est de 0,1 à 5 % ; dans la couche superficielle (b), la teneur en MXD6 est de 10 à 30 %, la teneur en PA6 est de 63 à 85 %, la teneur en mélange maître anti-collant est de 2 à 4 %, la teneur en agent de compatibilité est de 8,5 à 12 % et la teneur en agent de nucléation de terres rares nanométrique est de 2 à 4,5 %. Le film à barrière élevée modifié présente un allongement à la rupture amélioré et un trouble réduit.
PCT/CN2016/088464 2016-07-04 2016-07-04 Film à barrière élevée modifié Ceased WO2018006251A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/CN2016/088464 WO2018006251A1 (fr) 2016-07-04 2016-07-04 Film à barrière élevée modifié

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CN2016/088464 WO2018006251A1 (fr) 2016-07-04 2016-07-04 Film à barrière élevée modifié

Publications (1)

Publication Number Publication Date
WO2018006251A1 true WO2018006251A1 (fr) 2018-01-11

Family

ID=60901495

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2016/088464 Ceased WO2018006251A1 (fr) 2016-07-04 2016-07-04 Film à barrière élevée modifié

Country Status (1)

Country Link
WO (1) WO2018006251A1 (fr)

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6365248B1 (en) * 1998-07-15 2002-04-02 Idemitsu Petrochemical Co., Ltd. Easily tearable laminated barrier film and bag product using the same
EP1541340A1 (fr) * 2003-12-09 2005-06-15 Amcor Flexibles Europe A/S Stratifiés autoclavables avec barrière anti-migration
JP2006040595A (ja) * 2004-07-23 2006-02-09 Showa Denko Packaging Co Ltd 電子部品ケース用包材及び電子部品用ケース並びに電子部品
CN102837474A (zh) * 2011-06-20 2012-12-26 厦门长塑实业有限公司 一种高阻隔性薄膜及其制作方法
CN102896849A (zh) * 2012-07-19 2013-01-30 厦门长塑实业有限公司 高阻隔尼龙薄膜及其制备方法
CN103254635A (zh) * 2013-03-15 2013-08-21 东风(十堰)非金属部件有限公司 一种稀土改性增韧尼龙材料及其制备方法
CN104354411A (zh) * 2014-10-28 2015-02-18 厦门长塑实业有限公司 一种纳米稀土成核剂改性的高阻隔薄膜

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6365248B1 (en) * 1998-07-15 2002-04-02 Idemitsu Petrochemical Co., Ltd. Easily tearable laminated barrier film and bag product using the same
EP1541340A1 (fr) * 2003-12-09 2005-06-15 Amcor Flexibles Europe A/S Stratifiés autoclavables avec barrière anti-migration
JP2006040595A (ja) * 2004-07-23 2006-02-09 Showa Denko Packaging Co Ltd 電子部品ケース用包材及び電子部品用ケース並びに電子部品
CN102837474A (zh) * 2011-06-20 2012-12-26 厦门长塑实业有限公司 一种高阻隔性薄膜及其制作方法
CN102896849A (zh) * 2012-07-19 2013-01-30 厦门长塑实业有限公司 高阻隔尼龙薄膜及其制备方法
CN103254635A (zh) * 2013-03-15 2013-08-21 东风(十堰)非金属部件有限公司 一种稀土改性增韧尼龙材料及其制备方法
CN104354411A (zh) * 2014-10-28 2015-02-18 厦门长塑实业有限公司 一种纳米稀土成核剂改性的高阻隔薄膜

Similar Documents

Publication Publication Date Title
Wu et al. Polylactide/halloysite nanotube nanocomposites: Thermal, mechanical properties, and foam processing
CN104479205B (zh) 一种石墨烯改性聚乙烯高强度复合薄型制品的注塑成型方法
Montes et al. Synergistic reinforcement of poly (vinyl alcohol) nanocomposites with cellulose nanocrystal-stabilized graphene
Ljungberg et al. Nanocomposites of isotactic polypropylene reinforced with rod-like cellulose whiskers
CN103097445B (zh) 包含用改性层状硅酸盐增强的聚乳酸的聚合物纳米复合物
Bindhu et al. Boron Nitride reinforced polylactic acid composites film for packaging: Preparation and properties
JP6746911B2 (ja) エチレン−ビニルエステル系共重合体ケン化物組成物ペレットおよびその製造方法
McCardle et al. Effect of Reinforcement Orientation on the Mechanical Properties of Microfibrillar PP/PET and PET Single‐Polymer Composites
CN103640290B (zh) 高阻隔性完全生物降解复合膜
CN105835491B (zh) 一种双向收缩耐老化共聚酯薄膜及其制备方法
US20130085212A1 (en) Procedure for the obtainment of nanocomposite materials
Luna et al. Polymer nanocomposites for food packaging
CN105189633B (zh) Pet 纳米复合材料和由其制备的容器
Xu et al. Highly efficient three-dimensional gas barrier network for biodegradable nanocomposite films at extremely low loading levels of graphene oxide nanosheets
CN104877317A (zh) 一种熔融后能够快速立构复合的全生物基复合材料的制备方法
CN104448491A (zh) 一种石墨烯改性聚乙烯高强度复合薄型制品的挤出成型方法
CN104354411B (zh) 一种纳米稀土成核剂改性的高阻隔薄膜
Baouz et al. Effects of mixing protocols on impact modified poly (lactic acid) layered silicate nanocomposites
CN103540113A (zh) 碳酸钙填充改性提高聚碳酸亚丙酯力学性能的方法
Nuruddin et al. Processing and characterization of food-grade plasticizer-compatibilized cellulose nanocrystals and ethylene vinyl alcohol copolymer nanocomposites
CN112739779A (zh) 树脂组合物、成型体、及其应用
WO2018006251A1 (fr) Film à barrière élevée modifié
JP2018095863A (ja) 二軸延伸ポリアミド樹脂フィルム及びそれを用いた積層体。
CN104194016B (zh) 一种纳米花生蛋白高分子复合膜及其制备方法
EP3587478A1 (fr) Procédé d'obtention d'un film bioplastique et d'oxyde de graphène et / ou de graphène

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16907756

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

32PN Ep: public notification in the ep bulletin as address of the adressee cannot be established

Free format text: NOTING OF LOSS OF RIGHTS PURSUANT TO RULE 112(1) EPC (EPO FORM 1205 DATED 13/03/2019)

122 Ep: pct application non-entry in european phase

Ref document number: 16907756

Country of ref document: EP

Kind code of ref document: A1