WO2018084272A1 - Feuille de dissipation de chaleur pourvue d'une fine couche de saillies et d'évidements sur une surface de matériau de base, et élément de dissipation de chaleur - Google Patents

Feuille de dissipation de chaleur pourvue d'une fine couche de saillies et d'évidements sur une surface de matériau de base, et élément de dissipation de chaleur Download PDF

Info

Publication number
WO2018084272A1
WO2018084272A1 PCT/JP2017/039836 JP2017039836W WO2018084272A1 WO 2018084272 A1 WO2018084272 A1 WO 2018084272A1 JP 2017039836 W JP2017039836 W JP 2017039836W WO 2018084272 A1 WO2018084272 A1 WO 2018084272A1
Authority
WO
WIPO (PCT)
Prior art keywords
heat
fine uneven
uneven layer
area
substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2017/039836
Other languages
English (en)
Japanese (ja)
Inventor
修司 岩田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GlobaliCo ltd
Original Assignee
GlobaliCo ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GlobaliCo ltd filed Critical GlobaliCo ltd
Priority to JP2018549088A priority Critical patent/JP6839824B2/ja
Publication of WO2018084272A1 publication Critical patent/WO2018084272A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Le problème décrit par l'invention est de fournir une feuille de dissipation de chaleur qui puisse amener efficacement la température d'un élément chauffant à rayonner vers l'extérieur. La solution selon l'invention porte sur : un conducteur thermique qui diffuse la chaleur de l'élément chauffant sur toute la superficie; et un matériau de base disposé du côté surface du conducteur thermique, sur la surface duquel est formée une fine couche de saillies et d'évidements, et une partie en saille de la fine couche de saillies et d'évidements a une hauteur inférieure à 1 µm, et une densité supérieure ou égale à 100 unités/1 µm2. De préférence, la partie en saillie de la fine couche de saillies et d'évidements a une hauteur inférieure ou égale à 200 nm, et une densité supérieure ou égale à 400 unités/1 µm2. Dans la partie en saillie de la feuille de dissipation de chaleur, la taille de la superficie de la surface latérale de la partie en saillie est supérieure ou égale à 10 fois la taille de la superficie de base de la partie en saillie. La fine couche de saillies et d'évidements de la feuille de dissipation de chaleur est un film de revêtement formé sur le matériau de base de la feuille de dissipation de chaleur, au moyen d'une solution quelconque parmi : une solution d'un composé silicate de sel métallique alcalin, une solution d'un composé dioxyde de silicium particulaire ultrafin, ou une solution préparée par mélange d'alcools, d'un composé organique, d'un composé inorganique et d'eau avec ces solutions.
PCT/JP2017/039836 2016-11-02 2017-11-02 Feuille de dissipation de chaleur pourvue d'une fine couche de saillies et d'évidements sur une surface de matériau de base, et élément de dissipation de chaleur Ceased WO2018084272A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2018549088A JP6839824B2 (ja) 2016-11-02 2017-11-02 基材表面に微細凸凹層を設けた放熱シートおよび放熱部材

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016-215613 2016-11-02
JP2016215613 2016-11-02

Publications (1)

Publication Number Publication Date
WO2018084272A1 true WO2018084272A1 (fr) 2018-05-11

Family

ID=62076787

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/039836 Ceased WO2018084272A1 (fr) 2016-11-02 2017-11-02 Feuille de dissipation de chaleur pourvue d'une fine couche de saillies et d'évidements sur une surface de matériau de base, et élément de dissipation de chaleur

Country Status (2)

Country Link
JP (1) JP6839824B2 (fr)
WO (1) WO2018084272A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2022115093A (ja) * 2021-01-27 2022-08-08 河南▲き▼力新材料科技有限公司 熱伝導構造及び電子装置
JP2022115094A (ja) * 2021-01-27 2022-08-08 河南▲き▼力新材料科技有限公司 熱伝導構造及び電子装置

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09232482A (ja) * 1996-02-23 1997-09-05 Denso Corp 半導体の表面処理方法および半導体装置
WO2009142036A1 (fr) * 2008-05-21 2009-11-26 ニホンハンダ株式会社 Film de revêtement durci à rayonnement thermique, composition de revêtement, procédé de production dudit film de revêtement durci à rayonnement thermique, et dispositif électronique doté d’un film de revêtement à rayonnement thermique
JP2011096989A (ja) * 2009-11-02 2011-05-12 Keiwa Inc 太陽電池モジュール裏面用放熱シート及びこれを用いた太陽電池モジュール

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09232482A (ja) * 1996-02-23 1997-09-05 Denso Corp 半導体の表面処理方法および半導体装置
WO2009142036A1 (fr) * 2008-05-21 2009-11-26 ニホンハンダ株式会社 Film de revêtement durci à rayonnement thermique, composition de revêtement, procédé de production dudit film de revêtement durci à rayonnement thermique, et dispositif électronique doté d’un film de revêtement à rayonnement thermique
JP2011096989A (ja) * 2009-11-02 2011-05-12 Keiwa Inc 太陽電池モジュール裏面用放熱シート及びこれを用いた太陽電池モジュール

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2022115093A (ja) * 2021-01-27 2022-08-08 河南▲き▼力新材料科技有限公司 熱伝導構造及び電子装置
JP2022115094A (ja) * 2021-01-27 2022-08-08 河南▲き▼力新材料科技有限公司 熱伝導構造及び電子装置
JP7288101B2 (ja) 2021-01-27 2023-06-06 河南▲き▼力新材料科技有限公司 熱伝導構造及び電子装置
JP7288102B2 (ja) 2021-01-27 2023-06-06 河南▲き▼力新材料科技有限公司 熱伝導構造及び電子装置

Also Published As

Publication number Publication date
JPWO2018084272A1 (ja) 2019-12-19
JP6839824B2 (ja) 2021-03-10

Similar Documents

Publication Publication Date Title
CN104748606B (zh) 冷却结构体
US8537554B1 (en) Structured relief dielectric heat sink for planar photovoltaic cells and semiconductor devices
KR101070871B1 (ko) 태양광발전용 솔라셀 모듈의 백시트
KR101161735B1 (ko) 잠열을 이용한 지연 방열시트
US8592844B2 (en) Light-emitting diode device
JP2012508472A (ja) 太陽電池パネル部品用の熱伝導性材料
KR100923509B1 (ko) 자가 발전 조명장치와 이를 이용한 가로등
TW200933912A (en) Solar battery unit
WO2016111139A1 (fr) Feuille thermoconductrice d'accumulation de chaleur
WO2017086241A1 (fr) Radiateur, dispositif électronique, dispositif d'éclairage et procédé de fabrication de radiateur
JP5301173B2 (ja) 太陽電池アセンブリ
JP2016184706A (ja) 冷却構造および冷却部品
CN104267538A (zh) 一种高效散热的led背光源装置
TWI669843B (zh) 具備二次電池之發電裝置
US20170338166A1 (en) Structure, and electronic component and electronic device including the structure
JP6839824B2 (ja) 基材表面に微細凸凹層を設けた放熱シートおよび放熱部材
US20230140254A1 (en) Energy harvesting system using solar cell and thermoelectric device
JP2016100561A (ja) 放熱構造体、放熱構造体の製造方法、および電子機器
JP2005228855A (ja) 放熱器
CN204180460U (zh) 一种散热片
JP2017139842A (ja) 太陽電池モジュール用放熱性部材及びそれを用いた太陽電池モジュール
EP4349889A1 (fr) Film thermoconducteur et structure dissipatrice de chaleur mettant en oeuvre celui-ci
CN101785102B (zh) 具有发热部的装置
CN112270898A (zh) 一种用于液晶显示器的散热装置
KR20200136770A (ko) 방열효율이 향상된 탄소복합소재 구조를 포함하는 태양광모듈을 위한 방열시트 및 이를 포함하는 태양광모듈

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17867320

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2018549088

Country of ref document: JP

Kind code of ref document: A

32PN Ep: public notification in the ep bulletin as address of the adressee cannot be established

Free format text: NOTING OF LOSS OF RIGHTS PURSUANT TO RULE 112(1) EPC (EPO FORM 125A DATED 15-11-2019)

122 Ep: pct application non-entry in european phase

Ref document number: 17867320

Country of ref document: EP

Kind code of ref document: A1