WO2015159552A1 - メタクリル樹脂組成物、成形体、フィルムおよび偏光板 - Google Patents

メタクリル樹脂組成物、成形体、フィルムおよび偏光板 Download PDF

Info

Publication number
WO2015159552A1
WO2015159552A1 PCT/JP2015/002102 JP2015002102W WO2015159552A1 WO 2015159552 A1 WO2015159552 A1 WO 2015159552A1 JP 2015002102 W JP2015002102 W JP 2015002102W WO 2015159552 A1 WO2015159552 A1 WO 2015159552A1
Authority
WO
WIPO (PCT)
Prior art keywords
methacrylic resin
film
resin composition
mass
methacrylic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2015/002102
Other languages
English (en)
French (fr)
Inventor
淳裕 中原
達 阿部
祐作 野本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kuraray Co Ltd
Original Assignee
Kuraray Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kuraray Co Ltd filed Critical Kuraray Co Ltd
Priority to US15/304,970 priority Critical patent/US10633497B2/en
Priority to CN201580020421.3A priority patent/CN106232715B/zh
Priority to KR1020167031879A priority patent/KR20160147267A/ko
Priority to JP2016513649A priority patent/JP6470265B2/ja
Publication of WO2015159552A1 publication Critical patent/WO2015159552A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　透明性が高く、厚さ方向の位相差が小さく、また延伸しやすいメタクリル樹脂組成物を提供する。　本発明のメタクリル樹脂組成物は、メタクリル樹脂およびポリカーボネート樹脂を含み、前記ポリカーボネート樹脂は、１５０００より大きく３２０００より小さい粘度平均分子量を有し、前記メタクリル樹脂１００質量部に対する前記ポリカーボネート樹脂の含有量を１質量部以上、４質量部以下とし、当該メタクリル樹脂組成物に対して前記メタクリル樹脂と前記ポリカーボネート樹脂の合計量を８０～１００質量％とする。

Description

メタクリル樹脂組成物、成形体、フィルムおよび偏光板
　本発明は、メタクリル樹脂とポリカーボネート樹脂を含有して成るメタクリル樹脂組成物に関する。また、前記メタクリル樹脂組成物からなるフィルム、成形体、および前記フィルムを具備する偏光板に関する。
　液晶表示装置には各種の樹脂製フィルムが使用されている。このうち偏光子保護フィルムには、トリアセチルセルロースが主に使用されている。トリアセチルセルロースからなるフィルムは透湿度が高いため、薄膜化するにしたがって、偏光子の品質低下を引き起こす傾向がある。偏光子保護フィルムの改良は液晶表示装置の薄型化において課題となっている。
　そこで、新たな偏光子保護フィルムの材料としてメタクリル樹脂が検討されている。メタクリル樹脂からなるフィルムを延伸処理すると靭性が高まることが知られている（特許文献１参照）。ところが、通常のメタクリル樹脂フィルムを延伸すると位相差が大きくなり、例えばＩＰＳ液晶方式では画面の品位低下を引き起こしてしまう。
　メタクリル樹脂にポリカーボネート樹脂などの樹脂を添加することで、位相差の小さいフィルムを得やすくなることが知られている（特許文献２～５）。しかしながら、これらのメタクリル樹脂組成物は、延伸性に課題があった。このため、より薄膜に延伸する場合には割れ易くなり、また、延伸後のフィルムの強度を高めるために、より低い温度で延伸する場合には破断しやすくなるといった問題を抱えていた。
特公昭５７－３２９４２号公報 特開平５－３２８４６号公報 特開２０１２－５１４７５９号公報 特開２０１３－１４８６５５号公報 特開２０１４－５１６４９号公報
　本発明は、上記背景に鑑みて成されたものであり、その目的とするところは、透明性が高く、厚さ方向の位相差が小さく、延伸しやすいメタクリル樹脂組成物を提供することである。また、厚さが均一で且つ表面平滑性に優れ、生産性が高く、強度の大きいメタクリル樹脂組成物からなるフィルムを提供することである。
　本発明者らは、上記の目的を達成すべく検討を重ねた結果、以下の態様を包含する本発明を完成するに至った。
〔１〕：メタクリル樹脂およびポリカーボネート樹脂を含むメタクリル樹脂組成物であって、前記ポリカーボネート樹脂は、１５０００より大きく、３２０００より小さい粘度平均分子量を有しており、前記メタクリル樹脂１００質量部に対する前記ポリカーボネート樹脂の含有量が１質量部以上、４質量部以下であって、当該メタクリル樹脂組成物に対して前記メタクリル樹脂と前記ポリカーボネート樹脂の合計量を８０～１００質量％とするメタクリル樹脂組成物。
〔２〕：前記メタクリル樹脂組成物の分子量分布が１．３～１．５である〔１〕に記載のメタクリル樹脂組成物。
〔３〕：前記メタクリル樹脂が、三連子表示のシンジオタクティシティ（ｒｒ）が５０％以上であり、且つメタクリル酸メチルに由来する構造単位の含有量が９２質量％以上１００質量％以下である〔１〕または〔２〕に記載のメタクリル樹脂組成物。
〔４〕：前記メタクリル樹脂のシンジオタクティシティ（ｒｒ）が、５８％以上、８５％以下であるメタクリル樹脂である〔１〕～〔３〕のいずれかひとつに記載のメタクリル樹脂組成物。
〔５〕：前記メタクリル樹脂のメタクリル酸メチル由来の構造単位の含有量が、９９質量％以上であるメタクリル樹脂である〔１〕～〔４〕のいずれかひとつに記載のメタクリル樹脂組成物。
〔６〕：　前記メタクリル樹脂組成物の重量平均分子量が７００００～２０００００である〔１〕～〔５〕のいずれかひとつに記載のメタクリル樹脂組成物。
〔７〕：前記ポリカーボネート樹脂が、１５０００より大きく１８０００より小さい粘度平均分子量を有する〔１〕～〔６〕のいずれかひとつに記載のメタクリル樹脂組成物。
〔８〕：〔１〕～〔７〕のいずれかひとつに記載のメタクリル樹脂組成物からなる成形体。
〔９〕：〔１〕～〔７〕のいずれかひとつに記載のメタクリル樹脂組成物からなるフィルム。
〔１０〕：厚さが１０～５０μｍである、〔９〕に記載のフィルム。
〔１１〕：面積比で１．５～８倍に二軸延伸された〔９〕または〔１０〕に記載のフィルム。
〔１２〕：偏光子保護フィルムとして用いられる〔９〕～〔１１〕のいずれかひとつに記載のフィルム。
〔１３〕：〔１２〕に記載のフィルムが少なくとも１枚積層された偏光板。
　本発明によれば、透明性が高く、厚さ方向の位相差が小さく、且つ延伸しやすいメタクリル樹脂組成物を提供することができる。また、厚さが均一で且つ表面平滑性に優れ、生産性が高く、強度の大きいメタクリル樹脂組成物からなるフィルムを提供することができるという優れた効果を奏する。
本発明の実施形態に係る偏光板の一例を示す断面図である。
本発明のメタクリル樹脂組成物は、メタクリル樹脂およびポリカーボネート樹脂を含有するものである。また、本発明のフィルムは、メタクリル樹脂およびポリカーボネート樹脂を含有するメタクリル樹脂組成物からなるフィルムである。
　本発明に用いられるメタクリル樹脂は、得られるフィルムの耐熱性の観点からメタクリル酸メチルに由来する構造単位の含有量が、メタクリル樹脂の質量を基準にして、好ましくは９２質量％以上、より好ましくは９５質量％以上、さらに好ましくは９７質量％以上、特に好ましくは９９質量％以上、最も好ましくは１００質量％である。
　本発明に用いられるメタクリル樹脂は、メタクリル酸メチルに由来する構造単位以外の構造単位を含んでいても良く、例えば、メタクリル酸エチル、メタクリル酸シクロヘキシル、メタクリル酸ｔ－ブチル、メタクリル酸２－イソボルニル、メタクリル酸８－トリシクロ［５．２．１．０2,6］デカニル、メタクリル酸４－ｔ－ブチルシクロヘキシルなどのメタクリル酸メチル以外のメタクリル酸アルキルエステル；アクリル酸メチル、アクリル酸エチル、アクリル酸プロピル、アクリル酸ブチル、アクリル酸２－エチルへキシルなどのアクリル酸アルキルエステル；アクリル酸フェニルなどのアクリル酸アリールエステル；アクリル酸シクロへキシル、アクリル酸ノルボルネニルなどのアクリル酸シクロアルキルエステル；アクリルアミド；メタクリルアミド；アクリロニトリル；メタクリロニトリル；などの一分子中に重合性の炭素－炭素二重結合を一つだけ有するビニル系単量体に由来する構造単位が挙げられる。メタクリル酸メチルに由来する構造単位以外の構造単位は、好ましくは８質量％以下、より好ましくは５質量%以下、さらに好ましくは３質量％以下、特に好ましくは１質量％以下、最も好ましくは０質量％である。
　本発明に用いられるメタクリル樹脂は、三連子表示のシンジオタクティシティ（ｒｒ）の下限が、好ましくは５０％、より好ましくは５５％、さらに好ましくは５８％、よりさらに好ましくは５９％、最も好ましくは６０％である。該メタクリル樹脂は、製膜性の観点から、三連子表示のシンジオタクティシティ（ｒｒ）の上限が、好ましくは９９％、より好ましくは８５％、さらに好ましくは７７％、よりさらに好ましくは６５％、最も好ましくは６４％である。
　三連子表示のシンジオタクティシティ（ｒｒ）（以下、単に「シンジオタクティシティ（ｒｒ）」と称することがある。）は、連続する３つの構造単位の連鎖（３連子、ｔｒｉａｄ）が有する２つの連鎖（２連子、ｄｉａｄ）が、ともにラセモ（ｒｒと表記する）である割合である。なお、ポリマー分子中の構造単位の連鎖（２連子、ｄｉａｄ）において立体配置が同じものをメソ（ｍｅｓｏ）、逆のものをラセモ（ｒａｃｅｍｏ）と称し、それぞれｍ、ｒと表記する。
　メタクリル樹脂のシンジオタクティシティ（ｒｒ）（％）は、重水素化クロロホルム中、３０℃で、1Ｈ-ＮＭＲスペクトルを測定し、そのスペクトルからＴＭＳを０ｐｐｍとした際の、０．６～０．９５ｐｐｍの領域の面積（Ｘ）と０．６～１．３５ｐｐｍの領域の面積（Ｙ）とを計測し、式：（Ｘ／Ｙ）×１００にて算出することができる。
　本発明に用いられるメタクリル樹脂は、重量平均分子量（以下、「Ｍｗ」と称することがある。）が、好ましくは７００００以上、より好ましくは８００００～２０００００、さらに好ましくは８５０００～１６００００、さらにより好ましくは９００００～１２００００である。かかるＭｗが８００００以上で、かつ、シンジオタクティシティ（ｒｒ）が５０％以上あることで、得られるフィルムは、強度が高く、割れ難く、延伸し易い。そのためフィルムをより薄くすることができる。またＭｗが２０００００以下であることで、メタクリル樹脂の成形加工性が高まるので、得られるフィルムの厚さが均一で且つ表面平滑性に優れる傾向となる。
　本発明に用いられるメタクリル樹脂は、Ｍｗと数平均分子量（以下、「Ｍｎ」と称することがある。）の比（Ｍｗ／Ｍｎ：以下、この値を「分子量分布」と称することがある。）が、好ましくは１．２～２．０、より好ましくは１．３～１．７である。分子量分布が１．２以上であることでメタクリル樹脂の流動性が向上し、得られるフィルムは表面平滑性に優れる傾向となる。分子量分布が２．０以下であることで得られるフィルムは耐衝撃性および靭性に優れる傾向となる。なお、ＭｗおよびＭｎは、ゲルパーミエーションクロマトグラフィ（ＧＰＣ）で測定したクロマトグラムを標準ポリスチレンの分子量に換算した値である。
　本発明に用いられるメタクリル樹脂は、ＪＩＳ Ｋ７２１０に準拠して、２３０℃、３．８ｋｇ荷重の条件において測定される、メルトフローレートが、好ましくは０．１～５ｇ／１０分、さらに好ましくは０．５～４ｇ／１０分、最も好ましくは１.０～３ｇ／１０分である。
　本発明に用いられるメタクリル樹脂のガラス転移温度は、好ましくは１１０℃以上、より好ましくは１１８℃以上、さらに好ましくは１２０℃以上、よりさらに好ましくは１２３℃以上、最も好ましくは１２４℃以上である。該メタクリル樹脂のガラス転移温度の上限は、通常１３０℃である。ガラス転移温度は、分子量やシンジオタクティシティ（ｒｒ）を調節することによって制御することができる。ガラス転移温度がこの範囲にあると、得られるフィルムの熱収縮などの変形が起こり難い。なお、ガラス転移温度は、実施例に記載の方法で測定した中間点ガラス転移温度である。
　メタクリル樹脂の製造方法は特に制限されない。例えば、ラジカル重合法、アニオン重合法などの公知の重合法において、重合温度、重合時間、連鎖移動剤の種類や量、重合開始剤の種類や量などを調整することによって、Ｍｗ、シンジオタクティシティ（ｒｒ）などの特性が所望の範囲を満たすメタクリル樹脂を製造することができる。
　例えば、ラジカル重合法の場合、重合温度を８０℃以下にすることが好ましく、７０℃以下にすることがより好ましく、６０℃以下にすることがさらに好ましい。このように温度を調整すると、シンジオタクティシティ（ｒｒ）を高くすることが容易である。
　アニオン重合法の場合、重合開始剤として、ｎ－ブチルリチウム、ｓｅｃ－ブチルリチウム、イソブチルリチウム、ｔｅｒｔ－ブチルリチウム等のアルキルリチウムを用いることが好ましい。また、生産性の観点から、有機アルミニウム化合物を共存させることが好ましい。有機アルミニウムとしては、下記式：
　ＡｌＲ1Ｒ2Ｒ3
（式中、Ｒ1、Ｒ2およびＲ3はそれぞれ独立して置換基を有してもよいアルキル基、置換基を有していてもよいシクロアルキル基、置換基を有してもよいアリール基、置換基を有していてもよいアラルキル基、置換基を有してもよいアルコキシル基、置換基を有してもよいアリールオキシ基またはＮ，Ｎ－二置換アミノ基を表す。Ｒ2およびＲ3は、それぞれが結合してなる、置換基を有していてもよいアリーレンジオキシ基であってもよい。）
で示される化合物が挙げられる。具体的には、イソブチルビス（２，６－ジ－ｔｅｒｔ－ブチル－４－メチルフェノキシ）アルミニウム、イソブチルビス（２，６－ジ－ｔｅｒｔ－ブチルフェノキシ）アルミニウム、イソブチル〔２，２’－メチレンビス（４－メチル－６－ｔｅｒｔ－ブチルフェノキシ）〕アルミニウム等が挙げられる。
　また、アニオン重合法においては、重合反応を制御するために、エーテルや含窒素化合物などを共存させることもできる。
　また、メタクリル樹脂をアニオン重合法にて製造する場合、重合反応の途中で重合開始剤の量より少ない量、具体的には、重合開始剤の量に対して、好ましくは１モル％～５０モル％、より好ましくは２モル％～２０モル％、さらに好ましくは５モル％～１０モル％の重合停止剤を添加したり、または重合反応の途中で最初に添加した重合開始剤の量に対して、好ましくは１モル％～５０モル％、より好ましくは２モル％～２０モル％、さらに好ましくは５モル％～１０モル％の重合開始剤を追加添加したりすることによって、重量平均分子量を調整できる。
　重量平均分子量、シンジオタクティシティ（ｒｒ）などが所望の特性を有するメタクリ樹脂を得る第２の方法として、所望の特性を満たすメタクリル樹脂に、所望の特性を満たさないメタクリル樹脂を混合したり、所望の特性を満たさないメタクリル樹脂同士を適宜混合することにより、所望の特性（重量平均分子量、シンジオタクティシティ（ｒｒ）などの特性）を有するメタクリル樹脂を得る方法が挙げられる。かかる方法は、工程管理が容易である。複数種のメタクリル樹脂の混合は、公知の方法、例えばニーダールーダー、押出機、ミキシングロール、バンバリーミキサーなどの溶融混練装置を用いて行うことができる。混練時の温度は、使用するメタクリル樹脂の溶融温度に応じて適宜調節することができ、通常１５０℃～３００℃である。
　所望の特性を有するメタクリ樹脂を得る第３の製造方法として、所望の特性範囲から外れているメタクリル樹脂の存在下で単量体を重合して、所望の重量平均分子量、シンジオタクティシティ（ｒｒ）などの特性が所望の範囲を満たすメタクリル樹脂を製造する方法がある。かかる重合は上述したラジカル重合法やアニオン重合法と同様にして行うことができる。第３の製造方法によれば、第２の製造方法に比べて、メタクリル樹脂に掛かる熱履歴が短くなるので、メタクリル樹脂の熱分解が抑制され、着色や異物の少ないフィルムが得られやすい。
　上記のようなメタクリル樹脂の製造方法のうち、透明性の高いメタクリル樹脂が容易に製造できるという観点から、アニオン重合法によって特性が所望の範囲を満たすメタクリル樹脂を製造する方法；アニオン重合法で製造されたメタクリル樹脂と、ラジカル重合で製造されたメタクリル樹脂を混合することによって特性が所望の範囲を満たすメタクリル樹脂を製造する方法；およびアニオン重合法で製造されたメタクリル樹脂と、別のアニオン重合法で製造されたメタクリル樹脂とを混合することによって特性が本発明の所望の範囲を満たすメタクリル樹脂を製造する方法が好ましく、アニオン重合法で製造されたメタクリル樹脂と、ラジカル重合で製造されたメタクリル樹脂を混合することによって特性が本発明の所望の範囲を満たすメタクリル樹脂を製造する方法がより好ましい。
　本発明に用いられるポリカーボネート樹脂は、多官能ヒドロキシ化合物と炭酸エステル形成性化合物との反応によって得られる重合体である。該ポリカーボネート樹脂は、メタクリル樹脂との相溶性、得られるフィルムの透明性がよいという観点から、芳香族ポリカーボネート樹脂が好ましい。
　本発明に用いられるポリカーボネート樹脂は、得られるメタクリル樹脂組成物からなるフィルムの延伸性が高いという観点から、粘度平均分子量（以下、「Ｍｖ」と称することがある）が１５０００より大きいものを用いる。Ｍｖは、１５５００より大きいことが好ましく、１５８００より大きいことがより好ましく、１６０００より大きいことが最も好ましい。またメタクリル樹脂との相溶性の観点から、Ｍｖは３２０００より小さいものを用いる。Ｍｖは、２２０００より小さいことが好ましく、１９０００より小さいことが更に好ましく、１８０００より小さいことが最も好ましい。使用するメタクリル樹脂のシンジオタクティシティ（ｒｒ）が高いほど、ポリカーボネート樹脂との相溶性が高く、より大きな粘度平均分子量のポリカーボネート樹脂を使用することができる。
　ポリカーボネート樹脂の粘度平均分子量（Ｍｖ）は、キャノン－フェンスケ粘度計やウベローデ粘度計を用いてポリカーボネート樹脂０．５ｇを塩化メチレン１００ｍＬに溶解した溶液の比粘度ηｓｐを２０℃で測定し、下記のＳｃｈｎｅｌｌの式を満足する値として、２０℃の塩化メチレン溶液の極限粘度[η]から、算出することができる。
ηｓｐ／ｃ＝［η］＋０．４５×［η］2 ｃ
（但し［η］は極限粘度、上記条件ではｃ＝０．５）
［η］＝１．２３×１０- 4 Ｍｖ0 . 8 3
　また、本発明に用いられるポリカーボネート樹脂の３００℃、１．２ＫｇでのＭＶＲ（メルトボリュームフローレート）値は、メタクリル樹脂との相溶性の観点から、１ｃｍ3／１０分より大きいことが好ましく、１０ｃｍ3／１０分より大きいことがより好ましく、２０ｃｍ3／１０分より大きいことが更に好ましく、２５ｃｍ3／１０分より大きいことが最も好ましい。また、得られるメタクリル樹脂組成物の延伸性が高いという観点から、６０ｃｍ3／１０分より小さいことが好ましく、５１ｃｍ3／１０分より小さいことがより好ましく、４７ｃｍ3／１０分より小さいことが更に好ましく、４４ｃｍ3／１０分より小さいことが最も好ましい。
　また、本発明に用いられるポリカーボネート樹脂は、ゲルパーミエーションクロマトグラフィ（ＧＰＣ）で測定したクロマトグラムを標準ポリスチレンの分子量に換算した重量平均分子量（Ｍｗ）が、得られるメタクリル樹脂組成物の延伸性が高いという観点から、３０８００ｇ／モルより大きいことが好ましい。前記Ｍｗは、３２１００ｇ／モルより大きいことがより好ましく、３２８００ｇ／モルより大きいことが更に好ましく、３３３００ｇ／モルより大きいことが最も好ましい。また、メタクリル樹脂との相溶性の観点から、前記Ｍｗは、７５０００ｇ／モルより小さいことが好ましく、４８４００ｇ／モルより小さいことがより好ましく、４０７００ｇ／モルより小さいことが更に好ましく、３８２００ｇ／モルより小さいことが最も好ましい。
　なお、ポリカーボネート樹脂の粘度平均分子量、ＭＶＲ値および重量平均分子量は末端停止剤や分岐剤の量を調整することによって行うことができる。
　本発明に用いられるポリカーボネート樹脂は、メタクリル樹脂との相溶性を高め、メタクリル樹脂組成物の透明性を高めるという観点から、１５０００より大きい粘度平均分子量のポリカーボネート樹脂と、１２０００より小さい粘度平均分子量のポリカーボネート樹脂を混合することで、上述したように１５０００より大きく、３２０００より小さい粘度平均分子量を有するポリカーボネート樹脂に調整することもできる。
　本発明に用いられるポリカーボネート樹脂のガラス転移温度は、好ましくは１３０℃以上、より好ましくは１３５℃以上、さらに好ましくは１４０℃以上である。該ポリカーネト樹脂のガラス転移温度の上限は、通常１８０℃である。
　ポリカーボネート樹脂の製造方法は、特に限定されない。例えば、ホスゲン法（界面重合法）及び溶融重合法（エステル交換法）などが挙げられる。また、本発明に好ましく用いられる芳香族ポリカーボネート樹脂は、溶融重合法で製造したポリカーボネート樹脂原料に、末端ヒドロキシ基量を調整するための処理を施して成るものであってもよい。
　ポリカーボネート樹脂を製造するための原料である多官能ヒドロキシ化合物としては、置換基を有していてもよい４，４’－ジヒドロキシビフェニル類；置換基を有していてもよいビス（ヒドロキシフェニル）アルカン類；置換基を有していてもよいビス（４－ヒドロキシフェニル）エーテル類；置換基を有していてもよいビス（４－ヒドロキシフェニル）スルフィド類；置換基を有していてもよいビス（４－ヒドロキシフェニル）スルホキシド類；置換基を有していてもよいビス（４－ヒドロキシフェニル）スルホン類；置換基を有していてもよいビス（４－ヒドロキシフェニル）ケトン類；置換基を有していてもよいビス（ヒドロキシフェニル）フルオレン類；置換基を有していてもよいジヒドロキシ－ｐ－ターフェニル類；置換基を有していてもよいジヒドロキシ－ｐ－クォーターフェニル類；置換基を有していてもよいビス（ヒドロキシフェニル）ピラジン類；置換基を有していてもよいビス（ヒドロキシフェニル）メンタン類；置換基を有していてもよいビス〔２－（４－ヒドロキシフェニル）－２－プロピル〕ベンゼン類；置換基を有していてもよいジヒドロキシナフタレン類；置換基を有していてもよいジヒドロキシベンゼン類；置換基を有していてもよいポリシロキサン類；置換基を有していてもよいジヒドロパーフルオロアルカン類などが挙げられる。
　これらの多官能ヒドロキシ化合物の中でも、２，２－ビス（４－ヒドロキシフェニル）プロパン、１，１－ビス（４－ヒドロキシフェニル）シクロヘキサン、ビス（４－ヒドロキシフェニル）ジフェニルメタン、１，１－ビス（４－ヒドロキシフェニル）－１－フェニルエタン、２，２－ビス（４－ヒドロキシ－３－メチルフェニル）プロパン、２，２－ビス（４－ヒドロキシ－３－フェニルフェニル）プロパン、４，４'－ジヒドロキシビフェニル、ビス（４－ヒドロキシフェニル）スルホン、２，２－ビス（３，５－ジブロモ－４－ヒドロキシフェニル）プロパン、３，３－ビス（４－ヒドロキシフェニル）ペンタン、９，９－ビス（４－ヒドロキシ－３－メチルフェニル）フルオレン、ビス（４－ヒドロキシフェニル）エーテル、４，４’－ジヒドロキシベンゾフェノン、２，２－ビス（４－ヒドロキシ－３－メトキシフェニル）１，１，１，３，３，３－ヘキサフルオロプロパン、α，ω－ビス〔３－（２－ヒドロキシフェニル）プロピル〕ポリジメチルシロキサン、レゾルシン、２，７－ジヒドロキシナフタレンが好ましく、特に２，２－ビス（４－ヒドロキシフェニル）プロパンが好ましい。
　炭酸エステル形成性化合物としては、ホスゲンなどの各種ジハロゲン化カルボニルや、クロロホーメートなどのハロホーメート、ビスアリールカーボネートなどの炭酸エステル化合物が挙げられる。この炭酸エステル形成性化合物の量は、反応の化学量論比（当量）を考慮して適宜調整すればよい。
　反応は、通常、酸結合剤の存在下に溶媒中で行われる。酸結合剤としては、水酸化ナトリウム、水酸化カリウム、水酸化リチウム、水酸化セシウムなどのアルカリ金属水酸化物や、炭酸ナトリウム、炭酸カリウムなどのアルカリ金属炭酸塩や、トリメチルアミン、トリエチルアミン、トリブチルアミン、Ｎ，Ｎ－ジメチルシクロヘキシルアミン、ピリジン、ジメチルアニリンなどの三級アミン、トリメチルベンジルアンモニウムクロライド、トリエチルベンジルアンモニウムクロライド、トリブチルベンジルアンモニウムクロライド、トリオクチルメチルアンモニウムクロライド、テトラブチルアンモニウムクロライド、テトラブチルアンモニウムブロマイドなどの四級アンモニウム塩、テトラブチルホスホニウムクロライド、テトラブチルホスホニウムブロマイドなどの四級ホスホニウム塩などが挙げられる。さらに、所望により、この反応系に亜硫酸ナトリウムやハイドロサルファイドなどの酸化防止剤を少量添加してもよい。酸結合剤の量は、反応の化学量論比（当量）を考慮して適宜調整すればよい。具体的には、原料の多官能ヒドロキシ化合物の水酸基１モル当たり、１当量もしくはそれより過剰な量、好ましくは１～５当量の酸結合剤を使用すればよい。
　また、反応には、公知の末端停止剤や分岐剤を用いることができる。末端停止剤としては、ｐ－ｔｅｒｔ－ブチル－フェノール、ｐ－フェニルフェノール、ｐ－クミルフェノール、ｐ－パーフルオロノニルフェノール、ｐ－（パーフルオロノニルフェニル）フェノール、ｐ－（パーフルオロヘキシルフェニル）フェノール、ｐ－ｔｅｒｔ－パーフルオロブチルフェノール、１－（Ｐ－ヒドロキシベンジル）パーフルオロデカン、ｐ－〔２－（１Ｈ，１Ｈ－パーフルオロトリドデシルオキシ）－１，１，１，３，３，３－ヘキサフルオロプロピル〕フェノール、３，５－ビス（パーフルオロヘキシルオキシカルボニル）フェノール、ｐ－ヒドロキシ安息香酸パーフルオロドデシル、ｐ－（１Ｈ，１Ｈ－パーフルオロオクチルオキシ）フェノール、２Ｈ，２Ｈ，９Ｈ－パーフルオロノナン酸、１，１，１，３，３，３－テトラフロロ－２－プロパノールなどが挙げられる。
　分岐剤としては、フロログリシン、ピロガロール、４，６－ジメチル－２，４，６－トリス（４－ヒドロキシフェニル）－２－ヘプテン、２，６－ジメチル－２，４，６－トリス（４－ヒドロキシフェニル）－３－ヘプテン、２，４－ジメチル－２，４，６－トリス（４－ヒドロキシフェニル）ヘプタン、１，３，５－トリス（２－ヒドロキシフェニル）ベンゼン、１，３，５－トリス（４－ヒドロキシフェニル）ベンゼン、１，１，１－トリス（４－ヒドロキシフェニル）エタン、トリス（４－ヒドロキシフェニル）フェニルメタン、２，２－ビス〔４，４－ビス（４－ヒドロキシフェニル）シクロヘキシル〕プロパン、２，４－ビス〔２－ビス（４－ヒドロキシフェニル）－２－プロピル〕フェノール、２，６－ビス（２－ヒドロキシ－５－メチルベンジル）－４－メチルフェノール、２－（４－ヒドロキシフェニル）－２－（２，４－ジヒドロキシフェニル）プロパン、テトラキス（４－ヒドロキシフェニル）メタン、テトラキス〔４－（４－ヒドロキシフェニルイソプロピル）フェノキシ〕メタン、２，４－ジヒドロキシ安息香酸、トリメシン酸、シアヌル酸、３，３－ビス（３－メチル－４－ヒドロキシフェニル）－２－オキソ－２，３－ジヒドロインドール、３，３－ビス（４－ヒドロキシアリール）オキシインドール、５－クロロイサチン、５，７－ジクロロイサチン、５－ブロモイサチンなどが挙げられる。
　ポリカーボネート樹脂は、ポリカーボネート単位以外に、ポリエステル、ポリウレタン、ポリエーテルもしくはポリシロキサン構造を有する単位等を含有しているものであってもよい。
　本発明に用いられるメタクリル樹脂組成物に含有されるポリカーボネート樹脂の量は、前記メタクリル樹脂１００質量部に対して１質量部以上、４質量部以下、より好ましくは２質量部以上、４質量部以下、さらに好ましくは、２質量部以上、３質量部以下である。
　本発明に用いられるメタクリル樹脂組成物に含有されるメタクリル樹脂とポリカーボネート樹脂との合計量は、メタクリル樹脂組成物に対して８０～１００質量％、好ましくは９０～１００質量％、より好ましくは９４～１００質量％、さらに好ましくは９６～１００質量％である。
　本発明のメタクリル樹脂組成物は、本発明の効果を損なわない範囲で、必要に応じてフィラーを含んでいてもよい。フィラーとしては、炭酸カルシウム、タルク、カーボンブラック、酸化チタン、シリカ、クレー、硫酸バリウム、炭酸マグネシウムなどが挙げられる。本発明のメタクリル樹脂組成物に含有し得るフィラーの量は、好ましくは３質量％以下、より好ましくは１．５質量％以下である。
　本発明のメタクリル樹脂組成物には、本発明の効果を損なわない範囲で、他の重合体を含んでいてもよい。他の重合体としては、ポリエチレン、ポリプロピレン、ポリブテン－１、ポリ－４－メチルペンテン－１、ポリノルボルネンなどのポリオレフィン樹脂；エチレン系アイオノマー；ポリスチレン、スチレン－無水マレイン酸共重合体、ハイインパクトポリスチレン、ＡＳ樹脂、ＡＢＳ樹脂、ＡＥＳ樹脂、ＡＡＳ樹脂、ＡＣＳ樹脂、ＭＢＳ樹脂などのスチレン系樹脂；メチルメタクリレート－スチレン共重合体；ポリエチレンテレフタレート、ポリブチレンテレフタレートなどのポリエステル樹脂；ナイロン６、ナイロン６６、ポリアミドエラストマーなどのポリアミド；ポリ塩化ビニル、ポリ塩化ビニリデン、ポリビニルアルコール、エチレン－ビニルアルコール共重合体、ポリアセタール、ポリフッ化ビニリデン、ポリウレタン、変性ポリフェニレンエーテル、ポリフェニレンスルフィド、シリコーン変性樹脂；アクリルゴム、シリコーンゴム；ＳＥＰＳ、ＳＥＢＳ、ＳＩＳなどのスチレン系熱可塑性エラストマー；ＩＲ、ＥＰＲ、ＥＰＤＭなどのオレフィン系ゴムなどが挙げられる。本発明のメタクリル樹脂組成物に含有され得る他の重合体の量は、好ましくは１０質量％以下、より好ましくは５質量％以下、最も好ましくは０質量％である。
　本発明のメタクリル樹脂組成物には、本発明の効果を損なわない範囲で、酸化防止剤、熱劣化防止剤、紫外線吸収剤、光安定剤、滑剤、離型剤、高分子加工助剤、帯電防止剤、難燃剤、染顔料、光拡散剤、有機色素、艶消し剤、耐衝撃性改質剤、蛍光体などの添加剤を含有していてもよい。
　酸化防止剤は、酸素存在下においてそれ単体で樹脂の酸化劣化防止に効果を有するものである。例えば、リン系酸化防止剤、ヒンダードフェノール系酸化防止剤、チオエーテル系酸化防止剤などが挙げられる。これらの中、着色による光学特性の劣化防止効果の観点から、リン系酸化防止剤やヒンダードフェノール系酸化防止剤が好ましく、リン系酸化防止剤とヒンダードフェノール系酸化防止剤との併用がより好ましい。
　リン系酸化防止剤とヒンダードフェノール系酸化防止剤とを併用する場合、リン系酸化防止剤／ヒンダードフェノール系酸化防止剤を質量比で０．２／１～２／１で使用するのが好ましく、０．５／１～１／１で使用するのがより好ましい。
　リン系酸化防止剤としては、２，２－メチレンビス（４，６－ジ－ｔｅｒｔ－ブチルフェニル）オクチルホスファイト（ＡＤＥＫＡ社製；商品名：アデカスタブＨＰ－１０）、トリス（２，４－ジ－ｔｅｒｔ－ブチルフェニル）ホスファイト（ＢＡＳＦ社製；商品名：ＩＲＧＡＦＯＳ１６８）、３，９－ビス（２，６－ジ－ｔｅｒｔ－ブチル－４－メチルフェノキシ）－２，４，８，１０－テトラオキサ－３，９－ジホスファスピロ［５．５］ウンデカン（ＡＤＥＫＡ社製；商品名：アデカスタブＰＥＰ－３６）などが好ましい。
　ヒンダードフェノール系酸化防止剤としては、ペンタエリスリチル－テトラキス〔３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート〕（ＢＡＳＦ社製；商品名ＩＲＧＡＮＯＸ１０１０）、オクタデシル－３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート（ＢＡＳＦ社製；商品名ＩＲＧＡＮＯＸ１０７６）などが好ましい。
　熱劣化防止剤としては、実質上無酸素の状態下で高熱にさらされたときに生じるポリマーラジカルを捕捉することによって樹脂の熱劣化を防止できるものである。
　該熱劣化防止剤としては、２－ｔｅｒｔ－ブチル－６－（３’－ｔｅｒｔ－ブチル－５’－メチル－ヒドロキシベンジル）－４－メチルフェニルアクリレート（住友化学社製；商品名スミライザーＧＭ）、２，４－ジｔｅｒｔ－アミル－６－（３’，５’－ジ－ｔｅｒｔ－アミル－２’－ヒドロキシ－α－メチルベンジル）フェニルアクリレート（住友化学社製；商品名スミライザーＧＳ）などが好ましい。
　紫外線吸収剤は、紫外線を吸収する能力を有する化合物であり、主に光エネルギーを熱エネルギーに変換する機能を有すると言われるものである。
　紫外線吸収剤としては、ベンゾフェノン類、ベンゾトリアゾール類、トリアジン類、ベンゾエート類、サリシレート類、シアノアクリレート類、蓚酸アニリド類、マロン酸エステル類、ホルムアミジン類などが挙げられる。これらの中でも、ベンゾトリアゾール類、トリアジン類、または波長３８０～４５０ｎｍにおけるモル吸光係数の最大値εmaxが１００ｄｍ3・ｍｏｌ-1ｃｍ-1以下である紫外線吸収剤が好ましい。
　ベンゾトリアゾール類は紫外線被照による着色などの光学特性低下を抑制する効果が高いので、本発明のフィルムを光学用途に適用する場合に用いる紫外線吸収剤として好ましい。ベンゾトリアゾール類としては、２－（２Ｈ－ベンゾトリアゾール－２－イル）－４－（１，１，３，３－テトラメチルブチル）フェノール（ＢＡＳＦ社製；商品名ＴＩＮＵＶＩＮ３２９）、２－（２Ｈ－ベンゾトリアゾール－２－イル）－４，６－ビス（１－メチル－１－フェニルエチル）フェノール（ＢＡＳＦ社製；商品名ＴＩＮＵＶＩＮ２３４）、２，２’－メチレンビス［６－（２Ｈ－ベンゾトリアゾール－２－イル）－４－ｔｅｒｔ－オクチルフェノール］（ＡＤＥＫＡ社製；ＬＡ－３１）などが好ましい。
　また、波長３８０～４５０ｎｍにおけるモル吸光係数の最大値εmaxが１２００ｄｍ3・ｍｏｌ-1ｃｍ-1以下である紫外線吸収剤は、得られるフィルムの変色を抑制できる。このような紫外線吸収剤としては、２－エチル－２’－エトキシ－オキサルアニリド（クラリアントジャパン社製；商品名サンデユボアＶＳＵ）などが挙げられる。
　これら紫外線吸収剤の中、紫外線被照による樹脂劣化が抑えられるという観点からベンゾトリアゾール類が好ましく用いられる。
　また、波長３８０ｎｍ付近の波長を効率的に吸収したい場合は、トリアジン類の紫外線吸収剤が好ましく用いられる。このような紫外線吸収剤としては、２，４，６－トリス（２－ヒドロキシ－４－ヘキシルオキシ－３－メチルフェニル）－１，３，５－トリアジン（ＡＤＥＫＡ社製；ＬＡ－Ｆ７０）や、その類縁体であるヒドロキシフェニルトリアジン系紫外線吸収剤（ＢＡＳＦ社製；ＴＩＮＵＶＩＮ４７７やＴＩＮＵＶＩＮ４６０）などが挙げられる。
　なお、紫外線吸収剤のモル吸光係数の最大値εmaxは、次のようにして測定する。シクロヘキサン１Ｌに紫外線吸収剤１０．００ｍｇを添加し、目視による観察で未溶解物がないように溶解させる。この溶液を１ｃｍ×１ｃｍ×３ｃｍの石英ガラスセルに注入し、日立製作所社製Ｕ－３４１０型分光光度計を用いて、波長３８０～４５０ｎｍ、光路長１ｃｍでの吸光度を測定する。紫外線吸収剤の分子量（ＭUV）と、測定された吸光度の最大値（Ａmax）とから次式により計算し、モル吸光係数の最大値εmaxを算出する。
　εmax＝［Ａmax／（１０×１０-3）］×ＭUV
　光安定剤は、主に光による酸化で生成するラジカルを捕捉する機能を有すると言われる化合物である。好適な光安定剤としては、２，２，６，６－テトラアルキルピペリジン骨格を持つ化合物などのヒンダードアミン類が挙げられる。
　滑剤としては、例えば、ステアリン酸、ベヘニン酸、ステアロアミド酸、メチレンビスステアロアミド、ヒドロキシステアリン酸トリグリセリド、パラフィンワックス、ケトンワックス、オクチルアルコール、硬化油などが挙げられる。
　離型剤としては、成形品の金型からの離型を容易にする機能を有する化合物である。離型剤としては、セチルアルコール、ステアリルアルコールなどの高級アルコール類；ステアリン酸モノグリセライド、ステアリン酸ジグリセライドなどのグリセリン高級脂肪酸エステルなどが挙げられる。本発明においては、離型剤として、高級アルコール類とグリセリン脂肪酸モノエステルとを併用することが好ましい。高級アルコール類とグリセリン脂肪酸モノエステルとを併用する場合、高級アルコール類／グリセリン脂肪酸モノエステルの質量比が、２．５／１～３．５／１の範囲で使用するのが好ましく、２．８／１～３．２／１の範囲で使用するのがより好ましい。
　高分子加工助剤としては、通常、乳化重合法によって製造することができる、０．０５～０．５μｍの粒子径を有する重合体粒子が挙げられる。該重合体粒子は、単一組成比および単一極限粘度の重合体からなる単層粒子であってもよいし、また組成比または極限粘度の異なる２種以上の重合体からなる多層粒子であってもよい。この中でも、内層に低い極限粘度を有する重合体層を有し、外層に５ｄＬ／ｇ以上の高い極限粘度を有する重合体層を有する２層構造の粒子が好ましいものとして挙げられる。高分子加工助剤としては、極限粘度が３～６ｄＬ／ｇであることが好ましい。具体的には、三菱レイヨン社製メタブレン－Ｐシリーズやロームアンドハース社製パラロイドシリーズが挙げられる。
　耐衝撃性改質剤としては、アクリル系ゴムもしくはジエン系ゴムをコア層成分として含むコアシェル型改質剤；ゴム粒子を複数包含した改質剤などが挙げられる。
　有機色素としては、樹脂に対しては有害とされている紫外線を可視光線に変換する機能を有する化合物が好ましく用いられる。
　光拡散剤や艶消し剤としては、ガラス微粒子、ポリシロキサン系架橋微粒子、架橋ポリマー微粒子、タルク、炭酸カルシウム、硫酸バリウムなどが挙げられる。
　蛍光体として、蛍光顔料、蛍光染料、蛍光白色染料、蛍光増白剤、蛍光漂白剤などが挙げられる。
　これらの添加剤は、１種を単独でまたは２種以上を組み合わせて用いてもよい。また、これらの添加剤は、メタクリル樹脂やポリカーボネート樹脂を製造する際の重合反応液に添加してもよいし、製造されたメタクリル樹脂やポリカーボネート樹脂に添加してもよいし、メタクリル樹脂組成物を調製する際に添加してもよい。本発明のメタクリル樹脂組成物に含有される添加剤の合計量は、フィルムの外観不良を抑制する観点から、メタクリル樹脂とポリカーボネート樹脂の合計量に対して好ましくは７質量％以下、より好ましくは５質量％以下、さらに好ましくは４質量％以下である。
　本発明のメタクリル樹脂組成物の調製方法は特に限定されない。例えば、ポリカーボネート樹脂の存在下にメタクリル酸メチルを含む単量体混合物を重合してメタクリル樹脂を生成させる方法や、メタクリル樹脂およびポリカーボネート樹脂を溶融混練する方法などが挙げられる。これらのうち溶融混練法は工程が単純であるので、好ましい。溶融混練の際に、必要に応じて他の重合体や添加剤を混合してもよいし、メタクリル樹脂を他の重合体および添加剤と混合した後にポリカーボネート樹脂と混合してもよいし、ポリカーボネート樹脂を他の重合体および添加剤と混合した後にメタクリル樹脂と混合してもよい。混練は、例えば、ニーダールーダー、押出機、ミキシングロール、バンバリーミキサーなどの既知の混合装置または混練装置を使用して行なうことができる。これらのうち、二軸押出機が好ましい。混合・混練時の温度は、使用するメタクリル樹脂およびポリカーボネート樹脂の溶融温度などに応じて適宜調節することができるが、好ましくは１１０℃～３００℃である。上記のような方法で調製されたメタクリル樹脂組成物は、ペレット、顆粒、粉末などの任意の形態にして、フィルムを含む様々な成形体に成形することができる。
　本発明のメタクリル樹脂組成物は、ガラス転移温度が、好ましくは１２０℃以上、より好ましくは１２３℃以上、さらに好ましくは１２４℃以上である。メタクリル樹脂組成物のガラス転移温度の上限は特に制限はないが、通常１３５℃である。
　本発明に用いられるメタクリル樹脂組成物をＧＰＣにて測定して決定されるＭｗは、好ましくは７００００～２０００００、より好ましくは７２０００～１６００００、さらに好ましくは７５０００～１２００００である。本発明に用いられるメタクリル樹脂組成物をＧＰＣにて測定して決定される分子量分布は、好ましくは１．２～２．５、より好ましくは１．３～２．０、さらに好ましくは１．３～１．５である。Ｍｗや分子量分布がこの範囲にあると、メタクリル樹脂組成物の成形加工性が良好となり、耐衝撃性や靭性に優れた成形体を得易くなる。
　本発明に用いられるメタクリル樹脂組成物を２３０℃および３．８ｋｇ荷重の条件で測定して決定されるメルトフローレートは、好ましくは０．１～６ｇ／１０分、さらに好ましくは０．５～５ｇ／１０分、最も好ましくは１．０～３ｇ／１０分である。
　本発明のメタクリル樹脂組成物は、３．２ｍｍ厚さのヘイズが、３．０％以下が好ましく、２．０％以下がより好ましく、１．５％以下がさらに好ましい。
　本発明のフィルムは、その製法によって特に限定されない。本発明のフィルムは、例えば、前記メタクリル樹脂組成物を、溶液キャスト法、溶融流延法、押出成形法、インフレーション成形法、ブロー成形法などの公知の方法にて製膜することによって得ることができる。これらのうち、押出成形法が好ましい。押出成形法によれば、透明性に優れ、改善された靭性を持ち、取扱い性に優れ、靭性と表面硬度および剛性とのバランスに優れたフィルムを得ることができる。押出機から吐出されるメタクリル樹脂組成物の温度は好ましくは１６０～２７０℃、より好ましくは２２０～２６０℃に設定する。
　押出成形法のうち、良好な表面平滑性、良好な鏡面光沢、低ヘイズのフィルムが得られるという観点から、前記メタクリル樹脂組成物を溶融状態でＴダイから押出し、次いでそれを二つ以上の鏡面ロールまたは鏡面ベルトで挟持して成形することを含む方法が好ましい。鏡面ロールまたは鏡面ベルトは、金属製であることが好ましい。一対の鏡面ロールまたは鏡面ベルトの間の線圧は、好ましくは１０Ｎ／ｍｍ以上、より好ましくは３０Ｎ／ｍｍ以上である。
　また、鏡面ロールまたは鏡面ベルトの表面温度は共に１３０℃以下であることが好ましい。また、一対の鏡面ロール若しくは鏡面ベルトは、少なくとも一方の表面温度が６０℃以上であることが好ましい。このような表面温度に設定すると、押出機から吐出される前記メタクリル樹脂組成物を自然放冷よりも速い速度で冷却することができ、表面平滑性に優れ且つヘイズの低い本発明のフィルムを製造し易い。
　本発明のフィルムは延伸処理を施したものであってもよい。延伸処理によって、機械的強度が高まり、ひび割れし難いフィルムを得ることができる。延伸方法は特に限定されず、一軸延伸、同時二軸延伸法、逐次二軸延伸法、チュブラー延伸法などが挙げられる。延伸時の温度は、均一に延伸でき、高い強度のフィルムが得られるという観点から、１００～２００℃が好ましく、１２０℃～１６０℃がより好ましい。また特に強度を大きくしたい場合は、低い温度である方が好ましく、例えば１１０～１５０℃が好ましく、１２５～１４０℃がより好ましい。延伸は、通常長さ基準で１００～５０００％／分で行われる。延伸の後、熱固定を施したり、フィルムを弛緩したりすることにより、熱収縮の少ないフィルムとすることもできる。延伸倍率に制限はないが、通常面積比で１．５～８倍程度とする。
　本発明のフィルムは、その中に含まれるメタクリル樹脂の量が、透明性や厚さ方向の位相差が小さいという観点から、好ましくは７８～９９質量％、より好ましくは８５～９７質量％である。
　また、本発明のフィルムは、その中に含まれるポリカーボネート樹脂の量が、厚さ方向の位相差が小さいという観点から、好ましくは１～３．８質量％、より好ましくは２～２．９質量％である。
　本発明のフィルムの厚さは、特に制限されないが、光学フィルムとして用いる場合、その厚さは、好ましくは１～３００μｍ、より好ましくは１０～５０μｍ、さらに好ましくは１５～４０μｍである。
　本発明のフィルムは、厚さ５０μｍにおけるヘイズが、好ましくは０．２％以下、より好ましくは０．１％以下である。これにより、表面光沢や透明性に優れる。また、液晶保護フィルムや導光フィルムなどの光学用途においては、光源の利用効率が高まり好ましい。さらに、表面賦形を行う際の賦形精度に優れるため好ましい。
　本発明のフィルムは、波長５９０ｎｍの光に対する面内方向位相差Ｒｅが、フィルムの厚さ４０μｍの時に、好ましくは－５ｎｍ以上、５ｎｍ以下、より好ましくは－４ｎｍ以上、４ｎｍ以下、さらに好ましくは－３ｎｍ以上、３ｎｍ以下、特に好ましくは－２ｎｍ以上、２ｎｍ以下、最も好ましくは－１ｎｍ以上、１ｎｍ以下である。
　本発明のフィルムは、波長５９０ｎｍの光に対する厚さ方向位相差Ｒｔｈが、フィルムの厚さ４０μｍの時に、好ましくは－５ｎｍ以上、５ｎｍ以下、より好ましくは－４ｎｍ以上、４ｎｍ以下、さらに好ましくは－３ｎｍ以上、３ｎｍ以下、特に好ましくは－２ｎｍ以上、２ｎｍ以下、最も好ましくは－１ｎｍ以上、１ｎｍ以下である。
　面内位相差および厚さ方向位相差がこのような範囲であれば、位相差に起因する画像表示装置の表示特性への影響が顕著に抑制され得る。より具体的には、干渉ムラや３Ｄディスプレイ用液晶表示装置に用いる場合の３Ｄ像の歪みが顕著に抑制され得る。
　なお、面内方向位相差Ｒｅおよび厚さ方向位相差Ｒｔｈは、それぞれ、以下の式で定義される値である。
　Ｒｅ＝（ｎｘ－ｎｙ）×ｄ
　Ｒｔｈ＝（（ｎｘ＋ｎｙ）／２－ｎｚ）×ｄ
　ここで、ｎｘはフィルムの遅相軸方向の屈折率であり、ｎｙはフィルムの進相軸方向の屈折率であり、ｎｚはフィルムの厚さ方向の屈折率であり、ｄ（ｎｍ）はフィルムの厚さである。遅相軸は、フィルム面内の屈折率が最大になる方向をいい、進相軸は、面内で遅相軸に垂直な方向をいう。
　本発明のフィルムは、透明性が高く、耐熱性が高く、位相差が小さく、薄いため、偏光子保護フィルムや後述する各種フィルム、成形体等に好適である。
　本発明の偏光板は、本発明の偏光子保護フィルムを少なくとも１枚含むものである。好ましくは、ポリビニルアルコール系樹脂から形成される偏光子と本発明の偏光子保護フィルムが接着剤層を介して積層されてなるものである。
　本発明の好ましい一実施形態に係る偏光板は、図１に示すように、偏光子１１の一方の面に、接着剤層１２、易接着層１３、および本発明の偏光子保護フィルム１４がこの順で積層され、偏光子１１のもう一方の面に、接着剤層１５、および光学フィルム１６がこの順で積層されてなるものである。
　上記ポリビニルアルコール系樹脂から形成される偏光子は、例えば、ポリビニルアルコール系樹脂フィルムを二色性物質（代表的には、ヨウ素、二色性染料）で染色して一軸延伸することによって得られる。ポリビニルアルコール系樹脂フィルムは、ポリビニルアルコール系樹脂を任意の適切な方法（例えば、樹脂を水または有機溶媒に溶解した溶液を流延成膜する流延法、キャスト法、押出法）にて製膜することによって得ることができる。該ポリビニルアルコール系樹脂は、重合度が、好ましくは１００～５０００、さらに好ましくは１４００～４０００である。また、偏光子に用いられるポリビニルアルコール系樹脂フィルムの厚さは、偏光板が用いられるＬＣＤの目的や用途に応じて適宜設定され得るが、代表的には５～８０μｍである。
　偏光子の製造方法としては、目的、使用材料および条件等に応じて任意の適切な方法が採用され得る。代表的には、上記ポリビニルアルコール系樹脂フィルムを、膨潤、染色、架橋、延伸、水洗、および乾燥工程からなる一連の製造工程に供する方法が採用される。乾燥工程を除く各処理工程においては、それぞれの工程に用いられる溶液を含む浴中にポリビニルアルコール系樹脂フィルムを浸漬することにより処理を行う。膨潤、染色、架橋、延伸、水洗、および乾燥の各処理の順番、回数および実施の有無は、目的、使用材料および条件等に応じて適宜設定され得る。例えば、いくつかの処理を１つの工程で同時に行ってもよく、特定の処理を省略してもよい。より詳細には、例えば延伸処理は、染色処理の後に行ってもよく、染色処理の前に行ってもよく、膨潤処理、染色処理および架橋処理と同時に行ってもよい。また例えば、架橋処理を延伸処理の前後に行うことが、好適に採用され得る。また例えば、水洗処理は、すべての処理の後に行ってもよく、特定の処理の後のみに行ってもよい。
　膨潤工程は、代表的には、上記ポリビニルアルコール系樹脂フィルムを水で満たした処理浴（膨潤浴）中に浸漬することにより行われる。この処理により、ポリビニルアルコール系樹脂フィルム表面の汚れやブロッキング防止剤を洗浄するとともに、ポリビニルアルコール系樹脂フィルムを膨潤させることで染色ムラ等の不均一性を防止し得る。膨潤浴には、グリセリンやヨウ化カリウム等が適宜添加され得る。膨潤浴の温度は、代表的には２０～６０℃程度であり、膨潤浴への浸漬時間は、代表的には０．１～１０分程度である。
　染色工程は、代表的には、上記ポリビニルアルコール系樹脂フィルムを、ヨウ素等の二色性物質を含む処理浴（染色浴）中に浸漬することにより行われる。染色浴の溶液に用いられる溶媒は、水が一般的に使用されるが、水と相溶性を有する有機溶媒が適量添加されていてもよい。二色性物質は、溶媒１００質量部に対して、代表的には０．１～１．０重量部の割合で用いられる。二色性物質としてヨウ素を用いる場合には、染色浴の溶液は、ヨウ化物等の助剤をさらに含有することが好ましい。染色効率が改善されるからである。助剤は、溶媒１００質量部に対して、好ましくは０．０２～２０質量部、さらに好ましくは２～１０質量部の割合で用いられる。ヨウ化物の具体例としては、ヨウ化カリウム、ヨウ化リチウム、ヨウ化ナトリウム、ヨウ化亜鉛、ヨウ化アルミニウム、ヨウ化鉛、ヨウ化銅、ヨウ化バリウム、ヨウ化カルシウム、ヨウ化錫、ヨウ化チタンが挙げられる。染色浴の温度は、代表的には２０～７０℃ 程度であり、染色浴への浸漬時間は、代表的には１～
２０分程度である。
　架橋工程は、代表的には、上記染色処理されたポリビニルアルコール系樹脂フィルムを、架橋剤を含む処理浴（架橋浴）中に浸漬することにより行われる。架橋剤としては、任意の適切な架橋剤が採用され得る。架橋剤の具体例としては、ホウ酸、ホウ砂等のホウ素化合物、グリオキザール、グルタルアルデヒド等が挙げられる。これらは、単独で、または組み合わせて使用され得る。架橋浴の溶液に用いられる溶媒は、水が一般的に使用されるが、水と相溶性を有する有機溶媒が適量添加されていてもよい。架橋剤は、溶媒１００質量部に対して、代表的には１～１０質量部の割合で用いられる。架橋剤の濃度が１重量部未満の場合には、十分な光学特性を得ることができない場合が多い。架橋剤の濃度が１０質量部を超える場合には、延伸時にフィルムに発生する延伸力が大きくなり、得られる偏光板が収縮してしまう場合がある。架橋浴の溶液は、ヨウ化物等の助剤をさらに含有することが好ましい。面内に均一な特性が得られやすいからである。助剤の濃度は、好ましくは０．０５～１５重量％ 、さらに好ましくは０．５～８．０重量％である。ヨウ化物の具体例は、染色工程の場合と同様である。架橋浴の温度は、代表的には２０～７０℃程度、好ましくは４０～６０℃ である。架橋浴への浸漬時間は、代表的には１秒～１５分程度、好ましくは５秒～１０分である。
　延伸工程は、上記のように、いずれの段階で行ってもよい。具体的には、染色処理の後に行ってもよく、染色処理の前に行ってもよく、膨潤処理、染色処理および架橋処理と同時に行ってもよく、架橋処理の後に行ってもよい。ポリビニルアルコール系樹脂フィルムの累積延伸倍率は、５倍以上にすることが必要であり、好ましくは５～７倍、さらに好ましくは５～６．５倍である。累積延伸倍率が５倍未満である場合には、高偏光度の偏光板を得ることが困難となる場合がある。累積延伸倍率が７倍を超える場合には、ポリビニルアルコール系樹脂フィルム（偏光子）が破断しやすくなる場合がある。延伸の具体的な方法としては、任意の適切な方法が採用され得る。例えば、湿式延伸法を採用した場合には、ポリビニルアルコール系樹脂フィルムを、処理浴（延伸浴）中で所定の倍率に延伸する。延伸浴の溶液としては、水または有機溶媒（例えば、エタノール）などの溶媒中に、各種金属塩、ヨウ素、ホウ素または亜鉛の化合物を添加した溶液が好適に用いられる。
　水洗工程は、代表的には、上記各種処理を施されたポリビニルアルコール系樹脂フィルムを、処理浴（水洗浴）中に浸漬することにより行われる。水洗工程により、ポリビニルアルコール系樹脂フィルムの不要残存物を洗い流すことができる。水洗浴は、純水であってもよく、ヨウ化物（例えば、ヨウ化カリウム、ヨウ化ナトリウム）の水溶液であってもよい。ヨウ化物水溶液の濃度は、好ましくは０．１～１０質量％である。ヨウ化物水溶液には、硫酸亜鉛、塩化亜鉛などの助剤を添加してもよい。水洗浴の温度は、好ましくは１０～６０℃、さらに好ましくは３０～４０℃ である。浸漬時間は、代表的には１秒～１分である。水洗工程は１回だけ行ってもよく、必要に応じて複数回行ってもよい。複数回実施する場合、各処理に用いられる水洗浴に含まれる添加剤の種類や濃度は適宜調整され得る。例えば、水洗工程は、ポリマーフィルムをヨウ化カリウム水溶液（０．１～１０質量％、１０～６０℃）に１秒～１分浸漬する工程と、純水ですすぐ工程とを含む。
　乾燥工程としては、任意の適切な乾燥方法（例えば、自然乾燥、送風乾燥、加熱乾燥）が採用され得る。例えば、加熱乾燥の場合には、乾燥温度は代表的には２０～８０℃であり、乾燥時間は代表的には１～１０分である。以上のようにして、偏光子が得られる。
　本発明の偏光板に設けることができる接着剤層は光学的に透明であれば特に制限されない。接着剤層を構成する接着剤として、例えば、水系接着剤、溶剤系接着剤、ホットメルト系接着剤、活性エネルギー線硬化型接着剤などを用いることができる。これらのうち、水系接着剤および活性エネルギー線硬化型接着剤が好適である。
　水系接着剤としては、特に限定されないが、例えば、ビニルポリマー系、ゼラチン系、ビニル系ラテックス系、ポリウレタン系、イソシアネート系、ポリエステル系、エポキシ系等を例示できる。このような水系接着剤には、必要に応じて、架橋剤や他の添加剤、酸等の触媒も配合することができる。前記水系接着剤としては、ビニルポリマーを含有する接着剤などを用いることが好ましく、ビニルポリマーとしては、ポリビニルアルコール系樹脂が好ましい。またポリビニルアルコール系樹脂には、ホウ酸やホウ砂、グルタルアルデヒドやメラミン、シュウ酸などの水溶性架橋剤を含有することができる。特に偏光子としてポリビニルアルコール系のポリマーフィルムを用いる場合には、ポリビニルアルコール系樹脂を含有する接着剤を用いることが、接着性の点から好ましい。さらには、アセトアセチル基を有するポリビニルアルコール系樹脂を含む接着剤が耐久性を向上させる点からより好ましい。前記水系接着剤は、通常、水溶液からなる接着剤として用いられ、通常、０．５～６０重量％の固形分を含有してなる。
　活性エネルギー線硬化型接着剤としては、単官能および二官能以上の（メタ）アクリロイル基を有する化合物やビニル基を有する化合物を硬化性成分として用いる他、エポキシ化合物やオキセタン化合物と光酸発生剤とを主体とする光カチオン型硬化成分を使用することもできる。活性エネルギー線としては、電子線や紫外線を用いることができる。
　また前記接着剤には、金属化合物フィラーを含有させることができる。金属化合物フィラーにより、接着剤層の流動性を制御することができ、膜厚を安定化して、良好な外観を有し、面内が均一で接着性のバラツキのない偏光板が得られる。
　接着剤層の形成方法は特に制限されない。例えば、上記接着剤を対象物に塗布し、次いで加熱または乾燥することによって形成できる。接着剤の塗布は本発明の偏光子保護フィルムまたは光学フィルムに対して行ってもよいし、偏光子に対して行ってもよい。接着剤層を形成した後、偏光子保護フィルム若しくは光学フィルムと偏光子とを押し合わせることによって両者を積層することができる。積層においてはロールプレス機や平板プレス機などを用いることができる。加熱乾燥温度、乾燥時間は接着剤の種類に応じて適宜決定される。
　接着剤層の厚さは、乾燥状態において、好ましくは０．０１～１０μｍ、さらに好ましくは０．０３～５μｍである。
　本発明の偏光板に設けることができる易接着層は、偏光子保護フィルムと偏光子とが接する面の接着性を向上させるものである。易接着層は、易接着処理などによって設けることができる。易接着処理としては、コロナ処理、プラズマ処理、低圧ＵＶ処理等の表面処理が挙げられる。また、易接着層は、アンカー層を形成する方法、または前記の表面処理とアンカー層を形成する方法との併用によって設けることができる。これらの中でも、コロナ処理、アンカー層を形成する方法、およびこれらを併用する方法が好ましい。
　上記アンカー層としては、例えば、反応性官能基を有するシリコーン層が挙げられる。反応性官能基を有するシリコーン層の材料は、特に制限されないが、例えば、イソシアネート基含有のアルコキシシラノール類、アミノ基含有アルコキシシラノール類、メルカプト基含有アルコキシシラノール類、カルボキシ含有アルコキシシラノール類、エポキシ基含有アルコキシシラノール類、ビニル型不飽和基含有アルコキシシラノール類、ハロゲン基含有アルコキシシラノール類、イソシアネート基含有アルコキシシラノール類が挙げられる。これらのうち、アミノ系シラノールが好ましい。シラノールを効率よく反応させるためのチタン系触媒や錫系触媒を上記シラノールに添加することにより、接着力を強固にすることができる。また上記反応性官能基を有するシリコーンに他の添加剤を加えてもよい。他の添加剤としては、テルペン樹脂、フェノール樹脂、テルペン-フェノール樹脂、ロジン樹脂、キシレン樹脂などの粘着付与剤；紫外線吸収剤、酸化防止剤、耐熱安定剤などの安定剤等を挙げることができる。また、アンカー層として、セルロースアセテートブチレート樹脂をケン化させたものからなる層も挙げられる。
　上記アンカー層は公知の技術により塗工、乾燥して形成される。アンカー層の厚さは、乾燥状態において、好ましくは１～１００ｎｍ、さらに好ましくは１０～５０ｎｍである。塗工の際、アンカー層形成用薬液を溶剤で希釈してもよい。希釈溶剤は特に制限されないが、アルコール類が挙げられる。希釈濃度は特に制限されないが、好ましくは１～５重量％、より好ましくは１～３重量％である。
　光学フィルム１６は本発明の偏光子保護フィルムであってもよいし、別の任意の適切な光学フィルムであってもよい。用いられる光学フィルムは、特に制限されず、例えば、セルロース樹脂、ポリカーボネート樹脂、環状ポリオレフィン樹脂、メタクリル樹脂等からなるフィルムが挙げられる。
　セルロース樹脂は、セルロースと脂肪酸のエステルである。このようセルロースエステル系樹脂の具体例としては、セルローストリアセテート、セルロースジアセテート、セルローストリプロピオネート、セルロースジプロピオネート等が挙げられる。これらのなかでも、セルローストリアセテートが特に好ましい。セルローストリアセテートは多くの製品が市販されており、入手容易性やコストの点でも有利である。セルローストリアセテートの市販品の例としては、富士フイルム社製の商品名「ＵＶ－５０」、「ＵＶ－８０」、「ＳＨ－８０」、「ＴＤ－８０Ｕ」、「ＴＤ－ＴＡＣ」、「ＵＺ－ＴＡＣ」や、コニカミノルタ社製の「ＫＣシリーズ」等が挙げられる。
　環状ポリオレフィン樹脂は、環状オレフィンを重合単位として重合される樹脂の総称であり、例えば、特開平１－２４０５１７号公報、特開平３－１４８８２号公報、特開平３－１２２１３７号公報等に記載されている樹脂が挙げられる。具体例としては、環状オレフィンの開環（共）重合体、環状オレフィンの付加重合体、環状オレフィンとエチレン、プロピレン等のα－オレフィンとその共重合体（代表的にはランダム共重合体）、および、これらを不飽和カルボン酸やその誘導体で変性したグラフト重合体、ならびに、それらの水素化物などが挙げられる。環状オレフィンの具体例としては、ノルボルネン系モノマーが挙げられる。
　環状ポリオレフィン樹脂としては、種々の製品が市販されている。具体例としては、日本ゼオン社製の商品名「ゼオネックス」、「ゼオノア」、ＪＳＲ社製の商品名「アートン」、ポリプラスチックス社製の商品名「トーパス」、三井化学社製の商品名「ＡＰＥＬ」が挙げられる。
　光学フィルム１６等の光学フィルムに用いられるメタクリル樹脂としては、本発明の効果を損なわない範囲内で、任意の適切なメタクリル樹脂を採用し得る。例えば、ポリメタクリル酸メチルなどのポリメタクリル酸エステル、メタクリル酸メチル－（メタ）アクリル酸共重合、メタクリル酸メチル－（メタ）アクリル酸エステル共重合体、メタクリル酸メチル－アクリル酸エステル－（メタ）アクリル酸共重合体、（メタ）アクリル酸メチル－スチレン共重合体（ＭＳ樹脂など）、脂環族炭化水素基を有する重合体（ 例えば、メタクリル酸メチル－ メタクリル酸シクロヘキシル共重合体、メタクリル酸メチル－（メタ）アクリル酸ノルボルニル共重合体など）が挙げられる。
　光学フィルム１６等の光学フィルムに用いられるメタクリル樹脂の具体例として、例えば、三菱レイヨン社製のアクリペットＶＨやアクリペットＶＲＬ２０Ａ 、特開２０１３－０３３２３７やＷＯ２０１３／００５６３４号公報に記載のメタクリル酸メチルとマレイミド系単量体を共重合したアクリル樹脂、ＷＯ２００５／１０８４３８号公報に記載の分子内に環構造を有するアクリル樹脂、特開２００９－１９７１５１号公報に記載の分子内に環構造を有するメタクリル樹脂、分子内架橋や分子内環化反応により得られる高ガラス転移温度（Ｔｇ）メタクリル樹脂が挙げられる。
　光学フィルム１６に用いるメタクリル樹脂として、ラクトン環構造を有するメタクリル樹脂を用いることもできる。高い耐熱性、高い透明性、二軸延伸することにより高い機械的強度を有するからである。
　上記ラクトン環構造を有するメタクリル樹脂としては、特開２０００－２３００１６号公報、特開２００１－１５１８１４号公報、特開２００２－１２０３２６号公報、特開２００２－２５４５４４号公報、特開２００５－１４６０８４号公報などに記載の、ラクトン環構造を有するメタクリル樹脂が挙げられる。
　本発明の偏光板は、画像表示装置に使用することができる。画像表示装置の具体例としては、エレクトロルミネッセンス（ＥＬ）ディスプレイ、プラズマディスプレイ（ＰＤ）、電界放出ディスプレイ（ＦＥＤ：Field Emission Display）のような自発光型表示装置、液晶表示装置が挙げられる。液晶表示装置は、液晶セルと、当該液晶セルの少なくとも片側に配置された上記偏光板とを有する。
　本発明のメタクリル樹脂組成物によれば、メタクリル樹脂とポリカーボネート樹脂とが均一に相溶するため透明性が高く、また、延伸させても厚さ方向の位相差が小さい。また、これにより得られるフィルムは、延伸性が高い。故に、好適な実施形態においては、薄くて、面内均一性に優れ、表面平滑性の高いフィルムを得ることができる、また、低い温度での延伸が可能となり、強度の大きいフィルムが得られる。さらに、メタクリル樹脂のシンジオタクシティティ（ｒｒ）を特定の範囲とすれば、前述した効果に加えて、耐熱性を高くし、熱収縮率の小さいフィルムを提供することもできる。
　以下、実施例および比較例によって本発明を具体的に説明するが、本発明は下記実施例に限定されない。なお、物性値等の測定は以下の方法によって実施した。
（重合転化率）
　島津製作所社製ガスクロマトグラフ　ＧＣ－１４Ａに、カラムとしてＧＬ　Ｓｃｉｅｎｃｅｓ　Ｉｎｃ．社製　Ｉｎｅｒｔ　ＣＡＰ　１（ｄｆ＝０．４μｍ、０．２５ｍｍＩ．Ｄ．×６０ｍ）を繋ぎ、インジェクション温度を１８０℃に、検出器温度を１８０℃に、カラム温度を６０℃（５分間保持）から昇温速度１０℃／分で２００℃まで昇温して、１０分間保持する条件に設定して、測定を行い、この結果に基づいて重合転化率を算出した。
（重量平均分子量（Ｍｗ）、分子量分布（Ｍｗ／Ｍｎ））
　各製造例、実施例および比較例で得られたメタクリル樹脂およびメタクリル樹脂組成物のＭｗおよび分子量分布は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）にて下記の条件でクロマトグラムを測定し、標準ポリスチレンの分子量に換算した値を算出した。ベースラインはＧＰＣチャートの高分子量側のピークの傾きが保持時間の早い方から見てゼロからプラスに変化する点と、低分子量側のピークの傾きが保持時間の早い方から見てマイナスからゼロに変化する点を結んだ線とした。
ＧＰＣ装置：東ソー社製、ＨＬＣ－８３２０
　検出器：示差屈折率検出器
　カラム：東ソー社製のＴＳＫｇｅｌ　ＳｕｐｅｒＭｕｌｔｉｐｏｒｅ　ＨＺＭ－Ｍの２本とＳｕｐｅｒＨＺ４０００を直列に繋いだものを用いた。
　溶離剤： テトラヒドロフラン
　溶離剤流量： ０．３５ｍＬ／分
　カラム温度： ４０℃
　検量線：標準ポリスチレン１０点のデータを用いて作成
（粘度平均分子量（Ｍｖ））
　ポリカーボネート樹脂の粘度平均分子量は、ウベローデ粘度計を用いてポリカーボネート樹脂０．５ｇを塩化メチレン１００ｍＬに溶解した溶液の比粘度ηｓｐを２０℃で測定し、下記のＳｃｈｎｅｌｌの式を満足する値として、２０℃の塩化メチレン溶液の極限粘度[η]から、算出した。
ηｓｐ／ｃ＝［η］＋０．４５×［η］2 ｃ
（但し［η］は極限粘度、上記条件ではｃ＝０．５）
［η］＝１．２３×１０- 4 Ｍｖ0 . 8 3　
（三連子表示のシンジオタクティシティ（ｒｒ））
　メタクリル樹脂の1Ｈ－ＮＭＲスペクトルを、核磁気共鳴装置（Ｂｒｕｋｅｒ社製　ＵＬＴＲＡ　ＳＨＩＥＬＤ　４００　ＰＬＵＳ）を用いて、溶媒として重水素化クロロホルムを用い、室温、積算回数６４回の条件にて、測定した。そのスペクトルからＴＭＳを０ｐｐｍとした際の０．６～０．９５ｐｐｍの領域の面積（Ｘ）と、０．６～１．３５ｐｐｍの領域の面積（Ｙ）とを計測し、次いで、三連子表示のシンジオタクティシティ（ｒｒ）を式：（Ｘ／Ｙ）×１００にて算出した。
（ガラス転移温度Ｔｇ）
　メタクリル樹脂、ポリカーボネート樹脂およびメタクリル樹脂組成物を、ＪＩＳ Ｋ７１２１に準拠して、示差走査熱量測定装置（島津製作所製、ＤＳＣ－５０（品番））を用いて、２３０℃まで一度昇温し、次いで室温まで冷却し、その後、室温から２３０℃までを１０℃／分で昇温させる条件にてＤＳＣ曲線を測定した。２回目の昇温時に測定されるＤＳＣ曲線から求められる中間点ガラス転移温度を本発明におけるガラス転移温度とした。
（メルトマスフローレート（ＭＦＲ））
　各実施例および比較例でフィルムの製造に用いたメタクリル樹脂組成物の原料であるメタクリル樹脂を、ＪＩＳ Ｋ７２１０に準拠して、２３０℃、３．８ｋｇ荷重、１０分間の条件で測定した。
（メルトボリュームフローレート（ＭＶＲ））
　各実施例および比較例でフィルムの製造に用いたメタクリル樹脂組成物の原料であるポリカーボネート樹脂を、ＪＩＳ Ｋ７２１０に準拠して、３００℃、１．２ｋｇ荷重、１０分間の条件で測定した。
（膜厚安定性）
　各実施例および比較例で得られた未延伸フィルムの押出方向と直交する幅方向の中央１０ｍｍの平均厚さを中央部の厚さ（ＴＣ）とし、端部から１５ｍｍ離れた位置から２５ｍｍ離れた位置までの１０ｍｍ分の平均厚さを一方の端部の厚さとし、両端の端部の厚さの平均値を端部の厚さ（ＴＳ）とした。
　そして端部の厚さ（ＴＳ）と中央部の厚さ（ＴＣ）との厚さの差を求め、以下の基準で膜厚安定性を評価した。厚さの測定はマイクロメータを用いた。膜厚を測定し、以下の基準で評価した。
　　Ａ：端部の厚さ（ＴＳ）と中央部の厚さ（ＴＣ）との厚さの差が３μｍ未満である。
　　Ｂ：端部の厚さ（ＴＳ）と中央部の厚さ（ＴＣ）との厚さの差が３μｍ以上である。
（引張強度）
　各実施例および比較例で得られた未延伸フィルムを、ＪＩＳ Ｋ７１２７に準拠し、試験片タイプ１Ｂの形状に切り出し、引張速度２０ｍｍ／ｍｉｎでフィルムの押出方向の引張降伏強度を測定し、以下の基準で評価した。
　　Ａ：引張降伏強度が７０ＭＰａ以上である。
　　Ｂ：引張降伏強度が７０ＭＰａ未満である。
（表面平滑性）
　各実施例および比較例で得られた二軸延伸フィルムの表面を目視により観察し、以下の基準で表面平滑性を評価した。
　　Ａ：表面が平滑である。
　　Ｂ：表面に凹凸がある。
（加熱収縮率）
　各実施例および比較例で得られた二軸延伸フィルムから１００ｍｍ×３０ｍｍの試験片を切り出し、その表面に７０ｍｍの長さの直線を記入し、１１０℃の温度に保たれた強制温風循環式恒温オーブン内で３０分間加熱後、記入した直線の長さ（Ｌ（ｍｍ））をスケールで読取り、下記式により加熱収縮率を求めた。
　加熱収縮率（％）＝（７０－Ｌ）／７０×１００
（全光線透過率）
　各実施例および比較例で得られた二軸延伸フィルムから５０ｍｍ×５０ｍｍの試験片を切り出し、ＪＩＳ　Ｋ７３６１－１に準じて、ヘイズメータ（村上色彩研究所製、ＨＭ－１５０）を用いてその全光線透過率を測定した。またメタクリル樹脂組成物の評価は、１．０ｍｍ厚の成形体を熱プレスにて成形し、全光線透過率を測定した。
（ヘイズ）
　各実施例および比較例で得られた二軸延伸フィルムから５０ｍｍ×５０ｍｍの試験片を切り出し、ＪＩＳＫ７１３６に準拠して、ヘイズメータ（村上色彩研究所製、ＨＭ－１５０）を用いてそのヘイズを測定した。またメタクリル樹脂組成物の評価は、１．０ｍｍ厚の成形体を熱プレスにて成形し、ヘイズを測定した。
（厚さ方向位相差Ｒｔｈおよび面内方向位相差Ｒｅ）
　各実施例および比較例で得られた二軸延伸フィルムから４０ｍｍ×４０ｍｍの試験片を切り出した。この試験片を、自動複屈折計（王子計測社製 ＫＯＢＲＡ－ＷＲ）を用いて、温度２３±２℃、湿度５０±５％において、波長５９０ｎｍ、４０°傾斜方向の位相差値から３次元屈折率ｎｘ、ｎｙ、ｎｚを求め、前述した式より厚さ方向位相差Ｒｔｈおよび面内位相差Ｒｅを計算した。試験片の厚さｄ（ｎｍ）は、デジマティックインジケータ（ミツトヨ社製）を用いて測定し、屈折率ｎは、デジタル精密屈折計（カルニュー光学工業社製　ＫＰＲ－２０）で測定した。
（延伸性）
　各実施例および比較例で得られた未延伸フィルムを二軸延伸する際、以下の基準で延伸性を評価した。
　Ａ：割れやクラックのないフィルムを１０サンプル中、５サンプル以上取得できたもの。
　Ｂ：割れやクラックのないフィルムを１０サンプル中、４サンプル以下しか取得できなかったもの。
製造例１
　撹拌翼と三方コックが取り付けられた５Ｌのガラス製反応容器内を窒素で置換した。これに、室温下にて、トルエン１６００ｇ、１，１，４，７，１０，１０－ヘキサメチルトリエチレンテトラミン２．４９ｇ（１０．８ｍｍｏｌ）、濃度０．４５Ｍのイソブチルビス（２，６－ジ－ｔ－ブチル－４－メチルフェノキシ）アルミニウムのトルエン溶液５３．５ｇ（３０．９ｍｍｏｌ）、および濃度１．３Ｍのｓｅｃ－ブチルリチウムの溶液（溶媒：シクロヘキサン９５質量％、ｎ－ヘキサン５質量％）６．１７ｇ（１０．３ｍｍｏｌ）を仕込んだ。撹拌しながら、これに、蒸留精製したメタクリル酸メチル５５０ｇを－２０℃にて３０分間かけて滴下した。滴下終了後、－２０℃にて１８０分間撹拌した。溶液の色が黄色から無色に変わった。この時点におけるメタクリル酸メチルの重合転化率は１００％であった。
　得られた溶液にトルエン１５００ｇを加えて希釈した。次いで、該希釈液をメタノール１００ｋｇに注ぎ入れ、沈澱物を得た。得られた沈殿物を８０℃、１４０Ｐａにて２４時間乾燥して、Ｍｗが９６１００で、分子量分布が１．０７で、シンジオタクティシティ（ｒｒ）が８３％で、ガラス転移温度が１３３℃で、且つメタクリル酸メチルに由来する構造単位の割合が１００質量％であるメタクリル樹脂〔PMMA1〕を得た。
製造例２
　撹拌翼と三方コックが取り付けられた５Ｌのガラス製反応容器内を窒素で置換した。これに、室温下にて、トルエン１６００ｇ、１，１，４，７，１０，１０－ヘキサメチルトリエチレンテトラミン２．４９ｇ（１０．８ｍｍｏｌ）、濃度０．４５Ｍのイソブチルビス（２，６－ジ－ｔ－ブチル－４－メチルフェノキシ）アルミニウムのトルエン溶液５３．５ｇ（３０．９ｍｍｏｌ）、および濃度１．３Ｍのｓｅｃ－ブチルリチウムの溶液（溶媒：シクロヘキサン９５％、ｎ－ヘキサン５％）６．１７ｇ（１０．３ｍｍｏｌ）を仕込んだ。撹拌しながら、これに、蒸留精製したメタクリル酸メチル５５０ｇを２０℃にて３０分かけて滴下した。滴下終了後、２０℃で９０分間撹拌した。溶液の色が黄色から無色に変わった。この時点におけるメタクリル酸メチルの重合転化率は１００％であった。
　得られた溶液にトルエン１５００ｇを加えて希釈した。次いで、希釈液をメタノール１００ｋｇに注ぎ入れ、沈澱物を得た。得られた沈殿物を８０℃、１４０Ｐａにて２４時間乾燥して、Ｍｗが８１４００で、分子量分布が１．０８で、シンジオタクティシティ（ｒｒ）が７３％で、ガラス転移温度が１３１℃で、且つメタクリル酸メチルに由来する構造単位の含有量が１００質量％であるメタクリル樹脂〔PMMA2〕を得た。
製造例３
　攪拌機および採取管が取り付けられたオートクレーブ内を窒素で置換した。これに、精製されたメタクリル酸メチル１００質量部、２，２’－アゾビス（２－メチルプロピオニトリル）（水素引抜能：１％、１時間半減期温度：８３℃）０．００５２質量部、およびｎ－オクチルメルカプタン０．２８質量部を入れ、撹拌して、原料液を得た。かかる原料液中に窒素を送り込み、原料液中の溶存酸素を除去した。
　オートクレーブと配管で接続された槽型反応器に容量の２／３まで原料液を入れた。温度を１４０℃に維持して先ずバッチ方式で重合反応を開始させた。重合転化率が５５質量％になったところで、平均滞留時間１５０分となる流量で、原料液をオートクレーブから槽型反応器に供給し、且つ原料液の供給流量に相当する流量で、反応液を槽型反応器から抜き出して、温度１４０℃に維持し、連続流通方式の重合反応に切り替えた。切り替え後、定常状態における重合転化率は５５質量％であった。
　定常状態になった槽型反応器から抜き出される反応液を、平均滞留時間２分間となる流量で内温２３０℃の多管式熱交換器に供給して加温した。次いで加温された反応液をフラッシュ蒸発器に導入し、未反応単量体を主成分とする揮発分を除去して、溶融樹脂を得た。揮発分が除去された溶融樹脂を内温２６０℃の二軸押出機に供給してストランド状に吐出し、ペレタイザーでカットして、ペレット状の、Ｍｗが８２０００で、分子量分布が１．８５で、シンジオタクティシティ（ｒｒ）が５２％で、ガラス転移温度が１２０℃で、且つメタクリル酸メチルに由来する構造単位の含有量が１００質量％であるメタクリル樹脂〔PMMA3〕を得た。
製造例４
　ｎ－オクチルメルカプタンの量を０．２２５質量部に変更した以外は製造例３と同じ操作を行って、Ｍｗが１０３６００で、分子量分布が１．８１で、シンジオタクティシティ（ｒｒ）が５２％で、ガラス転移温度が１２０℃で、且つメタクリル酸メチルに由来する構造単位の割合が１００質量％であるメタクリル樹脂〔PMMA4〕を得た。
製造例５
　ｎ－オクチルメルカプタンの量を０．３０質量部に変更した以外は製造例３と同じ操作を行って、Ｍｗが７６４００で、分子量分布が１．８１で、シンジオタクティシティ（ｒｒ）が５３％、ガラス転移温度が１１９℃で、且つメタクリル酸メチルに由来する構造単位の含有量が１００質量％であるメタクリル樹脂〔PMMA5〕を得た。
製造例６
　メタクリル樹脂〔PMMA2〕５７質量部およびメタクリル樹脂〔PMMA4〕４３質量部を混ぜ合わせ、二軸押出機（テクノベル社製、商品名：ＫＺＷ２０ＴＷ-４５ＭＧ-ＮＨ-６００）で２５０℃にて混練押出してメタクリル樹脂〔PMMA6〕を製造した。
　スミペックスＭＨＦ（住友化学社製）をメタクリル樹脂〔PMMA7〕とした。
　上記〔PMMA1〕～〔PMMA7〕の物性を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　実施例で使用したポリカーボネート樹脂を以下に記載し、物性を表２に記載した。
　ＰＣ１：帝人社製、パンライトＡＤ－５５０３（品番）、ＭＶＲ（３００℃、１．２Ｋｇ）＝５４ｃｍ3／１０分、Ｍｖ＝１５２００
　ＰＣ２：出光興産社製、タフロンＬＣ１７００（品番）、ＭＶＲ（３００℃、１．２Ｋｇ）＝４０ｃｍ3／１０分、Ｍｖ＝１６２００
　ＰＣ３：三菱エンジニアリングプラスチックス社製、ユーピロンＨＬ４０００（品番）、ＭＶＲ（３００℃、１．２Ｋｇ）＝６０ｃｍ3／１０分、Ｍｖ＝１５１００
　ＰＣ４：住化スタイロンポリカーボネート社製、ＳＤ ＰＯＬＹＣＡ　ＳＤ－２２０１Ｗ（品番）、ＭＶＲ（３００℃、１．２Ｋｇ）＝１１５ｃｍ3／１０分、Ｍｖ＝１３０００
　ＰＣ５：住化スタイロンポリカーボネート社製、ＳＤ ＰＯＬＹＣＡ　ＴＲ－２００１（品番）、ＭＶＲ（３００℃、１．２Ｋｇ）＝２００ｃｍ3／１０分、Ｍｖ＝１１４００
　ＰＣ６：ＤＯＷ社製、ＤＶＤ１０８０（品番）、ＭＶＲ（３００℃、１．２Ｋｇ）＝８０ｃｍ3／１０分、Ｍｖ＝１４１００
　ＰＣ７：住化スタイロンポリカーボネート社製、ＣＡＬＩＢＲＥ　３０１－２２（品番）、ＭＶＲ（３００℃、１．２Ｋｇ）＝２２ｃｍ3／１０分、Ｍｖ＝１８８００
Figure JPOXMLDOC01-appb-T000002
　紫外線吸収剤として、２，４，６－トリス（２－ヒドロキシ－４－ヘキシルオキシ－３－メチルフェニル）－１，３，５－トリアジン（ＡＤＥＫＡ社製；ＬＡ－Ｆ７０）を使用した。
＜実施例１＞
　メタクリル樹脂〔PMMA１〕１００質量部およびポリカーボネート樹脂〔PC１〕２．６質量部を混ぜ合わせ、二軸押出機（テクノベル社製、商品名：ＫＺＷ２０ＴＷ-４５ＭＧ-ＮＨ-６００）で２５０℃にて混練押出してメタクリル樹脂組成物〔1〕を製造した。得られたメタクリル樹脂組成物〔1〕を熱プレス成形して５０ｍｍ×５０ｍｍ×１．０ｍｍの板状成形体を成形し、全光線透過率、ヘイズおよびガラス転移温度を測定した。メタクリル樹脂組成物〔1〕の物性を表３に示す。
　メタクリル樹脂組成物〔1〕を、８０℃で１２時間乾燥させた。２０ｍｍφ単軸押出機（ＯＣＳ社製）を用いて、樹脂温度２６０℃にて、メタクリル樹脂組成物〔1〕を１５０ｍｍ幅のＴダイから押し出し、それを表面温度８５℃のロールにて引き取り、幅１１０ｍｍ、厚さ１６０μｍの未延伸フィルムを得た。得られた未延伸フィルムについての膜厚安定性と強度の測定結果を表３に示す。
　前記の手法にて得られた未延伸フィルムを、１００ｍｍ×１００ｍｍに切り出し、パンタグラフ式二軸延伸試験機（東洋精機社製）により、ガラス転移温度＋１５℃の延伸温度、一方向５００％／分の延伸速度、一方向２倍の延伸倍率で逐次二軸延伸し（面積比で４倍）、２分かけて１００℃以下に冷却して取り出し、厚さ４０μｍの二軸延伸フィルムを得た。得られた二軸延伸フィルムについての表面平滑性、加熱収縮率、全光線透過率、ヘイズ、面内位相差Ｒｅ、厚さ方向位相差Ｒｔｈおよび未延伸フィルムから延伸フィルムを作製する際の延伸性の測定結果を表３に示す。
＜実施例２～９、比較例１～７＞
　表３および表４に示す配合とする以外は実施例１と同じ方法でメタクリル樹脂組成物〔2〕～〔16〕を製造した。得られたメタクリル樹脂組成物〔2〕～〔16〕を熱プレス成形して５０ｍｍ×５０ｍｍ×１．０ｍｍの板状成形体を成形し、全光線透過率、ヘイズおよびガラス転移温度を測定した。メタクリル樹脂組成物〔2〕～〔16〕の物性を表３および表４に示す。
　メタクリル樹脂組成物〔1〕の代わりにメタクリル樹脂組成物〔2〕～〔16〕を用いた以外は実施例１と同じ方法で未延伸フィルム並びに二軸延伸フィルムを得た。評価結果を表３および表４に示す。
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
（偏光子）
　平均重合度２４００、ケン化度９９．９モル％、厚さ７５μｍのポリビニルアルコールフィルムを、３０℃の温水中に６０秒間浸漬して膨潤させた。次いで、０．３重量％（重量比：ヨウ素／ヨウ化カリウム＝０．５／８）の３０℃のヨウ素溶液中で１分間染色しながら、３．５倍まで延伸した。その後、６５℃の４重量％のホウ酸水溶液中に０．５分間浸漬しながら総合延伸倍率が６倍まで延伸した。延伸後、７０℃のオーブンで３分間乾燥を行い、厚さ２２μｍの偏光子を得た。
＜偏光板Ｘの作製＞
　実施例７の二軸延伸フィルムを偏光子保護フィルムＡとして用いた。
　ポリエステルウレタン（第一工業製薬社製、商品名：スーパーフレックス２１０、固形分：３３％）１６．８ｇ、架橋剤（オキサゾリン含有ポリマー、日本触媒社製、商品名：エポクロスＷＳ－７００、固形分：２５％）４．２ｇ、１重量％のアンモニア水２．０ｇ、コロイダルシリカ（扶桑化学工業社製、クォートロンＰＬ－３、固形分：２０重量％）０．４２ｇおよび純水７６．６ｇを混合し、易接着剤組成物を得た。
　得られた易接着剤組成物を、コロナ放電処理を施した実施例７の二軸延伸フィルムのコロナ放電処理面に、乾燥後の厚さが１００ｎｍとなるように、バーコーターで塗布した。その後、フィルムを熱風乾燥機（１１０℃）に投入し、易接着剤組成物を約５分乾燥させて、実施例７の二軸延伸フィルム上に易接着層を形成した。
　次に、Ｎ－ヒドロキシエチルアクリルアミド（興人社製）を３８．３質量部と、トリプロピレングリコールジアクリレート（商品名：アロニックスＭ－２２０，東亞合成社製）を１９．１質量部と、アクリロイルモルホリン（興人社製）を３８．３部と、光重合開始剤（商品名：ＫＡＹＡＣＵＲＥ　ＤＥＴＸ－Ｓ，ジエチルチオキサントン，日本化薬社製）１．４質量部とを混合して５０℃で１時間撹拌して活性エネルギー線硬化型接着剤を得た。
　上記活性エネルギー線硬化型接着剤を、偏光子保護フィルムＡの易接着層側に、乾燥後の厚さが５００ｎｍとなるように塗布した。その後、活性エネルギー線硬化型接着剤を介して、前述の偏光子の両側に1枚ずつの偏光子保護フィルムＡを、小型ラミネーターを用いて積層した。貼り合わせた偏光子保護フィルムＡの両側から、ＩＲヒーターを用いて５０℃に加温し、積算照射量１０００ｍＪ／ｃｍ２の紫外線を両面に照射して、活性エネルギー線硬化型接着剤を硬化させ、偏光子の両面に透明な偏光子保護フィルムＡを有する偏光板Ｘを得た。作製した偏光板Ｘを８０℃９０％ＲＨの恒温恒湿機に投入して１００時間後の偏光子の劣化の程度を目視にて観察したところ劣化は認められなかった。
＜偏光板Ｙの作製＞
　厚さ４０μｍのトリアセチルセルロースフィルムを、１０％の水酸化ナトリウム水溶液（６０℃）に３０秒間浸漬してケン化した後、６０秒間水洗し、偏光子保護フィルムＢを得た。
　アセトアセチル基含有ポリビニルアルコール系樹脂（平均重合度：１２００、ケン化度：９８．５モル％，アセトアセチル基変性度：５モル％）１００質量部に対し、メチロールメラミン２０質量部を３０℃の温度条件下で純水に溶解し、固形分濃度０．５％の水溶液を得た。得られた水溶液を接着剤組成物として、３０℃の温度条件下で用いた。
　偏光子保護フィルムＢに、上記接着剤組成物をその調製から３０分後に、乾燥後の厚さが５０ｎｍとなるように塗布した。その後、接着剤組成物を介して、前述した偏光子の両側それぞれに偏光子保護フィルムＢを、小型ラミネーターを用いて積層し、熱風乾燥機（７０℃）に投入して５分間乾燥させて、偏光板Ｙを得た。作製した偏光板Ｙを８０℃９０％ＲＨの恒温恒湿機に投入して１００時間後の偏光子の劣化の程度を目視にて観察したところ、全面に劣化が認められた。
　この出願は、２０１４年４月１８日に出願された日本出願特願２０１４－８５９６５を基礎とする優先権を主張し、その開示の全てをここに取り込む。
　本発明のメタクリル樹脂組成物は、透明性が高く、耐熱性が高く、位相差が小さく、且つ薄く延伸できるため、偏光子保護フィルム、位相差フィルム、液晶保護板、携帯型情報端末の表面材、携帯型情報端末の表示窓保護フィルム、導光フィルム、銀ナノワイヤーやカーボンナノチューブを表面に塗布した透明導電フィルム、各種ディスプレイの前面板用途などに好適である。特に本発明のフィルムは位相差が小さいため、偏光子保護フィルムに好適である。
　本発明のフィルムは透明性、耐熱性が高いため、光学用途以外の用途として、IRカットフィルムや、防犯フィルム、飛散防止フィルム、加飾フィルム、金属加飾フィルム、太陽電池のバックシート、フレキシブル太陽電池用フロントシート、シュリンクフィルム、インモールドラベル用フィルムに使用することができる。
１１　偏光子
１２　接着剤層
１３　易接着層
１４　偏光子保護フィルム
１５　接着剤層
１６　光学フィルム

Claims (13)

  1. 　メタクリル樹脂およびポリカーボネート樹脂を含むメタクリル樹脂組成物であって、
    　前記ポリカーボネート樹脂は、１５０００より大きく、３２０００より小さい粘度平均分子量を有しており、
    　前記メタクリル樹脂１００質量部に対する前記ポリカーボネート樹脂の含有量が１質量部以上、４質量部以下であって、
    　当該メタクリル樹脂組成物に対して前記メタクリル樹脂と前記ポリカーボネート樹脂の合計量を８０～１００質量％とするメタクリル樹脂組成物。
  2. 　前記メタクリル樹脂組成物の分子量分布が１．３～１．５である請求項１に記載のメタクリル樹脂組成物。
  3. 　前記メタクリル樹脂が、
    　三連子表示のシンジオタクティシティ（ｒｒ）が５０％以上であり、
    　且つメタクリル酸メチルに由来する構造単位の含有量が９２質量％以上、１００質量％以下である請求項１または２に記載のメタクリル樹脂組成物。
  4. 　前記メタクリル樹脂の三連子表示のシンジオタクティシティ（ｒｒ）が、５８％以上、８５％以下である請求項１～３のいずれかひとつに記載のメタクリル樹脂組成物。
  5. 　前記メタクリル樹脂のメタクリル酸メチル由来の構造単位の含有量が、９９質量％以上である請求項１～４のいずれかひとつに記載のメタクリル樹脂組成物。
  6. 　前記メタクリル樹脂組成物の重量平均分子量が７００００～２０００００である請求項１～５のいずれかひとつに記載のメタクリル樹脂組成物。
  7. 　前記ポリカーボネート樹脂が、
    　１５０００より大きく、１８０００より小さい粘度平均分子量を有する請求項１～６のいずれかひとつに記載のメタクリル樹脂組成物。
  8. 　請求項１～７のいずれかひとつに記載のメタクリル樹脂組成物からなる成形体。
  9. 　請求項１～７のいずれかひとつに記載のメタクリル樹脂組成物からなるフィルム。
  10. 　厚さが１０～５０μｍである、請求項９に記載のフィルム。
  11. 　面積比で１．５～８倍に二軸延伸された請求項９または１０に記載のフィルム。
  12. 　偏光子保護フィルムとして用いられる請求項９～１１のいずれかひとつに記載のフィルム。
  13. 　請求項１２に記載のフィルムが少なくとも１枚積層された偏光板。
PCT/JP2015/002102 2014-04-18 2015-04-16 メタクリル樹脂組成物、成形体、フィルムおよび偏光板 Ceased WO2015159552A1 (ja)