WO2015093289A1 - Condensateur au lithium-ion - Google Patents

Condensateur au lithium-ion Download PDF

Info

Publication number
WO2015093289A1
WO2015093289A1 PCT/JP2014/081932 JP2014081932W WO2015093289A1 WO 2015093289 A1 WO2015093289 A1 WO 2015093289A1 JP 2014081932 W JP2014081932 W JP 2014081932W WO 2015093289 A1 WO2015093289 A1 WO 2015093289A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
positive electrode
active material
electrode active
lithium ion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2014/081932
Other languages
English (en)
Japanese (ja)
Inventor
奥野　一樹
真嶋　正利
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Electric Industries Ltd
Original Assignee
Sumitomo Electric Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Electric Industries Ltd filed Critical Sumitomo Electric Industries Ltd
Publication of WO2015093289A1 publication Critical patent/WO2015093289A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention porte sur un condensateur au lithium-ion qui comprend une électrode positive contenant un matériau actif d'électrode positive, une électrode négative contenant un matériau actif d'électrode négative, un séparateur disposé entre l'électrode positive et l'électrode négative, et un électrolyte. Le matériau actif d'électrode positive contient au moins un matériau qui porte de manière réversible des anions. Le matériau actif d'électrode négative contient un matériau carboné ayant une structure de cristal de type graphite. Le rapport de la capacité (Cn) par zone projetée d'unité de l'électrode négative sur la capacité (Cp) par zone projetée d'unité de l'électrode positive, à savoir Cn/(Cp est de 20 ou plus.
PCT/JP2014/081932 2013-12-17 2014-12-03 Condensateur au lithium-ion Ceased WO2015093289A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2013-259930 2013-12-17
JP2013259930 2013-12-17
JP2014226231A JP2015135947A (ja) 2013-12-17 2014-11-06 リチウムイオンキャパシタ
JP2014-226231 2014-11-06

Publications (1)

Publication Number Publication Date
WO2015093289A1 true WO2015093289A1 (fr) 2015-06-25

Family

ID=53402638

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/081932 Ceased WO2015093289A1 (fr) 2013-12-17 2014-12-03 Condensateur au lithium-ion

Country Status (2)

Country Link
JP (1) JP2015135947A (fr)
WO (1) WO2015093289A1 (fr)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015170737A (ja) * 2014-03-07 2015-09-28 住友重機械工業株式会社 リチウムイオンキャパシタ、蓄電装置、及びショベル
CN110372068B (zh) * 2019-07-10 2021-07-27 常州大学 一种cof负载的金属氢氧化物电极的制备方法及其应用

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1154383A (ja) * 1997-08-06 1999-02-26 Asahi Glass Co Ltd 電気二重層キャパシタ
JP2010171154A (ja) * 2009-01-22 2010-08-05 Sumitomo Electric Ind Ltd キャパシタ
JP2012253072A (ja) * 2011-05-31 2012-12-20 National Institute Of Advanced Industrial & Technology リチウムイオンキャパシタ

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1154383A (ja) * 1997-08-06 1999-02-26 Asahi Glass Co Ltd 電気二重層キャパシタ
JP2010171154A (ja) * 2009-01-22 2010-08-05 Sumitomo Electric Ind Ltd キャパシタ
JP2012253072A (ja) * 2011-05-31 2012-12-20 National Institute Of Advanced Industrial & Technology リチウムイオンキャパシタ

Also Published As

Publication number Publication date
JP2015135947A (ja) 2015-07-27

Similar Documents

Publication Publication Date Title
EP3109876A1 (fr) Dispositif de stockage électrique, et système de charge et décharge
WO2015098903A1 (fr) Condensateur à ions de métal alcalin
WO2014148250A1 (fr) Condensateur lithium-ion et son procédé de chargement et déchargement
US20160336118A1 (en) Positive electrode for lithium ion capacitor and lithium ion capacitor using the same
EP3073500A1 (fr) Condensateur et son procédé de fabrication
JP6260209B2 (ja) アルカリ金属イオンキャパシタ、その製造方法および充放電方法
JP2015153700A (ja) 蓄電デバイス
KR101138522B1 (ko) 전극 구조체 및 이를 구비하는 리튬 이온 캐패시터
WO2015093289A1 (fr) Condensateur au lithium-ion
JP2015095634A (ja) 蓄電デバイスおよびその製造方法
EP3109877A1 (fr) Condensateur et son procédé de charge et de décharge
WO2015107965A1 (fr) Corps poreux d'aluminium, électrode pour dispositif condensateur et dispositif condensateur associé
JP2016164948A (ja) キャパシタ用正極およびキャパシタの製造方法ならびにキャパシタ
WO2015107800A1 (fr) Corps poreux de cuivre, électrode pour dispositif condensateur et dispositif condensateur associé
JP2015204437A (ja) リチウムイオンキャパシタ
WO2016002564A1 (fr) Cathode de condensateur et procédé de production de condensateur
WO2015087591A1 (fr) Condensateur et procédé de charge/décharge associé
JP2015133183A (ja) ナトリウム溶融塩電池
JP2004273942A (ja) 電気二重キャパシタ
JP2017098365A (ja) リチウムイオンキャパシタおよびリチウムイオンキャパシタが装着された電子機器
JP2017098363A (ja) リチウムイオンキャパシタおよびリチウムイオンキャパシタが装着された電子機器
JP2016181603A (ja) リチウムイオンキャパシタ

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14872715

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14872715

Country of ref document: EP

Kind code of ref document: A1