WO2014090877A1 - Iso(thio)cyanates (hétéro)aromatiques en tant qu'additifs navettes redox pour cellules galvaniques - Google Patents

Iso(thio)cyanates (hétéro)aromatiques en tant qu'additifs navettes redox pour cellules galvaniques Download PDF

Info

Publication number
WO2014090877A1
WO2014090877A1 PCT/EP2013/076234 EP2013076234W WO2014090877A1 WO 2014090877 A1 WO2014090877 A1 WO 2014090877A1 EP 2013076234 W EP2013076234 W EP 2013076234W WO 2014090877 A1 WO2014090877 A1 WO 2014090877A1
Authority
WO
WIPO (PCT)
Prior art keywords
alkyl
atoms
redox
aqueous electrolyte
lithium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2013/076234
Other languages
German (de)
English (en)
Inventor
Ulrich Wietelmann
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Albemarle Germany GmbH
Original Assignee
Rockwood Lithium GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rockwood Lithium GmbH filed Critical Rockwood Lithium GmbH
Publication of WO2014090877A1 publication Critical patent/WO2014090877A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un électrolyte non aqueux d'une cellule galvanique qui contient un additif ayant une activité redox. Cet additif possède une structure de formule générale A ou B, où X = O, S ou Se; Y = N ou C; Z = O, S ou NR (R = alkyle contenant 1 à 8 atomes de C); R1, R2, R3 sont indépendamment les uns des autres NCS, NCO, alkyle (1 à 8 atomes de C), perfluoroalkyle (CnF2n+1 avec n = 1 à 8), aryle, F ou Cl, CN, OR (R = alkyle contenant 1 à 8 atomes de C, peut également contenir d'autres groupes alcoxy), NR2 (R = alkyle contenant 1 à 8 atomes de C); R4 = H, NCS, NCO, alkyle (1 à 8 atomes de C), perfluoroalkyle (CnF2n+1 avec n = 1 à 8), aryle, F ou Cl, CN, OR (R = alkyle contenant 1 à 8 atomes de C, peut également contenir d'autres groupes alcoxy), NR2 (R = alkyle contenant 1 à 8 atomes de C); uniquement pour Y = C, R5 = H, NCS, NCO, alkyle (1 à 8 atomes de C), perfluoroalkyle (CnF2n+1 avec n = 1 à 8), aryle, F ou Cl, CN, OR (R = alkyle contenant 1 à 8 atomes de C, peut également contenir d'autres groupes alcoxy), NR2 (R = alkyle contenant 1 à 8 atomes de C), et l'additif comprenant au moins un groupe isocyanate ou/et isothiocyanate ou/et isosélénocyanate. L'invention concerne en outre des cellules galvaniques contenant ces additifs ayant une activité redox.
PCT/EP2013/076234 2012-12-12 2013-12-11 Iso(thio)cyanates (hétéro)aromatiques en tant qu'additifs navettes redox pour cellules galvaniques Ceased WO2014090877A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102012222941.8 2012-12-12
DE102012222941 2012-12-12

Publications (1)

Publication Number Publication Date
WO2014090877A1 true WO2014090877A1 (fr) 2014-06-19

Family

ID=49759305

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2013/076234 Ceased WO2014090877A1 (fr) 2012-12-12 2013-12-11 Iso(thio)cyanates (hétéro)aromatiques en tant qu'additifs navettes redox pour cellules galvaniques

Country Status (2)

Country Link
DE (1) DE102013225596A1 (fr)
WO (1) WO2014090877A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110183356A (zh) * 2019-05-20 2019-08-30 江苏蓝丰生物化工股份有限公司 取代类对苯二异氰酸酯的制备方法及非腈极性有机溶剂在其制备中的应用
CN115395102A (zh) * 2022-09-30 2022-11-25 珠海冠宇电池股份有限公司 一种电解液和电池
CN118867392A (zh) * 2024-08-19 2024-10-29 东莞理工学院 一种锂离子电池电解液及其应用

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102014109237A1 (de) * 2014-07-02 2016-01-07 Clariant Produkte (Deutschland) Gmbh Lithium-Ionen-Batterie mit reduzierter Gasentwicklung
CN105036091A (zh) * 2015-09-18 2015-11-11 花垣县强桦矿业有限责任公司 一种从电解锰压滤渣中回收硒的方法
DE102015218189B4 (de) * 2015-09-22 2025-02-27 Bayerische Motoren Werke Aktiengesellschaft Lithium-Ionen-Zelle
CN109585919B (zh) * 2018-11-06 2020-08-28 欣旺达电子股份有限公司 锂离子电池及其电解液

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10042149A1 (de) * 1999-09-17 2001-05-17 Merck Patent Gmbh Nichtwäßriger Elektrolyt sowie diesen enthaltende elektrochemische Zelle
JP2002008719A (ja) * 2000-06-27 2002-01-11 Mitsui Chemicals Inc 非水電解液およびそれを使用した二次電池
US6905762B1 (en) * 2001-02-13 2005-06-14 The United States Of America As Represented By The Secretary Of The Army Non-aqueous electrolyte solutions comprising additives and non-aqueous electrolyte cells comprising the same
JP2006012713A (ja) * 2004-06-29 2006-01-12 Asahi Denka Kogyo Kk 非水電解液及び該電解液を用いた非水電解液二次電池
EP2190054A1 (fr) * 2007-09-12 2010-05-26 Mitsubishi Chemical Corporation Solution électrolytique non aqueuse pour batterie secondaire et batterie secondaire à électrolyte non aqueux
WO2012115119A1 (fr) * 2011-02-22 2012-08-30 三菱化学株式会社 Solution d'électrolyte non aqueux et batterie utilisant cette dernière

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20070072085A1 (en) 2005-09-26 2007-03-29 Zonghai Chen Overcharge protection for electrochemical cells
US8367253B2 (en) 2006-02-02 2013-02-05 U Chicago Argonne Llc Lithium-ion batteries with intrinsic pulse overcharge protection
US8877390B2 (en) 2010-05-25 2014-11-04 Uchicago Argonne, Llc Redox shuttles for lithium ion batteries
EP2539956B1 (fr) 2010-05-25 2017-09-06 UChicago Argonne, LLC Adjuvants de navette redox fonctionnalisés par polyéther pour accumulateurs lithium-ion
US8968940B2 (en) 2010-05-25 2015-03-03 Uchicago Argonne, Llc Redox shuttles for high voltage cathodes

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10042149A1 (de) * 1999-09-17 2001-05-17 Merck Patent Gmbh Nichtwäßriger Elektrolyt sowie diesen enthaltende elektrochemische Zelle
JP2002008719A (ja) * 2000-06-27 2002-01-11 Mitsui Chemicals Inc 非水電解液およびそれを使用した二次電池
US6905762B1 (en) * 2001-02-13 2005-06-14 The United States Of America As Represented By The Secretary Of The Army Non-aqueous electrolyte solutions comprising additives and non-aqueous electrolyte cells comprising the same
JP2006012713A (ja) * 2004-06-29 2006-01-12 Asahi Denka Kogyo Kk 非水電解液及び該電解液を用いた非水電解液二次電池
EP2190054A1 (fr) * 2007-09-12 2010-05-26 Mitsubishi Chemical Corporation Solution électrolytique non aqueuse pour batterie secondaire et batterie secondaire à électrolyte non aqueux
WO2012115119A1 (fr) * 2011-02-22 2012-08-30 三菱化学株式会社 Solution d'électrolyte non aqueux et batterie utilisant cette dernière
US20130337317A1 (en) * 2011-02-22 2013-12-19 Mitsubishi Chemical Corporation Nonaqueous electrolytic solution, and battery using same

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
C. KOREPP ET AL: "Isocyanate compounds as electrolyte additives for lithium-ion batteries", JOURNAL OF POWER SOURCES, vol. 174, no. 2, 6 December 2007 (2007-12-06), pages 387 - 393, XP025917571, ISSN: 0378-7753, [retrieved on 20071206], DOI: 10.1016/J.JPOWSOUR.2007.06.141 *
S.S. ZHANG ET AL: "Aromatic isocyanate as a new type of electrolyte additive for the improved performance of Li-ion batteries", JOURNAL OF POWER SOURCES, vol. 163, no. 1, 7 December 2006 (2006-12-07), pages 567 - 572, XP027938506, ISSN: 0378-7753, [retrieved on 20061207] *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110183356A (zh) * 2019-05-20 2019-08-30 江苏蓝丰生物化工股份有限公司 取代类对苯二异氰酸酯的制备方法及非腈极性有机溶剂在其制备中的应用
CN115395102A (zh) * 2022-09-30 2022-11-25 珠海冠宇电池股份有限公司 一种电解液和电池
CN118867392A (zh) * 2024-08-19 2024-10-29 东莞理工学院 一种锂离子电池电解液及其应用

Also Published As

Publication number Publication date
DE102013225596A1 (de) 2014-06-12

Similar Documents

Publication Publication Date Title
EP3113274B1 (fr) Solution d'électrolyte non aqueux et batterie secondaire à solution d'électrolyte non aqueux l'utilisant
WO2014090877A1 (fr) Iso(thio)cyanates (hétéro)aromatiques en tant qu'additifs navettes redox pour cellules galvaniques
EP3979383B1 (fr) Composition d'électrolyte, composition de solvant, électrolyte non aqueux et leur utilisation
EP3738167B1 (fr) Compositions d'électrolytes non-aqueux comprenant du bis(fluorosulfonyl)imidure de lithium
US11050087B2 (en) Silane functionalized ionic liquids
EP4106070A1 (fr) Électrolytes contenant du phosphore
JP4320914B2 (ja) 非水電解液及びそれを用いたリチウム二次電池
EP3709426B1 (fr) Solution d'électrolyte non aqueux et dispositif de stockage d'énergie l'utilisant
KR20070121034A (ko) 비수 전해액, 및 그것을 이용한 전기 화학 에너지 축적디바이스 및 비수 전해액 2차 전지
EP3583653B1 (fr) Additif électrolytique pour batteries lithium-ion
EP2618418A1 (fr) Électrolyte non aqueux et batterie secondaire à électrolyte non aqueux
WO2014060077A2 (fr) Additifs pour cellules galvaniques
CN117613381A (zh) 含有六元环环状硫酸酯的电解质
US20170162909A1 (en) Nonaqueous electrolytic solution including ester having 3,3,3-trifluoropropionate group and nonaqueous electrolyte battery using same
CN105428720B (zh) 一种非水电解液及其制备方法以及一种锂二次电池
EP3373379B1 (fr) Additif pour solutions électrolytiques non aqueuses, solution électrolytique non aqueuse et dispositif de stockage d'électricité
EP1187244A2 (fr) Amines organiques pour piles électrochimiques
US5681669A (en) Electrolyte for lithium secondary battery
KR20180118452A (ko) 이차전지용 전해액 첨가제 및 이를 포함하는 이차전지용 전해액
EP3893311B1 (fr) Utilisation d'un composé comme additif d'une solution d'électrolyte non-aqueux, solution d'électrolyte non-aqueux pour batterie secondaire au lithium et batterie secondaire au lithium la comprenant
DE102014108012B4 (de) Substituierte Pyrazole und deren Verwendung als Leitsalz für Lithium-basierte Energiespeicher
JP4253921B2 (ja) リチウム二次電池
CN110635166B (zh) 电解液、含有该电解液的电池和电动车辆
US6413677B1 (en) Lithium secondary battery electrolyte and lithium secondary battery using the same
KR20160004665A (ko) 리튬 이차 전지용 전해액 및 이를 포함하는 리튬 이차 전지

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13802984

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13802984

Country of ref document: EP

Kind code of ref document: A1