WO2012128337A1 - プラスチック消しゴム、それを含むプラスチック消しゴム複合体及びその製造方法 - Google Patents

プラスチック消しゴム、それを含むプラスチック消しゴム複合体及びその製造方法 Download PDF

Info

Publication number
WO2012128337A1
WO2012128337A1 PCT/JP2012/057419 JP2012057419W WO2012128337A1 WO 2012128337 A1 WO2012128337 A1 WO 2012128337A1 JP 2012057419 W JP2012057419 W JP 2012057419W WO 2012128337 A1 WO2012128337 A1 WO 2012128337A1
Authority
WO
WIPO (PCT)
Prior art keywords
plastic eraser
weight
eraser
plasticizer
range
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2012/057419
Other languages
English (en)
French (fr)
Inventor
伸二 辻尾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sakura Color Products Corp
Original Assignee
Sakura Color Products Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sakura Color Products Corp filed Critical Sakura Color Products Corp
Priority to US14/007,209 priority Critical patent/US9079450B2/en
Priority to GB1318551.7A priority patent/GB2505341B/en
Publication of WO2012128337A1 publication Critical patent/WO2012128337A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

（課題）消字性にすぐれるのみならず、環境負荷が極めて少ないプラスチック消しゴムを提供する。更に、そのようなプラスチック消しゴムを有機ポリマーからなる多孔性構造体に充填してなるプラスチック消しゴム複合体とその製造方法を提供する。 （解決手段）基材樹脂である塩化ビニル系樹脂と可塑剤として４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせを含むプラスチック消しゴムにおいて、上記基材樹脂を２５～６０重量％と上記可塑剤の組み合わせを３０～６０重量％含み、上記可塑剤の組み合わせにおけるジエチレングリコールジベンゾエートの割合が５～６０重量％の範囲であると共に、硬さが５５～７５の範囲にあり、ゲル硬度が３．０～６．０ｋｇｆの範囲にあるプラスチック消しゴムが提供される。

Description

プラスチック消しゴム、それを含むプラスチック消しゴム複合体及びその製造方法
　本発明は、プラスチック消しゴムに関し、詳しくは、環境負荷が極めて少なく、しかも、消字性にすぐれるプラスチック消しゴムに関し、更には、有機ポリマーからなる多孔性構造体にそのようなプラスチック消しゴムを含むプラスチック消しゴム複合体とその製造方法に関する。
　従来、プラスチック消しゴムは、通常、基材樹脂に可塑剤と、必要に応じて、安定剤や着色剤等のその他の添加剤を適宜に加えて均一に攪拌した後、適宜の成形手段を用いて加熱、成形して製造されている。
　このような従来のプラスチック消しゴムにおいて、上記基材樹脂としては、塩化ビニル系樹脂が最も広く用いられており、また、上記可塑剤としては、例えば、ジオクチルフタレート、ジベンジルフタレート等のフタル酸エステル系可塑剤が最も広く用いられている。
　しかし、上述したようなフタル酸エステル系可塑剤は、近年、所謂環境ホルモン（内分泌攪乱物質）として作用する可能性が指摘されており、プラスチック消しゴムについても、フタル酸エステル系可塑剤に代わる新たな可塑剤が望まれている。
　そこで、非フタル酸エステル系可塑剤として、例えば、アセチルクエン酸トリブチル（特許文献１参照）、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）（特許文献２参照）、セバシン酸ジエステル（特許文献３参照）、アルキルスルホン酸フェニル（特許文献４参照）等を用いるプラスチック消しゴムが提案されている。
　更に、ウレタンを基材樹脂とするプラスチック消しゴムにおいては、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジアルキレングリコールベンゾエートの非フタル酸エステル系可塑剤の組み合わせも提案されている（特許文献５参照）。
　また、最近では、有機ポリマーからなる多孔性構造体の空隙にプラスチック消しゴムを有し、紙面上の文字を擦過して消字したとき、消しゴムがその表面で磨耗すると共に、消しゴム表面の上記多孔性構造体の骨格構造が破断されて、よく消字することができるのみならず、消し屑の纏まりのよいプラスチック消しゴム複合体が提案されている（特許文献６参照）。
　しかし、基材樹脂を塩化ビニル系樹脂とするプラスチック消しゴムについては、環境負荷の低減と消字性の向上という観点からは、未だ、効果的な非フタル酸エステル系可塑剤が提案されていない。
特開２００３－１０５１５０号公報 特開２００１－８１２５９号公報 特開２００７－２１７６８号公報 特開２００５－１３８３５９号公報 国際公開ＷＯ２００９／１４５１３２号公報 特開２００１－１３８６８８号公報
　本発明は、プラスチック消しゴム、特に、基材樹脂を塩化ビニル系樹脂とするプラスチック消しゴムにおける上述した問題を解決するためになされたものであって、環境負荷が極めて少なく、しかも、すぐれた消字性を有するプラスチック消しゴムを提供することを目的とする。更に、本発明は、そのようなプラスチック消しゴムを有機ポリマーからなる多孔性構造体の空隙に有するプラスチック消しゴム複合体とその製造方法を提供することを目的とする。
　本発明によれば、基材樹脂である塩化ビニル系樹脂と可塑剤として４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせを含むプラスチック消しゴムにおいて、上記基材樹脂を２５～６０重量％と上記可塑剤の組み合わせを３０～６０重量％含み、上記可塑剤の組み合わせにおけるジエチレングリコールジベンゾエートの割合が５～６０重量％の範囲であると共に、硬さが５５～７５の範囲にあり、ゲル硬度が３．０～６．０ｋｇｆの範囲にあるプラスチック消しゴムが提供される。
　本発明によれば、好ましくは、上記プラスチック消しゴムは、上記可塑剤の組み合わせを３５～５５重量％の範囲で含み。また、上記可塑剤の組み合わせにおけるジエチレングリコールジベンゾエートの割合は１０～５０重量％の範囲である。
　また、本発明によれば、上記プラスチック消しゴムを有機ポリマーからなる多孔性構造体の空隙に有する消しゴム複合体が提供される。
　更に、本発明によれば、上記消しゴム複合体の製造方法において、基材樹脂である塩化ビニル系樹脂２５～６０重量％と可塑剤として４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせ３０～６０重量％を含み、上記可塑剤の組み合わせにおけるジエチレングリコールジベンゾエートの割合が５～６０重量％の範囲であるプラスチゾルを有機ポリマーからなる多孔性構造体に含浸し、その空隙に充填した後、加熱して、上記プラスチゾルを硬化させる製造方法が提供される。
　本発明によるプラスチック消しゴムは、基材樹脂である塩化ビニル系樹脂と可塑剤として４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせを含み、上記基材樹脂を２５～６０重量％、上記可塑剤の組み合わせを３０～６０重量％を含み、上記可塑剤の組み合わせにおけるジエチレングリコールジベンゾエートの割合が５～６０重量％の範囲であると共に、硬さが５５～７５の範囲にあり、ゲル硬度が３．０～６．０ｋｇｆの範囲にある。
　ここに、硬さとは、プラスチック消しゴムが外力に対して可逆的に反発する強さである。ゲル硬度とは、プラスチック消しゴムを構成するゲルを非可逆的に破壊する外力の大きさである。
　本発明によるプラスチック消しゴムの基材樹脂は塩化ビニル系樹脂である。ここに、塩化ビニル系樹脂とはポリ塩化ビニルと塩化ビニル共重合体をいい、塩化ビニル共重合体とは塩化ビニルとこれに共重合性を有するラジカル重合性単量体との共重合体をいい、そのような塩化ビニルと共重合性を有するラジカル重合性単量体は、特に、限定されるものではないが、例えば、エチレン、酢酸ビニル、フッ化ビニル、塩化ビニリデン、メチルビニルエーテル、（メタ）アクリル酸、（メタ）アクリル酸エチル、無水マレイン酸、アクリロニトリル、スチレン等を挙げることができる。本発明において、代表的な塩化ビニル共重合体として、例えば、塩化ビニル－エチレン共重合体や塩化ビニル－酢酸ビニル共重合体等を挙げることができる。
　しかし、本発明においては、基材樹脂として、なかでも、ポリ塩化ビニルが好ましく用いられ、更に、成形によって容易にプラスチック消しゴムを得ることができるように、ポリ塩化ビニルは可塑剤に分散させてなるペースト状のプラスチゾルとして用いられる。
　本発明によれば、可塑剤として、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせが用いられる。このような４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせにおいて、ジエチレングリコールジベンゾエートの割合は５～６０重量％の範囲であり、好ましくは、１０～５０重量％の範囲であり、最も好ましくは、１５～４５重量％の範囲である。
　可塑剤として、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせにおいて、ジエチレングリコールジベンゾエートの割合が低すぎるときは、得られるプラスチック消しゴムのゲル硬度が小さくなり、消字に際して崩れやすい。しかし、ジエチレングリコールジベンゾエートの割合が高すぎるときは、得られるプラスチック消しゴムがゲル硬度が高すぎて、消字率が低下する。
　更に、本発明によれば、可塑剤としての４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせは、プラスチック消しゴムにおいて、３０～６０重量％の範囲で、好ましくは、３０重量％を越えて、６０重量％まで、より好ましくは、３５～５５重量％の範囲で用いられ、最も、好ましくは、４０～５５重量％の範囲で用いられる。プラスチック消しゴムにおける上記可塑剤の組み合わせの割合が少なすぎるときは、得られるプラスチック消しゴムの硬さが高く、弾力性が低下して、消字率が低く、使用感も悪い。しかし、プラスチック消しゴムにおける上記可塑剤の組み合わせの割合が多すぎるときは、得られるプラスチック消しゴムの摩擦抵抗が大きくなって、使用感が悪い。
　本発明によるプラスチック消しゴムは、適度の硬さを有するように、好ましくは、充填剤を含む。充填剤としては、従来、知られている充填剤が適宜に用いられる。具体例として、例えば、炭酸カルシウム、炭酸マグネシウム、酸化マグネシウム、シリカ、タルク、クレー、珪藻土、石英粉、アルミナ、アルミナシリケート、マイカ、セリサナイト、モンモリロナイト等を挙げることができる。特に、限定されるものではないが、プラスチック消しゴムにおける充填剤の割合は、通常、５０重量％以下の範囲であり、好ましくは、５～５０重量％の範囲である。プラスチック消しゴムにおける充填剤の割合が少なすぎるときは、使用に際して、摩耗よりも変形が起こりやすくなり、反対に、多すぎるときは、硬さが高くなって、弾力性が低下する。
　更に、基材樹脂の高温における劣化を防止するために、本発明によれば、プラスチック消しゴムは、安定剤を含むことができる。安定剤としては、例えば、バリウム－亜鉛安定剤、カルシウム－亜鉛系安定剤、マグネシウム－亜鉛安定剤等を挙げることができる。
　本発明においては、プラスチック消しゴムは、上述した充填剤や安定剤のほか、必要に応じて、例えば、粘度調整剤、滑剤、溶剤、着色剤、紫外線吸収剤、防腐剤、防黴剤、芳香剤等の添加剤を含んでもよい。これらの添加剤のプラスチック消しゴムにおける割合は特に、限定されるものではないが、通常、５重量％以下の範囲であり、好ましくは、０．３重量％以下の範囲である。
　本発明によるプラスチック消しゴムは、その製造方法において、特に制約を受けるものではない。例えば、注入法によれば、基材樹脂を可塑剤と、必要に応じて、充填剤、滑剤、着色剤、防腐剤、防黴剤、芳香剤等と混合して、プラスチゾルを調製し、適宜の金型に注入し、加熱して、上記プラスチゾルを硬化させた後、冷却し、適宜に裁断して、プラスチック消しゴムを得ることができる。しかし、成形方法は、上記例示に限定されず、押出成形、射出成形、プレス成形等によることもできる。
　また、本発明によれば、有機ポリマーからなる多孔性構造体の有する空隙に上述したようなプラスチック消しゴムを有するプラスチック消しゴム複合体として得ることもできる。上記有機ポリマーからなる多孔性構造体は既に知られており（特許文献６参照）、空隙を有する三次元の連通空孔（連通気泡ともいう。）を有する骨格構造乃至三次元網状構造を有機ポリマーが構成しており、上記骨格構造は消しゴムを補強すると共に、このような消しゴムを用いて、紙面上の文字を擦過して消字するときには、紙面によって磨耗する消しゴムと共に、紙面を擦過した部分の骨格構造が破壊されて、消しゴムに由来する消し屑と共に纏まりのある消し屑を形成する。
　上記有機ポリマーからなる多孔性構造体において、骨格構造（即ち、空隙を形成する壁体又は骨格）の平均肉厚は、特に制限されないが、例えば、１～１００μｍ、好ましくは、１０～５０μｍであり、骨格構造の有する空隙の平均孔径は、特に制限されないが、例えば、１０μｍから３ｍｍの範囲であり、好ましくは、２０μｍから１ｍｍの範囲である。
　本発明において、多孔性構造体における空隙率（気孔率）は、特に制限されないが、例えば、６０％以上、好ましくは、８０％以上、より好ましくは、９０％以上であり、例えば、９０～９９．８％である。
　本発明によるプラスチック消しゴム複合体は、このような多孔質構造体の空隙に前述したようなプラスチック消しゴムを有する複合体であって、多孔性構造体の空隙の全容積に対するプラスチック消しゴムの充填率は、特に限定されないが、通常、５０％以上、１００％未満であるが、消し屑の纏まり性、消字性及び使用感にバランスよくすぐれるように、好ましくは、７０～９９％、最適には８５％程度である。
　更に、本発明においては、多孔性構造体は、引張強度が３ｋｇｆ／ｃｍ２以下、好ましくは、２ｋｇｆ／ｃｍ２以下である。多孔性構造体が３ｋｇｆ／ｃｍ２を超える引張強度を有するときは、得られるプラスチック消しゴム複合体を用いて消字する際に、消しゴムが摩耗しても、骨格構造がその部分において破壊され難くなるからである。上記引張強度は、サンプル厚みを１０ｍｍ、ダンベルは２号形状、引張速度は３００ｍｍ／分として、ＪＩＳ Ｋ ６４０２に準拠して測定するものとする。
　また、本発明によれば、上記多孔性構造体は、伸びが５００％以下であり、好ましくは、１００％以下である。多孔性構造体が５００％を超える伸びを有するときは、消字の際に消しゴムの摩耗面と多孔性構造体の破断面が一致せず、多孔性構造体の骨格構造が摩耗面から浮き出て、外観上好ましくないからである。この伸びも、上記と同じく、サンプル厚みを１０ｍｍ、ダンベルは２号形状、引張速度は３００ｍｍ／分として、ＪＩＳ Ｋ ６４０２に準拠して測定するものとする。
　また、上記多孔性構造体は、圧縮反発力が０．２ｋｇｆ以上を有し、好ましくは、０．７ｋｇｆ以上を有する。多孔性構造体の圧縮反発力が０．２ｋｇｆ未満であるとき、消しゴムの剛性が十分でなく、強い腰をもたせ難い。この圧縮反発力は、厚さ１０ｍｍのサンプルに直径１５．２ｍｍのディスクを当て、７ｍｍ／分の速さで５ｍｍ圧縮したときの反発力を測定した数値である。
　以上から、本発明において、多孔性構造体は、好ましくは、３ｋｇｆ／ｃｍ２以下の引張強度、５００％以下の伸び、０．２ｋｇｆ以上の圧縮反発力を有することが好ましい。本発明において、多孔性構造体を構成する有機ポリマーとしては、例えば、メラミン系樹脂、エポキシ系樹脂、ウレタン系樹脂、尿素系樹脂、フェノール系樹脂等の熱硬化性樹脂、ポリスチレンのようなスチレン系樹脂、ポリエステルのようなエステル系樹脂、ポリアクリル酸エステルのようなアクリル系樹脂、ポリエチレンのようなオレフィン系樹脂、ポリ塩化ビニルのような塩化ビニル系樹脂等の熱可塑性樹脂、天然ゴム、スチレン－ブタジエンゴム、ニトリル－ブタジエンゴム等のゴム類を挙げることができる。
　特に、本発明においては、例えば、メラミン系樹脂、ウレタン系樹脂、オレフィン系樹脂、塩化ビニル樹脂からなる連続気泡を有する硬くて、脆い多孔性構造体が好ましく用いられる。このような有機ポリマーからなる多孔性構造体は、所謂樹脂発泡体として市販品を入手することができる。例えば、メラミン系樹脂からなる多孔性構造体はＢＡＳＦ社製の「バソテクト」として、また、ウレタン系樹脂からなる多孔性構造体はＩＮＯＡＣ　ＣＯＲＰ．社製の「ＭＦ－５０」として、エチレン系樹脂からなる多孔性構造体は三和加工（株）製の「ＯＰＥＣＥＬＬ　ＬＣ－３００」として、それぞれ入手することができる。
　本発明によるプラスチック消しゴム複合体は、その製造方法において、特に限定されるものではないが、一例を挙げれば、必要に応じて、前述したような種々の添加剤を含む塩化ビニル系樹脂のプラスチゾルを有機ポリマーからなる多孔性構造体に含浸して、その多孔性構造体の空隙に上記プラスチゾルを充填した後、加熱し、プラスチゾルを硬化させ、冷却し、硬化物を適宜に裁断すれば、本発明によるプラスチック消しゴム複合体を得ることができる。
　上述した製造方法において、上記プラスチゾルを加熱、硬化させる際の温度は、通常、１００～１６０℃の範囲であり、加熱時間は、通常、１０分から５０分程度である。
　上述したような方法によって本発明によるプラスチック消しゴム複合体を製造するにあたっては、例えば、温度２０℃、Ｂ型粘度計、回転数６ｒｐｍの条件下に１００～２００００ｍＰａ・s、好ましくは、８００～７０００ｍＰａ・sのプラスチゾルを用いることが望ましい。この範囲内の粘度のプラスチゾルであれば、常温において、多孔性構造体の空隙に容易に含浸させることができる。
　このようにして得られる本発明によるプラスチック消しゴム複合体は、硬さが５５～７５の範囲であり、ゲル硬度が３．０～６．０ｋｇｆの範囲であって、腰が強く、それでいて、崩れ難く、しかも、高い消字性を有する。
　本発明によるプラスチック消しゴム複合体は、上述したように、腰が強く、それでいて、崩れ難く、しかも、高い消字性を有し、使用感にすぐれている。勿論、消し屑は纏まり性にすぐれている。
　本発明によるプラスチック消しゴム複合体の摩擦係数は、消字の際のタッチが軽いように、０．８以下であることが好ましい。また、摩耗率は、消字の際、表面が汚れにくく、容易に消字することができるように、１％以上であることが好ましい。
　更に、本発明によれば、プラスチック消しゴム複合体の製造においても、塩化ビニル系樹脂と共に、可塑剤として、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）９５～４０重量％とジエチレングリコールジベンゾエート５～６０重量％からなる組み合わせを用いることに種々の利点がある。
　即ち、塩化ビニル系樹脂と上記可塑剤を含むプラスチゾルを加熱してゲル化させるための温度を、可塑剤としてフタル酸オクチルやフタル酸ベンジルのようなフタル酸エステル系のものを用いる場合に比べて、約３℃低くすることができる。そのうえ、塩化ビニル系樹脂と上記可塑剤の組み合わせを含むプラスチゾルは、有機ポリマーからなる多孔性構造体への含浸性にもすぐれており、プラスチック消しゴムを生産性高く製造することができる。
　例えば、有機ポリマーからなる多孔性構造体に上記塩化ビニル系樹脂と上記可塑剤の組み合わせを含むプラスチゾルを常圧下に含浸させる際に、雰囲気を真空にせずとも、短時間に容易に、且つ、十分に含浸させることができる。
　以下に実施例を挙げて本発明を詳細に説明するが、本発明はそれら実施例によって何ら限定されるものではない。
実施例１
　表１に示すように、ポリ塩化ビニル（新第一塩ビ（株）製ゼストＰ２１）３１．７重量部、可塑剤として、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）（大日本インキ化学工業（株）製モノサイザーＷ－１５０、表１中、可塑剤１）４３．７重量部とジエチレングリコールジベンゾエート（大日本インキ化学工業（株）製モノサイザーＰＢ－３Ａ、表１中、可塑剤２）４．９重量部の組み合わせ及び炭酸カルシウム（備北粉化工（株）製重質炭酸カルシウム）１９．８重量部を混合、攪拌して、プラスチゾルを調製した。
　このプラスチゾルを金型に充填し、１００℃で２０分間、予備加熱した後、１１６℃で３０分間、本加熱した。その後、金型を冷却し、得られたゲル化物を金型から取り出し、裁断して、プラスチック消しゴムを得た。
　得られたプラスチック消しゴムの硬さ、ゲル硬度及び消字率を表１に示す。但し、硬さ、ゲル硬度及び消字率の数値はいずれも、３回の測定値の平均値である。プラスチック消しゴムの硬さ、ゲル硬度及び消字率の測定方法は下記のとおりである。
（プラスチック消しゴムの硬さ）
　ＪＩＳ　Ｓ　６０５０に準じて測定した。
（プラスチック消しゴムのゲル硬度）
　厚さ５ｍｍ、直径１０ｍｍの円盤状の試料を調製し、その中央に直径４．４ｍｍのロッドを７ｍｍ／分の速度で押し当てていき、ロッドを押し当てた部分が破断した時の加重をゲル硬度として測定した。測定器はアイコーエンジニアリング（株）製ゲル硬度計を用いた。
（プラスチック消しゴムの消字率）
　ＪＩＳ　Ｓ　６０５０に準じて測定した。
実施例２及び３
　実施例１と同じポリ塩化ビニル、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）、ジエチレングリコールジベンゾエート及び炭酸カルシウムをそれぞれ表１に示す量にて用いて、実施例１と同様にして、プラスチック消しゴムを得た。得られたプラスチック消しゴムの硬さ、ゲル硬度及び消字率を表１に示す。
比較例１及び２
　実施例１と同じポリ塩化ビニル、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）、ジエチレングリコールジベンゾエート及び炭酸カルシウムをそれぞれ表１に示す量にて用いて、実施例１と同様にして、プラスチック消しゴムを得た。得られたプラスチック消しゴムの硬さ、ゲル硬度及び消字率を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　表１に示す結果から明らかなように、本発明によるプラスチック消しゴムは、硬さが５５～７５の範囲にあり、ゲル硬度が３．０～６．０ｋｇｆの範囲にあって、腰が強く、崩れ難く、しかも、高い消字率を有している。これに対して、比較例１によるプラスチック消しゴムは、ゲル硬度が小さく、消字に際して崩れやすい。また、比較例２によるプラスチック消しゴムは、ゲル硬度が高く、消字率が低い。
実施例４
（プラスチゾルの多孔性構造体への含浸性の評価）
　実施例１において調製したプラスチゾルを温度２５℃にて有底のプレート状金型内に充填し、その上に厚み１０ｍｍ、空隙率９８％のメラミン樹脂からなる多孔性構造体のシートを載せて、この多孔性構造体のシートの上表面まで上記プラスチゾルが含浸するまでの時間を測定したところ、５分であった。
　実施例１において、可塑剤として、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせに代えて、フタル酸オクチル、アセチルクエン酸トリブチル、アルキルスルホン酸フェニルをそれぞれ４８．６重量部用いた以外は、同様にして、プラスチゾルを調製し、上述したようにして、多孔性構造体のシートをこれらプラスチゾルがそれぞれ含浸するまでの時間を測定したところ、それぞれ７分、１５分及び１７分であった。
　即ち、可塑剤として、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせを用いるとき、可塑剤として、上記その他の可塑剤を用いる場合に比べて、プラスチゾルをより速やかに多孔性構造体に含浸させることができる。
（プラスチゾルのゲル化性の評価）
　実施例１において調製したプラスチゾルを金型に充填し、１００℃で２０分間予備加熱した後、１１６℃で３０分間することによって、プラスチゾルをゲル化させることができた。
　実施例１において、可塑剤として、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせに代えて、フタル酸オクチルを４８．６重量部用いた以外は、同様にして、プラスチゾルを調製し、これを金型に充填し、１００℃で２０分間予備加熱した後、１１９℃で３０分間することによって、プラスチゾルはゲル化した。
　即ち、可塑剤として、４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせを用いるとき、可塑剤として、フタル酸オクチルを用いる場合に比べて、プラスチゾルをより低温にてゲル化させることができる。
 
 

Claims (5)

  1. 　基材樹脂である塩化ビニル系樹脂と可塑剤として４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせを含むプラスチック消しゴムにおいて、上記基材樹脂を２５～６０重量％と上記可塑剤の組み合わせを３０～６０重量％含み、上記可塑剤の組み合わせにおけるジエチレングリコールジベンゾエートの割合が５～６０重量％の範囲であると共に、硬さが５５～７５の範囲にあり、ゲル硬度が３．０～６．０ｋｇｆの範囲にあるプラスチック消しゴム。
  2. 　可塑剤の組み合わせを３５～５５重量％の範囲で含む請求項１に記載のプラスチック消しゴム。
  3. 　可塑剤の組み合わせにおけるジエチレングリコールジベンゾエートの割合が１０～５０重量％の範囲である請求項１又は２に記載のプラスチック消しゴム。
  4. 　請求項１から３のいずれかに記載のプラスチック消しゴムを有機ポリマーからなる多孔性構造体の空隙に有するプラスチック消しゴム複合体。
  5. 　請求項４に記載の消しゴム複合体の製造方法において、基材樹脂である塩化ビニル系樹脂２５～６０重量％と可塑剤として４，５－エポキシ－１，２－シクロヘキサンジカルボン酸ビス（２－エチルヘキシル）とジエチレングリコールジベンゾエートの組み合わせ３０～６０重量％を含み、上記可塑剤の組み合わせにおけるジエチレングリコールジベンゾエートの割合が５～６０重量％の範囲であるプラスチゾルを有機ポリマーからなる多孔性構造体に含浸し、その空隙に充填した後、加熱して、上記プラスチゾルを硬化させる製造方法。
     
PCT/JP2012/057419 2011-03-24 2012-03-23 プラスチック消しゴム、それを含むプラスチック消しゴム複合体及びその製造方法 Ceased WO2012128337A1 (ja)