[go: up one dir, main page]

WO2011071742A2 - Procédé de préparation de dispersions stables d'amidon - Google Patents

Procédé de préparation de dispersions stables d'amidon Download PDF

Info

Publication number
WO2011071742A2
WO2011071742A2 PCT/US2010/058690 US2010058690W WO2011071742A2 WO 2011071742 A2 WO2011071742 A2 WO 2011071742A2 US 2010058690 W US2010058690 W US 2010058690W WO 2011071742 A2 WO2011071742 A2 WO 2011071742A2
Authority
WO
WIPO (PCT)
Prior art keywords
starch
dispersion
extruder
liquid
feed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2010/058690
Other languages
English (en)
Other versions
WO2011071742A3 (fr
Inventor
Gregory W. Welsch
Michael D. Read
John A. Roper, Iii
Brian J. Ninness
Evelyn L. Wilson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Global Technologies LLC
Original Assignee
Dow Global Technologies LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Global Technologies LLC filed Critical Dow Global Technologies LLC
Priority to KR1020127017748A priority Critical patent/KR101819056B1/ko
Priority to EP10836442.3A priority patent/EP2509445B1/fr
Priority to CN201080056089.3A priority patent/CN102651977B/zh
Priority to US13/514,380 priority patent/US9068062B2/en
Publication of WO2011071742A2 publication Critical patent/WO2011071742A2/fr
Publication of WO2011071742A3 publication Critical patent/WO2011071742A3/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un procédé de préparation d'une dispersion d'amidon dans un liquide hydroxylique, le procédé comprenant l'introduction d'une charge d'alimentation à base d'amidon et d'un liquide hydroxylique dans une extrudeuse, et l'application, dans l'extrudeuse, de forces de cisaillement à l'amidon et au liquide dans des conditions suffisantes pour préparer une dispersion stable de particules d'amidon dans le liquide hydroxylique.
PCT/US2010/058690 2009-12-10 2010-12-02 Procédé de préparation de dispersions stables d'amidon Ceased WO2011071742A2 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
KR1020127017748A KR101819056B1 (ko) 2009-12-10 2010-12-02 안정한 전분 분산액의 제조 방법
EP10836442.3A EP2509445B1 (fr) 2009-12-10 2010-12-02 Procédé de préparation de dispersions stables d'amidon
CN201080056089.3A CN102651977B (zh) 2009-12-10 2010-12-02 制备稳定的淀粉分散体的方法
US13/514,380 US9068062B2 (en) 2009-12-10 2010-12-02 Process for preparing stable starch dispersions

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US28540409P 2009-12-10 2009-12-10
US61/285,404 2009-12-10

Publications (2)

Publication Number Publication Date
WO2011071742A2 true WO2011071742A2 (fr) 2011-06-16
WO2011071742A3 WO2011071742A3 (fr) 2011-10-13

Family

ID=44146115

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2010/058690 Ceased WO2011071742A2 (fr) 2009-12-10 2010-12-02 Procédé de préparation de dispersions stables d'amidon

Country Status (5)

Country Link
US (1) US9068062B2 (fr)
EP (1) EP2509445B1 (fr)
KR (1) KR101819056B1 (fr)
CN (1) CN102651977B (fr)
WO (1) WO2011071742A2 (fr)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013538238A (ja) * 2010-06-07 2013-10-10 ダウ グローバル テクノロジーズ エルエルシー デンプン粒子の安定分散体の調製方法
US20140201872A1 (en) * 2011-08-30 2014-07-17 Dow Global Technologies Llc Coating composition comprising a cellulose ether and starch
US9580846B2 (en) 2011-06-03 2017-02-28 Ecosynthetix Ltd. Curable sheared or extruded, cross linked starch nanoparticle latex binder for use with mineral, natural organic or synthetic fibre products and non-woven mats
US9616696B2 (en) 2013-10-23 2017-04-11 Ecosynthetix Inc. Coating for paper adapted for inkjet printing
WO2017070578A1 (fr) 2015-10-21 2017-04-27 The Regents Of The University Of Michigan Détection et traitement de caries et de microcavités avec des nanoparticules
CN103814073B (zh) * 2011-09-19 2018-09-04 诺瓦蒙特股份公司 含络合淀粉的稳定水性分散体
US10285943B2 (en) 2010-12-02 2019-05-14 Greenmark Biomedical Inc. Aptamer bioconjugate drug delivery device
JP2020026527A (ja) * 2018-08-10 2020-02-20 緑世界環保材料科技股▲ふん▼有限公司Ｇｒｅｅｎ Ｗｏｒｌｄ Ｂｉｏｔｅｃｈ Ｍａｔｅｒｉａｌｓ Ｃｏ．，Ｌｔｄ． 疎水性を有する熱可塑性デンプン複合材料とその製造方法
US11453798B2 (en) 2013-12-05 2022-09-27 Ecosynthetix Ltd. Formaldehyde free binder and multi-component nanoparticle
US11666515B2 (en) 2018-03-28 2023-06-06 Greenmark Biomedical Inc. Phosphate crosslinked starch nanoparticle and dental treatments
WO2023244879A1 (fr) * 2022-06-15 2023-12-21 Westrock Mwv, Llc Structures cellulosiques revêtues

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3535396A1 (fr) 2016-11-01 2019-09-11 Novartis AG Procédés et compositions pour améliorer l'édition de gènes
CN111548608A (zh) * 2020-05-25 2020-08-18 常州龙骏天纯环保科技有限公司 一种可堆肥降解生物基薄膜及其制备方法

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1097466A (fr) 1976-03-25 1981-03-17 Henry R. Hernandez Traduction non-disponible
CA1079016A (fr) 1976-03-25 1980-06-10 Donald S. Greif Fibres d'amidon insensibles a l'eau et procede de fabrication de celles-ci
DE4143132A1 (de) 1991-12-28 1993-07-01 Univ Dresden Tech Verfahren zum loesen von staerke allein oder in kombination mit anderen natuerlichen und synthetischen polymeren
US5539021A (en) 1995-06-05 1996-07-23 The Dow Chemical Company Process for preparing high internal phase ratio emulsions and latexes derived thereof
NL1006444C2 (nl) 1997-07-01 1999-01-05 Inst Voor Agrotech Onderzoek Inkapseling van werkzame stoffen.
US5872199A (en) 1997-08-29 1999-02-16 Lions Adhesives, Inc. Sugar based vinyl monomers and copolymers useful in repulpable adhesives and other applications
NL1010926C2 (nl) 1998-12-30 2000-07-03 Inst Voor Agrotech Onderzoek Werkwijze voor de bereiding van zetmeeldeeltjes.
CA2361722C (fr) 1999-01-25 2009-04-21 Ato B.V. Nanoparticules de biopolymere
US6355734B1 (en) 1999-08-20 2002-03-12 Ecosynthetix Inc. Resin-fortified sugar-based vinyl emulsion copolymers and methods of preparing the same
AU7247000A (en) * 2000-01-11 2001-07-19 Givaudan Sa Composite materials
EP1148067A1 (fr) * 2000-04-18 2001-10-24 Coöperatieve Verkoop- en Productievereniging van Aardappelmeel en Derivaten 'AVEBE' B.A. Extrusion d'un amidon possedant une teneur elevee en amylopectine
EP1176254A1 (fr) 2000-07-24 2002-01-30 The Dow Chemical Company Utilisation de dispersions d'amidon reticulé dans la fabrication du papier
EP1176255A1 (fr) 2000-07-24 2002-01-30 The Dow Chemical Company Utilisation de dispersions d'amidon comme liant dans des compositions pour couchage et procédé pour la préparation des dispersions d'amidon
WO2002074814A1 (fr) 2001-03-16 2002-09-26 National Starch And Chemical Investment Holding Corporation Amidons pregelatinises modifies cuisables en masse a forte teneur en amylose pour l'encollage du papier
CN100378186C (zh) 2001-05-02 2008-04-02 生态合成材料股份有限公司 环境友好的生物高聚物粘合剂和基于其的应用
ATE329980T1 (de) 2001-05-02 2006-07-15 Ecosynthetix Inc Verfahren zur herstellung einer wellpappe und die hergestellte wellpappe
CN1618817A (zh) * 2003-11-19 2005-05-25 长春大成实业集团有限公司 一种凝胶剂及其制备方法和用途
EP1724300A1 (fr) 2004-03-10 2006-11-22 Agri Future Joetsu Co., Ltd. Composition de resine melange de lamidon, moulage de celle-ci et procede servant produre celui-ci
CA2597077A1 (fr) 2005-02-10 2006-08-17 Ecosynthetix Inc. Appareil et procede de production de carton ondule et contrecolle et compositions associees
US8318230B2 (en) 2005-05-02 2012-11-27 Henkel Ag & Co. Kgaa Use of debranched starch in extrusion-spheronization pharmaceutical pellets
US7276126B2 (en) * 2005-06-03 2007-10-02 Tate And Lyle Ingredients Americas, Inc. Production of enzyme-resistant starch by extrusion
ZA200901007B (en) * 2006-08-15 2010-05-26 Ecosynthetix Inc Process for producing biopolymer nanoparticles

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
None
See also references of EP2509445A4

Cited By (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013538238A (ja) * 2010-06-07 2013-10-10 ダウ グローバル テクノロジーズ エルエルシー デンプン粒子の安定分散体の調製方法
US10285943B2 (en) 2010-12-02 2019-05-14 Greenmark Biomedical Inc. Aptamer bioconjugate drug delivery device
US11369570B2 (en) 2010-12-02 2022-06-28 Greenmark Biomedical Inc. Aptamer bioconjugate drug delivery device
US9580846B2 (en) 2011-06-03 2017-02-28 Ecosynthetix Ltd. Curable sheared or extruded, cross linked starch nanoparticle latex binder for use with mineral, natural organic or synthetic fibre products and non-woven mats
US20140201872A1 (en) * 2011-08-30 2014-07-17 Dow Global Technologies Llc Coating composition comprising a cellulose ether and starch
US11352519B2 (en) 2011-09-19 2022-06-07 Novamont S.P.A. Stable aqueous dispersions comprising complexed starch
CN103814073B (zh) * 2011-09-19 2018-09-04 诺瓦蒙特股份公司 含络合淀粉的稳定水性分散体
US10160877B2 (en) 2011-09-19 2018-12-25 Novamont S.P.A. Stable aqueous dispersions comprising complexed starch
US9616696B2 (en) 2013-10-23 2017-04-11 Ecosynthetix Inc. Coating for paper adapted for inkjet printing
US11453798B2 (en) 2013-12-05 2022-09-27 Ecosynthetix Ltd. Formaldehyde free binder and multi-component nanoparticle
WO2017070578A1 (fr) 2015-10-21 2017-04-27 The Regents Of The University Of Michigan Détection et traitement de caries et de microcavités avec des nanoparticules
US10987434B2 (en) 2015-10-21 2021-04-27 The Regents Of The University Of Michigan Detection and treatment of caries and microcavities with nanoparticles
EP4088744A1 (fr) 2015-10-21 2022-11-16 The Regents Of The University Of Michigan Détection et traitement de caries et de microcavités avec des nanoparticules
US12023388B2 (en) 2015-10-21 2024-07-02 The Regents Of The University Of Michigan Detection and treatment of caries and microcavities with nanoparticles
US11666515B2 (en) 2018-03-28 2023-06-06 Greenmark Biomedical Inc. Phosphate crosslinked starch nanoparticle and dental treatments
US12508212B2 (en) 2018-03-28 2025-12-30 Greenmark Biomedical Inc. Phosphate crosslinked starch nanoparticle and dental treatments
JP2020026527A (ja) * 2018-08-10 2020-02-20 緑世界環保材料科技股▲ふん▼有限公司Ｇｒｅｅｎ Ｗｏｒｌｄ Ｂｉｏｔｅｃｈ Ｍａｔｅｒｉａｌｓ Ｃｏ．，Ｌｔｄ． 疎水性を有する熱可塑性デンプン複合材料とその製造方法
WO2023244879A1 (fr) * 2022-06-15 2023-12-21 Westrock Mwv, Llc Structures cellulosiques revêtues

Also Published As

Publication number Publication date
CN102651977A (zh) 2012-08-29
KR101819056B1 (ko) 2018-01-16
EP2509445A4 (fr) 2014-05-14
EP2509445A2 (fr) 2012-10-17
WO2011071742A3 (fr) 2011-10-13
KR20120123306A (ko) 2012-11-08
US9068062B2 (en) 2015-06-30
EP2509445B1 (fr) 2019-01-23
US20130000514A1 (en) 2013-01-03
CN102651977B (zh) 2014-08-20

Similar Documents

Publication Publication Date Title
EP2509445B1 (fr) Procédé de préparation de dispersions stables d'amidon
CN103068855B (zh) 制备淀粉颗粒的稳定分散体的方法
EP1303670B1 (fr) Utilisation de dispersions d'amidon comme liant dans des compositions d'enduction et procede de preparation de ces dispersions d'amidon
RU2531297C2 (ru) Способ получения композиций биополимерного наночастичного биолатекса, демонстрирующих улучшенные эксплуатационные характеристики, и композиции на их основе
US5236977A (en) Corrugating adhesive containing soluble high amylose starch
US20250277104A1 (en) Continuous processing of cellulose nanofibril sheets through conventional extrusion
CA2446773C (fr) Procede de production de carton ondule et produit obtenu a partir de ce carton
EA028114B1 (ru) Способ и средства для нанесения пленочного покрытия на бумагу
CN110945067A (zh) 树脂组合物及其制造方法
JPH10202181A (ja) 紙及び板の被覆方法及び被覆着色剤
AU2002303569A1 (en) Method for production of corrugated board and product obtained thereof
BE1023282B1 (nl) Coatingsamenstelling omvattende gehydrolyseerde tarwe-eiwitten
US10837142B2 (en) Paper coating composition with highly modified starches
TR201904642T4 (tr) Cf-kağit
SE536606C2 (sv) Förfarande för framställning av en bestrykningssmet innehållande en starkt koncentrerad stärkelselösning för bestrykningav papper och kartong

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201080056089.3

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10836442

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 13514380

Country of ref document: US

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2010836442

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 20127017748

Country of ref document: KR

Kind code of ref document: A