WO2010079330A1 - Formulation intercouches pour films plats - Google Patents

Formulation intercouches pour films plats Download PDF

Info

Publication number
WO2010079330A1
WO2010079330A1 PCT/GB2010/000019 GB2010000019W WO2010079330A1 WO 2010079330 A1 WO2010079330 A1 WO 2010079330A1 GB 2010000019 W GB2010000019 W GB 2010000019W WO 2010079330 A1 WO2010079330 A1 WO 2010079330A1
Authority
WO
WIPO (PCT)
Prior art keywords
solvent
composition
hole transport
layer
transport material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/GB2010/000019
Other languages
English (en)
Inventor
Simon Goddard
Paul Wallace
Emine Tekin
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cambridge Display Technology Ltd
Original Assignee
Cambridge Display Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cambridge Display Technology Ltd filed Critical Cambridge Display Technology Ltd
Publication of WO2010079330A1 publication Critical patent/WO2010079330A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne une composition adaptée à l'impression d'un dispositif opto-électrique comprenant un matériau de transport de trous semi-conducteur, un premier solvant et un second solvant, le premier solvant étant composé de 1-tetralone, de benzyl benzoate et de 1 méthoxynaphthalène o-xylène, de xylène mixte, d'éthylbenzène, de propylbenzène, de butylbenzène ayant un point d'ébullition supérieur et une viscosité supérieure à ceux du second solvant, le second solvant étant composé de mésitylène, d'o-xylène, de xylène mixte, d'éthylbenzène, de propylbenzène, de butylbenzène. Les solvants sont miscibles entre eux et la viscosité du premier solvant est comprise dans la plage de 5 à 12 mPas. Le premier solvant présente un point d'ébullition compris entre 250 et 350 °C, et le second solvant présente un point d'ébullition compris entre 100 et 200 °C. La figure représente les profils de film intercouches dérivés lorsqu'ils sont imprimés sur du PEDOT (PD239). L'ancienne formulation représente des zones d'épaississement des bords tandis que les deux nouvelles formulations présentent un léger amincissement des bords.
PCT/GB2010/000019 2009-01-12 2010-01-08 Formulation intercouches pour films plats Ceased WO2010079330A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB0900451A GB2466842B (en) 2009-01-12 2009-01-12 Interlayer formulation for flat films
GB0900451.6 2009-01-12

Publications (1)

Publication Number Publication Date
WO2010079330A1 true WO2010079330A1 (fr) 2010-07-15

Family

ID=40379462

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2010/000019 Ceased WO2010079330A1 (fr) 2009-01-12 2010-01-08 Formulation intercouches pour films plats

Country Status (3)

Country Link
GB (1) GB2466842B (fr)
TW (1) TW201033300A (fr)
WO (1) WO2010079330A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105658742A (zh) * 2013-10-31 2016-06-08 科迪华公司 用于喷墨印刷的包含聚噻吩的墨水组合物
WO2017001823A1 (fr) * 2015-06-30 2017-01-05 Cambridge Display Technology Limited Procédé de préparation de couche semiconductrice organique
US10093819B2 (en) 2011-09-16 2018-10-09 Kateeva, Inc. Fluorosurfactant-containing ink compositions for inkjet printing
CN111554832A (zh) * 2019-02-12 2020-08-18 三星显示有限公司 形成有机发光器件的组合物和制备有机发光器件的方法

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5844590B2 (ja) * 2011-09-27 2016-01-20 理想科学工業株式会社 非水系インクジェットインク
JP6015073B2 (ja) * 2012-04-02 2016-10-26 セイコーエプソン株式会社 機能層形成用インク、発光素子の製造方法
JP6225413B2 (ja) * 2012-11-16 2017-11-08 セイコーエプソン株式会社 機能層形成用インク、インク容器、吐出装置、機能層の形成方法、有機ｅｌ素子の製造方法
KR102436600B1 (ko) 2016-10-31 2022-08-25 메르크 파텐트 게엠베하 유기 기능성 재료의 제형
JP7046938B2 (ja) * 2016-10-31 2022-04-04 メルク パテント ゲーエムベーハー 有機機能材料の調合物
US11248138B2 (en) 2016-11-23 2022-02-15 Guangzhou Chinaray Optoelectronic Materials Ltd. Printing ink formulations, preparation methods and uses thereof
CN107177239B (zh) 2017-02-17 2019-03-08 纳晶科技股份有限公司 墨水配方、光电器件以及光电器件的功能层的制备方法

Citations (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5723873A (en) 1994-03-03 1998-03-03 Yang; Yang Bilayer composite electrodes for diodes
WO1998010621A1 (fr) 1996-09-04 1998-03-12 Cambridge Display Technology Limited Appareils organiques electroluminescents avec cathode amelioree
US5798170A (en) 1996-02-29 1998-08-25 Uniax Corporation Long operating life for polymer light-emitting diodes
EP0880303A1 (fr) 1996-11-25 1998-11-25 Seiko Epson Corporation Procede de production d'elements el organiques, elements el organiques et dispositif d'affichage el organique
WO1998057381A1 (fr) 1997-06-10 1998-12-17 Uniax Corporation Metaux alcalino-terreux en couche ultra-mince en tant que cathode stable d'injection d'electrons pour diodes electroluminescentes polymeres
EP0901176A2 (fr) 1997-08-29 1999-03-10 Cambridge Display Technology Limited Dispositif électroluminescent
WO1999048160A1 (fr) 1998-03-13 1999-09-23 Cambridge Display Technology Ltd. Dispositifs electroluminescents
EP0947123A1 (fr) 1996-07-29 1999-10-06 Cambridge Display Technology Limited Dispositifs electroluminescents avec protection d'electrode
EP0949850A1 (fr) 1998-04-02 1999-10-13 Cambridge Display Technology Limited Supports flexibles pour dispositif organique
EP0989778A1 (fr) 1998-03-17 2000-03-29 Seiko Epson Corporation Substrat de formation de motifs sur film mince et son traitement de surface
WO2000048258A1 (fr) 1999-02-12 2000-08-17 Cambridge Display Technology Ltd. Composants opto-electriques
WO2000053656A1 (fr) 1999-03-05 2000-09-14 Cambridge Display Technology Limited Preparation de polymere
GB2348316A (en) 1999-03-26 2000-09-27 Cambridge Display Tech Ltd Organic opto-electronic device
EP1083775A1 (fr) * 1999-03-29 2001-03-14 Seiko Epson Corporation Composition, procede de preparation d'un film, et element fonctionnel et son procede de preparation
WO2001019142A1 (fr) 1999-09-03 2001-03-15 Uniax Corporation Encapsulation de dispositifs electroniques organiques
US6268695B1 (en) 1998-12-16 2001-07-31 Battelle Memorial Institute Environmental barrier material for organic light emitting device and method of making
WO2001081649A1 (fr) 2000-04-20 2001-11-01 Battelle Memorial Institute Revetement barriere
WO2002066552A1 (fr) 2001-02-20 2002-08-29 Isis Innovation Limited Dendrimeres contenant du metal
WO2002069119A1 (fr) * 2001-02-27 2002-09-06 Cambridge Display Tech Ltd Preparation et technique de depot d'un materiau sur un substrat
WO2002084759A1 (fr) 2001-04-17 2002-10-24 Koninklijke Philips Electronics N.V. Del comprenant une couche polymere transparente conductrice ayant une teneur faible en ions sulfate et elevee en ions metalliques
WO2003083960A1 (fr) 2002-03-27 2003-10-09 Cambridge Display Technology Limited Procede de preparation de dispositifs optoelectroniques et electroniques organiques et dispositifs ainsi obtenus
US20050067949A1 (en) * 2003-09-30 2005-03-31 Sriram Natarajan Solvent mixtures for an organic electronic device
WO2005076386A1 (fr) 2004-02-05 2005-08-18 Cambridge Display Technology Limited Structures et procedes de fabrication de dispositifs electroniques moleculaires
DE102004007777A1 (de) * 2004-02-18 2005-09-08 Covion Organic Semiconductors Gmbh Lösungen organischer Halbleiter
WO2006123167A1 (fr) 2005-05-20 2006-11-23 Cambridge Display Technology Limited Solvants pour solutions de poly(3,4-ethylenedioxythiophene) ou 'pedot' pour impression par jets d'encre
EP1894976A1 (fr) * 2005-05-20 2008-03-05 Sumitomo Chemical Company, Limited Composition polymerique et dispositif polymerique electroluminescent l'utilisant

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7510672B2 (en) * 2004-05-18 2009-03-31 Merck Patent Gmbh Formulation for ink-jet printing comprising semiconducting polymers
JP4616596B2 (ja) * 2004-08-27 2011-01-19 株式会社 日立ディスプレイズ 電子装置の製造方法

Patent Citations (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5723873A (en) 1994-03-03 1998-03-03 Yang; Yang Bilayer composite electrodes for diodes
US5798170A (en) 1996-02-29 1998-08-25 Uniax Corporation Long operating life for polymer light-emitting diodes
EP0947123A1 (fr) 1996-07-29 1999-10-06 Cambridge Display Technology Limited Dispositifs electroluminescents avec protection d'electrode
WO1998010621A1 (fr) 1996-09-04 1998-03-12 Cambridge Display Technology Limited Appareils organiques electroluminescents avec cathode amelioree
EP0880303A1 (fr) 1996-11-25 1998-11-25 Seiko Epson Corporation Procede de production d'elements el organiques, elements el organiques et dispositif d'affichage el organique
WO1998057381A1 (fr) 1997-06-10 1998-12-17 Uniax Corporation Metaux alcalino-terreux en couche ultra-mince en tant que cathode stable d'injection d'electrons pour diodes electroluminescentes polymeres
EP0901176A2 (fr) 1997-08-29 1999-03-10 Cambridge Display Technology Limited Dispositif électroluminescent
WO1999048160A1 (fr) 1998-03-13 1999-09-23 Cambridge Display Technology Ltd. Dispositifs electroluminescents
EP0989778A1 (fr) 1998-03-17 2000-03-29 Seiko Epson Corporation Substrat de formation de motifs sur film mince et son traitement de surface
EP0949850A1 (fr) 1998-04-02 1999-10-13 Cambridge Display Technology Limited Supports flexibles pour dispositif organique
US6268695B1 (en) 1998-12-16 2001-07-31 Battelle Memorial Institute Environmental barrier material for organic light emitting device and method of making
WO2000048258A1 (fr) 1999-02-12 2000-08-17 Cambridge Display Technology Ltd. Composants opto-electriques
WO2000053656A1 (fr) 1999-03-05 2000-09-14 Cambridge Display Technology Limited Preparation de polymere
GB2348316A (en) 1999-03-26 2000-09-27 Cambridge Display Tech Ltd Organic opto-electronic device
EP1083775A1 (fr) * 1999-03-29 2001-03-14 Seiko Epson Corporation Composition, procede de preparation d'un film, et element fonctionnel et son procede de preparation
WO2001019142A1 (fr) 1999-09-03 2001-03-15 Uniax Corporation Encapsulation de dispositifs electroniques organiques
WO2001081649A1 (fr) 2000-04-20 2001-11-01 Battelle Memorial Institute Revetement barriere
WO2002066552A1 (fr) 2001-02-20 2002-08-29 Isis Innovation Limited Dendrimeres contenant du metal
WO2002069119A1 (fr) * 2001-02-27 2002-09-06 Cambridge Display Tech Ltd Preparation et technique de depot d'un materiau sur un substrat
WO2002084759A1 (fr) 2001-04-17 2002-10-24 Koninklijke Philips Electronics N.V. Del comprenant une couche polymere transparente conductrice ayant une teneur faible en ions sulfate et elevee en ions metalliques
WO2003083960A1 (fr) 2002-03-27 2003-10-09 Cambridge Display Technology Limited Procede de preparation de dispositifs optoelectroniques et electroniques organiques et dispositifs ainsi obtenus
US20050067949A1 (en) * 2003-09-30 2005-03-31 Sriram Natarajan Solvent mixtures for an organic electronic device
WO2005076386A1 (fr) 2004-02-05 2005-08-18 Cambridge Display Technology Limited Structures et procedes de fabrication de dispositifs electroniques moleculaires
DE102004007777A1 (de) * 2004-02-18 2005-09-08 Covion Organic Semiconductors Gmbh Lösungen organischer Halbleiter
WO2006123167A1 (fr) 2005-05-20 2006-11-23 Cambridge Display Technology Limited Solvants pour solutions de poly(3,4-ethylenedioxythiophene) ou 'pedot' pour impression par jets d'encre
EP1894976A1 (fr) * 2005-05-20 2008-03-05 Sumitomo Chemical Company, Limited Composition polymerique et dispositif polymerique electroluminescent l'utilisant

Non-Patent Citations (7)

* Cited by examiner, † Cited by third party
Title
"Dodecylbenzene", INTERNET CITATION, 1 June 1999 (1999-06-01), XP009131056, Retrieved from the Internet <URL:http://cameochemicals.noaa.gov/chris/DDB.pdf> *
ADV. MATER., vol. 12, no. 23, 2000, pages 1737 - 1750
APPL. PHYS. LETT. 2001, vol. 79, no. 5, 2001
APPL. PHYS. LETT., vol. 81, no. 4, 2002, pages 634
JOURNAL OF PHYSICS D: APPLIED PHYSICS, vol. 29, no. 11, 1996, pages 2750 - 2753
MICHAELSON, J. APPL. PHYS., vol. 48, no. 11, 1977, pages 4729
T. YAMAMOTO: "Electrically Conducting And Thermally Stable Tr - Conjugated Poly(arylene)s Prepared by Organometallic Processes", PROGRESS IN POLYMER SCIENCE, vol. 17, 1993, pages 1153 - 1205, XP024135546, DOI: doi:10.1016/0079-6700(92)90009-N

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10093819B2 (en) 2011-09-16 2018-10-09 Kateeva, Inc. Fluorosurfactant-containing ink compositions for inkjet printing
CN105658742A (zh) * 2013-10-31 2016-06-08 科迪华公司 用于喷墨印刷的包含聚噻吩的墨水组合物
WO2017001823A1 (fr) * 2015-06-30 2017-01-05 Cambridge Display Technology Limited Procédé de préparation de couche semiconductrice organique
CN111554832A (zh) * 2019-02-12 2020-08-18 三星显示有限公司 形成有机发光器件的组合物和制备有机发光器件的方法
KR20200099217A (ko) * 2019-02-12 2020-08-24 삼성디스플레이 주식회사 유기 발광 소자 형성용 조성물 및 유기 발광 소자의 제조 방법
CN111554832B (zh) * 2019-02-12 2024-12-03 三星显示有限公司 形成有机发光器件的组合物和制备有机发光器件的方法
KR102851580B1 (ko) 2019-02-12 2025-08-29 삼성디스플레이 주식회사 유기 발광 소자 형성용 조성물 및 유기 발광 소자의 제조 방법

Also Published As

Publication number Publication date
GB2466842A (en) 2010-07-14
GB2466842B (en) 2011-10-26
GB0900451D0 (en) 2009-02-11
TW201033300A (en) 2010-09-16

Similar Documents

Publication Publication Date Title
US8404159B2 (en) Solvent for a printing composition
WO2010079330A1 (fr) Formulation intercouches pour films plats
TWI442563B (zh) 製造光電裝置之方法
CN102124588B (zh) 用于制造发光器件的组合物和方法
CN1879236B (zh) 具有包含客体材料的区域的有机层状材料,以及结合了该材料的有机电子器件
EP2695212B1 (fr) Dispositif d&#39;émission de lumière organique et procédé associé
WO2010079331A1 (fr) Formulation intercouche pour films plats
JP5456781B2 (ja) ディスプレイを製造する方法
US20180127604A1 (en) Phosphorescent ink
CN101512791B (zh) 光电器件及其制造方法
WO2013178975A1 (fr) Dispositif électroluminescent organique à anode métallique et couche d&#39;injection de trous polymère
GB2460216A (en) Hole transport material composition
US20150167152A1 (en) Method of forming an organic light emitting device
HK1154309A (en) Solvent for a printing composition

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10701891

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10701891

Country of ref document: EP

Kind code of ref document: A1