WO2008152666A1 - Procédé de dépôt de couches de carbure de silicium hydrogéné - Google Patents

Procédé de dépôt de couches de carbure de silicium hydrogéné Download PDF

Info

Publication number
WO2008152666A1
WO2008152666A1 PCT/IT2007/000431 IT2007000431W WO2008152666A1 WO 2008152666 A1 WO2008152666 A1 WO 2008152666A1 IT 2007000431 W IT2007000431 W IT 2007000431W WO 2008152666 A1 WO2008152666 A1 WO 2008152666A1
Authority
WO
WIPO (PCT)
Prior art keywords
deposition
silicon carbide
layers
hydrogenated silicon
substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IT2007/000431
Other languages
English (en)
Inventor
Giovanni Taglioni
Luca Novella
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Selex Galileo SpA
Original Assignee
Galileo Avionica SpA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Galileo Avionica SpA filed Critical Galileo Avionica SpA
Priority to PCT/IT2007/000431 priority Critical patent/WO2008152666A1/fr
Publication of WO2008152666A1 publication Critical patent/WO2008152666A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention porte sur un procédé de dépôt de couches de carbure de silicium hydrogéné au moyen de la technique de PECVD. Ce procédé consiste à placer dans une chambre de dépôt (2) un mélange gazeux comprenant un gaz vecteur inerte et un composé organosilane ayant la formule (CH3)3-Si-X-Si-(CH3)3 dans laquelle X est choisi dans le groupe constitué par O et NH; à générer un plasma à partir du mélange; et à déposer une couche de SiC sur un substrat (5) situé dans la chambre de dépôt (2).
PCT/IT2007/000431 2007-06-14 2007-06-14 Procédé de dépôt de couches de carbure de silicium hydrogéné Ceased WO2008152666A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/IT2007/000431 WO2008152666A1 (fr) 2007-06-14 2007-06-14 Procédé de dépôt de couches de carbure de silicium hydrogéné

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IT2007/000431 WO2008152666A1 (fr) 2007-06-14 2007-06-14 Procédé de dépôt de couches de carbure de silicium hydrogéné

Publications (1)

Publication Number Publication Date
WO2008152666A1 true WO2008152666A1 (fr) 2008-12-18

Family

ID=39792990

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IT2007/000431 Ceased WO2008152666A1 (fr) 2007-06-14 2007-06-14 Procédé de dépôt de couches de carbure de silicium hydrogéné

Country Status (1)

Country Link
WO (1) WO2008152666A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ITRM20090675A1 (it) * 2009-12-21 2011-06-22 Galileo Avionica Spa Trattamento protettivo per componenti ottici atti a trasmettere nell'ir
WO2014074229A1 (fr) * 2012-11-09 2014-05-15 Dow Corning Corporation Procédé pour préparer un silane organofonctionnel

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1191123A2 (fr) * 2000-09-12 2002-03-27 Applied Materials, Inc. Déposition chimique en phase vapeur de couches de carbure de silicium plasma à fréquences duales
EP1420439A2 (fr) * 2002-11-14 2004-05-19 Air Products And Chemicals, Inc. Procédé non-thermique pour la fabrication des couches à faible constante diélectrique
US20040126929A1 (en) * 2002-12-30 2004-07-01 Novellus Systems, Inc. Silicon carbide having low dielectric constant

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1191123A2 (fr) * 2000-09-12 2002-03-27 Applied Materials, Inc. Déposition chimique en phase vapeur de couches de carbure de silicium plasma à fréquences duales
EP1420439A2 (fr) * 2002-11-14 2004-05-19 Air Products And Chemicals, Inc. Procédé non-thermique pour la fabrication des couches à faible constante diélectrique
US20040126929A1 (en) * 2002-12-30 2004-07-01 Novellus Systems, Inc. Silicon carbide having low dielectric constant

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
A. M. WRÓBEL ET AL: "Remote hydrogen plasma chemical vapor deposition of silicon-carbon thin-film materials from a hexamethyldisilane source: Characterization of the process and the deposits", JOURNAL OF APPLIED POLYMER SCIENCE, vol. 86, no. 6, 7 November 2002 (2002-11-07), Wilmington, DE, United States, pages 1445 - 1458, XP002499263 *
SEEKAMP J ET AL: "PECVD a-SiC:H thin films from liquid organosilanes dependence of photoluminescence on starting material", 1 May 2000, JOURNAL OF NON-CRYSTALLINE SOLIDS, NORTH-HOLLAND PHYSICS PUBLISHING. AMSTERDAM, NL, PAGE(S) 704 - 707, ISSN: 0022-3093, XP004198630 *

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ITRM20090675A1 (it) * 2009-12-21 2011-06-22 Galileo Avionica Spa Trattamento protettivo per componenti ottici atti a trasmettere nell'ir
WO2014074229A1 (fr) * 2012-11-09 2014-05-15 Dow Corning Corporation Procédé pour préparer un silane organofonctionnel

Similar Documents

Publication Publication Date Title
US5186973A (en) HFCVD method for producing thick, adherent and coherent polycrystalline diamonds films
US5124179A (en) Interrupted method for producing multilayered polycrystalline diamond films
EP0154483B1 (fr) Procédé amélioré utilisant un plasma pulsé
CN101092691B (zh) 消除pecvd膜的第一晶片效应
US5147687A (en) Hot filament CVD of thick, adherent and coherent polycrystalline diamond films
US4444467A (en) Coated laser mirror and method of coating
JP3945664B2 (ja) 撥水性酸化シリコン皮膜の製造方法
US6815052B2 (en) Filled diamond foam material and method for forming same
JPH1171681A (ja) 高速アークプラズマ成膜による保護皮膜
EP2412011B1 (fr) Procédé de dépôt chimique en phase vapeur
WO2003029517A1 (fr) Procede de controle de l'uniformite de films minces et produits resultants
US6605352B1 (en) Corrosion and erosion resistant thin film diamond coating and applications therefor
JP2007513257A (ja) 化学蒸着によって形成される自立型炭化ケイ素製品及びそれらを製造するための方法
JP2005093737A (ja) プラズマ成膜装置，プラズマ成膜方法，半導体装置の製造方法，液晶表示装置の製造方法及び有機ｅｌ素子の製造方法
JP5504924B2 (ja) 静電チャック装置
CN101595245B (zh) 用来稳定涂层的方法和设备
JP7679470B2 (ja) セラミック電極プレート付きプラズマ源
EP3276651A1 (fr) Procédé de fabrication d'un film mince annulaire de matériau synthétique et dispositif de mise en oeuvre de ce procédé
US7897521B2 (en) Low dielectric constant plasma polymerized thin film and manufacturing method thereof
EP0437830B1 (fr) Eléments d'anneau recouverts, en phase vapeur, de diamant et leur procédé de fabrication
WO2008152666A1 (fr) Procédé de dépôt de couches de carbure de silicium hydrogéné
US20130074773A1 (en) Heating systems for thin film formation
US20130074774A1 (en) Heating systems for thin film formation
KR100757694B1 (ko) 반도체 및 ｌｃｄ 제조장비의 세라믹 용사코팅을 이용한다중코팅 발열 장치
CN103540913B (zh) 应用于气相沉积的反应器

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07790163

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 07790163

Country of ref document: EP

Kind code of ref document: A1