[go: up one dir, main page]

WO2008075505A1 - 耐熱性接結２重織物とこれを用いた衣類及び耐熱手袋 - Google Patents

耐熱性接結２重織物とこれを用いた衣類及び耐熱手袋 Download PDF

Info

Publication number
WO2008075505A1
WO2008075505A1 PCT/JP2007/071366 JP2007071366W WO2008075505A1 WO 2008075505 A1 WO2008075505 A1 WO 2008075505A1 JP 2007071366 W JP2007071366 W JP 2007071366W WO 2008075505 A1 WO2008075505 A1 WO 2008075505A1
Authority
WO
WIPO (PCT)
Prior art keywords
heat
resistant
yarn
woven fabric
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2007/071366
Other languages
English (en)
French (fr)
Inventor
Kenji Kita
Hiromu Hayashi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hayashi Yarn Twisting Co Ltd
Original Assignee
Hayashi Yarn Twisting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hayashi Yarn Twisting Co Ltd filed Critical Hayashi Yarn Twisting Co Ltd
Priority to JP2008550063A priority Critical patent/JPWO2008075505A1/ja
Publication of WO2008075505A1 publication Critical patent/WO2008075505A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　本発明の耐熱性接結２重織物は、経糸と緯糸からなる上下２層の地組織層(10,20)と、上下２層の地組織層(10,20)間を接結糸(1a,1b)で連結し、上下２層の地組織層(10,20)のうち少なくとも１層は耐熱性繊維糸で構成し、接結糸(1a,1b)はループを含む意匠撚糸で構成する。本発明の衣類は、前記耐熱性接結２重織物を一部又は全部に含む衣類であって、前記耐熱性繊維糸で構成された地組織層を表面側に配置する。本発明の手袋は、前記耐熱性接結２重織物を把持面に一体化した手袋であって、前記耐熱性繊維糸で構成された地組織層を表面側に配置する。これにより、断熱性、耐熱性、防炎性、難燃性、防護性の高い耐熱性接結２重織物とこれを用いた衣類及び耐熱手袋を提供する。

Description

明 細 書
耐熱性接結 2重織物とこれを用いた衣類及び耐熱手袋
技術分野
[0001] 本発明は、断熱性、耐熱性、防炎性、難燃性の高!/、耐熱性接結 2重織物とこれを 用いた衣類及び耐熱手袋に関する。
背景技術
[0002] 経糸と緯糸からなる上下 2層の地組織層と、前記上下 2層の地組織層間を接結糸 で連結した接結 2重織物は、通常モケット布帛といわれる立毛織物の材料として知ら れている。すなわち、モケット織物機を用いて製織した後、接結糸をカッティングして 2枚のカットパイル織物とし、立毛を整えてカーシート、車両の座席シート、ソファシー ト等として使用されてレ、る（特許文献;!〜 3)。
[0003] 一方、アーク溶接などの溶接作業、溶鉱炉などの炉前作業、加熱調理などの高熱 物体を扱う作業には、安全の面から耐熱服や耐熱手袋が必要である。また、消防服 等も耐熱性を要求される。従来から、ァラミド繊維、ポリべンズイミダゾール繊維、ポリ ベンズォキサゾール繊維、ポリべンズァゾール繊維、ポリアミドイミド繊維、メラミン繊 維及びポリイミド繊維などの耐熱性繊維を用いて耐熱手袋や消防服を作成すること は提案されている（例えば非特許文献 1、特許文献 1)。非特許文献 1には、消防服 は防炎性と作業性のためメタ型ァラミド繊維を 95%、寸法安定性、収縮率防止のた めパラ型ァラミド繊維を 5%使用することが記載されている。また特許文献 4には、ァ ラミド繊維糸単体を用いて手袋を編成し、手のひら部分に合成樹脂を加熱融着する ことが記載されている。
特許文献 1：特開 2005— 154952号公報
特許文献 2：特開平 10— 130992号公報
特許文献 3：特開平 9 250052号公報
特許文献 4：実用新案登録第 3048633号
非特許文献 1：「繊維の百科事典」、丸善、平成 14年 3月 25日、 619頁
発明の開示 [0004] 耐熱手袋としては、従来動物の皮を用いた手袋が使用されているが、指が動かしに くぐ作業性に問題があり、かつ汗を吸水する機能もなぐ洗濯もできず、使用勝手の 悪い材料であった。また、従来の耐熱性繊維糸単体の布帛を用いた手袋は、断熱性 に問題があり、例えばアーク溶接でアークが前記手袋に降りかかったとき、肌が火傷 するという問題があった。布帛の厚さを大きくすればこの問題は解消される力 今度 は指が動かしに《作業性に問題が生じ、かつコストが高くなる問題がある。さらに、 耐熱性繊維を用いた消防服は、最外層にアルミ箔 (コーティングを含む）を形成し、そ の内部に前記耐熱性繊維単体の布帛を形成し、その内部に断熱のために不織布を 配置しており、全体として重量が重くなり、作業に支障が出たり、人体が故障する問 題があった。さらに近年は耐熱性及び防護性を備えた衣類も要請されている。
[0005] 本発明は、前記従来の問題を解決するため、断熱性、耐熱性、防炎性、難燃性、 防護性の高!/、耐熱性接結 2重織物とこれを用いた衣類及び耐熱手袋を提供する。
[0006] 本発明の耐熱性接結 2重織物は、経糸と緯糸からなる上下 2層の地組織層と、前記 上下 2層の地組織層間を接結糸で連結した接結 2重織物であって、前記上下 2層の 地組織層のうち少なくとも 1層は耐熱性繊維糸で構成し、前記接結糸はループを含 む意匠撚糸であることを特徴とする。
[0007] 本発明の衣類は、前記耐熱性接結 2重織物を一部又は全部に含む衣類であって、 前記耐熱性繊維糸で構成された地組織層を表面側に配置したことを特徴とする。
[0008] 本発明の手袋は、前記耐熱性接結 2重織物を把持面に一体化した手袋であって、 前記耐熱性繊維糸で構成された地組織層を表面側に配置したことを特徴とする。 図面の簡単な説明
[0009] [図 1]図 1Aは本発明で使用する一実施例の意匠撚糸の側面図、図 1Bは同断面図 である。
[図 2]図 2A— Bは本発明の一実施例で使用する接結 2重織物の断面組織図である。
[図 3]図 3A— Cは本発明の実施例 1〜4の接結 2重織物の断面組織図である。
[図 4]図 4は本発明の一実施例で得られた耐熱手袋の正面図である。
[図 5]図 5は同、裏面図である。
発明を実施するための最良の形態 [0010] 本発明は、耐熱性繊維と意匠撚糸と含む接結 2重織物とし、少なくとも一方の地組 織に耐熱性糸を配置し、接結糸として意匠撚糸を使用して多くの空気を含ませること により、断熱性、耐熱性、防炎性、難燃性、防護性の高い耐熱性布帛とこれを用いた 衣類及び耐熱手袋とすることができる。すなわち、意匠撚糸には多数のループが存 在するため、これを接結糸に用いた接結 2重織物は、地組織間に多くの空気を含ま せること力 Sできる。空気は断熱性が高!/、ため前記接結 2重織物も断熱性が高!/、ものと なる。さらに、一方の面には前記耐熱性繊維が多く存在しているため、この部分で耐 熱性、防炎性、難燃性、防護性を発揮する。加えて本発明の耐熱性接結 2重織物と これを用いた衣類及び耐熱性手袋は、通気性があり、作業性も良好で、洗濯すること もできる。
[0011] 本発明の接結 2重織物とは、接結糸をカットしない 2重織物構造の織物をいう。
[0012] 従来のモケット布帛は、接結糸の面がカットパイルとなりシートの表面に配置され、 地組織の反対面はシートの裏面となる。これに対して本発明の接結 2重織物は、接 結糸をカットすることなく断熱層とし、耐熱性糸を経糸と緯糸に配置した地組織の接 結糸のない側、すなわち従来のモケット布帛でいうシートの裏面側を表面側（大気側 )に配置して使用する。
[0013] 本発明において耐熱性繊維は、融点又は分解点が約 350°C以上、好ましくは 400 °C以上であれば、無機繊維又は有機繊維のいかなるものであってもよい。好ましくは ァラミド繊維 (パラ系ァラミドの融点又は分解点： 480〜570°C、メタ系同： 400〜430 °C)、ポリべンズイミダゾール繊維（ガラス転移温度： 400°C以上）、ポリ（p—フエユレ ンベンゾビスォキザール） (PBO)等のポリべンズォキサゾール繊維（融点又は分解 温度： 650°C)、ポリ（p—フエ二レンべンゾビスチアゾール）（PBZT)等のポリべンズチ ァゾール繊維（融点又は分解温度： 650°C)、ポリアミドイミド繊維（融点又は分解温 度： 350°C以上）、メラミン繊維（融点又は分解温度： 400°C以上）、ポリイミド繊維（融 点又は分解温度： 350°C以上）、ポリアリレート繊維（融点又は分解温度： 400°C以上 )及び炭素繊維（融点又は分解温度： 2000〜3500°C)から選ばれる少なくとも一つ である。これらの繊維は編物又は織物に加工しやすい。繊度は綿番手で 1〜50番程 度が好ましい。単糸で使用することもできるし、複数本引き揃えるか、あるいは合撚し て使用できる。
[0014] 前記意匠撚糸は、一例として芯糸とループヤーンと押さえ糸で構成される。さらに 好ましくは、前記意匠撚糸は、芯糸とループヤーンの上から押さえ糸を、撚り数 200 〜600回/ mで実撚した構造である。
[0015] 前記ループヤーンは、木綿、レーヨン、麻、羊毛、アクリル繊維及び前記耐熱性繊 維から選ばれる少なくとも一つであることが好ましい。芯糸と押さえ糸は、ァラミド、ポリ ベンズイミダゾーノレ、ポリベンズォキサゾーノレ、ポリべンズチアゾーノレ、ポリアミドイミド 、メラミン、ポリイミド、ポリアリレート、ポリエステル、ナイロン及びポリオレフインから選 ばれる少なくとも一つの繊維糸であることが好ましい。さらに好ましい芯糸と押さえ糸 は、ポリエステルフィラメント糸又は前記耐熱性繊維である。
[0016] 芯糸に対してループヤーンは 1. 0；!〜 10倍の範囲、好ましくは 1. 2〜6倍オーバ 一フィードして作成すると、芯糸の周囲にあらゆる方向にランダムにループが形成で きる。芯糸に対してループヤーンをオーバーフィードさせると、オーバーフィードした 分、芯糸に対して相対的にループヤーンの方が長くなり、ループを形成するようにな
[0017] 意匠撚糸の繊度は 1 18〜； 11811dtex (綿番手： 0. 5〜50番）程度が好ましい。単 糸で使用することもできるし、複数本引き揃えるか、あるいは合撚して使用できる。前 記意匠撚糸のループヤーンには低融点熱接着繊維を含んでもよ!/、。低融点熱接着 繊維を含むと意匠撚糸の一体性が良くなりほつれ防止が高ぐさらに腰も高くなる。
[0018] 本発明の耐熱性接結 2重織物の厚さは 0. 5mm以上 5mm以下が好ましぐさらに は lmm以上 3mm以下が好ましい。前記織物の厚さは、接結糸の接結長さを調整す るによって目的とする厚さに制御できる。
[0019] 前記耐熱性接結 2重織物の単位面積あたりの重量（目付け）は、 100〜3000g/m
2の範囲カ好ましく、さらに 300〜2000g/cm2の範囲、とくに 400〜； 1500g/cm2の 範囲が好ましい。厚さ及び単位面積あたりの重量が前記の範囲であると、熱遮断性 に加えて耐燃焼性も向上する。
[0020] 本発明の耐熱性接結 2重織物は、耐熱性繊維糸で構成された地組織層と、多数の ループが存在する意匠撚糸で構成した接結糸により、断熱性及び耐熱性が相乗的 に高くなる。また、外側に配置される耐熱繊維糸により防護性も良好となる。用途とし ては、例えば飛行機乗務員、消防隊員、警察官、 自衛隊員等の制服、ジャンパー、 コート、ベスト等の外衣類、腕力バー、前掛け、防護頭巾、消防服、防護服、作業服、 防火布、飛行機、自動車、電車等の内装材に有用である。また、アーク溶接などの溶 接作業、溶鉱炉などの炉前作業、加熱調理、消火作業、エンジン補修などの高熱物 体を扱う作業に使用する耐熱手袋としても有用である。
[0021] 以下図面を用いて説明する。図 1Aは本発明で使用する一実施例の意匠撚糸 1の 側面図、図 1Bは同断面図である。この意匠撚糸 1は、芯糸 2とループヤーン 3とその 上からの押さえ糸 4で構成され、ループヤーン 3は木綿又はウール等の天然繊維の 例である。ループヤーン 3には低融点繊維を含ませてもよい。低融点繊維は合糸、混 繊、混紡等により天然繊維に含ませる。天然繊維に対する低融点繊維の混合率は 1 0〜30重量％の範囲が好ましい。
[0022] 図 2A— Bは本発明の一実施例で使用する耐熱性接結 2重織物の組織図である。
図 2Aに示すように、上の地組織 10は耐熱性繊維糸からなる経糸 11 , 12と緯糸 13 で形成される。下の地組織 20は耐熱性繊維糸からなる経糸 21 , 22と緯糸 23で形成 される。上下の地組織は、平織、斜文織、朱子織、又はこれらの変化織、サテン等の 変り織、紋織等の織物組織を採用できる。
[0023] 上下の地組織 10, 20の間を、図 2Bに示すように意匠撚糸 la, lbからなる接結糸 3 0で連結させる。接結糸 30はドビー、ジャカード等により上下の地組織の緯糸 13, 23 に絡めるか又は揷入する。このようにして耐熱性接結 2重織物を形成する。意匠撚糸 には多数のループが存在するため、これを接結糸に用いた接結 2重織物は、地組織 間に多くの空気を含ませることができ、断熱効果を発揮できる。また、意匠撚糸には 多数のループが存在するため、嵩高になっており、上下の地組織を手で押さえたとき に斜め方向につぶれることはなぐ通常の厚手織物の感触が得られる。
[0024] 前記においては、上下の地組織 10, 20を耐熱性繊維糸で形成したが、どちらか一 方の地組織のみを耐熱性糸で形成しても良!/、。一方の地組織のみを耐熱性糸で形 成する場合は、他方の地組織を意匠撚糸で形成しても良いし、通常の織物に使用さ れる天然繊維、合成繊維、これらの混紡品の紡績糸、フィラメント糸、又は紡績糸とフ イラメント糸の撚糸で形成しても良レ、。
[0025] 耐熱性繊維糸 11 , 12, 13は表面に配置され、意匠撚糸 la, lbは織物内部に配 置される。意匠撚糸 la, lbには多数のループ 3 (図 1A,図 1B)が突出しており、空 隙を多く含み、断熱作用を発揮する。表面には耐熱性繊維糸 11 , 12, 13が存在す るので、耐熱性、防炎性、難燃性を発揮する。耐熱性繊維糸 11 , 12, 13側表面にも 多少のループ 3は突出する力 S、耐熱性にはあまり影響しない。むしろ炎を受けたり、 高温の物体を触ったとき、耐熱性繊維糸 11 , 12, 13側表面のループ 3は焦げるので 、作業者は危険を感ずることができる。
実施例
[0026] 以下実施例を用いて、さらに本発明を具体的に説明する。本発明は下記の実施例 に限定されるものではない。
[0027] (実施例 1)
(1)意匠撚糸の製造
芯糸及び押さえ糸としてポリエステルマルチフィラメント、ウーリー加工糸（東レ社製 )、トータル繊度 167dtex (150デニール）、フィラメント数 96本を 1本使用した。
[0028] ループヤーンとして木綿糸 196. 9dtex (綿番手： 30番）単糸を 4本と、低融点熱接 着繊維糸（低融点ナイロン、融点1 10〜113° 東レ社製商品名"エルダー"） l lOd texを 2本使用した。
[0029] 芯糸に対してループヤーンをオーバーフィード率 1. 5〜2. 0倍で供給して絡みつ け、絡みつけと同時にその上から押さえ糸を撚り数を 200〜600回/ mで実撚を掛 けた。得られた意匠撚糸は、図 1A—Bに示すとおりであり、ループの平均突出長さ 3 mm、 1インチあたり平均 20〜30個のループが 360° の角度であらゆる角度に突出 していた。この意匠撚糸の繊度は 1007. 6dtexであった。
[0030] (2)耐熱性繊維糸の準備
市販の帝人社製商品名 "コーネックス"（メタ系ァラミド繊維）の紡績糸、繊度： 295 · 3dtex (綿番手： 20番）を双糸で使用した。
[0031] (3)接結 2重織物の製織
モケット織物機を使用し、前記耐熱性繊維糸を経糸密度（上下組織)各 40本 /2. 54cm,緯糸密度（上下組織)各 30本 /2. 54cmで打ち込み、上下の地組織を図 2 Aに示すように平組織に製織した。得られた織物を 110°Cで、 40分間ヒートセットした
〇
[0032] 上下の地組織間を連結する接結糸として前記意匠撚糸を使用し、図 3Aに示す接 結糸 la, lbのように配置した。得られた接結 2重織物 31の厚さは約 3mm、 目付けは lkg/m2であった。この織物は、人力によるカッターナイフでは切断できず、突き破る こともできな力 たことから、防護性もあることが確認できた。
[0033] (4)手袋の編成と耐熱性試験
前記で得られた接結 2重織物の耐熱性を評価するために、丸編み機を使用して二 ットを編成し、得られたニットを手袋に縫製した。ニットは前記耐熱性繊維糸を 60重量 %、前記意匠撚糸を 40重量％の割合で使用して編成した。編み物構造は両面編み 物とし、耐熱性繊維糸は表面側に配置し、意匠撚糸は裏面側に配置し、ループは裏 面側に主として存在している力 S、一部は表面側にも露出していた。図 4〜5に示すよう に、この手袋 40の掌部（把持部） 41と各指の先端部 42〜46に前記接結 2重織物を 縫製により一体化した。
[0034] 得られた手袋の掌部にニッケルバーナーの約 800°Cの炎を 2分間当てても燃焼せ ず、表面はうつすらと焦げるが内部に熱は感じな力、つた。また、 400°Cの加熱物体を つかむ作業をしても熱さは感じられず、焦げも発生しな力 た。このことから難燃性と 耐熱性を確認できた。
[0035] また、アーク溶接作業に使用したところ、熱さは感じず、溶接の火花 (約 1200°C)が 力、かっても熱くなぐ薄くて作業動作を損なうことがなぐ通気性もあり、作業性はきわ めて良かった。作業後の洗濯もすることができ、繰り返し使用ができた。
[0036] また、燃焼炉でピザパイを焼く加熱調理作業に使用したところ、同様に断熱性が高 ぐ耐熱性、防炎性、難燃性、通気性があり、作業性も良好で、洗濯もできること力、ら、 衛生†生も良好であった。
[0037] 前記接結 2重織物と他の物質との熱伝導率を測定すると表 1のとおりとなった。熱伝 導率は大阪府立産業技術総合研究所の KES— F7 (サーモラボ)装置で測定した。
[0038] [表 1] 物質 熱伝導率 (w/mK)
木綿 0 . 2 4 3
水 0 . 5 8 2
鉄 8 3 . 5
銅 4 0 3 . 0
空気 0 . 0 2 1
実施例 1の接結 2重織物 0 . 0 8 0 表 1から明らかなとおり、本発明の実施例 1の接結 2重織物は熱伝導率が低かった
〇
[0039] 次に本発明の実施例 1の接結 2重織物を用いて切創強さを測定した。切創強さは、 JIS— 1096破裂強さ B法に規定されている「定速伸長計法試験」に準じ、押し棒先端 にナイフ (OLFA SDS-7)を取り付け、ナイフ速度 2cm/minでナイフがサンプルを突き切 る時の強さを測定した。比較例として切創性が良!/、と!/、われて!/、る市販の耐熱用皮 手袋を測定した。結果を表 2に示す。
[0040] [表 2]
Figure imgf000010_0001
表 2に示すように本発明の実施例 1で得られた接結 2重織物の切創強さは、市販の 耐熱用皮手袋よりはるかに高かった。
[0041] (実施例 2)
意匠撚糸のループヤーンとして、木綿糸 196. 9dtex (綿番手： 30番）単糸を 2本と し、低融点熱接着繊維糸（低融点ナイロン、融点110〜113° 東レ社製商品名"ェ ルダ一"） l lOdtexを 1本とした以外は、実施例 1と同様に製織した。得られた接結 2 重織物の厚さは約 2mm、 目付けは 600g/m2であった。風合いは、実施例 1の織物 に比べて柔軟であった。この織物も実施例 1と同様の防護性が認められた。
[0042] この接結 2重織物を実施例 1と同様に手袋の掌部と指部に縫製により一体化して耐 熱性を調べたところ、実施例 1と同様に断熱性、耐熱性、防炎性、難燃性、通気性、 作業性も良好で、洗濯もでき、衛生性も良好であった。
[0043] (実施例 3)
実施例 2と同じ意匠撚糸を使用し、織物構造を図 3Bに示すように接結糸 la, lbを 上下地組織の緯糸に一本置きに配置した以外は、実施例 1と同様に製織した。得ら れた接結 2重織物 32の厚さは約 1. 5mm、 目付けは 550g/m2であった。風合いは 、実施例 1の織物に比べて柔軟であった。この織物も実施例 1と同様の防護性が認 められた。
[0044] この接結 2重織物を実施例 1と同様に手袋の掌部と指部に縫製により一体化して耐 熱性を調べたところ、実施例 1と同様に断熱性、耐熱性、防炎性、難燃性、通気性、 作業性も良好で、洗濯もでき、衛生性も良好であった。
[0045] (実施例 4)
実施例 2と同じ意匠撚糸を使用し、織物構造を図 3Cに示すように接結糸 la, lbを 上下地組織の緯糸に Wとなるように配置した以外は、実施例 2と同様に製織した。得 られた接結 2重織物 33の厚さは約 1. 5mm、 目付けは 500g/m2であった。風合い は、実施例 3の織物に比べてさらに柔軟であった。この織物も実施例 1と同様の防護 性が認められた。
[0046] この接結 2重織物を実施例 1と同様に手袋の掌部と指部に縫製により一体化して耐 熱性を調べたところ、実施例 1と同様に断熱性、耐熱性、防炎性、難燃性、通気性、 作業性も良好で、洗濯もでき、衛生性も良好であった。
[0047] さらに、得られた接結 2重織物 33を使用して紳士用ジャケットに縫製した。このジャ ケットは厚手のウール服と同様の重量感と厚み感があり、着心地は良ぐ耐熱性と防 護性が要求される飛行機乗務員、消防隊員、警察官、自衛隊員等の制服に好適で あることがわかった。
[0048] (比較例 1)
実施例 1の手袋生地を使用し、実施例 1同じ掌部と指部の位置に厚さ 2mmの牛皮 革を縫製により一体した。そして耐熱性を調べたところ、 400°Cの加熱物体で焦げて 発煙し、耐熱性は低かった。また、蒸れもあり、着用感も悪ぐ洗濯ができないことから 衛生性にも問題があった。さらに実施例 1と同じカッターで簡単に切れてしまい、防護 性は認められなかった。
産業上の利用可能性
本発明の耐熱性接結 2重織物の用途としては、例えば飛行機乗務員、消防隊員、 警察官、 自衛隊員等の制服、ジャンパー、コート、ベスト等の外衣類、腕力バー、前 掛け、防護頭巾、消防服、防護服、作業服、防火布、飛行機、 自動車、電車等の内 装材に有用である。また、アーク溶接などの溶接作業、溶鉱炉などの炉前作業、カロ 熱調理、消火作業、エンジン補修などの高熱物体を扱う作業に使用する耐熱手袋と しても有用である。

Claims

請求の範囲
[1] 経糸と緯糸からなる上下 2層の地組織層と、前記上下 2層の地組織層間を接結糸 で連結した接結 2重織物であって、
前記上下 2層の地組織層のうち少なくとも 1層は耐熱性繊維糸で構成し、 前記接結糸はループを含む意匠撚糸であることを特徴とする耐熱性接結 2重織物
〇
[2] 前記地組織を構成する耐熱性繊維糸は、ァラミド繊維、ポリべンズイミダゾール繊 維、ポリべンズォキサゾール繊維、ポリべンズチアゾール繊維、ポリアミドイミド繊維、 メラミン繊維、ポリイミド繊維及びポリアリレート繊維から選ばれる少なくとも一つの糸 である請求項 1に記載の耐熱性接結 2重織物。
[3] 前記意匠撚糸は、芯糸とループヤーンと押さえ糸で構成される請求項 1に記載の 耐熱性接結 2重織物。
[4] 前記意匠撚糸は、芯糸とループヤーンの上から押さえ糸を、撚り数 200〜600回/ mで実撚した構造である請求項 1又は 3に記載の耐熱性接結 2重織物。
[5] 前記ループヤーンは、木綿、レーヨン、麻、羊毛、アクリル、ァラミド、ポリべンズイミ ダゾール、ポリべンズォキサゾール、ポリべンズチアゾール、ポリアミドイミド、メラミン、 ポリイミド及びポリアリレートから選ばれる少なくとも一つの繊維糸である請求項 3又は
4に記載の耐熱性接結 2重織物。
[6] 前記ループヤーンは、芯糸に対して 1. 01〜； 10倍の範囲長い請求項 3〜5のいず れかに記載の耐熱性接結 2重織物。
[7] 前記芯糸と押さえ糸は、ァラミド、ポリべンズイミダゾール、ポリべンズォキサゾール、 ポリべンズチアゾール、ポリアミドイミド、メラミン、ポリイミド、ポリアリレート、ポリエステ ノレ、ナイロン及びポリオレフインから選ばれる少なくとも一つの繊維糸である請求項 3 又は 4に記載の耐熱性接結 2重織物。
[8] 前記意匠撚糸のループヤーンには低融点熱接着繊維を含む請求項 1、 3又は 4に 記載の耐熱性接結 2重織物。
[9] 前記意匠撚糸の繊度は、 118〜； 11811dtex (綿番手： 0· 5〜50番）の範囲である 請求項 1〜8のいずれかに記載の耐熱性接結 2重織物。
[10] 前記耐熱性接結 2重織物の目付けは、 100〜3000g/m2の範囲である請求項 1
〜9のいずれかに記載の耐熱性接結 2重織物。
[11] 前記耐熱性接結 2重織物の厚さは 0. 5〜5mmの範囲である請求項;!〜 10のいず れかに記載の耐熱性接結 2重織物。
[12] 請求項 1〜； 11のいずれかに記載の耐熱性接結 2重織物を一部又は全部に含む衣 類であって、前記耐熱性繊維糸で構成された地組織層を表面側に配置したことを特 徴とする衣類。
[13] 請求項 1〜； 11のいずれかに記載の耐熱性接結 2重織物を把持面に一体化した手 袋であって、前記耐熱性繊維糸で構成された地組織層を表面側に配置したことを特 徴とする耐熱性手袋。
PCT/JP2007/071366 2006-12-18 2007-11-02 耐熱性接結２重織物とこれを用いた衣類及び耐熱手袋 Ceased WO2008075505A1 (ja)