WO2006124995B1 - Ballistic laminate structure - Google Patents

Ballistic laminate structure

Info

Publication number
WO2006124995B1
WO2006124995B1 PCT/US2006/019075 US2006019075W WO2006124995B1 WO 2006124995 B1 WO2006124995 B1 WO 2006124995B1 US 2006019075 W US2006019075 W US 2006019075W WO 2006124995 B1 WO2006124995 B1 WO 2006124995B1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
adhesive
laminate sheet
fiber bundles
oriented
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2006/019075
Other languages
French (fr)
Other versions
WO2006124995A2 (en
WO2006124995A3 (en
Inventor
Lawrence J Dickson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Composix Co
Original Assignee
Composix Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Composix Co filed Critical Composix Co
Priority to EP06760019A priority Critical patent/EP1885553A2/en
Publication of WO2006124995A2 publication Critical patent/WO2006124995A2/en
Publication of WO2006124995A3 publication Critical patent/WO2006124995A3/en
Anticipated expiration legal-status Critical
Publication of WO2006124995B1 publication Critical patent/WO2006124995B1/en
Ceased legal-status Critical Current

Abstract

A ballistic structure having at least one laminate sheet of a plurality of fiber bundles is disclosed. The laminate sheet has adhesive resin on at least one surface thereof, without substantial penetration of the adhesive resin into the fiber bundles. In embodiments having more than one laminate sheet, the inter-laminate shear strength between the laminate sheets is controlled to control ballistic effectiveness of the ballistic structure.

Claims

AMENDED CLAIMS received by the International Bureau on 02 July 2007, (02.07.2007)
I claim:
1. A laminate sheet for use in a ballistic structure, comprising at least one layer of unidirectionally-oriented fiber bundles and a discontinuous array of adhesive applied to at least one surface of the sheet without substantial penetration of the adhesive into the fiber bundles, wherein the adhesive comprises an elastomeric material having a tensile modulus between about 7,000 psi and about 80,000 psi, and wherein the discontinuous array of adhesive binds the fiber bundles together.
2. The laminate sheet of claim 1, wherein the adhesive comprises no more than about 20 percent by weight of the laminate sheet.
3. (cancelled).
4. (cancelled).
5. The laminate sheet of claim 1, wherein the adhesive is a non- woven array of thermoplastic material.
6. The laminate sheet of claim 1, further comprising at least a first and a second layer of unidirectionally-oriented fiber bundles, wherein the second layer is oriented at an angle between 0 and 180 degrees relative to the first layer.
7. The laminate sheet of claim 1, further comprising a plurality of unidirectionally-oriented fiber bundles, wherein at least one of the layers is oriented at an angle between 0 and 180 degrees relative to at least one other layer.
8. The laminate sheet of claim 1, wherein the unidirectionally-oriented fiber bundles comprise fibers selected from the group consisting of nylon, polypropylene, polyethylene, aramid, and liquid crystalline polymer.
9. The laminate sheet of claim 6, further comprising at least one release layer disposed between the first and second layer, the release layer comprising plastic film, metal foil, or paper.
10. A laminate sheet for use in a ballistic structure, comprising:
a. at least a first layer of fiber bundles having a first adhesive associated therewith, wherein the first adhesive comprises an elastomeric material having a tensile modulus between about 7,000 psi and about 80,000 psi;
b. at least a second layer of fiber bundles laminated to the first layer and oriented at an angle between 0 and 180 degrees relative to the first layer; and
c. means for reducing the inter-laminar shear strength between the first layer and the second layer.
11. The laminate sheet of claim 10, wherein the first adhesive is applied to one or more surfaces of the first layer and does not substantially penetrate into the fiber bundles of the first layer.
12. The laminate sheet of claim 10, wherein the means for reducing inter-laminar shear strength comprises a release layer disposed between the second layer and the first layer.
13. The laminate sheet of claim 12, wherein the release layer comprises polyester film, polypropylene film, polyethylene film, urethane film, aluminum foil, steel foil, titanium foil, brass foil, copper foil, or paper.
14. The laminate sheet of claim 12, wherein the first adhesive is disposed between the release layer and the first layer.
15. The laminate sheet of claim 10, further comprising a second adhesive applied to one or more surfaces of the second layer and that does not substantially penetrate into the fiber bundles of the second layer.
16. The laminate sheet of claim 15, wherein the second adhesive is disposed between the release layer and the second layer.
17. The laminate sheet of claim 15, wherein the means for reducing the inter- laminar shear strength between the first layer and the second layer comprises selecting the first adhesive and the second adhesive such that there is relatively low bonding affinity therebetween, and such that localized de-bonding between the first layer and the second layer occurs at a point of ballistic impact.
18. The laminate sheet of claim 10, wherein the first layer and the second layer are oriented at non-zero angle relative to each other.
19. The laminate sheet of claim 10, further comprising more than two layers of fiber bundles and means for reducing the inter-laminar shear strength between selected layers.
20. The laminate sheet of claim 10, wherein the means for reducing inter-laminar shear strength comprises a release layer disposed between the second layer and the first layer; and wherein the first adhesive is disposed between the release layer and the first layer; and wherein the release layer has relatively low bonding affinity for the first adhesive, such that localized debonding between the first layer and the second layer occurs at the point of ballistic impact.
21. The laminate sheet of claim 20, further comprising a second adhesive between the release layer and the second layer.
22. The laminate sheet of claim 21, wherein the first adhesive and the second adhesive are substantially the same material.
23. The laminate sheet of claim 21, wherein the first adhesive and the second adhesive are different materials.
24. The laminate sheet of claim 20, further comprising additional layers of unidirectionally-oriented fiber bundles oriented at angles between 0 and 180 degrees relative to other layers, each additional layer comprising at least one adhesive layer, at least one release layer, or both.
25. A ballistic structure comprising the laminate sheet of claim 20.
26. A laminate sheet for use in a ballistic structure comprising:
a. a plurality of complex laminates laminated together; each complex laminate oriented at an angle between 0 and 180 degrees relative to at least one other complex laminate, each complex laminate comprising:
i. a plurality of laminated layers laminated together, each laminated layer comprising;
1. unidirectionally-oriented fiber bundles, and
2. a discontinuous array of adhesive applied to at least one surface of the laminated layer, the adhesive comprising an elastomeric material having a tensile modulus between about 7,000 psi and about 80,000 psi, and
ii. each laminated layer oriented at an angle between 0 and 180 degrees relative to at least one other laminated layer;
b. means for reducing the inter-laminar shear strength between selected laminated layers; and
c. means for reducing the inter-laminar shear strength between selected complex laminates.
27. The laminate sheet of claim 26, wherein the means for reducing inter-laminar shear strength between selected complex laminates comprises a release layer disposed between selected complex laminates.
28. (cancelled).
29. The laminate sheet of claim 26, wherein the discontinuous array of adhesive further comprises a non- woven array of thermoplastic material.
30. The laminate sheet of claim 27, wherein the release layer comprises a polyethylene film having a thickness less than about 2 mil, and wherein the adhesive layer is selected to have relatively low bonding affinity for the polyethylene film such that localized de-bonding between selected complex laminates occurs at a point of ballistic impact.
31. The laminate sheet of claim 26, wherein the unidirectionally-oriented fiber bundles comprise fibers selected from the group consisting of nylon, polypropylene, polyethylene, aramid, and liquid crystalline polymer.
32. A ballistic structure comprising at least one laminate sheet, the laminate sheet comprising:
a. a first layer of fiber bundles having a first adhesive on a surface thereof, wherein the first adhesive comprises an elastomeric material having a tensile modulus between about 7,000 psi and about 80,000 psi;
b. a second layer of fiber bundles laminated to the first layer; and
c. means for reducing the inter-laminar shear strength between the first layer and the second layer.
33. The ballistic structure of claim 32, further comprising at least one rigid impact resistant layer.
34. The ballistic structure of claim 33, wherein the rigid impact resistant layer comprises ceramic, metallic, perforated metallic, or composite material.
35. The ballistic structure of claim 33, wherein the rigid impact resistant layer is bonded to at least one laminate sheet.
36. The ballistic structure of claim 32, wherein the fiber bundles comprise fibers selected from the group consisting of nylon, polypropylene, polyethylene, aramid, and liquid crystalline polymer.
37. The ballistic structure of claim 32, wherein the adhesive comprises a non- woven array of thermoplastic material.
38. The laminate sheet of either of claim 15 or 21, wherein the second adhesive comprises an elastomeric material having a tensile modulus between about 7,000 psi and about 80,000 psi.
39. The laminate sheet of any of claims 21-24, wherein the release layer has relatively low bonding affinity for the first adhesive, the second adhesive, or both such that localized de-bonding between the first layer and the second layer occurs at a point of ballistic impact.
40. The laminate sheet of any of claims 20-24, wherein the release layer is selected to have sufficiently poor adhesion with the first adhesive, the second adhesive, or both, such that the inter-laminar shear strength between the first layer and the second layer is reduced by at least 15% compared to the inter-laminar shear strength between the first layer and the second layer in the absence of the release layer.
PCT/US2006/019075 2005-05-18 2006-05-17 Ballistic laminate structure Ceased WO2006124995A2 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP06760019A EP1885553A2 (en) 2005-05-18 2006-05-17 Ballistic laminate structure

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US13199205A 2005-05-18 2005-05-18
US11/131,992 2005-05-18

Publications (3)

Publication Number Publication Date
WO2006124995A2 WO2006124995A2 (en) 2006-11-23
WO2006124995A3 WO2006124995A3 (en) 2007-07-12
WO2006124995B1 true WO2006124995B1 (en) 2007-11-22

Family

ID=36939244

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2006/019075 Ceased WO2006124995A2 (en) 2005-05-18 2006-05-17 Ballistic laminate structure

Country Status (2)

Country Link
EP (1) EP1885553A2 (en)
WO (1) WO2006124995A2 (en)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9857148B2 (en) 2010-12-15 2018-01-02 The Boeing Company Controlled fiber-matrix adhesion in polymer fiber composites
US20140206248A1 (en) * 2011-12-20 2014-07-24 Matscitechno Licensing Company Impact dissipating fabric
CZ305248B6 (en) * 2013-09-30 2015-07-01 Vysoké Učení Technické V Brně Material for ballistic protection, method of preparation and use
JP5994060B2 (en) * 2013-11-15 2016-09-21 八田経編株式会社 Thermoplastic resin reinforced sheet material and method for producing the same

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4623574A (en) * 1985-01-14 1986-11-18 Allied Corporation Ballistic-resistant composite article
US5190802A (en) * 1989-01-06 1993-03-02 Pilato Louis A Ballistic resistant laminate
GB2308094B (en) * 1995-12-16 1999-07-28 T & N Technology Ltd Anti-ballistic garment
NL1003405C2 (en) * 1996-06-24 1998-01-07 Dsm Nv Anti-ballistic molded part.
US20040221712A1 (en) * 1999-03-20 2004-11-11 Stewart Ricky William Ballistic-resistant laminate assemblies and panels
DE10011701A1 (en) * 2000-03-10 2001-09-27 Verseidag Indutex Gmbh Flexible laminate
HRP20030973B1 (en) * 2001-06-12 2011-02-28 Teijin Aramid Gmbh Laminated ballistic structure comprising alternating unidirectional and thermoplastic layers
NO316296B1 (en) * 2002-04-05 2004-01-05 Hiform As Lightweight ballistic protection and method of manufacturing such
DE10232269A1 (en) * 2002-07-16 2004-02-05 Hänsel Textil GmbH Flexible textile reinforcement composite
WO2005066577A1 (en) * 2004-01-01 2005-07-21 Dsm Ip Assets B.V. Ballistic-resistant article
US7148162B2 (en) * 2004-03-08 2006-12-12 Park Andrew D Ballistic laminate structure in sheet form

Also Published As

Publication number Publication date
WO2006124995A2 (en) 2006-11-23
EP1885553A2 (en) 2008-02-13
WO2006124995A3 (en) 2007-07-12

Similar Documents

Publication Publication Date Title
EP3870436B1 (en) Insulation board with improved performance
US7964267B1 (en) Ballistic-resistant panel including high modulus ultra high molecular weight polyethylene tape
US8168022B2 (en) Process for producing laminates of unidirectionally arranged polymeric tapes
JP4420466B2 (en) High performance composite
JP5453278B2 (en) Advanced bulletproof material
JP2010530052A6 (en) Ballistic resistant panel containing high elasticity ultra high molecular weight polyethylene tape
CA2491717A1 (en) Ballistic laminate structure in sheet form
HRP20030973A2 (en) Laminated ballistic structure comprising alternating unidirectional and thermoplastic layers
WO2010001273A3 (en) Elastic composite containing a low strength and lightweight nonwoven facing
JP2012528294A (en) Ballistic resistant panel containing high modulus ultra high molecular weight polyethylene tape
WO2007103673A1 (en) Impact resistant composite building panel
US7972679B1 (en) Ballistic-resistant article including one or more layers of cross-plied uhmwpe tape in combination with cross-plied fibers
AU2005301309A1 (en) Method of forming adhesives mixtures and ballistic composites utilizing the same
RU2007146414A (en) LAYERED FELT PRODUCTS
AU2016214287B2 (en) Ballistic resistant sheet and use of such a sheet
US11319708B2 (en) Insulation board with improved performance
WO2006124995B1 (en) Ballistic laminate structure
CN211552613U (en) Composite bulletproof plate
WO2008105929A2 (en) Method of forming adhesive mixtures and ballistic composites utilizing the same
US20060018504A1 (en) Multi-layer composite material panel
JPH0628946B2 (en) Impact resistant plate
JPH04276435A (en) Sandwich panel
JP7263704B2 (en) LAMINATED FILM, LAMINATED AND MOLDED BODY
JP2007038609A (en) Composite material for molding and molding using the same
CA2613081A1 (en) Increased ballistic performance of fabrics coated with polymer stripes

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase in:

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2006760019

Country of ref document: EP

NENP Non-entry into the national phase in:

Ref country code: RU