WO2006006593A1 - 封止用エポキシ樹脂成形材料及び電子部品装置 - Google Patents

封止用エポキシ樹脂成形材料及び電子部品装置 Download PDF

Info

Publication number
WO2006006593A1
WO2006006593A1 PCT/JP2005/012831 JP2005012831W WO2006006593A1 WO 2006006593 A1 WO2006006593 A1 WO 2006006593A1 JP 2005012831 W JP2005012831 W JP 2005012831W WO 2006006593 A1 WO2006006593 A1 WO 2006006593A1
Authority
WO
WIPO (PCT)
Prior art keywords
epoxy resin
sealing
compound
group
molding material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2005/012831
Other languages
English (en)
French (fr)
Inventor
Ryoichi Ikezawa
Hidetaka Yoshizawa
Seiichi Akagi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Resonac Corp
Original Assignee
Hitachi Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hitachi Chemical Co Ltd filed Critical Hitachi Chemical Co Ltd
Priority to US11/572,162 priority Critical patent/US20090143511A1/en
Publication of WO2006006593A1 publication Critical patent/WO2006006593A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　本発明は、（Ａ）エポキシ樹脂、（Ｂ）硬化剤、（Ｃ）水酸化マグネシウムを含有し、（Ｃ）水酸化マグネシウムがＸ線回折での[101]/[001]ピーク強度比が０.９以上で、ＢＥＴ比表面積が１～４ｍ2/ｇ、かつ平均粒子径が５μｍ以下であるものを含む封止用エポキシ樹脂成形材料に関し、これにより、難燃性、成形性、耐リフロー性、耐湿性及び高温放置特性等の信頼性に優れ、ＶＬＳＩの封止用に好適な封止用エポキシ樹脂成形材料、及びこの成形材料で封止した素子を備えた電子部品装置を提供する。

Description

明 細 書
封止用エポキシ樹脂成形材料及び電子部品装置
技術分野
[0001] 本発明は、封止用エポキシ榭脂成形材料及びこの成形材料で封止した素子を備 えた電子部品装置に関する。
背景技術
[0002] 従来から、トランジスタ、 IC等の電子部品装置の素子封止の分野では生産性、コス ト等の面力も榭脂封止が主流となり、エポキシ榭脂成形材料が広く用いられている。 この理由としては、エポキシ榭脂が電気特性、耐湿性、耐熱性、機械特性、インサー ト品との接着性などの諸特性にバランスがとれているためである。これらの封止用ェ ポキシ榭脂成形材料の難燃ィ匕は主にテトラブロモビスフエノール Aのジグリシジルェ 一テル等のブロム化榭脂と酸ィ匕アンチモンの組合せにより行われている。
[0003] 近年、環境保護の観点からハロゲンィ匕榭脂やアンチモンィ匕合物に量規制の動きが あり、封止用エポキシ榭脂成形材料にっ ヽてもノンハロゲン化 (ノンブロム化)及びノ ンアンチモンィ匕の要求が出てきている。また、プラスチック封止 ICの高温放置特性に ブロム化合物が悪影響を及ぼすことが知られており、この観点からもブロム化榭脂量 の低減が望まれている。
[0004] そこで、ブロム化榭脂ゃ酸化アンチモンを用いずに難燃化を達成する手法としては 、赤リンを用いる方法 (例えば日本国特開平 9— 227765号公報参照。）、リン酸エス テルィ匕合物を用いる方法 (例えば日本国特開平 9— 235449号公報参照。）、ホスフ ァゼン化合物を用いる方法 (例えば日本国特開平 8— 225714号公報参照。）、金属 水酸ィ匕物を用いる方法 (例えば日本国特開平 9 241483号公報参照。）、金属水 酸化物と金属酸化物を併用する方法 (例えば日本国特開平 9 100337号公報参 照。）、フエ口セン等のシクロペンタジェ二ルイ匕合物（例えば日本国特開平 11— 2693 49号公報参照。）、ァセチルァセトナート銅 (例えば、加藤寛、機能材料 (シーエムシ 一出版)、 11 (6)、 34 (1991)参照。）等の有機金属化合物を用いる方法などのハロ ゲン、アンチモン以外の難燃剤を用いる方法、充填剤の割合を高くする方法 (例えば 日本国特開平 7— 82343号公報参照。）、難燃性の高い榭脂を使用する方法 (例え ば日本国特開平 11— 140277号公報参照。）、表面に処理を施した金属水酸ィ匕物 を使用する方法 (例えば日本国特開平 1— 24503号公報及び特開平 10— 338818 号公報参照。）等が試みられている。
発明の開示
[0005] し力しながら、封止用エポキシ榭脂成形材料に赤リンを用いた場合は耐湿性の低 下の問題、リン酸エステルイ匕合物やホスファゼンィ匕合物を用いた場合は可塑ィ匕によ る成形性の低下や耐湿性の低下の問題、金属水酸化物を用いた場合は流動性や 金型離型性の低下の問題、金属酸化物を用いた場合や、充填剤の割合を高くした 場合は流動性の低下の問題がそれぞれある。また、ァセチルァセトナート銅等の有 機金属化合物を用いた場合は、硬化反応を阻害し成形性が低下する問題がある。さ らには難燃性の高い樹脂を使用する方法では、難燃性が電子部品装置の材料に求 められる規格 UL - 94 V- 0を十分に満足するものではな力つた。
[0006] また金属水酸ィ匕物の中で水酸ィ匕マグネシウムは耐熱性が高ぐ封止用エポキシ榭 脂成形材料に好適に使用される可能性が示唆されていた。しかし、多量に添加しな いと難燃性が発現せず、これにより流動性等の成形性が損なわれるといった問題が あった。また耐酸性に劣るため、半導体装置作製時の半田メツキ工程にて表面が腐 食され白化現象が起こるといった問題も有していた。このような問題は上記表面処理 にても解決できるものではなかった。
[0007] 以上のようにこれらノンハロゲン、ノンアンチモン系の難燃剤、充填剤の割合を高く する方法及び難燃性の高 、榭脂を使用する方法では、 V、ずれの場合もブロム化榭 脂と酸化アンチモンを併用した封止用エポキシ榭脂成形材料と同等の成形性、信頼 性及び難燃性を得るに至って ヽな ヽ。
[0008] 本発明は力かる状況に鑑みなされたもので、ノンハロゲンかつノンアンチモンで、成 形性、耐リフロー性、耐湿性及び高温放置特性等の信頼性を低下させずに難燃性 が良好な封止用エポキシ榭脂材料、及びこれにより封止した素子を備えた電子部品 装置を提供しょうとするものである。
[0009] 本発明者らは上記の課題を解決するために鋭意検討を重ねた結果、特定の水酸 化マグネシウムを配合した封止用エポキシ榭脂成形材料により上記の目的を達成し うることを見い出し、本発明を完成するに至った。
[0010] 本発明は以下の（1)〜（27)に関する。
[0011] (1) (A)エポキシ榭脂、（B)硬化剤、（C)水酸ィ匕マグネシウムを含有し、（C)水酸ィ匕 マグネシウムが X線回折での [101M001]ピーク強度比が 0.9以上で、 BET比表面積 力 Si〜4m2/g、かつ平均粒子径が 5 μ m以下であるものを含む封止用エポキシ榭脂 成形材料。
[0012] (2) (C)水酸ィ匕マグネシウム粒子が原料水酸ィ匕マグネシウムもしくは原料酸化マグネ シゥムの水懸濁液に、水酸化リチウムもしくは水酸ィ匕ナトリウムを、水酸化マグネシゥ ム換算の固形分 100質量％に対して、 100質量％以上添カ卩して湿式粉砕し、 180〜 230°Cで水熱処理して得られたものであることを特徴とする上記（1)記載の封止用ェ ポキシ榭脂成形材料。
[0013] (3) (C)水酸ィ匕マグネシウムの表面に、 Siィ匕合物と A1ィ匕合物との混合被覆層を SiO
2 と Al O換算の合計量で水酸化マグネシウム 100質量％に対して、 0.2〜10質量％
2 3
の割合で形成したものを含有する上記（1)又は（2) V、ずれか記載の封止用エポキシ 榭脂成形材料。
[0014] (4) Siィ匕合物がケィ酸ソーダ、コロイダルシリカ及びこれらの前駆体力 なる群の少な くとも 1種の化合物、 A1ィ匕合物が塩ィ匕アルミニウム、硫酸アルミニウム、硝酸アルミ- ゥム、アルミン酸ソーダ、アルミナゾル及びこれらの前駆体力 なる群の少なくとも 1種 の化合物を各々含む上記（3)記載の封止用エポキシ榭脂成形材料。
[0015] (5) Siィ匕合物と A1ィ匕合物の混合被覆層を形成した水酸ィ匕マグネシウムがさらに脂肪 族金属塩、シランカップリング剤の少なくとも 1種により、水酸ィ匕マグネシウム 100質量 %に対して 0.1〜 10質量％の割合で表面処理されているものを含む上記（3)又は（ 4) V、ずれか記載の封止用エポキシ榭脂成形材料。
[0016] (6) (C)水酸化マグネシウムが (A)エポキシ榭脂 100質量部に対し、 5〜300質量部 含有する上記（1)〜（5) V、ずれか記載の封止用エポキシ榭脂成形材料。
[0017] (7) (D)金属酸ィ匕物をさらに含有する上記（1)〜（6)いずれか記載の封止用ェポキ シ榭脂成形材料。 [0018] (8) (D)金属酸ィ匕物が典型金属元素の酸ィ匕物及び/又は遷移金属元素の酸ィ匕物か ら選ばれる上記（7)記載の封止用エポキシ榭脂成形材料。
[0019] (9) (D)金属酸化物が亜鉛、マグネシウム、銅、鉄、モリブデン、タングステン、ジルコ ユウム、マンガン及びカルシウムの酸ィ匕物の少なくとも 1種である上記（8)記載の封止 用エポキシ榭脂成形材料。
[0020] (10) (A)エポキシ榭脂がビフエ-ル型エポキシ榭脂、ビスフエノール F型エポキシ榭 脂、スチルベン型エポキシ榭脂、硫黄原子含有エポキシ榭脂、ノボラック型エポキシ 榭脂、ジシクロペンタジェン型エポキシ榭脂、ナフタレン型エポキシ榭脂、トリフエ- ルメタン型エポキシ榭脂、ビフエ-レン型エポキシ榭脂及びナフトール ·ァラルキル型 フエノール榭脂の少なくとも 1種を含有する上記（ 1)〜（9) 、ずれか記載の封止用ェ ポキシ榭脂成形材料。
[0021] (11)硫黄原子含有エポキシ榭脂が下記一般式 (I)で示される化合物である上記（10 )記載の封止用エポキシ榭脂成形材料。
[化 1]
Figure imgf000005_0001
[0022] (一般式 (I)で、 〜 は水素原子、置換又は非置換の炭素数 1〜10の一価の炭化 水素基から選ばれ、全てが同一でも異なっていてもよい。 nは 0〜3の整数を示す。） (12) (B)硬ィ匕剤がビフヱ-ル型フエノール榭脂、ァラルキル型フエノール榭脂、ジシ クロペンタジェン型フエノール榭脂、トリフエ-ルメタン型フエノール榭脂及びノボラッ ク型フ ノール榭脂の少なくとも 1種を含有する上記（1)〜（11) 、ずれか記載の封 止用エポキシ榭脂成形材料。
[0023] (13) (E)硬化促進剤をさらに含有する上記（1)〜（12)いずれか記載の封止用ェポ キシ榭脂成形材料。
[0024] (14) (E)硬化促進剤がホスフィン化合物とキノン化合物との付加物を含む上記（13) 記載の封止用エポキシ榭脂成形材料。 [0025] (15) (E)硬化促進剤が、リン原子に少なくとも一つのアルキル基が結合したホスフィ ン化合物とキノンィ匕合物との付加物を含む上記（14)記載の封止用エポキシ榭脂成 形材料。
[0026] (16) (F)カップリング剤をさらに含有する上記（1)〜（15)いずれか記載の封止用ェ ポキシ榭脂成形材料。
[0027] (17) (F)カップリング剤が 2級アミノ基を有するシランカップリング剤を含有する上記（
16)記載の封止用エポキシ榭脂成形材料。
[0028] (18) 2級アミノ基を有するシランカップリング剤が下記一般式 (Π)で示される化合物 を含有する上記（17)記載の封止用エポキシ榭脂成形材料。
[化 2]
Figure imgf000006_0001
[0029] (一般式 (II)で、 R1は水素原子、炭素数 1〜6のアルキル基及び炭素数 1〜2のアル コキシ基力 選ばれ、 R2は炭素数 1〜6のアルキル基及びフ -ル基力 選ばれ、 R3 はメチル基又はェチル基を示し、 nは 1〜6の整数を示し、 mは 1〜3の整数を示す。 ) (19) (G)リン原子を有する化合物をさらに含有する上記（1)〜（18)いずれか記載 の封止用エポキシ榭脂成形材料。
[0030] (20) (G)リン原子を有する化合物がリン酸エステル化合物を含有する上記（19)記 載の封止用エポキシ榭脂成形材料。
[0031] (21)リン酸エステルイ匕合物が下記一般式 (III)で示される化合物を含有する上記（2 0)記載の封止用エポキシ榭脂成形材料。
[化 3]
Figure imgf000007_0001
[0032] (一般式（III)で、式中の 8個の Rは炭素数 1〜4のアルキル基を示し、全て同一でも 異なっていてもよい。 Arは芳香族環を示す。 )
(22) (G)リン原子を有する化合物がホスフィンオキサイドを含有し、該ホスフィンォキ サイドが下記一般式 (IV)で示されるホスフィン化合物を含有する上記（19)記載の封 止用エポキシ榭脂成形材料。
[化 4]
Figure imgf000007_0002
[0033] (一般式 (IV)で、 R R2及び R3は炭素数 1〜10の置換又は非置換のアルキル基、 ァリール基、ァラルキル基または水素原子を示し、すべて同一でも異なってもよい。 ただしすべてが水素原子である場合を除く。 )
(23) (H)重量平均分子量が 4, 000以上の直鎖型酸化ポリエチレン、および (I)炭 素数 5〜30の α—ォレフインと無水マレイン酸との共重合物を炭素数 5〜25の一価 のアルコールでエステルィヒした化合物をさらに含有する上記（1)〜（22) 、ずれか記 載の封止用エポキシ榭脂成形材料。
[0034] (24) (Η)成分および (I)成分の少なくとも一方が、（Α)成分の一部または全部と予 備混合されてなる上記 (23)記載の封止用エポキシ榭脂成形材料。
[0035] (25) C 無機充填剤をさらに含有する上記（1)〜（24)いずれか記載の封止用ェポ キシ榭脂成形材料。 [0036] (26) (C)水酸化マグネシウムと CO無機充填剤の含有量の合計が封止用エポキシ榭 脂成形材料に対して 60〜95質量％である上記（25)記載の封止用エポキシ榭脂成 形材料。
[0037] (27)上記（1)〜（26)の 、ずれかに記載の封止用エポキシ榭脂成形材料で封止さ れた素子を備えた電子部品装置。
[0038] 本発明による封止用エポキシ榭脂成形材料は難燃性が良好で、かつ成形性ゃ耐リ フロー性、耐湿性及び高温放置特性等の信頼性が良好な電子部品装置等の製品を 得ることができ、その工業的価値は大である。
[0039] 本願の開示は、 2004年 7月 13日に出願された特願 2004— 206396号に記載の 主題と関連しており、それらの開示内容は引用によりここに援用される。
発明を実施するための最良の形態
[0040] 本発明にお ヽて用いられる (Α)エポキシ榭脂は、封止用エポキシ榭脂成形材料に 一般に使用されているもので特に制限はないが、たとえば、フエノールノボラック型ェ ポキシ榭脂、オルソクレゾールノボラック型エポキシ榭脂、トリフエ-ルメタン骨格を有 するエポキシ榭脂（トリフエ-ルメタン型エポキシ榭脂）をはじめとする、フエノール、ク レゾール、キシレノール、レゾルシン、カテコール、ビスフエノーノレ Α、ビスフエノール F 等のフエノール類及び Ζ又は α ナフトール、 β ナフトール、ジヒドロキシナフタレ ン等のナフトール類とホルムアルデヒド、ァセトアルデヒド、プロピオンアルデヒド、ベ ンズアルデヒド、サリチルアルデヒド等のアルデヒド基を有する化合物とを酸性触媒下 で縮合又は共縮合させて得られるノボラック榭脂をエポキシィ匕したもの（ノボラック型 エポキシ榭脂）；ビスフエノール Α、ビスフエノール F、ビスフエノール S、アルキル置換 又は非置換のビフエノール等のジグリシジルエーテル;スチルベン型エポキシ榭脂； ハイドロキノン型エポキシ榭脂；フタル酸、ダイマー酸等の多塩基酸とェピクロルヒドリ ンの反応により得られるグリシジルエステル型エポキシ榭脂；ジアミノジフエ-ルメタン 、イソシァヌル酸等のポリアミンとェピクロルヒドリンの反応により得られるグリシジルァ ミン型エポキシ榭脂；ジシクロペンタジェンとフエノール類の共縮合榭脂のエポキシィ匕 物（ジシクロペンタジェン型エポキシ榭脂）；ナフタレン環を有するエポキシ榭脂（ナフ タレン型エポキシ榭脂）；フエノール 'ァラルキル榭脂、ナフトール'ァラルキル榭脂等 のァラルキル型フエノール榭脂のエポキシ化物；ビフエ-レン型エポキシ榭脂；トリメ チロールプロパン型エポキシ榭脂;テルペン変性エポキシ榭脂;ォレフィン結合を過 酢酸等の過酸で酸化して得られる線状脂肪族エポキシ榭脂;脂環族エポキシ榭脂； 硫黄原子含有エポキシ榭脂などが挙げられ、これらを単独で用いても 2種以上を組 み合わせて用いてもよい。
[0041] なかでも、耐リフロー性の観点からはビフエ-ル型エポキシ榭脂、ビスフエノール F 型エポキシ榭脂、スチルベン型エポキシ榭脂及び硫黄原子含有エポキシ榭脂が好 ましぐ硬化性の観点からはノボラック型エポキシ榭脂が好ましぐ低吸湿性の観点か らはジシクロペンタジェン型エポキシ榭脂が好ましぐ耐熱性及び低反り性の観点か らはナフタレン型エポキシ榭脂及びトリフエ-ルメタン型エポキシ榭脂が好ましぐ難 燃性の観点からはビフエ-レン型エポキシ榭脂及びナフトール'ァラルキル型ェポキ シ榭脂が好ましい。これらのエポキシ榭脂の少なくとも 1種を含有していることが好ま しい。
[0042] ビフエニル型エポキシ榭脂としてはたとえば下記一般式 (V)で示されるエポキシ榭 脂等が挙げられ、ビスフエノール F型エポキシ榭脂としてはたとえば下記一般式 (VI) で示されるエポキシ榭脂等が挙げられ、スチルベン型エポキシ榭脂としてはたとえば 下記一般式 (VII)で示されるエポキシ榭脂等が挙げられ、硫黄原子含有エポキシ榭 脂としてはたとえば下記一般式 (I)で示されるエポキシ榭脂等が挙げられる。
[化 5]
Figure imgf000009_0001
(一般式 (V)で、 R R8は水素原子及び炭素数 1〜10の置換又は非置換の一価の 炭化水素基から選ばれ、全てが同一でも異なっていてもよい。 nは 0〜3の整数を示 す。）
[化 6]
Figure imgf000010_0001
(一般式 (VI)で、 R R8は水素原子、炭素数 1〜： L0のアルキル基、炭素数 1〜： L0の アルコキシル基、炭素数 6〜10のァリール基、及び炭素数 6〜 10のァラルキル基か ら選ばれ、全てが同一でも異なっていてもよい。 nは 0〜3の整数を示す。）
[化 7] 11)
Figure imgf000010_0002
(一般式 (VII)で、 R R8は水素原子及び炭素数 1〜5の置換又は非置換の一価の 炭化水素基から選ばれ、全てが同一でも異なっていてもよい。 nは 0〜10の整数を示 す。）
[化 8]
Figure imgf000010_0003
(一般式 (I)で、 R R8は水素原子、置換又は非置換の炭素数 1〜10のアルキル基 及び置換又は非置換の炭素数 1〜10のアルコキシ基力も選ばれ、全てが同一でも 異なっていてもよい。 nは 0〜3の整数を示す。 )
上記一般式 (V)で示されるビフエ-ル型エポキシ榭脂としては、たとえば、 4, 4' - ビス（2, 3 エポキシプロポキシ）ビフエ-ノレ又は 4, 4' ビス（2, 3 エポキシプロボ キシ）ー3, 3', 5, 5'—テトラメチルビフエニルを主成分とするエポキシ榭脂、ェピク ロノレヒドリンと 4, 4'ービフエノーノレ又は 4, 4' - (3, 3', 5, 5'—テトラメチノレ）ビフエノ 一ルとを反応させて得られるエポキシ榭脂等が挙げられる。なかでも 4, 4, ビス（2, 3—エポキシプロポキシ）ー 3, 3', 5, 5'—テトラメチルビフエ-ルを主成分とするェ ポキシ榭脂が好まし ヽ。 n=0を主成分とする YX— 4000 (ジャパンエポキシレジン株 式会社製商品名）等が市販品として入手可能である。
[0047] 上記一般式 (VI)で示されるビスフエノール F型エポキシ榭脂としては、例えば、
Figure imgf000011_0001
Figure imgf000011_0002
R6及び R8力メチル基で、 R2、 R5及び R7が水素原子であり、 n=0を主成分と する YSLV— 80XY (新日鐡化学株式会社製商品名）等が市販品として入手可能で ある。
[0048] 上記一般式 (VII)で示されるスチルベン型エポキシ榭脂は、原料であるスチルベン 系フエノール類とェピクロルヒドリンとを塩基性物質存在下で反応させて得ることがで きる。この原料であるスチルベン系フエノール類としては、たとえば 3—t—ブチルー 4 , 4' —ジヒドロキシ— 3' , 5, 5' —トリメチルスチルベン、 3—t—ブチル—4, 4' —ジヒドロキシ一 3' , 5' , 6—トリメチルスチルベン、 4, 4'—ジヒドロキシ一 3, 3', 5, 5'—テトラメチルスチルベン、 4, 4'ージヒドロキシ 3, 3'—ジ tーブチルー 5, 5'—ジメチルスチルベン、 4, 4'ージヒドロキシ 3, 3'—ジ tーブチルー 6, 6' - ジメチルスチルベン等が挙げられ、なかでも 3—t—ブチルー 4, 4' ージヒドロキシー 3' , 5, 5' —トリメチルスチルベン、及び 4, 4'—ジヒドロキシ— 3, 3 5, 5'—テト ラメチルスチルベンが好まし!/、。これらのスチルベン型フエノール類は単独で用いて も 2種以上を組み合わせて用いてもょ 、。
[0049] 上記一般式 (I)で示される硫黄原子含有エポキシ榭脂のなかでも、 R2、
Figure imgf000011_0003
及び R7が水素原子で、
Figure imgf000011_0004
R4、 R5及び R8がアルキル基であるエポキシ榭脂が好ましぐ R2 、 R6及び R7が水素原子で、 R1及び R8力 ¾ ブチル基で、 R4及び R5力メチル基で あるエポキシ榭脂がより好ましい。このような化合物としては、 YSLV— 120TE (東都 化成株式会社製商品名)等が市販品として入手可能である。
[0050] これらのエポキシ榭脂は 、ずれ力 1種を単独で用いても 2種以上を組合わせて用い てもよいが、その配合量は、その性能を発揮するためにエポキシ榭脂全量に対して 合わせて 20質量％以上とすることが好ましぐ 30質量％以上がより好ましぐ 50質量 %以上とすることがさらに好ましい。
[0051] ノボラック型エポキシ榭脂としては、たとえば下記一般式 (VIII)で示されるエポキシ 榭脂等が挙げられる。 [化 9]
Figure imgf000012_0001
[0052] (一般式 (VIII)で、 Rは水素原子及び炭素数 1〜： LOの置換又は非置換の一価の炭 化水素基から選ばれ、 nは 0〜 10の整数を示す。 )
上記一般式 (VIII)で示されるノボラック型エポキシ榭脂は、ノボラック型フエノール 榭脂にェピクロルヒドリンを反応させることによって容易に得られる。なかでも、一般式 (VIII)中の Rとしては、メチル基、ェチル基、プロピル基、ブチル基、イソプロピル基、 イソブチル基等の炭素数 1〜： L0のアルキル基、メトキシ基、エトキシ基、プロポキシ基 、ブトキシ基等の炭素数 1〜： L0のアルコキシル基が好ましぐ水素原子又はメチル基 力 り好ましい。 nは 0〜3の整数が好ましい。上記一般式 (VIII)で示されるノボラック 型エポキシ榭脂のなかでも、オルトクレゾールノボラック型エポキシ榭脂が好まし 、。 N— 600シリーズ (大日本インキ化学工業株式会社製商品名）等が市販品として入 手可能である。
[0053] ノボラック型エポキシ榭脂を使用する場合、その配合量は、その性能を発揮するた めにエポキシ榭脂全量に対して 20質量％以上とすることが好ましぐ 30質量％以上 力 り好ましい。
[0054] ジシクロペンタジェン型エポキシ榭脂としては、たとえば下記一般式 (IX)で示される エポキシ榭脂等が挙げられる。
[化 10]
Figure imgf000012_0002
[0055] (一般式 (IX)で、 R1及び R2は水素原子及び炭素数 1〜： L0の置換又は非置換の一価 の炭化水素基力もそれぞれ独立して選ばれ、 nは 0〜 10の整数を示し、 mは 0〜6の 整数を示す。 )
上記式 (IX)中の R1としては、たとえば、水素原子、メチル基、ェチル基、プロピル基 、ブチル基、イソプロピル基、 t ブチル基等のアルキル基、ビニル基、ァリル基、ブ テニル基等のアルケニル基、ハロゲンィヒアルキル基、アミノ基置換アルキル基、メル カプト基置換アルキル基などの炭素数 1〜5の置換又は非置換の一価の炭化水素基 が挙げられ、なかでもメチル基、ェチル基等のアルキル基及び水素原子が好ましぐ メチル基及び水素原子がより好ましい。 R2としては、たとえば、水素原子、メチル基、 ェチル基、プロピル基、ブチル基、イソプロピル基、 t ブチル基等のアルキル基、ビ -ル基、ァリル基、ブテニル基等のァルケ-ル基、ハロゲンィヒアルキル基、アミノ基置 換アルキル基、メルカプト基置換アルキル基などの炭素数 1〜5の置換又は非置換 の一価の炭化水素基が挙げられ、なかでも水素原子が好ましい。 HP— 7200 (大日 本インキ化学工業株式会社製商品名）等が市販品として入手可能である。
[0056] ジシクロペンタジェン型エポキシ榭脂を使用する場合、その配合量は、その性能を 発揮するためにエポキシ榭脂全量に対して 20質量％以上とすることが好ましぐ 30 質量％以上がより好ましい
ナフタレン型エポキシ榭脂としてはたとえば下記一般式 (X)で示されるエポキシ榭 脂等が挙げられ、トリフエ-ルメタン型エポキシ榭脂としてはたとえば下記一般式 (XI) で示されるエポキシ榭脂等が挙げられる。
[化 11]
Figure imgf000013_0001
[0057] (一般式 (X)で、 R1〜 は水素原子及び置換又は非置換の炭素数 1〜12の一価の 炭化水素基から選ばれ、それぞれ全てが同一でも異なっていてもよい。 ρは 1又は 0 で、 1、 mはそれぞれ 0〜： L 1の整数であって、（1+m)が 1〜： L 1の整数でかつ（1+p)が 1〜12の整数となるよう選ばれる。 iは 0〜3の整数、 jは 0〜2の整数、 kは 0〜4の整 数を示す。 )
上記一般式 (X)で示されるナフタレン型エポキシ榭脂としては、 1個の構成単位及 び m個の構成単位をランダムに含むランダム共重合体、交互に含む交互共重合体、 規則的に含む共重合体、ブロック状に含むブロック共重合体が挙げられ、これらのい ずれ力 1種を単独で用いても、 2種以上を組み合わせて用いてもょ 、。
[化 12]
Figure imgf000014_0001
[0058] (一般式 (XI)で、 Rは水素原子及び炭素数 1〜10の置換又は非置換の一価の炭化 水素基から選ばれ、 nは 1〜10の整数を示す。 )
一般式 (XI)で示されるトリフエ-ルメタン型エポキシ榭脂としては例えば EPPN— 50
0シリーズ（日本ィ匕薬株式会社製商品名）が市販品として入手可能である。
[0059] これらのエポキシ榭脂は 、ずれか 1種を単独で用いても両者を組合わせて用いて もよいが、その配合量は、その性能を発揮するためにエポキシ榭脂全量に対して合 わせて 20質量％以上とすることが好ましぐ 30質量％以上がより好ましぐ 50質量％ 以上とすることがさらに好ましい。
[0060] 上記のビフエ-ル型エポキシ榭脂、ビスフエノール F型エポキシ榭脂、スチルベン型 エポキシ榭脂、硫黄原子含有エポキシ榭脂、ノボラック型エポキシ榭脂、ジシクロべ ンタジェン型エポキシ榭脂、ナフタレン型エポキシ榭脂及びトリフエニルメタン型ェポ キシ榭脂は、いずれか 1種を単独で用いても 2種以上を組合わせて用いてもよいが、 その配合量はエポキシ榭脂全量に対して合わせて 50質量％以上とすることが好まし く、 60質量％以上がより好ましぐ 80質量％以上がさらに好ましい。
[0061] ビフエ-レン型エポキシ榭脂としてはたとえば下記一般式 (XII)で示されるエポキシ 榭脂等が挙げられ、ナフトール'ァラルキル型エポキシ榭脂としてはたとえば下記一 般式 (xm)で示されるエポキシ榭脂等が挙げられる。
[化 13]
Figure imgf000015_0001
(上記一般式 (XII)中の Ri R9は全てが同一でも異なっていてもよぐ水素原子、メチ ル基、ェチル基、プロピル基、ブチル基、イソプロピル基、イソブチル基等の炭素数 1 〜： L0のアルキル基、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基等の炭素数 1 〜 10のアルコキシル基、フエ-ル基、トリル基、キシリル基等の炭素数 6〜 10のァリ ール基、及び、ベンジル基、フエネチル基等の炭素数 6〜 10のァラルキル基から選 ばれ、なかでも水素原子とメチル基が好ましい。 nは 0〜10の整数を示す。 )
[化 14]
Figure imgf000015_0002
[0063] (一般式 (XIII)で、 Ri〜R2は水素原子及び置換又は非置換の炭素数 1〜12の一価 の炭化水素基から選ばれ、それぞれ全てが同一でも異なっていてもよい。 nは 1〜10 の整数を示す。 )
ビフエ-レン型エポキシ榭脂としては NC - 3000 (日本化薬株式会社製商品名）等 が市販品として入手可能である。またナフトール'ァラルキル型エポキシ榭脂としては ESN- 175 (東都化成株式会社製商品名）等が市販品として入手可能である。
[0064] これらのビフエ-レン型エポキシ榭脂及びナフトール ·ァラルキル型エポキシ榭脂は いずれか 1種を単独で用いても両者を組合わせて用いてもよいが、その配合量は、 その性能を発揮するためにエポキシ榭脂全量に対して合わせて 20質量％以上とす ることが好ましぐ 30質量％以上がより好ましぐ 50質量％以上とすることがさらに好 ましい。
[0065] 上記エポキシ榭脂の中でも、特には耐リフロー性等の信頼性、成形性及び難燃性 の観点力ゝらは上記一般式 (I)で示される構造の硫黄原子含有エポキシ榭脂が最も好 ましい。
[0066] 本発明において用いられる (A)エポキシ榭脂の 150°Cにおける溶融粘度は、流動 性の観点から 2ボイズ以下が好ましぐ 1ボイズ以下がより好ましぐ 0.5ボイズ以下が さらに好ましい。ここで、溶融粘度とは ICIコーンプレート粘度計で測定した粘度を示 す。
[0067] 本発明にお ヽて用いられる (B)硬化剤は、封止用エポキシ榭脂成形材料に一般に 使用されているもので特に制限はないが、たとえば、フエノール、クレゾール、レゾル シン、カテコール、ビスフエノール A、ビスフエノール F、フエ-ルフエノール、ァミノフエ ノール等のフエノール類及び Z又は α—ナフトール、 β ナフトール、ジヒドロキシナ フタレン等のナフトール類とホルムアルデヒド、ベンズアルデヒド、サリチルアルデヒド 等のアルデヒド基を有する化合物とを酸性触媒下で縮合又は共縮合させて得られる ノボラック型フエノール榭脂；フエノール類及び/又はナフトール類とジメトキシパラキ シレン又はビス (メトキシメチル）ビフエ-ルカ 合成されるフエノール ·ァラルキル榭脂 、ナフトール'ァラルキル榭脂、ビフエ-ル 'ァラルキル榭脂等のァラルキル型フエノー ル榭脂；フエノール類及び Ζ又はナフトール類とジシクロペンタジェンから共重合に より合成されるジシクロペンタジェン型フエノール榭脂；テルペン変性フエノール榭脂 ；トリフエニルメタン型フエノール榭脂などが挙げられ、これらを単独で用いても 2種以 上を組み合わせて用いてもょ 、。
[0068] なかでも、難燃性の観点からはビフエニル型フエノール榭脂が好ましぐ耐リフロー 性及び硬化性の観点からはァラルキル型フエノール榭脂が好ましく、低吸湿性の観 点からはジシクロペンタジェン型フエノール榭脂が好ましぐ耐熱性、低膨張率及び 低そり性の観点からはトリフエ-ルメタン型フエノール榭脂が好ましぐ硬化性の観点 力もはノボラック型フエノール榭脂が好ましぐこれらのフエノール榭脂の少なくとも 1 種を含有して 、ることが好まし 、。 ビフエニル型フエノール榭脂としては、たとえば下記一般式 (XIV)で示されるフエノ ル榭脂等が挙げられる。
[化 15]
Figure imgf000017_0001
[0070] 上記式 (XIV)中の！^〜尺9は全てが同一でも異なっていてもよぐ水素原子、メチル 基、ェチル基、プロピル基、ブチル基、イソプロピル基、イソブチル基等の炭素数 1〜 10のアルキル基、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基等の炭素数 1〜1 0のアルコキシル基、フエ-ル基、トリル基、キシリル基等の炭素数 6〜 10のァリール 基、及び、ベンジル基、フエネチル基等の炭素数 6〜 10のァラルキル基力も選ばれ、 なかでも水素原子とメチル基が好ましい。 nは 0〜 10の整数を示す。
[0071] 上記一般式 (XIV)で示されるビフエ-ル型フエノール榭脂としては、たとえば R^R9 が全て水素原子である化合物等が挙げられ、なかでも溶融粘度の観点から、 nが 1以 上の縮合体を 50質量％以上含む縮合体の混合物が好ま 、。このような化合物とし ては、 MEH- 7851 (明和化成株式会社製商品名）等が市販品として入手可能であ る。
[0072] ビフエニル型フエノール榭脂を使用する場合、その配合量は、その性能を発揮する ために硬化剤全量に対して 30質量％以上とすることが好ましぐ 50質量％以上がよ り好ましぐ 60質量％以上がさらに好ましい。
[0073] ァラルキル型フエノール榭脂としては、たとえばフエノール 'ァラルキル榭脂、ナフト ール ·ァラルキル榭脂等が挙げられ、下記一般式 (XV)で示されるフエノール ·ァラル キル榭脂、下記一般式 (XVI)で示されるナフトール'ァラルキル榭脂が好ましい。一 般式 (XV)中の Rが水素原子で、 nの平均値が 0〜8であるフエノール.ァラルキル榭脂 力 り好ましい。具体例としては、 p—キシリレン型フエノール'ァラルキル榭脂、 m— キシリレン型フエノール 'ァラルキル榭脂等が挙げられる。これらのァラルキル型フエノ 一ル榭脂を用いる場合、その配合量は、その性能を発揮するために硬化剤全量〖こ 対して 30質量％以上とすることが好ましぐ 50質量％以上がより好ましい,
[化 16]
Figure imgf000018_0001
[0074] (一般式 (XV)で、 Rは水素原子及び炭素数 1〜： 10の置換又は非置換の一価の炭化 水素基から選ばれ、 nは 0〜 10の整数を示す。 )
[化 17]
Figure imgf000018_0002
[0075] (一般式 (XVI)で、 Ri〜R2は水素原子及び炭素数 1〜： L0の置換又は非置換の一価 の炭化水素基力も選ばれ、それぞれ全てが同一でも異なっていてもよい。 nは 0〜10 の整数を示す。 )
ジシクロペンタジェン型フエノール榭脂としては、たとえば下記一般式 (XVII)で示さ れるフ ノール榭脂等が挙げられる。
[化 18]
Figure imgf000018_0003
[0076] (一般式 (XVII)で、 R1及び R2は水素原子及び炭素数 1〜 10の置換又は非置換の一 価の炭化水素基力もそれぞれ独立して選ばれ、 ηは 0〜 10の整数を示し、 mは 0〜6 の整数を示す。 ) ジシクロペンタジェン型フエノール榭脂を用いる場合、その配合量は、その'性能を 発揮するために硬化剤全量に対して 30質量％以上とすることが好ましぐ 50質量％ 以上がより好ましい。
トリフエ-ルメタン型フエノール榭脂としては、たとえば下記一般式 (xvm)で示される フエノール榭脂等が挙げられる。
[化 19]
Figure imgf000019_0001
[0078] (一般式 (XVIII)で、 Rは水素原子及び炭素数 1〜： L0の置換又は非置換の一価の炭 化水素基から選ばれ、 nは 1〜10の整数を示す。 )
トリフエ-ルメタン型フエノール榭脂を用いる場合、その配合量は、その性能を発揮 するために硬化剤全量に対して 30質量％以上とすることが好ましぐ 50質量％以上 力 り好ましい。
[0079] ノボラック型フエノール榭脂としては、たとえばフエノールノボラック榭脂、タレゾール ノボラック榭脂、ナフトールノボラック榭脂等が挙げられ、なかでもフエノールノボラック 榭脂が好ましい。ノボラック型フエノール榭脂を用いる場合、その配合量は、その性 能を発揮するために硬化剤全量に対して 30質量％以上とすることが好ましぐ 50質 量％以上がより好ましい。
[0080] 上記のビフエ-ル型フエノール榭脂、ァラルキル型フエノール榭脂、ジシクロペンタ ジェン型フエノール榭脂、トリフエニルメタン型フエノール榭脂及びノボラック型フエノ 一ル榭脂は、いずれか 1種を単独で用いても 2種以上を組合わせて用いてもよい。そ の配合量は硬化剤全量に対して合わせて 60質量％以上とすることが好ましぐ 80質 量％以上がより好ましい。
[0081] 本発明において用いられる（B)硬化剤の 150°Cにおける溶融粘度は、流動性の観 点から 2ボイズ以下が好ましぐ 1ボイズ以下がより好ましい。ここで、溶融粘度とは ICI 粘度を示す。
[0082] (A)エポキシ榭脂と（B)硬化剤との当量比、すなわち、エポキシ榭脂中のエポキシ 基数に対する硬化剤中の水酸基数の比 (硬化剤中の水酸基数 Zエポキシ榭脂中の エポキシ基数）は、特に制限はないが、それぞれの未反応分を少なく抑えるために 0 . 5〜2の範囲に設定されることが好ましぐ 0. 6〜1. 3がより好ましい。成形性及び 耐リフロー性に優れる封止用エポキシ榭脂成形材料を得るためには 0. 8〜1. 2の範 囲に設定されることがさらに好ましい。
[0083] 本発明にお 、て用いられる (C)水酸ィ匕マグネシウムは難燃剤として作用するもので 、 X線回折での [101M001]ピーク強度比が 0.9以上で、 BET比表面積が l〜4m2/g 、かつ平均粒子径が 5 μ m以下であるものを含む。上記のような水酸化マグネシウム の合成方法は特に限定するものではないが、原料水酸ィ匕マグネシウムもしくは原料 酸ィ匕マグネシウムの水懸濁液に、水酸化リチウムもしくは水酸ィ匕ナトリウムを、水酸ィ匕 マグネシウム換算の固形分 100質量％に対して、 100質量％以上添加して湿式粉砕 し、 180〜230°Cで水熱処理して得られたものが好まし！/、。
[0084] なお、本発明では、平均粒子径は、レーザ回折散乱法で測定した粒度分布で累積 50質量％となる粒径とし、 日機装株式会社製マイクロトラック粒度分布測定装置を使 用して測定した。また、 BET比表面積は JIS Z8830に準拠して測定される。
[0085] 上記水酸ィ匕マグネシウムは耐酸性の観点力 表面を被覆することが好ましぐ被覆 は Siィ匕合物と A1ィ匕合物との混合被覆層であることが好ましい。混合被覆層は SiOと
2
Al O換算の合計量で水酸化マグネシウム 100質量％に対して、 0.2〜10質量％の
2 3
割合で形成したものであることが耐酸性の観点カゝら好まし ヽ。本混合被覆層は Siィ匕 合物がケィ酸ソーダ、コロイダルシリカ及びこれらの前駆体力 なる群の少なくとも 1 種の化合物、 A1ィ匕合物が塩ィ匕アルミニウム、硫酸アルミニウム、硝酸アルミニウム、ァ ルミン酸ソーダ、アルミナゾル及びこれらの前駆体力 なる群の少なくとも 1種の化合 物を各々含むものであることが製造上の観点力も好ま 、。
[0086] 水酸ィ匕マグネシウムを Siィ匕合物にて被覆する方法は特に限定するものではな 、が 、例えば水酸ィ匕マグネシウムを水中に分散させたスラリーに水溶性の珪酸ソーダをカロ え、酸で中和して水酸ィ匕マグネシウム表面に析出させる方法が好ましい。水溶液の 温度は被覆性の観点から 5〜： L00°Cが好ましぐさらには 50〜95°Cとすることがより 好ましぐまた中和は被覆性の観点からスラリーの pHを 6〜： LOとするのが好ましぐさ らには 6〜9.5とするのがより好ましい。
[0087] また水酸ィ匕マグネシウムを A1ィ匕合物にて被覆する方法は特に限定するものではな いが、例えばアルミン酸ソーダと酸をそれぞれ、水酸ィ匕マグネシウムスラリー中にカロえ て析出させる方法がある。また、 Siィ匕合物と A1ィ匕合物とを同時に水酸ィ匕マグネシウム に被覆させてもよい。同時に被覆させる場合は、例えば水酸ィ匕マグネシウムを珪酸ソ ーダと塩ィ匕アルミニウムとの水溶液に加える方法等がある。
[0088] 本発明における Siィ匕合物と A1ィ匕合物の混合被覆層を形成した水酸ィ匕マグネシウム には、さらなる耐酸性向上の観点から、さらに脂肪族金属塩、シランカップリング剤の 少なくとも 1種により表面処理されることが好ましい。表面処理量は水酸ィ匕マグネシゥ ム 100質量％に対して 0.1〜10質量％の割合であることが好ましい。
[0089] 脂肪族金属塩としてはォレイン酸ゃステアリン酸等の高級脂肪酸のナトリウム塩、力 リウム塩等が好ましい。
[0090] シランカップリング剤としては、特に限定されるものではないが、例えばビニルェトキ シシラン、ビニルトリス（2—メトキシエトキシ）シラン、 γ—メタクリロキシプロピルトリメト キシシラン、 γ—ァミノプロピルトリメトキシシラン、 j8 —（3, 4—エポキシシクロへキシ ル）ェチルトリメトキシシラン、 Ύーグリシドキシプロピルトリメトキシシラン、 γ—メルカ プトプロピルトリメトキシシラン、 3—クロ口プロピルトリメトキシシラン等を挙げることがで きる。また、アルミニウムカップリング剤としては、例えばァセチルアルコキシアルミ-ゥ ムジイソプロピレートを例示することができ、チタネートカップリング剤としては、例えば 、イソプロピルトリイソステアロイルチタネート、イソプロピルトリス（ジォクチルパイロホス フェート）チタネート、イソプロピルトリ（Ν—アミノエチルアミノエチル）チタネート、イソ プロピルトリデシルベンゼンスルホ-ルチタネート等を例示することができる。
[0091] 本発明の封止用エポキシ榭脂成形材料で用いられる (C)水酸ィ匕マグネシウムは流 動性の観点から、 X線回折での [101M001]ピーク強度比が 0.9以上であることが好ま しい。 0.9未満であると結晶の厚みが低下し、流動性が低下する傾向にある。また BE T比表面積が l〜4m2/gであることが難燃性、流動性の観点力も好ましい。 lm2/g未 満であると難燃性が低下し、 4m2/gを超える場合は流動性が低下する傾向がある。さ らには平均粒子径が 5 μ m以下であることが好ましい。より好ましくは 1〜4 μ mである 。 5 μ mを超える場合は難燃性が低下する傾向にある。また 1 μ m未満であると流動 性が低下する傾向にある。
[0092] (C)水酸ィ匕マグネシウムの配合量は (A)エポキシ榭脂 100質量部に対して、 5〜3 00質量部配合することが好ましい。 10〜200質量部がより好ましぐ 20〜100質量 部がさらに好ましい。配合量が 5質量部未満であると難燃性に劣る傾向があり、 300 質量部を超える場合、流動性等の成形性、耐酸性に劣る傾向がある。
[0093] 上記水酸ィ匕マグネシウムを合成するために用いられる原料水酸ィ匕マグネシウムは 特に限定するものではないが、天然鉱石を粉砕して得られた天然物、マグネシウム 塩水溶液をアルカリで中和して得られた合成物、またこれら水酸ィ匕マグネシウムをホ ゥ酸塩、リン酸塩、亜鉛塩等で処理したものでもよい。さらには下記組成式 (XIX)で 示される複合金属水酸化物でもよ ヽ。
[0094] (化 20)
p M1 O ) · q(M2 O ) · r(M3 O ) · mH O (XIX)
a b d c d 2
(組成式 (XIX)で、
Figure imgf000022_0001
M2及び M3は互いに異なる金属元素を示し、 M1がマグネシゥ ム元素で、 a、 b、 c、 d、 p、 q及び mは正の数、 rは 0又は正の数を示す。 )
なかでも、上記組成式 (XIX)中の rが 0である化合物、すなわち、下記組成式 (XlXa )で示される化合物がさらに好ましい。
[0095] (化 21)
mCM1 O ) · n(M2 O ) · 1(H O) (XlXa)
a b c d 2
(組成式 (XlXa)で、 M1及び M2は互いに異なる金属元素を示し、 M1がマグネシウム 元素で、 a、 b、 c、 d、 m、 n及び 1は正の数を示す。 )
上記糸且成式（XIX)及び（XlXa)中の M1及び M2は M1がマグネシウム元素で一方は マグネシウム元素と異なる金属元素であれば特に制限はないが、難燃性の観点から は、 M1と M2が同一とならないようにマグネシウム以外の元素が第 3周期の金属元素、 ΠΑ族のアルカリ土類金属元素、 IVB族、 ΠΒ族、 VIII族、 IB族、 ΙΠΑ族及び IVA族に属 する金属元素から選ばれ、 M2が ΠΙΒ〜ΠΒ族の遷移金属元素力 選ばれることが好ま しぐ M1がマグネシウム、 M2がカルシウム、アルミニウム、スズ、チタン、鉄、コバルト、 ニッケル、銅及び亜鉛力も選ばれることがより好ましい。流動性の観点からは、 M1が マグネシウム、 M2が亜鉛又はニッケルであることが好ましぐ M1がマグネシウムで M2 が亜鉛であることがより好ましい。上記組成式 (XIX)中の p、 q、 rのモル比は本発明の 効果が得られれば特に制限はないが、 r = 0で、 p及び qのモル比 pZqが 99Zl〜50 Z50であることが好ましい。すなわち、上記組成式（XlXa)中の m及び nのモル比 m Znが 99Zl〜50Z50であることが好ましい。
[0096] なお、金属元素の分類は、典型元素を Α亜族、遷移元素を B亜族とする長周期型 の周期律表（出典:共立出版株式会社発行「化学大辞典 4」 1987年 2月 15日縮刷版 第 30刷）に基づいて行った。
[0097] 本発明の封止用エポキシ榭脂成形材料には、難燃性を向上させる観点から (D)金 属酸ィ匕物を用いることができる。（D)金属酸化物としては IA族、 ΠΑ族、 IIIA〜VIA族 に属する元素中の金属元素、いわゆる典型金属元素、及び ΠΙΒ〜ΠΒ族に属する遷 移金属元素の酸ィ匕物力 選ばれることが好ましぐ難燃性の観点力 はマグネシウム 、銅、鉄、モリブデン、タングステン、ジルコニウム、マンガン及びカルシウムの酸化物 の少なくとも一種であることが好まし 、。
[0098] (D)金属酸ィ匕物の配合量は (Α)エポキシ榭脂 100質量部に対して 0. 1〜100質 量部であることが好ましぐ 1〜50質量部であることがより好ましぐ 3〜20質量部であ ることがさらに好ましい。 0. 1質量部未満であると、難燃性の効果に劣る傾向があり、 また 100質量部を超えると流動性や硬化性が低下する傾向にある。
[0099] 本発明の封止用エポキシ榭脂成形材料には、 (Α)エポキシ榭脂と (Β)硬化剤の反 応を促進させるために必要に応じて (Ε)硬化促進剤を用いることができる。 (Ε)硬化 促進剤は、封止用エポキシ榭脂成形材料に一般に使用されているもので特に制限 はないが、たとえば、 1, 8 ジァザービシクロ（5, 4, 0)ゥンデセン 7、 1, 5 ジァ ザ一ビシクロ（4, 3, 0)ノネン、 5,6 ジブチルァミノ一 1, 8 ジァザ一ビシクロ（5, 4 , 0)ゥンデセン 7等のシクロアミジン化合物及びこれらの化合物に無水マレイン酸 、 1, 4一べンゾキノン、 2, 5 トルキノン、 1, 4 ナフトキノン、 2, 3 ジメチルベンゾ キノン、 2, 6 ジメチルベンゾキノン、 2, 3 ジメトキシー 5—メチルー 1, 4一べンゾ キノン、 2, 3 ジメトキシ 1, 4一べンゾキノン、フエニノレー 1, 4一べンゾキノン等の キノンィ匕合物、ジァゾフエニルメタン、フエノール榭脂等の π結合をもつ化合物を付 加してなる分子内分極を有する化合物、ベンジルジメチルァミン、トリエタノールァミン 、ジメチルァミノエタノール、トリス（ジメチルアミノメチル）フエノール等の 3級ァミン類 及びこれらの誘導体、 2—メチルイミダゾール、 2—フエ-ルイミダゾール、 2—フエ- ルー 4ーメチルイミダゾール等のイミダゾール類及びこれらの誘導体、トリブチルホス フィン、メチルジフエ-ルホスフィン、トリフエ-ルホスフィン、トリス（4—メチルフエ-ル )ホスフィン、ジフエ-ルホスフィン、フエ-ルホスフィン等のホスフィン化合物及びこれ らのホスフィン化合物に無水マレイン酸、上記キノン化合物、ジァゾフエ-ルメタン、フ エノール榭脂等の π結合をもつ化合物を付加してなる分子内分極を有するリンィ匕合 物、テトラフエ-ルホスホ-ゥムテトラフエ-ルポレート、トリフエ-ルホスフィンテトラフ ェ-ルボレート、 2 ェチルー 4ーメチルイミダゾールテトラフエ-ルポレート、 Ν—メチ ルモルホリンテトラフヱ-ルポレート等のテトラフヱ-ルポロン塩及びこれらの誘導体 などが挙げられ、これらを単独で用いても 2種以上を組み合わせて用いてもよい。特 にホスフィンィ匕合物とキノンィ匕合物との付加物を含むのが好ましい。
なかでも、難燃性、硬化性の観点からは、トリフエ-ルホスフィンが好ましぐ難燃性 、硬化性、流動性及び離型性の観点からは第三ホスフィン化合物とキノン化合物との 付加物が好ましい。第三ホスフィンィ匕合物としては、特に限定するものではないが、ト リシクロへキシルホスフィン、トリブチルホスフィン、ジブチルフエニルホスフィン、ブチ ルジフエ-ルホスフィン、ェチルジフエ-ルホスフィン、トリフエ-ルホスフィン、トリス（4 —メチルフエ-ル）ホスフィン、トリス（4—ェチルフエ-ル）ホスフィン、トリス（4—プロピ ルフエ-ル）ホスフィン、トリス（4—ブチルフエ-ル）ホスフィン、トリス（イソプロピルフエ -ル）ホスフィン、トリス（t—ブチルフエ-ル）ホスフィン、トリス（2, 4 ジメチルフエ- ル）ホスフィン、トリス（2, 6 ジメチルフエ-ル）ホスフィン、トリス（2, 4, 6 トリメチル フエ-ル）ホスフィン、トリス（2, 6 ジメチルー 4 エトキシフエ-ル）ホスフィン、トリス（ 4—メトキシフエ-ル）ホスフィン、トリス（4—エトキシフエ-ル）ホスフィンなどのアルキ ル基、ァリール基を有する第三ホスフィンィ匕合物が好ましい。またキノンィ匕合物として は o べンゾキノン、 p べンゾキノン、ジフエノキノン、 1, 4 ナフトキノン、アントラキ ノン等があげられ、なかでも耐湿性、保存安定性の観点力 p—ベンゾキノンが好まし い。トリス（4—メチルフエ-ル）ホスフィンと p—ベンゾキノンとの付カ卩物力 離型性の 観点からより好ましい。さらにはリン原子に少なくとも一つのアルキル基が結合したホ スフインィ匕合物とキノンィ匕合物との付加物が硬化性、流動性及び難燃性の観点から 好ましい
硬化促進剤の配合量は、硬化促進効果が達成される量であれば特に制限されるも のではないが、封止用エポキシ榭脂成形材料に対して 0. 005〜2質量％が好ましく 、 0. 01〜0. 5質量％がより好ましい。 0. 005質量％未満では短時間での硬化性に 劣る傾向があり、 2質量％を超えると硬化速度が速すぎて良好な成形品を得ることが 困難になる傾向がある。
[0101] 本発明では必要に応じて ω無機充填剤を配合することができる。無機充填剤は、 吸湿性、線膨張係数低減、熱伝導性向上及び強度向上の効果があり、たとえば、溶 融シリカ、結晶シリカ、アルミナ、ジルコン、珪酸カルシウム、炭酸カルシウム、チタン 酸カリウム、炭化珪素、窒化珪素、窒化アルミ、窒化ホウ素、ベリリア、ジルコユア、ジ ルコン、フォステライト、ステアタイト、スピネル、ムライト、チタ-ァ等の粉体、又はこれ らを球形ィ匕したビーズ、ガラス繊維等が挙げられる。さらに、難燃効果のある無機充 填剤としては水酸ィ匕アルミニウム、硼酸亜鉛、モリブデン酸亜鉛などが挙げられる。こ こで、ホウ酸亜鉛としては FB— 290、 FB— 500 (U. S. Borax社製）、 FRZ— 500C (水澤化学工業株式会社製)等が、モリブデン酸亜鉛としては KEMGARD911B、 9 11C, 1100 (Sherwin— Williams社製）等が各々市販品として入手可能である。
[0102] これらの無機充填剤は単独で用いても 2種以上を組み合わせて用いてもよい。なか でも、充填性、線膨張係数の低減の観点力ゝらは溶融シリカが、高熱伝導性の観点か らはアルミナが好ましぐ無機充填剤の形状は充填性及び金型摩耗性の点から球形 が好ましい。
[0103] 無機充填剤の配合量は、難燃性、成形性、吸湿性、線膨張係数低減、強度向上及 び耐リフロー性の観点から、 (C)水酸化マグネシウムと合計して封止用エポキシ榭脂 成形材料に対して 50質量％以上が好ましぐ 60〜95質量％がより好ましぐ 70〜9 0質量％がさらに好ましい。 60質量％未満では難燃性及び耐リフロー性が低下する 傾向があり、 95質量％を超えると流動性が不足する傾向があり、また難燃性も低下 する傾向にある。
ω無機充填剤を用いる場合、本発明の封止用エポキシ榭脂成形材料には、榭脂 成分と充項剤との接着性を高めるために、（F)カップリング剤をさらに配合することが 好ましい。（F)カップリング剤としては、封止用エポキシ榭脂成形材料に一般に使用 されているもので特に制限はないが、たとえば、 1級及び Ζ又は 2級及び Ζ又は 3級 アミノ基を有するシランィ匕合物、エポキシシラン、メルカプトシラン、アルキルシラン、ゥ レイドシラン、ビュルシラン等の各種シラン系化合物、チタン系化合物、アルミニウム キレート類、アルミニウム Ζジルコニウム系化合物等が挙げられる。これらを例示する と、ビュルトリクロロシラン、ビュルトリエトキシシラン、ビュルトリス（j8—メトキシェトキシ )シラン、 γ—メタクリロキシプロピルトリメトキシシラン、 j8 —（3, 4—エポキシシクロへ リシドキシプロピルメチルジメトキシシラン、ビュルトリァセトキシシラン、 γ —メルカプト プロピルトリメトキシシラン、 γ—ァミノプロピルトリメトキシシラン、 γ—ァミノプロピノレメ チルジメトキシシラン、 γ—ァミノプロピルトリエトキシシラン、 γ—ァミノプロピルメチル ジエトキシシラン、 Ί—ァニリノプロピルトリメトキシシラン、 γ—ァニリノプロピルトリエト キシシラン、 γ - (Ν, Ν—ジメチル）ァミノプロピルトリメトキシシラン、 γ - (Ν, Ν—ジ ェチル）ァミノプロピルトリメトキシシラン、 γ— (Ν, Ν—ジブチル）ァミノプロピルトリメト キシシラン、 γ - (Ν—メチル）ァ-リノプロピルトリメトキシシラン、 γ - (Ν—ェチル） ァニリノプロピルトリメトキシシラン、 Ύ — (Ν, Ν—ジメチル）ァミノプロピルトリエトキシ シラン、 γ - (Ν, Ν—ジェチル）ァミノプロピルトリエトキシシラン、 γ - (Ν, Ν—ジブ チル）ァミノプロピルトリエトキシシラン、 γ— (Ν—メチル）ァ-リノプロピルトリエトキシ シラン、 γ - (Ν—ェチル）ァ-リノプロピルトリエトキシシラン、 γ - (Ν, Ν—ジメチル )ァミノプロピルメチルジメトキシシラン、 γ— (Ν, Ν—ジェチル）ァミノプロピルメチル ジメトキシシラン、 γ— (Ν, Ν—ジブチル）ァミノプロピルメチルジメトキシシラン、 γ— (Ν—メチル）ァ-リノプロピルメチルジメトキシシラン、 Ύ — (Ν—ェチル）ァ-リノプロ ジメトキシメチルシリルイソプロピル）エチレンジァミン、メチルトリメトキシシラン、ジメチ ルジメトキシシラン、メチルトリエトキシシラン、 γ—クロ口プロピルトリメトキシシラン、へ キサメチルジシラン、ビュルトリメトキシシラン、 γ メルカプトプロピルメチルジメトキシ シラン等のシラン系カップリング剤、イソプロピルトリイソステアロイルチタネート、イソプ 口ピルトリス（ジォクチルパイロホスフェート）チタネート、イソプロピルトリ（Ν アミノエ チル—アミノエチル）チタネート、テトラオクチルビス（ジトリデシルホスフアイト）チタネ ート、テトラ（2, 2—ジァリルォキシメチル一 1—ブチル)ビス（ジトリデシル)ホスフアイ トチタネート、ビス（ジォクチルパイロホスフェート）ォキシアセテートチタネート、ビス（ ジォクチルパイロホスフェート）エチレンチタネート、イソプロピルトリオクタノィルチタネ ート、イソプロピルジメタクリルイソステアロイルチタネート、イソプロピルトリドデシルべ ンゼンスルホ-ルチタネート、イソプロピルイソステアロイルジアクリルチタネート、イソ プロピルトリ（ジォクチルホスフェート）チタネート、イソプロピルトリタミルフエ-ルチタ ネート、テトライソプロピルビス（ジォクチルホスフアイト）チタネート等のチタネート系力 ップリング剤などが挙げられ、これらの 1種を単独で用いても 2種類以上を組み合わ せて用いてもよい。
なかでも流動性、難燃性の観点からはシランカップリング剤、特に 2級アミノ基を有 するシランカップリング剤を含むのが好ま 、。 2級アミノ基を有するシランカップリン グ剤は分子内に 2級アミノ基を有するシランィ匕合物であれば特に制限はないが、たと えば、 γ—ァ-リノプロピルトリメトキシシラン、 γ—ァ-リノプロピルトリエトキシシラン 、 γーァニリノプロピルメチルジメトキシシラン、 γ—ァニリノプロピルメチルジェトキシ シラン、 γ—ァニリノプロピルェチルジェトキシシラン、 Ίーァニリノプロピルェチルジ メトキシシラン、 γ—ァニリノメチルトリメトキシシラン、 γ—ァニリノメチルトリエトキシシ ラン、 γ—ァニリノメチルメチルジメトキシシラン、 γ—ァニリノメチルメチルジェトキシ シラン、 γ—ァニリノメチルェチルジェトキシシラン、 Ίーァニリノメチルェチルジメトキ シシラン、 Ν— (ρ—メトキシフエ-ル） γ—ァミノプロピルトリメトキシシラン、 Ν— (ρ —メトキシフエニル） γ—ァミノプロピルトリエトキシシラン、 Ν— (ρ—メトキシフエ二 ル） γ—ァミノプロピルメチルジメトキシシラン、 Ν— (ρ—メトキシフエ-ル） γ ァ ミノプロピルメチルジェトキシシラン、 Ν— (ρ—メトキシフエ-ル） γ—ァミノプロピル ェチルジェトキシシラン、 Ν— (ρ—メトキシフエ-ル） γ—ァミノプロピルェチルジメ トキシシラン、 γ - (Ν—メチル）ァミノプロピルトリメトキシシラン、 γ - (Ν ェチル）ァ ミノプロピルトリメトキシシラン、 γ— (Ν ブチル）ァミノプロピルトリメトキシシラン、 γ - (Ν ベンジル）ァミノプロピルトリメトキシシラン、 γ - (Ν—メチル）ァミノプロビルト リエトキシシラン、 Ί - (Ν ェチル）ァミノプロピルトリエトキシシラン、 γ - (Ν ブチ ル）ァミノプロピルトリエトキシシラン、 γ— (Ν ベンジル）ァミノプロピルトリエトキシシ ラン、 y - (N—メチル)ァミノプロピルメチルジメトキシシラン、 y - (N ェチル)アミ ノプロピルメチルジメトキシシラン、 γ—（N ブチル）ァミノプロピルメチルジメトキシ シラン、 γ - (Ν ベンジル）ァミノプロピルメチルジメトキシシラン、 N— j8— (アミノエ チル） γ—ァミノプロピルトリメトキシシラン、 γ—（ 13—アミノエチル）ァミノプロピル トリメトキシシラン、 Ν— β— (Ν ビュルべンジルアミノエチル） γ—ァミノプロピル トリメトキシシラン等が挙げられる。なかでも下記一般式 (II)で示されるアミノシランカツ プリング剤を含むことが特に好まし 、。
[化 22]
Figure imgf000028_0001
[0106] (一般式 (II)で、 R1は水素原子、炭素数 1〜6のアルキル基及び炭素数 1〜2のアル コキシ基力 選ばれ、 R2は炭素数 1〜6のアルキル基及びフエ-ル基力 選ばれ、 R3 はメチル基又はェチル基を示し、 ηは 1〜6の整数を示し、 mは 1〜3の整数を示す。 ) カップリング剤の全配合量は、封止用エポキシ榭脂成形材料に対して 0. 037〜5 質量％であることが好ましぐ 0. 05〜4. 75質量％であることがより好ましぐ 0. 1〜2 . 5質量％であることがさらに好ましい。 0. 037質量％未満ではフレームとの接着性 が低下する傾向があり、 5質量％を超えるとパッケージの成形性が低下する傾向があ る。
[0107] 本発明の封止用エポキシ榭脂成形材料には、難燃性を向上させる観点から (G)リ ン原子を有する化合物を用いることができる。 (G)リン原子を有する化合物としては、 本発明の効果が得られれば特に制限はなぐ被覆又は無被覆の赤リン、シクロホスフ ァゼン等のリン及び窒素含有ィ匕合物、ユトリロトリスメチレンホスホン酸三カルシウム塩
、メタン一 1—ヒドロキシ一 1, 1—ジホスホン酸二カルシウム塩等のホスホン酸塩、トリ フエ-ルホスフィンオキサイド、 2- (ジフエ-ルホスフィエル）ハイドロキノン、 2,2— [ ( 2— (ジフエ-ルホスフィエル）一 1,4 フエ-レン）ビス（ォキシメチレン）]ビス一ォキシ ラン、トリー n—ォクチルホスフィンオキサイド等のホスフィン及びホスフィンオキサイド 化合物、リン酸エステル化合物などが挙げられ、これらの 1種を単独で用いても 2種 以上を組合わせて用いてもょ ヽ。
[0108] 赤リンとしては、熱硬化性榭脂で被覆された赤リン、無機化合物及び有機化合物で 被覆された赤リン等の被覆赤リンが好まし 、。
[0109] 熱硬化性榭脂で被覆された赤リンに用いられる熱硬化性榭脂としては、たとえば、 エポキシ榭脂、フエノール榭脂、メラミン榭脂、ウレタン榭脂、シアナート榭脂、尿素— ホルマリン榭脂、ァニリン ホルマリン榭脂、フラン榭脂、ポリアミド榭脂、ポリアミドイミ ド榭脂、ポリイミド榭脂等が挙げられ、これらの 1種を単独で用いても 2種以上組み合 わせて用いてもよい。また、これらの榭脂のモノマー又はオリゴマーを用いて被覆と重 合を同時に行い、重合によって製造された熱硬化榭脂が被覆されるものでもよぐ熱 硬化性榭脂は、被覆後に硬化されていてもよい。なかでも、封止用エポキシ榭脂成 形材料に配合されるベース樹脂との相溶性の観点からは、エポキシ榭脂、フエノール 榭脂及びメラミン榭脂が好ま ヽ。
[0110] 無機化合物及び有機化合物で被覆された赤リンに用いられる無機化合物としては
、たとえば、水酸化アルミニウム、水酸化マグネシウム、水酸化カルシウム、水酸化チ タン、水酸ィ匕ジルコニウム、含水酸ィ匕ジルコニウム、水酸ィ匕ビスマス、炭酸バリウム、 炭酸カルシウム、酸化亜鉛、酸化チタン、酸化ニッケル、酸化鉄等が挙げられ、これ らの 1種を単独で用いても 2種以上組み合わせて用いてもよい。なかでも、リン酸ィォ ン捕捉効果に優れる水酸ィ匕ジルコニウム、含水酸ィ匕ジルコニウム、水酸ィ匕アルミ-ゥ ム及び酸ィ匕亜鉛が好まし 、。
[0111] また、無機化合物及び有機化合物で被覆された赤リンに用いられる有機化合物と しては、たとえば、カップリング剤ゃキレート剤など表面処理に用いられる低分子量の 化合物、熱可塑性榭脂、熱硬化性榭脂等の比較的高分子量の化合物などが挙げら れ、これらの 1種を単独で用いても 2種以上組み合わせて用いてもよい。なかでも、被 覆効果の観点力 熱硬化性榭脂が好ましぐ封止用エポキシ榭脂成形材料に配合さ れるベース樹脂との相溶性の観点からエポキシ榭脂、フエノール榭脂及びメラミン榭 脂がより好ましい。
[0112] 赤リンを無機化合物及び有機化合物で被覆する場合、その被覆処理の順序は、無 機化合物で被覆した後に有機化合物で被覆しても、有機化合物で被覆した後に無 機化合物で被覆しても、両者の混合物を用いて両者を同時に被覆してもよい。また、 被覆形態は、物理的に吸着したものでも、化学的に結合したものでも、その他の形態 であってもよい。また、無機化合物と有機化合物は、被覆後に別個に存在していても 、両者の一部又は全部が結合した状態であってもよ 、。
[0113] 無機化合物及び有機化合物の量は、無機化合物と有機化合物の質量比 (無機化 合物 Z有機化合物）は、 1Z99〜99Z1が好ましぐ 10Z90〜95Z5がより好ましく 、 30Z70〜90ZlOがさらに好ましぐこのような質量比となるように無機化合物及び 有機化合物又はその原料となるモノマー、オリゴマーの使用量を調整することが好ま しい。
[0114] 熱硬化性榭脂で被覆された赤リン、無機化合物及び有機化合物で被覆された赤リ ン等の被覆赤リンの製造方法は、たとえば、特開昭 62— 21704号公報、特開昭 52 — 131695号公報等に記載された公知の被覆方法を用いることができる。また、被覆 膜の厚さは本発明の効果が得られれば特に制限はなぐ被覆は、赤リン表面に均一 に被覆されたものでも、不均一であってもよい。
[0115] 赤リンの粒径は、平均粒径 (粒度分布で累積 50質量％となる粒径）が 1〜： LOO /z m が好ましぐ 5〜50 /z mがより好ましい。平均粒径が 1 μ m未満では、成形品のリン酸 イオン濃度が高くなつて耐湿性に劣る傾向があり、 100 /z mを超えると、狭いパッドピ ツチの高集積'高密度化半導体装置に用いた場合、ワイヤの変形、短絡、切断等に よる不良が生じやすくなる傾向がある。
[0116] (G)リン原子を有する化合物のなかでも流動性の観点からは、リン酸エステル化合 物、ホスフィンオキサイドを含むことが好ましい。リン酸エステル化合物はリン酸とアル コールィ匕合物又はフエノールイ匕合物のエステルイ匕合物であれば特に制限はないが、 例えばトリメチルホスフェート、トリェチルホスフェート、トリフエ-ルホスフェート、トリク レジノレホスフェート、 トリキシレニノレホスフェート、クレジルジフエ-ノレホスフェート、キシ レニルジフエ-ルホスフェート、トリス（2, 6ジメチルフエ-ル）ホスフェート及び芳香族 縮合リン酸エステル等が挙げられる。なかでも耐加水分解性の観点からは、下記一 般式 (III)で示される芳香族縮合リン酸エステルイ匕合物を含むことが好ま Uヽ。
[化 23]
Figure imgf000031_0001
(一般式（III)で、式中の 8個の Rは炭素数 1〜4のアルキル基を示し、全て同一でも 異なっていてもよい。 Arは芳香族環を示す。 )
上記式 (III)のリン酸エステル化合物を例示すると、下記構造式 (XX)〜 (XXIV)で 示されるリン酸エステル等が挙げられる。
[化 24]
Figure imgf000032_0001
[0118] これらリン酸エステル化合物の添加量は、充填剤を除く他の全配合成分に対して、 燐原子の量で 0. 2〜3. 0質量％の範囲内であることが好ましい。 0. 2質量％ょり少 ない場合は難燃効果が低くなる傾向がある。 3. 0質量％を超えた場合は成形性、耐 湿性の低下や、成形時にこれらのリン酸エステルイ匕合物がしみ出し、外観を阻害する 場合がある。
[0119] ホスフィンオキサイドを難燃剤として用いる場合、ホスフィンオキサイドとしては下記 一般式 (IV)で示されるホスフィン化合物を含むことが好ま 、。
[化 25]
0
R1—— P—— R ,3
(IV)
R 2
[0120] (一般式 (IV)で、
Figure imgf000033_0001
R2及び R3は炭素数 1〜： L0の置換又は非置換のアルキル基、 ァリール基、ァラルキル基及び水素原子のいずれかを示し、すべて同一でも異なつ てもよい。ただしすべてが水素原子である場合を除く。 )
上記一般式 (IV)で示されるホスフィンィ匕合物の中でも、耐加水分解性の観点から は！^〜 が置換又は非置換のァリール基であることが好ましく、特に好ましくはフエ -ル基である。
[0121] ホスフィンオキサイドの配合量は封止用エポキシ榭脂成形材料に対してリン原子の 量が 0. 01-0. 2質量％であることが好ましい。より好ましくは 0. 02-0. 1質量％で あり、さらに好ましくは 0. 03〜0. 08質量％である。 0. 01質量％未満であると難燃 性が低下する傾向があり、 0. 2質量％を超えると成形性、耐湿性が低下する傾向が ある。
[0122] またシクロホスファゼンとしては主鎖骨格中に次式 (XXV)及び Z又は次式 (XXVI) を繰り返し単位として含む環状ホスファゼンィ匕合物、あるいはホスファゼン環中の燐 原子に対する置換位置が異なる次式 (XXVII)及び Z又は次式 (XXVIII)を繰り返し 単位として含む化合物等が挙げられる。
[化 26] I)
Figure imgf000034_0001
ここで、式（XXV)及び式（XXVII)中の mは 1〜10の整数で、 I^〜Rは置換基を有 しても良い炭素数 1〜12のアルキル基、ァリール基及び水酸基から選ばれ、全て同 一でも異なっていても良い。 Aは炭素数 1〜4のアルキレン基又はァリレン基を示す。 式 (XXVI)及び式 (XXVIII)中の nは 1〜10の整数で、 R5〜R8は置換基を有しても良 い炭素数 1〜12のアルキル基又はァリール基力も選ばれ、全て同一でも異なってい ても良ぐ Aは炭素数 1〜4のアルキレン基又はァリレン基を示す。また、式中 m個の R\ R2、 R3、 R4は m個全てが同一でも異なっていても良ぐ n個の R5、 R6、 R R8は n 個全てが同一でも異なっていても良い。上記式 (XXV)〜式 (xxvm)において、尺1〜
R8で示される置換基を有しても良 ヽ炭素数 1〜 12のアルキル基又はァリール基とし ては特に制限はないが、例えばメチル基、ェチル基、プロピル基、イソプロピル基、ブ チル基、イソブチル基、 sec ブチル基、 tert ブチル基等のアルキル基、フエニル 基、 1 ナフチル基、 2—ナフチル基等のァリール基、 o トリル基、 m トリル基、 p— 卜リル基、 2, 3 キシリル基、 2, 4 キシリル基、 o—タメ-ル基、 m—タメ-ル基、 p— タメ二ル基、メシチル基等のアルキル基置換ァリール基、ベンジル基、フエネチル基 等のァリール基置換アルキル基などが挙げられ、さらにこれらに置換する置換基とし ては、アルキル基、アルコキシル基、ァリール基、水酸基、アミノ基、エポキシ基、ビ- ル基、ヒドロキシアルキル基、アルキルアミノ基等が挙げられる。 [0124] これらの中で、エポキシ榭脂成形材料の耐熱性、耐湿性の観点からはァリール基 が好ましぐより好ましくはフエニル基もしくはヒドロキシフエ-ル基である。
[0125] また、上記式（XXV)〜式（XXVIII)中の Aで示される炭素数 1〜4のアルキレン基又 はァリレン基としては特に制限はないが、例えばメチレン基、エチレン基、プロピレン 基、イソプロピレン基、ブチレン基、イソブチレン基、フエ-レン基、トリレン基、キシリレ ン基、ナフチレン基及びビフエ-レン基等が挙げられ、エポキシ榭脂成形材料の耐 熱性、耐湿性の観点からはァリレン基が好ましぐ中でもフエ-レン基がより好ましい。
[0126] 環状ホスファゼン化合物は、上記式（XXV)〜式（XXVIII)の!、ずれかの重合物、上 記式（XXV)と上記式（XXVI)との共重合物、又は上記式（XXVII)と上記式（XXVIII) との共重合物が挙げられる力 共重合物の場合、ランダム共重合物でも、ブロック共 重合物でも、交互共重合物のいずれでも良い。その共重合モル比 mZnは特に限定 するものではないが、エポキシ榭脂硬化物の耐熱性や強度向上の観点から 1Z0〜 1Z4が好ましぐ 1ΖΟ〜： LZ1. 5がより好ましい。また、重合度 m+nは 1〜20であり 、好ましくは 2〜8、より好ましくは 3〜6である。
[0127] 環状ホスファゼンィヒ合物として好まし!/、ものを例示すると、次式 (XXIX)の重合物、 次式 (XXX)の共重合物等が挙げられる。
[化 27]
Figure imgf000035_0001
[0128] (ここで、一般式 (XXIX)中の nは、 0〜9の整数で、！^〜 はそれぞれ独立に水素原 子又は水酸基を示す。 )
[化 28]
Figure imgf000036_0001
[0129] ここで、上記一般式（XXX)中の m、 nは、 0〜9の整数で、 I^〜Rはそれぞれ独立 に水素原子または水酸基力 選ばれる。また、上記一般式 (XXX)で示される環状ホ スファゼンィ匕合物は、次に示す m個の繰り返し単位 (a)と n個の繰り返し単位 (b)を交 互に含むもの、ブロック状に含むもの、ランダムに含むもののいずれであってもかまわ ないが、ランダムに含むものが好ましい。
[化 29]
Figure imgf000036_0002
[0130] (上記一般式 (a)中の R1 !^はそれぞれ独立に水素原子または水酸基力も選ばれ る。）
中でも、上記式 (XXIX)で nが 3〜6の重合体を主成分とするものや、上記式 (XXX) で 〜1^6が全て水素原子又は 1つが水酸基であり、 nZmが 1Z2〜1Z3で、 n+m力 S 3〜6の共重合体を主成分とするものが好ましい。また、市販のホスファゼンィ匕合物と しては、 SPE— 100 (大塚化学株式会社製商品名）等が入手可能である。
[0131] (G)リン原子を有する化合物の配合量は特に制限はないが、 CO無機充填剤を除く 他の全配合成分に対して、リン原子の量で 0. 01〜50質量％が好ましぐ 0. 1〜10 質量％がより好ましぐ 0. 5〜3質量％がさらに好ましい。配合量が 0. 01質量％未満 では難燃性が不十分となる傾向があり、 50質量％を超えると成形性、耐湿性が低下 する傾向がある。
[0132] 本発明にお 、ては離型性の観点から (H)重量平均分子量が 4, 000以上の直鎖 型酸化ポリエチレン、および（I)炭素数 5〜30の α—ォレフィンと無水マレイン酸との 共重合物を炭素数 5〜25の一価のアルコールでエステル化した化合物をさらに含有 させてもよい。（Η)重量平均分子量が 4, 000以上の直鎖型酸化ポリエチレンは、離 型剤として働くものである。ここで、直鎖型ポリエチレンとは、側鎖アルキル鎖の炭素 数が主鎖アルキル鎖の炭素数の 10%程度以下のポリエチレンをいい、一般的には、 針入度が 2以下のポリエチレンとして分類される。
[0133] また、酸化ポリエチレンとは、酸価を有するポリエチレンをいう。
[0134] (Η)成分の重量平均分子量は、離型性の観点力も 4, 000以上であることが好まし ぐ接着性、金型'パッケージの汚れ防止の観点からは 30, 000以下であることが好 まし <、 5, 000〜20, 000力より好まし <、 7, 000〜15, 000力 ^さらに好まし!/、。ここ で、重量平均分子量は、高温 GPC (ゲルパーミエーシヨンクロマトグラフィ）で測定し た値をいう。なお、本発明での高温 GPC測定方法は以下のとおりである。
[0135] 測定器: Waters社製高温 GPC
(溶媒：ジクロ口ベンゼン
温度： 140°C、
標準物質:ポリスチレン）
カラム：ポリマーラボラトリーズ社製商品名 PLgel MIXED- B
10 (7. 5mm X 300mm) X 2本
流量： 1. OmlZ分 (試料濃度： 0. 3wt/vol%)
(注入量： 100 1)
また、（H)成分の酸価は、特に制限はないが、離型性の観点から 2〜50mgZKO Hであることが好ましぐ 10〜35mgZKOHがより好ましい。
[0136] (H)成分の配合量は、特に制限はないが、（A)エポキシ榭脂に対して 0. 5〜10質 量％が好ましぐ 1〜5質量％がより好ましい。配合量が 0. 5質量％未満では離型性 が低下する傾向にあり、 10質量％を超えると接着性及び金型'パッケージ汚れの改 善効果が不充分となる場合がある。
[0137] 本発明にお!/、て用いられる（I)炭素数 5〜30の ocーォレフインと無水マレイン酸と の共重合物を炭素数 5〜25の一価のアルコールでエステルイ匕したィ匕合物も、離型剤 として働くもので、（H)成分の直鎖型酸化ポリエチレンおよび (A)成分のエポキシ榭 脂の 、ずれとも相溶性が高く、接着性の低下や金型 ·パッケージ汚れを防ぐ効果が ある。
[0138] (I)成分に用いられる炭素数 5〜30の α—ォレフインとしては、特に制限はないが、 たとえば、 1—ペンテン、 1—へキセン、 1—ヘプテン、 1—オタテン、 1—ノネン、 1—デ セン、 1—ゥンデセン、 1—ドデセン、 1—トリデセン、 1—テトラデセン、 1 ペンタデセ ン、 1一へキサデセン、 1一へプタデセン、 1ーォクタデセン、 1 ノナデセン、 1 エイ コセン、 1—ドコセン、 1ートリコセン、 1—テトラコセン、 1—ペンタコセン、 1—へキサコ セン、 1一へプタコセン等の直鎖型 α—ォレフイン、 3—メチルー 1ーブテン、 3, 4— ジメチルーペンテン、 3—メチル 1—ノネン、 3, 4 ジメチルーオタテン、 3 ェチル 1ードデセン、 4ーメチルー 5 ェチルー 1ーォクタデセン、 3, 4, 5 トリェチルー 1—1 エイコセン等の分岐型 α—ォレフイン等が挙げられ、これらを単独で用いても
2種以上を組み合わせて用いてもよい。中でも炭素数 10〜25の直鎖型 α ォレフィ ンが好ましぐ 1—エイコセン、 1—ドコセン、 1—トリコセン等の炭素数 15〜25の直鎖 型 α—ォレフィンがより好ましい。
[0139] (I)成分に用いられる炭素数 5〜25の一価のアルコールとしては、特に制限はない 1S たとえば、ァミルアルコール、イソアミルアルコール、へキシルアルコール、へプチ ルアルコール、ォクチルアルコール、力プリルアルコール、ノ-ルアルコール、デシル アルコール、ゥンデシルアルコール、ラウリルアルコール、トリデシルアルコール、ミリ スチノレアノレコーノレ、ペンタデシノレアノレコーノレ、セチノレアノレコーノレ、ヘプタデシノレアノレ コール、ステアリルアルコール、ノナデシルアルコール、エイコシルアルコール等の直 鎖型または分岐型の脂肪族飽和アルコール、へキセノール、 2—へキセン 1ーォ ール、 1一へキセンー3 オール、ペンテノール、 2—メチルー 1 ペンテノール等の 直鎖型または分岐型の脂肪族不飽和アルコール、シクロペンタノール、シクロへキサ ノール等の脂環式アルコール、ベンジルアルコール、シンナミルアルコール等の芳香 族アルコール、フルフリルアルコール等の複素環式アルコール等が挙げられ、これら を単独で用いても 2種以上を組み合わせて用いてもよい。中でも炭素数 10〜20の直 鎖型アルコールが好ましぐ炭素数 15〜20の直鎖型脂肪族飽和アルコールがより好 ましい。
[0140] 本発明の（I)成分における炭素数 5〜30の α—ォレフインと無水マレイン酸との共 重合物は、特に制限はないが、たとえば、下記一般式 (XXXI)で示される化合物、下 記一般式 (XXXII)で示される化合物等が挙げられ、市販品としては、 1—エイコセン、 1 -ドコセンおよび 1—テトラコセンを原料としたニッサンエレクトール WPB— 1 (日本 油脂株式会社製商品名）等が入手可能である。
[化 30]
iXXXH)
Figure imgf000039_0001
[0141] (一般式 (XXXI)および (XXXII)で、 Rは炭素数 3〜28の一価の脂肪族炭化水素基 から選ばれ、 nは 1以上の整数、 mは正の数を示す。 )
上記一般式（XXXI)および（XXXII)中の mは、無水マレイン酸 1モルに対し α— ォレフィンを何モル共重合させたかを示し、特に制限はないが、 0. 5〜10が好ましく 、 0. 9〜1. 1力より好まし!/ヽ。
[0142] (I)成分の共重合物の製造方法としては、特に制限はなぐ一般的な共重合法を用 いることができる。反応には、 OC一才レフインと無水マレイン酸が可溶な有機溶媒等を 用いてもよい。有機溶媒としては特に制限はないが、トルエンが好ましぐアルコール 系溶媒、エーテル系溶媒、アミン系溶媒等も使用できる。反応温度は、使用する有機 溶媒の種類によっても異なる力 反応性、生産性の観点から、 50〜200°Cとすること が好ましぐ 80〜120°Cがより好ましい。反応時間は、共重合物が得られれば特に制 限はないが、生産性の観点から 1〜30時間とするのが好ましぐ 2〜15時間とするの 力 り好ましぐ 4〜： LO時間とするのがさらに好ましい。反応終了後、必要に応じて、 加熱減圧下等で未反応分、溶媒等を除去することができる。その条件は、温度を 10 0〜220。C、より好ましくは 120〜180。C、圧力を 13. 3 X 103Pa以下、より好ましくは 8 X 103Pa以下、時間を 0. 5〜： LO時間とすることが好ましい。また、反応には、必要 に応じてアミン系触媒、酸触媒等の反応触媒を加えてもよい。反応系の pHは、 1〜1 0程度とするのが好ましい。
[0143] (I)成分の共重合物を炭素数 5〜25の一価のアルコールでエステル化する方法と しては、特に制限はなぐ共重合物に一価のアルコールを付加反応させる等の一般 的な方法を用いることができる。共重合物と一価のアルコールの反応モル比は、特に 制限はなぐ任意に設定可能であるが、この反応モル比を調整することによって親水 性の度合いをコントロールすることができるので、目的の封止用エポキシ榭脂成形材 料に合わせて適宜設定することが好ましい。反応には、共重合物が可溶な有機溶媒 等を用いてもよい。有機溶媒としては特に制限はないが、トルエンが好ましぐアルコ ール系溶媒、エーテル系溶媒、アミン系溶媒等も使用できる。反応温度は、使用する 有機溶媒の種類によっても異なる力 反応性、生産性の観点から、 50〜200°Cとす ることが好ましぐ 80〜120°Cがより好ましい。反応時間は、特に制限はないが、生産 性の観点から 1〜30時間とするのが好ましぐ 2〜15時間とするのがより好ましぐ 4 〜： LO時間とするのがさらに好ましい。反応終了後、必要に応じて、加熱減圧下等で 未反応分、溶媒等を除去することができる。その条件は、温度を 100〜220°C、より 好ましくは 120〜180°C、圧力を 13. 3 X 103Pa以下、より好ましくは 8 X 103Pa以下 、時間を 0. 5〜： LO時間とすることが好ましい。また、反応には、必要に応じてアミン系 触媒、酸触媒等の反応触媒を加えてもよい。反応系の pHは、 1〜10程度とするのが 好ましい。
[0144] (I)成分の α—ォレフインと無水マレイン酸との共重合物を一価のアルコールでェ ステルイ匕した化合物としては、たとえば、下記の式 (a)または (b)で示されるジエステ ル、および式 (c)〜(f)で示されるモノエステルカゝら選ばれる 1種以上を繰り返し単位 として構造中に含む化合物等が挙げられる。また、式 (g)または (h)で示されるノンェ ステルを含んでいても、無水マレイン酸が開環して二つの COOH基を有する構造 を含んでいてもよい。このような化合物としては、
(1)主鎖骨格が式 (a) (f)の 、ずれか 1種単独で構成されるもの、
(2)主鎖骨格中に式 (a) (f)の 、ずれか 2種以上をランダムに含むもの、規則的に 含むもの、ブロック状に含むもの、
(3)主鎖骨格中に式 (a) (f)の 、ずれか 1種または 2種以上と式 (g)および (h)の少 なくとも一方とをランダムに含むもの、規則的に含むもの、ブロック状に含むもの、 等が挙げられ、これらを単独で用いても 2種以上を組み合わせて用いてもょ 、。 また、（4)主鎖骨格中に式 (g)および (h)をランダムに含むもの、規則的に含むもの 、ブロック状に含むもの、と
(5)主鎖骨格が式 (g)または (h)の 、ずれか単独で構成されるもの、
との、いずれかまたは両方を含んでいてもよい。
[化 31]
Figure imgf000041_0001
[化 32]
Figure imgf000041_0002
[化 33]
Figure imgf000042_0001
[0146] (上記式 (a)〜(h)で、 R1は炭素数 3〜28の一価の脂肪族炭化水素基、 R2は炭素数 5〜25の一価の炭化水素基力 選ばれ、 mは正の数を示す。 )
上記式（a)〜（h)中の mは、無水マレイン酸 1モルに対し α—ォレフインを何モル共 重合させたかを示し、特に制限はないが、 0. 5〜10カ 子ましく、0. 9〜1. 1がより好 ましい。
[0147] (I)成分のモノエステルイ匕率は、（Η)成分との組み合わせにより適宜選択可能であ る力 離型性の観点から 20%以上とすることが好ましぐ（I)成分としては式 (c)〜(f) で示されるモノエステルのいずれ力 1種または 2種以上を併せて 20モル％以上含む 化合物が好ましぐ 30モル％以上含む化合物がより好ましい。
[0148] また、（I)成分の重量平均分子量は、金型'パッケージ汚れ防止及び成形性の観点 力ら 5, 000〜100, 000とすること力 S好ましく、 10, 000〜70, 000力 Sより好ましく、 1 5, 000-50, 000がさらに好ましい。重量平均分子量が 5, 000未満では金型 'パッ ケージ汚れを防ぐ効果が低い傾向にあり、 100, 000を超えると化合物の軟化点が 上昇し、混練性等に劣る傾向がある。ここで、重量平均分子量は、常温 GPCで測定 した値をいう。本発明での常温 GPCによる重量平均分子量の測定方法は以下のと おりである。
[0149] 測定器:島津製作所製 LC— 6C
カラム： shodex KF-802.5 + KF-804+KF-806
溶媒： THF (テトラヒドロフラン）
温度：室温（25°C)
標準物質:ポリスチレン
流量： l.OmlZ分 (試料濃度約 0.2wtZvol%) 注入量： 200 /z l
(I)成分の配合量は、特に制限はないが、（A)エポキシ榭脂に対して 0. 5〜10質 量％が好ましぐ 1〜5質量％がより好ましい。配合量が 0. 5質量％未満では離型性 が低下する傾向にあり、 10質量％を超えると耐リフロー性が低下する傾向にある。
[0150] 耐リフロー性や金型'パッケージ汚れの観点から、本発明における離型剤である (H )成分および (I)成分の少なくとも一方は、本発明のエポキシ榭脂成形材料の調製時 に (A)成分のエポキシ榭脂の一部または全部と予備混合することが好ま 、。 (H) 成分および (I)成分の少なくとも一方を (A)成分と予備混合すると、これらのベース榭 脂中での分散性が上がり、耐リフロー性の低下や金型'パッケージ汚れを防ぐ効果が ある。
[0151] 予備混合の方法は、特に制限するものではなぐ（H)成分および (I)成分の少なく とも一方が (A)成分のエポキシ榭脂中に分散されれば 、かなる方法を用いてもょ 、 力 たとえば、室温〜 220°Cで 0. 5〜20時間撹拌する等の方法が挙げられる。分散 性、生産性の観点からは、温度を 100〜200°C、より好ましくは 150〜170°C、撹拌 時間を 1〜10時間、より好ましくは 3〜6時間とすることが好ましい。
[0152] 予備混合するための（H)成分および (I)成分の少なくとも一方は、（A)成分の全量 と予備混合してもよいが、一部と予備混合することでも十分な効果が得られる。その 場合、予備混合する (A)成分の量は、（A)成分の全量の 10〜50質量％とすることが 好ましい。
[0153] また、 (H)成分と (I)成分との ヽずれか一方を (A)成分と予備混合することで、分散 性向上の効果が得られるが、 (H)成分および (I)成分の両方を (A)成分と予備混合 した方がより効果が高く好ましい。予備混合する場合の 3成分の添加順序は、特に制 限はなぐ全てを同時に添加混合しても、（H)成分と (I)成分とのいずれか一方を先 に (A)成分と添加混合し、その後残りの成分を添加混合してもよ 、。
[0154] 本発明の封止用エポキシ榭脂成形材料には、さらに難燃性を向上する目的で従来 公知のノンハロゲン、ノンアンチモンの難燃剤を必要に応じて配合することができる。 たとえばメラミン、メラミン誘導体、メラミン変性フエノール榭脂、トリアジン環を有する 化合物、シァヌル酸誘導体、イソシァヌル酸誘導体等の窒素含有化合物、水酸化ァ ルミ二ゥム、錫酸亜鉛、硼酸亜鉛、モリブデン酸亜鉛、ジシクロペンタジェニル鉄等の 金属元素を含む化合物などが挙げられ、これらの 1種を単独で用いても 2種以上を組 合わせて用いてもよい。
[0155] また、本発明の封止用エポキシ榭脂成形材料には、 IC等の半導体素子の耐湿性 及び高温放置特性を向上させる観点力ゝら陰イオン交換体を添加することもできる。陰 イオン交換体としては特に制限はなぐ従来公知のものを用いることができる力 たと えば、ハイド口タルサイト類や、マグネシウム、アルミニウム、チタン、ジルコニウム、ビ スマス等力 選ばれる元素の含水酸ィ匕物等が挙げられ、これらを単独又は 2種以上 を組み合わせて用いることができる。なかでも、下記組成式 (ΧΧΧΙΠ)で示されるハイ ドロタルサイトが好ましい。
[0156] (化 34)
Mg Ο (ΧΧΧΙΙΙ)
Figure imgf000044_0001
(上記式（XXXIII)中 0<χ≤0.5、 mは正の数）
さらに、本発明の封止用エポキシ榭脂成形材料には、その他の添加剤として、高級 脂肪酸、高級脂肪酸金属塩、エステル系ワックス、ポリオレフイン系ワックス、ポリェチ レン、酸ィ匕ポリエチレン等の離型剤、カーボンブラック等の着色剤、シリコーンオイル やシリコーンゴム粉末等の応力緩和剤などを必要に応じて配合することができる。
[0157] 本発明の封止用エポキシ榭脂成形材料は、各種原材料を均一に分散混合できる のであれば、いかなる手法を用いても調製できるが、一般的な手法として、所定の配 合量の原材料をミキサー等によって十分混合した後、ミキシングロール、押出機、ら いかい機、プラネタリミキサ等によって混合又は溶融混練した後、冷却し、必要に応 じて脱泡、粉砕する方法等を挙げることができる。また、必要に応じて成形条件に合う ような寸法及び質量でタブレツトイ匕してもょ 、。
[0158] 本発明の封止用エポキシ榭脂成形材料を封止材として用いて、半導体装置等の 電子部品装置を封止する方法としては、低圧トランスファ成形法が最も一般的である 力 インジェクション成形法、圧縮成形法等も挙げられる。デイスペンス方式、注型方 式、印刷方式等を用いてもよい。
[0159] 本発明で得られる封止用エポキシ榭脂成形材料により封止した素子を備えた本発 明の電子部品装置としては、リードフレーム、配線済みのテープキャリア、配線板、ガ ラス、シリコンウェハ等の支持部材ゃ実装基板に、半導体チップ、トランジスタ、ダイ オード、サイリスタ等の能動素子、コンデンサ、抵抗体、コイル等の受動素子等の素 子を搭載し、必要な部分を本発明の封止用エポキシ榭脂成形材料で封止した、電子 部品装置等が挙げられる。
[0160] ここで、実装基板としては特に制限するものではなぐたとえば、有機基板、有機フ イルム、セラミック基板、ガラス基板等のインターポーザ基板、液晶用ガラス基板、 M CM (Multi Chip Module)用基板、ハイブリット IC用基板等が挙げられる。
[0161] このような素子を備えた電子部品装置としては、たとえば半導体装置が挙げられ、 具体的には、リードフレーム (アイランド、タブ)上に半導体チップ等の素子を固定し、 ボンディングパッド等の素子の端子部とリード部をワイヤボンディングやバンプで接続 した後、本発明の封止用エポキシ榭脂成形材料を用いてトランスファ成形などにより 封止してなる、 DIP (Dual Inline Package)、 PLCC (Plastic Leaded Chip C arrier)、 QFP (Quad Flat Package)、 SOP (Small Outline Package)、 SOJ (Small Outline J— lead package)、 TSOP (Tnm Small Outline Package ) , TQFP (Thin Quad Flat Package)等の榭脂封止型 IC、テープキャリアにリ ードボンディングした半導体チップを、本発明の封止用エポキシ榭脂成形材料で封 止した TCP (Tape Carrier Package)、配線板やガラス上に形成した配線に、ワイ ャボンディング、フリップチップボンディング、はんだ等で接続した半導体チップを、 本発明の封止用エポキシ榭脂成形材料で封止した COB (Chip On Board)、 CO G (Chip On Glass)等のベアチップ実装した半導体装置、配線板やガラス上に形 成した配線に、ワイヤボンディング、フリップチップボンディング、はんだ等で接続した 半導体チップ、トランジスタ、ダイオード、サイリスタ等の能動素子及び Z又はコンデ ンサ、抵抗体、コイル等の受動素子を、本発明の封止用エポキシ榭脂成形材料で封 止したハイブリッド K、 MCM (Multi Chip Module)マザ一ボード接続用の端子 を形成したインターポーザ基板に半導体チップを搭載し、バンプまたはワイヤボンデ イングにより半導体チップとインターポーザ基板に形成された配線を接続した後、本 発明の封止用エポキシ榭脂成形材料で半導体チップ搭載側を封止した BGA (Ball Grid Array)、 CSP (Chip Size Package)、 MCP (Multi Chip Package) などが挙げられる。また、これらの半導体装置は、実装基板上に素子が 2個以上重な つた形で搭載されたスタックド (積層）型パッケージであっても、 2個以上の素子を一 度に封止用エポキシ榭脂成形材料で封止した一括モールド型パッケージであっても よい。
実施例
[0162] 次に実施例により本発明を説明するが、本発明の範囲はこれらの実施例に限定さ れるものではない。
[0163] (実施例用水酸ィ匕マグネシウムの合成例）
(1)水酸ィ匕マグネシウム 1
原料となる水酸ィ匕マグネシウム lOOgを懸濁させた水溶液 2リットルに水酸化リチウ ム 150gを攪拌しながら添加し、水酸化リチウムを完全に溶解させた。この水懸濁液を ミキサーにて湿式粉砕した後、オートクタレーブに移し、 200°C/1時間加熱処理した 。その後、室温まで冷却した後、ろ過にて分離、水洗、乾燥して水酸ィ匕マグネシウム 1 を得た。
[0164] (2)水酸化マグネシウム 2
水酸化リチウムの添加量を 300gとした以外は (1)と同様にして水酸ィ匕マグネシウム 2 を得た。
[0165] (3)水酸化マグネシウム 3
水酸化リチウムの添加量を 50gとした以外は (1)と同様にして水酸ィ匕マグネシウム 3 を得た。
[0166] (4)水酸化マグネシウム 4
lOOgの水酸化マグネシウム 1をケィ酸ソーダ lg、塩化アルミニウム lgを溶解した水 溶液 2リットルに加え、 80°C/1時間攪拌した後、ろ過にて分離、水洗、乾燥して水酸 化マグネシウム 4を得た。
[0167] (5)水酸化マグネシウム 5
ケィ酸ソーダ 0.05g、塩ィ匕アルミニウム 0.05gとした以外は (4)と同様にして水酸ィ匕マ グネシゥム 5を得た。 [0168] (6)水酸化マグネシウム 6
ケィ酸ソーダ 15g、塩ィ匕アルミニウム 15gとした以外は (4)と同様にして水酸ィ匕マグネ シゥム 6を得た。
[0169] (7)水酸化マグネシウム 7
BET比表面積 0.5m2/g、平均粒径 8 mの水酸化マグネシウムをそのまま水酸化 マグネシウム 7として用いた。
[0170] (8)水酸化マグネシウム 8
BET比表面積 8m2/g、平均粒径 0.5 mの水酸化マグネシウムをそのまま水酸化 マグネシウム 7として用いた。
[0171] 合成した各種水酸化マグネシウムの処理比率を表 1に示す。
[表 1] 表 1 各種水酸化マグネシウム
Figure imgf000047_0001
[0172] (離型剤の合成例）
aーォレフインと無水マレイン酸との共重合物として 1 エイコセン、 1ードコセンお よび 1ーテトラコセンの混合物と無水マレイン酸との共重合物（日本油脂株式会社製 商品名ニッサンエレクトール WPB— 1)、一価のアルコールとしてステアリルアルコー ルを用い、これらをトルエンに溶解して 100°Cで 8時間反応させた後、 160°Cまで段 階的に昇温しながらトルエンを除去し、さらに減圧下 160°Cで 6時間反応させて未反 応分を除去し、重量平均分子量 34, 000、モノエステル化率 70モル％のエステル化 化合物（(1)成分:離型剤 3)を得た。ここで、重量平均分子量は、溶媒として THF (テ トラヒドロフラン)を用いて GPCで測定した値である。
(実施例 1〜19、比較例 1〜8)
エポキシ榭脂として、エポキシ当量 196、融点 106°Cのビフエ-ル型エポキシ榭脂（ ジャパンエポキシレジン株式会社製商品名ェピコート YX— 4000H) (エポキシ榭脂
1)、エポキシ当量 245、融点 110°Cの硫黄原子含有エポキシ榭脂 (東都化成株式会 社製商品名 YSLV— 120TE) (エポキシ榭脂 2)、エポキシ当量 266、軟化点 67°C の β—ナフトール'ァラルキル型エポキシ榭脂 (東都化成株式会社製商品名 ESN— 175) (エポキシ榭脂 3)及びエポキシ当量 195、軟化点 65°Cの o—クレゾールノボラ ック型エポキシ榭脂 (住友ィ匕学工業株式会社製商品名 ESCN— 190) (エポキシ榭 脂 4)、
硬化剤として軟化点 70°C、水酸基当量 175のフエノール'ァラルキル榭脂（三井化学 株式会社製商品名ミレックス XLC— 3L) (硬化剤 1)、軟化点 80°C、水酸基当量 199 のビフエ-ル 'ァラルキル榭脂（明和化成株式会社製商品名 MEH— 7851) (硬化剤
2)及び軟ィ匕点 80°C、水酸基当量 106のフエノールノボラック榭脂（明和化成株式会 社製商品名 H— 1) (硬化剤 3)、
硬化促進剤としてトリフエニルホスフィン (硬化促進剤 1)、トリフエ-ルホスフィンと 1, 4 —ベンゾキノンの付加物（硬化促進剤 2)及びトリブチルホスフィンと 1, 4—ベンゾキノ ンの付加物 (硬化促進剤 3)、
カップリング剤として γ—グリシドキシプロピルトリメトキシシラン (エポキシシラン）、 2 級アミノ基を含有するシランカップリング剤として γ—ァ-リノプロピルトリメトキシシラ ン（ァニリノシラン）、
難燃剤として上記表 1に示す各種水酸ィ匕マグネシウム (水酸ィ匕マグネシウム 1〜8)、 酸化亜鉛、芳香族縮合リン酸エステル (大八化学工業株式会社製商品名 ΡΧ— 200 )、トリフエ-ルホスフィンオキサイド、三酸化アンチモン及びエポキシ当量 397、軟化 点 69°C、臭素含量 49質量％のビスフヱノール A型ブロム化エポキシ榭脂 (東都化成 株式会社製商品名 YDB— 400)、
無機充填剤として平均粒径 14. 5 m、比表面積 2. 8m2Zgの球状溶融シリカ、 その他の添加剤としてカルナバワックス（離型剤 1)、重量平均分子量 8, 800、針入 度 1、酸価 30mgZKOHの直鎖型酸ィ匕ポリエチレン（ (H)成分：離型剤 2：クラリアン トネ土製商品名 PED153)、上記で調製した (I)成分 (離型剤 3)、及びカーボンブラック (三菱ィ匕学株式会社製商品名 MA— 100)をそれぞれ表 2〜表 5に示す質量部で配 合し、混練温度 80°C、混練時間 10分の条件でロール混練を行い、実施例 1〜19、 比較例 1〜8を作製した。
[表 2] 表 2 配合組成 1
Figure imgf000049_0001
[表 3] 表 3 配合組成 2
Figure imgf000050_0001
[表 4]
表 4 配合組成 3
Figure imgf000051_0001
[表 5]
表 5 B£合組成 4
Figure imgf000052_0001
[0174] 作製した実施例 1〜19、比較例 1〜8の封止用エポキシ榭脂成形材料の特性を、 次の各試験により求めた。結果を表 6〜表 9に示す。
[0175] (1)スパイラルフロー
EMMI— 1— 66に準じたスパイラルフロー測定用金型を用いて、封止用エポキシ 榭脂成形材料をトランスファ成形機により、金型温度 180°C、成形圧力 6. 9MPa、硬 化時間 90秒の条件で成形し、流動距離 (cm)を求めた。
[0176] (2)熱時硬度 封止用エポキシ榭脂成形材料を上記（1)の成形条件で直径 50mm X厚さ 3mmの 円板に成形し、成形後直ちにショァ D型硬度計を用いて測定した。
[0177] (3)難燃性
厚さ 1Z16インチの試験片を成形する金型を用いて、封止用エポキシ榭脂成形材 料を上記（1)の成形条件で成形して、さらに 180°Cで 5時間後硬化を行い、 UL- 94 試験法に従って難燃性を評価した。
[0178] (4)耐酸性
8mm X 10mm X O. 4mmのシリコンチップを搭載した外开寸法 20mm X 14mm X 2mmの 80ピンフラットパッケージ (QFP)を、封止用エポキシ榭脂成形材料を用い て上記（3)の条件で成形、後硬化して作製し、半田メツキ処理を行い、表面の腐食の 度合いを目視で観察した。
[0179] (5)せん断離型性
縦 50mm X横 35mm X厚さ 0. 4mmのクロムめつきステンレス板を挿入し、この上 に直径 20mmの円板を成形する金型を用いて、封止用エポキシ榭脂成形材料を上 記条件で成形し、成形後直ちに該ステンレス板を引き抜!、て最大引き抜き力を記録 した。これを同一のステンレス板に対して連続で 10回繰り返し、 2回目から 10回目ま での引き抜き力の平均値を求めて評価した。
[0180] (6)耐リフロー性
8mm X 10mm X O. 4mmのシリコンチップを搭載した外开寸法 20mm X 14mm X 2mmの 80ピンフラットパッケージ (QFP)を、封止用エポキシ榭脂成形材料を用い て上記（3)の条件で成形、後硬化して作製し、 85°C、 85%RHの条件で加湿して所 定時間毎に 240°C、 10秒の条件でリフロー処理を行い、クラックの有無を観察し、試 験パッケージ数（5個）に対するクラック発生パッケージ数で評価した。
[0181] (7)耐湿性
5 μ m厚の酸化膜上に線幅 10 m、厚さ 1 mのアルミ配線を施した 6mm X 6mm X O. 4mmのテスト用シリコンチップを搭載した外形寸法 20mm X 14mm X 2. 7mm の 80ピンフラットパッケージ (QFP)を、封止用エポキシ榭脂成形材料を用いて上記（ 3)の条件で成形、後硬化して作製し、前処理を行った後、加湿して所定時間毎にァ ルミ配線腐食による断線不良を調べ、試験パッケージ数（10個）に対する不良パッケ ージ数で評価した。
[0182] なお、前処理は 85°C、 85%RH、 72時間の条件でフラットパッケージを加湿後、 21 5°C、 90秒間のベーパーフェーズリフロー処理を行った。その後の加湿は 0. 2MPa 、 121°Cの条件で行った。
[0183] (8)高温放置特性
5 μ m厚の酸化膜上に線幅 10 m、厚さ 1 mのアルミ配線を施した 5mm X 9mm X O. 4mmのテスト用シリコンチップを、部分銀メツキを施した 42ァロイのリードフレー ム上に銀ペーストを用いて搭載し、サーモニック型ワイヤボンダにより、 200°Cでチッ プのボンディングパッドとインナリードを Au線にて接続した 16ピン型 DIP (Dual Inli ne Package)を、封止用エポキシ榭脂成形材料を用いて上記（3)の条件で成形、 後硬化して作製して、 200°Cの高温槽中に保管し、所定時間毎に取り出して導通試 験を行い、試験パッケージ数（10個）に対する導通不良パッケージ数で、高温放置 特性を評価した。
[表 6] 表 6 封止材物性 1
剛
特性
1 2 3 4 5 6 7 8 難燃性 総残炎時間 （S) 1 5 20 9 12 29 13 8 6
判定 V-0 V-0 V-0 V-0 V-0 V-0 V-0 V-0
JA' i w- (cm) 1 24 138 1 33 129 1 35 1 28 1 22 129 熱時硬度 (Sho reD) 74 76 78 76 80 78 72 70 耐酸性 〇 〇 ◎ ◎ ◎ 〇 〇 〇 離型性 4. 2 3. 9 3. 2 3. 8 3. 0 3. 8 4. 2 5. 0 酎リフ Q-性 48h 0/5 0/5 0/5 0/5 0/5 0/5 0/5 0/5
72h 0/5 0/5 0/5 0/5 0/5 0/5 0/5 0/5
96h 0/5 0/5 0/5 0/5 0/5 1 /5 0/5 0/5
168h 5/5 3/5 1/5 4/5 3/5 5/5 5/5 1/5 耐湿性 l OOh 0/10 0/10 0/10 0/10 0/10 0/10 0/10 0/10
500h 0/10 0/10 0/10 0/10 0/10 0/10 0/10 0/10
1000h 0/10 0/10 0/10 0/10 0/10 0/10 0/10 0/10
1500h 0/10 0/10 0/10 0/10 0/10 0/10 0/10 1/10
S温放置特性 500 0/10 0/10 0/10 0/10 0/10 0/10 0/10 0/10
画 h 0/10 0/10 0/10 0/10 0/10 0/10 0/10 0/10
1500h 0/10 0/10 0/10 0/10 0/10 0/10 0/10 0/10
2000h 0/10 0/10 0/10 0/10 0/10 0/10 0/10 0/10 [表 7] 表 7 封止材物性 2
Figure imgf000055_0001
[表 8] 表 8 封止材物性 3
実施例 特性
17 18 19 難燃性 総残炎時間 （S) 48 0 17
判定 V-0 V-0 V-0 ス Λ·ィラルフ口- (cm) 133 102 128 熱時硬度 (Sho reD) 78 70 75 耐酸性 〇 △ 〇 離型性 3. 6 8. 5 4. 1 耐リフ u-性 48h 0/5 0/5 0/5
72h 0/5 0/5 0/5
96h 0/5 3/5 0/5
168h 2/5 5/5 5/5 耐湿性 藤 0/10 0/10 0/10
500h 0/10 0/10 0/10 誦 h 0/10 0/10 0/10
1500h 0/10 0/10 0/10 高温放置特性 500h 0/10 0/10 0/10 lOOOh 0/10 0/10 0/10
1500h 0/10 0/10 0/10
2000h 0/10 0/10 0/10 [表 9] 表 9 封止材物性 3
Figure imgf000056_0001
[0184] 本発明の構成力 なる水酸ィ匕マグネシウムを含まな 、水酸化マグネシウムを使用し た比較例 1、 3は耐酸性に劣り、比較例 2、 3は難燃性に劣り UL— 94 V—0を達成し て 、な 、。また難燃剤を配合して 、な 、比較例 4及び酸ィ匕亜鉛のみを用いた比較例 5は難燃'性に劣っており、 UL- 94 V— 0を達成していない。またリン系難燃剤のみ を使用した比較例 6、 7は耐湿性に劣っている。臭素系難燃剤/アンチモン系難燃剤 を使用した比較例 8は高温放置特性に劣っている。
[0185] これに対し、本発明の構成成分を全て含んだ実施例 1〜19は全て UL— 94 V— 0 を達成し、難燃性が良好で、また耐酸性、成形性も良好である。さらには実施例 1〜1 5、 16〜19は耐リフロー性に優れ、実施例 1〜19は耐湿性及び高温放置特性に優 れると!/、つた信頼性にも優れて!/、る。
産業上の利用の可能性
[0186] 本発明による封止用エポキシ榭脂成形材料は難燃性が良好で、かつ成形性ゃ耐リ フロー性、耐湿性及び高温放置特性等の信頼性が良好な電子部品装置等の製品を 得ることができ、その工業的価値は大である。

Claims

請求の範囲
[1] (A)エポキシ榭脂、（B)硬化剤、（C)水酸ィ匕マグネシウムを含有し、（C)水酸化マ グネシゥムが X線回折での [101M001]ピーク強度比が 0.9以上で、 BET比表面積が l〜4m2/g、かつ平均粒子径が 5 μ m以下であるものを含む封止用エポキシ榭脂成 形材料。
[2] (C)水酸ィ匕マグネシウム粒子が原料水酸ィ匕マグネシウムもしくは原料酸化マグネシ ゥムの水懸濁液に、水酸化リチウムもしくは水酸ィ匕ナトリウムを、水酸化マグネシウム 換算の固形分 100質量％に対して、 100質量％以上添カ卩して湿式粉砕し、 180〜2 30°Cで水熱処理して得られたものである請求項 1記載の封止用エポキシ榭脂成形 材料。
[3] (C)水酸ィ匕マグネシウムの表面に、 Siィ匕合物と A1ィ匕合物との混合被覆層を SiOと
2
Al O換算の合計量で水酸化マグネシウム 100質量％に対して、 0.2〜10質量％の
2 3
割合で形成したものを含有する請求項 1又は 2記載の封止用エポキシ榭脂成形材料
[4] Siィ匕合物がケィ酸ソーダ、コロイダルシリカ及びこれらの前駆体力 なる群の少なく とも 1種の化合物、 A1ィ匕合物が塩ィ匕アルミニウム、硫酸アルミニウム、硝酸アルミニゥ ム、アルミン酸ソーダ、アルミナゾル及びこれらの前駆体力 なる群の少なくとも 1種の 化合物を各々含む請求項 3記載の封止用エポキシ榭脂成形材料。
[5] Si化合物と A1ィ匕合物の混合被覆層を形成した水酸ィ匕マグネシウムがさらに脂肪族 金属塩、シランカップリング剤の少なくとも 1種により、水酸ィ匕マグネシウム 100質量％ に対して 0.1〜： L0質量％の割合で表面処理されているものを含む請求項 3又は 4記 載の封止用エポキシ榭脂成形材料。
[6] (C)水酸ィ匕マグネシウムが (A)エポキシ榭脂 100質量部に対し、 5〜300質量部含 有する請求項 1〜5いずれか記載の封止用エポキシ榭脂成形材料。
[7] (D)金属酸ィ匕物をさらに含有する請求項 1〜6いずれか記載の封止用エポキシ榭 脂成形材料。
[8] (D)金属酸化物が典型金属元素の酸化物及び遷移金属元素の酸化物から選ば れる請求項 7記載の封止用エポキシ榭脂成形材料。
[9] (D)金属酸化物が亜鉛、マグネシウム、銅、鉄、モリブデン、タングステン、ジルコ- ゥム、マンガン及びカルシウムの酸ィ匕物の少なくとも 1種である請求項 8記載の封止 用エポキシ榭脂成形材料。
[10] (A)エポキシ榭脂がビフエニル型エポキシ榭脂、ビスフエノール F型エポキシ榭脂、 スチルベン型エポキシ榭脂、硫黄原子含有エポキシ榭脂、ノボラック型エポキシ榭脂 、ジシクロペンタジェン型エポキシ榭脂、ナフタレン型エポキシ榭脂、トリフエ-ルメタ ン型エポキシ榭脂、ビフエ-レン型エポキシ榭脂及びナフトール ·ァラルキル型フエノ ール榭脂の少なくとも 1種を含有する請求項 1〜9いずれか記載の封止用エポキシ榭 脂成形材料。
[11] 硫黄原子含有エポキシ榭脂が下記一般式 (I)で示される化合物である請求項 10記 載の封止用エポキシ榭脂成形材料。
[化 1]
Figure imgf000059_0001
(一般式 (I)で、 〜 は水素原子、置換又は非置換の炭素数 1〜10の一価の炭化 水素基から選ばれ、全てが同一でも異なっていてもよい。 nは 0〜3の整数を示す。）
[12] (B)硬化剤がビフエ-ル型フエノール榭脂、ァラルキル型フエノール榭脂、ジシクロ ペンタジェン型フエノール榭脂、トリフエ-ルメタン型フエノール榭脂及びノボラック型 フエノール榭脂の少なくとも 1種を含有する請求項 1〜： L 1いずれか記載の封止用ェ ポキシ榭脂成形材料。
[13] (E)硬化促進剤をさらに含有する請求項 1〜 12 ヽずれか記載の封止用エポキシ榭 脂成形材料。
[14] (E)硬化促進剤がホスフィン化合物とキノン化合物との付加物を含む請求項 13記 載の封止用エポキシ榭脂成形材料。
[15] (E)硬化促進剤が、リン原子に少なくとも一つのアルキル基が結合したホスフィン化 合物とキノン化合物との付加物を含む請求項 14記載の封止用エポキシ榭脂成形材 料。
[16] (F)カップリング剤をさらに含有する請求項 1〜15いずれか記載の封止用エポキシ 榭脂成形材料。
[17] (F)カップリング剤が 2級アミノ基を有するシランカップリング剤を含有する請求項 1
6記載の封止用エポキシ榭脂成形材料。
[18] 2級アミノ基を有するシランカップリング剤が下記一般式 (Π)で示される化合物を含 有する請求項 17記載の封止用エポキシ榭脂成形材料。
[化 2]
Figure imgf000060_0001
(一般式 (II)で、 R1は水素原子、炭素数 1〜6のアルキル基及び炭素数 1〜2のアル コキシ基力 選ばれ、 R2は炭素数 1〜6のアルキル基及びフ -ル基力 選ばれ、 R3 はメチル基又はェチル基を示し、 nは 1〜6の整数を示し、 mは 1〜3の整数を示す。 )
[19] (G)リン原子を有する化合物をさらに含有する請求項 1〜18のいずれかに記載の 封止用エポキシ榭脂成形材料。
[20] (G)リン原子を有する化合物がリン酸エステル化合物を含有する請求項 19記載の 封止用エポキシ榭脂成形材料。
[21] リン酸エステルィヒ合物が下記一般式 (III)で示される化合物を含有する請求項 20記 載の封止用エポキシ榭脂成形材料。
[化 3]
Figure imgf000060_0002
(一般式（III)で、式中の 8個の Rは炭素数 1〜4のアルキル基を示し、全て同一でも 異なっていてもよい。 Arは芳香族環を示す。 )
(G)リン原子を有する化合物がホスフィンオキサイドを含有し、該ホスフィンォキサイ ドが下記一般式 (IV)で示されるホスフィン化合物を含有する請求項 19記載の封止 用エポキシ榭脂成形材料。
[化 4]
Figure imgf000061_0001
(一般式 (IV)で、
Figure imgf000061_0002
R2及び R°は炭素数 1〜： L0の置換又は非置換のアルキル基、 ァリール基、ァラルキル基または水素原子を示し、すべて同一でも異なってもよい。 ただしすべてが水素原子である場合を除く。 )
[23] (H)重量平均分子量が 4, 000以上の直鎖型酸化ポリエチレン、および (I)炭素数 5〜30の aーォレフインと無水マレイン酸との共重合物を炭素数 5〜25の一価のァ ルコールでエステルイ匕した化合物をさらに含有する請求項 1〜 22いずれか記載の封 止用エポキシ榭脂成形材料。
[24] (H)成分および (I)成分の少なくとも一方が、（A)成分の一部または全部と予備混 合されてなる請求項 23記載の封止用エポキシ榭脂成形材料。
[25] C 無機充填剤をさらに含有する請求項 1〜24いずれか記載の封止用エポキシ榭 脂成形材料。
[26] (C)水酸化マグネシウムと ω無機充填剤の含有量の合計が封止用エポキシ榭脂 成形材料に対して 60〜95質量％である請求項 25記載の封止用エポキシ榭脂成形 材料。
[27] 請求項 1〜26の 、ずれかに記載の封止用エポキシ榭脂成形材料で封止された素 子を備えた電子部品装置。
PCT/JP2005/012831 2004-07-13 2005-07-12 封止用エポキシ樹脂成形材料及び電子部品装置 Ceased WO2006006593A1 (ja)