WO2006004011A1 - Filtre et méthode de fabrication de celui-ci - Google Patents

Filtre et méthode de fabrication de celui-ci Download PDF

Info

Publication number
WO2006004011A1
WO2006004011A1 PCT/JP2005/012116 JP2005012116W WO2006004011A1 WO 2006004011 A1 WO2006004011 A1 WO 2006004011A1 JP 2005012116 W JP2005012116 W JP 2005012116W WO 2006004011 A1 WO2006004011 A1 WO 2006004011A1
Authority
WO
WIPO (PCT)
Prior art keywords
sintered body
powder
molding material
filter
molding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2005/012116
Other languages
English (en)
Japanese (ja)
Inventor
Yoshimitsu Kankawa
Hiroshi Setowaki
Hiroshi Satomi
Hiroshi Kitou
Motoi Fukuda
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mold Research Co Ltd
Original Assignee
Mold Research Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mold Research Co Ltd filed Critical Mold Research Co Ltd
Priority to JP2006528823A priority Critical patent/JPWO2006004011A1/ja
Publication of WO2006004011A1 publication Critical patent/WO2006004011A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L’invention décrit un filtre fritté de type intégré doté d’une couche dense pour une partie de couche externe et une partie de couche interne poreuse ainsi qu’une méthode de fabrication à précision dimensionnelle élevée pour ledit filtre. Ce filtre est conçu pour filtrer un échantillon en permettant à l’échantillon de passer par une partie de filtrage composée d’un corps fritté poreux. Dans la partie filtrante, les parties autres que les parties d’entrée et de sortie sont couvertes par un corps fritté haute densité. La densité relative de frittage du corps fritté poreux est de 50 à 90% et celle du corps fritté haute densité est de 95% ou plus. Une interface entre le corps fritté poreux et le corps fritté haute densité est intégrée par frittage.
PCT/JP2005/012116 2004-07-02 2005-06-30 Filtre et méthode de fabrication de celui-ci Ceased WO2006004011A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2006528823A JPWO2006004011A1 (ja) 2004-07-02 2005-06-30 フィルター及びその製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/JP2004/009410 WO2006003703A1 (fr) 2004-07-02 2004-07-02 Étui fritté ayant des parties de différentes densités relatives de frittage et procédé de production de celui-ci
JPPCT/JP2004/009410 2004-07-02

Publications (1)

Publication Number Publication Date
WO2006004011A1 true WO2006004011A1 (fr) 2006-01-12

Family

ID=35782520

Family Applications (2)

Application Number Title Priority Date Filing Date
PCT/JP2004/009410 Ceased WO2006003703A1 (fr) 2004-07-02 2004-07-02 Étui fritté ayant des parties de différentes densités relatives de frittage et procédé de production de celui-ci
PCT/JP2005/012116 Ceased WO2006004011A1 (fr) 2004-07-02 2005-06-30 Filtre et méthode de fabrication de celui-ci

Family Applications Before (1)

Application Number Title Priority Date Filing Date
PCT/JP2004/009410 Ceased WO2006003703A1 (fr) 2004-07-02 2004-07-02 Étui fritté ayant des parties de différentes densités relatives de frittage et procédé de production de celui-ci

Country Status (2)

Country Link
JP (1) JPWO2006004011A1 (fr)
WO (2) WO2006003703A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008056989A (ja) * 2006-08-31 2008-03-13 Osaka Yakin Kogyo Kk 金属複合体の製造方法
JP2018536526A (ja) * 2015-12-04 2018-12-13 キドニ ラボズ, インク.Qidni Labs, Inc. 埋込型腎代替療法システム
US20190091029A1 (en) * 2009-04-29 2019-03-28 Flextronics Global Services Canada Inc. Services G lobaux Flextronics Canada Inc. Method for co-processing components in a metal injection molding process, and components made via the same
JP2020025881A (ja) * 2018-08-13 2020-02-20 ハナテク カンパニー リミテッド 注射機器用及びリンゲル輸液器用注射液のチタンフィルタ及びその製造方法
JP2023503954A (ja) * 2019-11-27 2023-02-01 モット・コーポレーション セラミックディスクおよびロッド、それらの製造方法、ならびにそれらを備える物品

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015211099A (ja) * 2014-04-25 2015-11-24 京セラ株式会社 真空チャック部材および真空チャック部材の製造方法。
DE102015204752A1 (de) * 2015-03-17 2016-09-22 Schaeffler Technologies AG & Co. KG Verfahren zur Herstellung eines porösen Bauteils aus mindestens einem Material M und mit einer Schaumstruktur sowie ein danach hergestelltes poröses Bauteil
WO2018097188A1 (fr) * 2016-11-22 2018-05-31 大阪冶金興業株式会社 Procédé de moulage par injection de poudre métallique

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01176285A (ja) * 1987-12-28 1989-07-12 Nippon Denso Co Ltd 多孔セラミック体
JP2001276533A (ja) * 2000-03-28 2001-10-09 Ibiden Co Ltd 多孔質炭化珪素フィルター
JP2003129111A (ja) * 2001-10-18 2003-05-08 Sanalloy Industry Co Ltd 多孔質焼結体

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5852528B2 (ja) * 1979-04-10 1983-11-24 葛城産業株式会社 金属の多孔質焼結板状体およびその製造法
JPH066283B2 (ja) * 1988-09-22 1994-01-26 日本碍子株式会社 セラミックス多層構造体の押出成形方法
JPH10251712A (ja) * 1997-03-12 1998-09-22 Kubota Corp 金属系複合多孔質部材およびその製造方法並びに溶接接合体
JP4057095B2 (ja) * 1997-04-14 2008-03-05 日本碍子株式会社 セラミックスの押出成形装置
JP2001278672A (ja) * 2000-03-31 2001-10-10 Japan Fine Ceramics Center セラミックス材料及びその製造方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01176285A (ja) * 1987-12-28 1989-07-12 Nippon Denso Co Ltd 多孔セラミック体
JP2001276533A (ja) * 2000-03-28 2001-10-09 Ibiden Co Ltd 多孔質炭化珪素フィルター
JP2003129111A (ja) * 2001-10-18 2003-05-08 Sanalloy Industry Co Ltd 多孔質焼結体

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008056989A (ja) * 2006-08-31 2008-03-13 Osaka Yakin Kogyo Kk 金属複合体の製造方法
US20190091029A1 (en) * 2009-04-29 2019-03-28 Flextronics Global Services Canada Inc. Services G lobaux Flextronics Canada Inc. Method for co-processing components in a metal injection molding process, and components made via the same
JP2018536526A (ja) * 2015-12-04 2018-12-13 キドニ ラボズ, インク.Qidni Labs, Inc. 埋込型腎代替療法システム
JP2020025881A (ja) * 2018-08-13 2020-02-20 ハナテク カンパニー リミテッド 注射機器用及びリンゲル輸液器用注射液のチタンフィルタ及びその製造方法
JP2023503954A (ja) * 2019-11-27 2023-02-01 モット・コーポレーション セラミックディスクおよびロッド、それらの製造方法、ならびにそれらを備える物品
JP7708756B2 (ja) 2019-11-27 2025-07-15 モット・コーポレーション セラミックディスクおよびロッド、それらの製造方法、ならびにそれらを備える物品

Also Published As

Publication number Publication date
JPWO2006004011A1 (ja) 2008-04-24
WO2006003703A1 (fr) 2006-01-12

Similar Documents

Publication Publication Date Title
EP2900404B1 (fr) Procédés de formation d'un article métallique ou de céramique présentant une nouvelle composition de matériau fonctionnellement nuancé
KR100686427B1 (ko) 세라믹스 세터 및 그 제조방법
US20210163364A1 (en) 3d printing material, preparation method and use thereof
CN103317140B (zh) 一种流延法制备W-Cu体系梯度复合材料的方法
JP5970795B2 (ja) 射出成形用組成物の製造方法
JP5970794B2 (ja) 射出成形用組成物および焼結体の製造方法
JP2001505825A (ja) 複雑な形状のセラミック−金属複合体製品の浸透を制御する方法およびそれによって作られた製品
JP2010515829A (ja) セラミックス複合成形体および／または粉末冶金複合成形体およびその製造法
WO2006004011A1 (fr) Filtre et méthode de fabrication de celui-ci
EP2607396A1 (fr) Composition pour moulage par injection, corps compact fritté et procédé de production d'un corps compact fritté
JP5503838B2 (ja) 多孔質焼結体の製造方法、多孔質焼結成形材料及び多孔質焼結体
US20070071962A1 (en) Multi-layer ceramic compound
JP4514560B2 (ja) 筒状セラミック多孔質体及びその製造方法ならびにこれを用いたセラミックフィルター
JP2009254581A (ja) 生体用インプラント及びその製造方法
JP4122431B2 (ja) 層状構造を有する酸化アルミニウム耐摩耗性部材及びその製造方法
JP3569682B2 (ja) 高耐食性金属焼結フィルタ
US12479124B2 (en) Additive manufactured fired body, and method for manufacturing the additive manufactured fired body
KR101001253B1 (ko) 다공질 지지체의 내벽에 산소분리막을 코팅하는 방법 및 이로써 제조된 산소분리용 튜브
Scheithauer et al. Functionally graded materials made by water-based multilayer technology
KR20240156608A (ko) 결합제 제트 적층 제조용 초경합금 분말
JP2003306386A (ja) アルミナセラミックスセッター及びその製造方法
Nishiyabu et al. Net-shape manufacturing of micro porous metal components by powder injection molding
JP4445141B2 (ja) 傾斜複合材の製造方法
JPH01210306A (ja) スラリー状材料成形用型およびその製造方法
JP2942212B2 (ja) セラミックスの製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KM KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NG NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2006528823

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

WWW Wipo information: withdrawn in national office

Country of ref document: DE

122 Ep: pct application non-entry in european phase