WO1997032715A1 - Procede et dispositif de production de plaques de metal enduites de resine - Google Patents

Procede et dispositif de production de plaques de metal enduites de resine Download PDF

Info

Publication number
WO1997032715A1
WO1997032715A1 PCT/JP1996/001369 JP9601369W WO9732715A1 WO 1997032715 A1 WO1997032715 A1 WO 1997032715A1 JP 9601369 W JP9601369 W JP 9601369W WO 9732715 A1 WO9732715 A1 WO 9732715A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin
metal plate
film
resin film
solidified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP1996/001369
Other languages
English (en)
Japanese (ja)
Inventor
Takaaki Okamura
Yasuo Ohhashi
Hiroshi Nakamura
Atsuo Tanaka
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toyo Kohan Co Ltd
Original Assignee
Toyo Kohan Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toyo Kohan Co Ltd filed Critical Toyo Kohan Co Ltd
Priority to AU57788/96A priority Critical patent/AU5778896A/en
Publication of WO1997032715A1 publication Critical patent/WO1997032715A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Procédé et dispositif de production de plaques de métal enduites de résine à faible coût et à bon rendement sans gaspillage de résine et de plaques de métal. Etant donné que l'on atteint cet objectif par deux effets économiques constitués par l'économie d'un processus de formation de couches minces et de stratification d'une couche mince ainsi formée sur une plaque de métal dans un même processus, et par le fait qu'on limite le gaspillage de matériau tel que la résine et les plaques de métal autant que possible, la couche mince de résine durcie extrudée par un moule en T n'est stratifiée sur une plaque de métal que lorsque l'épaisseur de ladite couche mince de résine durcie devient stable. En d'autres termes, la couche mince de résine durcie est tout d'abord prise et elle n'est stratifiée sur la surface d'une plaque de métal chauffée que lorsque l'épaisseur de ladite couche mince devient stable. Ce procédé permet d'éviter la production de plaques de métal enduites de résine défectueuses présentant une couche mince de résine durcie stratifiée d'une épaisseur non-uniforme, il améliore le rendement en plaques de métal enduites de résine et réduit le gaspillage de matériaux. De plus, la couche mince de résine durcie maintenue prise jusqu'à ce que son épaisseur devienne stable peut être recyclée lorsqu'elle est refusionnée, et ceci peut à nouveau réduire la perte de matériaux (résine).
PCT/JP1996/001369 1996-03-04 1996-05-23 Procede et dispositif de production de plaques de metal enduites de resine Ceased WO1997032715A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU57788/96A AU5778896A (en) 1996-03-04 1996-05-23 Method and device for manufacturing resin-coated metal plates

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP8/70903 1996-03-04
JP8070903A JP2971391B2 (ja) 1996-03-04 1996-03-04 樹脂被覆金属板の製造方法及び製造装置

Publications (1)

Publication Number Publication Date
WO1997032715A1 true WO1997032715A1 (fr) 1997-09-12

Family

ID=13444962

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP1996/001369 Ceased WO1997032715A1 (fr) 1996-03-04 1996-05-23 Procede et dispositif de production de plaques de metal enduites de resine

Country Status (3)

Country Link
JP (1) JP2971391B2 (fr)
AU (1) AU5778896A (fr)
WO (1) WO1997032715A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998039160A1 (fr) * 1997-01-23 1998-09-11 Hoogovens Staal B.V. Procede et dispositif de revetement d'une bande plastique pelable sur un substrat metallique en forme de ruban et ruban ainsi obtenu
CN105216428A (zh) * 2015-11-24 2016-01-06 苏州弘瀚自动化科技有限公司 一种液晶屏撕膜装置的智能控制系统
CN107053334A (zh) * 2017-05-17 2017-08-18 深圳市伟铂瑞信科技有限公司 一种新型高分子界面材料的模切装置

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4154662B2 (ja) * 2002-02-01 2008-09-24 東洋紡績株式会社 樹脂被覆金属板の製造方法
RU2715661C2 (ru) * 2014-10-17 2020-03-02 Тетра Лаваль Холдингз Энд Файнэнс С.А. Способ получения ламинированного упаковочного материала

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5073964A (fr) * 1973-11-01 1975-06-18
JPH04294142A (ja) * 1991-03-25 1992-10-19 Nippon Steel Corp 両面樹脂被覆鋼板の製造方法
JPH06305024A (ja) * 1993-04-23 1994-11-01 Toyo Kohan Co Ltd 樹脂被覆金属板の製造方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5073964A (fr) * 1973-11-01 1975-06-18
JPH04294142A (ja) * 1991-03-25 1992-10-19 Nippon Steel Corp 両面樹脂被覆鋼板の製造方法
JPH06305024A (ja) * 1993-04-23 1994-11-01 Toyo Kohan Co Ltd 樹脂被覆金属板の製造方法

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998039160A1 (fr) * 1997-01-23 1998-09-11 Hoogovens Staal B.V. Procede et dispositif de revetement d'une bande plastique pelable sur un substrat metallique en forme de ruban et ruban ainsi obtenu
US6758933B2 (en) 1997-01-23 2004-07-06 Corus Staal Bv Method and apparatus for strip-coating a metallic strip-shaped substrate with a plastic band and strip thus obtained
CN105216428A (zh) * 2015-11-24 2016-01-06 苏州弘瀚自动化科技有限公司 一种液晶屏撕膜装置的智能控制系统
CN107053334A (zh) * 2017-05-17 2017-08-18 深圳市伟铂瑞信科技有限公司 一种新型高分子界面材料的模切装置

Also Published As

Publication number Publication date
JPH10309775A (ja) 1998-11-24
AU5778896A (en) 1997-09-22
JP2971391B2 (ja) 1999-11-02

Similar Documents

Publication Publication Date Title
KR101133970B1 (ko) 복층의 무연신필름의 제조방법, 복층수지피복 금속판의제조방법 및, 복층의 무연신필름의 제조장치
JP3711815B2 (ja) 押出ラミネート材の製造方法
JP3931958B2 (ja) ラミネート材の製造方法及び製造装置
RU2396167C1 (ru) Способ и установка для изготовления металлического листа с покрытием из органической смолы
JP2971391B2 (ja) 樹脂被覆金属板の製造方法及び製造装置
CA2235903A1 (fr) Methode et appareil permettant de plastifier des bandes de metal par extrusion directe
JP3470527B2 (ja) 樹脂金属ラミネート材の製造方法
EP1019248B1 (fr) Procédé et dispositif de revêtement d'une bande plastique sur un substrat métallique en forme de ruban
CN117245878A (zh) 一种在基材上多层共挤覆膜的复合薄膜机
CN114514106B (zh) 制造能密封的双轴取向的基于聚酯的膜的方法和膜拉伸设备
JP3941576B2 (ja) 樹脂フィルムラミネート金属板の製造方法および製造装置
JP3891031B2 (ja) 樹脂フィルムラミネート金属板の製造方法および製造装置
JP3470526B2 (ja) 両面樹脂被覆金属ラミネート材の製法
JP3941577B2 (ja) 樹脂フィルムラミネート金属板の製造方法および製造装置
JP3809399B2 (ja) 有機樹脂被覆金属板の製造方法および有機樹脂被覆金属板の製造装置
JPH11100006A (ja) 押出ラミネート用ロール
WO2006048956A1 (fr) Procédé servant à produire un film non étiré, procédé servant à produire une feuille de métal recouverte de résine et appareil servant à produire un film non étiré
JP2005349787A (ja) 樹脂密着性に優れた樹脂被覆金属板の製造方法
JP2001322152A (ja) 溶融樹脂のラミネート方法及び装置
JP4756979B2 (ja) 有機樹脂被覆金属板の製造方法および有機樹脂被覆金属板の製造装置
WO2006013633A1 (fr) Film de résine multicouches, plateau métallique enduit de résine, procédé de production de film de résine multicouches, et procédé de production de plateau métallique enduit de résine
JPH03158235A (ja) ラミネート金属板の製造方法
JP3060249B2 (ja) ラミネート金属板の製造方法
JP3057333B2 (ja) ラミネート金属板の製造方法
RU2632493C1 (ru) Способ получения многослойного материала путем нанесения полимерного покрытия экструзией при каландрировании

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU BR CA CN KR MX NO NZ PL SG TR US VN

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA