WO1992003509A1 - Matiere de revetement active sous l'effet des micro-ondes comprenant une resine polymere - Google Patents

Matiere de revetement active sous l'effet des micro-ondes comprenant une resine polymere Download PDF

Info

Publication number
WO1992003509A1
WO1992003509A1 PCT/US1991/005724 US9105724W WO9203509A1 WO 1992003509 A1 WO1992003509 A1 WO 1992003509A1 US 9105724 W US9105724 W US 9105724W WO 9203509 A1 WO9203509 A1 WO 9203509A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating material
solvent
resin
binder system
electrically conductive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US1991/005724
Other languages
English (en)
Inventor
Joseph Anthony Milenkevich
William David Geib
Christopher William Widenhouse
Andrew Julian Wnuk
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Procter and Gamble Co
Original Assignee
Procter and Gamble Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Procter and Gamble Co filed Critical Procter and Gamble Co
Publication of WO1992003509A1 publication Critical patent/WO1992003509A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Matière de revêtement active sous l'effet des micro-ondes comprenant des éléments électroconducteurs ainsi qu'un système de liaison. Le système de liaison comprend un solvent ainsi qu'une résine polymère choisie dans le groupe constitué de nitrocellulose, cellulose éthylique, polyvinylbutyral, poly(éther de vinylméthylique/anhydride maléique) co-polymère ou ses dérivés, et polyvinylpyrrolidone. La matière de revêtement est capable de constituer un revêtement configuré sur un substrat afin de former une pluralité d'éléments électroconducteurs discrets. Les éléments électroconducteurs discrets ont une dimension maximum suffisamment réduite pour éviter l'allumage. De plus, les éléments forment un réseau faisant office d'agent modifiant le champ des micro-ondes. L'agent modifiant peut constituer un substrat diélectrique comportant une pluralité d'aires de surface discrètes revêtues d'une matière de revêtement électroconductrice afin de former des éléments électroconducteurs discrets, ces derniers étant disposés sur une surface donnée en un réseau prédéterminé. Les éléments sont de préférence allongés et le réseau constitue une pluralité de rangées d'éléments en alignement linéaire lesquelles sont parallèles, et les éléments du réseau en rangées adjacentes sont disposés en quinconce. Lesdits éléments électroconducteurs sont de préférence formés par impression d'une matière de revêtement électroconductrice analogue à de l'encre sur le substrat diélectrique.
PCT/US1991/005724 1990-08-16 1991-08-13 Matiere de revetement active sous l'effet des micro-ondes comprenant une resine polymere Ceased WO1992003509A1 (fr)

Applications Claiming Priority (16)

Application Number Priority Date Filing Date Title
US56800690A 1990-08-16 1990-08-16
US56801090A 1990-08-16 1990-08-16
US56810390A 1990-08-16 1990-08-16
US56810490A 1990-08-16 1990-08-16
US568,103 1990-08-16
US568,104 1990-08-16
US568,010 1990-08-16
US568,006 1990-08-16
US61434490A 1990-11-15 1990-11-15
US61434390A 1990-11-15 1990-11-15
US61434290A 1990-11-15 1990-11-15
US61434190A 1990-11-15 1990-11-15
US614,343 1990-11-15
US614,342 1990-11-15
US614,341 1990-11-15
US614,344 1990-11-15

Publications (1)

Publication Number Publication Date
WO1992003509A1 true WO1992003509A1 (fr) 1992-03-05

Family

ID=27575483

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1991/005724 Ceased WO1992003509A1 (fr) 1990-08-16 1991-08-13 Matiere de revetement active sous l'effet des micro-ondes comprenant une resine polymere

Country Status (5)

Country Link
EP (1) EP0543948A1 (fr)
JP (1) JPH06500357A (fr)
AU (1) AU8725891A (fr)
NZ (1) NZ239400A (fr)
WO (1) WO1992003509A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5897813A (en) * 1995-08-23 1999-04-27 Mirson Electrically conducting paint material
US20110271973A1 (en) * 2009-01-28 2011-11-10 Naoko Iwagaki Solution for forming double eyelid and method for forming double eyelid using same
US9303507B2 (en) 2013-01-31 2016-04-05 Saudi Arabian Oil Company Down hole wireless data and power transmission system
CN115552550A (zh) * 2020-05-14 2022-12-30 汉高股份有限及两合公司 可高速印刷的碳油墨

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4518651A (en) * 1983-02-16 1985-05-21 E. I. Du Pont De Nemours And Company Microwave absorber
US4914266A (en) * 1989-03-22 1990-04-03 Westvaco Corporation Press applied susceptor for controlled microwave heating

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4518651A (en) * 1983-02-16 1985-05-21 E. I. Du Pont De Nemours And Company Microwave absorber
US4914266A (en) * 1989-03-22 1990-04-03 Westvaco Corporation Press applied susceptor for controlled microwave heating

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Patent Abstracts of Japan, Vol 12, No 482, C553, abstract of JP 63-196672, publ 1988-08-15 *

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5897813A (en) * 1995-08-23 1999-04-27 Mirson Electrically conducting paint material
US20110271973A1 (en) * 2009-01-28 2011-11-10 Naoko Iwagaki Solution for forming double eyelid and method for forming double eyelid using same
US9061165B2 (en) * 2009-01-28 2015-06-23 Naoko Iwagaki Solution for forming double eyelid and method for forming double eyelid using same
US9303507B2 (en) 2013-01-31 2016-04-05 Saudi Arabian Oil Company Down hole wireless data and power transmission system
CN115552550A (zh) * 2020-05-14 2022-12-30 汉高股份有限及两合公司 可高速印刷的碳油墨

Also Published As

Publication number Publication date
AU8725891A (en) 1992-03-17
EP0543948A1 (fr) 1993-06-02
JPH06500357A (ja) 1994-01-13
NZ239400A (en) 1995-02-24

Similar Documents

Publication Publication Date Title
US4914266A (en) Press applied susceptor for controlled microwave heating
CA2140518C (fr) Materiau interactif a auto-limitation pour micro-ondes
US5118747A (en) Microwave heater compositions for use in microwave ovens
US5002826A (en) Heaters for use in microwave ovens
EP2350176B1 (fr) Composition d'argent en film polymère épais de haute conductivité pour utilisation dans les rfid et d'autres applications
US4477296A (en) Method for activating metal particles
EP2303957B1 (fr) Composition pour électrode d argent en couche épaisse de polymère destinée à être utilisée dans les cellules photovoltaïques en couche mince
EP0722996A1 (fr) Adhésifs autocollants électroconducteurs
DE3786589T2 (de) Zusammengesetztes Material, das Mikrowellen absorbierende Materialien enthält.
WO1992003509A1 (fr) Matiere de revetement active sous l'effet des micro-ondes comprenant une resine polymere
AU662301B2 (en) Microwave package having a microwave field modifier of discrete electrically conductive elements disposed thereon
CA2048340A1 (fr) Matiere de revetement active aux micro-ondes, comportant du polyvinylbutyral
CA2048341A1 (fr) Matiere de revetement active aux micro-ondes, comportant une resine copolymerique de type methylvinylether/anhydride maleique
CA2048342A1 (fr) Matiere de revetement active aux micro-ondes comportant de la polyvinylpyrrolidone
JPH0625452A (ja) プラスチックフィルム用塗布剤
CA2048343A1 (fr) Matiere de revetement active aux micro-ondes comportant une resine de nicrocellulose ou d'ethylcellulose
NZ239399A (en) Microwave field modifier: rows of patterned electrically conductive elements
KR100411397B1 (ko) 알루미늄시이트를이용한피티씨면상발열체
JP3526743B2 (ja) 導電性シート
JPH03271362A (ja) 電気絶縁性金属蒸着膜
JPH01243401A (ja) 感圧抵抗変化型導電性組成物
JP2002309154A (ja) 車両用プライマー塗料、車両用塗膜構造および車両用ポリオレフィン系基材の塗装方法
JPS6074208A (ja) 導電性塗膜の形成方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU JP

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IT LU NL SE

WWE Wipo information: entry into national phase

Ref document number: 1991917866

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1991917866

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1991917866

Country of ref document: EP