WO1980002245A1 - Electrode de soudage a ame et methode de fabrication et d'utilisation - Google Patents

Electrode de soudage a ame et methode de fabrication et d'utilisation Download PDF

Info

Publication number
WO1980002245A1
WO1980002245A1 PCT/US1980/000485 US8000485W WO8002245A1 WO 1980002245 A1 WO1980002245 A1 WO 1980002245A1 US 8000485 W US8000485 W US 8000485W WO 8002245 A1 WO8002245 A1 WO 8002245A1
Authority
WO
WIPO (PCT)
Prior art keywords
tube
welding electrode
flat surfaces
electrode
tubular welding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US1980/000485
Other languages
English (en)
Inventor
R Eytchison
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE19803041413 priority Critical patent/DE3041413A1/de
Publication of WO1980002245A1 publication Critical patent/WO1980002245A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Cette electrode presente une forme carree (100) avec les cotes plats (102) relies par des coins arrondis (104). Avec cette forme, on obtient une surface plus lisse qui diminue l'usure du dispositif d'alimentation de fils (60) et de l'assemblage du cable et du pistolet (84). Une electrode carree (100) peut etre matricee (104) pour en reduire ses dimensions et former une electrode circulaire (24). La methode de formation de l'electrode consiste a donner au metal une forme de tube (18), le remplir avec du fondant et lui donner la forme desiree.
PCT/US1980/000485 1979-04-23 1980-04-21 Electrode de soudage a ame et methode de fabrication et d'utilisation Ceased WO1980002245A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
DE19803041413 DE3041413A1 (de) 1979-04-23 1980-04-21 A flux cored welding electrode and method of making and using

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US3252879A 1979-04-23 1979-04-23
US32528 1979-04-23

Publications (1)

Publication Number Publication Date
WO1980002245A1 true WO1980002245A1 (fr) 1980-10-30

Family

ID=21865400

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1980/000485 Ceased WO1980002245A1 (fr) 1979-04-23 1980-04-21 Electrode de soudage a ame et methode de fabrication et d'utilisation

Country Status (3)

Country Link
EP (1) EP0027467A1 (fr)
GB (1) GB2059845A (fr)
WO (1) WO1980002245A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20110073790A (ko) * 2009-12-24 2011-06-30 재단법인 포항산업과학연구원 플럭스 코어드 와이어 제조 방법
KR101428185B1 (ko) * 2012-08-29 2014-09-23 주식회사 포스코 각형 용접와이어의 제조방법
KR101461722B1 (ko) * 2012-11-01 2014-11-20 주식회사 포스코 용접 와이어 제조방법

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2290734A (en) * 1940-02-14 1942-07-21 Minerals And Metals Corp Manufacture of metal products
US2829236A (en) * 1956-05-03 1958-04-01 Ray P Miles Welding apparatus
NL6501675A (fr) * 1965-02-11 1966-08-12
US3466907A (en) * 1966-01-03 1969-09-16 Lincoln Electric Co Metal ribbon,welding electrodes and method and apparatus for forming same
US3497669A (en) * 1968-07-12 1970-02-24 Air Reduction Control of drop size in spray welding
US3543381A (en) * 1968-03-06 1970-12-01 Astor Mfg Co Inc Method and apparatus for making a filled tubular product

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2290734A (en) * 1940-02-14 1942-07-21 Minerals And Metals Corp Manufacture of metal products
US2829236A (en) * 1956-05-03 1958-04-01 Ray P Miles Welding apparatus
NL6501675A (fr) * 1965-02-11 1966-08-12
US3466907A (en) * 1966-01-03 1969-09-16 Lincoln Electric Co Metal ribbon,welding electrodes and method and apparatus for forming same
US3543381A (en) * 1968-03-06 1970-12-01 Astor Mfg Co Inc Method and apparatus for making a filled tubular product
US3497669A (en) * 1968-07-12 1970-02-24 Air Reduction Control of drop size in spray welding

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20110073790A (ko) * 2009-12-24 2011-06-30 재단법인 포항산업과학연구원 플럭스 코어드 와이어 제조 방법
KR101591026B1 (ko) 2009-12-24 2016-02-03 재단법인 포항산업과학연구원 플럭스 코어드 와이어 제조 방법
KR101428185B1 (ko) * 2012-08-29 2014-09-23 주식회사 포스코 각형 용접와이어의 제조방법
KR101461722B1 (ko) * 2012-11-01 2014-11-20 주식회사 포스코 용접 와이어 제조방법

Also Published As

Publication number Publication date
EP0027467A1 (fr) 1981-04-29
GB2059845A (en) 1981-04-29

Similar Documents

Publication Publication Date Title
EP3269489A1 (fr) Tuyau en acier revêtu inoxydable soudé par résistance électrique et son procédé de fabrication
US3108180A (en) Welding electrode mouthpiece
WO1980002245A1 (fr) Electrode de soudage a ame et methode de fabrication et d'utilisation
US4514900A (en) Apparatus to manufacture heat exchanger finned tube
US3423003A (en) Method and means for the manufacture of spiral piping
GB2101799A (en) Electrode assembly for gas-tight electric storage batteries
KR101017397B1 (ko) Ｓｒ 동축케이블의 제조방법
JP3566862B2 (ja) 小径管のプラズマ溶接造管方法
GB2034206A (en) Copper Soldered Brazed Multilayer Tubes
US3181236A (en) Apparatus for fabricating finned tubing
JPS5846400B2 (ja) ガスシ−ルドア−ク溶接用ソリッドワイヤの製造方法
WO2014052363A2 (fr) Électrode de soudure bimétallique
US2430701A (en) Welding electrode
US5586461A (en) Methods and apparatus for manufacturing helical products
RU2012460C1 (ru) Способ подачи проволоки
JPS608918B2 (ja) 送給性の良好な細径フラックス入り溶接用ワイヤ
JPH01202391A (ja) ワイヤ送給性の良好なフラックス入リワイヤ
KR102232132B1 (ko) 소모성 용접 와이어, 바람직하게는 mig/mag, 및 관련 제조 방법
JP2732937B2 (ja) 溶接用フラックス入りワイヤの製造方法
KR102168338B1 (ko) 용접장치가 구비된 체인제작장치
JPS63115697A (ja) フラツクス入りワイヤの製造方法
JPH02112820A (ja) ワイヤカット放電加工用電極線の製造方法
JPH0659558B2 (ja) フラツクスコア−ドワイヤの製造方法
JPH02112822A (ja) 伝熱管の製造方法
JPS60130472A (ja) ア−ク溶接方法及び装置

Legal Events

Date Code Title Description
AK Designated states

Designated state(s): DE GB JP

AL Designated countries for regional patents

Designated state(s): FR

RET De translation (de og part 6b)

Ref document number: 3041413

Country of ref document: DE

Date of ref document: 19810423

WWE Wipo information: entry into national phase

Ref document number: 3041413

Country of ref document: DE