US20130192726A1 - Method of hot forming a steel blank and the hot formed part - Google Patents

Method of hot forming a steel blank and the hot formed part Download PDF

Info

Publication number
US20130192726A1
US20130192726A1 US13/819,281 US201113819281A US2013192726A1 US 20130192726 A1 US20130192726 A1 US 20130192726A1 US 201113819281 A US201113819281 A US 201113819281A US 2013192726 A1 US2013192726 A1 US 2013192726A1
Authority
US
United States
Prior art keywords
steel
temperature
blank
article
hot forming
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/819,281
Other languages
English (en)
Inventor
Shangping Chen
Christiaan Theodorus Wilhelmus Lahaye
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tata Steel Ijmuiden BV
Original Assignee
Tata Steel Ijmuiden BV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=43640446&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=US20130192726(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Tata Steel Ijmuiden BV filed Critical Tata Steel Ijmuiden BV
Assigned to TATA STEEL IJMUIDEN B.V. reassignment TATA STEEL IJMUIDEN B.V. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CHEN, SHANGPING, LAHAYE, CHRISTIAAN THEODORUS WILHELMUS
Publication of US20130192726A1 publication Critical patent/US20130192726A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/005—Modifying the physical properties by deformation combined with, or followed by, heat treatment of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals

Definitions

  • the invention relates to a method of hot forming a steel blank into a hot formed article having very high mechanical properties, such as an automotive part, to an article thus hot formed and to a steel strip, sheet or blank for use in a thermomechanical treatment process, in particular for use in a hot forming method according to the invention.
  • AHSS advanced high strength steels
  • hot (press) forming (hot stamping or is press hardening) has been developed.
  • hot (press) forming the strength of the steel article is improved through fast cooling after heating it to a temperature range where an austenitic phase exists and through the phase transformations of the austenite to harder phases such as bainite and martensite.
  • a typical steel used for the hot press forming is based on a composition system of 22MnB5, i.e. 0.22% of C, 1.2% of Mn, maximum 50 ppm of B, specified in EN10083.
  • Hot press forming of 22MnB5 steel can produce complex parts such as bumpers and pillars with ultrahigh strength, minimum springback, and reduced sheet thickness.
  • the tensile strength of boron steels is up to 1600 MPa, which is far above that of the highest-strength conventional cold stamping steels.
  • the ductility of total elongation A5 is less than 6%.
  • Advanced high strength steels with TRIP (transformation induced plasticity) added multiphase microstructure are a solution. These steels are characterized by a ferritic-bainitic microstructure with retained austenite, which undergoes martensitic transformation during forming of products, additionally contributing to the strengthening of a ready part.
  • US2008/0286603 A1 has disclosed a steel sheet that exhibits an ultra-high strength after hot press forming followed by rapid cooling, and an enhanced yield strength after painting.
  • the steel sheet has a composition (expressed in % by is weight) comprising 0.1 to 0.5 C, 0.01 to 1.0 Si, 0.5 to 4.0 Mn, 0.1 or less P, 0.03 or less S, 0.1 soluble Al, 0.01 to 0.1 N, 0.3 or less W, and the balance being Fe and other inevitable impurities.
  • a hot-pressed part made of the steel sheet and a method for manufacturing the hot-pressed part are disclosed.
  • the hot-pressed part achieves a high increment in yield strength after heat treatment for painting while ensuring an ultra-high tensile strength.
  • the steel provided according to this US patent application has an ultimate tensile strength (UTS) of 1500 MPa with the total elongation being less than 8%.
  • a high-strength cold-rolled steel sheet having an uniform elongation including (in wt. %): 0.10-0.28 C; 1.0-2.0 Si; and 1.0-3.0 Mn.
  • the structure has the space factors: 30-65% of bainitic ferrite; 30-50% of polygonal ferrite; and 5-20% of residual austenite.
  • the desired microstructures were obtained according to the following process.
  • the steel sheet was heated for soaking up to a temperature which is equal to or higher than the A3 transformation point (A3), then cooled down temporarily to a temperature Tq expressed by the formula A3-250 (° C.) ⁇ Tq ⁇ A3-20 (° C.) at an average cooling rate of 1-10° C./s, and then quenched from this temperature down into a bainitic transformation temperature range at an average cooling rate of 11° C./s or faster.
  • US2008/0308194 A1 has disclosed a process for manufacturing a part made of steel having a multiphase microstructure.
  • the composition of steel comprises, in % by weight: C 0.01-0.50, Mn 0.5-3.0, Si 0.001-3.0, Al 0.005-3.0, Mo ⁇ 1.0, Cr ⁇ 1.5, P ⁇ 0.10, Ti ⁇ 0.20, V ⁇ 1.0 and optionally, one or more elements such as: Ni ⁇ 2.0, Cu ⁇ 2.0, S ⁇ 0.05 and Nb ⁇ 15, the balance of the composition being iron and inevitable impurities.
  • the steel sheet is heated to reach a soaking temperature Ts above Ac1 but below Ac3 and is held at this soaking temperature Ts for a soaking time is so that the steel has an austenite content equal to or greater than 25% by area; the steel blank is transferred into a forming tool for hot forming; and the part obtained is cooled within the tool at a is cooling rate V to obtain a multiphase microstructure comprising ferrite, martensite or bainite and retained austenite, and ferrite is homogeneous in each of the regions.
  • JP2003193193 teaches steel sheet having a two phase microstructure comprising bainite/bainitic ferrite as a main phase and austenite as a second phase.
  • the manufacturing process comprises an isothermal heat treatment at 200-450° C. for 1-3000 seconds.
  • TBF TBF-aided bainitic ferrite
  • Another object of the present invention is to provide a multiphase microstructured steel resulting in simultaneously improved strength and ductility.
  • the invention provides a method of hot forming a steel blank into an article, such as an automotive part, as defined in claim 1 , wherein the method comprises the following steps:
  • the steel blank as a starting material for executing the method according to the invention can be obtained by standard casting processes, or indirectly from steel strip or sheet material.
  • the preheating temperature may be about 1100-1250° C.
  • Traditional hot rolling passes and rolling conditions may be implemented to roll the steel ingot to a sheet product of about 3 to 5 mm in thickness.
  • the finish rolling temperature is about 850-880° C.
  • the steel sheet is cooled at an average cooling rate of 5-50° C./s to a coiling temperature between 550 and 700° C. An excess of martensite or bainite is formed at a coiling temperature lower than 550° C., resulting in an excessive increase in the strength of the hot-rolled steel sheet.
  • the excessively increased strength acts as a load during subsequent cold rolling for the production of a cold-rolled steel sheet causing problems, such as a poor appearance.
  • cold rolling the coiled hot-rolled sheet is pickled and cold-rolled.
  • Cold rolling can also be carried out under standard conditions at a reduction of about 30-75%.
  • the cold rolling reduction is preferably controlled to range from 40 to 70%.
  • the sheet has a thickness of about 1 to 2 mm according to product requirements.
  • the sheet may be decoiled and blanked to proper size suitable for hot forming according to the invention.
  • a cold rolled sheet is a preferred starting product in the method according to the invention.
  • the two-step cooling pattern and the interrupt cooling temperature are properly controlled.
  • the heated steel blank used in step d) has an austenite structure.
  • the method according to the invention also comprises the steps of
  • These austenitizing steps of the method for obtaining an austenite structure are performed by heating steel sheets, strips of blanks e.g. in a furnace or in a hot forming facility itself, to a temperature T 1 above Ac3, more preferably in the is range of Ac3+20° C. to Ac3+60° C.
  • the heating rate is in the range of 10-25° C./s.
  • This heating step is followed by soaking at a temperature above Ac3, preferably in the range of Ac3+20° C. to Ac3+60° C., for a short period of time, preferably 1-5 min (Ac3 being the temperature at which transformation of ferrite into austenite is completed in hypoeutectoid steel, upon heating).
  • the austenitizing temperature (T 1 ) and soaking time are selected to ensure complete dissolution of carbides. If applicable, then the steel blank thus soaked is transferred to the hot forming device such as a hot forming press. If applicable, the transferring time is controlled, usually to a short transfer time such as less than 10 seconds to prevent cooling of the blank below the starting temperature T 2 of the next hot forming step.
  • the starting temperature T 2 for hot forming and simultaneous cooling should be above the Ar3 point (typically in the range of 780 ⁇ 830° C.) to prevent any ferrite phase transformation, e.g. during transferring.
  • the steel blank is allowed to cool down further to room temperature at a further cooling rate V 3 of 0.2-10° C./s.
  • the higher cooling rates above 5° C./s within said range are advantageous for achieving a high total elongation (At).
  • the range of 0.5-5° C./s is preferred in view of high Ultimate Tensile Strength (UTS).
  • UTS Ultimate Tensile Strength
  • T 3 is too high, generally above 550° C., some pearlite structure may form during the following slow cooling step at cooling rate V 3 . If T 3 is too low, below Ms point, bainitic structure may be obtained in an insufficient amount in the final microstructure. If V 3 is too fast, too much martensite is obtained in the final microstructure, and it is impossible to ensure sufficient elongation. If V 3 is too small, too less martensite is obtained in order to guarantee the high strength. Moreover, the combination of T 3 and V 3 is selected such that the article obtained comprises a multiphase microstructure comprising by volume fraction 55-90% of bainitic ferrite, 5-15% retained austenite and 5-30% martensite.
  • a relatively high UTS is achieved if the multiphase microstructure comprises 55-85% bainitic ferrite, 5-15% retained austenite and 10-30% martensite. Generally the higher the interrupt temperature T 3 , the lower V 3 has to be in order to get this multiphase microstructure.
  • the steel, in particular TBF steel, in the article as manufactured is characterized by a multiphase structure comprising, more preferably consisting of, carbide free bainitic ferrite, carbon enriched retained austenite and a relatively small amount of martensite.
  • the mother-phase structure comprises fine plates of essentially carbide free bainitic ferrite.
  • the formation of such a microstructure is due to the fact that the precipitation of cementite during bainitic transformation is suppressed by alloying the steel with a sufficient amount of Si and/or Al, which have very low solubility in cementite and greatly retards growth of cementite from austenite. Carbon that is rejected from the bainitic ferrite enriches the residual austenite, thereby transforming to martensite during cooling after bainitic transformation or stabilizing it down to room temperature.
  • the advantages of this type of microstructure are manifold.
  • the bainitic ferrite in TBF steel is present in the form of plates with an ultra fine grain size, usually the length ranging up to about 15 micrometer at most and the thickness ranging up to 0.3 micrometer at most (typically ⁇ 10 ⁇ m long and ⁇ 0.2 ⁇ m thick). Furthermore the strength and ductility are improved simultaneously.
  • the high flow stresses are due to the small thickness of the bainitic laths and to the absence of proeutectoid polygonal ferrite contrary to existing TRIP (transformation induced plasticity) steels. It is assumed that the retained austenite offers an additional TRIP effect, and that it is useful for improving total elongation.
  • the multiphase microstructure according to the invention can be obtained by designing steel with a specific composition and by applying careful control of the thermomechanical treatment process as discussed above.
  • a preferred embodiment of the present invention relates to a method of hot forming a steel blank into an article, wherein the method comprises heating the steel blank to an austenitizing temperature T 1 , advantageously in the range of Ac3+20° C.
  • the steel comprises the following elements (in wt. %):C 0.15-0.45, Si 0.6-2.5, Mn 1.0-3.0, Mo 0-0.5, Cr 0-1.0, P 0.001 - 0.05, S ⁇ 0.03, Ca ⁇ 0.003, Ti 0.1 or less and V 0.1 or less and the balance Fe and other inevitable impurities.
  • the steel may also contain Al less than 1.5%, partially replacing the same amount of Si, provided that the sum of Si and Al is in the range of 1.2-2.5%.
  • the amounts of Mn and Cr satisfy Mn+Cr ⁇ 3%, while also preferably, the amounts of C and Mo satisfy C+1 ⁇ 3 Mo ⁇ 0.45% for better control of the multiphase microstructure.
  • C is an element for securing high strength, and for securing retained austenite.
  • C is added in an amount of 0.15% or more to form the desired multiphase microstructure to achieve ultra-high strength and ductility. Meanwhile, when the C content exceeds 0.45%, it is difficult to obtain the multiphase microstructure through the method according to the invention comprising a contiguous cooling subprocess. Moreover, there is a great possibility that the toughness and weldability of the steel sheet will be deteriorated.
  • C is preferably present in an amount of 0.2-0.4%, more preferably 0.2-0.35%.
  • Mn is one of the main elements in the steel composition according to the invention.
  • the functions of Mn include stabilizing the austenite and obtaining the desired multiphase microstructure. If Mn is less than 1.0%, the effects are not sufficiently marked. Whereas if the content exceeds 3%, a fully martensite structure is easily created. As a result, the steel is hardened and embrittled during press forming.
  • Mn is an element that is useful in lowering the Ac3 temperature. A higher Mn content is advantageous in lowering the temperature necessary for hot press forming.
  • the Mn content is limited to the range of 1.0-3.0%, preferably 1.5-2.5% and more preferably 1.6-2.5%, even more preferably 1.7-2.4%.
  • Si is an element effective for reinforcing a solid solution, and is useful for suppressing production of carbide due to decomposition of retained austenite.
  • carbides either transition carbide or cementite
  • Si suppresses the precipitation of brittle cementite during bainite formation, and hence results in an improvement in formability and toughness.
  • a minimum of 1.0% Si is needed to form carbide free bainite.
  • Si is also known to deteriorate galvanizability due to the formation of oxides adherent to the steel substrate. Therefore, the upper limit of Si is controlled below 2.5%.
  • the Si content is advantageously limited to the range of 1.2-2.5% and more preferably to the range of 1.4-2.0%.
  • Al is also an element useful for suppressing production of carbide due to decomposition of, particularly, retained austenite. Partial replacement of Si by a same amount of Al has been shown to effectively retard cementite formation without a detrimental effect on hot-dip coatability in TBF steels. However, a high concentration of Al leads to higher possibility of polygonal ferrite to be generated, which is less effective than fine plate ferrite in view of strength. A full substitution of Si by an equivalent amount of Al leads to a marked deterioration of the strength-ductility balance. If added, the amount of Al is limited to 1.5% or smaller.
  • P is an element useful for maintaining desired retained austenite, and its effect is exerted by an amount of P of 0.001% or larger, more preferably 0.005% or larger, but P may deteriorate the workability of the steel when it is added in an excess amount. Accordingly, the P content is preferably limited to 0.05% or less.
  • S is a harmful element which forms sulfide based inclusions such as MnS, which initiates crack formation, and deteriorates processibility. Therefore, it is desirable to reduce the amount of S as much as possible. Accordingly, S is controlled to 0.03% or smaller.
  • Mo and Cr serve to improve the hardenability of the steel and facilitate the formation of bainite ferrite. At the same time, they are elements having similar is effectiveness useful for stabilizing retained austenite. Therefore, Mo and Cr are very effective for process control. It is advantageous that each of them is contained at 0.05% or larger. However, when each of them is added excessively, the effect is saturated and a higher addition is not economical. Therefore, the amount of Mo is 0.5% or smaller, and the amount of Cr is 1% or smaller.
  • Ti and V have the effect of forming strengthening precipitates and refining microstructure.
  • the amount of each of them is 0.1% or smaller, preferably 0.05% or smaller.
  • Ca is an element effective for controlling a form of sulfide in the steel, and improving processibility. It is recommended that Ca is contained at 0.0003% or more. However, when it is added excessively, the effect is saturated. Therefore, the preferred amount is 0.0003-0.003%.
  • the heat treatment described above may be carried out by heating and cooling in a continuous annealing facility (CAL), hot press forming facility, salt bath or the like.
  • CAL continuous annealing facility
  • hot press forming facility salt bath or the like.
  • the first combined deformation/cooling step d) is performed in a hot forming facility.
  • the second cooling step e) is performed in air or in stock outside the hot forming facility.
  • the steel of the formed article has an ultimate tensile strength (UTS) of at least 1400 MPa, advantageously at least 1500 MPa, more preferably at least 1600 MPa, and most preferably at least 1700 MPa.
  • UTS ultimate tensile strength
  • the steel of the formed article has a total elongation of at least 8%, preferably at least 10%, more preferably at least 12%, and most preferably at least 14%.
  • the heat treatment processes can be simply performed by applying the hot (press) forming in a standard hot forming facility with only modification of the simultaneous cooling process, including cooling interrupt temperature and velocities.
  • the heat blank is inserted into the die sets of a hot press, in which the blank is shaped and cooled.
  • the transfer time e.g. 5 to 10 s
  • the cooling rate V 2 of the steel part in the forming tool depends on the deformation and on the quality of the contact between the tool and the steel blank.
  • the forming tools may be cooled for example by using circulation of a liquid to ensure that the cooling rate is high enough (>25° C./s) during quenching in the press mould.
  • the interrupt cooling temperature can be controlled by the time for separation of the pressing tools.
  • the formed article is then removed from the mould and cooled to room temperature in air.
  • the formed articles, e.g. sheets, may also be stacked and then cooled to ambient temperature in air.
  • the present invention provides a steel article, preferably formed according to the method of the present invention, wherein the steel has a microstructure comprising by volume fraction:
  • the steel has an Ultimate Tensile Strength of at least 1400 MPa, advantageously at least 1500 MPa, preferably at least 1600 MPa, more preferably at least 1700 MPa and/or a total elongation of at least 8%, preferably at least 10%, more preferably at least 12%, most preferably at least 14%.
  • the present invention provides a steel strip, sheet or strip for use in a thermomechanical treatment, in particular a hot forming method according to the invention described above, having a composition, in weight %:
  • compositions of the steel strip, sheet or blank according to the third aspect of the invention comprises, the alloying elements are present in, expressed in weight %:
  • the articles obtained from the strip, sheet or blank exhibit a high tensile strength by rapid cooling after heat treatment and achieve a high increment in yield is strength after heat treatment, especially for painting. Based on these advantages, excellent impact properties of the steel article according to the present invention are attained. In addition, the steel article according to the present invention advantageously exhibits good adhesion to a coating layer. Furthermore, other advantages of the steel article according to the present invention are good surface appearance and superior corrosion resistance after painting.
  • FIG. 1 A schematic representation of a practical embodiment of the method according to the invention is shown in FIG. 1 , showing a temperature vs. time plot.
  • a steel blank is heated at a heating rate of 15° C. to the austenitizing temperature T 1 in the range of Ac3+20° C. to Ac3+60° C. and soaked at that temperature during a soaking time t 1 .
  • the thus heated and soaked blank is transferred from the furnace to the hot forming facility, during which cooling by air occurs to some extent. Care is taken that the temperature T 2 is not decreased below Ar3 before hot press forming of the blank.
  • After hot press forming the blank thus formed is cooled down to the interrupt temperature T 3 at a rate of more than 25° C. Then air cooling is carried out.
  • Steels having compositions A-F as specified in Table 1 were cast to ingots of about 25 kg (100 ⁇ 110 ⁇ 330 mm). The ingots were reheated and then roughly hot rolled to slabs having a thickness of 40 mm. Then finish hot rolling was applied with the following process parameters: preheating at 1200° C. for 30 min; multi-pass rolling to thickness 4 mm (40-27-18-12-8-6-4 mm); and finishing rolling temperature 860 ⁇ 20° C. Controlled cooling at a rate 30° C./s to 600° C. in a run-out-table was carried out in order to simulate the commercially used coiling process. After the coiling process the steel plates contain a microstructure consisting of ferrite and pearlite and have a tensile strength less than 700 MPa. The plate was then cold rolled from 4 to 1 mm sheet.
  • the critical temperatures such as Ac3 and Ms were determined by applying standard dilatometric analysis to facilitate the determination of the temperatures in the process according to the invention.
  • the resulting cold rolled sheets were subjected to a heat treatment by using a CASIM simulator. Specifically, the steel sheets were heated to 870 to 920° C. at a rate of 15° C./s, holding the sheets at this temperature for 2 min, then cooling at a rate of 50° C./s to an interrupt temperature between 400 and 550° C., thereafter, cooling at a rate of 0.2 to 10° C./s to simulate different air cooling conditions.
  • Tensile tests were conducted by applying JIS 5 tensile test specimen to measure tensile strength and elongation of the specimens with the required microstructures.
  • the volume fraction of bainite and/or martensite in the microstructures was estimated by using metallographic characterisation in combination with dilatametric analysis.
  • the volume fraction of the retained austenite was determined by using TEM. Other measurements are standard.
  • the tensile test results and the invented alloys with the required the microstructure constituents are given in Table 2.
  • the conditions for the required multiphase microstructures of the alloys according to the invention can be obtained by careful adjustment of T 3 and V 3 .
  • the cooling rate V 3 can be controlled in a lower range 0.25 to 2° C./s; for alloys containing lower C or lower Mo, the cooling rate V 3 can be controlled in a higher range 2 to 10° C./s.
  • higher cooling rate will result in less bainitic ferrite, but relatively more martensite. Therefore higher strength will be obtained.
  • Lower cooling rate will result in more bainitic ferrite, but relatively less martensite, then higher elongation will be achieved.
  • the higher T 3 temperature is, the relatively more bainitic ferrite will be in the final microstructure for a given cooling rate, resulting in high strength but lower elongation.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Heat Treatment Of Steel (AREA)
US13/819,281 2010-10-12 2011-10-10 Method of hot forming a steel blank and the hot formed part Abandoned US20130192726A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP10013537.5 2010-10-12
EP10013537 2010-10-12
PCT/EP2011/005053 WO2012048841A1 (fr) 2010-10-12 2011-10-10 Procédé de formage à chaud d'un flan d'acier et pièce formée à chaud

Publications (1)

Publication Number Publication Date
US20130192726A1 true US20130192726A1 (en) 2013-08-01

Family

ID=43640446

Family Applications (1)

Application Number Title Priority Date Filing Date
US13/819,281 Abandoned US20130192726A1 (en) 2010-10-12 2011-10-10 Method of hot forming a steel blank and the hot formed part

Country Status (5)

Country Link
US (1) US20130192726A1 (fr)
EP (1) EP2627790B1 (fr)
JP (1) JP2013545890A (fr)
CN (1) CN103154279B (fr)
WO (1) WO2012048841A1 (fr)

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20160130675A1 (en) * 2013-05-28 2016-05-12 Salzgitter Flachstahl Gmbh Method for producing a component by hot forming a pre-product made of steel
US9475112B2 (en) 2011-06-10 2016-10-25 Kobe Steel, Ltd. Hot press-formed product and process for producing same
EP3045550A4 (fr) * 2013-09-10 2017-05-31 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Procédé pour fabriquer un article moulé à la presse, et article moulé à la presse
EP3327152A1 (fr) * 2016-11-29 2018-05-30 Tata Steel UK Ltd Procédé de formage à chaud d'une ébauche d'acier
WO2018115933A1 (fr) * 2016-12-21 2018-06-28 Arcelormittal Tôle d'acier laminée à froid à haute résistance présentant une formabilité élevée et son procédé de fabrication
CN109844158A (zh) * 2016-10-17 2019-06-04 塔塔钢铁艾默伊登有限责任公司 用于涂漆零件的钢基底
US10392677B2 (en) 2014-10-24 2019-08-27 Jfe Steel Corporation High-strength hot-pressed part and method for manufacturing the same
US20210047705A1 (en) * 2018-03-08 2021-02-18 Northwestern University Carbide-free bainite and retained austenite steels, producing method and applications of same
US20210189517A1 (en) * 2018-05-22 2021-06-24 Thyssenkrupp Steel Europe Ag Sheet Metal Part Formed from a Steel Having a High Tensile Strength and Method for Manufacturing Said Sheet Metal Part
CN113373288A (zh) * 2013-10-21 2021-09-10 麦格纳国际公司 用于修剪热成型部件的方法
US11124850B2 (en) * 2014-12-01 2021-09-21 Voestalpine Stahl Gmbh Method for the heat treatment of a manganese steel product, and manganese steel product having a special alloy
US11344941B2 (en) * 2011-07-21 2022-05-31 Kobe Steel, Ltd. Method of manufacturing hot-press-formed steel member
US12285794B2 (en) 2021-10-29 2025-04-29 Hyundai Steel Company Hot stamping component and method of manufacturing the same
US12540383B2 (en) 2023-08-07 2026-02-03 Colorado School Of Mines Modified hot-dip galvanize coatings with low liquidus temperature, methods of making and using the same

Families Citing this family (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
PL3290200T3 (pl) 2006-10-30 2022-03-28 Arcelormittal Powlekane taśmy stalowe, sposoby wytwarzania takich powlekanych taśm, sposoby zastosowania takich powlekanych taśm, półfabrykaty do wytłaczania przygotowane z powlekanych taśm, wyroby wytłaczane przygotowane z powlekanych taśm, wyroby zawierające takie wyroby wytłaczane
JP5883350B2 (ja) * 2011-06-10 2016-03-15 株式会社神戸製鋼所 熱間プレス成形品、その製造方法および熱間プレス成形用薄鋼板
JP5802155B2 (ja) * 2012-03-09 2015-10-28 株式会社神戸製鋼所 プレス成形品の製造方法およびプレス成形品
WO2014019844A1 (fr) * 2012-08-03 2014-02-06 Tata Steel Ijmuiden Bv Procédé permettant de produire une bande d'acier laminée à chaud, et bande d'acier ainsi produite
JP5862591B2 (ja) 2013-03-28 2016-02-16 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
DE102013010946B3 (de) * 2013-06-28 2014-12-31 Daimler Ag Verfahren und Anlage zum Herstellen eines pressgehärteten Stahlblechbauteils
CA2916941C (fr) * 2013-09-18 2018-01-09 Nippon Steel & Sumitomo Metal Corporation Corps moule par estampage a chaud et son procede de production
EP2851440A1 (fr) * 2013-09-19 2015-03-25 Tata Steel IJmuiden BV Acier pour formage à chaud
US10472698B2 (en) * 2014-10-03 2019-11-12 Nippon Steel Corporation Method of production of brazed joint and such a brazed joint
CN104513927B (zh) 2014-12-19 2017-04-05 宝山钢铁股份有限公司 一种抗拉强度800MPa级高强度高韧性钢板及其制造方法
CN104561790B (zh) * 2015-01-23 2017-11-28 宝钢特钢有限公司 一种1500MPa级高强度钢及其生产方法
EP3061837A1 (fr) * 2015-02-27 2016-08-31 Swiss Steel AG Produit longitudinal bainitique nu et son procédé de fabrication
EP3162558A1 (fr) * 2015-10-30 2017-05-03 Outokumpu Oyj Composant constitué d'un matériau composite métallique et procédé pour la fabrication du composant par formage à chaud
GB201521443D0 (en) * 2015-12-04 2016-01-20 Impression Technologies Ltd Method for operating a press for metal sheet forming
CN106048430B (zh) * 2016-07-06 2017-11-03 马钢(集团)控股有限公司 一种高韧性轨道交通用贝氏体钢车轮及其制造方法
CN106191666B (zh) * 2016-07-06 2018-01-02 马钢(集团)控股有限公司 一种低成本精节生产的轨道交通用贝氏体钢车轮及其制造方法
KR102048241B1 (ko) * 2016-11-25 2019-11-25 닛폰세이테츠 가부시키가이샤 ?칭 성형품의 제조 방법, 열간 프레스용 강재의 제조 방법, 및 열간 프레스용 강재
WO2018099819A1 (fr) * 2016-11-29 2018-06-07 Tata Steel Ijmuiden B.V. Procédé de fabrication d'un article formé à chaud, et article obtenu
CN106947907B (zh) * 2017-03-03 2018-12-07 北京科技大学 一种石墨化易切削钢高速线材的制备方法
US20180372146A1 (en) * 2017-06-26 2018-12-27 GM Global Technology Operations LLC Fine grain steel alloy and automotive components formed thereof
KR101978054B1 (ko) * 2017-09-27 2019-05-13 현대제철 주식회사 핫 스탬핑 부품의 제조방법
CN111254351B (zh) * 2020-01-21 2021-07-20 鞍钢股份有限公司 一种高性能热轧耐磨钢薄板及其生产方法
CA3177824A1 (fr) * 2020-05-18 2021-11-25 Timothy W. Skszek Procede pour le traitement d'un acier a haute resistance avance
KR102345608B1 (ko) * 2020-12-23 2021-12-30 현대제철 주식회사 핫 스탬핑 부품, 및 이의 제조 방법
DE102021119047A1 (de) * 2021-07-22 2023-01-26 Thyssenkrupp Steel Europe Ag Verfahren zur Herstellung eines kaltgewalzten Stahlflachprodukts mit einem bainitischen Grundgefüge und kaltgewalztes Stahlflachprodukt mit einem bainitischen Grundgefüge

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SE435527B (sv) 1973-11-06 1984-10-01 Plannja Ab Forfarande for framstellning av en detalj av herdat stal
JP3854506B2 (ja) 2001-12-27 2006-12-06 新日本製鐵株式会社 溶接性、穴拡げ性および延性に優れた高強度鋼板およびその製造方法
KR100764253B1 (ko) 2005-01-28 2007-10-05 가부시키가이샤 고베 세이코쇼 내수소취화 특성이 우수한 고강도 스프링용 강
CN100510142C (zh) * 2005-01-28 2009-07-08 株式会社神户制钢所 耐氢脆特性优良的高强度螺栓
JP4716359B2 (ja) 2005-03-30 2011-07-06 株式会社神戸製鋼所 均一伸びに優れた高強度冷延鋼板およびその製造方法
EP1767659A1 (fr) 2005-09-21 2007-03-28 ARCELOR France Procédé de fabrication d'une pièce en acier de microstructure multi-phasée
DE112006003169B4 (de) 2005-12-01 2013-03-21 Posco Stahlbleche zum Warmpressformen mit ausgezeichneten Wärmebehandlungs- und Schlageigenschaften, daraus hergestellte Warmpressteile und Verfahren zu deren Herstellung
KR100990772B1 (ko) * 2005-12-28 2010-10-29 가부시키가이샤 고베 세이코쇼 초고강도 박강판
EP1832667A1 (fr) * 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
EP1990431A1 (fr) * 2007-05-11 2008-11-12 ArcelorMittal France Procédé de fabrication de tôles d'acier laminées à froid et recuites à très haute résistance, et tôles ainsi produites

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9475112B2 (en) 2011-06-10 2016-10-25 Kobe Steel, Ltd. Hot press-formed product and process for producing same
US11344941B2 (en) * 2011-07-21 2022-05-31 Kobe Steel, Ltd. Method of manufacturing hot-press-formed steel member
US20160130675A1 (en) * 2013-05-28 2016-05-12 Salzgitter Flachstahl Gmbh Method for producing a component by hot forming a pre-product made of steel
EP3045550A4 (fr) * 2013-09-10 2017-05-31 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Procédé pour fabriquer un article moulé à la presse, et article moulé à la presse
CN113373288A (zh) * 2013-10-21 2021-09-10 麦格纳国际公司 用于修剪热成型部件的方法
US10392677B2 (en) 2014-10-24 2019-08-27 Jfe Steel Corporation High-strength hot-pressed part and method for manufacturing the same
US11124850B2 (en) * 2014-12-01 2021-09-21 Voestalpine Stahl Gmbh Method for the heat treatment of a manganese steel product, and manganese steel product having a special alloy
CN109844158A (zh) * 2016-10-17 2019-06-04 塔塔钢铁艾默伊登有限责任公司 用于涂漆零件的钢基底
EP3327152A1 (fr) * 2016-11-29 2018-05-30 Tata Steel UK Ltd Procédé de formage à chaud d'une ébauche d'acier
US11279984B2 (en) 2016-12-21 2022-03-22 Arcelormittal High-strength cold rolled steel sheet having high formability and a method of manufacturing thereof
WO2018116155A1 (fr) * 2016-12-21 2018-06-28 Arcelormittal Tôle d'acier laminée à froid à haute résistance présentant une formabilité élevée et son procédé de fabrication
WO2018115933A1 (fr) * 2016-12-21 2018-06-28 Arcelormittal Tôle d'acier laminée à froid à haute résistance présentant une formabilité élevée et son procédé de fabrication
US20210047705A1 (en) * 2018-03-08 2021-02-18 Northwestern University Carbide-free bainite and retained austenite steels, producing method and applications of same
US11920209B2 (en) * 2018-03-08 2024-03-05 Northwestern University Carbide-free bainite and retained austenite steels, producing method and applications of same
US20210189517A1 (en) * 2018-05-22 2021-06-24 Thyssenkrupp Steel Europe Ag Sheet Metal Part Formed from a Steel Having a High Tensile Strength and Method for Manufacturing Said Sheet Metal Part
US12285794B2 (en) 2021-10-29 2025-04-29 Hyundai Steel Company Hot stamping component and method of manufacturing the same
US12540383B2 (en) 2023-08-07 2026-02-03 Colorado School Of Mines Modified hot-dip galvanize coatings with low liquidus temperature, methods of making and using the same

Also Published As

Publication number Publication date
EP2627790A1 (fr) 2013-08-21
WO2012048841A1 (fr) 2012-04-19
CN103154279A (zh) 2013-06-12
JP2013545890A (ja) 2013-12-26
EP2627790B1 (fr) 2014-10-08
WO2012048841A8 (fr) 2013-04-25
CN103154279B (zh) 2015-09-23

Similar Documents

Publication Publication Date Title
EP2627790B1 (fr) Methode pour deformation a chaud d' une tole d'acier et tole d'acier
US12503739B2 (en) Method for manufacturing a high strength steel product and steel product thereby obtained
EP3548641B1 (fr) Procédé de fabrication d'un article formé à chaud et article ainsi obtenu
US8888934B2 (en) Method for producing a formed steel part having a predominantly ferritic-bainitic structure
EP3556896B1 (fr) Tôle d'acier laminée à froid à haute résistance présentant une excellente limite d'élasticité, une excellente ductilité et une excellente capacité d'expansion de trou, et tôle d'acier galvanisée par immersion à chaud
US12286682B2 (en) High strength steel product and a process to produce a high strength steel product
US8999085B2 (en) High manganese steel strips with excellent coatability and superior surface property, coated steel strips using steel strips and method for manufacturing the steel strips
CN103562417B (zh) 制造极高强度马氏体钢的方法及如此获得的板材或部件
US20130295402A1 (en) Steel Sheet for Formed Member Having Enhanced Ductility, Formed Member, and Method for Manufacturing the Formed Member
EP3395993B1 (fr) Tôle d'acier haute résistance laminée à froid de type à haute limite d'élasticité et son procédé de fabrication
KR20170106480A (ko) 핫 스탬핑용 강판, 핫 스탬핑 방법 및 핫 스탬핑된 부품
US20190185951A1 (en) Method for producing a high-strength steel strip with improved properties for further processing, and a steel strip of this type
CN112585284A (zh) 由钢形成的具有高抗拉强度的板材成型件及其制造方法
EP4114994B1 (fr) Tôle d'acier laminée à froid à résistance élevée et recuite après galvanisation et son procédé de fabrication
US12509740B2 (en) Hot rolled and steel sheet and a method of manufacturing thereof
CN111465710B (zh) 高屈强比型高强度钢板及其制造方法
KR101406444B1 (ko) 연신율 및 굽힘가공성이 우수한 초고강도 냉연강판 및 이의 제조방법
KR20250093772A (ko) 냉연강판 및 그 제조방법

Legal Events

Date Code Title Description
AS Assignment

Owner name: TATA STEEL IJMUIDEN B.V., NETHERLANDS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:CHEN, SHANGPING;LAHAYE, CHRISTIAAN THEODORUS WILHELMUS;REEL/FRAME:030078/0202

Effective date: 20130318

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION