US20090194004A1

US20090194004A1 - O/W wax dispersions and plaster products obtainable from them

Info

Publication number: US20090194004A1
Application number: US11/989,259
Authority: US
Inventors: Gernot Meyer; Thomas Haas
Original assignee: Individual
Current assignee: Individual
Priority date: 2005-07-26
Filing date: 2006-07-25
Publication date: 2009-08-06
Also published as: DK1907480T3; WO2007012316A1; AU2006274324A1; US8741056B2; DE502006004808D1; US20140245928A1; AU2006274324B2; DE102005035515A1; CA2614395C; ZA200800034B; US9981874B2; CA2614395A1; EP1907480B1; EP1907480A1; US20130305962A1; ATE442419T1; PL1907480T3

Abstract

The invention relates to O/W wax dispersions based on water, an emulsifier and a wax phase containing predominantly aliphatic hydrocarbons and polar compounds having chain lengths of at least 18 carbon atoms, and also plaster compositions comprising the O/W wax dispersion, and the use of the O/W wax dispersion.

Description

The invention relates to aqueous compounds containing waxes and gypsum products that can be manufactured from these, particularly aerated gypsum and plasterboard.
Gypsum is calcium sulphate that can be present with and without crystallisation water. Naturally occurring gypsum rock is calcium sulphate dihydrate (CaSO₄×2H₂O); the anhydrous form of calcium, sulphate is frequently referred to as anhydrite (CaSO₄). In the language of this application, “gypsum” refers to naturally occurring gypsum rock, the corresponding products of industrial processes and also the products obtained during the burning of these raw materials.
Gypsum is ideally suited as a construction and working material, due to the fact that it is easy to dehydrate (dehydration (1)). Dehydration is a reversible process. Exposure to energy drives some or all of the crystallisation water out of the calcium sulphate dihydrate. The reverse reaction after water is added (rehydration (2)) causes the previously burned, i.e. at least partially dehydrated gypsum, to become solid, forming a crystalline structure.
(CaSO₄×2H₂O)+T→(CaSO₄×0.5H₂O)+1.5H₂O
(CaSO₄×2H₂O)+T→CaSO₄×2H₂O
Gypsum stone+energy burnt gypsum (1)
Gypsum stone+energy burnt gypsum (2)
Naturally occurring gypsum varies in terms of its purity. Natural impurities include, e.g. limestone (e.g. muscovite or dolomite CaCO₃×MgCO₃), marl, mineral clay (e.g. montinorillonite or caolinite), and occasionally also sand, bitumen or a variety of salts. However, gypsum is also accessible from various technical processes. For example, flue-gas or REA gypsum with a high degree of purity is produced during the desulphurisation of flue gases.
Gypsum plasterboards are industrially manufactured building boards essentially made up of gypsum, the surfaces and possibly also the longitudinal edges of which are surrounded by firmly adhered paperboard to suit the application. The gypsum core surrounded by paperboard may contain air spaces and additives to achieve given properties.
Essential mechanical plasterboard properties result from the combined effect of the gypsum core and the paperboard casing. This involves the paperboard acting to reinforce the tension area, which in conjunction with the gypsum core gives the gypsum plasterboard the required strength and flexural rigidity. Various types of gypsum plasterboard (GKB) are distinguished, e.g. those that include additives to delay water absorption (impregnated gypsum plasterboard (GKBI) and impregnated fire-resistant gypsum plasterboard (GKFI)).
The water absorption and drying-out time of gypsum plaster-board is tested according to DIN 18180 (2 hours' spent in water).


	GKB/GKF	GKBI/GKFI

Water absorption in (w/w) %	30-50	<10
Drying-out time in hrs	70	15

Gypsum plasterboard is made from gypsum and additives for the gypsum core, as well as high-grade, repeatedly couched paperboard on large belt systems running continuously. Plaster of Paris (low-fired gypsum, produced at temperatures of roughly 120° C. to 180° C.) is frequently used. The production process comprises the following steps:

- paperboard supplied at the bottom,
- gypsum slurry supplied and distributed by the moulding station while paperboard is simultaneously supplied from above to form the top layer,
- hardening section,
- insertion in a dryer (usually after being divided up into individual boards) and
- delivery and possible trimming of the transverse edges and bundling of the boards.

In addition, there are also gypsum building materials in the form of wallboards made from gypsum, which are briefly referred to as “gypsum wallboards”. These are factory-made building panels made from plaster of Paris and water for non-weight-bearing structural components. Gypsum wallboards may contain fibres, fillers and additive substances, as well as other additives, and they may be coloured with pigments to distinguish them visually. They have smooth visible surfaces and are designed with alternating tongue and groove finishes on the abutting and storage surfaces. Here, too, water-repellent boards are known.
Board production takes place in largely automated production plants. Uniform, runny slurry is made from plaster of Paris, water and possibly additives in a dosage and mixing apparatus and used to fill the moulding boxes of the gypsum plasterboard machine. Once the mixture has set, the boards are ejected hydraulically and transported to the dryer. This is followed by drying in heated continuous driers. After drying, the boards are combined into packages or loaded onto pallets.
Gypsum fibre boards are furthermore referred to as gypsum-based plasterboard.
The production of gypsum with low bulk densities, particularly so-called foam or aerated gypsum, is the object of many patents and publications. The solutions known hitherto can generally be divided into two groups:
(1) Use of gas formers (propellants), which are added to the binding agent partially dry or are completely or partially added to the latter only during the aerated gypsum production process via the mixing water. The gas formers mainly comprise several material components in which a chemical reaction is activated by the water coupled with the creation of a gas. The resulting gas bubbles force the gypsum slurry up in the mould.
(2) Undermixing of separately prepared foam, which is added to the mixture in the mixer and immediately causes pores to form in the made-up material slurry. Foam is mainly produced by atomising water and air enriched with surface-active substances (surfactants).
It is also known that aerated gypsum elements produced using the aforementioned method are additionally water-repellent. This involves water-repellent additives being added to the mixer in the mixture preparation phase.
Gypsum products, particularly gypsum plasterboard, are provided with additives that delay water absorption, for use in damp areas. The impregnating additives are usually added to the gypsum mixture before the gypsum products are made and worked into it uniformly, after which the gypsum mixtures are usually dried in layers at a high temperature of e.g. 100 to 150° C. and then cooled. If the gypsum boards are covered with paperboard, they are referred to as gypsum plasterboards.
If the gypsum does not receive suitable water-repellent treatment, the effect of dampness can cause the paperboard to soften, leading to deformation. The use of gypsum plasterboard in damp rooms, such as bathrooms, laundry rooms, etc. is therefore problematic due to its diminishing rigidity and deformation. This has particularly serious effects when the gypsum plasterboard has ceramic tiles adhered to it, for example. The dampness causes the paperboard to soften, lose its inner rigidity and split under the weight of the ceramic tiles, causing the layer of paperboard attached to the boards to fall away. The destruction of the remaining gypsum paperboard is then only a matter of time.
In addition to the diminishing rigidity and deformation, corrosion and mildew can accelerate the destruction. Even the adhesive layer applied to the entire surface for the ceramic tiles, which usually has a synthetic base, cannot inhibit the effect of the dampness.
The use of silicon or siloxane emulsions/dispersions for impregnation is known. In addition, dispersions based on paraffin or montan waxes are known. However, polymers and resins are also used, which do not fall into the wax category. Polyvinyl alcohols are referred to as polymers. The wax components are in some cases also added to the gypsum mixture in powder form. Mixtures of asphalt or bitumen dispersions, in some cases used in combination with polyvinyl alcohols, in which a silicon compound or a synthetic resin emulsion has been added to the gypsum, are likewise known from the literature.
However, it is difficult to obtain a satisfactory water-repellent or hydrophobic product, which is sufficiently hydrophobic and, at the same time, facilitates the necessary foam stability to produce an aerated product.
U.S. Pat. No. 3,935,021 describes a gypsum wallboard in which polyvinyl alcohol and a wax-asphalt emulsion are introduced into the gypsum core. Wax-asphalt emulsions are widely used in gypsum wallboards, although certain disadvantages are associated with their use.
In U.S. Pat. No. 5,437,722 an aqueous emulsion is used to make gypsum products water-repellent, which comprises a hydrocarbon wax, a montan wax and an emulsifier/stabiliser system with the addition of polyvinyl alcohol.
WO 98/09.925 describes an aerated gypsum product, which is made water-repellent through the inclusion of an aqueous emulsion, which comprises a hydrocarbon wax, a montan wax and a colloid-stabilised emulsifier system.
Other aqueous wax dispersions for making gypsum products water-repellent, which contain starch, long-chain alkyl phenols, saponified montan waxes, surfactant, complexing agents and paraffin waxes are known from U.S. Pat. No. 6,585,820. U.S. Pat. No. 6,595,553 also mentions surfactant, montan wax and paraffin wax as an integral part of the aqueous wax dispersion.
The problem addressed by the present invention is that of finding a water-repelling agent that is suitable for both traditional gypsum plasterboard and also for the technically more complex production of aerated gypsum. A further problem facing the invention is that of guaranteeing sufficient vapour permeability, despite the water-repellent nature. Furthermore, the wax additive must improve the flow performance of the gypsum mixture, bring about a slight change in the reinforcing behaviour of the gypsum, cause a significant improvement in the paperboard adhesion and have a very slight effect on foaming in the process.
The effectiveness of wax dispersions in gypsum products is crucially dependent on the composition. It is obviously important for the internal surface of the micropores to be sealed in the gypsum. On the other hand, the pores must not be completely closed off, in order to retain the desired vapour permeability. This cannot be achieved with pure hydrocarbon dispersions according to our findings. In the past, montan wax was used here in the mixture with paraffin. Montan wax is a hard fossil wax of vegetable origin, which has survived the carbonisation process virtually unchanged. It therefore occurs in some brown coal as an extractable element. Important chemical parameters include the acid number (AN) and saponification number (SN) of the montan wax. Furthermore, a small number of hydrocarbons are contained in montan waxes, but not unsubstantial proportions of montan resins and asphalt substances, whereby the latter contain a not unsubstantial proportion of inorganic ash components (0.4 to 4% by wt.).
Montan resins and ash components may affect the colour if, for example, a particularly light-coloured gypsum is required when the material is used in visible construction work. The hydrocarbon chains in the wax acids and wax alcohols have a chain length of 20 to 34 C units with a maximum of around 30 C units. In this case, the focus lies on chains with a straight-line number of carbon atoms.
When using wax dispersions in impregnated gypsum plasterboard (GKBI) and impregnated fire-resistant gypsum plasterboard (GKFI), it is generally of particular significance that these do not have a negative effect on the paperboard's adhesion to the surface of the gypsum core. Furthermore, the emulsifier systems must also be based on optimum adhesion of the paperboard layer and minimum interference with the foaming behaviour of the gypsum slurry. Surprisingly, it was found that the water-repelling effect in gypsum products known hitherto predominantly from wax dispersions containing montan wax can also be achieved with other specially selected polar synthetic and natural components. Apart from paraffin, longer-chain alphaolefins (hydrogenated and/or not hydrogenated) and Fischer-Tropsch waxes can also be used as the basic wax phase. Also capable of being used in the composition are natural waxes, fats, fatty alcohols and synthetic and synthetically modified natural resin components.
It emerged that the desired water-repellence could also be achieved with the help of wax phases without montan wax. In this case, other wax phases and also other polar additives were identified as useable. This produces lighter/whiter gypsum products that can also be used for visible construction, as the wax phases, particularly the additives used, display significantly lower ash contents or none at all and also contain no dark asphalt and resin components.
The O/W wax dispersion according to the invention for use in gypsum products consist of:

- at least 30% by wt., particularly 30 to 80% by wt., preferably around 40 to 65% by wt., water,
- at least 20% by wt., particularly 70 to 20% by wt., preferably 35 to 60% by wt, wax phase as the disperse phase, wherein the wax phase or the total substances used to create the wax phase (i.e. before further saponification, where appropriate, through optional alkalisation or the alkali/earth alkali addition) display a saponification number greater than 0.2 mgKOH/g,
- at least 0.1% by wt., particularly 0.5 to 5% by wt., of an emulsifier or thickening agent as the dispersal agent, and
- maximum 20% by wt., particularly under 10% by wt., other substances, particularly as a component of the continuous phase,
  wherein the wax phase consists of the following, each based on the wax phase:
(a) 50 to 98% by wt. aliphatic hydrocarbons (HC) or an HC mixture, each with a solidification point above 50° C. and below 95° C., particularly 55 to 80° C.,
(b) 2 to below 50% by wt., particularly 5 to 20% by wt., from polar, long-chain compounds with chain lengths of at least 18 carbon atoms, particularly aliphatic, containing
- at least one carboxyl group, possibly
- partially or fully derivated,
- an ether group and/or
- at least one hydroxyl group (—OH)
- per molecule, but no more than three of the afore-mentioned groups together, particularly polar, long-chain compounds, which contain per molecule at least one carboxyl group, possibly partially or fully derivated, alongside possibly up to two other groups per molecule, including the carboxyl group, possibly derivated,
  and possibly
(c) maximum 10% by wt., particularly below 5 and preferably below 0.5% by wt., other substances solid at room temperature, particularly aromatic-free, or none and
(d) maximum 3% by wt. substances liquid at room temperature (at room temperature and normal pressure), particularly below 1.5% by wt.

Advantageous embodiments are the subject of the dependent claims or are described below. Also claimed are gypsum compositions, as described above, containing wax dispersions and the use of wax dispersions in such gypsum compounds or else the gypsum products described above.
Substances that can be used as aliphatic hydrocarbons according to the invention are paraffin, synthetic Fischer-Tropsch waxes and alphaolefins (AO, hydrogenated and not hydrogenated) with a solidification point of over 50° C. and below 95° C. and, particularly, with average C chain lengths greater than 25 in each case.
Polar compounds within the meaning of the present invention are compounds displaying hydrocarbon chains with per molecule over 18 C atoms and at least one hydroxyl group, an ether group and/or a carboxyl group (—C(═O)O—), possibly also derivated, i.e. esterified or saponified. The polar compounds preferably display no more than three of the aforementioned groups or a total of three polar groups, particularly one or two groups, per molecule overall.
The polar compounds may be oxidised and possibly also partially saponified Fisher-Tropsch waxes, oxidised paraffin, oxidised polyethylene, so-called PE wax esters (jointly referred to as oxidised hydrocarbons (HC) or partially saponified oxidised HC's) and modified natural and/or synthetic resins, as well as natural waxes such as beeswax and, in particular, carnauba wax. Furthermore, fats (triglycerides), e.g. of vegetable origin, such as palm, soya and rutabaga fats, are suitable. The acid groups contained in the polar additives may be saponified during the course of the wax dispersion production with the aid of alkaline substances (e.g. potassium or caustic soda). These lyes are preferably overdosed in this case, so that pH values of over 11 are obtained. This also has a favourable effect on the resistance of the wax dispersions to biological decomposition and mildew. Synthetically modified, particularly esterified, colophonium resins (colophony) such as glycerine and/or pentaerythrite maleic acid colophonium resins, preferably combined particularly with oxidised HC's and/or partially saponified oxidised HC's are also suitable.
It is particularly preferable for the wax dispersion to contain carnauba wax as a constituent part of the polar compounds, particularly at 1 to 20% by wt., particularly 1 to 15% by wt., relative to the wax phase.
Particularly advantageous are mixtures of polar compounds, which contain as polar compounds the above oxidised hydrocarbons (HC) or partially saponified, oxidised HC's (greater than 1% by wt.) and carnauba wax (greater than 1% by wt.) or the above oxidised hydrocarbons (HC) or partially saponified, oxidised HC's (greater than 1% by wt.) and the above synthetically modified colophonium resins or aliphatic hydrocarbon resins (greater than 1% by wt.). The percentages by weight each relate to the wax phase (=100% by wt.).
The water-repellent effect is reinforced if the polar compounds contain as the predominant constituent part oxidised and possibly also partially saponified Fischer-Tropsch waxes, oxidised paraffin, oxidised polyethylene, so-called PE waxes and, as the lesser component, fats (e.g. palm fats or soya oils) and/or fatty alcohols (e.g. Nafol® 20+). This produces synergistic effects. In other words, the reduction in water absorption when additives are combined increases even more than can be expected from the sum of the individual effects.
In this case, the wax phase is preferably added to the gypsum slurry in the form of an aqueous wax dispersion, as gypsum board production is water-based and the dosing of the wax phase can therefore be significantly more accurate. Furthermore, the preferably small particle size of the disperse wax phase (average particle size less than 2 μm and particularly roughly 1 μm) ensures a particularly uniform distribution of the active substance in the gypsum slurry.
In principle, all types used for the production of wax dispersions, i.e. non-ionic, anionic and cationic emulsifier types, but also combinations of these (non-ionic with anionic and non-ionic with cationic) are suitable as emulsifiers. Non-ionic and anionic emulsifiers are particularly suitable. Furthermore, emulsifiers that achieve stabilisation by concentrating the water phase are also suitable. These may be natural resins, for example, (Gum Ghatti, derivated cellulose) or xanthane polymers or else polysaccharide, but also inorganic substances of the bentonite type. Particularly suitable as emulsifiers are sulphonates such as naphthaline sulphonate and/or lignin sulphonate, preferably along with a thickening agent such as Gum Ghatti, in particular.
Furthermore, polyvinyl alcohols may be added to the wax dispersion, particularly up to 0.5 to 4% by wt. relative to the wax dispersion, which are available, for example, as partially hydrolised ethylene vinyl acetate polymers, but also produced from acrylates and other polyvinyl esters. Degrees of hydrolysis of over 70%, particularly over 85%, are desirable, but not a requirement.
The compositions according to the invention are advantageously wax dispersions, which can be produced with the aid of homogenisers. In this case, at least two phases are combined with one another (pre-emulsion).
At least the wax-containing phase is heated above the solidification point for this, in order to melt the wax. The other phase is the aqueous phase. This is preferably mixed with the emulsifier and is advantageously heated likewise.
The pre-emulsion is then passed through the circuit e.g. via splitting homogenisers, until the desired particle size of the wax phase is achieved. The emulsion is then cooled to temperatures below the solidification point of the wax phase. The individual wax particles of the disperse phase are evenly distributed in the aqueous, continuous phase by the process and a wax dispersion with prolonged stability is thereby obtained. The wax dispersion is thereby created. This is an oil in water (O/W) wax suspension with an average particle diameter of particularly 0.1 to 10 μm, advantageously 0.5 to 2 μm. The wax dispersion according to the invention is particularly suitable for the production of the water-repellent gypsum compositions described above, particularly those containing or comprising foamed gypsum or aerated gypsum and, in particular, coated gypsum plasterboard, preferably using the aforementioned gypsum.
FIG. 1 shows how the O/W emulsions are typically produced. In a wax boiler (1) fitted with a temperature sensor and temperature monitoring system, the wax emulsifier (2), water and hot steam (3) are produced, agitated and moved into the pre-emulsion boiler (4) by means of a pump (5), where the water-emulsifier mixture (6) is added. Delivery and transfer into the homogeniser (8) takes place using the pump (7). By means of a cooling medium (9), the temperature of the emulsion is lowered in the cooling system (10), e.g. to 30° C., in order to obtain the finished wax dispersion (11).

EXPERIMENTS

The degree of water repellence can be determined by subjecting the gypsum body to an immersion test. This involves the water absorption being determined in % by wt. after a 120 minute immersion period (H₂O 120 mins column in the following table). Suitable threshold values in this case are <10% by wt. and, particularly, <5% by wt. water absorption.
Table 1 shows the data for the finished wax phases (% stands for % by wt. in each case). It emerges that predominantly hard wax phases (needle penetration at 25° C.<20 [0.1 mm] in accordance with ASTM D1321) with solidification points of between 60 and 80° C. and also acid numbers (DIN 51558) of between 0 and 10 (mgKOH/g) and also saponification numbers from 0 to 20 mgKOH/g have a beneficial effect on water repellence. This produces the values required by DIN 18180 of <10% by wt. water absorption. The water absorption is therefore significantly reduced compared with the blind value (31%) of the natural gypsum used in this case, which demonstrates the effect of the wax mixtures used as wax dispersions. The wax dispersions (WD) were made according to the following suggested formulation:
60% by wt. water; 3% by wt. Marlophen® NP 10 (non-ionic surfactant from Sasol Olefins and Surfactants GmbH on an ethoxylate base); 1% by wt. KOH (45% by wt.) and 36% wax phase.

Laboratory Production of the Wax Dispersion:

The water was heated to approx. 80° C. along with the surfactant and the KOH and agitated for roughly 20 mins. The molten (80-100° C.) wax phase was then added and agitated for a further 5 minutes. The pre-emulsion was added to the homogeniser and passed through the circuit for 1 minute, after which it was homogenised for 1 minute at a pressure of roughly 200 bar. The wax emulsion was then cooled to room temperature during which the wax particles solidified and the wax dispersion was produced.

TABLE 2

Substances used

Name	Type	Manufacturer

Paraffin	Sasolwax 6403 (Fully Paraffin)	Sasol Wax GmbH
	EP 64/66
Carnauba wax	Natural palm wax	Kahl & Co
Resin	Escorene 1102 F, aliphatic	Exxon Mobil
	hydrocarbon resin

Key to Table 1

(*) Blind value of the untreated natural gypsum 31%
(**) These two dispersions serve for comparison purposes with the state of the art
(1) Solidification point ASTMD 938
(2) Needle penetration ASTM D 1321 at 25° C.
(3) Acid number according to DIN 51558
(4) Saponification number according to DIN 51559
(5) Water absorption according to DIN 81180
(6) Internal house methods
+ better than blind value (possibly better than gypsum value by how much)
= equal to blind value—not measured

TABLE 1

Properties of different wax dispersions

Data

				Foam	H₂O	Paper	Start of	End of	Flow
	PenN25	AN	SN	reduction	120 min	adhesion	hardening	hardening	measure
EP	(1)	(2)	(3)	(4)	(5)	(6)	(6)	(6)	(6)

Composition

unit

No.	Dispersion	(° C.)	(0.1 mm)	(mgKOH/g)		(% by wt.)	Min	(*)

*	Gypsum blind value						31	=	6	9	=
VI *	Montan wax/paraffin	70.5	10	3	8.7	=	2.4	+	+2	+4	Higher
**
V2	Montan wax/paraffin	64.5	11	3.1	9	=	2.5	+	+2	+4	Higher
**
1	Carnauba wax/	66	16	0.3	1.4	=	2.3	+	=	+4	Higher
	paraffin (2.5%
	carnauba)
2	Carnauba wax/	65	11	0.5	4.1	Smaller	4.6	+	+2	+2	=
	paraffin (5%
	carnauba)
3	Carnauba wax/	67	11	1	8.2	=	3.6	+	=	+4	Thicker
	resin/paraffin
	(10% carnauba,
	5% escorez)
4	Carnauba wax/	66	19	1	8.2	−	6	−	−	−	−
	paraffin (10%
	carnauba wax)

Claims

1. An O/W wax dispersion comprising:

at least 30% by wt. water,

at least 20% by wt. wax phase as the disperse phase, wherein the wax phase or all of the substances used to create the wax phase have a saponification number greater than 0.2 mgKOH/g,

at least 0.1% by wt. of an emulsifier or thickening agent as dispersing adjuvant, and

wherein the wax phase comprises the following, based on the wax phase:

(a) 50 to 98% by wt. aliphatic hydrocarbons (HC) or mixtures thereof, each with a solidification point above 50° C. and below 95° C.,

(b) 2 to below 50% by wt. from polar, long-chain compounds with at least 18 carbon atoms, containing

at least one carboxyl group, optionally partially or fully derivated, and/or

an ether group and/or

at least one hydroxyl group (—OH)

per molecule, but no more than three of the afore-mentioned groups together,

and optionally a maximum of 20% by wt. other substances wherein

(c) a maximum of 10% by wt. of said other substances are solid at room temperature and

(d) a maximum of 3% by wt. of said other substances are liquid at room temperature,

wherein the wax phase comprises carnauba wax, esterified colophonium resins and/or beeswax and the wax dispersion has a pH value greater than 11.

2. (canceled)

3. The wax dispersion according to any one of claims 1 or 25, characterised in that over 0 to 10% by wt., particularly 1 to 3% by wt., water-soluble alkaline substances, optionally at least partially bound through the saponification of acid groups, are contained or added.

4. The wax dispersion according to any one of claims 1 or 25, characterised in that the HC's are selected from:

petroleum paraffin (PP) with over 25 carbon atoms on average,

synthetic alphaolefins (hydrogenated or not hydrogenated) (AO) with over 30 carbon atoms on average,

Fisher-Tropsch (FT) waxes with over 25 carbon atoms on average and

mixtures thereof.

5. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax phase or the total substances used to create the wax phase has a saponification number of 0 to 40 mgKOH/g, particularly 0 to 7 mgKOH/g, before the possible (further) saponification or (further) alkali/earth alkali addition.

6. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax phase or the total substances used to create the wax phase has a saponification number of over 0.2 to 120 mgKOH/g, particularly 1 to 20 mgKOH/g, before the possible (further) saponification or (further) alkali/earth alkali addition.

7. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax phase has a colour number below 0.5 (according to ASTM D 1500).

8. The wax dispersion according to any one of claims 1 or 25, characterised in that the polar compounds are oxidised HC's, comprising oxidised FT and/or polyethylene types and/or ethers, alone or in mixtures, particularly oxidised HC's and/or partially saponified oxidised HC's or mixtures of carnauba wax and oxidised HC's, optionally each saponified.

9. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax phase has a solidification point of over 55° C. to 95° C., preferably 62° C. to 80° C.

10. The wax dispersion according to any one of claims 1 or 25, characterised in that the proportion of HC's being linear is greater than 50% by wt., particularly greater than 65% by wt.

11. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax phase has a pH value of 11 to 13.

12. The wax dispersion according to any one of claims 1 or 25, characterised in that the particle/droplet diameter of the disperse phase is 0.1 to 10 μm, advantageously from 0.5 to 2 μm.

13. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax phase has a needle penetration value from 7 to 17 (according to ASTM D 1321) at 25° C.

14. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax dispersion has a Brookfield viscosity at 25° C. (ASTM D 2983) of under 2000 mPas/s.

15. The wax dispersion according to any one of claims 1 or 25, characterised in that the polar, long-chain compounds are aliphatic.

16. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax phase contains less than 5% by wt. and particularly less than 0.5% by wt. other substances that are solid at room temperature, the O/W wax dispersion preferably contains no other solid substances at room temperature.

17. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax phase contains under 0.2% by wt. substituted phenols, such as alkyl phenols, preferably none.

18. The wax dispersion according to any one of claims 1 or 25, characterised in that the polar compounds comprise carnauba wax, particularly 1 to 20% by wt. relative to the wax phase.

19. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax dispersion comprises polyvinyl alcohols, particularly 0.5 to 4% by wt., optionally partially hydrolised (over 70%).

20. The wax dispersion according to any one of claims 1 or 25, characterised in that the polar compounds comprises esterified colophonium resins, beeswax and/or carnauba wax and/or mixtures of these, optionally each partially saponified.

21. The wax dispersion according to any one of claims 1 or 25, characterised in that the wax dispersion contains less than 5% by wt., particularly less than 2% by wt., montan waxes relative to the wax phase in each case, preferably none.

22. (canceled)

23. A gypsum composition containing over 50% by wt., particularly 50 to 70% by wt. gypsum, relative to calcium sulphate dihydrate, optionally hydrated, and 0.1 to 5% by wt., preferably 0.5 to 2.5% by wt., of the wax dispersion of claim 1.

24. The gypsum composition of claim 23, characterised in that the gypsum composition contains less than 5% by wt., particularly less than 2% by wt., montan waxes, relative to the wax phase in each case, preferably none.

25. A method of obtaining a wax dispersion comprising:

combining at least 30% by wt. water with at least 20% by wt. wax phase as the disperse phase, wherein the wax phase or all of the substances used to create the wax phase have a saponification number greater than 0.2 mgKOH/g, and

wherein the wax phase comprises the following, based on the wax phase:

at least one carboxyl group, optionally partially or fully derivated, and/or

an ether group and/or

at least one hydroxyl group (—OH)

per molecule, but no more than three of the afore-mentioned groups together,

and at least one emulsifier to form a mixture;

homogenizing the mixture, wherein the wax phase liquefies as a result of temperature rise during homogenization; and

cooling the homogenized mixture to solidify at least a part of the mixture.