US20080296662A1 - Discrete Trap Memory (DTM) Mediated by Fullerenes - Google Patents
Discrete Trap Memory (DTM) Mediated by Fullerenes Download PDFInfo
- Publication number
- US20080296662A1 US20080296662A1 US11/755,509 US75550907A US2008296662A1 US 20080296662 A1 US20080296662 A1 US 20080296662A1 US 75550907 A US75550907 A US 75550907A US 2008296662 A1 US2008296662 A1 US 2008296662A1
- Authority
- US
- United States
- Prior art keywords
- fullerenes
- layer
- dielectric layer
- oxide
- fullerene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A discrete trap memory, comprising a silicon substrate layer, a bottom oxide layer on the silicon substrate layer, a Fullerene layer on the bottom oxide layer, a top oxide layer on the Fullerene layer, and a gate layer on the top oxide layer; wherein the Fullerene layer comprises spherical, elliptical or endohedral Fullerenes that act as charge traps.
Description
- The present invention relates generally to discrete trap memories and, more particularly, to discrete trap memories that use Fullerenes to hold or place the trapped charge.
- Discrete Trap Memories (DTM) contribute substantially to the development of Flash memory.
FIG. 1 is a schematic drawing of DTM 100.Source 101 anddrain 102 are formed insubstrate 103, which is typically a silicon layer.Bottom oxide layer 104 is thermally grown onsilicon 103. Nitridelayer 105 is deposited onbottom oxide layer 104 and holdsdiscrete charge traps 106.Top oxide layer 107 is grown or deposited onnitride layer 105.Gate layer 108, which may be polycrystalline silicon or metal, is deposited ontop oxide layer 107. This structure is well known and is referred to as SONOS or MONOS. The local potential of the channel, and therefore the local threshold voltage, will be modified by charging of thediscrete charge traps 106 with electrons. TheDTM device 100 operates such that when a voltage higher than the threshold voltage is applied togate 108, a percolation path betweensource 101 anddrain 102 allows current to flow through the device. The course of the percolation path depends upon the distribution oftraps 106 as described, for example, in D. Ielmini et al., A new channel percolation model for V T shift in discrete-trap memories, Reliability Physics Symposium Proceedings, 42nd Annual 2004, 515-521 (25-29 Apr. 2004 IEEE International), the disclosure of which is hereby incorporated by reference herein in its entirety. - In accordance with a preferred embodiment of the present invention, a discrete trap memory comprises a silicon substrate layer, a bottom dielectric layer on the silicon substrate layer, a Fullerene layer on the bottom dielectric layer, a top dielectric layer on the Fullerene layer, and a gate layer on the top dielectric layer; wherein the Fullerene layer comprises spherical, elliptical or endohedral Fullerenes that act as charge traps.
- For a more complete understanding of the present invention, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawings, in which:
-
FIG. 1 is a diagram of a known discrete trap memory (DTM) device; -
FIG. 2A illustrates the distribution of charge traps in a known DTM; -
FIG. 2B illustrates a trapping layer when threshold voltage is applied to a DTM; -
FIG. 3A illustrates the distribution of charge traps in a known DTM; -
FIG. 3B illustrates a trapping layer when threshold voltage is applied to a DTM; -
FIG. 4 is a diagram of a discrete trap memory device according to embodiments of the present invention; -
FIG. 5 illustrates Fullerenes arranged in a layer of a discrete trap memory device according to an embodiment of the invention; -
FIG. 6 illustrates Fullerenes arranged in a layer of a discrete trap memory device according to another embodiment of the invention; -
FIG. 7 illustrates endohedral Fullerenes arranged in a layer of a discrete trap memory device according to an embodiment of the invention; and -
FIG. 8 illustrates Fullerenes arranged as a mask layer according to an embodiment of the invention. - The making and using of the presently preferred embodiments are discussed in detail below. It should be appreciated, however, that the present invention provides many applicable inventive concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed are merely illustrative of specific ways to make and use the invention, and do not limit the scope of the invention.
- Known DTMs are limited by the effects of non-uniform distribution of the trapped charge. The charge distribution effects the operation and electrical characteristics of the memory. Referring to
FIG. 1 ,discrete traps 106 are statistically distributed withinnitride layer 105. Accordingly, in some devices the distribution will be less uniform than in other devices. This can result in a configuration that will block the percolation path between the source and the drain or that will require a higher threshold voltage at the gate to allow a percolation path to form. -
FIG. 2A illustrates the distribution ofcharge traps 201 in a SONOS or MONOSdiscrete trap memory 200.Charge traps 201 are distributed non-uniformly indevice 200.FIG. 2B illustratesdevice 200 when a threshold voltage is applied to the gate ofdevice 200. As shown inFIG. 2B , the distribution ofcharge traps 201 does not allow for creation of a percolation path betweensource 202 anddrain 203. -
FIG. 3A illustrates anotherdiscrete trap memory 300 having a different distribution ofcharge traps 301.Charge traps 301 are distributed more uniformly indevice 300 compared todevice 200. Accordingly, when a threshold voltage is applied to the gate ofdevice 300,percolation path 304 is created betweensource 302 anddrain 303 as shown inFIG. 3B . - Distribution of charge traps in known DTMs follows Poisson statistics. The DTMs are restricted by available boundary conditions as the devices are scaled, for example, from 200 nm×200 nm toward 25 nm×25 nm. The density of the charge trap distribution remains the same in the devices independent of the device size. Accordingly, as the devices are made smaller, the chance for the charge distribution to block the percolation path or to allow a permanent percolation path increases. The statistical characteristics of known DTM devices can be improved by homogeneous distribution of the charge traps. One method for providing homogenous distribution of charge traps is to use a nano-mask for nano-crystals, wherein the nano-mask is developed by means of proteins. This technique is described, for example, in Shan Tung et al., Nanocrystal Flash Memory Fabricated with Protein-mediated Assembly, Electron Devices Meeting, 2005, IEDM Technical Digest, 174-177 (5-7 Dec. 2005 IEEE International) the disclosure of which is hereby incorporated by reference herein in its entirety.
- The present invention provides a flexible alternative by which charge traps can be homogenously ordered in DTM using Fullerenes. Fullerenes can be manufactured in diverse sizes and forms, such as spherical Fullerenes known as C60, C70, and C240. Endohedral Fullerenes that have additional atoms, ions, or clusters enclosed within their inner spheres are also known. For example, a nitrogen-endowed C60 Fullerene (N@C60) carries individual nitrogen atoms in their inside. Using these characteristics one can use Fullerenes to control the density and the distribution of the charge traps.
-
FIG. 4 is a schematic drawing of anew DTM 400.Source 401 and drain 402 are formed insubstrate 403, which may be a silicon layer.Bottom oxide layer 404 is thermally grown onsilicon 403. Instead of the nitride layer that is deposited on the bottom oxide layer in some known DTMs, one embodiment of the present invention replaces the nitride with a dense pattern ofendohedral Fullerenes 405 that create charge traps 406.Top oxide layer 407 is deposited onFullerene layer 405.Gate layer 408, which may be polycrystalline silicon or metal, is deposited ontop oxide layer 407.DTM device 400 operates such that when a threshold voltage is applied togate 408, a percolation path betweensource 401 and drain 402 allows current to flow through the device.Layer 405 may be a regular and dense organization ofendohedral Fullerenes 406. UsingFullerenes 406, the present invention removes the statistical, random distribution of charge traps that are found in nitride layers of known DTMs and decreases variations in threshold voltage. In alternative embodiments, other materials may be used in place of 404, 407, such as a high-k dielectric, an insulator, a tunnel barrier, silicon oxide, Al2O3, HfO2, SiC, SiN, or other materials.oxide layers - By using endohedral Fullerenes, the size and kind of the charge traps can be controlled and the local effect of the local traps can be specified. Thus, DTMs with a more precise threshold voltage and a smaller cell sizes can be manufactured.
FIG. 5 is a top-view diagram of a Fullerene layer in a DTM according to one embodiment of the present invention.Fullerenes 501 may be spherical Fullerenes or endohedral Fullerenes. As shown inFIG. 5 ,Fullerenes 501 can be closely-spaced, which allows for a more regular arrangement of the charge traps in the Fullerenes. This arrangement minimizes variations in threshold voltage by eliminating the rougher geometric effects that are present in known nitride DTMs. The more densely packed the Fullerenes are, the less variation there will be in devices of the same size. DTMs with densely packed Fullerenes also allow for a more accurate prediction of a device's characteristics when scaled to different sizes.FIG. 6 illustrates an alternative embodiment in whichFullerenes 601 are arranged in a more random pattern that is less closely spaced. -
Fullerenes 401 may act as discrete trapping objects as shown inFIG. 5 . Alternatively, as shown inFIG. 7 ,endohedral Fullerenes 701 holdingother atoms 702 can be used as charge traps. In one embodiment,atoms 702 inFullerenes 701 may be atoms with a large electronegativity, such as Flourine, which is an electron acceptor or electron trap. Elements with a smaller electronegativity, such as Oxygen, might also be used. Atoms such as Manganese may also be used as well as clusters of atoms. Different endohedral objects may cause beneficial effects due to complex orbital structures. In other embodiments, Heterofullerenes (i.e. Fullerene-type structures in which other atoms, such as Nitrogen atoms, are substituted for some of the carbon atoms in the “Fullerens”) may be used in place ofFullerenes 601. Alternatively, Fullerenes compounded from atoms such as Gold may be used in place ofFullerenes 401. -
FIG. 8 illustrates howFullerenes 801 may be used as a mask.Fullerenes 801 may be spherical, elliptical or endohedral. The type and size ofFullerenes 801 are chosen to control the size ofarea 802 betweenadjacent Fullerenes 801. Thearea 802 is an open space tounderlying layer 803.Fullerenes 801 are used as a mask for the production of charge traps by usingspaces 802 for deposition of nano-clusters onsurface 803 thereby causing charge traps to develop. - A discrete trap memory device may be manufactured by thermally growing an oxide layer on a silicon substrate, arranging a plurality of Fullerenes on the oxide layer to form a mask, wherein the oxide layer is exposed through the mask at gaps between the plurality of Fullerenes, depositing nano-crystals over the mask, and trapping the nano-crystals in gaps between the plurality of Fullerenes. The plurality of Fullerenes may be removed so that nano-crystals remaining on the oxide layer act as charge traps in the discrete memory device. Silicon oxide may be deposited over the nano-crystals, and a gate layer formed over the silicon oxide. In alternative embodiments, other materials may be used in place of the oxide layer, such as a high-k dielectric, an insulator, a tunnel barrier, silicon oxide, Al2O3, HfO2, SiC, SiN, or other materials.
- Although the present invention and its advantages have been described in detail, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the invention as defined by the appended claims. Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the process, machine, manufacture, composition of matter, means, methods and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure of the present invention, processes, machines, manufacture, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the present invention. Accordingly, the appended claims are intended to include within their scope such processes, machines, manufacture, compositions of matter, means, methods, or steps.
Claims (20)
1. An integrated circuit device, comprising:
a Fullerene layer having a plurality of Fullerene molecules, wherein the Fullerene molecules act as charge traps.
2. The integrated circuit device of claim 1 , wherein the plurality of Fullerenes are spherical or elliptical Fullerenes.
3. The integrated circuit device of claim 1 , wherein the plurality of Fullerenes are endohedral Fullerenes.
4. The integrated circuit device of claim 1 , wherein the plurality of Fullerenes are arranged to form a single layer of Fullerenes.
5. The integrated circuit device of claim 1 , wherein the Fullerenes are Hetrofullerenes.
6. A discrete trap memory, comprising:
a silicon substrate layer;
a bottom dielectric layer on the silicon substrate layer;
a Fullerene layer on the bottom dielectric layer;
a top dielectric layer on the Fullerene layer; and
a gate layer on the top dielectric layer.
7. The discrete trap memory of claim 6 , wherein the Fullerene layer further comprises:
a plurality of Fullerenes arranged in a single layer.
8. The discrete trap memory of claim 6 , wherein the Fullerene layer comprises Hetrofullerenes.
9. The discrete trap memory of claim 6 , wherein the Fullerene layer further comprises:
a plurality of endohedral Fullerenes that act as charge traps.
10. The discrete trap memory of claim 6 , wherein the Fullerene layer further comprises:
a plurality of spherical or elliptical Fullerenes that act as charge traps.
11. The discrete trap memory of claim 6 , wherein a material forming the bottom dielectric layer is selected from the group consisting of:
a high-k dielectric;
an insulator;
a tunnel barrier;
an oxide;
silicon oxide;
Al2O3;
HfO2;
SiC; and
SiN.
12. The discrete trap memory of claim 6 , wherein a material forming the top dielectric layer is selected from the group consisting of:
a high-k dielectric;
an insulator;
a tunnel barrier;
an oxide;
silicon oxide;
Al2O3;
HfO2;
SiC; and
SiN.
13. A method for manufacturing a discrete trap memory device, comprising:
arranging a plurality of Fullerenes on an oxide layer to form a mask, wherein the oxide layer is exposed through the mask at gaps between the plurality of Fullerenes;
depositing nano-crystals over the mask; and
trapping the nano-crystals in gaps between the plurality of Fullerenes.
14. The method of claim 13 , further comprising:
removing the plurality of Fullerenes, wherein nano-crystals remaining on the oxide layer act as charge traps in the discrete memory device.
15. The method of claim 14 , further comprising:
thermally growing the oxide layer on a silicon substrate;
depositing silicon oxide over the nano-crystals; and
forming a gate layer over the silicon oxide.
16. A method for manufacturing a discrete trap memory device, comprising:
arranging a plurality of Fullerenes on a bottom dielectric layer to form a mask, wherein the bottom dielectric layer is exposed through the mask at gaps between the plurality of Fullerenes;
depositing nano-crystals over the mask; and
trapping the nano-crystals in gaps between the plurality of Fullerenes.
17. The method of claim 16 , further comprising:
removing the plurality of Fullerenes, wherein nano-crystals remaining on the bottom dielectric layer act as charge traps in the discrete memory device.
18. The method of claim 17 , further comprising:
thermally growing the bottom dielectric layer on a silicon substrate;
depositing a top dielectric layer over the nano-crystals; and
forming a gate layer over the top dielectric layer.
19. The method of claim 16 , wherein a material forming the bottom dielectric layer is selected from the group consisting of:
a high-k dielectric;
an insulator;
a tunnel barrier;
an oxide;
silicon oxide;
Al2O3;
HfO2;
SiC; and
SiN.
20. The method of claim 16 , wherein a material forming the top dielectric layer is selected from the group consisting of:
a high-k dielectric;
an insulator;
a tunnel barrier;
an oxide;
silicon oxide;
Al2O3;
HfO2;
SiC; and
SiN.