US20080006435A1

US20080006435A1 - Non-halogenated heavy metal free vehicular cable insulation and harness covering material

Info

Publication number: US20080006435A1
Application number: US11/483,788
Authority: US
Inventors: Mark A. Scheel; Edward L. Monroe; Raman V. Chiruvella
Original assignee: Individual
Current assignee: Delphi Technologies Inc
Priority date: 2006-06-23
Filing date: 2006-07-10
Publication date: 2008-01-10
Anticipated expiration: 2026-06-23
Also published as: EP1879197A3; US7534962B2; CN101105987B; KR100896588B1; US20090014201A9; EP1879197A2; CN101105987A; KR20080005864A

Abstract

Described is a vehicular harness comprising a plurality of insulated non-halogenated, heavy metal free vehicular cables, each comprising an inner core of a copper based metal wire having a thickness area of at least about 0.1 mm, an outer insulation, covering the length of the inner core, comprised of a thermoplastic polyphenylene ether composition that has no halogen or heavy metal added thereto, the insulated cable capable of meeting the testing standard ISO 6722, and a tape comprised of the thermoplastic polyphenylene ether composition wrapped around the plurality of cables to hold the cables together. Also described is a tape having a plastic PPE layer with an adhesive on the bottom and a pealable layer.

Description

TECHNICAL FIELD

The present invention is concerned with a vehicular cable insulation and harness covering material that is non-halogenated and heavy metal free. In particular, the invention pertains to an automotive wire harness insulation and a harness covering material of a non-halogenated composition.

BACKGROUND OF THE INVENTION

Environmental regulations dictate that the material selection in the vehicular industry needs to be halogen free and heavy metal free compositions especially for the vehicular materials. Typically, polyvinyl chloride (PVC) is utilized because of its combination of competitive raw materials costs and desirable properties. These properties include processibility, toughness, chemical resistance and ability to withstand temperatures typical for many applications in automotive environments.
Unfortunately, the chlorine content of PVC limits its disposal at the end of the life of the vehicle. Also there are concerns about effects on health and the environment by PVC by-products and PVC plasticizer. Accordingly, therefore, a replacement for PVC has long been sought with an intent to find competitive cost efficient replacements. In addition, performance must be taken into account including high temperature endurance, toughness, processability and also reduction in weight.
Polyethylene terephthalate (PET) can also be considered a halogen free material for tape. However, PET based tapes are limited to uses where high performance is needed because of cost and price. Typically, this would be for performance needs such as high temperature, endurance sound deadening or toughness.
It is therefore desirable to have a harness covering material that is cost effective and still achieves desirable characteristics such as lack of halogens and heavy metals, appropriate temperature resistance, scrape abrasion resistance, resistance to heat aging, resistance to automotive fluids and resistance to flame and in particular to be capable of meeting the standard SAE (Society of automotive Engineers) J2192 or LV312 and offers all these properties with a reduction in weight.

SUMMARY OF THE INVENTION

Described is an insulated non-halogenated, heavy metal free vehicular cable comprising an inner core of a copper based metal wire having a thickness area of at least about 0.1 mm, and an outer insulation, covering the length of the inner core, comprised of a thermoplastic polyphenylene ether composition that has no halogen or heavy metal added thereto, the insulated cable capable of meeting the testing standard ISO 6722.
Also described is a tape comprised of a layer, having a top and bottom thereto, of a thermoplastic polyphenylene ether composition that has no halogen or heavy metal added thereto; a contact adhesive adhering to one side of the thermoplastic polyphenylene ether composition and optionally a pealable layer or release liner adhered to the contact adhesive, which pealable layer is capable of being pealed off the tape, thereby permitting the thermoplastic polyphenylene ether composition to be applied to a desired surface.

BRIEF DESCRIPTION OF THE DRAWINGS

Further objects and advantages of the invention will be apparent from the following description and appended claims, reference being made to the accompanying drawings forming a part of the specification, wherein like reference characters designate corresponding parts in several views.

FIG. 1 is a perspective view of the vehicular cable of the present invention;

FIG. 2 is a cross-section of FIG. 1 taken along lines 2-2;

FIG. 3 is a die used to manufacture an embodiment of the insulated vehicular cable of the present invention; and

FIG. 4 is a cross-section of FIG. 3 taken along lines 4-4.

FIG. 5 is a tape of the present invention; and

FIG. 6 is the tape of the present invention wrapped around a plurality of vehicular cables of FIG. 1.

DETAILED DESCRIPTION OF THE INVENTION

With increasing electronic content in automobiles there is an ever growing need for miniaturizing the size of the cables that provide resistance to physical abuse and provide resistance to flame and automotive fluids among other requirements to be met for the automotive industry such as ISO 6722. It has been found to be particularly desirable to utilize an insulated non-halogenated, heavy metal free vehicular cable containing a copper based metal wire that has a diameter of at least about 0.1 mm or more and an outer insulation covering the length of the inner core comprised of a thermoplastic polyphenylene ether composition which has no halogen or heavy metal added thereto.
Definitions:
By “non-halogenated” is meant that the polymeric material that is utilized has no halogen material that is added to the composition, as a desirable component of the composition.
By “heavy metal free” is meant that no heavy metal such as mercury, hexavalent chrome, cadmium, lead and the like are added to the metal core, as a desirable component of the metal composition.
By “copper based metal” is meant that the metal wire is comprised of greater than 50% by weight of the metal being copper, or copper alloyed with other metal components as is well known in the industry yet maintaining suitable electrical conductivity. Well known copper based alloys may be used such as HPC-80EF, trademark Phelps Dodge.
By “polyphenylene ether” is meant a thermoplastic polymeric material which is commercially available and generally are polymers of monohydroxy aromatic materials. Other readily available materials are 2,6-xylenol or a 2,3,6-trimethylphenyl and polymers thereof. Polyphenylene ether (PPE) is also known as polyphenylene oxide (PPO) and is described in the literature. See U.S. Pat. Nos. 3,306,874, 3,306,875; 3,257,357; and 3,257,358, which are herein incorporated by reference.
Frequently polyphenylene ether materials are a blend of other thermoplastic or cross-linked ethylenically unsaturated materials such as polyolefinic materials, styrene or styrene butadiene or polyacryamide and the like. These materials are commercially available such as Noryl, Luranyl, Ultranyl or Vestoblend, trademarks of GE. Some materials that may be utilized include Noryl WCV072, WCV072L-111, and the like of GE.
It has been found that the ultra thin cable and cable wall that is utilized in the present case even at a small cross section of 0.1 mm²give a very satisfactory result in abrasion cycling tests such as that called for in ISO-6722.
The cross sectional area of the copper wire can range from about 0.1 to about 3 square millimeters, such as 26 AWG to 12 AWG, alternatively 0.13 to 1.5 square millimeters.
The insulated cable of the present invention is prepared utilizing normal well known commercially available equipment where the desired polyphenylene ether polymer is fed to an extrusion machine where the molten viscous polymer is passed through a die, as shown in FIGS. 3-4, so that the insulating PPE is wrapped around the linear portion of the metal conductor wire. The processing temperatures that may be utilized can vary as is well known in the industry. However, it has been found desirable to heat the resin material obtained from the supplier as follows. The thermoplastic polyphenylene ether material is dried at about 180° F. for at least 2 hours and is then passed through the first stage of an extrusion machine. The feed temperature is approximately 115° F. The compression temperature and the metering temperature in the barrels of the extruder can vary. A compression temperature may be from about 475° F. to 490° F. The metering temperature is approximately 500° F. to 540° F. The cross head or the die temperature is approximately 540° F. to 560° F. After the wire is extruded with the insulated material thereon, it passes through a cooling water bath and mist which is maintained at room temperature and then is packed as a cable in a barrel for subsequent handling.
Turning now to a description of the drawings. FIG. 1 is the insulated vehicular cable 10 of the present invention having an insulated member 12 of PPE extruded or wrapped around the copper base metal core 14. An embodiment is shown in FIGS. 1 and 2 wherein the inner copper core is comprised of several wires 14 A-G with a central wire 14 A. The central wire 14A is surrounded by the other wires 14 B-G. There can be 7, 19 or 37 strands in metal core 14, in some instances they are compressed and in the other they are bunched.
During the extrusion process of the insulated vehicular cable 10, the copper based core is fed through the middle of die 20 entering the back end 22 of the die and exiting from the die at 24. The die has a central portion 26 through which the copper based wire 14 passes. The hot viscous PPE will be passed into the space 28 at the entrance end 22 of the die 20 and proceeds to envelop the copper wire. The die begins to narrow at 30 as PPE is extruded with the copper based wire passing from 30 through exit 24 of the die. At the exit 24 of the die, the insulated vehicular cable 10 of the present invention is obtained. The cooling process as described above and the packaging of the cable follows thereafter.
The diameter of the insulated vehicular cable 10 of the present invention can vary substantially. A cable diameter that has been found useful is between 0.85 and 0.92 mm in case of 0.13 mm²cable. Other dimensions of an insulated vehicular cable would be one that has approximately 0.13 square millimeters of wire as its cross sectional area but which is used to form the embodiment shown in FIG. 1 namely a central wire with six surrounding wires. In that case, the conductor diameter may be approximately 0.465 millimeters with a cable diameter 10 of approximately 0.88 millimeters with the minimum insulated wall thickness of 0.198 millimeters.
As indicated above a wide variety of commercially available extruding equipment may be utilized such as an extruder identified as BMD60-24D or a Nokia Maillefer, and the like.
The die utilized in the present invention may be manufactured from a wide variety of commercially available materials such as D2 hardened tool steel.
Following the procedures outlined in ISO-6722, scrape abrasion resistance using 7(N) load and 0.45 millimeter needle was used on three sets of cables, the first being compressed halogen free cable ISO ultra thin wall cable referred as CHFUS, the second ISO thin wall cable referred as HFSS and the third ISO thick wall cable referred as HF. The test results are identified in tables 1 and 2 below.
Following the procedures outlined in ISO-6722 a number of tests were so performed where the thickness of the copper wire varied as well as the diameter of insulated polyphyenelyene ether varied as is shown in tables 3-4.

TABLE 1

CHFUS

	0.13*	0.22*	0.35*	0.50*	0.75*	1.00*	1.25*

Normal Force(N)	4.0	4.0	5.0	5.0	6.0	6.0	6.0
Minimum cycles	100	100	100	150	150	180	180
required at the
normal force
Result	166	550	338	376	536	526	1315
7N Load	151	338	244	1150	836	960	2181
	125	379	223	458	1078	1171	610
	174	397	287	560	722	984	2673
Minimum cycles	125	338	223	376	536	526	610
attained by the
cable at
7 Newton load
Pass/Fail	∘	∘	∘	∘	∘	∘	∘

*Wire Size (square mm)

TABLE 2

HFSS

						HF
0.35*	0.50*	0.75*	1.00*	1.25*	2.00*	3.00*

Normal Force(N)	5.0	5.0	6.0	6.0	6.0	7.0	7.0
Minimum cycles required	100	150	150	180	180	750	750
at the normal force
Result	443	4067	7193	6043	10434	12586	*>5000
7N Load	2396	893	9636	3896	5158	10835
	830	4271	4512	7771	3559	11203
	1031	2586	6198	8776	16333	12308
Minimum cycles	443	893	4512	3896	3559	10835	*>5000
attained by the
cable at 7 Newton load
Pass/Fail	∘	∘	∘	∘	∘	∘	∘

*Wire Size (square mm)

Following the procedures outlined in ISO-6722 a number of tests were so performed where the cross sectional area of the copper wire varied as well as the diameter of insulated polyphyenelyene ether varied as is shown in tables 3-4.

	TABLE 3

	Cable Type and Size

	CHFUS
	Size

Test		Item		Unit	Wire Thickness Area (square mm)	0.13	0.22	0.35	0.50	0.75	1.00	1.25	1.50

ISO6722

Certifi-

Dimensions

Thickness of

(mm)

0.179

0.274

0.190

0.211

0.194

0.196

0.210

0.223

cation

Ins. (min)

Cable Outer

(mm)

0.872

1.027

1.127

1.279

1.391

1.590

1.794

1.849

Dia.

Electrical

Resistance

(mΩ/m)

Sec 6.1 Must be smaller than requirement

157.100

78.600

49.600

34.600

24.300

17.200

14.100

12.000

(Measured result) See Table 4

(mΩ/m)

Requirement

169.900

84.400

54.400

37.100

24.700

18.500

14.900

12.700

Ins. Resistance

Sec. 6.2 Breakdown shall not occur

Pass

in water

Spark test

Sec. 6.3 No breakdown shall occur when the earthed

Pass

cable is drawn through the test electrode

Mechanical

Pressure test at

Sec. 7.1 Breakdown shall not occur during the

Pass

high temp.

withstand voltage test

Low-temp

Winding under

Sec. 8.1 After winding, no conductor shall be visible.

Pass

low temp

During the withstand voltage test,

breakdown shall not occur.

Abrasion

Scrape

(N)

Sec. 9.3 Load requirement

4

5

6

(times)

Scrape requirement

100

150

180

200

(times)

Min. scrape result

1309

3052

951

1636

441

844

883

1058

Heat aging

Short high

Sec. 10.1 After winding, no conductor shall be visible.

Pass

temp

During the withstand voltage test,

breakdown shall not occur.

Long high

Sec. 10.2 After winding, no conductor shall be visible.

Pass

temp 85 deg C.

During the withstand voltage test,

breakdown shall not occur.

Shrinkage by

(mm)

Sec. 10.4 The maximum shrinkage shall not exceed

Pass

high temp

2 mm at either end

Resistance

Gasoline

Sec. 11.1 The maximum outside cable diameter change

Pass

to chemical

(%)

shall meet the requirement shown in Table 13. After

5.15

5.40

0.09

2.83

−6.39

0.06

0.00

0.32

Diesel

winding, no conductor shall be visible. During the

Pass

pass

Pass

(%)

withstand voltage test, breakdown shall not occur.

4.56

4.72

8.63

−0.58

−0.40

6.20

3.55

1.88

Engine Oil

Pass

(%)

5.75

2.44

2.70

−8.91

−5.66

−4.84

0.83

0.70

Flame

Flamability at

(Sec)

Sec. 12 Any combustion flame of insulating material

0.0

4.0

45 degree angle

shall extinguish within 70 s, and a minimum of 50 mm

of insulation at the top of the test sample shall remain

unburned

If

Electrical

Insulation

Ohm mm

Sec. 6.4 Greater than 10⁹Ohm mm

Pass

required

volume

1.6E+15

1.0E+16

1.70E+16

2.50E+21

8.60E+17

3.50E+21

7.30E+17

9.10E+19

resistivity

Mechanical

Strip force

(N)

Sec. 7.2 Greater than specified by customer

28.8 Pass

31.6 Pass

41 Pass

69.7 Pass

52.5 Pass

75.7 Pass

70.1 Pass

63.8 Pass

Requirement (Min)

2

5

Low-temp

Impact

Sec. 8.2 After impact, no conductor shall be visible.

Not

During the withstand voltage test, breakdown

required

shall not occur.

Heat aging

Thermal

Sec. 10.3 After winding, no conductor shall be visible.

Pass

overload

During the withstand voltage, breakdown shall not occur

Resistance

Ethanol

Sec. 11.1 The maximum outside cable diameter change

Pass

to chemical

(%)

shall meet the requirement shown in Table 13. After

4.01

4.42

2.70

−6.98

−6.06

−5.26

1.33

1.61

Power steering

winding, no conductor shall be visible. During the

Pass

fluid

(%)

withstand voltage test, breakdown shall not occur.

4.00

6.39

3.68

5.76

−4.73

−3.48

1.33

3.71

Automatic

Pass

transmission

(%)

4.07

5.52

4.31

6.05

−2.46

−3.96

2.11

1.51

fluid

Engine coolant

Pass

(%)

3.09

0.29

0.99

1.65

−0.20

0.06

0.44

−0.32

Battery

Pass

(%)

−0.11

1.46

1.08

2.12

−1.00

0.24

0.00

−0.32

Ozone		Sec. 11.3 The visual examination of the insulation shall	Pass
		not reveal any crac
Hot water	(Ω · mm)	Sec. 11.4 The insulation volume resistivity shall not be	Pass
		less than 10⁹Ohm mm. A visual examination of
		the insulation

Temp. and

Sec. 11.5 After winding, no conductor shall be visible.

Pass

humidity

During the withstand voltage test, breakdown shall

cycling

not occur

	TABLE 4

	Cable Type and Size

		PPO
	HFSS	HF
	Size	Size

Test		Item		Unit	Wire Thickness Area (square mm)	0.35	0.50	0.75	1.00	1.25	2.00	3.00

ISO6722

Certifi-

Dimensions

Thickness

(mm)

0.258

0.231

0.252

0.322

0.320

0.348

0.653

cation

of Ins. (min)

Cable Outer

(mm)

1.289

1.481

1.773

1.943

2.088

2.551

3.598

Dia.

Electrical

Resistance

(mΩ/m)

Sec 6.1 Must be smaller than requirement

46.200

33.100

23.200

16.800

13.900

8.840

5.76

(Measured result) See Table 4

(mΩ/m)

Requirement

54.400

37.100

24.700

18.500

14.900

9.420

6.150

Ins. Resistance

Sec. 6.2 Breakdown shall not occur

Pass

in water

Spark test

Sec. 6.3 No breakdown shall occur when the earthed cable

Pass

is drawn through the test electrode

Mechanical

Pressure test

Sec. 7.1 Breakdown shall not occur during the withstand voltage test

Pass

at high temp.

Low-temp

Winding under

Sec. 8.1 After winding, no conductor shall be visible.

Pass

low temp

During the withstand voltage test,

breakdown shall not occur.

Abrasion

Scrape

(N)

Sec. 9.3 Load requirement

5

6

7

(times)

Scrape requirement

100

150

180

750

(times)

Min. scrape result

1688

2141

>5000

10835

>5000

Heat aging

Short high

Sec. 10.1 After winding, no conductor shall be visible.

Pass

temp

During the withstand voltage test,

breakdown shall not occur.

Long high

Sec. 10.2 After winding, no conductor shall be visible.

Pass

temp 85

During the withstand voltage test,

deg C.

breakdown shall not occur.

Shrinkage by

(mm)

Sec. 10.4 The maximum shrinkage shall not exceed

Pass

high temp

2 mm at either end

Resistance

Gasoline

Sec. 11.1 The maximum outside cable diameter change shall

Pass

to chemical

(%)

meet the requirement shown in Table 13. After winding,

−4.79

−4.54

−3.57

2.07

2.23

6.77

13.4

Diesel

no conductor shall be visible. During the withstand voltage test,

Pass

(%)

breakdown shall not occur.

−3.50

−2.71

−1.65

3.16

−2.00

2.20

1.63

Engine Oil

Pass

(%)

−6.36

−5.74

1.17

2.19

−3.91

0.94

0.14

Flame

Flamability at

(Sec)

Sec. 12 Any combustion flame of insulating material shall

0.0

4.0

5.0

4.0

8.0

14

45 degree

extinguish within 70 s, and a minimum of 50 mm of insulation

angle

at the top of the test sample shall remain unburned

If

Electrical

Insulation

Ohm mm

Sec. 6.4 Greater than 10⁹Ohm mm

Pass

required

volume

2.90E+21

7.70E+17

8.30E+16

2.80E+16

3.20E+16

9.70E+16

3.40E+21

resistivity

Mechanical

Strip force

(N)

Sec. 7.2 Greater than specified by customer

63 Pass

115.3

69.4 Pass

88.0 Pass

112 Pass

113.3 Pass

230

Requirement (Min)

5

10

15

Low-temp

Impact

Sec. 8.2 After impact, no conductor shall be visible.

Not

Pass

During the withstand voltage test, breakdown shall not occur.

required

Heat aging

Thermal

Sec. 10.3 After winding, no conductor shall be visible.

Pass

overload

During the withstand voltage, breakdown shall not occur

Resistance

Ethanol

Sec. 11.1 The maximum outside cable diameter change

Pass

to chemical

(%)

shall meet the requirement shown in Table 13. After winding,

5.93

−5.36

1.17

5.97

−3.82

1.45

1.3

Power steering

no conductor shall be visible. During the withstand voltage test,

Pass

fluid

(%)

breakdown shall not occur.

−5.36

−3.72

−3.52

6.99

−2.64

2.08

0.36

Automatic

Pass

transmission

(%)

−5.65

−4.61

−3.09

6.99

−2.55

1.92

0.58

fluid

Engine coolant

Pass

(%)

−7.22

0.13

−5.54

−1.17

0.00

0.74

0.64

Battery

Pass

(%)

0.78

−0.19

−0.32

5.00

0.38

−0.04

0

Ozone		Sec. 11.3 The visual examination of the insulation shall not	Pass
		reveal any cracks
Hot water	(Ω · mm)	Sec. 11.4 The insulation volume resistivity shall not be less	Pass
		than 10⁹Ohm mm. A visual examination of the insulation

Temp. and	Sec. 11.5 After winding, no conductor shall be visible.	Pass	Pass	Pass	Pass	Pass	Pass	Pass
humidity	During the withstand voltage test, breakdown shall not occur
cycling

Listed below in Table 5 is a measurement of the PPE toughness for ISO 6722 needle abrasion cycles to failure compared to material thickness using a 7-N load and 0.45 millimeter needle.

TABLE 5

	0.4-mm cable
Insulation	insulation	0.25-mm cable	0.16-mm cable
Material	thickness	insulation thickness	insulation thickness

PPE	10000	200	110

Current PVC tape construction has thicknesses for backings of 0.09-mm and above. This thickness for PVC is required to provide a minimum amount of toughness or abrasion protection while also providing sufficient tensile and tear strength that PVC tape may be applied. Given data from Table 5 and the current film thickness, one can conclude that significantly thinner backings are possible with PPE. PPE backings as thin as 0.03-mm or less could be achieved and still maintain equivalent abrasion protection and toughness to the current PVC backings. Given this potential for reducing backing thickness and specific gravity differences, a weight reduction of 75% seems reasonable with a PPE tape compared to a PVC tape.
With thinner backings, greater linear length of tape can be put up on each roll of tape. This is important for handling in and application of tapes on substrates or wire harnesses. The physical dimensions of a tape roll are limited to physical constraints with a manufacturing operation and by human ergonomic issues. Too large of roll diameters are ergonomically awkward and uncomfortable for continuous daily use. However with thinner tapes, longer roll lengths are possible while still maintaining an acceptable roll diameter. This then benefits the manufacturing by minimizing the number of times workers must retrieve new rolls. For an automotive wire harness manufacturing, a new roll may be required as often as once or twice per wire harness. Also benefit is achieved in shipping since more tape can be shipped for a given container volume.
In addition to being halogen free and tougher than PVC, PPE also offers ability to be used in higher temperature environments. Currently PVC may be rated for use at 105° C. which limits it to select exterior automotive applications. Many of the applications however, such as engine and chassis require temperature ratings of 125° C. and above. This is feasible with PPE which has been rated to 125° C. for continuous use and with excursions to 150° C. and above.
PPE backings could be used with any desired pressure sensitive adhesive available today. This would include natural rubber, natural rubber/synthetic rubber blends, synthetic rubber, acrylic, or other adhesive systems.
Turning now to FIG. 5 it is a schematic representation of the tape 50 of the present invention with the PPE material 52 having top 53 and bottom 55 surfaces where an adhesive 54 would be attached to the bottom surface. The adhesive is generally a pressure sensitive adhesive which would facilitate the adhesion of the PPE tape to a desirable substrate. The tape would frequently be made available with a pealable backing 56.
There are a wide variety of pressure sensitive adhesives well known in the trade for applying such adhesives to thermal plastic materials. Such adhesives can be natural rubber, synthetic rubber, cross-link acrylics or blends of these polymers. Formulated adhesives may be include Morscic, Acronyl or Duro-Tak that are particular types of acrylic adhesive to be used to coat the bottom portion of the PPE material. The pealable tape can be a variety of materials such as paper, cellulose or any plastic film materials that can be coated with a release layer such as a silicone coating well known in the art.

Claims

1. A vehicular harness comprising:

a plurality of insulated non-halogenated, heavy metal free vehicular cables, each comprising:

an inner core of a copper based metal wire having a thickness area of at least about 0.1 sq. mm, and

an outer insulation, covering the length of the inner core, comprised of a thermoplastic polyphenylene ether composition that has no halogen or heavy metal added thereto, the inner core of a copper based metal wire with the outer insulation capable of meeting the testing standard ISO 6722; and

a tape comprising a layer, wherein the layer has a first surface and a second surface, of the thermoplastic polyphenylene ether composition that has no halogen or heavy metal added thereto, and a contact adhesive adhering to the first surface, wrapped around the plurality of cables to hold the cables together.

2. The vehicular harness of claim 1 wherein the copper core has a thickness area in a cross section of the core of about 0.1 to 1.5 sq. mm.

3. The vehicular harness of claim 1 wherein the copper core has a thickness area in a cross section of the core of up to about 3 sq. mm.

4. The vehicular harness of claim 1 wherein the polyphenylene ether is further comprised of a polymer formed from an ethylenically unsaturated material.

5. The vehicular harness of claim 4 wherein the ethylenically unsaturated material is comprised of an olefinically unsaturated material.

6. The vehicular harness of claim 5 wherein the ethylenically unsaturated material is comprised of a styrene butadiene material.

7. A tape comprised of a layer, having a top and bottom thereto, of a thermoplastic polyphenylene ether composition that has no halogen or heavy metal added thereto; a contact adhesive adhering to one side the thermoplastic polyphenylene ether composition; and a pealable layer adhered to the contact adhesive, which pealable layer is capable of being pealed off the tape, thereby permitting the thermoplastic polyphenylene ether composition to be applied to a desired surface.

8. The vehicular harness of claim 1 wherein the testing standard ISO 6722 comprises the inner core of a copper based metal wire with the outer insulation being constructed and arranged to withstand flame at a 45 degree angle such that any combustion flame of the outer insulation extinguishes within 70 seconds and a minimum of 50 mm of insulation at the top of the insulated cable remains unburned.

9. The vehicular harness of claim 1 wherein the inner core of a copper based metal wire has a thickness area of about 0.1 mm₂to about 0.13 mm₂.

10. The tape of claim 7 wherein the thickness of the tape is 0.03 mm or less.

11. The tape of claim 7 wherein the thickness of the tape is 0.03 mm to 0.09 mm.

12. The vehicular harness of claim 1 wherein the thickness of the tape is 0.03 mm or less.

13. The vehicular harness of claim 1 wherein the thickness of the tape is 0.03 mm to 0.09 mm.