US20050227007A1

US20050227007A1 - Volatile copper(I) complexes for deposition of copper films by atomic layer deposition

Info

Publication number: US20050227007A1
Application number: US10/903,060
Authority: US
Inventors: Alexander Bradley; Jeffrey Thompson
Original assignee: Individual
Current assignee: EIDP Inc
Priority date: 2004-04-08
Filing date: 2004-07-30
Publication date: 2005-10-13
Also published as: US20080063882A1; US7759508B2

Abstract

The present invention relates to novel 1,3-diimine copper complexes and the use of 1,3-diimine copper complexes for the deposition of copper on substrates or in or on porous solids in an Atomic Layer Deposition process.

Description

FIELD OF THE INVENTION

TECHNICAL BACKGROUND

Atomic layer deposition (ALD) processes are useful for the creation of thin films, as described by M. Ritala and M. Leskela in “Atomic Layer Deposition” in Handbook of Thin Film Materials, H. S. Nalwa, Editor, Academic Press, San Diego, 2001, Volume 1, Chapter 2. Such films, especially metal and metal oxide films, are critical components in the manufacture of electronic circuits and devices.
In an ALD process for depositing copper films, a copper precursor and a reducing agent are alternatively introduced into a reaction chamber. After the copper precursor is introduced into the reaction chamber and allowed to adsorb onto a substrate, the excess (unadsorbed) precursor vapor is pumped or purged from the chamber. This process is followed by introduction of a reducing agent that reacts with the copper precursor on the substrate surface to form copper metal and a free form of the ligand. This cycle can be repeated if needed to achieve the desired film thickness.
This process differs from chemical vapor deposition (CVD) in the decomposition chemistry of the metal complex. In a CVD process, the complex undergoes pyrolytic decomposition on contact with the surface to give the desired film. In an ALD process, the complex is not completely decomposed to metal on contact with the surface. Rather, formation of the metal film takes place on introduction of a second reagent, which reacts with the deposited metal complex. In the preparation of a copper film from a copper(I) complex, the second reagent is a reducing agent. Advantages of an ALD process include the ability to control the film thickness and improved conformality of coverage because of the self-limiting adsorption of the precursor to the substrate surface in the first step of the process.
The ligands used in the ALD processes must also be stable with respect to decomposition and be able to desorb from the complex in a metal-free form. Following reduction of the copper, the ligand is liberated and must be removed from the surface to prevent its incorporation into the metal layer being formed.
S. G. McGeachin, Canadian Journal of Chemistry, 46, 1903-1912 (1968), describes the synthesis of 1,3-diimines and metal complexes of these ligands, including bis-chelate or homoleptic complexes of the form ML₂.
U.S. Pat. No. 6,464,779 discloses a Cu atomic layer CVD process that requires treatment of a copper precursor containing both oxygen and fluorine with an oxidizing agent to form copper oxide, followed by treatment of the surface with a reducing agent.
WO 2004/036624 describes a two-step ALD process for forming copper layers comprising forming a copper oxide layer from a non-fluorine containing copper precursor on a substrate and reducing the copper oxide layer to form a copper layer on the substrate. Copper alkoxides, copper β-diketonates and copper dialkylamides are preferred copper precursors. The reducing agent is a hydrogen (H₂) containing gas.
U.S. 2003/0135061 discloses a dimeric copper(I) precursor which can be used to deposit metal or metal-containing films on a substrate under ALD or CVD conditions.
WO 2004/046417 describes the use of dimeric copper (I) complexes comprising amidinate ligands for use in an ALD process.

SUMMARY OF THE INVENTION

This invention describes a process for forming copper deposits on a substrate comprising:

a. contacting a substrate with a copper complex, (I), to form a deposit of a copper complex on the substrate; and
b. contacting the deposited copper complex with a reducing agent, wherein
L is selected from the group of C₂-C₁₅olefins, C₂-C₁₅alkynes, nitriles, aromatic heterocycles, and phosphines;
R¹and R⁴are independently selected from the group consisting of hydrogen, methyl, ethyl, propyl, isopropyl, isobutyl, and neopentyl;
R², R³and R⁵are independently selected from the group consisting of hydrogen, fluorine, trifluoromethyl, phenyl and C₁-C₁₀alkyl groups; and the reducing agent is selected from the group consisting of 9-BBN (9-borabicyclo[3.3.1]nonane); diborane; boranes of the form BR_xH_3-x, where x=0, 1 or 2, and R is independently selected from the group consisting of phenyl and C₁-C₁₀alkyl groups; dihydrobenzofuran; pyrazoline; disilane; silanes of the form SiR′_yH_4-y, where y=0, 1, 2 or 3, and R′ is independently selected from the group consisting of phenyl and C₁-C₁₀alkyl groups; and germanes of the form GeR″_zH_4-z, where z=0, 1, 2, or 3, and R″ is independently selected from the group consisting of phenyl and C₁-C₁₀alkyl groups.

DETAILED DESCRIPTION

Applicants have discovered an atomic layer deposition (ALD) process suitable for creation of copper films for use as seed layers in the formation of copper interconnects in integrated circuits, or for use in decorative or catalytic applications. This process uses copper(I) complexes that are volatile, thermally stable and derived from ligands that contain C, H, Si and N, but are not limited to these elements. The ligands are chosen to form copper(I) complexes that are volatile in an appropriate temperature range but do not decompose to copper metal in this temperature range; rather, the complexes decompose to metal on addition of a suitable reducing agent. The ligands are further chosen so that they will desorb without decomposition upon exposure of the copper complex to a reducing agent. The reduction of these copper complexes to copper metal by readily available reducing agents has been demonstrated to proceed cleanly at moderate temperatures.
In the process of this invention, copper is deposited on a substrate by means of:

a. contacting a substrate with a copper complex, (I), to form a deposit of a copper complex on the substrate; and
b. contacting the deposited copper complex with a reducing agent, wherein
L is selected from the group of C₂-C₁₅olefins, C₂-C₁₅alkynes, nitriles, aromatic heterocycles, and phosphines;
R¹and R⁴are independently selected from the group consisting of hydrogen, methyl, ethyl, propyl, isopropyl, isobutyl, and neopentyl;
R², R³and R⁵are independently selected from the group consisting of hydrogen, fluorine, trifluoromethyl, phenyl and C₁-C₁₀alkyl groups; and the reducing agent is selected from the group consisting of 9-BBN; diborane; boranes of the form BR_xH_3-x, where x=0, 1 or 2, and R is independently selected from the group consisting of phenyl and C₁-C₁₀alkyl groups; dihydrobenzofuran; pyrazoline; disilane; silanes of the form SiR′_yH_4-y, where y=0, 1, 2 or 3, and R′ is independently selected from the group consisting of phenyl and C₁-C₁₀alkyl groups; and germanes of the form GeR″_zH_4-z, where z=0, 1, 2, or 3, and R″ is independently selected from the group consisting of phenyl and C₁-C₁₀alkyl groups.

The deposition process of this invention improves upon the processes described in the art by allowing the use of lower temperatures and producing higher quality, more uniform films. The process of this invention also provides a more direct route to a copper film, avoiding the formation of an intermediate oxide film.
In the copper deposition process of this invention, the copper can be deposited on the surface, or in or on porosity, of the substrate. Suitable substrates include conducting, semiconducting and insulating substrates, including copper, silicon wafers, wafers used in the manufacture of ultra large scale integrated circuits, wafers prepared with dielectric material having a lower dielectric constant than silicon dioxide, and silicon dioxide and low k substrates coated with a barrier layer. Barrier layers to prevent the migration of copper include tantalum, tantalum nitride, titanium, titanium nitride, tantalum silicon nitride, titanium silicon nitride, tantalum carbon nitride, and niobium nitride.
This process can be conducted in solution, i.e., by contacting a solution of the copper complex with the reducing agent. However, it is preferred to expose the substrate to a vapor of the copper complex, and then remove any excess copper complex (i.e., undeposited complex) by vacuum or purging before exposing the deposited complex to a vapor of the reducing agent. After reduction of the copper complex, the free form of the ligand can be removed via vacuum, purging, heating, rinsing with a suitable solvent, or a combination of such steps.
This process can be repeated to build up thicker layers of copper, or to eliminate pin-holes.
The deposition of the copper complex is typically conducted at 0 to 200° C. The reduction of the copper complex is typically carried out at similar temperatures, 0 to 200° C.
In the process of this invention, it is initially a copper complex that is deposited on the substrate. The formation of a metallic copper film does not occur until the copper complex is exposed to the reducing agent.
Aggressive reducing agents are needed to reduce the copper complex rapidly and completely. Reducing agents must be volatile and not decompose on heating. They must also be of sufficient reducing power to react rapidly on contact with the copper complex deposited on the substrate surface. A group of suitable reducing agents has been identified that have been used for copper(I) reduction in an ALD process. One feature of these reagents is the presence of a proton donor. The reagent must be able to transfer at least one electron to reduce the copper ion of the complex and at least one proton to protonate the ligand. The oxidized reducing agent and the protonated ligand must be able to be easily removed from the surface of the newly formed copper deposit.
Suitable reducing agents for the copper deposition process of this invention include 9-BBN, borane, diborane, dihydrobenzofuran, pyrazoline, germanes, diethylsilane, dimethylsilane, ethylsilane, phenylsilane, silane and disilane. Diethylsilane and silane are preferred.
In one embodiment of the copper deposition process, the copper complexes are added to a reactor under conditions of temperature, time and pressure to attain a suitable fluence of complex to the surface of the substrate. One of skill in the art will appreciate that the selection of these variables will depend on individual chamber and system design, and the desired process rate. After at least a portion of the copper complex has been deposited on the substrate (e.g., a coated silicon wafer), the undeposited complex vapor is pumped or purged from the chamber and the reducing agent is introduced into the chamber at a pressure of approximately 50 to 760 mTorr to reduce the adsorbed copper complex. The substrate is held at a temperature between approximately 0 to 200° C. during reduction. With suitable combinations of copper complex and reducing agent, this reduction is rapid and complete. Reducing agent exposure times can be from less than a second to several minutes. It is important that the products from this reaction are readily removed from the surface of the substrate under the reducing conditions.
In one embodiment of this invention, the copper complex is a copper 1,3-diimine complex (L), wherein R¹and R⁴are isobutyl groups, R²and R³are methyl groups, and L=vinyltrimethylsilane, and the reducing agent is diethylsilane.
This invention also provides novel 1,3-diimine copper complexes, (I),

wherein

L is selected from the group of C₂-C₁₅olefins, C₂-C₁₅alkynes, nitrites, aromatic heterocycles, and phosphines;
R¹and R⁴are independently selected from the group consisting of hydrogen, methyl, ethyl, propyl, isopropyl, isobutyl, and neopentyl;
R², R³and R⁵are independently selected from the group consisting of hydrogen, fluorine, trifluoromethyl, phenyl and C₁-C₁₀alkyl groups.

In one embodiment, L is a linear, terminal olefin. For olefins of 4-15 carbons, L can also be an internal olefin of cis- or trans-configuration; cis- is preferred. L can be a cyclic or bicyclic olefin. L can also be substituted, for example with fluorine or silyl groups. Suitable olefins include, but are not limited to vinyltrimethylsilane, allyltrimethylsilane, 1-hexene, 4-methyl-1-pentene, 3,3-dimethyl-1-butene, and norbornene. L can also be alkyne, nitrile, or an aromatic nitrogen heterocycle such as pyridine, pyrazine, triazine, and N-substituted imidazole, pyrazole, and triazole. L can also be a phosphine.
The synthesis of one particular ligand useful for making the copper complexes of this invention is given in Example 1, below. Other ligands can be prepared similarly from analogous amino ketones.
In another embodiment, this invention provides an article comprising 1,3-diimine copper complexes, (I), deposited on a substrate. Suitable substrates include: copper, silicon wafers, wafers used in the manufacture of ultra-large scale integrated circuits, wafers prepared with dielectric material having a lower dielectric constant than silicon dioxide, and silicon dioxide and low k substrates coated with a barrier layer. Barrier layers can be used to prevent the migration of copper. Suitable barrier layers include: tantalum, tantalum nitride, titanium, titanium nitride, tantalum silicon nitride, titanium silicon nitride, tantalum carbon nitride, and niobium nitride.

EXAMPLES

Unless otherwise stated, all organic reagents are available from Sigma-Aldrich Corporation (Milwaukee, Wis., USA). The (2-amino)heptafluoro-4-imino-2-pentene was obtained from Matrix Scientific (Columbia, S.C., USA). The [Cu(CH₃CN)₄]SO₃CF₃can be prepared according to the method described in: T. Ogura, Transition Metal Chemistry, 1, 179-182 (976).

Example 1

Preparation and Reduction of Vinyltrimethylsilane(N,N′-diisobutyl-2,4-pentanediketiminate)copper

In a dry box under a nitrogen atmosphere, a 250 mL round-bottom flask was charged with 4-(isobutylamino)-3-pentene-2-one (36.9 g, 237 mmole) and dimethylsulfate (30.0 g, 237 mmole). The reaction solution was stirred for 5 minutes and then allowed to stand without stirring overnight. The yellow mixture became orange and viscous. Isobutyl amine (18 g, 246 mmole) was added with vigorous stirring via addition funnel. The solution was stirred for one hour until it solidified. The intermediate salt was not isolated, but was directly converted to the free amine (based on the theoretical yield of the intermediate salt) as described below.
A solution of NaOMe (12.8 g, 237 mmole) in MeOH (ca 40 mL) was added to the intermediate salt and stirred for one hour. The solvent was removed under vacuum to give a yellow oil that was extracted with pentane, filtered, and concentrated to give a yellow oil that consisted of the desired product (N,N′-diisobutyl-2,4-pentanediketimine) (ca 75%) and unreacted starting material (ca 25%) based on proton NMR data. The product was isolated by fractional distillation to give a yellow oil (35.4 g, 72% yield).
In the dry box, a 100-mL round-bottom flask was charged with [Cu(CH₃CN)₄]SO₃CF₃(1.0 g), vinyltrimethylsilane (26.0 mmole), and diethyl ether (20 mL). In a separate 100-mL round-bottom flask, 1.5 M t-butyl lithium (1.7 mL) was added to a solution of N,N′-diisobutyl-2,4-pentanediketimine (0.550 g), prepared as described above. After 0.5 h, the solutions were combined. The combined solution changed from a cloudy white suspension to a golden-brown, clear solution after the uptake of all solids. After 2 h, the solution was concentrated to a solid/sludge, extracted with pentane (3×15 mL), filtered and concentrated to give a viscous oil (0.600 g, 62% yield).

Example 2

The viscous oil isolated as the final product in Example 1 was used as a copper precursor to create a copper film on a substrate. The substrate consisted of a silicon dioxide wafer with 250-Å layer of tantalum and a 100 Å layer of copper. The wafer had a barely discernable copper color.
Approximately 0.040 g of copper precursor was loaded in a dry box into a porcelain boat. The boat and wafer (˜1 cm²) were placed in a glass tube approximately 3.5 inches apart. The glass tube was removed from the dry box and attached to a vacuum line. Heating coils were attached to the glass tube surrounding both the area around the porcelain boat and the area around the wafer chip; this configuration allows the two areas to be maintained at different temperatures. Following evacuation of the system, an argon flow was created through the tube, passing first over the sample in the boat and then over the wafer. The pressure inside the tube was maintained at 150-200 mTorr. The region around the wafer was warmed to 110° C. After approximately an hour, the temperature of the region around the sample boat was raised to 55° C. These temperatures and the Ar gas flow were maintained for approximately 2.5 hours. The area around the sample boat was then cooled to room temperature. The tube was evacuated to a pressure of ˜10 mTorr and was back-filled with diethylsilane. The area of the tube at 110° C. quickly turned a copper color. The apparatus was cooled and returned to the dry box. The copper color was perceptively darker. The process was repeated to yield a wafer with a smooth metallic copper film.

Example 3

Preparation of Pyridine(N,N′-diisopropyl-2,4-pentanediketiminate)copper

In the dry box, a 100-mL round-bottom flask was charged with Cu(CH₃CN)₄SO₃CF₃(1.0 g, 2.65 mmol), pyridine (2.65 mmol), and ether (20 mL). In a separate 100-mL round-bottom flask, 1.7 M t-butyl lithium (1.56 mL) was added to a solution of N,N′-diisopropyl-2,4-pentanediketimine (2.65 mmol) and ether (20 mL). Both solutions were stirred for 25 min, after which the later solution was added to the former via pipette, which turned yellow then orange after uptake of all solids. The reaction mixture was stirred for 1.5 h before being concentrated under vacuum to a light orange solid. The crude solid was extracted with pentane (4×25 ml) and filtered. The filtrate was concentrated to give the desired product as a yellow powder (562 mg, 65%).

Example 4

Preparation of 3,3,3-Trifluoropropene[(2-amino)-4-imino-2-pentene]copper

In the dry box, a 100-mL round-bottom flask was charged with Cu(CH₃CN)₄SO₃CF₃(1.0 g, 2.65 mmol), ether (20 mL), and 3,3,3-trifluoropropene (bubbled into solution). In a separate 100-mL round-bottom flask, 1.7 M t-butyl lithium (1.56 mL) was added to a solution of (2-amino)-4-imino-2-pentene (260 mg, 2.65 mmol) and ether (20 mL). Both solutions were stirred for 25 min, after which the later solution was added to the former via pipette, which turned yellow then brown after uptake of solid Cu(I). The reaction mixture was stirred for 1.5 hrs, then concentrated under vacuum to a light brown solid, extracted with pentane (100 ml), and filtered. The filtrate was concentrated to give the product as a yellow powder (398 mg, 58%).

Example 5

Preparation of Vinyltrimethylsilane[(2-amino)heptafluoro-4-imino-2-pentene]copper

In the dry box, a 100-mL round-bottom flask was charged with Cu(CH₃CN)₄SO₃CF₃(1.0 g, 2.65 mmol), vinyltrimethylsilane (1.06 g, 10.6 mmol), and ether (20 mL). In a separate 100-mL round-bottom flask, NaH (63 mg, 2.65 mmol) was added portion wise to a solution of (2-amino)heptafluoro-4-imino-2-pentene (2.65 mmol) and ether (20 mL). Both solutions were stirred for 25 min before the later solution was added to the former via pipette. The combined solution turned dark brown after uptake of all solids. The reaction mixture was stirred for 1.5 hrs before being concentrated under vacuum to a light brown solid. The crude solid was extracted with pentane (4×25 ml) and filtered. The filtrate was concentrated to give the desired product as an orange oil (953 mg, 95%).

Claims

1. A process for forming copper deposits on a substrate comprising:

a. contacting a substrate with a copper complex, (I), to form a deposit of a copper complex on the substrate; and

b. contacting the deposited copper complex with a reducing agent, wherein

L is selected from the group of C₂-C₁₅olefins, C₂-C₁₅alkynes, nitriles, aromatic heterocycles, and phosphines;

R¹and R⁴are independently selected from the group consisting of hydrogen, methyl, ethyl, propyl, isopropyl, isobutyl, and neopentyl;

R², R³and R⁵are independently selected from the group consisting of hydrogen, fluorine, trifluoromethyl, phenyl and C₁-C₁₀alkyl groups; and

the reducing agent is selected from the group consisting of 9-BBN (9-borabicyclo[3.3.1]nonane); diborane; boranes of the form BR_xH_3-x, where x=0, 1 or 2, and R is independently selected from the group consisting of phenyl and C₁-C₁₀alkyl groups; dihydrobenzofuran; pyrazoline; disilane;

silanes of the form SiR′_yH_4-y, where y=0, 1, 2 or 3, and R′ is independently selected from the group consisting of phenyl and C₁-C₁₀alkyl groups; and germanes of the form GeR″_zH_4-z, where z=0, 1, 2, or 3, and R″ is independently selected from the group consisting of phenyl and C₁-C₁₀alkyl groups.

2. The process of claim 1, wherein R⁵is hydrogen.

3. The process of claim 2, wherein R²and R³are methyl and R¹and R⁴are independently isobutyl or hydrogen.

4. The process of claim 1, wherein L is vinyltrimethylsilane.

5. The process of claim 1, wherein the substrate is selected from the group consisting of copper, silicon wafers and silicon dioxide coated with a barrier layer.

6. The process of claim 1, wherein the substrate is exposed to a vapor of the copper complex.

7. The process of claim 1, wherein the deposition is carried out at 0 to 200° C.

8. The process of claim 1, wherein the reducing agent is silane or diethylsilane.

9. A copper complex, (I),

wherein

R², R³and R⁵are independently selected from the group consisting of hydrogen, fluorine, trifluoromethyl, phenyl and C₁-C₁₀alkyl groups.

10. The copper complex (I) of claim 9, wherein

L is vinyltrimethylsilane; R¹and R⁴are iso-butyl; and R², R³are methyl and R⁵is H.

11. The copper complex (I) of claim 9, wherein

L is vinyltrimethylsilane; R¹and R⁴are H; and R², R³are methyl and R⁵is H.

12. An article produced by contacting a substrate with a copper complex of claim 9.

13. The article of claim 12, wherein the substrate is selected from the group of copper, silicon wafers, and silicon dioxide coated with a barrier layer.

14. The article of claim 13, wherein the barrier layer is selected from the group consisting of tantalum, tantalum nitride, titanium, titanium nitride, tantalum silicon nitride, titanium silicon nitride, tantalum carbon nitride, and niobium nitride.