US20010050414A1 - Semiconductor device and method of making same - Google Patents
Semiconductor device and method of making same Download PDFInfo
- Publication number
- US20010050414A1 US20010050414A1 US09/354,742 US35474299A US2001050414A1 US 20010050414 A1 US20010050414 A1 US 20010050414A1 US 35474299 A US35474299 A US 35474299A US 2001050414 A1 US2001050414 A1 US 2001050414A1
- Authority
- US
- United States
- Prior art keywords
- dielectric layer
- substrate
- semiconductor device
- base dielectric
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A second or cap dielectric layer is interposed between the usual or base dielectric layer and the metallic circuitry layer of a semiconductor device. The base dielectric layer has a plurality of recesses in an inactive part of the semiconductor device into which parts of the cap dielectric layer extend to interlock the cap dielectric layer to the base dielectric layer and to oppose shearing or tearing of the either (1) the metallic circuitry layer as the metallic circuitry layer is subjected to chemical-mechanical polishing, or (2) a hard mask layer from the base dielectric layer as the metallic circuitry layer is subjected to chemical-mechanical polishing.
Description
- The present invention relates generally to the formation and construction of semiconductor devices and, more particularly, to enhancing the integrity of mechanically weak dielectric substrate layers so that interfaces between such substrate layers and hard mask layer or circuitry layers can withstand subsequently applied chemical-mechanical polishing forces.
- Referring to FIGS. 1 through 4, which illustrate various stages in the conventional formation of semiconductor devices, a
hard mask layer 10, typically silicon based, is deposited on adielectric substrate layer 12, typically carbon based. Next, aphotomask 14 is formed on the top surface ofhard mask layer 10 as illustrated in FIG. 1. A pattern is formed in photomask 14 (a step not illustrated), typically by lithography. Recesses 16 are etched, using the pattern ofphotomask 14, throughhard mask layer 10 and intodielectric substrate layer 12. Recesses 16 extend only partially throughdielectric substrate layer 12, as illustrated in FIG. 2, when intended for lines and extend completely throughdielectric substrate layer 12 when intended for vias. - After
photomask 14 is removed, ametallic layer 18 is applied, for example by dipping, overhard mask layer 10 and to the walls and bottom surfaces of recesses 16. The resulting structure is illustrated in FIG. 3. Next, those portions ofmetallic layer 18 on top ofhard mask layer 10 are removed by chemical-mechanical polishing (CMP). The resulting structure is illustrated in FIG. 4. - The lateral forces, applied during chemical-mechanical polishing, are transferred as shear forces to the interface 20 between
hard mask layer 10 anddielectric substrate layer 12. Such shear forces tend to cause separation ofhard mask layer 10 fromdielectric substrate layer 12. It should be noted that similar shearing or tearing problems can arise during chemical-mechanical polishing when the semiconductor device is formed without a hard mask layer (i.e., when the metallic circuitry layer is applied directly to the substrate). The exposure ofdielectric substrate layer 12 to the chemical solution used during chemical-mechanical polishing can have adverse effects on the nature and character ofdielectric substrate layer 12. - New, organic, low dielectric constant substrate materials typically require an inorganic hard mask layer for protection from chemical-mechanical polishing damage. A large, lateral interface between the organic material substrate layer and inorganic material hard mask layer is typically weak and, as indicated above, often cannot withstand chemical-mechanical polishing forces which are applied subsequent to metalization to remove the metallic circuitry layer above the hard mask.
- Mechanical integrity of the material at interface 20 between the lower surface of the
hard mask layer 10 and the upper surface of thedielectric substrate layer 12 during chemical-mechanical polishing tends to be a problem when processing materials that are softer or weaker than, for example, oxide or nitride. Although many improvements have been made to theupper interface 21 between the top surface ofhard mask layer 10 and the lower surfacemetallic layer 18 placed on top ofhard mask layer 10, mechanical integrity is still a major problem with lower interface 20. - The deficiencies of the conventional semiconductor devices show that a need still exists for an improved device and method of manufacture. An object of the present invention is to provide a semiconductor device and a method of manufacture able to withstand chemical-mechanical polishing forces applied during manufacture. A related object is to enhance the mechanical integrity of the dielectric substrate component of a semiconductor device.
- To achieve these and other objects, and in view of its purposes, the present invention provides a method for forming semiconductor devices. In accordance with the present invention, the method includes the steps of providing a substrate and applying a photomask to the substrate. Next, a selected thickness of selected parts of the substrate is removed by etching. After the photomask is removed, a cap dielectric layer is deposited onto the substrate with portions of the cap dielectric layer extending into spaces in the substrate from which parts of the substrate have been etched.
- A semiconductor device, constructed in accordance with the present invention, includes a substrate having recesses extending inwardly from a surface of the substrate and a cap dielectric layer against the substrate having portions extending into the recesses in the substrate.
- It is to be understood that both the foregoing general description and the following detailed description are exemplary, but are not restrictive, of the invention.
- The invention is best understood from the following detailed description when read in connection with the accompanying drawing. It is emphasized that, according to common practice, the various features of the drawing are not to scale. On the contrary, the dimensions of the various features are arbitrarily expanded or reduced for clarity. Included in the drawing are the following figures:
- FIGS. 1 through 4 show various stages in the conventional formation of semiconductor devices and, in particular, FIG. 1 illustrates a semiconductor device following the sequential formation of a photomask over a hard mask layer over a dielectric substrate layer;
- FIG. 2 illustrates the device of FIG. 1 after recesses are etched, using the pattern of the photomask, through the hard mask layer and into the dielectric substrate layer;
- FIG. 3 illustrates the device of FIG. 2 after the photomask is removed and a metallic layer is applied over the hard mask layer and to the walls and bottom surfaces of the recesses;
- FIG. 4 illustrates the device of FIG. 3 after those portions of the metallic layer on top of the hard mask layer are removed;
- FIGS. 5 through 7 show various stages in the formation of semiconductor devices in accordance with a first embodiment of the present invention and, in particular, FIG. 5 illustrates a substrate (having a base dielectric layer and a hard mask) with a photomask applied to the substrate and a selected thickness of selected parts of the substrate removed by etching;
- FIG. 6 illustrates the device of FIG. 5 after the photomask is removed;
- FIG. 7 illustrates the device of FIG. 6 after a cap dielectric layer is deposited onto the substrate;
- FIGS. 8 through 10 show various stages in the formation of semiconductor devices in accordance with a second embodiment of the present invention and, in particular, FIG. 8 illustrates a base dielectric layer substrate with a photomask applied to the substrate and a selected thickness of selected parts of the substrate removed by etching;
- FIG. 9 illustrates the device of FIG. 8 after the photomask is removed; and
- FIG. 10 illustrates the device of FIG. 9 after a cap dielectric layer is deposited onto the substrate.
- Referring now to FIGS. 5 through 7, in which like reference numbers refer to like elements throughout, a semiconductor device constructed in accordance with a first embodiment of the present invention is formed as follows. A substrate having a base dielectric layer 30 and a
hard mask 22 is provided and aphotomask 24 is applied to the substrate. For the embodiment of the invention being described, and as illustrated in FIG. 5,photomask 24 is applied tohard mask 22. Base dielectric layer 30 can be an organic material (such as benzocyclobutanes, parylene-N, parylene-F, or polyamides) or an inorganic material (such as inorganic xerogels, SiCOH, hexametholsylsesquoixane, fluorinated spin-on glass, or spin-on glass).Hard mask 22 can be SiCOH, SiN, or SiO2. Photomask 24 can be a photosensitive polymer. A metal can be used but must be removed before subsequent layers are formed. - Next, also as illustrated in FIG. 5, a selected thickness of selected parts of the substrate is removed by etching. The etched parts of the substrate are in the form of
recesses 26 in an inactive part of the semiconductor device being formed and extend completely throughhard mask 22 and partially through base dielectric layer 30. For the embodiment of the invention being described, base dielectric layer 30 is etched in a pure oxygen-Ar mixture with at least 3:1 etch selectivity between an organic base dielectric layer and the silicon-containingphotomask 24. The thickness ofphotomask 24 preferably is less than the thickness of organic base dielectric layer 30 and the etch preferably should remove less than one-half of the total thickness of base dielectric layer 30 to achieve the desired vertical adhesion enhancement effect to be described below. -
Next photomask 24 is removed. Photomask 24 can be removed with an acid wash, a solvent cleaning procedure, or both or by using a fluorine-based chemistry reactive ion etch, which might result in a ten percent change in the mask lateral dimension. The structure that results afterphotomask 24 is removed is illustrated in FIG. 6. - Next, a cap dielectric layer 28 is deposited onto the substrate. Portions of cap dielectric layer 28 extend into the spaces (i.e., recesses 26) in the substrate from which parts of the substrate have been etched. For the embodiment of the invention being described, cap dielectric layer 28 is deposited onto
hard mask 22. The resulting structure is illustrated in FIG. 7. - Cap dielectric layer 28 can be a spin-on glass (e.g., fluorinated oxide). Cap dielectric layer 28 typically is spun onto
hard mask 22 to 300-500 Å and as much as 5,000 Å above the top surface ofhard mask 22. By using a liquid dielectric, cap dielectric layer 28 is locally planar in the areas that will be patterned. Cap dielectric layer 28 can serve as a hard mask (thin layer) or as the second dual damascene layer (thicker layer) for a dual damascene sequence. - As a result, by using a separate masking step, vertical sidewalls have been introduced into base dielectric layer 30 at an inactive part of the semiconductor device, whereby adhesion to base dielectric layer 30 is enhanced by the interlock of the parts of cap dielectric layer 28 and recesses 26 in base dielectric layer 30. The interlock between base dielectric layer 30 and cap dielectric layer 28 enhances the resistance to shearing or tearing away of
hard mask 22 as a metallic circuitry layer (not shown in FIG. 7 but which is deposited over cap dielectric layer 28) is subjected to chemical-mechanical polishing. It should be noted that cap dielectric layer 28 can be an inorganic material, such as SiN, SiCOH, SiO2, or spin-on glass, when the base dielectric material is an organic material. - Referring now to FIGS. 8 through 10, in which like reference numbers refer to like elements throughout, a semiconductor device constructed in accordance with a second embodiment of the present invention is formed as follows. A substrate comprising a
base dielectric layer 40 is provided with a photomask 42 that is applied directly tobase dielectric layer 40. In contrast to the first embodiment of the invention, the substrate does not have a hard mask applied to basedielectric layer 40. - Next, as illustrated in FIG. 8, a selected thickness of selected parts of
base dielectric layer 40 is removed by etching. The etched parts of the substrate are in the form ofrecesses 44 in an inactive part of the semiconductor device being formed and extend partially throughbase dielectric layer 40. - Next, photomask 42 is removed. The structure that results after photomask 42 is removed is illustrated in FIG. 9. A cap dielectric layer 46 is deposited onto the substrate with portions of cap dielectric layer 46 extending into the spaces (i.e., recesses 44) in
base dielectric layer 40 from which parts ofbase dielectric layer 40 have been etched. For the embodiment of the invention being described, cap dielectric layer 46 is deposited directly ontobase dielectric layer 40 and functions as a hard mask. The resulting structure is illustrated in FIG. 10. Cap dielectric layer 46 can be inorganic material, such as Dow Chemical Fox, 650F, whenbase dielectric layer 40 is an organic material. - Again, by using a separate masking step, vertical sidewalls have been introduced into
base dielectric layer 40 at an inactive part of the semiconductor device, whereby adhesion to the base dielectric layer is enhanced by the interlock of the parts of cap dielectric layer 46 and recesses 44 inbase dielectric layer 40. The interlock between basedielectric layer 40 and cap dielectric layer 46 enhances the resistance to shearing or tearing away as a metallic circuitry layer (not shown in FIG. 10 but which is deposited over cap dielectric layer 46) is subjected to chemical-mechanical polishing. - Although illustrated and described above with reference to certain specific embodiments, the present invention is nevertheless not intended to be limited to the details shown. Rather, various modifications may be made in the details within the scope and range of equivalents of the claims and without departing from the spirit of the invention. Specifically, the present invention has been described in connection with a single damascene semiconductor device. It will be apparent to those skilled in the art, however, that the present invention can be applied to dual damascene semiconductor devices.
Claims (20)
1. A method for forming semiconductor devices comprising the steps of:
providing a substrate;
applying a photomask to said substrate;
etching to remove a selected thickness of selected parts of said substrate;
removing said photomask; and
depositing a cap dielectric layer onto said substrate with portions of said cap dielectric layer extending into spaces in said substrate from which parts of said substrate have been etched.
2. The method for forming semiconductor devices according to wherein said selected parts of said substrate which are removed are removed from an inactive part of the semiconductor device to be formed.
claim 1
3. The method for forming semiconductor devices according to wherein said substrate includes a base dielectric layer and a hard mask.
claim 2
4. The method for forming semiconductor devices according to wherein said substrate is a base dielectric layer.
claim 2
5. The method for forming semiconductor devices according to wherein said base dielectric layer is an organic material and said cap dielectric layer is an inorganic material.
claim 3
6. The method for forming semiconductor devices according to wherein said base dielectric layer is an inorganic material and said cap dielectric layer is an organic material.
claim 3
7. The method for forming semiconductor devices according to wherein said base dielectric layer is an organic material and said cap dielectric layer is an inorganic material.
claim 4
8. The method for forming semiconductor devices according to wherein said base dielectric layer is an inorganic material and said cap dielectric layer is an organic material.
claim 4
9. A semiconductor device comprising:
a substrate having recesses extending inwardly from a surface of the substrate; and
a cap dielectric layer against said substrate having portions extending into said recesses in said substrate.
10. The semiconductor device according to wherein said recesses are in an inactive part of the semiconductor device.
claim 9
11. The semiconductor device according to wherein said substrate includes a base dielectric layer and a hard mask.
claim 10
12. The semiconductor device according to wherein said substrate is a base dielectric layer.
claim 10
13. The semiconductor device according to wherein said base dielectric layer is an organic material and said cap dielectric layer is an inorganic material.
claim 11
14. The semiconductor device according to wherein said base dielectric layer is selected from the group consisting of benzocyclobutanes, parylene-N, parylene-F, and polyamides and said cap dielectric layer is selected from the group consisting of SiN, SiCOH, SiO2, and spin-on glass.
claim 13
15. The semiconductor device according to wherein said base dielectric layer is an inorganic material and said cap dielectric layer is an organic material.
claim 11
16. The semiconductor device according to wherein said base dielectric layer is selected from the group consisting of inorganic xerogels, SiCOH, hexametholsylsesquoixane, fluorinated spin-on glass, and spin-on glass.
claim 15
17. The semiconductor device according to wherein said base dielectric layer is an organic material and said cap dielectric layer is an inorganic material.
claim 12
18. The semiconductor device according to wherein said base dielectric layer is selected from the group consisting of benzocyclobutanes, parylene-N, parylene-F, and polyamides and said cap dielectric layer is selected from the group consisting of SiN, SiCOH, Sio2, and spin-on glass.
claim 17
19. The semiconductor device according to wherein said base dielectric layer is an inorganic material and said cap dielectric layer is an organic material.
claim 12
20. The semiconductor device according to wherein said base dielectric layer is selected from the group consisting of inorganic xerogels, SiCOH, hexametholsylsesquoixane, fluorinated spin-on glass, and spin-on glass.
claim 19