US20010028518A1 - SiO2-coated mirror substrate for EUV - Google Patents
SiO2-coated mirror substrate for EUV Download PDFInfo
- Publication number
- US20010028518A1 US20010028518A1 US09/756,018 US75601801A US2001028518A1 US 20010028518 A1 US20010028518 A1 US 20010028518A1 US 75601801 A US75601801 A US 75601801A US 2001028518 A1 US2001028518 A1 US 2001028518A1
- Authority
- US
- United States
- Prior art keywords
- mirror
- substrate
- cover layer
- amorphous
- euv
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- This is a continuation of PCT/EP99/04209, which is pending.
- Not applicable.
- Not applicable.
- 1. Field of the Invention
- This invention relates to a mirror substrate, a mirror with such a mirror substrate, and a production process therefor, and also an EUV projection exposure device therewith.
- Monocrystalline silicon is a preferred substrate material for robust mirrors with a high thermal loading and best shape stability.
- For applications in the X-ray region, in particular for soft X-radiation, also termed “extreme ultraviolet” (EUV), extremely smooth surfaces with micro-roughness values in the angstrom range are required. This is attained with so-called “super-polish”.
- It has been found by experience that silicon substrates can be homogeneously polished to this standard only poorly or not at all homogeneously over sufficiently large surfaces, particularly in the case of strongly curved surfaces.
- 2. Discussion of Relevant Art
- The preferred application of such EUV mirrors is in EUV lithography, for the mirrors of illumination, mask and projection objective. Their quality of polishing is then decisive for the usability of the whole system. This follows, e.g., from K. Hoh, Bull. Electrotechn. Lab. 49, No. 12, October 1985, pp. 47-54; T. E. Jewell et al., Proc. SPIE, Vol. 1527 (1991); and David M. Williamson, OSA IODC Conference Paper LWA 2-1, pp. 181-184, Jun. 10, 1998.
- An X-ray mirror is known from Japanese Patent Document JP-B2-96/032 592, in which a matrix with sintered SiC is coated with crystalline SiC, by which means a precisely smooth surface is obtained.
- The invention has as its object the provision of a mirror substrate which combines the positive properties of the silicon single crystal substrate with outstanding “superpolish” properties.
- This object is attained by a mirror substrate of crystal, wherein an amorphous cover layer is applied to the substrate, and the amorphous cover layer is covered with a multilayer reflecting layer. According to one feature of the invention, a thin, amorphous layer, e.g. of quartz glass, amorphous SiO 2, or Al2O3, is applied to a substrate member comprising a crystal with low thermal expansion and high thermal conductivity (diamond, BN, SiC, silicon, as examples). A cover layer which is known to be well suited for “super-polish” is thereby prepared, without impairing the other properties of the substrate.
- The invention also includes the following features:
- The substrate comprises at least one of the following materials: diamond, BN, SiC, or silicon.
- The cover layer comprises at least one of the following amorphous materials: quartz glass, SiO 2 or Al2O3.
- The amorphous cover layer has a thickness in the range of 1 μm through 100 μm.
- The micro-roughness of the amorphous cover layer is in the angstrom range.
- The multilayer reflection layers are constituted for a wavelength region of 10 nm to 20 nm, preferably 13 nm.
- The mirror has a curved surface.
- In a production process for such a mirror, a substrate of crystal is shaped close to the final contour, an amorphous cover layer is deposited on the mirror side of the substrate, an optical final polishing takes place and a multilayer reflecting layer is applied.
- The amorphous cover layer is deposited by means of CVD.
- Application of mirrors according to the invention in EUV projection exposure devices comprises an EUV projection exposure device with an EUV source, an illuminating optics, a mask, a projection objective, and a wafer, wherein at least one mirror according to the invention is contained in the illuminating optics or in the projection objective.
- The invention will be described in more detail with reference to the drawing:
- FIG. 1 shows schematically an EUV projection exposure device according to the invention.
- The structure of such a EUV projection exposure device is known per se in numerous variants, e.g. from the above-cited reference Jewell and Williamson and the references cited therein. It includes a EUV source 1, e.g., a synchrotron or a laser plasma focus source, which produces a
EUV beam 2 with, e.g., 13 nm wavelength, or another wavelength in the preferred range of about 10-20 nm, for which suitable multilayer reflecting layers (see the reflectinglayer 533, below) are available. - An
illuminating optics 3 serves for the suitable shaping of the EUV light as regards light conducting value, pupil filling, homogeneity, telecentricity, and the like. The mask 4 is thereby illuminated, shown as a transmission mask, but in many cases, however, preferably as a reflection mask. This mask 4 is imaged on a reduced scale by aprojection objective 5 onto theobject 6, the wafer. - The
projection objective 5 contains, as in many known designs, four 51, 52, 53, 54. The structure according to the invention is representatively shown oncurved mirrors mirror 53 of these, with the siliconsingle crystal substrate 531, athin cover layer 532 of amorphous quartz, which with “super-polish” defines the highly accurate final contour of themirror 53, and themultilayer reflecting layer 533. The latter provides, as a distributed Bragg reflector, a relatively high reflectivity of about 40-60% for a given spectral region. - The shape of the
substrate 531 is determined by the requirements of mechanical stability, cooling, installation into a mount, matching to the beam path (vignetting), and the like. The usable surface is first precisely optically polished to near the final contour. The thin amorphous quartz layer is then deposited. The CVD process, for example, is suitable for this. Deformations of the mirror surfaces due to strains in thelayer 532 can be kept to a minimum by the process parameters and after-treatments. They can be kept to a minimum by deflection during the shaping of thesubstrate 531 and by corresponding polishing of thequartz layer 532. - The
amorphous quartz layer 532 thus does not serve as an adhesive base, diffusion barrier, or similar auxiliary layer of themultilayer reflection layers 533, but rather as the material which supports the contour of themirror 53. - The final shaping processing, the so-called “super-polish”, thus follows after the coating with the
quartz layer 532. - A
reflection layer 533, constructed as a multilayer EUV reflection layer, is then arranged on thislayer 532 in a known manner. - Mirrors constructed in this manner can of course be used at any other place of the projection exposure device and also in other devices, e.g., X-ray microscopes or telescopes.
- Each material of the substrate member, which is used for the “bulk”, such as the above mentioned materials of low thermal expansion and at the same time high thermal conductivity, can be provided with a thin cover layer of material which can well be polished to optical quality. Conformity as regards adhesion properties, strains, corrosion, and the like can be attained with known criteria.
Claims (11)