TWI892609B - 一種具有高對比的負性液晶組合物及其應用 - Google Patents

一種具有高對比的負性液晶組合物及其應用

Info

Publication number
TWI892609B
TWI892609B TW113115715A TW113115715A TWI892609B TW I892609 B TWI892609 B TW I892609B TW 113115715 A TW113115715 A TW 113115715A TW 113115715 A TW113115715 A TW 113115715A TW I892609 B TWI892609 B TW I892609B
Authority
TW
Taiwan
Prior art keywords
general formula
carbon atoms
liquid crystal
compound represented
crystal composition
Prior art date
Application number
TW113115715A
Other languages
English (en)
Other versions
TW202442856A (zh
Inventor
李承賀
楊雪彪
陳卯先
郭雲鵬
任婕
劉友然
葉宇行
王智成
Original Assignee
大陸商北京八億時空液晶科技股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大陸商北京八億時空液晶科技股份有限公司 filed Critical 大陸商北京八億時空液晶科技股份有限公司
Publication of TW202442856A publication Critical patent/TW202442856A/zh
Application granted granted Critical
Publication of TWI892609B publication Critical patent/TWI892609B/zh

Abstract

本發明涉及液晶材料及其應用領域，尤其涉及一種具有高對比的負性液晶組合物及其應用。所述液晶組合物至少包含一種或多種通式I~III所代表的化合物；通式I中，R 1代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，R 2代表1-7個碳原子的烷基或2-7個碳原子的烯基；通式II中，R 3、R 4各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基；通式III中，R 5、R 6各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，n代表1或2， 代表 、 和 中的一種或多種。

Description

一種具有高對比的負性液晶組合物及其應用
本發明涉及液晶材料及其應用領域，尤其涉及一種具有高對比的負性液晶組合物及其應用。
隨著資訊時代的進步，液晶顯示技術的發展作為資訊顯示的液晶應用領域，也在不斷發展。人們對液晶顯示器性能的要求越來越高，也激發了人們對液晶材料的研究興趣，使得液晶技術成為熱點，並持續發展。
目前，液晶顯示器正朝向大型化、寬視角、高對比、快速回應方面發展，負性液晶的性能起到了至關重要的作用，其中IPS和FFS模式顯示器因為其獨有的硬屏特性以及非常寬的視角特性，目前廣泛用於手機、筆記型電腦、平板電腦、電腦顯示器、電視等方面。
IPS和FFS顯示模式因其獨特的液晶平面排列方式導致顯示面板在暗態時容易出現漏光，對比度性能方面明顯劣勢於VA類（MVA、PVA、UV2A、PSVA）顯示器。經過研究發現，造成液晶顯示器件漏光的主要原因時是：光散射（LC Scattering）、摩擦均勻性（rubbing uniformity）、彩色濾光膜漏光以及極化能力（polarize ability），其中，光散射在漏光性能的影響因素中占比達60%以上。 根據散射係數關係式： 其中， 為光學各向異性， 為非尋常光折射率， 為尋常光折射率，d為液晶盒厚度， 為展曲彈性常數， 為旋轉粘度。由該關係式可知，LC Scattering與K 11成反比關係，在提高K 11的情況下，可以降低液晶材料的漏光。 由對比度公式： CR=L255/L0*100%， 其中，L255為開態亮度，L0為關態亮度。可以看出，顯著影響CR的應該是L0的變化。在關態下，L0與液晶分子的介電性能無關，而與液晶材料本身的LC Scattering相關；LC Scattering愈小，L0也愈小，從而對比度也就愈高。 鑒於此，特提出本申請。
本發明的目的在於提供一種負性液晶組合物，其具有較大的展曲彈性常數以及較小的液晶光散射係數，因而能夠在很大程度的提高液晶顯示器對比度，解決上述缺陷。
基於此，本發明的具體技術方案如下：
本發明首先提供一種液晶組合物，其至少包含一種或多種通式I所代表的化合物、一種或多種通式II所代表的化合物以及一種或多種通式III所代表的化合物；
所述通式I所代表的化合物的結構為： I 所述通式I中，R 1代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，R 2代表1-7個碳原子的烷基或2-7個碳原子的烯基；
所述通式為II所代表的化合物的結構為： II 所述通式II中，R 3、R 4各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基。
所述通式為III所代表的化合物的結構為： III 所述通式III中，R 5、R 6各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，n代表1或2， 代表 、 和 中的一種或多種。
本發明具體技術方案如下：
本發明首先提供一種液晶組合物，其至少包含一種或多種通式I所代表的化合物、一種或多種通式II所代表的化合物、以及一種或多種通式III所代表的化合物；
所述通式I所代表的化合物的結構為： I 所述通式I中，R 1代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，R 2代表1-7個碳原子的烷基或2-7個碳原子的烯基；
所述通式為II所代表的化合物的結構為： II 所述通式II中，R 3、R 4各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基。
所述通式為III所代表的化合物的結構為： III 所述通式III中，R 5、R 6各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，n代表1或2， 代表 、 和 中的一種或多種。
本發明發現，通式I所代表的化合物與上述通式II~III所代表的化合物協同配合後，能夠顯著提高液晶材料的展曲彈性常數K 11，降低液晶材料的漏光，提液晶顯示器的高對比。
作為優選，所述通式Ⅰ的化合物選自式IA1-IA22和IB1-IB14所代表化合物中的一種或幾種：
IA1 IA2
IA3 IA4
IA5 IA6
IA7 IA8
IA9 IA10
IA11 IA12
IA13 IA14
IA15 IA16
IA17 IA18
IA19 IA20
IA21 IA22
IB1 IB2
IB3 IB4
IB5 IB6
IB7 IB8
IB9 IB10
IB11 IB12
IB13 IB14
。
本發明提供的所述通式為II的化合物為含有雙環己烷的化合物，該化合物具有好的低溫溶解性能。
作為優選，所述通式II所代表的化合物選自IIA1-IIA12、IIB1-IIB14、IIC1-IIC4中所示化合物中的一種或幾種：
IIA1 IIA2
IIA3 IIA4
IIA5 IIA6
IIA7 IIA8
IIA9 IIA10
IIA11 IIA12
IIB1 IIB2
IIB3 IIB4
IIB5 IIB6
IIB7 IIB8
IIB9 IIB10
IIB11 IIB12
IIB13 IIB14
IIC1 IIC2
IIC3 IIC4
本發明提供的所述通式III所代表的化合物為含有三環中性化合物，該化合物具有高的清亮點、較好的低溫溶解性。
作為優選，所述通式III所代表的化合物選自IIIA1-IIIA48、IIIB1-IIIB48、IIIC1-IIIC48中所示化合物中的一種或幾種：
IIIA1 IIIA2
IIIA3 IIIA4
IIIA5 IIIA6
IIIA7 IIIA8
IIIA9 IIIA10
IIIA11 IIIA12
IIIA13 IIIA14
IIIA15 IIIA16
IIIA17 IIIA18
IIIA19 IIIA20
IIIA21 IIIA22
IIIA23 IIIA24
IIIA25 IIIA26
IIIA27 IIIA28
IIIA29 IIIA30
IIIA31 IIIA32
IIIA33 IIIA34
IIIA35 IIIA36
IIIA37 IIIA38
IIIA39 IIIA40
IIIA41 IIIA42
IIIA43 IIIA44
IIIA45 IIIA46
IIIA47 IIIA48
IIIB1 IIIB2
IIIB3 IIIB4
IIIB5 IIIB6
IIIB7 IIIB8
IIIB9 IIIB10
IIIB11 IIIB12
IIIB13 IIIB14
IIIB15 IIIB16
IIIB17 IIIB18
IIIB19 IIIB20
IIIB21 IIIB22
IIIB23 IIIB24
IIIB25 IIIB26
IIIB27 IIIB28
IIIB29 IIIB30
IIIB31 IIIB32
IIIB33 IIIB34
IIIB35 IIIB36
IIIB37 IIIB38
IIIB39 IIIB40
IIIB41 IIIB42
IIIB43 IIIB44
IIIB45 IIIB46
IIIB47 IIIB48
IIIC1 IIIC2
IIIC3 IIIC4
IIIC5 IIIC6
IIIC7 IIIC8
IIIC9 IIIC10
IIIC11 IIIC12
IIIC13 IIIC14
IIIC15 IIIC16
IIIC17 IIIC18
IIIC19 IIIC20
IIIC21 IIIC22
IIIC23 IIIC24
IIIC25 IIIC26
IIIC27 IIIC28
IIIC29 IIIC30
IIIC31 IIIC32
IIIC33 IIIC34
IIIC35 IIIC36
IIIC37 IIIC38
IIIC39 IIIC40
IIIC41 IIIC42
IIIC43 IIIC44
IIIC45 IIIC46
IIIC47 IIIC48
。
作為優選，所述液晶組合物中還含有通式Ⅳ所代表的化合物： Ⅳ 所述通式Ⅳ中，R 7、R 8各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，n代表1或2；
本發明提供的通式Ⅳ所代表的化合物為甲氧基橋的化合物，其加入到液晶組合物中有助於配合本發明所述通式I-通式III所代表的化合物，能夠進一步提高液晶組合物的介電各向異性。
優選地，所述通式Ⅳ所代表的化合物選自ⅣA1-ⅣA12、ⅣB1-ⅣB12、ⅣC1-ⅣC12、ⅣD1-ⅣD12中所示化合物中的一種或幾種：
ⅣA1 ⅣA2
ⅣA3 ⅣA4
ⅣA5 ⅣA6
ⅣA7 ⅣA8
ⅣA9 ⅣA10
ⅣA11 ⅣA12
ⅣB1 ⅣB2
ⅣB3 ⅣB4
ⅣB5 ⅣB6
ⅣB7 ⅣB8
ⅣB9 ⅣB10
ⅣB11 ⅣB12
ⅣC1 ⅣC2
ⅣC3 ⅣC4
ⅣC5 ⅣC6
ⅣC7 ⅣC8
ⅣC9 ⅣC10
ⅣC11 ⅣC12
ⅣD1 ⅣD2
ⅣD3 ⅣD4
ⅣD5 ⅣD6
ⅣD7 ⅣD8
ⅣD9 ⅣD10
ⅣD11 ⅣD12
。
作為優選，所述液晶組合物中還含有通式Ⅴ所代表的化合物，所述通式Ⅴ所代表的化合物為具有負的介電各向異性的化合物。
所述通式Ⅴ所代表的化合物的結構為： Ⅴ 所述通式Ⅴ中，R 9、R 10各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，n代表1或2， 代表 、 和 中的一種或多種；
優選地，所述通式Ⅴ所代表的化合物選自式ⅤA1-ⅤA48、ⅤB1-ⅤB48、ⅤC1-ⅤC48、ⅤD1-ⅤD48、ⅤE1-ⅤE48、ⅤF1-ⅤF48中所示化合物中的一種或幾種：
ⅤA1 ⅤA2
ⅤA3 ⅤA4
ⅤA5 ⅤA6
ⅤA7 ⅤA8
ⅤA9 ⅤA10
ⅤA11 ⅤA12
ⅤA13 ⅤA14
ⅤA15 ⅤA16
ⅤA17 ⅤA18
ⅤA19 ⅤA20
ⅤA21 ⅤA22
ⅤA23 ⅤA24
ⅤA25 ⅤA26
ⅤA27 ⅤA28
ⅤA29 ⅤA30
ⅤA31 ⅤA32
ⅤA33 ⅤA34
ⅤA35 ⅤA36
ⅤA37 ⅤA38
ⅤA39 ⅤA40
ⅤA41 ⅤA42
ⅤA43 ⅤA44
ⅤA45 ⅤA46
ⅤA47 ⅤA48
ⅤB1 ⅤB2
ⅤB3 ⅤB4
ⅤB5 ⅤB6
ⅤB7 ⅤB8
ⅤB9 ⅤB10
ⅤB11 ⅤB12
ⅤB13 ⅤB14
ⅤB15 ⅤB16
ⅤB17 ⅤB18
ⅤB19 ⅤB20
ⅤB21 ⅤB22
ⅤB23 ⅤB24
ⅤB25 ⅤB26
ⅤB27 ⅤB28
ⅤB29 ⅤB30
ⅤB31 ⅤB32
ⅤB33 ⅤB34
ⅤB35 ⅤB36
ⅤB37 ⅤB38
ⅤB39 ⅤB40
ⅤB41 ⅤB42
ⅤB43 ⅤB44
ⅤB45 ⅤB46
ⅤB47 ⅤB48
ⅤC1 ⅤC2
ⅤC3 ⅤC4
ⅤC5 ⅤC6
ⅤC7 ⅤC8
ⅤC9 ⅤC10
ⅤC11 ⅤC12
ⅤC13 ⅤC14
ⅤC15 ⅤC16
ⅤC17 ⅤC18
ⅤC19 ⅤC20
ⅤC21 ⅤC22
ⅤC23 ⅤC24
ⅤC25 ⅤC26
ⅤC27 ⅤC28
ⅤC29 ⅤC30
ⅤC31 ⅤC32
ⅤC33 ⅤC34
ⅤC35 ⅤC36
ⅤC37 ⅤC38
ⅤC39 ⅤC40
ⅤC41 ⅤC42
ⅤC43 ⅤC44
ⅤC45 ⅤC46
ⅤC47 ⅤC48
ⅤD1 ⅤD2
ⅤD3 ⅤD4
ⅤD5 ⅤD6
ⅤD7 ⅤD8
ⅤD9 ⅤD10
ⅤD11 ⅤD12
ⅤD13 ⅤD14
ⅤD15 ⅤD16
ⅤD17 ⅤD18
ⅤD19 ⅤD20
ⅤD21 ⅤD22
ⅤD23 ⅤD24
ⅤD25 ⅤD26
ⅤD27 ⅤD28
ⅤD29 ⅤD30
ⅤD31 ⅤD32
ⅤD33 ⅤD34
ⅤD35 ⅤD36
ⅤD37 ⅤD38
ⅤD39 ⅤD40
ⅤD41 ⅤD42
ⅤD43 ⅤD44
ⅤD45 ⅤD46
ⅤD47 ⅤD48
ⅤE1 ⅤE2
ⅤE3 ⅤE4
ⅤE5 ⅤE6
ⅤE7 ⅤE8
ⅤE9 ⅤE10
ⅤE11 ⅤE12
ⅤE13 ⅤE14
ⅤE15 ⅤE16
ⅤE17 ⅤE18
ⅤE19 ⅤE20
ⅤE21 ⅤE22
ⅤE23 ⅤE24
ⅤE25 ⅤE26
ⅤE27 ⅤE28
ⅤE29 ⅤE30
ⅤE31 ⅤE32
ⅤE33 ⅤE34
ⅤE35 ⅤE36
ⅤE37 ⅤE38
ⅤE39 ⅤE40
ⅤE41 ⅤE42
ⅤE43 ⅤE44
ⅤE45 ⅤE46
ⅤE47 ⅤE48
ⅤF1 ⅤF2
ⅤF3 ⅤF4
ⅤF5 ⅤF6
ⅤF7 ⅤF8
ⅤF9 ⅤF10
ⅤF11 ⅤF12
ⅤF13 ⅤF14
ⅤF15 IIF16
ⅤF17 ⅤF18
ⅤF19 ⅤF20
ⅤF21 ⅤF22
ⅤF23 ⅤF24
ⅤF25 ⅤF26
ⅤF27 ⅤF28
ⅤF29 ⅤF30
ⅤF31 ⅤF32
ⅤF33 ⅤF34
ⅤF35 ⅤF36
ⅤF37 ⅤF38
ⅤF39 ⅤF40
ⅤF41 ⅤF42
ⅤF43 ⅤF44
ⅤF45 ⅤF46
ⅤF47 ⅤF48
。
為確保本發明所述組合物中各組分之間實現更為顯著的協同效應，以有效提高所述液晶材料的綜合應用性能，本發明進一步對所述液晶材料的中各組分的用量進行了優選。
作為優選，所述的液晶組合物包括以下重量百分比的組分： （1）1~25%通式I所代表的化合物， （2）1~50%通式II所代表的化合物， （3）1~30%通式III所代表的化合物， （4）1~25%通式Ⅳ所代表的化合物， （5）1~50%通式Ⅴ所代表的化合物。
更優選地，所述液晶組合物包括以下重量百分比的組分： （1）1~20%通式I所代表的化合物， （2）5~50%通式II所代表的化合物， （3）5~30%通式III所代表的化合物， （4）5~25%通式Ⅳ所代表的化合物， （5）5~50%通式Ⅴ所代表的化合物。
進一步優選地，所述液晶組合物包括以下重量百分比的組分： （1）5~20%通式I所代表的化合物， （2）20~50%通式II所代表的化合物， （3）10~30%通式III所代表的化合物， （4）5~20%通式Ⅳ所代表的化合物， （5）20~50%通式Ⅴ所代表的化合物。
最優選地，所述液晶組合物包括以下重量百分比的組分： （1）5~15%通式I所代表的化合物， （2）30~45%通式II所代表的化合物， （3）10~25%通式III所代表的化合物， （4）10~20%通式Ⅳ所代表的化合物， （5）20~35%通式Ⅴ所代表的化合物。
本發明所提供的液晶組合物還包含一種或多種通式Ⅵ所代表的化合物，該化合物具有大的彈性常數、較低的旋轉粘度，對提高對比有很大幫助。
作為優選，所述通式Ⅵ所代表的化合物為： Ⅵ 所述通式Ⅵ中，R 11、R 1 2各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基。
更優選地，通式Ⅵ所代表的化合物選自ⅥA1-ⅥA20、ⅥB1-ⅥB18、ⅥC1-ⅥC14中所示化合物中的一種或幾種：
ⅥA1 ⅥA2
ⅥA3 ⅥA4
ⅥA5 ⅥA6
ⅥA7 ⅥA8
ⅥA9 ⅥA10
ⅥA11 ⅥA12
ⅥA13 ⅥA14
ⅥA15 ⅥA16
ⅥA17 ⅥA18
ⅥA19 ⅥA20
ⅥB1 ⅥB2
ⅥB3 ⅥB4
ⅥB5 ⅥB6
ⅥB7 ⅥB8
ⅥB9 ⅥB10
ⅥB11 ⅥB12
ⅥB13 ⅥB14
ⅥB15 ⅥB16
ⅥB17 ⅥB18
ⅥC1 ⅥC2
ⅥC3 ⅥC4
ⅥC5 ⅥC6
ⅥC7 ⅥC8
ⅥC9 ⅥC10
ⅥC11 ⅥC12
ⅥC13 ⅥC14
。
作為優選，在所述液晶組合物中所有組分的重量百分比總和為100%的情況下，通式Ⅵ所述化合物在組合物中的重量含量為0~30%；優選地為5~25%；進一步優選為5~15%。
本發明所提供的液晶組合物中，通式I所代表的化合物為含有二苯並噻吩的化合物，該化合物具有較大的介電常數、較大的彈性常數；通式II所代表的化合物為雙環己烷的化合物，具有低的旋轉粘度和優良的互溶性特點，是快回應液晶顯示必不可少的組分；通式為Ⅲ的化合物為三環中性化合物，該化合物具有較高的清亮點，可有效提升液晶組合物的清亮點；通式Ⅳ所代表的化合物為甲氧基橋介電各向異性的化合物，具有大的介電各向異性，可有效降低液晶面板的驅動電壓；通式為Ⅴ的化合物為負性化合物，其加入到液晶組合物中有助於配合本發明所述通式I-通式Ⅳ所代表的化合物，能夠進一步提高液晶組合物的介電各向異性；通式Ⅵ所代表的化合物為三環含有乙撐鍵的化合物，該化合物具有大的彈性常數、較低的旋轉粘度，其加入到液晶組合物中有助於配合本發明所述通式I-通式Ⅳ所代表的化合物，能夠進一步提高液晶組合物的彈性常數。
本發明中對所述液晶組合物的製備方法無特殊限制，可採用常規方法將兩種或多種化合物混合進行生產，如通過在高溫下混合不同組分並彼此溶解的方法製備，其中，將液晶組合物溶解在用於該化合物的溶劑中並混合，然後在減壓下蒸餾出該溶劑；或者本發明所述液晶組合物可按照常規的方法製備，如將其中含量較小的組分在較高的溫度下溶解在含量較大的主要組分中，或將各所屬組分在有機溶劑中溶解，如丙酮、氯仿或甲醇等，然後將溶液混合去除溶劑後得到。
本發明進一步提供上述液晶組合物在液晶顯示裝置上的應用，優選在VA、IPS或FFS模式顯示器中的應用。
基於上述技術方案，本發明的有益效果在於：
本發明所述液晶組合物具有低旋轉粘度、大的彈性常數、大的光學各向異性、良好的低溫互溶性、快的回應速度以及較大的對比度，能夠用於多種顯示模式的快回應液晶顯示，其在VA、IPS或FFS模式顯示器中的使用能明顯改善液晶顯示器顯示效果，尤其適用於IPS和FFS模式液晶顯示器。
為使本發明的目的、技術方案和優點更加清楚，下面將對本發明中的技術方案進行清楚、完整地描述，顯然，所描述的實施例是本發明一部分實施例，而不是全部的實施例。基於本發明中的實施例，本領域普通技術人員在沒有作出創造性勞動前提下所獲得的所有其他實施例，都屬於本發明保護的範圍。
除非另有說明，本發明中百分比為重量百分比；溫度單位為攝氏度；△n代表光學各向異性（25℃）；△ε代表介電各向異性（25℃，1000Hz）；γ1代表旋轉粘度（mPa.s，25℃）；Cp代表液晶組合物的清亮點（℃）；K 11、K 22、K 33分別代表展曲、扭曲和彎曲彈性常數（pN，25℃）。
以下各實施例中，液晶化合物中基團結構用表1所示代碼表示。 表1：液晶化合物的基團結構代碼
基團 代碼 基團名稱
C 1,4-環己基
L 1,4-環己烯基
P 1,4-亞甲苯
GⅠ 3-氟-1,4-亞甲苯
G 2-氟-1,4-亞甲苯
W 2,3-二氟-1,4-亞甲苯
S 2,11-二氟-3，10-二苯並噻吩
-O- O 氧取代基
-F F 氟取代基
C nH 2n+1或C mH 2m+1 n或m 烷基
-(CH 2) n- n 亞烷基
-C≡C- T 炔鍵
-HC=CH- V 烯基
以如下化合物結構為例：
表示为：4L3OSO3
表示為：4CC1OW01
以下各實施例中，液晶組合物的製備均採用熱溶解方法，包括以下步驟：用天平按重量百分比稱量液晶化合物，其中稱量加入順序無特定要求，通常以液晶化合物熔點由高到低的順序依次稱量混合，在60~100℃下加熱攪拌使得各組分溶解均勻，再經過濾，最後封裝即得目標樣品。
以下各實施例中，液晶組合物中各組分的重量百分比及液晶組合物的性能參數見下述表格。
實施例1 表2：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 3 △n △ε Cp γ1 K 11K 22K 33 0.100 -3.27 119.8 163.4 25.96 12.98 25.67
Ⅰ 2L3OSO3 3
II 3CCV 18
II 3CCV1 4
II 3CC2V1 6
II 5CC3 8
III 3CCP1 9
III 3CLP1 6
Ⅳ 3CC1OWO2 12
Ⅴ 2CPWO2 7
Ⅴ 3CCWO2 8
Ⅴ 3CLWO2 4
Ⅴ 3CCWO1 8
Ⅴ 2CLWO2 4
實施例2 表3：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 4 △n △ε Cp γ1 K 11K 22K 33 0.100 -3.36 120.0 164.9 26.10 13.05 26.15
Ⅰ 2L3OSO4 3
II 3CCV 20
II 3CCV1 4
II 3CC2V1 6
II 5CC3 6
III 3CCP1 7
III 3CLP1 8
Ⅳ 3CC1OWO2 12
Ⅴ 3CCWO2 11
Ⅴ 3CLWO2 2
Ⅴ 3CPWO2 2
Ⅴ 3CCWO1 6
Ⅴ 2CLWO2 2
Ⅴ 2CPWO2 3
Ⅴ 2CCWO2 4
實施例3 表4：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 4 △n △ε Cp γ1 K 11K 22K 33 0.100 -3.33 119.8 162.6 26.64 13.32 26.10
Ⅰ 2L3OSO2 3
II 3CCV 16
II 3CCV1 4
II 3CC2V1 6
II 5CC3 10
III 3CCP1 10
III 3CLP1 5
Ⅳ 3CC1OWO2 12
Ⅴ 3CCWO2 8
Ⅴ 3CLWO2 4
Ⅴ 3CCWO1 8
Ⅴ 2CLWO2 4
Ⅴ 2CPWO2 6
實施例4 表5：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 4 △n △ε Cp γ 1K 11K 22K 33 0.099 -3.29 121.7 168.9 26.46 13.23 26.24
Ⅰ 2L3OSO2 2
II 3CCV 18
II 3CCV1 4
II 3CC2V1 6
II 5CC3 8
III 3CCP1 7
III 3CLP1 8
Ⅳ 3CC1OWO2 12
Ⅴ 3CCWO2 11
Ⅴ 3CLWO2 5
Ⅴ 2CPWO2 4
Ⅴ 3CCWO1 8
Ⅴ 2CLWO2 3
實施例5 表6：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 2 △n △ε Cp γ 1K 11K 22K 33 0.099 -3.23 121.9 169.9 25.88 12.94 25.72
Ⅰ 2L3OSO2 3
II 3CCV 18
II 3CCV1 4
II 3CC2V1 6
II 5CC3 8
III 3CCP1 7
III 3CLP1 8
Ⅳ 3CC1OWO2 12
Ⅴ 2CPWO2 6
Ⅴ 3CCWO2 11
Ⅴ 3CLWO2 4
Ⅴ 3CCWO1 8
Ⅴ 2CLWO2 3
實施例6 表7：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 3 △n △ε Cp γ 1K 11K 22K 33 0.100 -3.23 121.0 165.9 26.88 13.44 25.38
Ⅰ 2L3OSO2 3
II 3CCV 18
II 3CCV1 4
II 3CC2V1 6
II 5CC3 8
III 3CCP1 5
III 3CCP3 3
III 3CLP1 8
Ⅳ 3CC1OWO2 12
Ⅴ 3CCWO1 7
Ⅴ 2CLWO2 2
Ⅴ 2CPWO2 6
Ⅴ 3CCWO2 11
Ⅴ 3CLWO2 4
實施例7 表8：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 4 △n △ε Cp γ 1K 11K 22K 33 0.099 -3.29 121.5 168.2 26.84 13.42 25.84
Ⅰ 2L3OSO2 2
II 3CCV 18
II 3CC2V1 6
II 5CC3 8
II 3CCV1 3
III 3CLP1 8
III 3CCP3 3
III 3CCP1 5
Ⅳ 3CC1OWO2 9
Ⅳ 5CC1OWO2 4
Ⅴ 2CPWO2 6
Ⅴ 3CCWO2 12
Ⅴ 3CCWO1 6
Ⅴ 4CLWO2 6
實施例8 表9：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 2 △n △ε Cp γ 1K 11K 22K 33 0.099 -3.29 119.3 165.8 26.62 13.31 27.79
Ⅰ 2L3OSO2 4
II 3CCV 20
II 3CC2V1 6
II 5CC3 4
III 3CCP1 9
III 3CCP3 6
III 3CLP1 8
Ⅳ 3CC1OWO2 11
Ⅳ 3C1OWO2 4
Ⅴ 2CCWO2 4
Ⅴ 3CCWO2 10
Ⅴ 3CCWO1 8
Ⅴ 3CLWO3 4
實施例9 表10：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 5 △n △ε Cp γ 1K 11K 22K 33 0.100 -3.39 115.8 167.8 26.84 13.42 26.02
Ⅰ 2L3OSO4 2
II 3CCV 21
II 3CC2V1 5
II 5CC3 5
III 3CCP1 10
III 3CCP3 6
III 3CLP1 6
Ⅳ 2CC1OWO2 10
Ⅳ 3CC1OWO2 10
Ⅴ 2CPWO2 8
Ⅴ 3CC2WO2 10
Ⅴ 3CCWO2 2
實施例10 表11：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 4 △n △ε Cp γ 1K 11K 22K 33 0.101 -3.29 120.4 167.4 26.62 13.31 25.93
Ⅰ 2L3OSO4 3
II 3CCV 20
II 3CC2V1 6
II 5CC3 8
III 3CLP1 8
III 3CCP1 10
Ⅳ 3CC1OWO2 12
Ⅴ 2CPWO2 4
Ⅴ 3CCWO2 7
Ⅴ 3CCWO1 4
Ⅴ 3CLWO2 4
Ⅴ 2CLWO2 4
Ⅴ 3CLWO3 2
Ⅴ 2CCWO2 4
實施例11 表12：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 3 △n △ε Cp γ 1K 11K 22K 33 0.101 -3.30 121.6 169.3 26.28 13.14 25.84
Ⅰ 2L3OSO4 3
II 3CCV 20
II 3CC2V1 6
II 5CC3 8
III 3CCP1 10
III 3CLP1 7
Ⅳ 3CC1OWO2 12
Ⅴ 2CPWO2 6
Ⅴ 3CCWO2 11
Ⅴ 3CCWO1 4
Ⅴ 3CLWO2 4
Ⅴ 2CLWO2 4
Ⅴ 3CLWO3 2
實施例12 表13：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 2 △n △ε Cp γ 1K 11K 22K 33 0.101 -3.34 117.3 160.6 26.08 13.04 25.02
Ⅰ 2L3OSO4 4
II 3CCV 20
II 3CC2V1 8
II 5CC3 10
III 3CLP1 8
III 3CCP1 4
Ⅳ 3CC1OWO2 12
Ⅴ 2CPWO2 7
Ⅴ 3CCWO2 10
Ⅴ 3CCWO1 8
Ⅴ 3PPWO4 2
Ⅴ 2CCWO2 5
實施例13 表14：液晶組合物中各組分的重量百分比及性能參數
類別 化合物代碼 重量百分比（%） 性能參數 參數值
Ⅰ 3L3OSO3 3 △n △ε Cp γ 1K 11K 22K 33 0.100 -3.36 116.3 162.6 26.88 13.44 25.72
Ⅰ 2L3OSO4 3
II 3CCV 20
II 3CC2V1 9
II 5CC3 10
III 3CLP1 7
III 3CCP1 4
Ⅳ 3CC1OWO2 12
Ⅴ 2CPWO2 7
Ⅴ 3CCWO2 10
Ⅴ 3CCWO1 8
Ⅴ 3PPWO4 2
Ⅵ 2CC2WO2 5
對比例1 表15：液晶組合物中各組分的重量百分比及性能參數
化合物代碼 重量百分比（%） 性能參數 參數值
3CCV 24 △n △ε Cp γ 1K 11K 22K 33 0.099 -3.26 123.6 169.7 21.06 10.53 23.18
3CCV1 5
3CC2V1 4
2CPWO2 6
3CPWO2 3
3CCWO2 10
3CLP1 6
3CCWO1 10
3CCP1 4
2CCWO2 10
3CLWO2 5
3CLWO3 5
VCCWO1 8
將實施例1與對比例1所得液晶組合物的各性能參數值進行比較，參見表16。 表16：液晶組合物的性能參數比較
Cp △n Δε K 11 γ 1
實施例1 119.8 0.100 -3.27 25.96 163.4
對比例1 123.6 0.099 -3.26 21.06 169.7
經比較可知：實施例1與對比例1相比，液晶混合物的介電各向異性（Δε）、清亮點（Cp）、光學各向異性（△n）、旋轉粘度（γ 1）基本一致，在此情況下實施例1提供的液晶混合物的彈性常數（K 11）更大，具有更小的液晶光學散射係數，這就表示在暗態時，實施例中的液晶漏光現象比較小，因此液晶顯示器在L0時具有較低的亮度值。因此在驅動電壓等條件近似的情況下，本發明所提供的液晶具有更高的對比度。
相對於實施例1，對比例1中減少了通式I所代表的化合物，然而實施例1卻相較於對比例1有更大的彈性常數，因此表明通式I化合物是本發明所提供的液晶組合物必不可少的組份之一。
由以上實施例可知，本發明所提供的液晶組合物具有大的彈性常數度、高電阻率、適合的光學各向異性、良好的低溫互溶性、低的旋轉粘度以及優異的光穩定性和熱穩定性，可降低液晶顯示器的回應時間，從而解決液晶顯示器回應速度慢的問題。因此，本發明所提供的液晶組合物適用於快回應的VA、IPS及FFS型TFT液晶顯示裝置，尤其適用於IPS及FFS液晶顯示裝置。
最後應說明的是：以上實施例僅用以說明本發明的技術方案，而非對其限制；儘管參照前述實施例對本發明進行了詳細的說明，本領域的普通技術人員應當理解：其依然可以對前述各實施例所記載的技術方案進行修改，或者對其中部分技術特徵進行等同替換；而這些修改或者替換，並不使相應技術方案的本質脫離本發明各實施例技術方案的精神和範圍。

Claims (10)

  1. 一種液晶組合物，其特徵在於，至少包含一種或多種通式I所代表的化合物、一種或多種通式II所代表的化合物以及一種或多種通式III所代表的化合物；所述通式I所代表的化合物的結構為：I所述通式I中，R1代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，R2代表1-7個碳原子的烷基或2-7個碳原子的烯基；所述通式為II所代表的化合物的結構為：II所述通式II中，R3、R4各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基；所述通式為III所代表的化合物的結構為：III所述通式III中，R5、R6各自独立地代表1-7个碳原子的烷基、1-7个碳原子的烷氧基或2-7个碳原子的烯基，n代表1或2，代表、和中的一种或多种。
  2. 如請求項1所述的液晶組合物，其特徵在於，所述通式Ⅰ所代表的化合物選自式IA1-IA22和IB1-IB14所示化合物中的一種或幾種： IA1 IA2 IA3 IA4 IA5 IA6 IA7 IA8 IA9 IA10 IA11 IA12 IA13 IA14 IA15 IA16 IA17 IA18 IA19 IA20 IA21 IA22 IB1 IB2 IB3 IB4 IB5 IB6 IB7 IB8 IB9 IB10 IB11 IB12 IB13 IB14
    。
  3. 如請求項1所述的液晶組合物，其特徵在於，所述通式II所代表的化合物選自IIA1-IIA12、IIB1-IIB14、IIC1-IIC4中所示化合物中的一種或幾種： IIA1 IIA2 IIA3 IIA4 IIA5 IIA6 IIA7 IIA8 IIA9 IIA10 IIA11 IIA12 IIB1 IIB2 IIB3 IIB4 IIB5 IIB6 IIB7 IIB8 IIB9 IIB10 IIB11 IIB12 IIB13 IIB14 IIC1 IIC2 IIC3 IIC4。
  4. 如請求項1所述的液晶組合物，其特徵在於，所述通式III所代表的化合物選自IIIA1-IIIA48、IIIB1-IIIB48、IIIC1-IIIC48中所示化合物中的一種或幾種： IIIA1 IIIA2 IIIA3 IIIA4 IIIA5 IIIA6 IIIA7 IIIA8 IIIA9 IIIA10 IIIA11 IIIA12 IIIA13 IIIA14 IIIA15 IIIA16 IIIA17 IIIA18 IIIA19 IIIA20 IIIA21 IIIA22 IIIA23 IIIA24 IIIA25 IIIA26 IIIA27 IIIA28 IIIA29 IIIA30 IIIA31 IIIA32 IIIA33 IIIA34 IIIA35 IIIA36 IIIA37 IIIA38 IIIA39 IIIA40 IIIA41 IIIA42 IIIA43 IIIA44 IIIA45 IIIA46 IIIA47 IIIA48 IIIB1 IIIB2 IIIB3 IIIB4 IIIB5 IIIB6 IIIB7 IIIB8 IIIB9 IIIB10 IIIB11 IIIB12 IIIB13 IIIB14 IIIB15 IIIB16 IIIB17 IIIB18 IIIB19 IIIB20 IIIB21 IIIB22 IIIB23 IIIB24 IIIB25 IIIB26 IIIB27 IIIB28 IIIB29 IIIB30 IIIB31 IIIB32 IIIB33 IIIB34 IIIB35 IIIB36 IIIB37 IIIB38 IIIB39 IIIB40 IIIB41 IIIB42 IIIB43 IIIB44 IIIB45 IIIB46 IIIB47 IIIB48 IIIC1 IIIC2 IIIC3 IIIC4 IIIC5 IIIC6 IIIC7 IIIC8 IIIC9 IIIC10 IIIC11 IIIC12 IIIC13 IIIC14 IIIC15 IIIC16 IIIC17 IIIC18 IIIC19 IIIC20 IIIC21 IIIC22 IIIC23 IIIC24 IIIC25 IIIC26 IIIC27 IIIC28 IIIC29 IIIC30 IIIC31 IIIC32 IIIC33 IIIC34 IIIC35 IIIC36 IIIC37 IIIC38 IIIC39 IIIC40 IIIC41 IIIC42 IIIC43 IIIC44 IIIC45 IIIC46 IIIC47 IIIC48。
  5. 如請求項1所述的液晶組合物，其特徵在於，所述液晶組合物中還含有通式Ⅳ所代表的化合物：Ⅳ所述通式Ⅳ中，R7、R8各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，n代表1或2。
  6. 如請求項1~4任一項所述的液晶組合物，其特徵在於，所述液晶組合物中還含有通式Ⅴ所代表的化合物，所述通式Ⅴ所代表的化合物的結構為：Ⅴ所述通式Ⅴ中，R9、R10各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，n代表1或2，代表、和中的一種或多種。
  7. 如請求項5所述的液晶組合物，其特徵在於，所述液晶組合物還含有通式Ⅴ所代表的化合物，所述通式Ⅴ所代表的化合物的結構為：Ⅴ所述通式Ⅴ中，R9、R10各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基，n代表1或2，代表、和中的一種或多種。
  8. 如請求項7所述的液晶組合物，其特徵在於，包括以下重量百分比的組分：（1）1~25%通式I所代表的化合物，（2）1~50%通式II所代表的化合物，（3）1~30%通式III所代表的化合物，（4）1~25%通式Ⅳ所代表的化合物，（5）1~50%通式Ⅴ所代表的化合物。
  9. 如請求項7所述的液晶組合物，其特徵在於，所述液晶組合物中還含有通式Ⅵ所代表的化合物：Ⅵ所述通式Ⅵ中，R11、R12各自獨立地代表1-7個碳原子的烷基、1-7個碳原子的烷氧基或2-7個碳原子的烯基。
  10. 一種液晶組合物在液晶顯示裝置上的應用，如請求項1~9所述的液晶組合物在VA、IPS或FFS模式顯示器中的應用。
TW113115715A 2023-04-28 2024-04-26 一種具有高對比的負性液晶組合物及其應用 TWI892609B (zh)