TWI886161B - 鉬填充 - Google Patents

鉬填充 Download PDF

Info

Publication number
TWI886161B
TWI886161B TW109135654A TW109135654A TWI886161B TW I886161 B TWI886161 B TW I886161B TW 109135654 A TW109135654 A TW 109135654A TW 109135654 A TW109135654 A TW 109135654A TW I886161 B TWI886161 B TW I886161B
Authority
TW
Taiwan
Prior art keywords
molybdenum
layer
filling method
precursor
features
Prior art date
Application number
TW109135654A
Other languages
English (en)
Other versions
TW202129049A (zh
Inventor
勞倫斯 施洛斯
思魯提 維克 湯貝爾
閆仲伯
克林帕 派崔克 Ａ 凡
約書亞 柯林斯
Original Assignee
美商蘭姆研究公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 美商蘭姆研究公司 filed Critical 美商蘭姆研究公司
Publication of TW202129049A publication Critical patent/TW202129049A/zh
Application granted granted Critical
Publication of TWI886161B publication Critical patent/TWI886161B/zh

Abstract

用鉬(Mo)填充特徵部之方法的實施例包括在包含有開口及內部之特徵部中沉積第一層Mo，並非保形地處理第一層，使得開口附近之區域比內部之區域被優先處理。在一些實施例中，第二Mo層係沉積於經處理之第一層上。用Mo填充特徵部之方法的實施例包括控制Mo前驅物通量，以在保形與非保形填充之間轉變。

Description

鉬填充
本發明係關於鉬填充。
材料(包括含鎢材料)的沉積是許多半導體製造製程之不可缺的部分。此些材料可用於水平互連、相鄰金屬層之間的貫孔、以及金屬層與裝置之間的接觸。在沉積的示例中，可使用WF6 透過化學氣相沉積(CVD)製程將鎢層沉積在氮化鈦(TiN)阻障層上以形成TiN/W雙層。然而，隨著裝置微縮及產業中採用更複雜的圖案化方案，薄鎢膜之沉積成為一項挑戰。特徵部尺寸及膜厚度上持續的減小對TiN/W膜堆帶來諸多挑戰。此些包括較薄膜之高電阻率及TiN阻障特性之劣化。在複雜之高深寬比結構(例如3D NAND結構)中進行沉積特別具挑戰性。
本文所提供的背景係為了概述本發明脈絡之目的。本案發明人的成果(在此先前技術段落中所述之範圍內)、以及在申請時可能未以其他方式認定為先前技術之描述態樣，並未明示或默示地被承認為相對於本發明的先前技術。
本發明之一態樣涉及一方法，其包括提供包含有一或更多特徵部之一基板，該一或更多特徵部之每一者具有至少一開口及透過該至少一開口可流體進入之一內部區域；沉積一第一層鉬於該一或更多特徵部；以及非保形地處理該第一層，使得該處理係相對於該第一層之更遠地位於該特徵部之該內部區域中的部位而優先施行於該第一層之位於該一或更多特徵部之該至少一開口附近的部位處。
在一些實施例中，非保形地處理該第一層包括非保形地抑制該第一層。在一些實施例中，非保形地處理該第一層包括非保形地蝕刻該第一層。
在一些實施例中，處理該第一層係於沉積該第一層鉬期間執行。在一些此等實施例中，該方法包括於前驅物通量或濃度較接近該一或更多特徵部之該至少一開口的條件下，將該一或更多特徵部暴露於鉬前驅物。在一些此等實施例中，鉬前驅物為氧鹵化鉬。在一些此等實施例中，該氧鹵化鉬在該一或更多特徵部之該一或更多開口附近因蝕刻反應而具有比在該內部區域中更低的生長速率。在一些此等實施例中，該氧鹵化鉬在該一或更多特徵部之該一或更多開口附近因抑制處理而具有比在該內部區域中更低的生長速率。
在一些實施例中，處理該第一層係在沉積該第一層鉬之後執行。
在一些實施例中，處理該第一層包括將其暴露於抑制化學物質。 在一些實施例中，該抑制化學物質為含氮化學物質。在一些此等實施例中，處理該第一層包括在將其暴露於含氮化學物質之後，將其暴露於氫氣與鉬前驅物之一或更多者。
在一些實施例中，處理該第一層包括將其暴露於蝕刻化學物質。在一些此等實施例中，其中該蝕刻化學物質為含鹵素化學物質。在一些此等實施例中，處理該第一層包括在將其暴露於含鹵素化學物質之後，沖洗容置該基板之一腔室。
在一些實施例中，處理該第一層包括將其暴露於含氮化合物。在一些實施例中，處理該第一層包括將其暴露於含鹵素化合物。在一些實施例中，處理該第一層包括將其暴露於氨或三氟化氮。在一些實施例中，處理該第一層為非電漿的熱製程。在一些實施例中，處理該第一層為電漿製程。
在以上任何方法中，沉積該第一層鉬包括原子層沉積製程，其係使用H2 作為用於氧鹵化鉬或鹵化鉬前驅物之還原劑。
在以上任何方法中，該方法可進一步包括在非保形地處理該第一層之後，進一步包括沉積一第二層鉬。在一些此等實施例中，沉積該第二層包括原子層沉積製程，其係使用H2 作為用於氧鹵化鉬或鹵化鉬前驅物之還原劑。
根據諸多實施例，基板包括具有側壁之3-D結構，其中該一或更多特徵部之該一或更多開口為該等側壁中的開口。根據諸多實施例，該一或更多特徵部具有一封閉端。
本發明之另一態樣涉及一方法，其包括：使用鉬(Mo)前驅物，在第一鉬(Mo)前驅物流速、鉬(Mo)前驅物分壓及鉬(Mo)前驅物注入時間下沉積一保形層鉬(Mo)；以及增加鉬(Mo)前驅物流速、鉬(Mo)前驅物分壓及鉬(Mo)前驅物注入時間中之至少一者，以增加該特徵部開口處之該鉬(Mo)前驅物通量，因而在該保形層鉬(Mo)上沉積一第二層鉬(Mo)。在一些此等實施例中，鉬(Mo)前驅物為氧氯化鉬。
本發明之另一態樣涉及一設備，其包括：一製程腔室，其具有各自配置成固持一基板之一或更多站；一或更多製程氣體入口，用於耦接至一氫(H2 )氣體源、一鉬前驅物氣體源、一惰性沖洗氣體源以及一處理氣體源；以及一控制器，用於控制該設備中之操作，其包括機器可讀指令用以：(a) 透過該一或更多製程氣體入口，交替H2 與鉬前驅物脈衝進入該製程腔室中，以在基板上沉積第一鉬層；(b) 於(a)之後，使一處理氣體進入以處理該第一鉬層； 以及(c) 於(b)之後，透過該一或更多製程氣體入口，使H2 與鉬前驅物脈衝交替進入該製程腔室中，以在基板上沉積第二鉬層。
本發明之又另一態樣涉及一設備，其包括：一製程腔室，其具有各自配置成固持一基板之一或更多站；一或更多製程氣體入口，用於耦接至一氫(H2 )氣體源、一鉬前驅物氣體源、一惰性沖洗氣體源以及一處理氣體源；以及一控制器，用於控制該設備中之操作，其包括機器可讀指令用以：(a) 透過該一或更多製程氣體入口，使H2 及鉬前驅物進入該製程腔室中，以在基板上沉積第一鉬層；(b) 於(a)之後，改變鉬(Mo)前驅物流速或注入時間之一或更多者，以在基板上沉積第二鉬層。
此些及其他態樣於下參考圖式進一步描述。
於下文描述中，闡述許多具體細節以對所呈現之實施例提供透徹的瞭解。可在沒有此些具體細節之一些或全部者下實施所揭示之實施例。在其他實例中，不再詳細描述眾所周知的製程操作，以免不必要地模糊所揭示之實施例。儘管將結合具體實施例來描述所揭示之實施例，但將理解，其並非意圖限制所揭示之實施例。
於下文描述中，闡述許多具體細節以對所呈現之實施例提供透徹的瞭解。可在沒有此些具體細節之一些或全部者下實施所揭示之實施例。在其他實例中，不再詳細描述眾所周知的製程操作，以免不必要地模糊所揭示之實施例。儘管將結合具體實施例來描述所揭示之實施例，但將理解，其並非意圖限制所揭示之實施例。
本文提供的是用鉬(Mo)填充特徵部之方法，其可用於邏輯與記憶體應用。圖1A及1B為根據諸多實施例之材料堆疊(包括Mo)的示意性示例。圖1A及1B說明特定堆疊中材料順序，並可與任何適當之架構及應用一起使用，如下相對於圖2A-2J進一步所述。在圖1A之示例中，基板102具有沉積其上之Mo層108。基板102可為矽或其他半導體晶圓，例如200 mm晶圓、300 mm晶圓或450 mm晶圓，其包括具有一或更多層材料(例如介電、導電或半導電材料)沉積其上之晶圓。該等方法亦可應用於在其他基板上(例如玻璃、塑料及其類似者)上形成金屬化堆疊結構。
在圖1A中，介電層104在基板102上。介電層104可直接沉積在基板102之半導體(例如，Si)表面上，或者可有任何數量之中間層。介電層之示例包括摻雜及未摻雜的氧化矽、氮化矽及氧化鋁層，具體示例包括摻雜或未摻雜之層SiO2 及Al2 O3 。又，在圖1A中，擴散阻障層106設置於Mo層108與介電層104之間。擴散阻障層之示例包括氮化鈦(TiN)、鈦/氮化鈦(Ti/TiN)、氮化鎢(WN)及碳氮化鎢(WCN)。擴散阻障層進一步示例為多成分含鉬膜，如下進一步所述。 Mo層108為該結構之主要導體。在一些實施例中，Mo層108可包括在不同條件下沉積之多個主體層。Mo層108可包括或可不包括Mo成核層。此外，在一些實施例中，可將Mo層108沉積在包括另一材料之生長起始層上，例如鎢(W)或含W生長起始層。
圖1B示出材料堆疊之另一示例。在此示例中，堆疊包括基板102、介電層104，且Mo層108直接沉積在介電層104上而無中間擴散阻障層。Mo層108係如相對於圖1A所述。透過使用具有比W更低電子平均自由徑之Mo作為主導體，可得到較低電阻率薄膜。
儘管圖1A及1B示出金屬化堆疊的示例，但該等方法及所得堆疊並不限於此。例如，在一些實施例中，Mo可在具有或不具有起始層下直接沉積在Si或其他半導體基板上。圖1A及1B說明特定堆疊中材料順序之示例，並可與任何適當的架構及應用一起使用，如下相對於圖2A-2J進一步所述。
本文所述之方法係在基板(可容置於腔室中)上執行。基板可為矽或其他半導體晶圓，例如200 mm晶圓、300 mm晶圓或450 mm晶圓，其包括具有一或更多層材料(例如介電、導電或半導電材料)沉積其上之晶圓。該等方法不限於半導體基板，並可執行於用鉬填充任何特徵部。
基板可具有例如貫孔或接觸孔之特徵部，其可透過狹窄及/或凹陷開口、特徵部內窄縮、及高深寬比中之一或更多者來表徵。特徵部可形成於一或更多上述層中。例如，特徵部可至少部分地形成於介電層中。在一些實施例中，特徵部可具有至少約2 : 1、至少約4 : 1、至少約6 : 1、至少約10 : 1、至少約25 : 1或更高的深寬比。特徵部之一示例為半導體基板或基板上之層中的孔或貫孔。
圖2A繪出動態隨機存取記憶體(DRAM)架構之示意性示例，其包括Mo埋入式字元線(bWL)208於矽基板202中。Mo bWL形成於蝕刻於矽基板202中之溝槽中。對溝槽形成襯底(lining)的是保形阻障層206及設置於保形阻障層206與矽基板202之間的絕緣層204。在圖2之示例中，絕緣層204可為由高k介電材料(例如氧化矽或氮化矽材料)所形成之閘極氧化物層。在本文所揭示之一些實施例中，保形阻障層為TiN或含鎢層，例如WN或WCN。在一些實施例中，其TiN係用作阻障層，保形阻障層206與Mo bWL 208之間可存有保形含鎢生長起始層。可替代地， Mo bWL 208可直接沉積在TiN或其他擴散阻障層上。在一些實施例中，不存在層204及206之一或兩者。
圖2A中所示之bWL結構為包含有Mo填充層之架構示例。在bWL之製造期間，Mo係沉積至由矽基板202中蝕刻凹部所定義之特徵部中，而該蝕刻凹部保形地襯有層206及204(若存在的話)。
圖2B-2H為根據所揭示實施例可在其中沉積Mo之諸多結構的額外示意性示例。圖2B示出將用Mo填充之垂直特徵部201的剖面繪圖示例。該特徵部可包括基板202中之特徵孔205。孔205或其他特徵部可具有接近開口的尺寸，如介於約10 nm至500 nm之間(例如介於約25 nm至約300 nm之間)的開口直徑或線寬。特徵孔205可稱為未填充特徵部或簡稱特徵部。特徵部201及任何特徵部可部份地透過延伸通過特徵部長度之軸線218來表徵，其垂直定向特徵部具有垂直軸，而水平定向特徵部則具有水平軸。
在一些實施例中，特徵部為3D NAND結構中之字元線特徵部。例如，基板可包括具有任意數量之字元線(例如50至150)的字元線結構，其具有至少200 Å深的垂直通道。另一示例為基板或層中的溝槽。特徵部可具任何深度。在諸多實施例中，特徵部可具有底層，例如阻障層或黏附層。底層之非限定示例包括介電層及導電層，例如，氧化矽、氮化矽、碳化矽、金屬氧化物、金屬氮化物、金屬碳化物及金屬層。
圖2C示出具有凹陷輪廓之特徵部201的示例。凹陷輪廓為從特徵部底部、封閉端或內部朝特徵部開口變窄的輪廓。根據諸多實施方式，輪廓可逐漸變窄及/或在特徵部開口處包括突部。 圖2C示出後者的示例，其底層213對特徵孔105之側壁或內表面形成襯底。底層213可為例如擴散阻障層、黏附層、成核層、其組合、或任何其他可應用材料。底層之非限定示例可包括介電層及導電層，例如，氧化矽、氮化矽、碳化矽、金屬氧化物、金屬氮化物、金屬碳化物及金屬層。在特定實施方式中，底層可為鈦、氮化鈦、氮化鎢、鋁化鈦、鎢及鉬中之一或更多者。在一些實施例中，底層為無鎢。在一些實施例中，底層為無鉬。底層213形成突部215，使得底層213在特徵部201開口附近比在特徵部201內部更厚。
在一些實施方式中，可填充在特徵部內具有一或更多縮部之特徵部。圖2D示出具有縮部之諸多填充特徵部的視圖示例。圖2D中之每一示例(a)、(b)及(c)在特徵部內之中點處包括縮部209。縮部209可例如介於約15 nm至20 nm寬。縮部會在使用習知技術於特徵部中沉積鎢或鉬期間導致夾止(pinch off)，且在一部分特徵部被填充之前，沉積的金屬會阻止進一步沉積超過縮部，從而導致特徵部中出現孔隙。示例(b) 在特徵部開口處進一步包括襯底/阻障突部215。此等突部亦可能是潛在的夾止點。示例(c)包括比示例(b)中突部215更遠離場區域之縮部212。
亦可填充例如3D記憶體結構中的水平特徵部。圖2E示出包含縮部251之水平特徵部250的示例。例如，水平特徵部250可為3D NAND(亦稱為垂直NAND或VNAND)結構中的字元線。在一些實施方式中，縮部可能是由於在3D NAND或其他結構中存在柱體。圖2F呈現3-D NAND結構210(形成於矽基板202上)之剖面側視圖，其具有VNAND堆疊(左225及右226)、中央垂直結構230、以及在中央垂直結構230之相對側壁240上具有開口222之複數堆疊水平特徵部220。注意，圖2F顯示所展示之3-D NAND結構210的兩個”堆疊”，其共同形成”溝槽狀”中央垂直結構230， 然而，在某些實施例中，可能有兩個以上的”堆疊”按順序排列並在空間上相互平行，每一相鄰”堆疊”對之間的間隙形成中央垂直結構230，如同圖2F中明確示出的那樣。在此實施例中，水平特徵部220為3-D記憶體字元線特徵部，其可從中央垂直結構230透過開口222而流體進入。雖然未在圖中明確指出，但圖2F中所示之3-D NAND堆疊225及226(即，左3-D NAND堆疊225及右3-D NAND堆疊226)兩者中存在的水平特徵部220亦可透過額外3-D NAND堆疊所形成之類似垂直結構(於最左側及最右側，但未示出)而從堆疊的另一側(分別為最左側及最右側)來進入。換言之， 每一3-D NAND堆疊225、226含有字元線特徵部堆疊，字元線特徵部可從3-D NAND堆疊之兩側透過中央垂直結構230而流體進入。在圖2F中示意性示出之特定示例中，每一3-D NAND堆疊包含6對堆疊字元線，但在其他實施例中，3-D NAND記憶體佈局可含有任意數量之字元線垂直堆疊對。
3-D NAND堆疊中之字元線特徵部通常是透過以下形成：沉積氧化矽與氮化矽層的交替堆疊，接著再選擇性地去除氮化物層並留下其間具有間隙之氧化物層堆疊。此些間隙為字元線特徵部。只要有可用之形成字元線的技術，以及可用以成功地完成垂直特徵部之(實質上)無孔隙填充的技術，則可在此等3-D NAND結構中垂直堆疊任何數量的字元線。因此，例如，VNAND堆疊可包括介於2與256之間的水平字元線特徵部、或介於8與128之間的水平字元線特徵部、或介於16與64之間的水平字元線特徵部等等(所列範圍當理解為包括所載端點)。
圖2G呈現圖2F側視圖中所示之相同3-D NAND結構210的剖面俯視圖，其剖面係穿過水平截面260而取得，如圖2F中水平虛線所示。圖2G之剖面示出幾行柱體255，其在圖2F中示為從半導體基板202之基底垂直走線至3-D NAND堆疊210之頂部。在一些實施例中，此些柱體255係由多晶矽材料形成，且對於3-D NAND結構210有結構及功能上的重要性。在一些實施例中，此等多晶矽柱體可作為堆疊記憶單元(形成於柱體內)之閘電極。圖2G之俯視圖示出，柱體255在通往字元線特徵部220之開口222中形成縮部-即，字元線特徵部220之流體可進入性(從中央垂直結構230經由開口222進入，如圖2G中的箭頭所示)被柱體255所抑制。在一些實施例中，相鄰多晶矽柱體之間的水平間隙尺寸介於約1與20 nm之間。流體可進入性的降低提高材料均勻填充字元線特徵部120的難度。字元線特徵部220之結構以及因柱體255存在導致用鉬材料對其進行均勻填充的挑戰進一步於圖2H、2I及2J中說明。
圖2H展示穿過類似於圖2F中所示之3-D NAND結構的垂直切面，但此處集中於一對字元線特徵部220，並額外示意性地示出導致在填充字元線特徵部220中形成孔隙之填充製程。圖2I亦示意性地示出孔隙275，但此圖中是經由穿過柱體255之水平切面來示出，其類似於圖2G中所展示之水平切面。 圖2J示出鉬材料在形成縮部之柱體255周圍處的積聚，該積聚導致開口222之夾止，使得在孔隙275之區域中不能沉積額外的鉬材料。從圖2H及2I可明顯得知，無孔隙之鉬填充依賴於在鉬沉積於柱體255周圍而造成開口222夾止並阻止前驅物遷移進入字元線特徵部220之前，有足夠數量之沉積前驅物向下遷移穿過垂直結構230、穿過開口222、越過窄縮柱體255、並進入字元線特徵部220之最遠範圍。類似地，圖2J展示從上方橫截面看到的單個字元線特徵部220，並示出鉬材料之大致保形沉積如何因柱體255之顯著寬度造成部分地阻塞及/或窄化及/或縮化原本將穿過字元線特徵部220之開放路徑而開始夾止字元線特徵部220的內部。(應注意，圖2J中之示例可理解為圖2I中所示之柱體縮部之3D特徵部的2D效果圖(rendering)，因而示出將在平面圖中而非剖面圖中看到的縮部)。
三維結構可能需要更長及/或更集中地暴露於前驅物，以允許最內部及最底部的區域得以被填充。三維結構在採用鹵化鉬及/或氧鹵化鉬前驅物時可能特別具挑戰性，因為其易於蝕刻，而更長且更集中的暴露使得作為結構的一部分有更多蝕刻。
用於水平定向及垂直定向特徵部之特徵部填充的示例於下描述。應注意，在至少大多數例子中，此些示例適用於水平定向或垂直定向特徵部兩者。此外，亦應注意，在以下描述中，術語”側向”可用於指大致正交於特徵部軸線的方向，術語”垂直”指大致沿特徵部軸線的方向。
特徵部內之材料的分佈可透過其階梯覆蓋率來表徵。為了此描述目的，將”階梯覆蓋率”定義為兩厚度的比率，即，特徵部內之材料的厚度除以開口附近之材料的厚度。為了本文目的，術語”特徵部內部”代表沿特徵部軸線位於特徵部中點附近之特徵部的中間部分，例如，從特徵部開口沿特徵部深度測得之距離大約25%至75%之間的區域，或者在某些實施例中約40%至60%，或者位於從開口沿特徵部軸線測得之距離大約75%至95%之間的特徵部末端。術語”在特徵部之開口附近”或”在特徵部開口附近”代表特徵部的頂部，其位於開口邊緣或代表開口邊緣之其他元件之25%內(在一些實施例中，於10%內)。保形膜將具有約100%的階梯覆蓋率。超過100%的階梯覆蓋率可例如透過在特徵部中間或底部附近比在特徵部開口處用更多材料填充特徵部來達到。
圖3為示出根據諸多實施例用鉬填充結構之操作的製程圖。首先，在操作302中，將鉬(Mo)膜沉積於結構中。此操作可稱為沉積1。在許多實施例中，操作302為大致保形沉積，其對結構之暴露表面形成襯底。例如，在3D NAND結構(例如圖2F所示)中，Mo膜對字元線特徵部220形成襯底。根據諸多實施例，使用ALD製程沉積Mo膜，以達到良好保形性。Mo ALD製程之進一步描述提供於下。在一些實施例中，在操作302之後，特徵部未被Mo封閉，而是充分開放以允許進一步的反應氣體於隨後沉積中進入特徵部。
接下來，在操作304中，對沉積膜進行非保形處理。本文中之非保形處理係指，比起在特徵部內部，優先在特徵部之一開口或多個開口處或附近進行處理。對於3D NAND結構，該處理可為垂直方向上保形，使得底部字元線特徵部處理程度與頂部字元線特徵部大致相同，而非保形則是，字元線特徵部的內部未受到處理或受處理程度顯著小於特徵部開口。
成核抑制作用抑制處理表面上之後續鉬成核。其可涉及以下一或更多者：抑制膜之沉積、處理物質與Mo膜之反應以形成化合物膜(如Mo2 N)、以及抑制物質之吸附。在後續沉積操作期間，相對於未被抑制或被抑制程度較小的部分，底層膜之被抑制部分上有成核延遲。蝕刻去除處理表面上之沉積膜。此可包括使蝕刻劑物質與鉬膜反應以形成氣態副產物，其接著被去除。可執行其他蝕刻方法，包括原子層蝕刻。操作304可為電漿或非電漿操作。若為非電漿操作，其可為純熱或由一些其他能量(例如UV)活化。
氮作用為抑制物質，而鹵素(例如，氟及氯)物質作用為蝕刻劑。為了進行純抑制處理，操作304可包括將Mo膜暴露於不含鹵素之含氮化學物質。為了執行純蝕刻處理，操作304可包括將Mo膜暴露於不含氮之含鹵素化學物質。可在一些實施例中使用其他抑制化學物質(例如，含氧化學物質)。使膜暴露於含氮且含鹵素之化學物質(例如，三氟化氮(NF3 )或氨/氟(NH3 /F2 ))可同時抑制並蝕刻。
根據諸多實施例，可在同一處理腔室或不同處理腔室中執行操作302。若在同一腔室中執行，其可在單站或多站腔室中執行。於一些實施例中，在多站腔室中，可在第一站中執行操作302，並在第二站中執行操作304。如下進一步討論，操作304可為連續流或脈衝製程。在後一例中，可依次脈衝不同氣體以調變該處理。
在操作304之後，在操作306中執行第二沉積。該第二沉積可透過ALD或CVD製程來執行。ALD製程係於下相對於圖8進一步描述，且通常包含用於表面介導反應之反應物的交替脈衝。在CVD方法中，通常使反應物流入，使其以氣相存在於反應腔室中。CVD可包含氣相反應。為了沉積至3D NAND結構中，可使用ALD製程以在整個結構中達良好階梯覆蓋率。氣體因該處理之作用而更易到達特徵部內部。在蝕刻製程之後，沉積於特徵部入口附近的膜被去除，從而對氣體提供更多空間以到達特徵部內部並防止夾止。在一些實施例中，可去除足夠的Mo膜，使得底層表面全部或部分暴露，從而增加此些區域處之成核延遲。在抑制製程之後，提高成核延遲，從而實現由內而外之填充製程。在一些實施例中，操作306(其可稱為沉積2製程)可完成結構之填充。在其他實施例中，可執行再一次額外處理/沉積操作。為了調整字元線中之側向非保形性，可調控壓力及處理氣體流速。較高的腔室壓力及較低的處理氣體流速(及/或濃度)促進字元線特徵部之開口處的處理，其多於字元線特徵部內部的處理。因此，在一些實施例中，腔室壓力之示例範圍為3托耳(Torr)至40托耳。
為了達到側向非保形性但具有從上到下的均勻性，可使用裝料容器來輸送氣體。此些係於下相對於圖7進行描述，且可能對深結構(如，7-10微米深)特別有用。在一些實施例中，可同時執行沉積及非保形處理。例如，圖3中之操作302及304可同時執行。根據諸多實施例，可執行後續沉積(例如，沉積2)，或者操作302及304可能足以填充特徵部。如上所述，可使用鹵化鉬及氧鹵化鉬作為蝕刻劑氣體。在一些實施例中，可使用此些作為沉積及蝕刻劑氣體。透過適當地控制特徵部內之沉積反應物的濃度，可在諸多階段控制特徵部中沉積及蝕刻的量。在特定示例中，可使用氧氯化鉬(MoOx Cly ，其中x及y為形成穩定化合物之大於0的數字)作為Mo沉積氣體及蝕刻劑氣體，其對特徵部內部有淨沉積，而對特徵部開口有較低沉積或淨蝕刻。如下相對於圖6D進一步所述，總生長速率對表面處之前驅物通量或濃度敏感。在一些實施例中，較高的MoOx Cly 通量可導致更多的蝕刻。並且，在高MoOx Cly 通量下，特徵部內部之前驅物濃度比開口附近或場區域上低，從而允許自下而上的生長。前驅物注入時間、前驅物流速、腔室壓力、前驅分壓可用於調變前驅物通量。
亦可在Mo沉積期間非保形地執行抑制處理。例如，Mo前驅物若未完全還原，則可抑制沉積。在一示例中，在高MoO2 Cl2 通量下，特徵部開口處之MoO2 Cl2 濃度比特徵內部高。若H2 共反應物流量足夠低，以致於MoO2 Cl2 無法在特徵部開口處全部還原，則其可作為抑制劑。
圖4示出執行以鉬填充3D NAND結構之製程的示例。在圖4中，示出3D NAND結構之單個字元線的剖面圖。(如圖2J之示例中，圖4中之字元線特徵部示出可在平面圖中而非剖面圖中看到的柱體縮部，以說明該縮部。) 於470，在沉積1製程之後示出字元線特徵部。示出底層406；此可例如為阻障層。保形Mo膜405對特徵部表面形成襯底。在一些實施例中，保形Mo膜405直接沉積於介電表面上，例如氧化鋁或氧化矽表面。Mo層405可為成核層、成核及主體層、或主體層。 接下來，在471將特徵部暴露於抑制化學物質以抑制部位465。在此示例中，穿過柱體縮部451之部位465被抑制，而452處的內部表面未被抑制。抑制可包括，例如暴露於NH3 氣體，或暴露於由氣體(例如N2 、H2 、形成氣體、NH3 、O2 、CH4 等)產生之遠端或直接(原位)電漿。接下來，執行製程以根據抑制輪廓選擇性地沉積鉬：主體Mo 408優先沉積於Mo層405之未被抑制部位上，從而在472填充縮部後方難以填充的區域。在此示例中，繼續進行主體沉積，在473用主體Mo 408填充特徵部之其餘處。
在一些實施例中，透過使用Mo前驅物(其可在沉積期間於特徵部開口處作為抑制劑)，可在如上所討論之操作中執行471及472所示之序列。
圖5示出執行以鉬填充3D NAND結構之製程的另一示例。在圖5之示例中，示出底層506；此可為例如阻障層。保形Mo膜505對特徵部表面形成襯底。在一些實施例中，保形Mo膜505直接沉積於介電表面上，例如氧化鋁或氧化矽表面。Mo層505可為成核層、成核及主體層、或主體層。在此之後於571進行非保形蝕刻(具高選擇性以保護底層506(若存在的話))。例如，對於TiN底層可進行具有高Mo : TiN選擇性之非保形蝕刻。非保形蝕刻之結果為，保形Mo層505於特徵部之內部552中完好無損，而於特徵部開口522處則變薄或完全去除。接下來，在572，將主體Mo 508沉積於Mo層405之其餘部位上，使得縮部後方難以填充的區域被填充。在此示例中，繼續進行主體沉積，在573用主體Mo 508填充特徵部之其餘處。在一些實施例中，可重複沉積-蝕刻-沉積操作以填充特徵部。根據諸多實施方式，每一後續沉積操作可包括或可不包括成核層之沉積。在一些實施方式中，該處理亦可包括抑制作用。
在一些實施例中，可透過使用Mo前驅物(其可於沉積期間在特徵部開口處作為蝕刻劑)，在如上所討論之操作中執行571及572所示之序列。
在一些實施例中，於圖4及圖5之示例中，沉積1及沉積2各自用於沉積主體Mo層，沉積1用以沉積保形層，而沉積2用以填充特徵部。
在一些實施例中，保形Mo層可被表徵為低電阻率，且在一些實施例中為低應力及/或低氟。由於未填充字元線特徵部(除了成核層之外，若沉積的話)，因此可使用相對快的沉積技術。在一些實施例中，此包括含鉬前驅物與氫(H2 )或其他還原劑之交替脈衝，以在ALD製程中沉積第一鎢層。沖洗操作可隔開脈衝。對於沉積可使用相對短的脈衝時間以增加產量。
可使用第二組條件來沉積第二主體層。如同第一主體層，第二主體層可為低電阻率層，且在一些實施例中可為低應力及/或低氟層。在一些實施例中，操作306包括相對於操作302增加的脈衝時間及增加的沖洗時間。在特定實施例中，可增加含Mo前驅物脈衝時間。增加脈衝及/或沖洗時間可促進反應物擴散至字元線中。在一些實施例中，從操作302至操作306亦可改變溫度；例如，較高溫度可用於加快反應時間。在一些實施例中，較低溫度可用於使反應物得以在反應之前擴散至字元線特徵部中。在一些實施例中，第二組條件可包括流速的變化。例如，可提高含鉬前驅物及/或還原劑的流速。
可在不同條件下沉積第三主體Mo層。此層可被表徵為覆蓋層，其在後續步驟中被去除並且可沉積於側壁上，例如圖2F之3D NAND結構中的側壁240。此層可被表徵為低粗糙度。當要去除鉬時，可容許較高電阻率及/或氟濃度。第三組條件可包括以下任一者：更快的時序(若以比操作405更短的脈衝時間使用ALD的話)、使用CVD代替ALD、以及在流入一或更多反應物氣體期間或之間引入氮(N2 )。
圖6A為示出根據諸多實施例處理Mo膜之操作的製程圖。首先，在操作602中，將表面暴露於含鹵素及/或氮的化學物質。在操作602中，氮為抑制化學物質；除了氮以外還可使用其他抑制化學物質或適當地用其代替氮。含氟及氯之化學物質係用於蝕刻。操作602可為連續流或脈衝操作，且可為電漿或熱之非電漿操作。亦可施加其他活化能。
用於抑制之示例性含氮氣體包括NF3 、NH3 、氮(N2 )及肼(N2 H4 )。可使用其他含氮氣體，但在許多實施例中則避免含氧化合物(例如，NO2 )。氣體可透過非電漿之熱製程流入腔室中，或者可用於在遠端或原位電漿產生器中產生電漿。在一些實施例中，較少的反應性氣體(例如，N2 )可能需要電漿活化以達有效抑制。
用於蝕刻之含鹵素氣體的示例包括NF3 、F2 、氟化氫(HF)、氯(Cl2 )、三氟化氯(ClF3 )及其他含Cl或F氣體。亦可使用鹵化鉬及氧鹵化鉬氣體。若無還原劑與其反應，則此些將蝕刻膜。
接下來，在操作604中，可使用非鹵素氣體進行沖洗。可使用惰性氣體，例如Ar或He。亦可使用N2 。該沖洗為非電漿製程，其可去除表面的氯或氟物質。在一些實施例中 (例如，在操作602中基板未暴露於氯或氟物質中)，可省略操作604。
接下來，在操作606中，可將表面暴露於表面形貌處理氣體。已發現，抑制處理會導致”粗糙”表面，其會不利地影響沉積2中沉積之膜的品質。表面形貌處理氣體可為鉬前驅物、還原劑(如H2 )、或兩者。
在一些實施例中，重複操作602-606一或更多次。例如，每一操作可被執行為多循環脈衝序列中的一個脈衝。在可替代實施例中，操作602可被執行為多個脈衝循環，而操作604與606之一或兩者僅在完成多個循環時才執行。操作604及606的順序在一些實施例中可顛倒。在一些實施例中，鉬特徵部填充可透過控制前驅物通量來執行，以控制所得填充之階梯覆蓋率。圖6B示出包括較窄且較密特徵部610與較寬且較不密特徵部620之結構的示意性示例，以及可如何透過適當地控制Mo前驅物通量來修改Mo膜635之階梯覆蓋率。(由於通量是每單位面積之流速，因此可透過增加或減少進入腔室之流速來增加或減少通量)。 在相對低之前驅物通量下，階梯覆蓋率低，且與特徵部內部640處相比，有更多的Mo沉積於特徵部之頂部附近及場區域630上。
隨著前驅物通量增加，沉積變得具保形性，有大致相同的Mo量保形地沉積於整個特徵部中。隨著增加前驅物通量所觀察到的階梯覆蓋率增加可能是由於從質傳受限生長轉變成表面反應受限生長。
在又更高之前驅物通量下，在較窄且較密的特徵部610中，生長變得超保形。可如較寬且較不密之特徵部620中所見，觀察到自下而上的生長，其在特徵部620底部顯現Mo膜635，但在此些特徵部之側壁上並無大量沉積。
在一些實施例中，可在Mo特徵部填充期間改變前驅物通量。例如，在Mo填充之第一階段中，可使用保形生長條件，並抑制場區域中的生長。在後續階段中，前驅物通量增加且具超保形及自下而上的生長。可有利地使用多步驟製程來填充變化尺寸的特徵部。圖6C為示出根據諸多實施例用鉬填充結構之操作的製程圖。在圖6C的製程中，Mo的保形層沉積於特徵部中(652)。可使用CVD或ALD。接著，在操作654中，前驅物通量增加，以轉變成自下而上的填充。為了增加前驅物通量，可增加以下一或更多者：Mo前驅物分壓、Mo前驅物流速及Mo前驅物注入時間。可在操作656中完成填充。在一些實施例中，操作656為操作654中條件的延續。在其他實施例中，一旦特徵部被填充到某一點，即可減少前驅物通量。
Mo生長速率對表面處之前驅物通量及前驅物濃度敏感。在一些實施例中，在高前驅物通量條件下觀察到自下而上的生長，其中特徵部內部更深處之前驅物濃度低於場區域及特徵部頂部附近之前驅物濃度。此乃由於較高的前驅物通量比起沉積反應更偏於蝕刻，從而導致較低的生長速率。含氯之Mo前驅物例如會導致沉積及蝕刻反應： MoOx Cly + H2 → Mo(s) + HCl + H2 O  (Mo主體沉積，透過低氯化物) Mo +Cl2 → MoCly (Mo蝕刻) Mo + MoCly → Moz Cly (Mo蝕刻) 若存在底層，如W底層，則可在某些條件下對其進行蝕刻： W +Cl2 → WCly (W蝕刻) W + WCly → Wz Cly (W蝕刻)
以上所給出的反應是高Mo前驅物條件下可能發生之反應示例。圖6D為示出沉積鉬厚度隨鉬前驅物流速變化的圖。圖6D示出使用MoOCl4 之高前驅物通量條件下Mo的淨沉積會如何減少。(圖6D中的數據來自Mo的CVD沉積；然而，使用ALD觀察到相同趨勢。較低與較高環境溫度相差10o C。) 示出三個沉積狀態 : 不良的階梯覆蓋率、保形生長、及自下而上的生長。從圖6D可看出，在高前驅物流速下，淨沉積減少。此可能導致自下而上的填充，其特徵部頂部之前驅物濃度較高(導致較低沉積速率)而特徵部內則較低(導致較高沉積速率)。如上所述，在如圖4及5所示之側向定向特徵部的情況下，自下而上的填充(即，非保形填充)是由內而外的填充，其特徵部是從內向外填充。
該等方法可使用多個裝料容器來實施。圖7中示意性地示出一示例性設備，其中3個氣體源(處理氣體1、處理氣體2及沖洗氣體)連接至裝料容器。在一些實施例中，一或更多氣體源可連接至多個裝料容器。該設備包括氣體歧管系統，其提供管線裝料至諸多氣體分佈管線。歧管透過帶閥裝料容器提供處理氣體及沖洗氣體至沉積腔室。打開或關閉諸多閥以提供管線裝料，亦即以加壓分佈管線。
使用裝料容器可達成輸送處理氣體輸至高深寬比結構的底部，例如，輸送至3D NAND結構之底部字元線。加壓氣體流穿過噴淋頭並到達待處理之晶圓或其他工件。
處理序列的示例包括： 示例1 : 一或更多(NF3 + Ar/沖洗/H2 + Ar)循環，其中+代表氣體同時流入腔室，而” /”代表時間間隔。 示例2 : 一或更多(NH3 + Ar/H2 + Ar)循環 示例3 : 一或更多(NH3 + Ar/Mo前驅物+ H2 + Ar)循環 示例4 : 一或更多(NH3 + Ar/Mo前驅物+ Ar)循環Mo 沉 積
為了以上述方法沉積鉬，可使用含鉬前驅物，其包括六氟化鉬(MoF6 )、五氯化鉬(MoCl5 )、二氯二氧化鉬(MoO2 Cl2 )、四氯氧化鉬(MoOCl4 )及六羰基鉬(Mo(CO)6 )。含Mo前驅物可為鹵化物前驅物，其包括MoF6 與MoCl5 、以及具有可形成穩定分子之兩個或更多鹵素的混合鹵化物前驅物。混合鹵化物前驅物之一示例為MoClx Bry ，其中x及y為可形成穩定分子之大於0的任何數字。有機金屬前驅物包括Mo(X)m (L)n 前驅物，其中每一X為鹵素，其獨立選自由F、Cl、Br及I所組成之群組；每一L為有機配位基，其包括選自由N、O及S所組成之群組的元素，且其中m選自1-4，而n選自1-3，如美國臨時專利申請案第62/816,648號中所揭示。亦可使用有機金屬前驅物，例如矽基環戊二烯基鉬(molybdenum silylcyclopentadienyl)及矽基烯丙基鉬(molybdenum silylallyl)錯合物。Mo 膜之沉積
圖8示出形成Mo膜之ALD方法的示例。根據圖8之方法可用於例如圖3之操作302與306之一或兩者中以及圖6C之任何操作中。首先，在操作805中，脈衝Mo前驅物。在脈衝Mo前驅物之後，可進行可選的沖洗815。可使用氬或任何惰性氣體沖洗腔室中任何未吸附的前驅物。將基板暴露於共反應物825，其可為還原劑以還原Mo前驅物、或其他共反應物以與Mo前驅物反應而形成元素Mo。反應物可為含氫反應物。在一些實施例中，含氫反應物可為熱(非電漿)氫(H2 )。 對於基於電漿的製程，可使用從H2 產生之遠端或原位電漿。可在835執行可選的沖洗，接著重複操作805-835，直到膜完全生長。此可為襯在特徵部上之保形膜，例如保形Mo膜405或505，或是填充所有或一些特徵部之主體層，例如主體Mo 408或508。
在一些實施例中，圖中的操作302包括Mo成核層的沉積，或者作為保形層，或者作為其上沉積主體Mo之保形層的一部分。
在一些實施例中，使用含硼還原劑(如B2 H6 )或含矽還原劑(如，SiH4 )中之一或更多者作為共反應劑來沉積Mo成核層。例如，可採用一或更多S /Mo循環(其中S/Mo係指矽烷脈衝接著是含Mo前驅物脈衝)，以沉積其上沉積主體Mo層之Mo成核層。在另一示例中，可採用一或更多B/Mo循環(其中B/Mo係指乙硼烷脈衝接著是含Mo前驅物脈衝)，以沉積其上沉積主體Mo層之Mo成核層。B/Mo與S/Mo循環兩者皆可用於沉積Mo成核層，例如x(B/Mo) + y(S/Mo)，其中x及y為整數。下文給出含B及S還原劑之示例。為了沉積Mo成核層，在一些實施例中，含Mo前驅物可為不含氧的前驅物，如MoF6 或MoCl5 。含氧前驅物中的氧可與含矽或硼還原劑反應，以形成MoSix Oy 或MoBx Oy ，其為不純之高電阻率膜。含氧前軀物可在氧摻入最少下使用。在一些實施例中，可使用H2 作為還原氣體，以取代含硼或含矽還原氣體。Mo成核層之沉積的示例性厚度範圍為5 Å至30 Å。 此範圍下限的膜可能為不連續；然而，只要其可幫助引發連續主體Mo生長，則該厚度就可能足夠了。在一些實施例中，還原劑脈衝可在比Mo前驅物脈衝更低之基板溫度下施行。例如，可在低於300o C的溫度下執行B2 H6 或SiH4 (或其他含硼或矽還原劑)脈衝，而在大於300o C的溫度下執行Mo脈衝。
保形沉積亦可透過如圖9所示之製程直接在例如介電質及TiN表面的表面上執行。其亦可用於含W的初始表面或Mo成核層上。在操作902中，基板暴露於還原劑氣體以形成還原劑層。在一些實施例中，還原劑氣體可為矽烷、硼烷或矽烷與乙硼烷的混合物。矽烷之示例包括SiH4 及Si2 H6，而硼烷之示例包括乙硼烷(B2 H6 )， 以及Bn Hn+4 、Bn Hn+6 、Bn Hn+8 、Bn Hm ，其中n為1至10之整數，m為不同於n的整數。亦可使用其他含硼化合物，如烷基硼烷、烷基硼、胺硼烷(CH3 )2 NB(CH2 )2 、碳硼烷如C2 Bn Hn+2 。在一些實施方式中，還原劑層可包括能夠還原鎢前驅物之矽或含矽材料、磷或含磷材料、鍺或含鍺材料、硼或含硼材料及其組合。可用於形成此等層之進一步示例性還原劑氣體包括PH3 、SiH2 Cl2 及GeH4 。根據諸多實施例，可在背景中流入或不流入氫。(儘管氫會還原鎢前驅物，但具有足夠量之較強還原劑(例如矽烷及乙硼烷)的氣體混合物中，氫不會作用為還原劑。)
在一些實施例中，還原劑氣體為包含少量含硼氣體(例如乙硼烷)與另一還原劑的混合物。添加少量含硼氣體會極大地影響另一還原劑的分解及黏附係數。應注意，可將基板依序地暴露於兩還原劑，例如矽烷及乙硼烷。然而，流入氣體混合物可助於添加非常少量之少數氣體，如至少100 : 1比例之矽烷與乙硼烷。在一些實施例中，可流入載氣。在一些實施例中，可在操作902期間流入載氣，例如氮(N2 )、氬(Ar)、氦(He)或其他惰性氣體。
在一些實施例中，還原劑層可包括元素矽(Si)、元素硼(B)、元素鍺(Ge)或其混合物。例如，還原劑層可包括Si及B。可調整B量以達成還原劑層之高沉積速率但具低電阻率。在一些實施例中， 還原劑層可具有例如介於5%與80%之間的B，或介於5%與50%之間的B、介於5%與30%之間、或介於5%與20%之間的B，餘量基本上由Si組成，於一些例子中則由H組成。存在氫原子，例如SiHx 、BHy 、GeHz 或其混合物，其中x、y及z可獨立地介於0與小於對應還原劑化合物之化學計量當量的數字之間。
在一些實施例中，可透過還原劑層的厚度而改變組成。例如，還原劑層在還原劑層的底部可為20% B，而在層之頂部為0%B。還原劑層的總厚度可介於在10 Å與50 Å之間，且在一些實施例中介於15 Å至40 Å之間、介於20 Å與30 Å之間。還原劑層保形地對該特徵部形成襯底。
操作902期間之基板溫度可保持於溫度T1，以使膜保形。若溫度太高，則膜可能不符合底層結構之形貌。在一些實施例中，達到大於90%或95%之階梯覆蓋率。對於矽烷、乙硼烷及矽烷/乙硼烷混合物，保形性在300o C時極佳，並在400o C或更高溫度下可能變差。因此，在一些實施例中，操作902期間之溫度最高為350℃、或者甚至最高為325℃、最高為315℃、或者最高為300℃。在一些實施例中，使用小於300℃的溫度。例如，溫度可能低至200℃。
操作902可執行任何合適的持續時間。在一些示例中，示例性持續時間包括介於約0.25秒與大30秒之間、約0.25秒與約20秒之間、約0.25秒與大5秒之間、或約0.5秒與約3秒之間。
在操作904中，可選地沖洗腔室以去除未吸附至基板表面的過量還原劑。可透過在固定壓力下流入惰性氣體來執行沖洗，因此在開始另一氣體暴露之前降低腔室的壓力並重新加壓腔室。示例性惰性氣體包括氮(N2 )、氬(Ar)、氦(He)及其混合物。沖洗可進行介於約0.25秒與約30秒之間、約0.25秒與約20秒之間、約0.25秒與約5秒、或約0.5秒與約3秒之間的持續時間。
在操作906中，在基板溫度T2下將基板暴露於含Mo前驅物。含鉬化合物之示例在上文給出，並包括氯化物及氧氯化物。使用含氧前驅物會導致雜質摻入及較高電阻率。然而，若摻入氧，則可使用非常薄且可能不連續的還原劑層以達可接受的電阻率。在一些實施例中，可在操作906期間流入載氣，例如氮(N2 )、氬(Ar)、氦(He)或其他惰性氣體。溫度的示例為500o C至700o C。
操作906可執行任何合適的持續時間。在一些實施例中，其可能包括含鉬前驅物之浸入，且在一些實施例中包括含鉬前驅物脈衝之序列。根據諸多實施例，於H2 存在下可執行或可不執行操作906。若使用H2 ，在一些實施例中，其與含Mo前驅物可用ALD型方式施加。例如： H2 脈衝 氬沖洗 背景中有或沒有H2 之含Mo前驅物脈衝 氬沖洗 重複
基板溫度T2足夠高，以使含Mo前驅物與還原劑層反應形成元素Mo。整個還原劑層轉化為Mo。在一些實施例中，溫度為至少450℃，且可為至少550℃，以獲得等於或接近100%的轉化率。所得之特徵部現襯有Mo之保形膜。其可介於10Å與50Å之間，且在一些實施例中介於15Å與40Å之間、或20Å與30Å之間。一般而言，其厚度將與還原劑層大約相同。在一些實施例中，由於轉化期間之體積膨脹，其可比還原劑層厚多達5%。
儘管下文描述集中於鉬特徵部填充，但本發明之態樣亦可實施於用其他材料填充特徵部。例如，圖6中所述之處理序列可以使用鎢、鈷或含釕材料之特徵部填充製程來實施。設備
可使用任何適當的腔室來實施所揭示之實施例。示例性沉積設備包括諸多系統，如ALTUS® 及ALTUS® Max (可獲自美國加州佛蒙特之蘭姆研究公司)、或任何多種其他商業可購得之處理系統。
在一些實施例中，第一沉積可在第一站執行，第一站是位於單一沉積腔室內之兩個、五個或甚至更多個沉積站中之一者。因此，例如，在第一站，可使用各別氣體供應系統(其在基板表面處產生局部氛圍)，以交替脈衝將氫(H2 )及二氯二氧化鉬(MoO2 Cl2 )引至半導體基板之表面。另一站可用於處理，而第三及/或第四站用於後續ALD主體填充。
圖10為根據實施例之適合執行沉積製程的製程系統示意圖。系統1000包括轉移模組1003。轉移模組1003提供乾淨且加壓環境，以將被處理基板在諸多反應器模組之間移動時受汙染的風險降至最低。安裝在轉移模組1003上的是多站反應器1109，其能夠根據諸多實施例來執行ALD、處理、及CVD。多站反應器1009可包括多個站1011、1013、1015、及1017，其可根據所揭示之實施例依序地執行操作。例如，多站反應器1009可配置成使得站1011使用含氯之鉬前驅物及含硼或矽還原劑以進行鉬成核層沉積，站1013使用H2 作為還原劑以進行保形層之ALD鉬主體沉積，站1015執行處理操作，而站1017可執行主體ALD填充。
站可包括加熱基座或基板支座、一或更多氣體入口、或噴淋頭、或分配板。沉積站之示例繪於圖7中，如上述。
返回圖10，亦安裝在轉移模組1003上的是一或更多單站或多站模組1007，其能夠執行電漿或化學(非電漿)預清潔、其他沉積操作、或蝕刻操作。該模組亦可用於諸多處理，例如以製備基板用於沉積製程。系統1000亦包括一或更多晶圓源模組1001，其為處理前後儲存晶圓之處。大氣轉移腔室1019中之大氣機器人(未示出)可先將晶圓從源模組1001移至裝載室1021。轉移模組1003中之晶圓轉移裝置(一般為機械手臂單元)將晶圓從裝載室1021移動至安裝在轉移模組903上之模組中並在該等模組之間移動。
在諸多實施例中，採用系統控制器1029來控制沉積期間之製程條件。控制器1029將通常包含一或更多記憶體裝置及一或更多處理器。處理器可包含中央處理單元(CPU)或電腦、類比及/或數位輸入/輸出連接、步進馬達控制器電路板等。
控制器1029可控制沉積設備之所有活動。系統控制器1029執行系統控制軟體，包含用以控制時序、氣體之混合、腔室壓力、腔室溫度、晶圓溫度、射頻(RF)功率位準、基板吸盤或基座位置、及特定製程之其他參數的指令組。儲存於與控制器1029相關聯之記憶體裝置上的其他電腦程式可用於一些實施例中。
通常將存有與控制器1029相關聯之使用者介面。該使用者介面可包含顯示螢幕、設備及/或製程條件之圖形化軟體顯示器、及使用者輸入裝置，例如指向裝置、鍵盤、觸控螢幕、麥克風等。
系統控制邏輯可以任何適合的方式配置。一般而言，邏輯可設計或配置於硬體及/或軟體中。用於控制驅動電路的指令可被硬編碼或被提供作為軟體。該等指令可由「程式設計」提供。此等程式設計被理解為包括任何形式的邏輯，包含在數位訊號處理器、特殊應用積體電路、及其他具有實現為硬體之特定演算法之裝置中的硬編碼邏輯。程式設計亦被理解為包含可在通用處理器上執行的軟體或韌體指令。系統控制軟體可以任何適合的電腦可讀程式設計語言編碼。
在製程序列中控制含鍺還原劑脈衝、氫流量、及含鎢前驅物脈衝、及其他製程的電腦程式碼可以任何習知電腦可讀程式設計語言寫入：例如，組合語言、C、C++、Pascal、Fortran或其他。編譯的目的碼或稿件係由處理器實行，以執行在程式中所識別的任務。亦如所指，程式碼可被硬編碼。
控制器參數涉及製程條件，例如舉例製程氣體組成及流速、溫度、壓力、冷卻氣體壓力、基板溫度、及腔室壁溫度。此些參數係以配方的形式提供至使用者，且可利用使用者介面輸入。
可藉由系統控制器1029之類比及/或數位輸入連接來提供用以監測製程的信號。用以控制製程之信號可在沉積設備1000之類比及數位輸出連接上輸出。
系統軟體可以許多不同方式設計或配置。例如，可寫入諸多腔室構件子程式或控制目標，以控制必須根據所揭示實施例來實行沉積製程之腔室構件的操作。用於此用途之程式或程式片段的示例包括基板定位程式碼、製程氣體控制程式碼、壓力控制程式碼、及加熱器控制程式碼。
在一些實施方式中，控制器1029為系統的一部分，其可為上述示例子的一部分。此等系統可包括半導體處理設備，其包含一處理工具或複數工具、一腔室或複數腔室、一處理平台或複數平台、及/或特定處理構件(晶圓基座、氣流系統等)。該等系統可與電子設備結合，以控制半導體晶圓或基板處理前、處理期間及處理後之操作。此等電子設備可指”控制器”，其可控制該系統或複數系統之諸多構件或次部件。決定於處理需求及/或系統類型之控制器1029可程式化，以控制本文所揭示之任何製程，包括處理氣體之輸送、溫度設定(如加熱及/或冷卻)、壓力設定、真空設定、功率設定、一些系統中之射頻(RF)產生器設定、射頻匹配電路設定、頻率設定、流速設定、流體輸送設定、位置及操作設定、晶圓轉移(進出與特定系統相連接或相接合之工具及其他轉移工具、及/或裝載室)。
廣泛地講，控制器可定義為具有用以接收指令、發佈指令、控制操作、啟動清洗操作、啟動終點量測以及類似者之諸多積體電路、邏輯、記憶體、及/或軟體的電子設備。積體電路可包含：儲存程式指令之韌體形式的晶片、數位訊號處理器(DSP，digital signal processor)、定義為特殊應用積體電路(ASIC，application specific integrated circuit)的晶片、及/或一或更多微處理器、或執行程式指令(例如，軟體)的微控制器。程式指令可為以諸多各別設定(或程式檔案)之形式而傳送至控制器的指令，該各別設定(或程式檔案)為實行(半導體晶圓上，或針對半導體晶圓，或對系統之)特定的製程而定義操作參數。操作參數在一些實施例中可為由製程工程師為了在一或更多以下者的製造期間實現一或更多處理步驟而定義之配方的一部分：層、材料、金屬、氧化物、矽、二氧化矽、表面、電路、及/或晶圓的晶粒。
控制器1029在一些實施例中可為電腦的一部分，或耦接至電腦，該電腦係與系統整合、耦接至系統、以其他網路的方式接至系統、或其組合。舉例而言，控制器1029可在能容許遠端存取晶圓處理之「雲端」或廠房主機電腦系統的全部、或部分中。電腦可使系統能夠遠端存取，以監控製造操作的目前進度、檢查過去製造操作的歷史、自複數的製造操作而檢查其趨勢或效能度量，以改變目前處理的參數、設定目前處理之後的處理步驟、或開始新的製程。在一些示例中，遠端電腦(例如，伺服器)可通過網路而提供製程配方至系統，該網路可包含局域網路或網際網路。遠端電腦可包含能夠進行參數及/或設定輸入或程式設計之使用者介面，接著該參數及/或設定可自遠端電腦傳送至系統。在一些示例中，控制器接收數據形式指令，該指令為即將於一或更多操作期間進行之每一處理步驟指定參數。應當理解，參數可特定針對待執行之製程類型、及控制器與之接合或加以控制之工具類型。因此，如上所述，控制器可為分散式，例如藉由包含以網路方式接在一起、且朝向共同目的(例如，本文所描述之製程及控制)運作之一或更多分離的控制器。用於此目的之分散式控制器舉例為，腔室上與位於遠端的一或更多積體電路(例如，於平臺水平處、或作為遠端電腦的一部分)進行通訊的一或更多積體電路，兩者相結合以控制腔室上的製程。
示例性系統可包含，但不限於，電漿蝕刻腔室或模組、沉積腔室或模組、旋轉清洗腔室或模組、金屬鍍覆腔室或模組、清潔腔室或模組、斜角緣部蝕刻腔室或模組、物理氣相沉積(PVD)腔室或模組、化學氣相沉積(CVD)腔室或模組、原子層沉積(ALD)腔室或模組、原子層蝕刻(ALE)腔室或模組、離子植入腔室或模組、顯影(track)腔室或模組、及可在半導體晶圓的製造及/或加工中相關聯的、或使用的任何其他半導體處理系統。
如上所述，取決於待藉由工具而執行之製程步驟或複數步驟，控制器可與半導體製造工廠中的一或更多以下者進行通訊：其他工具電路或模組、其他工具元件、叢集工具、其他工具介面、鄰近的工具、相鄰的工具、遍及工廠而分布的工具、主電腦、另一控制器、或材料輸送中使用之工具，該材料輸送中使用之工具攜帶晶圓容器往返工具位置及/或裝載埠。
控制器1029可包括諸多程式。基板定位程式可包括用於控制腔室構件的程式代碼，該等腔室構件用於將基板裝載至基座或吸盤上，並控制基板與腔室之其他部件(例如氣體入口及/或目標)之間的間距。製程氣體控制程式可包括用於控制氣體組成、流速、脈衝時間、以及可選地用於在沉積之前使氣體流入腔室以穩定腔室中壓力的代碼。壓力控制程式可包括用於透過調節例如腔室之排出系統中的節流閥來控制腔室中壓力之代碼。加熱器控制程式可包括用於控制流至用於加熱基板之加熱單元之電流的代碼。可替代地，加熱器控制程式可控制熱傳導氣體(例如氦)往晶圓吸盤的輸送。
沉積期間可被監測之腔室感測器的示例包括質量流量控制器、壓力感測計(例如壓力計)、及位於基座或吸盤之熱電偶。經適當程式化之反饋及控制演算法可與來自此些感測器的數據一起使用，以維持所欲製程條件。
上文描述所揭示之實施例於單一或多腔室半導體處理工具中的實施方式。本文所述之設備及製程可結合例如用於半導體裝置、顯示器、LEDs、太陽能板及其類似者之製造或生產的微影圖案化工具或製程來使用。通常，雖然非必要，此等工具/製程將一起使用或實施在普遍的製造設施中。膜之微影圖案化通常包括部份或全部之以下步驟(使用一些可能的工具來執行每一步驟) ： (1)使用旋塗或噴塗工具，將光阻塗佈在工件(即基板)上；(2)使用加熱板或爐或UV硬化工具，硬化光阻；(3)使用如晶圓步進機之工具，將光阻暴露於可見光、或UV光或X射線光；(4)使用如濕式工作台(wet bench)的工具對光阻進行顯影，以選擇性移除阻劑並因而對其圖案化；(5)藉由使用乾式或電漿輔助蝕刻工具，轉移阻劑圖案至底層膜或工件中；及(6)使用如RF或微波電漿阻劑去除機之工具，移除阻劑。 結論
雖然前述實施例基於清楚理解之目的而已描述一些細節，但將顯而易見的是，可在所附請求項之範圍內進行某些改變及修改。應該注意的是，有許多實施本實施例之製程、系統及設備的替代方式。據此，本實施例應視為是說明性而非限制性，且實施例不限於本文所給出的細節。
102:基板 104:介電層 106:擴散阻障層 108:鉬層 201:特徵部 202:基板 204:絕緣層 205:特徵孔 206:保形阻障層 208:鉬埋入式字元線 209:縮部 210:3-D NAND結構 212:縮部 213:底層 215:突部 218:軸線 220:水平特徵部 222:開口 225:VNAND堆疊 226:VNAND堆疊 230:中央垂直結構 240:側壁 250:水平特徵部 251:縮部 255:柱體 260:水平截面 275:孔隙 302:操作 304:操作 306:操作 405:鉬層 406:底層 408:主體鉬 451:柱體縮部 452:部位 465:部位 470:步驟 471:步驟 472:步驟 473:步驟 505:鉬膜 506:底層 508:主體鉬 522:特徵部開口 552:內部 570:步驟 571:步驟 572:步驟 573:步驟 602:操作 604:操作 606:操作 610:較窄且較密特徵部 620:較寬且較不密特徵部 630:場區域 635:鉬膜 640:特徵部內部 652:操作 654:操作 656:操作 800:方法 805:操作 815:操作 825:操作 835:操作 845:操作 902:操作 904:操作 906:操作 908:操作 1000:系統、沉積設備 1001:晶圓源模組 1003:轉移模組 1007:單站或多站模組 1009:多站反應器 1011:站 1013:站 1015:站 1017:站 1019:大氣轉移腔室 1021:裝載室 1029:系統控制器
圖1A及1B為根據諸多實施例包括鉬(Mo)之材料堆疊的示意性示例。
圖2A-2J為根據所揭示實施例可將鉬沉積至其中之諸多結構的示意性示例。
圖3為示出根據諸多實施例用鉬填充結構之操作的流程圖。
圖4示出執行以鉬填充3D NAND結構之製程的示例。
圖5示出執行以鉬填充3D NAND結構之製程的另一示例。
圖6A為示出根據諸多實施例處理鉬膜之操作的製程圖。
圖6B示出包括較窄且較密特徵部以及較寬且較不密特徵部之結構的示意性示例，以及可如何透過控制鉬前驅物通量來改變鉬膜之階梯覆蓋率。
圖6C為示出根據諸多實施例用鉬填充結構之操作的製程圖。
圖6D為示出沉積之鉬厚度隨鉬前驅物流速變化的圖。
圖7為可用於實施本文所述方法之設備的示例。
圖8為示出形成鉬膜之ALD方法中之操作的製程圖。
圖9為示出使用還原劑層形成鉬膜之操作的製程圖。
圖10為可用於實施本文所述方法之設備的示例。
302:操作
304:操作
306:操作

Claims (24)

  1. 一種鉬填充方法，包括： 提供一基板，其包括一或更多特徵部，該一或更多特徵部之每一者具有至少一開口及透過該至少一開口可流體進入之一內部區域； 沉積一第一層鉬於該一或更多特徵部中；以及 非保形地處理該第一層，使得該處理係相對於該第一層之更遠地位於該特徵部之該內部區域中的部位而優先施行於該第一層之位於該一或更多特徵部之該至少一開口附近的部位處，其中處理該第一層係於沉積該第一層鉬期間執行。
  2. 如請求項1所述之鉬填充方法，其中非保形地處理該第一層包括非保形地抑制該第一層。
  3. 如請求項1所述之鉬填充方法，其中非保形地處理該第一層包括非保形地蝕刻該第一層。
  4. 如請求項1所述之鉬填充方法，其中該方法包括係於前驅物通量或濃度較接近該一或更多特徵部之該至少一開口的條件下，將該一或更多特徵部暴露於鉬前驅物。
  5. 如請求項4所述之鉬填充方法，其中該鉬前驅物為氧鹵化鉬。
  6. 如請求項5所述之鉬填充方法，其中該氧鹵化鉬在該一或更多特徵部之該一或更多開口附近因蝕刻反應而具有比在該內部區域中更低的生長速率。
  7. 如請求項5所述之鉬填充方法，其中該氧鹵化鉬在該一或更多特徵部之該一或更多開口附近因抑制處理而具有比在該內部區域中更低的生長速率。
  8. 如請求項2或3所述之鉬填充方法，其中處理該第一層係在沉積該第一層鉬之後執行。
  9. 如請求項8所述之鉬填充方法，其中處理該第一層包括將其暴露於抑制化學物質。
  10. 如請求項9所述之鉬填充方法，其中該抑制化學物質為含氮化學物質。
  11. 如請求項10所述之鉬填充方法，其中處理該第一層包括在將其暴露於含氮化學物質之後，將其暴露於氫氣與鉬前驅物之一或更多者。
  12. 如請求項8所述之鉬填充方法，其中處理該第一層包括將其暴露於蝕刻化學物質。
  13. 如請求項12所述之鉬填充方法，其中該蝕刻化學物質為含鹵素化學物質。
  14. 如請求項13所述之鉬填充方法，其中處理該第一層包括在將其暴露於含鹵素化學物質之後，沖洗容置該基板之一腔室。
  15. 如請求項1-7中任一項所述之鉬填充方法，其中處理該第一層包括將其暴露於含氮化合物。
  16. 如請求項1-7中任一項所述之鉬填充方法，其中處理該第一層包括將其暴露於含鹵素化合物。
  17. 如請求項1-7中任一項所述之鉬填充方法，其中該處理該第一層包括將其暴露於氨或三氟化氮。
  18. 如請求項1-7中任一項所述之鉬填充方法，其中處理該第一層為非電漿的熱製程。
  19. 如請求項1-7中任一項所述之鉬填充方法，其中處理該第一層為電漿製程。
  20. 如請求項1-7中任一項所述之鉬填充方法，其中沉積該第一層鉬包括原子層沉積製程，其係使用H 2作為用於氧鹵化鉬或鹵化鉬前驅物之還原劑。
  21. 如請求項1-7中任一項所述之鉬填充方法，進一步包括：在非保形地處理該第一層之後，進一步包括沉積一第二層鉬。
  22. 如請求項21所述之鉬填充方法，其中沉積該第二層包括原子層沉積製程，其係使用H 2作為用於氧鹵化鉬或鹵化鉬前驅物之還原劑。
  23. 如請求項1-7中任一項所述之鉬填充方法，其中該基板包括具有複數側壁之3-D結構，其中該一或更多特徵部之該一或更多開口為該等側壁中的開口。
  24. 如請求項1-7中任一項所述之鉬填充方法，其中該一或更多特徵部具有一封閉端。
TW109135654A 2019-10-15 2020-10-15 鉬填充 TWI886161B (zh)