TW201937027A - 織物結構 - Google Patents
織物結構 Download PDFInfo
- Publication number
- TW201937027A TW201937027A TW107106048A TW107106048A TW201937027A TW 201937027 A TW201937027 A TW 201937027A TW 107106048 A TW107106048 A TW 107106048A TW 107106048 A TW107106048 A TW 107106048A TW 201937027 A TW201937027 A TW 201937027A
- Authority
- TW
- Taiwan
- Prior art keywords
- yarn
- fiber bundle
- fabric structure
- fiber
- polymer layer
- Prior art date
Abstract
本發明實施例的織物結構包括第一紗線與第二紗線。第一紗線與第二紗線彼此交錯。第一紗線包括第一纖維束。第一纖維束並未被高分子材料包覆。第二紗線包括第二纖維束以及高分子層。高分子層包覆第二纖維束。
Description
本發明是有關於一種織物結構，且特別是有關於一種含有複合纖維的織物結構。
目前對纖維布進行立體定型的方法包括先在纖維布上進行噴膠製程，再高溫去除溶劑後定型。接著，可再以樹脂轉注成型（resin transfer molding，RTM）或熱壓的方法進行立體定型。藉由進行噴膠製程，可優化纖維布的外觀。
然而，噴膠製程中會產生揮發性有機化合物（volatile organic compound，VOC），其對人體與環境均有可能造成危害。此外，膠體與纖維布之間的相容性差，易造成纖維布整體機械強度下降的問題。
本發明提供一種織物結構，可直接地被立體定型，而可省略對其進行噴膠的製程。
本發明的織物結構包括第一紗線以及第二紗線。第一紗線與第二紗線彼此交錯。第一紗線包括第一纖維束。第一纖維束並未被高分子材料包覆。第二紗線包括第二纖維束以及高分子層。高分子層包覆第二纖維束。
在本發明的一些實施例中，第一纖維束與高分子層可暴露於織物結構的表面。
在本發明的一些實施例中，第一纖維束與第二纖維束可分別包括聚對苯二甲酸乙二酯纖維、尼龍纖維、熱塑性聚酯彈性體纖維、碳纖維、玻璃纖維或其組合。
在本發明的一些實施例中，高分子層的材料可包括熱塑性高分子。
在本發明的一些實施例中，高分子層的材料可包括聚胺酯、聚丙烯、聚乙烯、聚醯胺、酚氧樹脂、苯氧基樹脂、苯氧基樹脂、環氧樹脂或其組合。
在本發明的一些實施例中，第一纖維束的丹尼數（Denier）與第二纖維束的丹尼數的範圍可分別為75 D至7200 D。
在本發明的一些實施例中，第二纖維束的體積對於高分子層的體積的比值範圍可為0.3至3。
在本發明的一些實施例中，第一紗線的體積對於第二紗線的體積的比值範圍可為0.25至9。
在本發明的一些實施例中，織物結構可具有彼此相連的平坦部以及立體部。立體部相對於所述平坦部凸出或下凹。
基於上述，本發明實施例的織物結構包括第一紗線與第二紗線。第一紗線包括未被高分子層包覆的第一纖維束，且第二紗線包括被高分子層包覆的第二纖維束。因此，第一紗線與第二紗線可具有不同的彎曲剛性，且可具有不同的觸感以及外觀。如此一來，可簡單地藉由調整織物結構中第一紗線與第二紗線的比例而調整織物結構的彎曲剛性、外觀以及觸感。據此，本發明實施例的織物結構可為一種可直接進行立體定型的織物結構。換言之，可直接地對本發明實施例的織物結構進行立體定型，而省略對其進行噴膠的製程。因此，可避免在噴膠製程中產生具有毒性的揮發性氣體，且可避免膠體與紗線的相容性差而降低織物結構的機械強度。
為讓本發明的上述特徵和優點能更明顯易懂，下文特舉實施例，並配合所附圖式作詳細說明如下。
圖1是依照本發明一些實施例的織物結構10的立體示意圖。圖2是依照本發明一些實施例的第二纖維120的放大示意圖。
請參照圖1，本發明實施例的織物結構10包括彼此交錯的多條第一紗線110與多條第二紗線120。在一些實施例中，可利用梭織、針織、平織等方法使第一紗線110與第二紗線120彼此交錯。換言之，可依據織物結構10的不同編織方法，而使得第一紗線110與第二紗線120具有不同的交錯圖案，本發明並不以此為限。
第一紗線110包括條第一纖維束112。第一纖維束112可包括多條單絲纖維。在一些實施例中，第一纖維束112可包括聚對苯二甲酸乙二酯（polyethylene terephthalate，PET）纖維、尼龍纖維、熱塑性聚酯彈性體（thermoplastic polyester elastomer，TPEE）纖維、碳纖維、玻璃纖維或其組合。然而，所屬領域中具有通常知識者可依據產品設計而選用其他的纖維材料製造第一纖維束112，本發明並不以此為限。在一些實施例中，第一紗線110的第一纖維束112並未被高分子材料包覆。換言之，第一纖維束112可暴露於織物結構10的表面。此外，第一纖維束112可為圓紗或扁紗。換言之，第一纖維束112的橫截面可為實質上為圓形、橢圓形或矩形。在一些實施例中，第一纖維束112的丹尼數（Denier）範圍為75 D至7200 D。
請參照圖1與圖2，第二紗線120包括第二纖維束122以及高分子層124。高分子層124包覆第二纖維束122。在一些實施例中，可藉由例如是熔融押出的方式將高分子層124形成於第二纖維束122的表面。此外，在將高分子層124形成於第二纖維束122的表面之前，可先對第二纖維束122進行熱處理及/或表面改質，以提高第二纖維束122與高分子層124之間的附著性。
在一些實施例中，第二纖維束122可包括聚對苯二甲酸乙二酯纖維、尼龍纖維、熱塑性聚酯彈性體纖維、碳纖維、玻璃纖維或其組合。然而，所屬領域中具有通常知識者可依據產品設計而選用其他的纖維材料製造第二纖維束122，本發明並不以此為限。在一些實施例中，第一纖維束112與第二纖維束122可由相同的纖維材料構成。在其他實施例中，第一纖維束112與第二纖維束122也可由不同的纖維材料構成。此外，第二纖維束122可為圓紗或扁紗。換言之，第二纖維束122的橫截面可為實質上為圓形、橢圓形或矩形。在一些實施例中，第二纖維束122的丹尼數（Denier）範圍為75 D至7200 D。第二纖維束122的丹尼數可等同於第一纖維束112的丹尼數，也可相異於第一纖維束112的丹尼數。
在一些實施例中，高分子層124的材料可包括（但不限於）熱塑性高分子。舉例而言，高分子層124的材料可包括聚胺酯、聚丙烯、聚乙烯、聚醯胺、酚氧樹脂、苯氧基樹脂、環氧樹脂或其組合。第二纖維束122被高分子層124包覆，且一些實施例的第一纖維束112並未被高分子材料包覆。因此，高分子層124與第一纖維束112可同時暴露於織物結構10的表面。請參照圖1所繪示的第二纖維120的放大剖面圖，在一些實施例中，高分子層124的厚度T的範圍可為0.1 mm至1 mm。
第二纖維束122的體積對於高分子層124的體積的比值越大，則第二紗線120的彎曲剛性越高。相對地，第二纖維束122的體積對於高分子層124的體積的比值越小，則第二紗線120的柔性越高（亦即彎曲剛性越小）。在一些實施例中，第二纖維束122的體積對於高分子層124的體積的比值範圍可為0.3至3。所屬領域中具有通常知識者可依據產品設計而調整第二纖維束122的體積對於高分子層124的體積的比值，本發明並不以此為限。
由於第二紗線120的彎曲剛性可相異於第一紗線110的彎曲剛性，故可藉由調整織物結構10中第一紗線110與第二紗線120的體積含量，以調整織物結構10的彎曲剛性。此外，也可藉由調整織物結構10中第一紗線110與第二紗線120的體積含量或第一紗線110與第二紗線120的編織方式，來調整織物結構10的外觀與觸感。在一些實施例中，第一紗線110的體積對於所述第二紗線120的體積的比值範圍為0.25至9。
由於可簡單地藉由調整第一紗線110與第二紗線120的比例或編織方式而調整織物結構10的彎曲剛性與外觀，故織物結構10可經形成為一種可直接進行立體定型的織物結構。換言之，可直接地對織物結構10進行立體定型，而省略對其進行噴膠的製程。如此一來，可避免在噴膠製程中產生具有毒性的揮發性氣體，且可避免膠體與紗線的相容性差而降低織物結構的機械強度。
圖3是依照本發明一些實施例的織物結構10a的平面部P1與立體部P2的影像。圖3的織物結構10a為圖1的織物結構10經立體定型後的影像。
請參照圖3，經立體定型的織物結構10a可包括平坦部P1與立體部P2，且平坦部P1與立體部P2為織物結構10a彼此相連。此外，立體部P2相對於平坦部P1凸出或下凹。在一些實施例中，可利用例如是樹脂轉注成型（resin transfer molding，RTM）或熱壓的方法進行立體定型。然而，所屬領域中具有通常知識者亦可選用其他立體定型的方法，本發明並不以此為限。
綜上所述，本發明實施例的織物結構包括第一紗線與第二紗線。第一紗線包括未被高分子層包覆的第一纖維束，且第二紗線包括被高分子層包覆的第二纖維束。因此，第一紗線與第二紗線可具有不同的彎曲剛性，且可具有不同的觸感以及外觀。如此一來，可簡單地藉由調整織物結構中第一紗線與第二紗線的比例或編織方式而調整織物結構的彎曲剛性、外觀以及觸感。據此，本發明實施例的織物結構可為一種可直接進行立體定型的織物結構。換言之，可直接地對本發明實施例的織物結構進行立體定型，而省略對其進行噴膠的製程。因此，可避免在噴膠製程中產生具有毒性的揮發性氣體，且可避免膠體與紗線的相容性差而降低織物結構的機械強度。
雖然本發明已以實施例揭露如上，然其並非用以限定本發明，任何所屬技術領域中具有通常知識者，在不脫離本發明的精神和範圍內，當可作些許的更動與潤飾，故本發明的保護範圍當視後附的申請專利範圍所界定者為準。
10、10a‧‧‧織物結構
110‧‧‧第一紗線
112‧‧‧第一纖維束
120‧‧‧第二紗線
122‧‧‧第二纖維束
124‧‧‧高分子層
P1‧‧‧平坦部
P2‧‧‧立體部
T‧‧‧厚度
圖1是依照本發明一些實施例的織物結構的立體示意圖。 圖2是依照本發明一些實施例的第二纖維的放大示意圖。 圖3是依照本發明一些實施例的織物結構的平面部與立體部的影像。
Claims (9)
- 一種織物結構，包括： 第一紗線，包括第一纖維束，其中所述第一纖維束並未被高分子材料包覆；以及 第二紗線，其中所述第一紗線與所述第二紗線彼此交錯，所述第二紗線包括第二纖維束以及高分子層，所述高分子層包覆所述第二纖維束。
- 如申請專利範圍第1項所述的織物結構，其中所述第一纖維束與所述高分子層暴露於所述織物結構的表面。
- 如申請專利範圍第1項所述的織物結構，其中所述第一纖維束與所述第二纖維束分別包括聚對苯二甲酸乙二酯纖維、尼龍纖維、熱塑性聚酯彈性體纖維、碳纖維、玻璃纖維或其組合。
- 如申請專利範圍第1項所述的織物結構，其中所述高分子層的材料包括熱塑性高分子。
- 如申請專利範圍第1項所述的織物結構，其中所述高分子層的材料包括聚胺酯、聚丙烯、聚乙烯、聚醯胺、酚氧樹脂、苯氧基樹脂、環氧樹脂或其組合。
- 如申請專利範圍第1項所述的織物結構，其中所述第一纖維束的丹尼數與所述第二纖維束的丹尼數範圍分別為75 D至7200 D。
- 如申請專利範圍第1項所述的織物結構，其中所述第二纖維束的體積對於所述高分子層的體積的比值範圍為0.3至3。
- 如申請專利範圍第1項所述的織物結構，其中所述第一紗線的體積對於所述第二紗線的體積的比值範圍為0.25至9。
- 如申請專利範圍第1項所述的織物結構，其中所述織物結構具有彼此相連的平坦部以及立體部，所述立體部相對於所述平坦部凸出或下凹。