TH10100C3 - Sheet material containing rice husk ash and manufacturing process - Google Patents

Abstract

DC60 (09/02/58) Sheet material containing rice husk ash powder. And manufacturing processes for sheet materials It contains rice husk ash powder mixed with Portland cement, fine sand and water and then extruded with a mold. According to the required format Cured until maturity The product has a dark texture on its own without the need for Fill or put on synthetic paint. It can be used as a product that has to bear loads, such as roof tiles, floor tiles, or masonry bricks, etc. Edit Conclusion 16/02/15 (9/02/2015) Material sheets containing rice husk ash And manufacturing processes for sheet materials It contains rice husk ash powder mixed with Portland cement, fine sand and water and then extruded with a mold. According to the required format Cured until maturity The product has a dark texture on its own without the need for Fill or put on synthetic paint. It can be used as a product that requires loads such as roof tiles, floor tiles, or masonry bricks, etc. --------------------------- ---------------------------------- Sheet material containing rice husk ash powder And manufacturing processes for sheet materials It contains rice husk ash powder mixed with Portland cement, fine sand and water and then extruded with a mold. According to the required format Cured until maturity The product has a dark texture on its own without the need for Fill or put on synthetic paint. It can be used as a product that is subject to loads such as roof tiles, floor tiles, or masonry bricks

Claims (2)

Disclaimer (all) which will not appear on the advertisement page: Edit 16/02/15 (9/02/2015) 1 sheet Material containing rice husk ash The following components are as follows: a. 80 percent fine sand by weight of dry mixture b. 14-19 percent portland cement by weight of dry mix plant. 16-25% water by weight of all dry ingredients 2. Production process for sheet materials containing rice husk ash According to claim 1, the steps are as follows: a. Sift rice husk ash by using a No. 35 sieve to eliminate the mixed material. After that, dry grinding for a period of 1.5-3 hours and rice husk ash powder can be sifted through a standard No. 325 sieve. B. Sifted sand through a standard No. 35 c sieve mixed with fine sand. Portland cement And rice husk ash powder, ground together for 10-30 minutes. D. Add water to the mixture, mix together, take 1-5 minutes. E. The mixture is pressed into a mold. E. Leave the mixture to harden for a time. 12-24 hours at room temperature f. Curing under 90-100% relative humidity for 7-14 days ------------------------- --------------------------------- 1 sheet material containing rice husk ash The following components are as follows: a. 80 percent fine sand by weight of dry mixture b. 14-19 percent portland cement by weight of dry mix plant. 16-25% water by weight of all dry ingredients 2. Production process for sheet materials containing rice husk ash According to claim 1, the steps are as follows: a. Sift rice husk ash by using a No. 35 sieve to eliminate the mixed material. After that, dry grinding for a period of 1.5-3 hours and rice husk ash powder can be sifted through a standard No. 325 sieve. B. Sifted sand through a standard No. 35 c sieve mixed with fine sand. Portland cement And rice husk ash powder, finely mashed for 10-30 minutes. D. Add water to the mixture, mix it for 1-5 minutes. -100% for 7-14 days