SU827436A1 - Binder - Google Patents
Binder Download PDFInfo
- Publication number
- SU827436A1 SU827436A1 SU792782191A SU2782191A SU827436A1 SU 827436 A1 SU827436 A1 SU 827436A1 SU 792782191 A SU792782191 A SU 792782191A SU 2782191 A SU2782191 A SU 2782191A SU 827436 A1 SU827436 A1 SU 827436A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- binder
- strength
- composition
- weight
- waste
- Prior art date
Description
Т а б л II ц аT a b l II c a
жущсго и стандартного вельского песка, в соотношени х 1 :3, изготовл ют призмы размерами 4X4X16 мм, при В/В - 0,5. После 28-суточного влажного хранени определ ют прочностные характеристики в жущего (табл. 2).Standard and white sand, in ratios 1: 3, made prisms with dimensions 4x4x16 mm, with B / B - 0.5. After a 28-day wet storage, the strength characteristics of the binder are determined (Table 2).
Таблица 2table 2
Прочность, через Strength through
Состав в жущего, % 28 сут. кгс/смComposition on the go,% 28 days. kgf / cm
В отличие от состава известного в жущего , которое включает дорогосто щий аглопорит , состав по изобретению содержит отходы хлоралюминиевого производства, что удещевл ет стоимость в жуи1его. Активность известного в жущего определ ют на образцах, приготовленных методом прессовани под нагрузкой 150 кг/см, тогдаUnlike the composition of the known agent, which includes expensive agloporite, the composition according to the invention contains chlorine-aluminum production wastes, which makes it cheaper to chew. The activity of the known host is determined on samples prepared by compression under a load of 150 kg / cm, then
как активность в жущего по изобретению онредел ют в образцах, изготовленных ручным уплотнением - подстукиванием. Несмотр на это, прочностные характеристики образцов, изготовленных на основе в жущего , но изобретению всегда больще, чем у соответствующего состава известного в жущего. Кроме того, удельна поверхность известного в жущего на 700-900 емЯг больн1е, чех: в жущего по изобретению . Отходы хлоралюминиевого производства не требует специального обжига и дроблени . Таким образом, применение в составе в жущего отходов хлоралюминиевого производства снижает расход электроэнергии , топлива и себеетоимость конечного продукта, при этом в жущее по изобретению имеет на 27,5% и на 16% выще прочность при сжатии и при изгибе, соответственно , по сравнению с прочностными характеристиками известного в жу;цего.as an activity in the inventive according to the invention, they are determined in samples made by manual compaction - by tapping. Despite this, the strength characteristics of the samples made on the base of a ghost, but the invention is always greater than that of the corresponding composition of a grounded pattern. In addition, the specific surface area of the known patient is 700-900 mm of the patient, Czech: the holder of the invention. Waste chloroaluminium production does not require special firing and crushing. Thus, the use of chlorine-aluminum production in the composition of waste materials reduces the consumption of electricity, fuel and the final product, while the substance of the invention has 27.5% and 16% higher compression and bending strength, respectively strength characteristics known in zhu; tsego.
Ф о р м у л а и 3 о б р е т е н и FORUMUA AND 3 ABOUT AND
В жущее, включающее портландцемен: 15-29 вес. % и тонкомолотый алюмосиликатный наполнитель 71-85 вес. %, отличающеес тем, что, с целью повыщени прочности и удешевлени в жущего, оноIncluding, including Portland cement: 15-29 wt. % and fine ground aluminosilicate filler 71-85 weight. %, characterized in that, in order to increase strength and reduce the cost of chewing, it
содержит в качестве тоикомолотого алюмосиликатного наполнител , криетобаллитомуллитовые отходы хлоралюмпниевого производства.It contains as a ground aluminosilicate filler, cryoallium thallium chlorite alumina production waste.
Источники информации,Information sources,
прин тые во внимание при экспертизеtaken into account in the examination
1. Юнг В. Н. и др. Технологи в жущих веществ. Госстройиздат. М., 1952, с. 402- 406.1. Jung, V.N., et al. Technologists in Surfactants. Gosstroyizdat. M., 1952, p. 402-406.
2. Авторское свидетельство СССР № 647275, С 04 В 7/12, 1977.2. USSR author's certificate No. 647275, C 04 B 7/12, 1977.
Claims (1)