SU1531860A3 - Elastoplastic composition - Google Patents

Elastoplastic composition Download PDF

Info

Publication number
SU1531860A3
SU1531860A3 SU782684153A SU2684153A SU1531860A3 SU 1531860 A3 SU1531860 A3 SU 1531860A3 SU 782684153 A SU782684153 A SU 782684153A SU 2684153 A SU2684153 A SU 2684153A SU 1531860 A3 SU1531860 A3 SU 1531860A3
Authority
SU
USSR - Soviet Union
Prior art keywords
ethylene
weight
oil
parts
relative
Prior art date
Application number
SU782684153A
Other languages
Russian (ru)
Inventor
Альберт Фас Майкл
Эбдоу Сэбет Сэбет
Original Assignee
Монсанто Компани (Фирма)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=25306493&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=SU1531860(A3) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Монсанто Компани (Фирма) filed Critical Монсанто Компани (Фирма)
Application granted granted Critical
Publication of SU1531860A3 publication Critical patent/SU1531860A3/en

Abstract

Thermoplastic elastomeric compositions exhibiting improved compression set and oil resistance comprise blends of olefin rubber and crystalline polyolefin resin in which the rubber is cured with phenolic curative.

Description

Изобретение относитс  к резиновой промьвпленности, в частности к злас- топластичному составу, из которюго могут быть изготовлены шины, рукава, и шланги, ремни, уплотнени  и прокладки , пресс-издели .The invention relates to rubber production, in particular to a plastic-plastic composition, from which tires, sleeves, and hoses, belts, seals and gaskets, and a press product can be made.

Цель изобретени  - уменьшение остаточного сжати  и повьшгение масло- стойкости резин.The purpose of the invention is to reduce the residual pressure and reduce the oil resistance of the rubber.

Маточную смесь, содержащую ТЭПК (тройной этилен- проп иле новый каучук) , парафиновое масло дл  наполненн ,,- газовую сажу, окись иинка, стеариновую кислоту и противостаритель, в указанных количественных соотношени х (мас.ч.), смешивают с полипропиленом в смесителе Брабендера при 80 об/минThe masterbatch containing TEPK (ternary ethylene-prop silt new rubber), paraffin oil filled with carbon black, oxide of ika, stearic acid and antioxidant, in the indicated proportions (parts by weight), are mixed with polypropylene in the mixer Brabender at 80 rpm

при температуре масл ной баии в течение 2,5 мин, после чего полипропилен плавитс  с получением однородной смеси. Под температурой смесител  Брабендера следует понимать температуру масл ной бани. После этого добавл ют фенольный вулканизатор, продолжа  перемешивать еще 4 мин; за зто врем  достигают максимальной консистенции по Брабендеру. Состав удал ют , испытуемые образцы подвергают пр мому прессованию при . Затем их охлаждают до температуры ниже под давлением перед выгрузкой. Свойства отформованного листового материала замер ют и регистрируют.at an oil baih temperature for 2.5 minutes, after which the polypropylene melts to form a homogeneous mixture. The temperature of the Brabender mixer means the temperature of the oil bath. After that, the phenolic vulcanizer is added, continuing to mix for another 4 minutes; During this time, the maximum consistency according to Brabender is reached. The composition is removed, the test specimens are directly compressed at. They are then cooled to a temperature below the pressure before unloading. The properties of the formed sheet material are measured and recorded.

сдsd

:о:about

эо eo

о about

Изобретение иллюстрируют примеры, представленные в табл. 1-5.The invention is illustrated by the examples presented in table. 1-5.

Остаточное сжатие определ ют в соответствии с А5ТМД-395, метод В - путем сжати  образца в течение 22 ч при 100 С. Маслонабухание (изменение в % по весу) определ ют в соответствии с ASTKn- i71 погружением образца на 3 дн  при 121°С в масло по STMResidual compression is determined in accordance with A5TMD-395, method B — by compressing the sample for 22 hours at 100 C. Oil masking (change in% by weight) is determined in accordance with ASTKn-i71 by immersing the sample for 3 days at 121 ° C in oil on STM

Nr.3. Механическую прочность определ ют по AS Tit Д 638 и AS П- Д 1566.Nr.3. Mechanical strength is determined by AS Tit D 638 and AS P-D 1566.

Claims (2)

Формула изобретени  Invention Formula I. Эластопластичньй состав, включающий тройной сополимер из 55- 69 мас.% этилена, 22,7-40,6 мас.% пропилена и 3,7-8,3 wac.Z зтилнцбн- норборнена, политфопилен, вулканизую- щий агент и активатор вулканизации, отличающийс  тем, что, с целью уменьшени  остаточного сжати  и пойышени  маслостойкости резин из данного состава, в качестве вулка низующего агента состав содержит бро мированную метилолЛенольную смолу р сочетании с окисью цинка в качестве активатора вулканизации или диметилол-п-октил-фенольную смолу в сочетании с окисью цинка в качестве активатора вулканизации и хлоридом олова или хлорсульфированным полиэтиленом при следующем соотношении компонентов , мае.ч. :I. The elastoplastic composition, comprising a ternary copolymer of 55- 69% by weight of ethylene, 22.7-40.6% by weight of propylene, and 3.7-8.3 wac.Z ztilyntsbn-norbornene, polytropylene, vulcanizing agent and vulcanization activator, characterized in that, in order to reduce the residual compression and increase the oil resistance of the rubber of this composition, the composition contains a brothed methylol Lenol resin p combined with zinc oxide as a vulcanization activator or dimethylol p-octyl phenol resin in combination with zinc oxide as an activate and curing and tin chloride or chlorosulfonated polyethylene with the following ratio of components, mae.ch. : Тройной сополимеTerpoly copolyme ПолипропиленPolypropylene Бронированна  метилолфенольйа Armored methylolphenol смолаresin Окись цршкаTsrshka oxide или диметилол-поктил-фенольна or dimethylol-poctyl-phenol смолаresin Окись цинкаZinc oxide Хлорид олова илиTin chloride or диметилол-п-октрЛенольиа  смолаdimethylol-p-octaneLolenia resin Окись ц1-ЕнкаOxide ts1-Enka Хлорсульфированный полиэтиленChlorosulfonated polyethylene 2. Состав по п . I, отличаю- щ и и с   тем, что он дополнительно содержит 28,9-36,4 мае.ч. парафинового масла и 18,66-36,4 мае.ч. газовой сажи.2. The composition according to claim. I, differing from the fact that it additionally contains 28.9-36.4 mph. paraffin oil and 18.66-36.4 ma.ch. gas soot. у име-, ,2,4 мети- зую I had, 2,4 metizu 6464 30,630.6 28,828,8 1,81.8 0,360.36 6464 30,730.7 28,828,8 1,81.8 0,360.36 0,72 0,720.72 0.72 43 8643 86 3,243.24 4747 : 15: 15 Таблица 1Table 1 77 8eight 66 6464 30,630.6 28,828,8 1,8 0,361.8 0.36 6464 30,630.6 28,828,8 1,81.8 0,360.36 6464 30,630.6 28,828,8 1,81.8 0,360.36 6464 30,630.6 28,828,8 1,81.8 0,360.36 0,720.72 1,311.31 4747 101101 35 7035 70 3,243.24 I U I u 1,31 391.31 39 8787 Предел прочности при раст жении , кг/см ПО 176 190 78 179 Относительное удлиненне приStrength at stretching, kg / cm PO 176 190 78 179 Relative elongation at разрьте, 7.А60 390 490 460 300tear, 7.A60 390 490 460 300 Маслонабухание, %131 67 88 68 53Oil swelling% 131 67 88 68 53 ASTM No.3 Остаточное сжатие, % - - - 68 36ASTM No.3 Residual Compression,% - - - 68 36 73 мас.% этилена: 4,4 .мае.% этилиден-норборнена;. полидиспериосТь 2,1;73% by weight of ethylene: 4.4.% Ee. Of ethylidene-norbornene; polydisperis 2.1; оти.пл. 0,86; в зкость по Муни (ML+1 аГС) Г 55 мас.% этилена; 4,4 мас.% этилццен-норборнена; полидисперность 5,2;from.pl. 0.86; Mooney viscosity (ML + 1 AGS) D 55 wt.% ethylene; 4.4 wt.% Ethylcene-norbornene; polydispersity 5,2; отн.пл. 0,86; в зкость по Муни 40 (ML 1+8; )relative pl. 0.86; Mooney viscosity 40 (ML 1 + 8;) 17,2 ч. серы; 10,3 ч. диметилдитиокарбамата цинка; 10,3 ч. тетраэтип- тиурамдисульфнда; 34,5 ч. 2-бис(бензоТиазолил)дису ьфвда и 27,7 ч. ди- пентаметилентиурамгексасульфида.17.2 parts of sulfur; 10.3 parts zinc dimethyldithiocarbamate; 10.3 parts of tetraethyl thiuram disulfund; 34.5 parts of 2-bis (benzoTiazolyl) disulfide and 27.7 parts of dipentamethyleniuramhexasulfide. Продолжение т«вл. IContinuation of t "vl. I 139139 390 75390 75 5252 Смесь КомпонентыMixture Components Предлагаема  Известна Proposed Known ..... .% каучука, раствор ющегос  в циклогексане при комнатной температуре (неисправление дл  ачетоно- растворимой части каучука) 80ОО1,7......% of rubber dissolved in cyclohexane at room temperature (non-correction for the acid-soluble part of rubber) 80OO1.7 Таблица 3Table 3 СмесьMixture Компоненты1утvГComponents1OUT Предлагаема  Нэвйст- Предла- Мзиест- Предла- 1 -: вест- на  гаема  нам гаема  нлнOffered by Nevist-Predla- Mziyest- Proposed- 1 -: West Germany 112 Э It 5 6 7112 O It 5 6 7 ТЭПК, наполненный масл Полипропилен Несло дл  наполнени  Газова  сажа П|)отивостаритель Окись цинка Стеаринова  кислотаTEC, filled with oil Polypropylene Carried for filling of Gas soot II |) oxidizing agent Zinc oxide Stearic acid sp-ipsbsp-ipsb Серный вулканизатор Твердость по Шору А Модуль (100%), кг/см Нодуль (300Z), tr/cr-, Предел прочности при рнии , кг/смSulfuric Vulcanizer Shore A hardness Module (100%), kg / cm Nodul (300Z), tr / cr-, Tensile strength, gusset / kg Относительное удлинени разрыве, ZRelative break elongation, Z Остаточное удлинение, Остаточное сжатие, % Набухание в насле, % А8ТИ Nr.3Residual Elongation, Residual Compression,% Swelling in Nas,% A8TI Nr.3 63 мас,% этилена; 3,7 мас.% этилиден-иорьорнена; nojui/incnepisocrb 2,6; относительна  плотность 0,90; в зкость по f yun (ML-4, 25°С) 50; rpoihioH сополимер, наполненный нержАвекгщим нефт ным маспом (50:50 по массе) Полипропилен и вулканизаторы те же, что и в т бл. I.63 wt.% Ethylene; 3.7 wt.% Ethylidene-yorornene; nojui / incnepisocrb 2.6; relative density 0.90; f yun viscosity (ML-4, 25 ° C) 50; rpoihioH copolymer filled with stainless oil masp (50:50 by weight) Polypropylene and vulcanizers are the same as in bl. I. Полинеризованный 1 , 2-дигидро-2 ,2,4-триметилхинолин .«Polynerised 1, 2-dihydro-2, 2,4-trimethylquinoline. " Продолжение табл. 2Continued table. 2 9, 2 54,49, 2 54.4 36,4 0,91 2,33 0,4636.4 0.91 2.33 0.46 ,65 В4 45 87, 65 V4 45 87 . «О. "ABOUT 550 14 47 550 14 47 100,6100.6 49.749.7 28,928.9 28,928.9 0,960.96 2,412.41 0,490.49 4,44.4 82 46 10182 46 101 134134 390 12 28 52390 12 28 52 100,6100.6 49,749.7 28, q 28,9 0,96 2,41 0,4928, q 28.9 0.96 2.41 0.49 1 ,82 8) 44 861, 82 8) 44 86 150150 560 1 I 49 84560 1 I 49 84 124,4 37,8 31,1 18,66124.4 37.8 31.1 18.66 1,16 0,62 6,841.16 0.62 6.84 71 3471 34 9191 290 6290 6 20 5920 59 124,4 37,8 31,1 18,66124.4 37.8 31.1 18.66 3,11 0,623.11 0.62 2,252.25 71 29 6071 29 60 6969 350 17350 17 34 9134 91 69 мас.% этилена; 8,3 мас.% этилиден-норборнена; полидисперсность 2,1; отн.пл. 0,86; в зкость по Муни 50 (ML-8, 100°С).69% by weight ethylene; 8.3 wt.% Ethylidene-norbornene; polydispersity 2.1; relative pl. 0.86; Mooney viscosity 50 (ML-8, 100 ° C). см. табл. 1. Диметилол-п-октил-фенол (не галоидироваиный). see tab. 1. Dimethylol-p-octyl-phenol (not halogenated).
SU782684153A 1977-11-09 1978-11-04 Elastoplastic composition SU1531860A3 (en)