SU1021586A1 - Metallic binding for making diamond tool - Google Patents
Metallic binding for making diamond tool Download PDFInfo
- Publication number
- SU1021586A1 SU1021586A1 SU823390055A SU3390055A SU1021586A1 SU 1021586 A1 SU1021586 A1 SU 1021586A1 SU 823390055 A SU823390055 A SU 823390055A SU 3390055 A SU3390055 A SU 3390055A SU 1021586 A1 SU1021586 A1 SU 1021586A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- copper
- granite
- tin
- cobalt
- carbide
- Prior art date
Abstract
1. МЕТАЛЛИЧЕСКАЯ СВЯЗКА ДЛЯ ИЗГОТОВЛЕНИЯ АЛМАЗНОГО ИНСТРУМЕНТА , содержаща кобальт, карбид хрома, медь и олово, отличающ а с тем, что, с целью повышени стойкости инструмента при об работке гранита, компоненты св зки вз ты в следующем соотношении, вес.%: Карбид хрома 10-18 Медь7-9 Олово1-1 5 КобальтОстальное 2. Св зка по п. 1, отличающа с тем, что, с целью повьвиени прочности л пластичности инструмента при обработке гранита с высоким, содержанием кварца, она дополннтельно содержит железо и никель при следующем соотношении компонентов , вес.%: . Карбид хрома 10-18 Медь- 7-9 Олово1-1,5 . Железо4-5 Никель5-6 Кобальт : Остальное1. METAL BOND FOR MANUFACTURING DIAMOND TOOLS containing cobalt, chromium carbide, copper and tin, differing from the fact that, in order to increase tool life during the processing of granite, the binder components are taken in the following ratio, wt.%: Carbide chromium 10–18 Copper 7–9 Tin 1–1 5 Cobalt Else 2. Linkage according to claim 1, characterized in that, in order to improve the strength and plasticity of the instrument, when processing granite with a high quartz content, it additionally contains iron and nickel at the following ratio of components, ve .%:. Chromium carbide 10-18 Copper- 7-9 Tin 1-1.5. Iron4-5 Nickel5-6 Cobalt: Else
Description
елate
00 А Изобретение относитс к области изготовлени алмазных инструментов в частности к составам св зки дл изготовлени алмазных отрезных кру гов дл резки гранитов. Известна металлическа св зка д изготовлени алмазного инструмента со следующим соотношением компонен тов, вес.%: СГдС,5-90 Си3-70 Fe(Co,Ni)2-30 Sn(2n,Cd,Al,PbJ 2-30 Известна св зка с высоким соде жанием (40-90%) примен етс в инструменте дл резки малопрочных и высокоабразивных пород, например гипса, мрамора, известн ка; песчаника и т.п. Г1 J. Однако при резке гранитов инструмент , изготовленный на этой св з быстро засаливаетс при высоком со держании (40-90%) и быстро и нашиваетс при низком содержании (5-40%). Это объ сн етс тем что прочность св зки недостаточно высока и удержание зерен алмазов в ней слабое, поскольку основу св ки составл ют пластичные металлы (Cu,Zn,Sn,Pb,Cd), не смачивающие алмаз. цель изобретени - создание ме;таллической св зки дл алмазного инструмента, обеспечивающей высокую его стойкость при обработке гранита а также повышает прсэчность и пластичность инструмента при обработке гранита с высоким содержанием квар ца. Поставленна цель достигаетс .те что компоненты св зки, содержащей кобальт, карбид хрома, медь, и олово вз ты в следующих вес.%: Сг,С-..10-18 Си7-9 Sn .1-1,5 СоОстальное При обработке инструментом гранита с высоким содержанием кварца она дополнительно содержит железо и никель при следующем соотношении компонентов, вес.%: Сг-С,10-18 Си7-9 Sn1-1,5 Fe4-5 Ni5-6 Со. Остальное В этой св зке кобальт обеспечивает высокую прочность, ударную в кость инструмента и надежное удержа ние алмазов. Карбид хрома обеспечивает диспер сионное упрочнение основы, повыша твердость и износостойкость инструмента . Но с увеличением содержани Сг Сз Сболее 18%) ударна в зкость св зки уменьшаетс настолько, что инструмент, например сегменты отрезных кругов, в услови х динамических нагрузок при силовом резании начинают разрушатьс . При содержании Ci Cj менее 10% износостойкость инструмента недостаточна. Медь и олово образуют легкоплавкую олов нистую бронзу, котора выдавлива сь при гор чем прессовании к стенкам графитовой пресс-формы, экранирует (защищает ее от взаимодействи с npeccyeNSJM изделием {св зкой ). При содержании меди и олова менее 8 и 1 вес.% соответственно нельз гарантировать надежной защиты графитовой пресс-формы от взаимодействи с прессуемым изделием при высокой температуре. С увеличением содержани меди и олова более 9 и 1,5 вес.% соответственно наблюдаютс избыточные вытеки. Железо повьааает прочность св зки ( с 90 кг/мм до 120 -кг/юл), никель - пластичность} но с увеличением содержани Fe и Ni более 5 и 6% соответственно отрезные круги начинают работать жестче. Надежное удержание алмазов достигаетс за счет прочного .адгезионного сцеплени алмазных зерен с кобальтом при грр чем прессовании при 1010-1050 С (ниже адгезионное сцепление слабое). Алмазосодержащие режущие элементы, например сегменты отрезных кругов, на св зке изготавливаютс методом порсшковой металлургии из порошков исходных ингредиентов с применением гор чего прессовани . Исходные порошки в нужном соотношении смешиваютс в шаровой мельнице пь на бочка со стальными шарс1ми 4-6 мм. Врем смешени 2 ч при соотношении веса шихты к весу шаров 1:3. Приготовленна шихтасв зка смешиваетс с алмазами и прессуетс при 2 тс/см в заготовки сегментов . Спрессоваиные заготовки подвергаютс гор чему прессованию в графитовой пресс-форме при 10101030 Я2 и 300 кг/см в течение 5 мин. Дл изготовлени алмазного инструмента дл резани гранита можно рекомендовать следующие варианты состава св зки. Примеры 1-3. Составы св зки , вес.% Сг С 1014 18 Си 789 Sn 11,5 1 Со(основа)8276,5 72 Примеры4,В.Составы св зки , вес.%: Сг,С,1810 Си 8,87 Sn 1,21 Ni 65 Co-J627200A The invention relates to the manufacture of diamond tools, in particular, to binder compositions for making diamond cutting discs for cutting granites. Known metal bond for the manufacture of diamond tools with the following ratio of components, wt.%: SGDS, 5-90 Cu3-70 Fe (Co, Ni) 2-30 Sn (2n, Cd, Al, PbJ 2-30 Known link with high content (40-90%) is used in the tool for cutting low-strength and highly abrasive rocks, such as gypsum, marble, limestone, sandstone, etc. G1 J. However, when cutting granites, the tool made on this link quickly it is salted at a high content (40-90%) and quickly and sewed at a low content (5-40%). This is due to the fact that the strength of the binder is insufficient High and the retention of diamond grains in it is weak, since the basis of the link is plastic metals (Cu, Zn, Sn, Pb, Cd) that do not wet the diamond. in the processing of granite and also increases the productivity and plasticity of the instrument in the processing of granite with a high content of quartz. The goal is achieved. - .. 10-18 Si7-9 Sn .1-1,5 CoE Really When working with granite with a high content of quartz, it additionally contains iron and nickel in the following ratio of components, wt.%: Cr – C, 10–18 Cu7–9 Sn1–1.5 Fe4–5 Ni5–6 Co. Else In this bond, cobalt provides high strength, shock to the bone of the tool and reliable retention of diamonds. Chromium carbide provides dispersion hardening of the base, increasing the hardness and wear resistance of the tool. But with an increase in the Cr Cz content of more than 18%, the toughness of the bond decreases to such an extent that the tool, for example, the segments of the cutting wheels, under conditions of dynamic loads during force cutting, begin to break. When the content of Ci Cj is less than 10% of the wear resistance of the tool is insufficient. Copper and tin form low-melting tin bronze, which is squeezed during hot pressing to the walls of the graphite mold, shields it (protects it from interaction with the npeccyeNSJM product {link). When the content of copper and tin is less than 8 and 1 wt.%, Respectively, it is impossible to guarantee reliable protection of the graphite mold from interaction with the extruded product at high temperature. With an increase in the copper and tin contents of more than 9 and 1.5 wt.%, Respectively, excessive outflows are observed. Iron increases bonding strength (from 90 kg / mm to 120 kg / l), nickel — plasticity} but with an increase in the content of Fe and Ni of more than 5 and 6%, respectively, the cutting wheels begin to work harder. Reliable retention of diamonds is achieved due to the durable adhesion of diamond grains with cobalt during heating than pressing at 1010-1050 ° C (weak adhesive adhesion below). Diamond-containing cutting elements, such as cutting wheel segments, are bonded by bonding metallurgy from powders of the original ingredients using hot pressing by bonding. The initial powders in the required ratio are mixed in a ball mill, dr on a barrel with steel balls 4-6 mm. Mixing time is 2 hours with the ratio of the weight of the charge to the weight of balls 1: 3 The prepared mixture is mixed with diamonds and pressed at 2 mc / cm into the workpiece segments. The pressing blanks are hot pressed in a graphite mold at 10101030 H2 and 300 kg / cm for 5 minutes. For the manufacture of diamond tools for cutting granite, we can recommend the following variants of the binder composition. Examples 1-3. Binding compositions, wt.% Cg C 1014 18 Cu 789 Sn 11.5 1 Co (base) 8276.5 72 Examples4, B. Composition of the bond, wt.%: Cg, C, 1810 Cu 8.87 Sn 1, 21 Ni 65 Co-J6272
ЭкСИЛуатационные свойства алмазных отрезных сегментных кругов на св зке оценивают в прсмылленных услови х при резке малопрочного, легкообрабатываемого гранита Вуоксинского месторождени и прочного, труднообрабатываемого гранита с высоким содержанием кварца Янцевского месторождени . ИспытЫвгиот сегментные круги 0 500 мм, оснащенные природами алмазами зернистостью 500/400 при концентрации 50%.The excilation properties of diamond cutting segment wheels on a bond are evaluated under the conditions of cutting low-strength, easily machined granite from the Vuoksinsky deposit and durable, difficult-to-work granite with a high content of quartz from the Yantsevo deposit. Tested in segment circles of 0 500 mm, equipped with diamonds of 500/400 grain nature at a concentration of 50%.
Испытани провод т на модернизированном станке 6М81Г; износ кругов измер ют скобой с индикатором часового-типа . Дл .сравнени испытаны круги на известной св зке. Результаты испытаний приведены в таблице.The tests were carried out on an upgraded 6M81G machine; wheel wear is measured with a bracket with a clock-type indicator. For comparison, circles on a known link were tested. The test results are shown in the table.
1-3 Гранит Вуоксинского месторож- До дени 700-7501-3 Granite of the Vuoksinsky gorodorozh- Until day 700-750
Гранит Янцевского месторождени (с высоким содержанием кварца) Granite of the Yantsevskoye deposit (with a high content of quartz)
Известна Гранит Вуоксинского месторож- До дени 600-750Famous Granite of the Vuoksinsky gorodorozh- Until the day 600-750
Гранит Янцевского месторождени (с высоким содержанием кварца)Granite of the Yantsevskoye deposit (with a high content of quartz)
Результаты испытаний показали, что круги на. данной св зке имеют более высокую стойкость при резкеThe test results showed that the circles on. This bond has a higher cutting resistance.
режет жестче, искрит, не за2 ,3-2,5 саливаетс cuts harder, sparks, not 2, 3-2,5 salives
Режет жестче. Cuts harder.
2,3-2,5 Искрит, не засаливаетс 2,3-2,5 Sparks, do not get dirty
Режет жестко, Cuts hard
3,5-4,0 сильно искрит, засаливаетс 3,5-4,0 strongly sparks, salted
До 400-500Up to 400-500
до 5,0up to 5.0
гранитов по сравнению с кругами на Д5 известной св зке, кроме того рабр- ают в режиме сгшозатачивани .granites in comparison with the circles on the D5 well-known bond, moreover, they work in the mode of sharpening.
Claims (3)