SU1099049A1 - Pulverized/reinforced plugging material for securing wells - Google Patents
Pulverized/reinforced plugging material for securing wells Download PDFInfo
- Publication number
- SU1099049A1 SU1099049A1 SU823468838A SU3468838A SU1099049A1 SU 1099049 A1 SU1099049 A1 SU 1099049A1 SU 823468838 A SU823468838 A SU 823468838A SU 3468838 A SU3468838 A SU 3468838A SU 1099049 A1 SU1099049 A1 SU 1099049A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- fiber
- adhesion
- cement stone
- cement
- water
- Prior art date
Abstract
ДИСПЕРСНО-АРМИРОВАННЫЙ ТАМ-ПОНАЖНЫЙ МАТЕРИАЛ ДЛЯ КРЕПЛЕНИЯ СКВАЖИН, содержащий потландцемент, воду и минеральное волокно с хризотил-асбестом , отличающий- с тем, что, с целью улучшени адгезионных свойств цементного камн путем увеличени адгезии между цементным камнем и волокном, а также увеличени деформативности цементного камн , материал дополнительно содержит кислую соль поливалентного металла или смесь этих солей, силикокристаллит и водорастворимый полимер при следующем соотношении компонентов , нас. ч,: Портландцемент100 Минеральное волокно с хризотил-асбестом 0,5-5,0 Кисла соль поливалентного металла или смесь этих солей 0,1-1,0 Силикокристаллит 20-30 Водорастворимый полимер0 ,01-0,5 Вода100-130DISPERSE REINFORCED TAM-RELEASE MATERIAL FOR FIXING WELLS, containing potland cement, water and mineral fiber with chrysotile asbestos, characterized in that, in order to improve the adhesion properties of the cement stone by increasing the adhesion between the cement stone and the fiber, as well as the adhesion between the cement stone and fiber by increasing the adhesion between the cement stone and fiber by increasing the adhesion between the cement stone and fiber by increasing the adhesion between the cement stone and fiber by increasing the adhesion between the cement stone and fiber. cement stone, the material additionally contains an acidic salt of a polyvalent metal or a mixture of these salts, silicocrystallite and a water-soluble polymer in the following ratio of components, us. h: Portlandcement100 Mineral fiber with chrysotile asbestos 0.5-5.0 Acid polyvalent metal salt or a mixture of these salts 0.1-1.0 Silicocrystalline 20-30 Water-soluble polymer0.0, 01-0.5 Water100-130
Description
И обретенне относитс к проичвод-ству тампонажиых материалов д.п цементирова н нефт :чьгх н гаювых сквлЖИ 1 .And it relates to the production of plugging materials d. Cementirova n nef: chng n guyvyh skvlzhi 1.
Известен тампонажный раствор, содержащий асбестовое минеральное волокиОз например с хризотил-асбестом,, гидросиликатам магни р и т.змпонал( -мый материал 5 содержащий портландцемент и декстрин (,дО)у 2j.Known cement slurry containing asbestos mineral pits, for example, with chrysotile asbestos, magnesium hydrosilicates, etc., (mymy material 5 containing portland cement and dextrin (, gO) y 2j.
Недостатком этих материалов вл етс их недостаточна сила сцаплени со стенками сквалсины и с колонной обсадных труб вследствие низких ад- гезионных свойств цементного камн .The disadvantage of these materials is their insufficient strength of scaling with squalseen walls and with casing string due to the low adhesion properties of the cement stone.
Наиболее близким по составу и технической сущности к предлагаемому вл етс дисперсно-армированнь;й тампонажный материал дл креплени скважин, содержащий, мае. %: портландцемент 96,5-99,5; декстрин 0,2-1,0 и минеральное волокно с хризотил-асбестом более 50% - 0,3-2,5, Нзвестньв материал имеет повьш енные ;1Дгезионные свойства по сравнению с; составами, перечисленными вьпие )| The closest in composition and technical essence to the present is dispersed-reinforced, and grouting material for well casing, containing, May. %: Portland cement 96.5-99.5; dextrin 0.2–1.0 and mineral fiber with chrysotile asbestos of more than 50% - 0.3–2.5, the known material has increased; 1 adhesive properties as compared to; compositions listed above) |
Однако эффект увеличени сцеплени цементного камн с металлом составл ет 0,5 кг/см и деформативпые свойства известного материала неве1 ИКИ .However, the effect of increasing the adhesion of cement stone to metal is 0.5 kg / cm and the deformable properties of the known material, non-ICI.
Это обусловлено тем, что минераль )юе волокно с хризотил-асбестом не имеет достаточного с- еплени с пементным камнем из-за отсутстви прочных химических св зей. Волокниста часть представл ет собой агрегаты (ассодиаты) фибрилл хризотил-асбеста н в силу этого не обладает высокими армирующими свойствами5 кроме того неравномерное ее распределение по объему цементной композиции предопредел ет неравномерность (анизотропность ) прочностных5 деформативньк и адгезионных свойств цементного камн .This is due to the fact that the mineral fiber with chrysotile asbestos does not have sufficient adhesion to the pemennial stone due to the absence of strong chemical bonds. The fibrous part is an aggregate (assodiate) of chrysotile asbestos fibrils and, therefore, does not have high reinforcing properties5 and, moreover, its uneven distribution over the volume of the cement composition determines the unevenness (anisotropy) of the strength5 deformative and adhesive properties of the cement stone.
Цель изобретени - улучпгание адгезионных свойств цементного камн .ЕУтем Увеличени адгезии мелсду цементным камнем и волокном, i. также .уве/шчени деформативности цементного камн .The purpose of the invention is to improve the adhesion properties of cement stone. EFF. Increase the adhesion of the cement stone and fiber, i. also. eve / schcheni deformativnosti cement stone.
Указанна цель достигаетс тем, что дисперсно--армированга)Ш тампонажН61Й материал дл креплени скважин, сэдержаи1Ий портландцемент, воду и минеральное волокно с хризотил-асбесГС )-,, /юпопиителько содержит кислую co.-Fij 11-оливалеит1 О Ч) металла шт смес ЗТ1-ГХ Силе,, си:,г1икокристалпит и водорг .створимьп при с/гкдующем с : отпо пении ком :сНептов 5 мае. ч:This goal is achieved by the fact that dispersively - reinforced reinforcement) cementing material for the attachment of wells, the restraint of Portland cement, water and mineral fiber with chrysotile asbestos) - / / yupititelko contains acidic co.-Fij 11-olivaleit1 O) metal piece mix ZT1-GH Sile, si:, gikikokratpit and vodorg. Dissolve with c / akkomuyuschimuyu with: repo com: snept 5 May. h:
1 00 100
ПортландцементPortland cement
Мит;рральное во,п()кно 0,5-5,0Mit; rral in, p () 0.5-5.0
с хризотил-асбестомwith chrysotile asbestos
Кисла со,7Ь по,тиваrjEHTiioro мета,п,та илиSour, 7b, tivarjEHTiioro meta, p, that or
О,1-1,0 Oh, 1-1.0
смесь этих солей 20-30a mixture of these salts 20-30
(летикокрпсталлит(Lettikorpstallit
;- оде р а с т в 1Э р пм iiiii; - clothing in 1E r pm iiiii
0,01-0,5 0.01-0.5
полн:мер 100-130full: measures 100-130
RcV-UiRcv-ui
1С И1 отовление i acTBOpa осугаествл ;;гс Б следук цэй ггос,:гедовательностн; гначапа осугдествл кгг активацию в жущего с мик(:)ол 5мирующей добавкой путем их совместного помола в помольно--сме ,сителы1о,й установке типа дезинтсгпатора , затем отов т 0,1-1%-ный jiacTBop на сзснова кислой соли полин ,- пптного металла, после этого в р,аствор вво,аи:тс коротксволок истьЕ асбест ,и получен а химически актиниг ),1 сусггензи перемешиваетс , кпггме тоо в по,,ггучеР1чую суспензию Fi)v;);iHTc,4 водорасгворимьш полимер и инг)1;ь осуществ;; етс перемешивание, 1ослс чего механо ;им11чески активированна тампо1-:ажна смесь затвор етс химмческн активированной суспеьзией.1C I1 otlovleniye i acTBOpa has become legal ;; bc sleduk tsey ggos,: hedging; Gnapapa disreputable kgg activation of a mic with a mic (:) ol 5miruyuschim additive by their joint grinding in a grinding - mix, cell1, installation of a type of disintegrator, then from 0.1-1% jiacTBop to the acid salt of polins, - of the metal, then in p, solution in, ai: ts short-wavelength and asbestos, and chemically actinig), 1 susghenzi is mixed, cpggma toto in g), suspension (Fi) v;); iHTc; 4 ) 1; s implemented ;; mixing, once mechanically; tampo-activated tampo1-: the whole mixture is shuttered by a chemically activated suspension.
при в заимодей(:тн}ии ионов 1Ю, ,пентного металла с поверхностными rpynriaMH асбеста,, Бо,г1окна минерала, приобретают высокую сорбционную активность . Кроме того, под воздейстпием кислой среды, образующейс за (,-. гидролиза кислых са,г1еЙ5 происходит интаисиБное вымывание малоактипиых окислов (bigO, СаО) из асбеста, ггс увеличивает псзверхность минерала количество активных центров. При ввеij , в суспензию, содержащую химичксри активированный асбест полимер ,н, последний св зываетс с поверх}1ос:п ью асбеста, образу ггрочнуК) полимер-ми ,н ралы-:ую структуру. стойку о к Ес здействию температуры и минерализованной средьк По,ц действием кислой средь; волокна асбеста расщепл ютс i-a э,пемектарные иголки (фибриллы) , Б рез:/лнтате чего значительно увеличиваетс их арм,ирутоща способность, определ ема отношетп ем (L/D), Посл чаТВорени механохимически активированной ампонажной смеси суспензий,when a loaner (: tn} and ions 1U, of a pent metal with surface rpynriaMH asbestos, Bo, mineralized minerals, acquire a high sorption activity. In addition, under the influence of an acidic medium formed by (, - hydrolysis of acidic acids, hydrolyzed acid occurs the intact leaching of low-acid oxides (bigO, CaO) from asbestos, ghs increases the mineral's superfusion, the number of active sites.When injected, the chemically reacted asbestos polymer contains, but the latter binds to the top of the asbestos to form the polymer th, n raly-: th with The structure is resistant to the effects of temperature and mineralized in the middle of Po, and acidic; asbestos fibers are split by ia e, pemectal needles (fibrils), Bres: /) which greatly increases their arm and curvature, determined by the ratio ( L / D), after mechanically chemically activated a mix of suspensions,
содержащих химически активированное асбестовое волокно, активные центры последнего взаимодействуют с Са(ОН). образу единую и прочную органоминеральную композицию, обладающую высокими адгезионными и деформативными свойствами.containing chemically activated asbestos fiber, the active centers of the latter interact with Ca (OH). image of a single and durable organic composition with high adhesive and deformative properties.
В опытах использовалс асбест 5,6 и 7-го сортов (Р-5-50, П-6-30, К-6-30, 7-450 по ГОСТ 12871-67 Асбест хризотиловый).Asbestos 5.6 and 7th grades (P-5-50, P-6-30, K-6-30, 7-450 according to GOST 12871-67 Chrysotile Asbestos) were used in the experiments.
Кисла соль металла выбираетс из группы - алюминий, железо, хром, медь, цинк.The acid salt of the metal is selected from the group of aluminum, iron, chromium, copper, zinc.
В качестве смеси кислых солей поливалентных металлов можно использовать отход расплавов титановых хлораторов (ОРТХ) со следующим средним химическим составом, мае. %: Ti 1,5-7,0; Fe 5,0-15,0; At 1,5-10,0; Na 5,0-16,0; Mg 0,5-3,0; Cr 0,2-2,0; Cl 50,0-60,0; Ca 0,2-2,0; Cu 0,2-1,5. Данный отход получают при хлорировании титановых шламов.As a mixture of acid salts of polyvalent metals, it is possible to use waste melts of titanium chlorinators (ORTX) with the following average chemical composition, May. %: Ti 1.5-7.0; Fe 5.0-15.0; At 1.5-10.0; Na 5.0-16.0; Mg 0.5-3.0; Cr 0.2-2.0; Cl 50.0-60.0; Ca 0.2-2.0; Cu 0.2-1.5. This waste is obtained by chlorination of titanium sludge.
Водорастворимые полимеры - полиакрил амид (ПАЛ) , реагенты на основеWater-soluble polymers - polyacryl amide (PAL), reagents based on
Мт/- / М Птг П1Mt / - / M Ptg P1
полиакрилонитрила К-ч , К-У , гипан, карбоксиметилцеллюлоза (КМЦ), крахмальный реагент (КР), силикокристаллит - микроармирующа добавка . Известны слоистые вЪлокнистые и каркасные силикокристаллиты.polyacrylonitrile K-h, K-Y, hypan, carboxymethylcellulose (CMC), starch reagent (CR), silicocrystallite - micro-reinforcing additive. Known layered in hollow and frame silicic crystallites.
Составы и свойства предлагаемого тампонажного материала приведены в табл. 1 и 2.The compositions and properties of the proposed grouting material are given in table. 1 and 2.
Анализ табл. 1 и 2 показьшает, что предлагаемый тампонажный материал при содержании компонентов в допустимых пределах и способ его приготовлени позвол ет значительно (на 30-90%) повысить деформативкость и адгезионные свойства цементного камн , что дает возможность повысить качество и обеспечить долговременную изол цию пластов. Указанные составы имеют необходимые технологические свойства, отвечающие требовани м ГОСТ-1581-78 Портландцементы тампонажные.Analysis table. 1 and 2 shows that the proposed grouting material with the content of components within acceptable limits and the method of its preparation allows significantly (30-90%) to increase the deformability and adhesion properties of cement stone, which makes it possible to improve the quality and ensure long-term isolation of the layers. These compositions have the necessary technological properties that meet the requirements of GOST-1581-78 Portland cementing.
оabout
UU
.;;
CJ CjCj cj
иand
(-(-
Cj Р Uj ОCj p uj o
С1)C1)
ЧH
о about
оabout
гg
а ж о,well oh
;э j :j; uh j
,q, q
кЭCE
кЗЩKZh
exЛexL
a)оa) about
у ;Qy; Q
ti;:0ti;: 0
ЩЧSchCH
2О2O
1)CQ1) CQ
иand
иand
а D, о кto этand D, oh kto et
К ТK T
сс tc; о mss tc; about m
га (Л Ш Sha (l sh s
Claims (1)