RU2017138372A - Магниевый сплав, способ его производства и использования - Google Patents
Магниевый сплав, способ его производства и использования Download PDFInfo
- Publication number
- RU2017138372A RU2017138372A RU2017138372A RU2017138372A RU2017138372A RU 2017138372 A RU2017138372 A RU 2017138372A RU 2017138372 A RU2017138372 A RU 2017138372A RU 2017138372 A RU2017138372 A RU 2017138372A RU 2017138372 A RU2017138372 A RU 2017138372A
- Authority
- RU
- Russia
- Prior art keywords
- mass
- mpa
- alloy
- biodegradable implant
- amount
- Prior art date
Links
- 229910000861 Mg alloy Inorganic materials 0.000 title claims 2
- 239000007943 implant Substances 0.000 claims 11
- 229910045601 alloy Inorganic materials 0.000 claims 4
- 239000000956 alloy Substances 0.000 claims 4
- 239000012535 impurity Substances 0.000 claims 4
- 229910052782 aluminium Inorganic materials 0.000 claims 3
- 229910052802 copper Inorganic materials 0.000 claims 3
- 229910052742 iron Inorganic materials 0.000 claims 3
- 229910052748 manganese Inorganic materials 0.000 claims 3
- 229910052759 nickel Inorganic materials 0.000 claims 3
- 229910052710 silicon Inorganic materials 0.000 claims 3
- 229910052749 magnesium Inorganic materials 0.000 claims 2
- 239000011777 magnesium Substances 0.000 claims 2
- 229910052727 yttrium Inorganic materials 0.000 claims 2
- 229910052726 zirconium Inorganic materials 0.000 claims 2
- 229910000838 Al alloy Inorganic materials 0.000 claims 1
- FYYHWMGAXLPEAU-UHFFFAOYSA-N Magnesium Chemical compound [Mg] FYYHWMGAXLPEAU-UHFFFAOYSA-N 0.000 claims 1
- 238000005275 alloying Methods 0.000 claims 1
- 229910052790 beryllium Inorganic materials 0.000 claims 1
- 230000015572 biosynthetic process Effects 0.000 claims 1
- 229910052793 cadmium Inorganic materials 0.000 claims 1
- 239000004053 dental implant Substances 0.000 claims 1
- 229910052738 indium Inorganic materials 0.000 claims 1
- 229910052745 lead Inorganic materials 0.000 claims 1
- 239000011159 matrix material Substances 0.000 claims 1
- 230000001537 neural effect Effects 0.000 claims 1
- 230000000399 orthopedic effect Effects 0.000 claims 1
- 239000002245 particle Substances 0.000 claims 1
- 238000001556 precipitation Methods 0.000 claims 1
- 229910052761 rare earth metal Inorganic materials 0.000 claims 1
- 229910052706 scandium Inorganic materials 0.000 claims 1
- 239000006104 solid solution Substances 0.000 claims 1
- -1 stents Substances 0.000 claims 1
- 229910052718 tin Inorganic materials 0.000 claims 1
- 229910052725 zinc Inorganic materials 0.000 claims 1
Classifications
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
- A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
- A61L27/02—Inorganic materials
- A61L27/04—Metals or alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/06—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of magnesium or alloys based thereon
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
- A61F2/00—Filters implantable into blood vessels; Prostheses, i.e. artificial substitutes or replacements for parts of the body; Appliances for connecting them with the body; Devices providing patency to, or preventing collapsing of, tubular structures of the body, e.g. stents
- A61F2/82—Devices providing patency to, or preventing collapsing of, tubular structures of the body, e.g. stents
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
- A61K6/00—Preparations for dentistry
- A61K6/80—Preparations for artificial teeth, for filling teeth or for capping teeth
- A61K6/84—Preparations for artificial teeth, for filling teeth or for capping teeth comprising metals or alloys
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
- A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
- A61L27/02—Inorganic materials
- A61L27/04—Metals or alloys
- A61L27/047—Other specific metals or alloys not covered by A61L27/042 - A61L27/045 or A61L27/06
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
- A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
- A61L27/50—Materials characterised by their function or physical properties, e.g. injectable or lubricating compositions, shape-memory materials, surface modified materials
- A61L27/58—Materials at least partially resorbable by the body
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
- A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
- A61L31/02—Inorganic materials
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
- A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
- A61L31/02—Inorganic materials
- A61L31/022—Metals or alloys
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
- A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
- A61L31/14—Materials characterised by their function or physical properties, e.g. injectable or lubricating compositions, shape-memory materials, surface modified materials
- A61L31/148—Materials at least partially resorbable by the body
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C23/00—Alloys based on magnesium
- C22C23/02—Alloys based on magnesium with aluminium as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C23/00—Alloys based on magnesium
- C22C23/04—Alloys based on magnesium with zinc or cadmium as the next major constituent
Landscapes
- Health & Medical Sciences (AREA)
- Chemical & Material Sciences (AREA)
- Veterinary Medicine (AREA)
- Public Health (AREA)
- General Health & Medical Sciences (AREA)
- Animal Behavior & Ethology (AREA)
- Life Sciences & Earth Sciences (AREA)
- Engineering & Computer Science (AREA)
- Epidemiology (AREA)
- Oral & Maxillofacial Surgery (AREA)
- Transplantation (AREA)
- Metallurgy (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Mechanical Engineering (AREA)
- Vascular Medicine (AREA)
- Heart & Thoracic Surgery (AREA)
- Inorganic Chemistry (AREA)
- Medicinal Chemistry (AREA)
- Dermatology (AREA)
- Surgery (AREA)
- Biomedical Technology (AREA)
- Physics & Mathematics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Thermal Sciences (AREA)
- Cardiology (AREA)
- Plastic & Reconstructive Surgery (AREA)
- Materials For Medical Uses (AREA)
- Manufacture Of Metal Powder And Suspensions Thereof (AREA)
- Prostheses (AREA)
- Powder Metallurgy (AREA)
Claims (7)
1. Биоразлагаемый имплантат, содержащий магниевый сплав с улучшенными механическими и электрохимическими свойствами, содержащий: Zn в количестве 4,0 масс. % или меньше, Al в количестве от 2,0 до 10,0 масс. %, причём содержание в сплаве Al в масс. % равно содержанию в сплаве Zn в масс. % или превышает его, остальное представлено магнием, содержащим примеси Fe, Si, Mn, Co, Ni, Cu, Zr, Y, Sc, или редкоземельных элементов, имеющих порядковые номера 21, от 57 до 71 и от 89 до 103, Be, Cd, In, Sn и/или Pb, а также Р, содействующие электрохимической разности потенциалов и/или образованию осадков и/или интерметаллических фаз, с суммарным содержанием, не превышающим 0,0063 масс. %, причем матрица сплава характеризуется увеличением упрочности твердого раствора благодаря Al и Zn, а также упрочнением частиц благодаря интерметаллическим фазам, образующимся из Mg и Al.
2. Биоразлагаемый имплантат по п,1, отличающийся тем, что содержание Zn является равняется или меньше чем 2,0 масс. %, в частности предпочтительно равняется или меньше чем 1,0 масс. % и/или в котором содержание Al составляет от 2,0 до 8,0 масс. %, предпочтительно от 3,0 до 8,0 масс. %, и, еще более предпочтительно, от 3,0 до 6,0 масс. %.
3. Биоразлагаемый имплантат по п. 1, отличающийся тем, что отдельные примеси в общем количестве примесей содержатся в следующем количестве в масс. %: Fe, Si, Mn, Ni, Со, Сu, каждый в количестве < 0,0005; Zr, Y, каждый в количестве < 0,0003; и P < 0,0002.
4. Биоразлагаемый имплантат по п. 1, отличающийся тем, что, в случае сочетания легирующих элементов Fe, Si, Mn, Co, Ni, Cu суммарное количество этих примесей не превышает 0,003 масс. %.
5. Биоразлагаемый имплантат по любому из пп. 1-4, отличающийся тем, что сплав имеет мелкозернистую микроструктуру с размером зерен, не превышающим 7,5 мкм, предпочтительно < 5 мкм, и, еще более предпочтительно, < 2,5 мкм.
6. Биоразлагаемый имплантат по любому из пп. 1-5, отличающийся тем, что сплав обладает прочностью на разрыв > 275 МПа, а предпочтительно > 300 МПа, предел текучести > 200 МПа, а предпочтительно > 225 МПа, а коэффициент текучести < 0,8 и, предпочтительно, < 0,75, отличающийся тем, при этом отношение предела текучести к пределу прочности > 50 МПа, а предпочтительно > 100 МПа, а механическая асимметрия < 1,25.
7. Биоразлагаемый имплантат по любому из пп. 1-6, отличающийся тем, что имплантат выбран из группы эндоваскулярных имплантатов, таких как стенты, имплантаты для крепления и временной фиксации имплантатов тканей и тканевых трансплантатов, ортопедических и стоматологических имплантатов, а также невральных имплантов.