RU2005759C1

RU2005759C1 - Adhesive composition

Info

Publication number: RU2005759C1
Authority: RU
Inventors: Ч.С. Асланов; Р.Б. Тагиев; А.А. Тамаркина; С.Л. Зильбертер; Э.С. Мамедова; А.И. Бабаев
Original assignee: Асланов Чингиз Саттар
Priority date: 1991-09-23
Filing date: 1991-09-23
Publication date: 1994-01-15

Abstract

FIELD: adhesive production process. SUBSTANCE: adhesive composition contains 12-204 parts by weight of butadiene-sterene rubber; 7-18 parts by weight of rosin; 0.6-3.5 parts by weight of epoxy-diane resin; 0.6-2.4 parts by weight of industrial oil; 0.2-0.8 parts by weight of oligooxypropylene glycol maleic acid esters of the general formula HO-CH(CH₃)CH₂-OOC-CH=CH-COO[CH₂-CH(CH₃)HO]_1-3-H and 172-187 parts by weight of an organic solvent. The ground butadiene-sterene rubber is dissolved in an organic solvent, the resulting solution is mixed together with the remaining components of the composition under stirring for 4-5 hours at 50-70 C. The characterization of adhesive is as follows: interlaminar strength of metallic material-base foamed polyurethane 0.85 kg/cm, polyethylene 1.1 kg/cm; siliconized paper-base foamed polyurethane 0.06 kgf/cm, polyethylene 0.06 kgf/cm; polyvinylchloride linoleum-concrete 1.8 kgf/cm; shear strength of polyvinylchloride-concrete 8 kgf/8 kgs/cm², flexibility 1 mm, adhesiveness 759 sec. EFFECT: increased bonding strength. 4 tbl

Description

Изобретение относится к получению клеевых композиций на основе синтетических каучуков и может быть использовано для липких лент, герметизации стыков панельных домов, устранения дефектов бетона, склеивания теплозвукоизоляционных материалов к металлу и в других областях народного хозяйства. The invention relates to the production of adhesive compositions based on synthetic rubbers and can be used for adhesive tapes, sealing joints of prefabricated houses, eliminating concrete defects, bonding heat and sound insulating materials to metal and in other areas of the national economy.

Известно использование для липких лент клеевой композиции на основе сополимеров моноакрилатолигооксипропиленгликолей со стиролом. It is known to use adhesive compositions based on copolymers of monoacrylate oligooxypropylene glycols with styrene for adhesive tapes.

Однако эта клеевая композиция многокомпонента; технология нанесения сложная (прилипание к валкам, неудовлетворительные дублирующие свойства, чрезмерная адгезия к силиконизированной бумаге). However, this adhesive composition is multicomponent; complex application technology (adhesion to rolls, poor duplicate properties, excessive adhesion to siliconized paper).

Известен клей на основе синтетических каучуков ГИПК-22-23М, предназначенный для теплозвукоизоляционных материалов. Known adhesive based on synthetic rubbers GIPK-22-23M, designed for heat and sound insulating materials.

Недостатком его является небольшая липкость и пониженная эластичность. Its disadvantage is a small stickiness and reduced elasticity.

Наиболее близким по технической сущности к заявляемой клеевой композиции является клей на основе бутадиен-стирольного каучука, содержащий канифоль, растворитель. The closest in technical essence to the claimed adhesive composition is an adhesive based on styrene-butadiene rubber containing rosin, a solvent.

Указанный клей также обладает низкими адгезией, эластичностью и небольшой липкостью. The specified adhesive also has low adhesion, elasticity and slight stickiness.

Технической задачей изобретения является создание клеевой композиции с повышенными адгезией, липкостью и эластичностью при сохранении пленкообразующих дублирующих свойств. An object of the invention is the creation of an adhesive composition with increased adhesion, stickiness and elasticity while maintaining film-forming duplicate properties.

Техническая задача достигается тем, что клеевая композиция, включающая бутадиен, стирольный каучук, канифоль, индустриальное масло и органический растворитель, дополнительносодержит олигооксипропиленгликольмалеинаты (ОПМ) общей формулы
HO-C

H₂-OOC-CH= CH-COO-

CH₂-C

H
где n= 1-3, и эпоксидную диановую смолу при следующем соотношении компонентов, мас. ч. :
Бутадиен-стирольный каучук 12,0 - 20,0 Канифоль 7,0 - 18,0
Эпоксидная диановая смола 0,6 - 3,6
Индустриальное масло 0,6 - 2,4
Олигооксипропиленгликоль- малеинаты 0,2 - 0,8
Органический рас- творитель 172 - 187
П р и м е р 1. Клеевую композицию готовят следующим образом.The technical problem is achieved in that the adhesive composition, including butadiene, styrene rubber, rosin, industrial oil and an organic solvent, additionally contains oligooxypropylene glycol maleates (OPM) of the general formula
HO-C

H ₂ -OOC-CH = CH-COO-

CH ₂ -C

H
where n = 1-3, and epoxy Dianova resin in the following ratio of components, wt. hours:
Styrene butadiene rubber 12.0 - 20.0 Rosin 7.0 - 18.0
Epoxy Dianne Resin 0.6 - 3.6
Industrial oil 0.6 - 2.4
Oligooxypropylene glycol maleates 0.2 - 0.8
Organic Solvent 172 - 187
PRI me R 1. An adhesive composition is prepared as follows.

12,0 г измельченного бутадиен-стирольного каучука (БСК) (табл. 3) растворяют в 100 мл бензина и толуола (или этилбензола, или этилацетата), добавляют 13,0 г канифоли, 1,2 г эподкидной смолы, 0,6 г индустриального масла и 0,2 г ОПМ и перемешивают в течение 4 - 5 ч при 50 - 70^оС.12.0 g of crushed styrene butadiene rubber (BSC) (Table 3) is dissolved in 100 ml of gasoline and toluene (or ethylbenzene or ethyl acetate), 13.0 g of rosin, 1.2 g of epoxy resin, 0.6 g are added. industrial oil and 0.2 g of OPM and stirred for 4 - 5 hours at 50 - 70 ^about C.

Вязкость клея по вискозиметру ВЗ-1 ( α= 5,8) - 150 - 200^оС.The viscosity of the adhesive on the viscometer VZ-1 (α = 5.8) - 150 - 200 ^about C.

ОПМ получают полимеризацией пропиленоксида [69,6 г (1,2 моля)] с малеиновой кислотой (116 г = 1,0 моль). Время реакции - 4 ч, температура реакции - 25 - 30^оС; продукт представляет собой прозрачную жидкость с приятным эфирным запахом; выход продукта - 158,1 г (85,0% ).An OPM is prepared by polymerizing propylene oxide [69.6 g (1.2 mol)] with maleic acid (116 g = 1.0 mol). The reaction time - 4 hours, the reaction temperature - 25 - 30 ^C; the product is a clear liquid with a pleasant ethereal odor; yield: 158.1 g (85.0%).

Молекулярная масса ОПМ = 245 - 460. The molecular weight of OPM = 245 - 460.

Показатель преломления n_D ²⁰ = 1,4635 - 1,4660.Refractive index n _D ²⁰ = 1.4635 - 1.4660.

Удельный вес, г/см³ 0,935 - 0,967.Specific gravity, g / cm ³ 0.935 - 0.967.

Кислотное число, мг КОН/г 45,6 - 54,7. Acid number, mg KOH / g 45.6 - 54.7.

Коэффициент полимеризации "n" изменяется от 1 до 3. The polymerization coefficient "n" varies from 1 to 3.

Характеристика бутадиен-стирольного каучука
Массовая доля связанного стирола, % 23,0 - 25,0
Массовая доля масла, % 14,0 - 17,0
Влажность, % не более 20,0
Посторонние включения, % Отсутствуют
Массовая доля золы, % , не более 2,0
Вязкость по Муни, Б-1-4-100 45 - 54
Массовая доля органических кислот, % 5,0 - 6,7
Массовая доля мыло органических кислот, не более 0,3
Готовую клеевую композицию наносят на силиконизированную бумагу с последующим дублированием на пеноматериалы.Styrene Butadiene Rubber Characterization
Mass fraction of bound styrene,% 23.0 - 25.0
Mass fraction of oil,% 14.0 - 17.0
Humidity,% no more than 20.0
Extraneous inclusions,% None
Mass fraction of ash,%, no more than 2.0
Mooney viscosity, B-1-4-100 45 - 54
Mass fraction of organic acids,% 5.0 - 6.7
Mass fraction of soap of organic acids, not more than 0.3
The finished adhesive composition is applied to siliconized paper, followed by duplication on foams.

Листы пеноматериалов с нанесенным на них клеем выдерживается в течение 24 ч, после чего подвергаются испытаниям на адгезионные свойства. В табл. 1 приведен режим нанесения клея, в табл. 2, 3, 4 - рецептуры и адгезионные свойства клеев и их сравнение с прототипом. Sheets of foams with adhesive applied on them are aged for 24 hours, after which they are tested for adhesive properties. In the table. 1 shows the mode of application of glue, in table. 2, 3, 4 - formulations and adhesive properties of adhesives and their comparison with the prototype.

Как следует из приведенных данных, состав клея обеспечивает в сравнении с известным составом клея (аналог, прототип) требуемую дублируемость, повышенную адгезию ППЭ и ППУ на металл. (56) Авторское свидетельство СССР N 1014876, кл. C 09 I 7/00, 1981. As follows from the above data, the composition of the adhesive provides, in comparison with the known composition of the adhesive (analog, prototype), the required duplicability, increased adhesion of the PPE and PUF to the metal. (56) Copyright certificate of the USSR N 1014876, cl. C 09 I 7/00, 1981.

Клей ГИПК 22 -23М ТУ 6-07-268-88. GIPK glue 22 -23M TU 6-07-268-88.

Авторское свидетельство ЧССР
N 162168, кл. D 06 N 3/06, опублик. 1976. Czechoslovak copyright certificate
N 162168, cl. D 06 N 3/06, published. 1976.

Claims

GLUE COMPOSITION comprising styrene butadiene rubber, rosin, industrial oil and an organic solvent, characterized in that, in order to increase adhesion and elasticity while maintaining the film-forming and duplicating properties of the composition, it additionally contains oligooxypropylene glycol maleate of the general formula
HO-C

H ₂ -OOC-CH = CH-COO-

CH ₂ -C

H
where n = 1 - 3,
and epoxy Dianova resin in the following ratio, wt. hours:
Styrene butadiene rubber 12 - 20
Rosin 7 - 18
Epoxy Dianne Resin 0.6 - 3.5
Industrial oil 0.6 - 2.4
Oligooxypropylene glycol maleates 0.2 - 0.8
Organic Solvent 172 - 187