LU83694A1 - IMPROVEMENTS IN CAST REFINING PROCESSES - Google Patents
IMPROVEMENTS IN CAST REFINING PROCESSES Download PDFInfo
- Publication number
- LU83694A1 LU83694A1 LU83694A LU83694A LU83694A1 LU 83694 A1 LU83694 A1 LU 83694A1 LU 83694 A LU83694 A LU 83694A LU 83694 A LU83694 A LU 83694A LU 83694 A1 LU83694 A1 LU 83694A1
- Authority
- LU
- Luxembourg
- Prior art keywords
- lime
- refining
- bath
- converter
- oxygen
- Prior art date
Description
( * » 5. h 50¾ -ίο 2159/8110.(* »5. h 50¾ -ίο 2159/8110.
CENTRE DE RECHERCHES METALLURGIQUES -CENTRUM VOOR RESEARCH IN DE METALLURGIE Association sans Lut lucratif -Vereniging zonder winstoogmerk à BRUXELLES, (Belgique) .METALLURGICAL RESEARCH CENTER -CENTRUM VOOR RESEARCH IN DE METALLURGIE Non-profit association -Vereniging zonder winstoogmerk in BRUXELLES, (Belgium).
Perfectionnements aux procédés d'affinage de la fonte.Improvements to the refining processes of cast iron.
La présente invention concerne un procédé d'affinage de fonte, en particulier de fonte hématite, dans un convertisseur à soufflage d'oxygène par le haut.The present invention relates to a method for refining pig iron, in particular hematite pig iron, in a top blown oxygen converter.
On connaît depuis longtemps le procédé d'affinage consistant à insuffler de l'oxygène industriellement pur sur la surface d'un bain de fonte, au moyen d'une lance introduite dans un convertisseur à fond plein.The refining process consisting in injecting industrially pure oxygen onto the surface of a cast iron bath has been known for a long time by means of a lance introduced into a full-bottom converter.
Cependant, à côté de nombreux avantages, ce procédé présente l'inconvénient, bien connu également, de donner lieu au phénomène de moussage de la scorie. Dans certains cas, ce phénomène peut conduire à des débordements de scorie, si des mesures y/ appropriées ne sont pas appliquées rapidement. * j (Jf ! 1 - - 2 -However, in addition to numerous advantages, this method has the disadvantage, also well known, of giving rise to the phenomenon of foaming of the slag. In some cases, this phenomenon can lead to slag overflows, if y / appropriate measures are not applied quickly. * j (Jf! 1 - - 2 -
On a proposé différents moyens, soit pour surveiller l'évolution du moussage et ainsi pouvoir intervenir au moment opportun pour éviter un débordement, soit pour réduire ou même supprimer pratiquement le phénomène.We have proposed different means, either to monitor the evolution of foaming and thus be able to intervene at the appropriate time to avoid an overflow, or to reduce or even virtually eliminate the phenomenon.
Un des moyens récemment proposés pour maîtriser le moussage de -1 la scorie, dans le cas de l'affinage de fonte phosphoreuse, est l'insufflation de gaz neutre sous la surface du bain de fonte à travers des organes de passage, par exemple des briques poreuses disposées dans le fond du convertisseur. Cette technique provoque un brassage du système métal-scorie qui permet également d'améliorer la qualité du métal produit.One of the means recently proposed for controlling the foaming of -1 slag, in the case of refining of phosphorous cast iron, is the blowing of neutral gas under the surface of the melt bath through passage members, for example porous bricks placed at the bottom of the converter. This technique causes a mixing of the metal-slag system which also makes it possible to improve the quality of the metal produced.
On sait par ailleurs que, dans les conditions économiques actuelles, il est avantageux d’utiliser au convertisseur le plus grand volume possible de ferrailles. Il importe cependant de ne pas accroître la consommation d'énergie nécessaire à la fusion de ces ferrailles. A cet égard, il est également connu de brûler, dans le convertisseur même, tout ou partie du CO dégagé par 1' affinage et de récupérer ainsi sa chaleur tant sensible que latente, pour assurer le préchauffage et/ou la fusion des ferrailles. La combustion du CO se déroule d'autant plus aisément que la lance à oxygène est descendue moins profondément dans le convertisseur. Toutefois, l'emploi d'une lance haute favorise l'oxydation et par conséquent le moussage de la scorie.We also know that, under current economic conditions, it is advantageous to use the largest possible volume of scrap in the converter. However, it is important not to increase the energy consumption necessary for the melting of this scrap. In this regard, it is also known to burn, in the converter itself, all or part of the CO released by refining and thus recover its heat, both sensitive and latent, to ensure the preheating and / or the melting of scrap. The combustion of CO takes place all the more easily when the oxygen lance is lowered less deeply into the converter. However, the use of a high lance promotes oxidation and therefore foaming of the slag.
Comme on l'a rappelé plus haut, le moussage de la scorie peut dans le cas des fontes phosphoreuses, être maîtrisé par l'insufflation de gaz neutre sous la surface du bain.As mentioned above, the foaming of the slag can in the case of phosphorous melts, be controlled by the blowing of neutral gas under the surface of the bath.
> .>.
Le demandeur a cependant constaté que dans le cas des fontes non phosphoreuses, dites fontes hématites, l'insufflation de gaz neutre par le fond du convertisseur ne suffisait pas pour * * f -.:¾ empêcher le moussage de la scorie.The applicant has however noted that in the case of non-phosphorous cast irons, called hematite cast irons, the blowing of neutral gas through the bottom of the converter was not sufficient to * * f -.:¾ prevent foaming of the slag.
- 3 - * »- 3 - * ”
Cela constitue un inconvénient sérieux, car les fontes hématites représentent une large part du volume des fontes destinées à l'affinage.This is a serious drawback, since hematite cast irons represent a large part of the volume of cast irons intended for refining.
La présente invention a pour objet un procédé permettant de remédier à cet inconvénient.The subject of the present invention is a method making it possible to remedy this drawback.
Le procédé qui fait l'objet de la présente invention permet d'affiner des fontes à faible teneur en phosphore, tout en assurant une bonne combustion du CO dégagé et par conséquent en permettant une mise au mille de ferrailles élevée, et tout en écartant pratiquement tout risque de moussage de la scorie.The process which is the subject of the present invention makes it possible to refine cast irons with a low phosphorus content, while ensuring good combustion of the CO released and therefore allowing a high scrapping of scrap, and while practically removing any risk of foaming the slag.
Le procédé d'affinage de fonte à faible teneur en phosphore dans un convertisseur à fond plein, qui fait l'objet de la présente invention, dans lequel on insuffle d'une part, un gaz oxydant, de préférence de l'oxygène industriellement pur, sur la surface du bain et d'autre part un gaz neutre sous la surface du bain, et dans lequel on brûle au moins une partie du CO dégagé par les réactions d'affinage au moyen d'oxygène introduit au-dessus du bain, est essentiellement caractérisé en ce que la chaux nécessaire à la formation de la scorie est ajoutée, au moins en partie, sous forme de poudre.The process for refining cast iron with a low phosphorus content in a solid-bottom converter, which is the subject of the present invention, into which is blown on the one hand, an oxidizing gas, preferably industrially pure oxygen , on the surface of the bath and on the other hand a neutral gas under the surface of the bath, and in which at least part of the CO is burned off by the refining reactions by means of oxygen introduced above the bath, is essentially characterized in that the lime necessary for the formation of the slag is added, at least in part, in the form of powder.
La chaux en poudre peut être ajoutée en vrac, notamment au moyen d'un dispositif existant de chargement du convertisseur, par exemple un auget de chargement de ferrailles. Dans ce cas, il est particulièrement avantageux d'ajouter la chaux en même temps que les ferrailles.Powdered lime can be added in bulk, in particular by means of an existing converter loading device, for example a scrap loading bucket. In this case, it is particularly advantageous to add the lime at the same time as the scrap.
·*%· *%
Elle peut aussi, et c'est là une mise en oeuvre particulièrement avantageuse du procédé de l'invention, être transportée par un courant d'oxygène et introduite dans le convertisseur/ au moyen de la lance de soufflage. y ,;fif i - 4 - fIt can also, and this is a particularly advantageous implementation of the method of the invention, be transported by a stream of oxygen and introduced into the converter / by means of the blowing lance. y,; fif i - 4 - f
Différents paramètres peuvent influencer la quantité de chaux qu'il faut introduire dans le convertisseur/ en particulier la granulométrie de la chaux en poudre, la teneur en silicium de la fonte et le volume spécifique du convertisseur.Different parameters can influence the quantity of lime to be introduced into the converter / in particular the particle size of the powdered lime, the silicon content of the pig iron and the specific volume of the converter.
Le demandeur a constaté qu'il est particulièrement avantageux, dans le cadre du procédé de l'invention, d'utiliser de la chaux en poudre ayant une granulométrie telle qu'au moins 95 % des grains ont une dimension inférieure à 160 microns.The applicant has found that it is particularly advantageous, within the framework of the process of the invention, to use powdered lime having a particle size such that at least 95% of the grains have a dimension of less than 160 microns.
Toujours dans le cadre de la présente invention, le demandeur a constaté qu'il était très intéressant d'ajouter la chaux en poudre avant le début de l'opération d'affinage ou tout au début de celle-ci, mais de préférence avant le début de l'affinage. Cette façon de procéder permet d'éviter l'entraînement de la chaux par les gaz de conversion et contribue dès lors à l'éco-/ r· t nomie du procédé .Still in the context of the present invention, the applicant has found that it was very advantageous to add the lime powder before the start of the refining operation or at the very beginning of it, but preferably before the start of ripening. This procedure makes it possible to avoid the lime being entrained by the conversion gases and therefore contributes to the economy of the process.
m , ··*m, ·· *
Claims (5)